Abstract: Steel sheet for porcelain enameling having excellent workability yet capable of providing an enamel layer having excellent adhesion with the steel sheet on direct-on enameling once and still free of black specks defects, a method for producing the same, as well as a porcelain enamel product and the method for producing the same are provided, in which low carbon Al-killed steel sheet, high oxygen steel sheet, Ti-added steel sheet, Nb-added steel sheet, Ti—Nb-added steel sheet or B-added steel sheet is used. A steel sheet for porcelain enameling is produced by applying Ni—Mo alloy plating to the low carbon Al-killed steel sheet, high oxygen steel sheet, Ti-added steel sheet, Nb-added steel sheet, Ti—Nb-added steel sheet or B-added steel sheet having specified components and composition ratio, and after performing heat treatment thereto to control the content of Ni, Mo, and Fe that are present on the surface of the steel sheet in a predetermined range, porcelain enamel is applied and fired.

Abstract: Steel sheet for porcelain enameling capable of realizing excellent enamel adhesion with the steel sheet by direct-on enameling once is provided by using a Ti-added steel sheet; there are also a method for producing the same, as well as a porcelain enamel product and the method for producing the same. A steel sheet for porcelain enameling is produced by providing a Ni—Mo alloy plating film on a Ti-added steel sheet containing 0.01% by weight (wherein, % represents “% by weight” hereinafter) or less of C, 0.5% or less of Mn, 0.04% or less of P, 0.04% or less of S, 0.01 to 0.50% of Ti, and balance Fe accompanied by unavoidable impurities, and by then performing heat treatment thereto to control the content of Ni, Mo, and Fe present in the surface of the steel sheet in a predetermined range, porcelain enamel is applied once and fired.

Abstract: Steel sheet for porcelain enameling having excellent workability yet capable of providing an enamel layer having excellent adhesion with the steel sheet on direct-on enameling once and still free of black specks defects, a method for producing the same, as well as a porcelain enamel product and the method for producing the same are provided, in which low carbon Al-killed steel sheet, high oxygen steel sheet, Ti-added steel sheet, Nb-added steel sheet, Ti—Nb-added steel sheet or B-added steel sheet is used. A steel sheet for porcelain enameling is produced by applying Ni—Mo alloy plating to the low carbon Al-killed steel sheet, high oxygen steel sheet, Ti-added steel sheet, Nb-added steel sheet, Ti—Nb-added steel sheet or B-added steel sheet having specified components and composition ratio, and after performing heat treatment thereto to control the content of Ni, Mo, and Fe that are present on the surface of the steel sheet in a predetermined range, porcelain enamel is applied and fired.

Abstract: Steel sheet for porcelain enameling capable of realizing excellent enamel adhesion with the steel sheet by direct-on enameling once is provided by using a Ti-added steel sheet; there are also a method for producing the same, as well as a porcelain enamel product and the method for producing the same. A steel sheet for porcelain enameling is produced by providing a Ni—Mo alloy plating film on a Ti-added steel sheet containing 0.01% by weight (wherein, % represents “% by weight” hereinafter) or less of C, 0.5% or less of Mn, 0.04% or less of P, 0.04% or less of S, 0.01 to 0.50% of Ti, and balance Fe accompanied by unavoidable impurities, and by then performing heat treatment thereto to control the content of Ni, Mo, and Fe present in the surface of the steel sheet in a predetermined range, porcelain enamel is applied once and fired.