Abstract: Soft magnetic stainless steel having good cold forgeability comprising, by weight, less than 0.015% of C, less than 0.20% of Si, less than 0.35% of Mn, less than 0.010% of S, 8 to 13% of Cr, less than 0.020% of Al, less than 0.0070% of O, less than 0.0100% of N and the balance of Fe and inevitable impurities, with a proviso that C+N content is less than 0.020%. The stainless steel can be incorporated additionally at least one of 0.03 to 0.20% of Ti, 0.002 to 0.02% of Ca, less than 0.30% of Bi, less than 0.040% of Se, 0.002% to 0.040% of Te, 0.02 to 0.15% of Zr, less than 2.5% of Mo, less than 0.50% of Cu, less than 0.50% of Ni, less than 0.20% of Nb and less than 0.20% of V. The stainless steel is suitable as magnetic core materials for use in electronic fuel injection devices, electromagnetic valves, magnetic sensors, etc.

Abstract: As for high strength stainless steels and method for manufacturing the high strength stainless steels, the strength of the stainless steels are enhanced by adding an appropriate amount of both nitrogen and niobium to austenitic stainless steels, inhibiting boron, an impure element, and decreasing the carbon content. The strength of the stainless steels are further enhanced by such heat treatment as control rolling and low temperature solution heat treatment applied to the stainless steels after the control rolling.

Abstract: The present invention relates to a soft magnetic steel improved in electric resistance, coercive force, magnetic flux density, magnetic response, cold forgeability, machinability, and corrosion resistance, which is characterized by the composition containing by weight, 0.015% or lower C+N, 0.20% or lower Si, 0.20% or lower Mn, 7 to 13% Cr, 2 to 5% Al, and balance of Fe with impurities, which is applicable to core materials of electronic fuel injection systems, solenoid valves, electromagnetic sensors, etc.

Abstract: A high strength non-magnetic stainless steel comprising by weight ratio, less than 0.20 % C, less than 1.00 % Si, 14-16 % Mn, less than 0.005 % S, 0.2-1.0 % Ni, 15-19 % Cr, 0.30-0.40 % N, and Fe and other impurity elements, of which C+N constitutes 0.40-0.55 % and the Mn equivalent equals 30-33. The stainless steel has a hardness more than Hv 500, a magnetic permeability less than 1.01 after drawing, the steel may be suitably used as the steel for the micro shafts of video tape recorders and electromagnetic valves.

Abstract: Stainless steels possessing a superior cold workability and hot workability, which are yet economical. The stainless steels comprise not more than 0.04% carbon, not more than 0.60% silicon, 2.2-3.8% manganese, 2.5-4.0% copper, 6-8% nickel, 17-19% chromium, and the remainder being iron together with impurities. And, not more than 0.002% sulfur is decreased to provide stainless steels which possess superior corrosion resistance, and not more than 0.010% nitrogen are decreased in the stainless steels as required.

Abstract: A soft magnetic stainless steel consists essentially of, by weight, up to 0.03% of C, 0.40 to 1.10% of Si, up to 0.50% of Mn, 9.0 to 19.0% of Cr, 0.31 to 0.60% of Al, 0.01 to 0.03% of S, 0.10 to 0.30% of Pb, 0.02 to 0.25% of Ti, 0.02 to 0.10% of Zr, and up to 0.03% of N, and the balance of Fe and inevitable impurities, with a proviso that the C+N content is not more than 0.04% and the Si+Al content is not more than 1.35%. The steel has a magnetic flux density of 13,000 G or more and a coercive force of 1.2 Oe or less as magnetic properties, and a tensile strength of 41 kgf/mm.sup.2 or less and a critical compressibility of 50% or more as formability in cold forging. The steel is suitable for manufacturing, by cold forging, parts with complex shapes such as cores of solenoid operated valves and electromagnetic clutches, and bodies of electronic fuel injection apparatuses for internal combustion engines.

Abstract: A soft magnetic stainless steel consisting essentially of, by weight, up to 0.03% of C, 2.0 to 3.0% of Si, up to 0.40% of Mn, 0.015 to 0.050% of S, 10 to 13% of Cr, 0.05 to 0.20% of Ti, up to 0.03% of N, up to 0.010% of Al, and the balance of Fe and inevitable impurities, with a proviso that the C+N content is not more than 0.05%. The steel has a maximum permeability of not less than 4400 and a magnetic flux density of not less than 12,000 G as magnetic properties, together with a fatigue strength after welding of not lower than 120 kgf cm.sup.2, retains the magnetic properties even after annealing at a high temperature of 920.degree. C., and is excellent in electrical resistance, corrosion resistance, mechanical properties and machinability.