Abstract: Wire rods containing an adequate quantity of C within the range from 0.70 to 1.00%, Si from 0.5 to 3.0%, Mn from 0.30 to 2.0%, Cr from 0.10 to 0.5%, Al from 0.030 to 0.10% and N from 0.004 to 0.015% and unavoidable impurities, and with Fe for all the rest are subjected to re-heat patenting to increase the tensile strength to 135 kgf/mm.sup.2 or higher, then are drawn by adequately selecting the conditions, number of times of drawing in the range from 7 to 16 times, drawings speed from 50 to 550 m/minute, extent of drawing form 70-90, and water cooling immediately after each drawing to manufacture steel wires of high strength and high toughness.The wires are used as PC wires, steel wires for skewed bridge cables, steel stranded wires, spring wires, main cable wires for extra-long suspension bridge large diameter wires for core of aluminum cables steel reinforced (transmission cable), and as galvanized steel wires for such applications.

Abstract: Circularly polarized light caused to be incident on a film surface is converted into three light beams by optical flats to obtain electrical signals corresponding to the intensities of the respective light beams. Two ellipsometric parameters .psi. and .DELTA. are claculated from these three electrical signals.

Abstract: A linearly polarized light beam is applied to the surface of a film and is reflected therefrom. The beam is then split into three light beams by three or four optical flats. These light beams are applied to photoelectric conversion devices after passing through analyzers with fixed analyzing angles. The photoelectric conversion devices convert the beams into electric signals representing the intensities of these light beams. Two ellipsometric parameters .psi. and .DELTA. are calculated from these three electric signals.

Abstract: A spring steel for vehicles having a composition substantially composed of 0.5-0.7 wt % of C, 1.0-1.8 wt & of Si, 0.1-1.0 wt % of Mn, below 0.7 wt % of Cr, 0.03-0.5 wt % of V and the balance of Fe and normally present impurities, and optionally at least one of Al, Zr, Nb and Ti each contained in an amount of 0.02-0.1 wt %.

Abstract: A method and apparatus for the controlled cooling of a hot rolled steel rod. A hot rolled steel rod issued from a final stand of mill train is rapidly cooled, and then formed into a coil. The coiled rod is transported in a generally horizontal direction with its loops held at an angle of 30.degree. to 60.degree. relative to the direction of transportation and with a pitch of at least 2d/sin .alpha. where d is a diameter of the rod and .alpha. is the above-mentioned angle. A cooling medium, e.g. air, is forcibly applied to the coiled rod upwardly from below the coiled rod to cool the coiled rod uniformly at such a cooling rate as to achieve a phase transformation to obtain a structure consisting essentially of fine pearlite. The apparatus includes a cooling device for the rapid cooling, a laying head for the coil forming, a conveyor for transporting the coiled rod while supporting its loops at the angle and pitch, a coolant supply, and a mechanism for collecting the treated rod.

Abstract: A large gauge high strength steel rod having a diameter of not less than 9 mm, is produced from high carbon steel containing, by weight percent, from 0.65 to 0.90% carbon and from 0.15 to 1.5% chromium capable of being drawn without subsequent heat treatment.

Abstract: A large gauge high strength steel rod having a diameter of not less than 9 mm, is produced from high carbon steel containing, by weight percent, from 0.65 to 0.90% carbon and from 0.15 to 1.5% chromium capable of being drawn without subsequent heat treatment.

Abstract: A method and apparatus for cooling a rod of a coil form, immediately after the hot-rolling thereof and within which the rod, whose loops are spaced a given pitch from one another, is laid flat upon a chain conveyor, and more particularly upon rails thereof, and transported therealong by means of endless chains, includes the cooling of the rod with cooling fluid or air which is introduced from below the cooling floors through means of nozzle portions formed within the bodies of the cooling floors. The method and apparatus features the arrangement and construction, including the configuration, of the nozzle portions thus formed, the cooling fluid being projected upwardly at an angle within the range of 10.degree.-70.degree. with respect to the plane of the cooling bed, and horizontally at an angle within the range of 10.degree.-150.degree.

Abstract: A method for cooling a steel wire which is being drawn in a dry lubricant wire drawing operation wherein the rear portion of the die, including the backrelief portion thereof and the wire which has just been drawn to the desired dimension, are brought into direct contact with a cooling medium so as to effect forced cooling thereof, the wire thereby being cooled before the commencement of strain-aging embrittlement within the wire.