Abstract: A plated article has an alloy thin film formed on a substrate and having a catalytically active metal (A) for electroless plating and a metal (B) capable of undergoing displacement plating with a metal ion contained in an electroless plating solution, and a metal thin film formed on the alloy thin film by electroless displacement and reduction plating. The alloy thin film of the catalytically active metal (A) and the metal (B) capable of displacement plating has a composition comprising 5 at % to 40 at % of the metal (A). The metal thin film formed by electroless displacement and reduction plating is a metal thin film having a thickness no greater than 10 nm and a resistivity no greater than 10 ??·cm. Preferably, the metal (B) has a barrier function with respect to a metal of the metal thin film.

Abstract: A metal nano particle can be supported and immobilized on a substrate uniformly. Thus, disclosed is a method for supporting a nano metal particle, which comprises applying a silane coupling agent having at least one functional group capable of capturing a metal (e.g., an imidazole group, an amino group, a diamino group, a mercapto group, and a vinyl group) in its molecule on a substrate, and then contacting the silane coupling agent with a nano particle of a metal (e.g., gold, platinum, silver, copper, palladium, nickel, cobalt), wherein the silane coupling agent may be produced by the reaction between an azole compound with an epoxysilane compound, and wherein the metal nano particle to be contacted with the silane coupling agent is preferably coated with an ionic fluid. Also disclosed is a substrate having a metal nano particle supported thereon, which is produced by the method.

Abstract: The present invention provides a plated article that has a thin seed layer having a uniform thickness, formed by electroless plating and allowing formation of ultrafine wiring, and that avoids the complicated formation of a bilayer of a barrier layer and a catalytic metal layer prior to forming the seed layer. The present invention also provides a method for manufacturing the plated article. The plated article has an alloy thin film formed on a substrate and containing a catalytically active metal (A) for electroless plating and a metal (B) capable of undergoing displacement plating with a metal ion contained in an electroless plating solution, and a metal thin film formed on the alloy thin film by electroless displacement and reduction plating. The alloy thin film of the catalytically active metal (A) and the metal (B) capable of displacement plating has a composition comprising 5at% to 40at% of the metal (A).

Abstract: A metal nano particle can be supported and immobilized on a substrate uniformly. Thus, disclosed is a method for supporting a nano metal particle, which comprises applying a silane coupling agent having at least one functional group capable of capturing a metal (e.g., an imidazole group, an amino group, a diamino group, a mercapto group, and a vinyl group) in its molecule on a substrate, and then contacting the silane coupling agent with a nano particle of a metal (e.g., gold, platinum, silver, copper, palladium, nickel, cobalt), wherein the silane coupling agent may be produced by the reaction between an azole compound with an epoxysilane compound, and wherein the metal nano particle to be contacted with the silane coupling agent is preferably coated with an ionic fluid. Also disclosed is a substrate having a metal nano particle supported thereon, which is produced by the method.

Abstract: The present invention provides a plated article that has a thin seed layer having uniform thickness, formed by electroless plating and allowing formation of ultrafine wiring, and that avoids the complicated formation of a bilayer of a barrier layer and a catalytic metal layer prior to forming the seed layer. The present invention also provides a method for manufacturing the plated article. The plated article has an alloy thin film formed on a substrate and having a catalytically active metal (A) for electroless plating and a metal (B) capable of undergoing displacement plating with a metal ion contained in an electroless plating solution, and a metal thin film formed on the alloy thin film by electroless displacement and reduction plating. The alloy thin film of the catalytically active metal (A) and the metal (B) capable of displacement plating has a composition comprising 5 at % to 40 at % of the metal (A).

Abstract: The present invention provides a plated article that has a thin seed layer having uniform thickness, formed by electroless plating and allowing formation of ultrafine wiring, and that avoids the complicated formation of a bilayer of a barrier layer and a catalytic metal layer prior to forming the seed layer. The present invention also provides a method for manufacturing the plated article. The plated article has an alloy thin film formed on a substrate and having a catalytically active metal (A) for electroless plating and a metal (B) capable of undergoing displacement plating with a metal ion contained in an electroless plating solution, and a metal thin film formed on the alloy thin film by electroless displacement and reduction plating. The alloy thin film of the catalytically active metal (A) and the metal (B) capable of displacement plating has a composition comprising 5 at % to 40 at % of the metal (A).

Abstract: There is provided a cyanide-free immersion type electroless gold plating liquid that is low in toxicity, can be used near a neutral ph, and has a good solder adhesion and plating film adhesion. The electroless gold plating liquid contains a cyanide-free water-soluble gold compound and a pyrosulfurous acid compound. The plating liquid may further contain a sulfurous acid compound and an aminocarboxylic acid compound. Pyrosulfurous acid or an alkali metal, alkaline earth metal, ammonium, or another such salt thereof can be used as the pyrosulfurous acid compound.

Abstract: There is provided a cyanide-free immersion type electroless gold plating liquid that is low in toxicity, can be used near neutral, and has good solder adhesion and plating film adhesion. An electroless gold plating liquid containing a cyanide-free water-soluble gold compound and a pyrosulfurous acid compound. The plating liquid may further contain a sulfurous acid compound and an aminocarboxylic acid compound. Pyrosulfurous acid or an alkali metal, alkaline earth metal, ammonium, or other such salt thereof can be used as the pyrosulfurous acid compound.

Abstract: A method for preventing formation of a "bridge" is provided for electrolessly plated nickel or gold between copper patterns. A circuit board having a copper pattern is immersed in a pretreatment solution containing thiosulfate for electroless nickel plating, or the pretreatment solution is sprayed over the board. The pretreatment solution may be incorporated with an additive, such as a pH adjustor, complexing agent, surfactant or corrosion inhibitor.

Abstract: An acidic pretreating solution for silver plating, which comprises as an agent for preventing the silver deposition by displacement, an inorganic acid and/or an organic acid, and a silver plating process which uses this pretreating solution. The pretreating solution provides long lasting preventive effect against silver deposition by displacement and the resulting silver plated layer firmly adheres to a metal substrate surface.