Abstract: A well cementing method is described for improving cementing quality by controlling the hydration heat of cement slurry. By controlling the degree and/or rate of hydration heat release from cement slurry, the method improves the hydration heat release during formation of cement with curing of cement slurry, improves the binding quality between the cement and the interfaces, and in turn improves the cementing quality at the open hole section and/or the overlap section. The cementing method improves cementing quality of oil and gas wells and reduces the risk of annular pressure.

Abstract: The present invention relates to a trifunctional catalyst used in catalytic cracking device in petroleum refining industry and a method for preparing the same. The trifunctional catalyst of the invention comprises absorbent, cerium dioxide and vanadium pentoxide acting as oxidative catalyst and cerium oxyfluoride acting as structural promoter. The oxidative catalyst and structural promoter are dispersed over the absorbent. The absorbent is spinel-based composite oxides having a general formula of MgAl2-xFexO4.yMgO, where the x is 0.01-0.5 and y is 0.2-1.2. In the trifunctional catalyst, the raw material for forming the chemical compound containing rare-earth cerium is hamartite powder. The method for preparing the trifunctional catalyst of the invention is shown as follows: the components relating to the preparation of the finished product are dissolved or dispersed into liquid materials; then the trifunctional catalyst is obtained after the mixing, drying and calcining of such liquid materials.

Abstract: The present invention relates to a trifunctional catalyst used in catalytic cracking device in petroleum refining industry and a method for preparing the same. The trifunctional catalyst of the invention comprises absorbent, cerium dioxide and vanadium pentoxide acting as oxidative catalyst and cerium oxyfluoride acting as structural promoter. The oxidative catalyst and structural promoter are dispersed over the absorbent. The absorbent is spinel-based composite oxides having a general formula of MgAl2-xFexO4.yMgO, where the x is 0.01-0.5 and y is 0.2-1.2. In the trifunctional catalyst, the raw material for forming the chemical compound containing rare-earth cerium is hamartite powder. The method for preparing the trifunctional catalyst of the invention is shown as follows: the components relating to the preparation of the finished product are dissolved or dispersed into liquid materials; then the trifunctional catalyst is obtained after the mixing, drying and calcining of such liquid materials.