Abstract: The carbon fibers of the present invention have the are configuration as stated below to achieve the object; carbon fibers, characterized in that a polymer having polar groups and groups capable of reacting with a matrix resin are deposited on the fiber surfaces. Furthermore, the carbon fibers of the present invention can be produced by heating the carbon fibers, on the surfaces of which either (1) a monomer having both polar groups and groups capable of reacting with the matrix resin, or (2) the mixture of a monomer having polar groups and a monomer having groups capable of reacting with the matrix resin, is deposited, to polymerize the monomer. The present invention can provide carbon fibers unlikely to cause fluffing and fiber breaking even if rubbed by guide bars and rollers in sophisticated processing, and since they are excellent in adhesion properties to the matrix resin, a carbon fiber reinforced composite material excellent in bending properties and compressive properties can be obtained.

Abstract: The carbon fibers of the present invention have the are configuration as stated below to achieve the object; carbon fibers, characterized in that a polymer having polar groups and groups capable of reacting with a matrix resin are deposited on the fiber surfaces.

Abstract: The carbon fibers of the present invention have a polymer having polar groups and groups capable of reacting with a matrix resin deposited on the fiber surfaces. The carbon fibers can be produced by depositing a monomer having both polar groups and groups capable of reacting with the matrix resin or a mixture of a monomer having polar groups and a monomer having groups capable of reacting with the matrix resin onto the fiber surface and heating to polymerize the monomer(s) forming a polymer having polar groups and groups capable of reacting with a matrix resin. The resultant fibers have excellent adhesion properties to the matrix resin and are unlikely to cause fluffing and fiber breakage.