Abstract: A conversion coating composition comprising 0.01 wt % to 0.2 wt % of phosphorous (P); 0.01 wt % to 0.2 wt % of magnesium (Mg); 0.005 wt % to 0.15 wt % of zirconium (Zr); 0.005 wt % to 0.15 wt % of titanium (Ti); 0.005 wt % to 0.15 wt % of vanadium (V); 0.05 wt % to 1 wt % of phenol resin; the balance of water and other unavoidable impurities is provided. A surface treated steel sheet comprising a base steel sheet; a zinc or zinc alloy plated layer formed on the base steel sheet; a blackening layer formed on the zinc or zinc alloy plated layer; and an organic and inorganic complex conversion coating layer formed on the blackening layer, wherein the organic and inorganic complex conversion coating layer may satisfy the weight ratio of P:Mg:Zr:Ti:V=1:0.045 to 2:0.035 to 1.5:0.035 to 1.3:0.035 to 1.5 (based on the weight of P) is also provided. A method for manufacturing a steel sheet treated with the conversion coating composition is also provided.

Abstract: The present invention relates to a Zn—Mg alloy-coated steel sheet with excellent blackening resistance and excellent coating adhesion and to a method for manufacturing same. Provided are a Zn—Mg alloy-coated steel sheet with excellent blackening resistance and excellent adhesion and a method for manufacturing same, the steel sheet comprising: a substrate steel sheet; a Zn—Fe intermetallic compound layer formed on the substrate steel sheet; a first Zn—Mg coating layer formed on the Zn—Fe intermetallic compound layer and comprising a Zn—Fe intermetallic compound in which the content of Zn is 95% by weight or higher; a second Zn—Mg coating layer formed on the first Zn—Mg coating layer and comprising a Zn—Mg intermetallic compound in which the content of Zn is 80 to 95% by weight; and an oxide film formed on the second Zn—Mg coating layer and comprising a metallic oxide.

Abstract: A passing apparatus includes: upper and lower sealing rolls dealing with variations in a thickness of a proceeding strip, the upper and lower sealing rolls allowing the strip to pass; and a strip sealing unit dealing with variations in a width of the proceeding strip, the strip sealing unit cooperating with the upper and lower sealing rolls to seal the proceeding strip passing through a chamber in a state in which the strip sealing unit surrounds the proceeding strip.

Abstract: An intra prediction method includes searching for a neighboring block restored prior to a current block from among blocks of an image; checking whether the neighboring block found by the searching is a block restored in an intra mode and whether an intra mode of the current block is also a Combined Intra Prediction (CIP) mode in which only blocks pre-restored in the intra mode are referred to; determining based on a checking result of the checking whether the found neighboring block is a reference block available for intra prediction of the current block; and performing intra prediction on the current block by using sample values of the reference block determined as available for the intra prediction of the current block.

Abstract: Provided is a film formation composition for improving the blackening of the surface of a steel sheet, particularly, the surface of a steel sheet containing Mg on the surface thereof, such as a Mg sheet, a plated steel sheet having a plated layer comprising Mg, and the like, a steel sheet comprising a film formed by the composition, and a method for forming the film. Provided are a film formation composition for preventing the blackening of the surface of the steel sheet, comprising: 2.5-7.5 parts by weight of a water-soluble phenoxy resin; 0.1-0.5 parts by weight of a fluorometal acid; 0.1-0.5 parts by weight of a metal compound; and 1-5 parts by weight of a cross-linking agent.

Abstract: Provided is a continuous coating apparatus which can supply a liquid coating material (a molten metal) to a levitation-heating space through various paths, and can easily control a supply flow rate of the liquid coating material, and has a simplified structure. The continuous coating apparatus includes: a vacuum chamber unit through which a coating target passes; a levitation-heating unit disposed in the vacuum chamber unit and generating an evaporation vapor by vaporizing a supplied coating material; and a liquid coating material supply unit connected so that a liquid coating material is supplied to at least one of an upper portion and a lower portion of the levitation-heating unit, and communicating with the outside of the vacuum chamber unit.

Abstract: Provided is an aluminum (Al) plating layer/aluminum (Al)-magnesium (Mg) plating layer multi-layered structure alloy plated steel sheet having excellent plating adhesiveness and corrosion resistance, which is characterized in that the Al—Mg plating layer is formed on the Al plating layer. According to the present invention, corrosion resistance of an Al plated steel sheet is further improved by forming an Al—Mg alloy plating layer, and plating adhesiveness between plating layer and underlying steel sheet may be improved as well as excellent stability and practicality being realized.

Abstract: Provided is a dry coating apparatus for coating a coating material, i.e., deposition vapor (metal vapor) on a substrate (a steel strip). The dry coating apparatus includes a coating part disposed in a vacuum to coat deposition vapor generated through heating and evaporation of a supplied coating material onto a proceeding object to be coated and a heating source disposed in an atmosphere to heat and levitate the coating material in the coating part.

Abstract: A passing apparatus includes: upper and lower sealing rolls dealing with variations in a thickness of a proceeding strip, the upper and lower sealing rolls allowing the strip to pass; and a strip sealing unit dealing with variations in a width of the proceeding strip, the strip sealing unit cooperating with the upper and lower sealing rolls to seal the proceeding strip passing through a chamber in a state in which the strip sealing unit surrounds the proceeding strip.

Abstract: There is provided a zinc alloy coated steel sheet including a vacuum deposited layer capable of improving corrosion resistance and sealer adhesion that are suitable for the use in automobiles, and a process of manufacturing the same. The zinc alloy coated steel sheet includes a zinc coating layer formed on a steel sheet; and a zinc/metal alloy deposited layer formed on the zinc coating layer, wherein the zinc coating layer, and a metal diffusion layer is present in the zinc coating layer.

Abstract: The steel plate is manufactured from a composition comprising C, N and S in an amount of 0.0150% by weight or less in total; Mn in an amount of 0.2 to 0.8% by weight; Al inan amount of 0.6% by weight or less; Si in an amount of 0.4% by weight or less; Cu and/or Sn in an amount of 0.1 to 0.6% by weight in total; and Fe for the remainder, and inevitably present elements, whereby the steel plate can show excellent electromagnetic shield effect and hot-dip galvanization properties.

Abstract: A steel plate and a hot-dip galvanized steel plate, superior in terms of high electromagnetic shield capacity. The steel plate is prepared from a composition comprising C, N and S in an amount of 0.150% by weight or less in total; Mn in an amount of 0.1 to 1.0% by weight; Si in an amount of 0.5% by weight or less; Al in an amount of 1.0% by weight or less; P in an amount of 0.06% by weight or less; and Fe for the remainder, and inevitable elements, and shows a yield strength of 18 kg/mm2 or higher, and an elongation of 40% or higher. The hot-dip galvanized steel plate is prepared from a composition comprising C, N and S in an amount of 0.0150 % by weight or less in total; Mn in an amount of 0.2 to 0.8% by weight; Al in an amount of 0.6% by weight or less; Si in an amount of 0.4% by weight or less; P in an amount of 0.06% by weight or less, with the proviso that the sum of Mn, Al, Si and P amounts to 0.2-1.0% by weight; and Fe for the remainder, and inevitably present elements.

Abstract: Disclosed are a steel plate and a hot-dip galvanized steel plate, superior in terms of high electromagnetic shield capacity. The steel plate is prepared from a composition comprising C, N and S in an amount of 0.150% by weight or less in total; Mn in an amount of 0.1 to 1.0% by weight; Si in an amount of 0.5% by weight or less; Al in an amount of 1.0% by weight or less; P in an amount of 0.06% by weight or less; and Fe for the remainder, and inevitable elements, and shows a yield strength of 18 kg/mm2 or higher, and an elongation of 40% or higher. The hot-dip galvanized steel plate is prepared from a composition comprising C, N and S in an amount of 0.0150% by weight or less in total; Mn in an amount of 0.2 to 0.8% by weight; Al in an amount of 0.6% by weight or less; Si in an amount of 0.4% by weight or less; P in an amount of 0.06% by weight or less, with the proviso that the sum of Mn, Al, Si and P amounts to 0.2˜1.0% by weight; and Fe for the remainder, and inevitably present elements.

Abstract: Disclosed are a high-strength steel plate with excellent electromagnetic shield capacity and a method for manufacturing the same. The steel plate is manufactured from a composition comprising C, N and S in an amount of 0.0150% by weight or less in total; Mn in an amount of 0.2 to 0.8% by weight; Al in an amount of 0.6% by weight or less; Si in an amount of 0.4% by weight or less; Cu and/or Sn in an amount of 0.1 to 0.6% by weight in total; and Fe for the remainder, and inevitably present elements, whereby the steel plate can show excellent electromagnetic shield effect and hot-dip galvanization property.