Abstract: A method of manufacturing a fuel cell catalyst can include a method of manufacturing a carbon carrier for a fuel cell catalyst, in which the carbon carrier can have an improved binding force to a catalytic metal and improved carbon durability. The carbon carrier can be coated with a carbon layer highly doped with heteroatoms. The carbon layer can be formed by uniformly compounding a conductive polymer containing the heteroatoms with the carbon carrier and heat-treating the compounded mixture.

Abstract: Disclosed are a mesoporous support for a catalyst of a fuel cell, which includes a graphite layer formed only on its surface and a method producing the same. The support may include a substrate; a graphite layer in a crystalline form and formed on a surface of a substrate, and further include a first pore having an average pore size of less than about 2 nm and a second pore having an average pore size of about 2 nm to 50 nm.

Abstract: An electrode for a membrane-electrode assembly having improved oxygen permeability by reducing the ionomer content includes a catalyst including a support and an active metal supported on the support, an ionomer, and an additive including a carbon material and a proton conductive functional group bonded to the carbon material.

Abstract: An activated carbon manufacturing method may include preparing activated carbon precursors, carbonizing the activated carbon precursors by performing a heat treatment on the activated carbon precursors, equalizing the activated carbon precursors carbonized, in the carbonizing, by grinding the activated carbon precursors, activating the activated carbon precursors by inserting an oxidizing agent and distilled water into the equalized activated carbon precursors and performing a heat treatment on the activated carbon precursors, and introducing metal oxide particles into the activated carbon precursors by mixing the activated precursors, a metal salt, and a reducing agent in a solvent to perform reaction on the activated carbon precursors.

Abstract: Disclosed is an activated carbon including pores formed on a surface thereof, in particular, the pores include ultra-micropores having a diameter that is equal to or less than about 1.0 nm.

Abstract: A method for manufacturing activated carbon may include preparing activated carbon precursors, carbonizing the activated carbon precursors by performing a heat treatment on the carbon precursors, equalizing the activated carbon precursors carbonized in the carbonizing, by grinding the activated carbon precursors, and activating the activated carbon precursors by introducing a mixture gas including carbon dioxide and steam into the ground activated carbon precursors and performing a heat treatment on the activated carbon precursors.

Abstract: An activated carbon manufacturing method may include preparing activated carbon precursors, carbonizing the activated carbon precursors by performing a heat treatment on the activated carbon precursors, equalizing the activated carbon precursors which were carbonized, in the carbonizing, by grinding the activated carbon precursors, activating the activated carbon precursors by inserting an oxidizing agent and distilled water into the equalized activated carbon precursors, and performing a heat treatment on the activated carbon precursors, and introducing a nitrogen-based functional group into a surface of the activated carbon precursors by mixing the activated carbon precursors, a nitrogen material, and a solvent to perform reaction on the activated carbon precursors.

Abstract: A method for manufacturing activated carbon may include preparing activated carbon precursors, carbonizing the activated carbon precursors by performing a heat treatment on the carbon precursors, equalizing the activated carbon precursors carbonized in the carbonizing, by grinding the activated carbon precursors, and activating the activated carbon precursors by introducing a mixture gas including carbon dioxide and steam into the ground activated carbon precursors and performing a heat treatment on the activated carbon precursors.

Abstract: An activated carbon manufacturing method may include preparing activated carbon precursors, carbonizing the activated carbon precursors by performing a heat treatment on the activated carbon precursors, equalizing the activated carbon precursors carbonized, in the carbonizing, by grinding the activated carbon precursors, activating the activated carbon precursors by inserting an oxidizing agent and distilled water into the equalized activated carbon precursors and performing a heat treatment on the activated carbon precursors, and introducing metal oxide particles into the activated carbon precursors by mixing the activated precursors, a metal salt, and a reducing agent in a solvent to perform reaction on the activated carbon precursors.

Abstract: An activated carbon manufacturing method may include preparing activated carbon precursors, carbonizing the activated carbon precursors by performing a heat treatment on the activated carbon precursors, equalizing the activated carbon precursors which were carbonized, in the carbonizing, by grinding the activated carbon precursors, activating the activated carbon precursors by inserting an oxidizing agent and distilled water into the equalized activated carbon precursors, and performing a heat treatment on the activated carbon precursors, and introducing a nitrogen-based functional group into a surface of the activated carbon precursors by mixing the activated carbon precursors, a nitrogen material, and a solvent to perform reaction on the activated carbon precursors.

Abstract: Disclosed is an activated carbon including pores formed on a surface thereof, in particular, the pores include ultra-micropores having a diameter that is equal to or less than about 1.0 nm.

Abstract: Disclosed is an active carbon that includes micropores having a diameter of about 0.5 nm to about 0.8 nm in a content of about 70 vol % to about 90 vol % based on the total volume of the total pores, and has a nitrogen-containing functional group introduced on the surface thereof. Moreover, disclosed is a method for preparing active carbon. The method may include steps of: forming a reaction mixture including a carbon precursor, an alkali salt, and an organic compound including a nitrogen-containing functional group; and heating the reaction mixture to a temperature of about 800° C. to about 1000° C. in the presence of nitrogen gas.

Abstract: Disclosed is an active carbon that includes micropores having a diameter of about 0.5 nm to about 0.8 nm in a content of about 70 vol % to about 90 vol % based on the total volume of the total pores, and has a nitrogen-containing functional group introduced on the surface thereof. Moreover, disclosed is a method for preparing active carbon. The method may include steps of: forming a reaction mixture including a carbon precursor, an alkali salt, and an organic compound including a nitrogen-containing functional group; and heating the reaction mixture to a temperature of about 800° C. to about 1000° C. in the presence of nitrogen gas.