Abstract: A silicon-carbon containing electrode material includes a porous carbon structure including pores, and a silicon-containing coating formed on the porous carbon structure. A volume ratio of mesopores is 70% or more based on a total pore volume of the porous carbon structure. A weight ratio of silicon is 30 wt % or more based on a total weight of the electrode material. A high-capacity secondary battery is effectively implemented by using silicon-carbon containing electrode material.

Abstract: The present disclosure relates to a method for preparing a mordenite zeolite, the method including crystallizing, at a temperature of 150° C. to 190° C., a gel which includes, in mol based on 1 mol of silica, 0.02 to 0.2 of an alumina precursor, 0.01 to 0.04 of a structure-directing agent, 0.1 to 0.18 of a pH control agent, and 10 to 100 of water. According to the present disclosure, a mordenite zeolite having high particle size uniformity and a particle size controllable while maintaining the particle size uniformity may be prepared.

Abstract: Disclosed are a process and system that are capable of performing selective hydrogenation on aromatic fractions by configuring a catalyst bed through staged loading of a plurality of hydrogenation catalysts with different catalytic properties, or configuring a catalyst system in which a plurality of hydrogenation catalysts are arranged using a plurality of reactors in such a way as to be equivalent with the staged loading, and as a result, are capable of suppressing aromatic loss while improving the selective removal of unsaturated hydrocarbons in the aromatic fraction and durability compared to the case of using a single catalyst.

Abstract: Disclosed are a process and system that are capable of performing selective hydrogenation on aromatic fractions by configuring a catalyst bed through staged loading of a plurality of hydrogenation catalysts with different catalytic properties, or configuring a catalyst system in which a plurality of hydrogenation catalysts are arranged using a plurality of reactors in such a way as to be equivalent with the staged loading, and as a result, are capable of suppressing aromatic loss while improving the selective removal of unsaturated hydrocarbons in the aromatic fraction and durability compared to the case of using a single catalyst.

Abstract: Disclosed herein are a dehydrogenation catalyst having single-atom cobalt loaded onto a silica support that has undergone pretreatment including a thermal treatment and a high-temperature aqueous treatment (reaction), a preparation method therefor, and a method for producing olefins by dehydrogenating corresponding paraffins, particularly light paraffins in the presence of the dehydrogenation catalyst.

Abstract: Provided are a separator and an electrochemical device using the same, in particular, a separator having significantly low heat shrinkage even at a high temperature and also significantly improved adhesive strength by including inorganic particles having specific fluorescence properties in the separator, and an electrochemical device using the same.

Abstract: Disclosed are a catalyst and a preparation method therefor, the catalyst being able to maintain a high production yield of C8 aromatic hydrocarbons in the process of converting a feedstock containing alkyl aromatics to C8 aromatic hydrocarbons such as mixed xylene through disproportionation/transalkylation/dealkylation while reducing a content of ethylbenzene in the products.

Abstract: Disclosed herein are a dehydrogenation catalyst having single-atom cobalt loaded onto a silica support that has undergone pretreatment including a thermal treatment and a high-temperature aqueous treatment (reaction), a preparation method therefor, and a method for producing olefins by dehydrogenating corresponding paraffins, particularly light paraffins in the presence of the dehydrogenation catalyst.

Abstract: Provided are a separator and a method for producing the same, and more particularly, a separator which may secure battery stability and has characteristics of significantly low heat shrinkage even at a high temperature and minimally increased resistance, and a method for producing the same. The separator according to the present disclosure includes: a porous substrate; and an inorganic particle layer positioned on one or both surfaces of the porous substrate, wherein the inorganic particle layer includes inorganic particles and a rod-shaped inorganic binder.

Abstract: Provided are a separator and a method for producing the same, and more particularly, a separator which may secure battery stability and has characteristics of significantly low heat shrinkage even at a high temperature and minimally increased resistance, and a method for producing the same. The separator according to the present disclosure includes: a porous substrate; and an inorganic particle layer positioned on one or both surfaces of the porous substrate, wherein the inorganic particle layer includes inorganic particles and a sheet-shaped inorganic binder.

Abstract: A method for producing a sheet phase pseudo-boehmite. The method includes: a) putting an organic acid into an aqueous solution in which an aluminum precursor is dispersed; and b) putting a product from the process of a) into a Taylor reactor, wherein a pressure of the Taylor reactor is 1 to 100 bar.

Abstract: Disclosed are a catalyst and a preparation method therefor, the catalyst being able to maintain a high production yield of C8 aromatic hydrocarbons in the process of converting a feedstock containing alkyl aromatics to C8 aromatic hydrocarbons such as mixed xylene through disproportionation/transalkylation/dealkylation while reducing a content of ethylbenzene in the products.

Abstract: Disclosed are a bifunctional catalyst and a preparation method therefor, the bifunctional catalyst being suitable to produce high-value aromatic hydrocarbons by subjecting alkylaromatic hydrocarbons to a disproportionation/transalkylation/dealkylation reaction while suppressing aromatic loss or subjecting C8 aromatic hydrocarbons to an isomerization reaction while suppressing xylene loss.

Abstract: Provided are a method for producing boehmite nanoparticles and an apparatus for producing the same, and more particularly, a method for producing boehmite nanoparticles and an apparatus for producing the same, which allow continuous production of nano-sized boehmite nanoparticles in a uniform size. The method for producing boehmite nanoparticles includes (S1) supplying a mixture including an aluminum hydroxide and an organic acid to a reaction unit; and (S2) heating and pressurizing the mixture supplied to the reaction unit simultaneously and sequentially.

Abstract: Provided are a nano-sized thin sheet-like pseudoboehmite and a method of producing the same. The method of producing a sheet-like pseudoboehmite is performed by a one-pot method, unlike the conventional method of performing the reaction first in a basic solution, and then performing redispersion in an acidic solution, thereby simplifying the production process, and thus, may be useful in the production industry of a separator for a secondary battery, and the like.

Abstract: The present invention relates to a method for preparing hierarchical zeolites, including the steps of preparing a first mixture solution including a structure-directing agent, an alumina precursor and a pH controller; preparing a second mixture solution by injecting a silica precursor into the first mixture solution; preparing an aqueous solution including a surfactant; preparing a third mixture solution by injecting the aqueous solution into the second mixture solution; and drying and heat-treating the third mixture solution. According to the present invention, hierarchical zeolites having a uniform morphology can be prepared, and thus hierarchical zeolites having improved activity are provided.

Abstract: Disclosed are a bifunctional catalyst and a preparation method therefor, the bifunctional catalyst being suitable to produce high-value aromatic hydrocarbons by subjecting alkylaromatic hydrocarbons to a disproportionation/transalkylation/dealkylation reaction while suppressing aromatic loss or subjecting C8 aromatic hydrocarbons to an isomerization reaction while suppressing xylene loss.

Abstract: Disclosed are a bifunctional catalyst and a preparation method therefor, the bifunctional catalyst being suitable to produce high-value aromatic hydrocarbons by subjecting alkylaromatic hydrocarbons to a disproportionation/transalkylation/dealkylation reaction while suppressing aromatic loss or subjecting C8 aromatic hydrocarbons to an isomerization reaction while suppressing xylene loss.

Abstract: The present disclosure relates to a method for preparing a mordenite zeolite, the method including crystallizing, at a temperature of 150° C. to 190° C., a gel which includes, in mol based on 1 mol of silica, 0.02 to 0.2 of an alumina precursor, 0.01 to 0.04 of a structure-directing agent, 0.1 to 0.18 of a pH control agent, and 10 to 100 of water. According to the present disclosure, a mordenite zeolite having high particle size uniformity and a particle size controllable while maintaining the particle size uniformity may be prepared.

Abstract: Disclosed are a dehydrogenation catalyst having single-atom cobalt loaded onto a support including a zirconia core surface-modified with silica, a method for producing the dehydrogenation catalyst, and a method for producing corresponding olefin through dehydrogenation of paraffin, particularly light paraffin, in the presence of the dehydrogenation catalyst.