Abstract: This invention relates to a polysiloxane with a comb-like structure and with tertiary amine groups, and the method of preparing the same. The polysiloxane of the invention does not include any active hydrogen groups so that the amount of the amine groups can increase, which in turn improves the effect of self-emulsification. This makes the polysiloxane applicable in water-soluble resins, for example as an accelerator in water-soluble epoxy resin or water soluble fiber dying treating agent. When used as fiber treatment agent, the polysiloxane will not cause yellowing.

Abstract: A pultrusion processing method for long fiber-reinforced nylon which combines the nylon anionic ring-opening polymerization technology and the pultrusion processing method to manufacture long fiber-reinforced thermoplastic nylon composites. The method comprises the steps of forming an active caprolactam sodium salt catalyst composition by reacting melt nylon 6 monomer raw material, i.e., caprolactum, with sodium hydride, forming co-catalyst composition by melting caprolactam and a polymeric co-catalyst, then mixing the active caprolactum sodium salt catalyst composition and the co-catalyst composition in a continuous mixing device to obtain a reaction mixture with low viscosity. The mixture is then charged into a closed impregnating tank to impregnate preheated and dried reinforced fiber, which is immediately pulled into a hot mold for composite molding processing to form a finished product of long fiber-reinforced nylon composites.