Abstract: A diagnostic method and system for measuring potential and electric field of plasma are provided. According to operation parameters of a magnetic confinement fusion device and relevant parameter data of a plurality of candidate particle elements, signal-noise ratios are calculated. to select a neutral beam particle element. Beam trajectories varying in incident velocity, incident angle and sampling area are obtained by iterative calculation, and a preset parameter which enables the beam trajectories to pass through an entrance slit of an analyzer is obtained. A neutral beam that meets the preset parameter is injected into the plasma. An energy of the primary beam generated by collision ionization in a sampling area is measured, and potential of the sampling area is obtained according to law of conservation of energy. Sampling areas are detected to obtain potential spatial distribution of the plasma and a radial electric field, and the diagnostic is finished.

Abstract: A multi-stage modified thermoplastic starch (TPS) masterbatch is obtained by four-stage modification treatment as follows: (i) 100 parts of starch with a moisture content of 15% to 30% are added to a high-speed mixer and stirred under room temperature; (ii) Heated to 50° C. to 70° C., polybutadiene (PB), plasticizer and a chemical modifier are added. The mixture is then stirred a second time; (iii) Heated to 75° C. to 95° C., tackifier, lubricant, filler and chain extender are added. The mixture is again stirred a third time. (iv) A biodegradable resin is added at this temperature, and the resulting mixture is stirred a fourth time. After the stirring is completed, the resulting mixture is incubated at this temperature for a predetermined time, and then added to a twin-screw extruder for melt extrusion. The present invention also discloses a preparation method and use.

Abstract: A multi-stage modified thermoplastic starch (TPS) masterbatch is obtained by four-stage modification treatment as follows: (i) 100 parts of starch with a moisture content of 15% to 30% are added to a high-speed mixer and stirred under room temperature; (ii) Heated to 50° C. to 70° C., polybutadiene (PB), plasticizer and a chemical modifier are added. The mixture is then stirred a second time; (iii) Heated to 75° C. to 95° C., tackifier, lubricant, filler and chain extender are added. The mixture is again stirred a third time. (iv) A biodegradable resin is added at this temperature, and the resulting mixture is stirred a fourth time. After the stirring is completed, the resulting mixture is incubated at this temperature for a predetermined time, and then added to a twin-screw extruder for melt extrusion. The present invention also discloses a preparation method and use.