Abstract: A titanium alloy blade tip with a wear-resistant protective coating and a preparation method thereof are provided. The method includes: (1) spraying MCrAlY alloy powder on a surface of a titanium alloy blade tip by high velocity oxygen fuel (HVOF) spraying at a spraying distance of 300-400 mm to obtain the titanium alloy blade tip with a MCrAlY layer on the surface; where M is one of Ni and NiCo; (2) pre-plating Ni at a current density of 4-10 A/dm2; (3) placing the pre-plated titanium alloy blade tip in a Watt solution, covering a surface of the pre-plated titanium alloy blade tip obtained in the step (2) with abrasive particles, and then performing composite electroplating at a current density of 0.5-2 A/dm2. In the method, the wear-resistant protective coating with the high adhesion strength is prepared on the titanium alloy blade tip, and the wear-resistant protective coating has good wear resistance.

Abstract: A titanium alloy blade tip with a wear-resistant protective coating and a preparation method thereof are provided. The method includes: (1) spraying MCrAlY alloy powder on a surface of a titanium alloy blade tip by high velocity oxygen fuel (HVOF) spraying at a spraying distance of 300-400 mm to obtain the titanium alloy blade tip with a MCrAlY layer on the surface; where M is one of Ni and NiCo; (2) pre-plating Ni at a current density of 4-10 A/dm2; (3) placing the pre-plated titanium alloy blade tip in a Watt solution, covering a surface of the pre-plated titanium alloy blade tip obtained in the step (2) with abrasive particles, and then performing composite electroplating at a current density of 0.5-2 A/dm2. In the method, the wear-resistant protective coating with the high adhesion strength is prepared on the titanium alloy blade tip, and the wear-resistant protective coating has good wear resistance.

Abstract: A dense thick alloy coating with no layered organizational structure and a preparation method thereof are provided. The preparation method includes the following steps: step 1, placing a substrate in a plasma spraying apparatus, controlling a vacuum degree of the plasma spraying apparatus to be 0.2 mbar-0.5 mbar, controlling a length of a plasma flame of the plasma spraying apparatus to be 1000 mm-1200 mm, and controlling a diameter of the plasma flame to be 200 mm-300 mm; step 2, preheating, by using a plasma spray gun, the substrate to a temperature of 700° C.-1000° C. to obtain a preheated substrate; step 3, plasma spraying an alloy powder on the preheated substrate under a specific plasma spraying condition to obtain a sprayed substrate; and step 4, cooling the sprayed substrate after the plasma spraying, to thereby obtain the dense thick alloy coating without layered organizational structure.