Abstract: A liquid low concentration sodium-containing silicate solution as electrolyte for lead-acid storage batteries and its applications, is prepared by mixing a silica gel containing 40˜60 wt % SiO2, the weight units of such a silica gel are 5˜15; add 15-25 weight units water and stir until the concentration of the mixture is 0.65˜0.85 0Be? measured by a Baum densimeter, adjusting the pH value of this mixture to 1-4 using inorganic acid and magnetizing the mixture under 1000-6000 Gauss magnetic field for 5-10 minutes, stir the magnetized mixture until the viscosity of the mixture is less than 0.02 poise and finally obtain a liquid low concentration sodium-containing silicate solution. The electrolyte can be used as electrolyte or activation solution for common or special lead-acid storage batteries.

Abstract: The present invention is related to a liquid low concentration sodium-containing silicate solution as electrolyte for lead-acid storage batteries and its applications. Such an electrolyte is prepared by mixing a silica gel containing 40˜60 wt % SiO2, the weight units of such a silica gel are 5˜15; add 15-25 weight units water and stir until the concentration of the mixture is 0.65˜0.85 0Be? measured by a Baumé densimeter, adjusting the pH value of this mixture to 1-4 using inorganic acid and magnetizing the mixture under 1000-6000 Gauss magnetic field for 5-10 minutes, stir the magnetized mixture until the viscosity of the mixture is less than 0.02 poise and finally obtain a liquid low concentration sodium-containing silicate solution. It can be used as electrolyte or activation solution for common or special lead-acid storage batteries. The lead-acid storage batteries using above electrolyte showed increased specific energy density up to more than 53 W/Kg.

Abstract: A liquid low concentration sodium-containing silicate solution as electrolyte for lead-acid storage batteries and its applications, is prepared by mixing a silica gel containing 40˜60 wt % SiO2, the weight units of such a silica gel are 5˜15; add 15-25 weight units water and stir until the concentration of the mixture is 0.65˜0.85 0Be? measured by a Baum densimeter, adjusting the pH value of this mixture to 1-4 using inorganic acid and magnetizing the mixture under 1000-6000 Gauss magnetic field for 5-10 minutes, stir the magnetized mixture until the viscosity of the mixture is less than 0.02 poise and finally obtain a liquid low concentration sodium-containing silicate solution. The electrolyte can be used as electrolyte or activation solution for common or special lead-acid storage batteries.

Abstract: The present invention is related to a liquid low concentration sodium-containing silicate solution as electrolyte for lead-acid storage batteries and its applications. Such an electrolyte is prepared by mixing a silica gel containing 40˜60 wt % SiO2, the weight units of such a silica gel are 5˜15; add 15-25 weight units water and stir until the concentration of the mixture is 0.65˜0.85 0Be′ measured by a Baumé densimeter, adjusting the pH value of this mixture to 1-4 using inorganic acid and magnetizing the mixture under 1000-6000 Gauss magnetic field for 5-10 minutes, stir the magnetized mixture until the viscosity of the mixture is less than 0.02 poise and finally obtain a liquid low concentration sodium-containing silicate solution. It can be used as electrolyte or activation solution for common or special lead-acid storage batteries. The lead-acid storage batteries using above electrolyte showed increased specific energy density up to more than 53 W/Kg.

Abstract: Present invention is related to a liquid low concentration sodium-containing silicate solution as the activation solution for lead-acid storage batteries and an internal activation method. Such an activation solution is prepared by mixing a silica gel containing 40˜60 wt % SiO2, the weight units of such a silica gel are 5-15, with 15-25 weight units of water. Adjusting the pH value of this mixture to 1-4 using inorganic acid and magnetizing the mixture in 1000-6000 Gauss magnetic field for 5-10 minutes, and finally obtains a liquid low concentration sodium-containing silicate solution with a viscosity less than 0.02 poise. Fill this activation solution into battery tank and use a charger to activate electrochemically. The operating temperature is room temperature and time is 30-50 hours. Using such an activation solution and procedures described above can avoid the releasing of acid smog and serious environmental pollution and healthy hazard for workers.