Abstract: Disclosed is a conductive polyamide resin composition that excels not only in electroconductivity, but also in fuel resistance, particularly resistance against alcohol-containing fuel, and further excels in fluidity and moldability, and is capable of yielding a molded article with high impact resistance, the conductive polyamide resin composition including: 84 to 40% by mass of a polyamide resin (A); 5 to 30% by mass of conductive carbon black (B); 3 to 30% by mass of an ethylene-?-olefin copolymer (C) that has a reactive functional group capable of reacting with a terminal group of polyamide resin and/or an amido group on a principal chain of polyamide resin; and 1 to 20% by mass of a conductive polyethylene resin (D).

Abstract: Disclosed is a conductive polyamide resin composition that excels not only in electroconductivity, but also in fuel resistance, particularly resistance against alcohol-containing fuel, and further excels in fluidity and moldability, and is capable of yielding a molded article with high impact resistance, the conductive polyamide resin composition including: 84 to 40% by mass of a polyamide resin (A); 5 to 30% by mass of conductive carbon black (B); 3 to 30% by mass of an ethylene-?-olefin copolymer (C) that has a reactive functional group capable of reacting with a terminal group of polyamide resin and/or an amido group on a principal chain of polyamide resin; and 1 to 20% by mass of a conductive polyethylene resin (D).

Abstract: Provided is a component used in a fuel feed apparatus (500), containing: a conductive polyamide layer (25) formed of a conductive polyamide resin composition, in which the conductive polyamide resin composition contains: a polyamide resin, a conductive carbon black, an ethylene-?-olefin copolymer, and a conductive polyethylene resin, and satisfies the following characteristics (a) and (b): (a) initial volume resistivity of a flat plate obtained by injection forming is 1×105 ?·cm or less, and volume resistivity after exposing the flat plate to CM15 fuel for 168 hours is 1×107 ?·cm or less, and (b) charpy impact strength at ?40° C. of a test piece obtained by injection forming is 2.0 KJ/m2 or greater.