Abstract: The present invention discloses a PBAT resin composition comprising: (a) Poly (butyleneadipate-co-terephthalate); (b) a cyclic esterified product having a structure represented by the formula (I) Wherein the content by weight of the cyclic esterified product is from 10 ppm to 2000 ppm, based on the total weight of the PBAT resin composition. In the present invention, the service life of the PBAT resin composition can be greatly extended by adding cyclic esterified product in the PBAT resin composition and controlling the content of the cyclic esterified product in the composition in the range of 10 ppm to 2000 ppm. And after boiled for 240 hours in 95% ethanol at 40° C., the film produced from blowing or the articles produced from injection have less surface precipitates, with excellent surface appearance properties.

Abstract: The present invention discloses a PBAT resin composition comprising following components: (a) poly(butyleneadipate-co-terephthalate); (b) iron element; wherein, based on a total weight of the PBAT resin composition, a weight content of the iron element is 1 ppm-500 ppm. By adding iron-containing compounds into the composition and controlling the content of the iron element in a range of 1 ppm-500 ppm in the composition, a speed of reaction of aromatic structure in the PBAT resin under a hot and humid condition can be postponed, so that after the prepared PBAT resin composition is aged in boiling water for 24 hours and 48 hours, a variation of b-value is less than 2. The PBAT resin composition has obviously improved color stability in resistance to boiling water aging.

Abstract: A biodegradable polyester composition based on a total weight of the biodegradable polyester composition, including a weight content of a cyclic ester compound having a structure shown as formula (I), which is 100 ppm-950 ppm; and based on the total weight of the biodegradable polyester composition, a weight content of cyclopentanone is 0.5 ppm-85 ppm is provided. The cyclic ester compound and cyclopentanone is added into the composition and controlling the content of the cyclic ester compound and the content of cyclopentanone in a certain range in the composition to realize an anti-thermal oxidative aging property of the biodegradable polyester composition. In addition, a film is prepared by blow molding or a part is prepared by injection molding after being digested with 95% ethanol at 40° C. for 240 hours.

Abstract: The present invention discloses a biodegradable polyester composition, wherein based on a total weight of the biodegradable polyester composition, a weight content of glycidyl methacrylate is 0.05 ppm-10 ppm. In the present invention, by adding a trace amount of glycidyl methacrylate into a chosen formula of the biodegradable polyester composition and controlling the weight content of glycidyl methacrylate which finally remains in the biodegradable polyester composition as 0.05 ppm-10 ppm, a compatibility between aliphatic-aromatic polyester and polylactic acid in the biodegradable polyester composition can be greatly enhanced, which enables the biodegradable polyester composition to have excellent surface property of film material, and no fisheye occurs on the film material because of a fluctuation of processing technique.

Abstract: The present invention discloses a biodegradable polyester composition, wherein based on a total weight of the biodegradable polyester composition, a weight content of styrene is 0.1 ppm-30 ppm. When the weight content of styrene which is added into a chosen formula of the biodegradable polyester composition based on the total weight of the biodegradable polyester composition is controlled as 0.1 ppm-30 ppm, the present invention may guarantee the biodegradable polyester composition with excellent transmittance and haze effect, and meanwhile may guarantee the biodegradable polyester composition with suitable UV resistance function, without reducing a degradation rate of the biodegradable polyester composition.

Abstract: A biodegradable polyester composition based on a total weight of the biodegradable polyester composition, including a weight content of a cyclic ester compound having a structure shown as formula (I) which is 100 ppm-950 ppm; and based on the total weight of the biodegradable polyester composition, a weight content of tetrahydrofuran is 3 ppm-200 ppm is provided. The cyclic ester compound and tetrahydrofuran is added into the composition and controlling the content of the cyclic ester compound and the content of tetrahydrofuran in a certain range in the composition to realize an anti-thermal oxidative aging property of the biodegradable polyester composition. In addition, a film is prepared by blow molding or a part is prepared by injection molding after being digested with 95% ethanol at 40° C. for 240 hours.

Abstract: A biodegradable polyester composition based on a total weight of the biodegradable polyester composition, including a weight content of tetrahydrofuran, which is 3 ppm-200 ppm; and based on the total weight of the biodegradable polyester composition, a weight content of cyclopentanone is 0.5 ppm-85 ppm is provided. The tetrahydrofuran and cyclopentanone is added into the composition and controlling the content of tetrahydrofuran and the content of cyclopentanone in a certain range in the composition to realize printing performance. Moreover, when a velocity of film blowing is 176 Kg/h, a range of a film thickness is less than 0.2 ?m and a relative deviation of the film thickness is less than 1%.

Abstract: The present invention discloses a PBAT resin composition comprising: (a) Poly (butyleneadipate-co-terephthalate); (b) a cyclic esterified product having a structure represented by the formula (I) Wherein the content by weight of the cyclic esterified product is from 10 ppm to 2000 ppm, based on the total weight of the PBAT resin composition. In the present invention, the service life of the PBAT resin composition can be greatly extended by adding cyclic esterified product in the PBAT resin composition and controlling the content of the cyclic esterified product in the composition in the range of 10 ppm to 2000 ppm. And after boiled for 240 hours in 95% ethanol at 40° C., the film produced from blowing or the articles produced from injection have less surface precipitates, with excellent surface appearance properties.

Abstract: The present invention discloses a biodegradable polyester composition, wherein based on a total weight of the biodegradable polyester composition, a weight content of glycidyl methacrylate is 0.05 ppm-10 ppm. In the present invention, by adding a trace amount of glycidyl methacrylate into a chosen formula of the biodegradable polyester composition and controlling the weight content of glycidyl methacrylate which finally remains in the biodegradable polyester composition as 0.05 ppm-10 ppm, a compatibility between aliphatic-aromatic polyester and polylactic acid in the biodegradable polyester composition can be greatly enhanced, which enables the biodegradable polyester composition to have excellent surface property of film material, and no fisheye occurs on the film material because of a fluctuation of processing technique.

Abstract: The present invention discloses a biodegradable polyester composition, wherein based on a total weight of the biodegradable polyester composition, a weight content of styrene is 0.1 ppm-30 ppm. When the weight content of styrene which is added into a chosen formula of the biodegradable polyester composition based on the total weight of the biodegradable polyester composition is controlled as 0.1 ppm-30 ppm, the present invention may guarantee the biodegradable polyester composition with excellent transmittance and haze effect, and meanwhile may guarantee the biodegradable polyester composition with suitable UV resistance function, without reducing a degradation rate of the biodegradable polyester composition.

Abstract: The present invention discloses a PBAT resin composition comprising following components: (a) poly(butyleneadipate-co-terephthalate); (b) iron element; wherein, based on a total weight of the PBAT resin composition, a weight content of the iron element is 1 ppm-500 ppm. By adding iron-containing compounds into the composition and controlling the content of the iron element in a range of 1 ppm-500 ppm in the composition, a speed of reaction of aromatic structure in the PBAT resin under a hot and humid condition can be postponed, so that after the prepared PBAT resin composition is aged in boiling water for 24 hours and 48 hours, a variation of b-value is less than 2. The PBAT resin composition has obviously improved color stability in resistance to boiling water aging.

Abstract: A biodegradable polyester composition based on a total weight of the biodegradable polyester composition, including a weight content of tetrahydrofuran, which is 3 ppm-200 ppm; and based on the total weight of the biodegradable polyester composition, a weight content of cyclopentanone is 0.5 ppm-85 ppm is provided. The tetrahydrofuran and cyclopentanone is added into the composition and controlling the content of tetrahydrofuran and the content of cyclopentanone in a certain range in the composition to realize printing performance. Moreover, when a velocity of film blowing is 176 Kg/h, a range of a film thickness is less than 0.2 ?m and a relative deviation of the film thickness is less than 1%.

Abstract: A biodegradable polyester composition based on a total weight of the biodegradable polyester composition, including a weight content of a cyclic ester compound having a structure shown as formula (I) which is 100 ppm-950 ppm; and based on the total weight of the biodegradable polyester composition, a weight content of tetrahydrofuran is 3 ppm-200 ppm is provided. The cyclic ester compound and tetrahydrofuran is added into the composition and controlling the content of the cyclic ester compound and the content of tetrahydrofuran in a certain range in the composition to realize an anti-thermal oxidative aging property of the biodegradable polyester composition. In addition, a film is prepared by blow molding or a part is prepared by injection molding after being digested with 95% ethanol at 40° C. for 240 hours.

Abstract: A biodegradable polyester composition based on a total weight of the biodegradable polyester composition, including a weight content of a cyclic ester compound having a structure shown as formula (I), which is 100 ppm-950 ppm; and based on the total weight of the biodegradable polyester composition, a weight content of cyclopentanone is 0.5 ppm-85 ppm is provided. The cyclic ester compound and cyclopentanone is added into the composition and controlling the content of the cyclic ester compound and the content of cyclopentanone in a certain range in the composition to realize an anti-thermal oxidative aging property of the biodegradable polyester composition. In addition, a film is prepared by blow molding or a part is prepared by injection molding after being digested with 95% ethanol at 40° C. for 240 hours.