Abstract: A coated electric wire for winding that includes an insulation coating including appropriate pores in a resin to suppress erosion due to partial discharge is provided. The present disclosure relates to a coated electric wire for winding that includes a conductor and an insulation coating that coats a periphery of the conductor, wherein the insulation coating includes a constant volume of pores having an average diameter equal to or more than a pore diameter (A) obtained by a specific measuring method.

Abstract: A coated electric wire for winding that includes an insulation coating including appropriate pores in a resin to suppress erosion due to partial discharge is provided. The present disclosure relates to a coated electric wire for winding that includes a conductor and an insulation coating that coats a periphery of the conductor, wherein the insulation coating includes a constant volume of pores having an average diameter equal to or more than a pore diameter (A) obtained by a specific measuring method.

Abstract: A method for insulating connection ends of a stator winding includes a resin placing step of placing a resin member formed of a thermosetting resin which is to be melted by heating on connection ends in a coil end portion of a stator winding of a rotary electric machine, a melting step of melting the resin member by heating to cover the connection ends with a melted resin, and a curing step of curing the melted resin after the melting step. Recesses and projections for positioning that correspond to the arrangement locations of the connection ends can be provided on a surface of the resin member.

Abstract: A method for insulating connection ends of a stator winding includes a resin placing step of placing a resin member formed of a thermosetting resin which is to be melted by heating on connection ends in a coil end portion of a stator winding of a rotary electric machine, a melting step of melting the resin member by heating to cover the connection ends with a melted resin, and a curing step of curing the melted resin after the melting step. Recesses and projections for positioning that correspond to the arrangement locations of the connection ends can be provided on a surface of the resin member.

Abstract: Using the dope containing the following cellulose acetate (1), (2), or (3), a film is prepared by the casting process: (1) a cellulose acetate having carboxyl groups binding to at least one member selected from the group consisting of a cellulose acetate and a hemicellulose acetate, wherein at least a part of said carboxyl groups are in an acidic form; (2) a cellulose acetate containing at least one member selected from the group consisting of an acid having an acid dissociation exponent pKa of 1.93 to 4.50 in water, an alkali metal salt of said acid and an alkaline earth metal of said acid; or (3) a cellulose acetate containing an alkali metal or an alkaline earth metal wherein the total content of an alkaline metal and an alkaline earth metal in 1 gram of the cellulose acetate is from an effective amount to 5.5×10?6 equivalent (in terms of ion equivalent). The above cellulose acetate is also useful for spinning process. The cellulose acetate includes a cellulose diacetate and a cellulose triacetate.