Abstract: Provided is powdered gyrolite-type calcium silicate that has a relatively large particle size, yet is endowed with both a high oil absorption and a high particle strength. The powdered gyrolite-type calcium silicate has (1) an oil absorption of at least 2.8 mL/g, (2) an average particle diameter of at least 40 ?m, and (3) in treatment where the gyrolite-type calcium silicate is charged into a laser diffraction-type particle size analyzer within the range of a diffraction volume of from 0.1 to 0.6 and circulated at a flow rate of 32.5 mL/s for 5 minutes, a percent change in average particle diameter following treatment with respect to average particle diameter before treatment of 15% or less.

Abstract: Provided is a powder containing ferric pyrophosphate that affords high iron absorbability, as a main component of an oral iron preparation. The present invention relates to a composite powder containing ferric pyrophosphate, which is a powder containing ferric pyrophosphate and a sodium component, wherein (1) the content of ferric pyrophosphate is 95 wt % or higher, and (2) a (Fe+Na)/P molar ratio is 0.8 to 1.0.

Abstract: Provided is a powdered tobermorite-type calcium silicate-based material capable of demonstrating high oil absorption. The powdered tobermorite-type calcium silicate-based material is characterized in that (1) a molar ratio of SiO2/CaO in the material is 1.5 or more, and (2) a cumulative pore volume having a pore size of 3.6 nm to 200 nm in the material is 0.9 cc/g or more, and a cumulative pore volume having a pore size of 3.6 nm to 5000 nm is 2.6 cc/g or more.

Abstract: Provided is a powder containing ferric pyrophosphate that affords high iron absorbability, as a main component of an oral iron preparation. The present invention relates to a composite powder containing ferric pyrophosphate, which is a powder containing ferric pyrophosphate and a sodium component, wherein (1) the content of ferric pyrophosphate is 95 wt % or higher, and (2) a (Fe+Na)/P molar ratio is 0.8 to 1.0.

Abstract: Provided is a powdered tobermorite-type calcium silicate-based material capable of demonstrating high oil absorption. The powdered tobermorite-type calcium silicate-based material is characterized in that (1) a molar ratio of SiO2/CaO in the material is 1.5 or more, and (2) a cumulative pore volume having a pore size of 3.6 nm to 200 nm in the material is 0.9 cc/g or more, and a cumulative pore volume having a pore size of 3.6 nm to 5000 nm is 2.6 cc/g or more.

Abstract: Provided is powdered gyrolite-type calcium silicate that has a relatively large particle size, yet is endowed with both a high oil absorption and a high particle strength. The powdered gyrolite-type calcium silicate has (1) an oil absorption of at least 2.8 mL/g, (2) an average particle diameter of at least 40 ?m, and (3) in treatment where the gyrolite-type calcium silicate is charged into a laser diffraction-type particle size analyzer within the range of a diffraction volume of from 0.1 to 0.6 and circulated at a flow rate of 32.5 mL/s for 5 minutes, a percent change in average particle diameter following treatment with respect to average particle diameter before treatment of 15% or less.

Abstract: Provided is a method that enables a calcium silicate-based material to be produced more efficiently. The method of producing a calcium silicate-based material comprises: (1) a step of obtaining a reaction product by reacting raw materials containing a calcium component, a silicon component and an aluminum component in an aqueous medium; and (2) a step of forming calcium silicate by subjecting the reaction product to hydrothermal treatment.

Abstract: Provided is a method that enables a calcium silicate-based material to be produced more efficiently. The method of producing a calcium silicate-based material comprises: (1) a step of obtaining a reaction product by reacting raw materials containing a calcium component, a silicon component and an aluminum component in an aqueous medium; and (2) a step of forming calcium silicate by subjecting the reaction product to hydrothermal treatment.

Abstract: Provided is a method that enables a calcium silicate-based material to be produced more efficiently. The method of producing a calcium silicate-based material comprises: (1) a step of obtaining a reaction product by reacting raw materials containing a calcium component, a silicon component and an aluminum component in an aqueous medium; and (2) a step of forming calcium silicate by subjecting the reaction product to hydrothermal treatment.