Abstract: An acrylic resin film material comprising at least a multilayer structure polymer with a particular structure prevent a molded item from being whitened during insert- or in-mold molding and meet the requirement for surface hardness, heat resistance, and transparency or matting performance for vehicle applications. It is also possible to use an acrylic resin film material exhibiting a difference of 30% or less between haze values as determined in accordance with the testing method of JIS K7136 (haze measurement method) after and before a tensile test where a test piece with a width of 20 mm is pulled under the conditions of an initial inter-chuck distance of 25 mm, a rate of 50 mm/min and a temperature of 23° C. until an end-point inter-chuck distance becomes 33 mm as well as having a pencil hardness of 2 B or higher as determined in accordance with JIS K5400.

Abstract: An acrylic resin film material comprising at least a multilayer structure polymer with a particular structure prevent a molded item from being whitened during insert- or in-mold molding and meet the requirement for surface hardness, heat resistance, and transparency or matting performance for vehicle applications. It is also possible to use an acrylic resin film material exhibiting a difference of 30% or less between haze values as determined in accordance with the testing method of JIS K7136 (haze measurement method) after and before a tensile test where a test piece with a width of 20 mm is pulled under the conditions of an initial inter-chuck distance of 25 mm, a rate of 50 mm/min and a temperature of 23° C. until an end-point inter-chuck distance becomes 33 mm as well as having a pencil hardness of 2B or higher as determined in accordance with JIS K5400.

Abstract: An acrylic resin film material comprising at least a multilayer structure polymer with a particular structure prevent a molded item from being whitened during insert- or in-mold molding and meet the requirement for surface hardness, heat resistance, and transparency or matting performance for vehicle applications. It is also possible to use an acrylic resin film material exhibiting a difference of 30% or less between haze values as determined in accordance with the testing method of JIS K7136 (haze measurement method) after and before a tensile test where a test piece with a width of 20 mm is pulled under the conditions of an initial inter-chuck distance of 25 mm, a rate of 50 mm/min and a temperature of 23° C. until an end-point inter-chuck distance becomes 33 mm as well as having a pencil hardness of 2 B or higher as determined in accordance with JIS K5400.

Abstract: The present invention provides a matte acrylic resin film which can realize unprecedented design characteristics and is excellent in handleability, the matte layer of which does not generate cracks even in the case of deep drawing of insert molding or in-mold decorating and which has anti-scratch property, surface hardness, heat resistance and flatting, a method for producing the same, and a laminated product in which the matte acrylic resin film is laminated on a substrate. More specifically the matte acrylic resin film comprises an acrylic resin film base and a matte layer which is formed, with the thickness of 0.1 to 5 ?m, on one surface of the acrylic resin film base and has a matting agent and a binder resin.

Abstract: An acrylic resin film material comprising at least a multilayer structure polymer with a particular structure prevent a molded item from being whitened during insert- or in-mold molding and meet the requirement for surface hardness, heat resistance, and transparency or matting performance for vehicle applications. It is also possible to use an acrylic resin film material exhibiting a difference of 30% or less between haze values as determined in accordance with the testing method of JIS K7136 (haze measurement method) after and before a tensile test where a test piece with a width of 20 mm is pulled under the conditions of an initial inter-chuck distance of 25 mm, a rate of 50 mm/min and a temperature of 23° C. until an end-point inter-chuck distance becomes 33 mm as well as having a pencil hardness of 2 B or higher as determined in accordance with JIS K5400.

Abstract: There is provided an acrylic resin film having good matted appearances and good printing characteristics, e.g., little suffering missing prints when printed. There is provided an acrylic resin film having a differential 60° surface gloss of 5% or more between the front and back sides, and thickness of 300 &mgr;m or less; a method of producing the above-described acrylic resin film, where a molten acrylic resin composition is extruded, and then rolled between a mirror-ground roll and rubber or embossed roll into the film; and a laminate (formed article coated with the acrylic resin film) with a side having a higher 60° surface gloss coming into contact with a base.

Abstract: A thermoplastic resin composition comprising 10 to 98 parts by weight of a graft polymer (1A) containing a rubber-like polymer (1G) having a diene unit content of 50% by weight or less, 2 to 50 parts by weight of a hydroxyl group-containing acrylic copolymer (1B) and 0 to 80 parts by weight of other thermoplastic resin (1F), wherein the rubber-like polymer (1G) is at least one selected from the group consisting of a diene-based rubber, a polyorganosiloxane-based rubber and an olefin-based rubber; and, a graft copolymer (2A) obtained by grafting a vinyl-based polymer to a (meth)acrylate-based rubber-like polymer (2G) expansion-treated with an acid group-containing copolymer latex (2K) wherein the (meth)acrylate-based rubber-like polymer contains two or more poly-functional monomer units.

Abstract: There is provided an acrylic resin film having good matted appearances and good printing characteristics, e.g., little suffering missing prints when printed.

Abstract: An acrylic film with excellent flexibility is easy to process and has 70 to 95 parts by weight of an acrylic rubber-containing polymer (A) and to 30 parts by weight of an acrylic-based thermoplastic polymer (B) and having a total amount of (A) and (B) of 100 parts by weight; a gel content of 50 to 70% by weight; and elongation at break in one direction of 180% or more. The acrylic rubber-containing polymer (A) has an elastic copolymer having a monomer unit whose polymer has a glass transition temperature of more than 65° C. The acrylic-based thermoplastic polymer (B) has a glass transition temperature of 65° C. or less and a weight average molecular weight of 100,000 to 300,000.

Abstract: Disclosed is a technology for providing a thermoplastic resin composition or resin laminate having an excellent mat property by using, as matting agent, a copolymer (B) prepared by polymerizing 0.5 to 80% by weight of a hydroxyalkyl (meth)acrylate having a C.sub.1-8 alkyl group and 10 to 99% by weight of an alkyl methacrylate having a C.sub.1-13 alkyl group, with a C.sub.1-8 alkyl acrylate, vinyl aromatic monomer, another vinyl monomer, and a cross-linking monomer being optional.

Abstract: Disclosed is a technology for providing a thermoplastic resin composition or resin laminate having an excellent mat property by using, as matting agent, a copolymer (B) prepared by polymerizing 0.5 to 80% by weight of a hydroxyalkyl (meth)acrylate having a C.sub.1-8 alkyl group and 10 to 99% by weight of an alkyl methacrylate having a C.sub.1-13 alkyl group, with a C.sub.1-8 alkyl acrylate, vinyl aromatic monomer, another vinyl monomer, and a cross-linking monomer being optional.

Abstract: Disclosed is a technology for providing a thermoplastic resin composition or resin laminate having an excellent mat property by using, as matting agent, a copolymer (B) prepared by polymerizing 0.5 to 80% by weight of a hydroxyalkyl (meth)acrylate having a C.sub.1-8 alkyl group and 10 to 99% by weight of an alkyl methacrylate having a C.sub.1-13 alkyl group, with a C.sub.1-8 alkyl acrylate, vinyl aromatic monomer, another vinyl monomer, and a cross-linking monomer being optional.