Abstract: The present invention provides a dental product comprising a base material formed of a zirconia sintered body, and having high aesthetic quality with enhanced fracture toughness and with reduced chipping and cracking in the porcelain layer. The present invention also provides a method for manufacturing such a dental product. The present invention relates to a dental product comprising: a base material formed of a zirconia sintered body, and a porcelain layer, wherein the porcelain of the porcelain layer has a suitable firing temperature of 900° C. or more, and the porcelain layer has a fracture toughness value of 1.20 MPa·m0.5 or more.

Abstract: A resin film-laminated metal sheet includes a metal sheet and thermoplastic resin films that are fused to both surfaces of the metal sheet, the metal sheet is a steel sheet having a thickness of 0.08 mm or more or an aluminum sheet having a thickness of 0.15 mm or more, and, when a surface of the thermoplastic resin film opposite to a surface that is fused to the metal sheet is defined as a first surface, the surface tension on the first surface in at least one of the thermoplastic resin films is 50 mN/m or less, the surface tension on the surface that is fused to the metal sheet is 36 mN/m or more, and the amount of a wax attached to the first surface is more than 0 mg/m2 and 5.00 mg/m2 or less.

Abstract: The present invention provides a coloring solution for zirconia, which, when used on zirconia before firing of the zirconia, causes the zirconia to exhibit only a slight color difference before and after the firing and thus enables accurate prediction of the post-firing color tone of the zirconia. The present invention relates to a coloring solution for zirconia, comprising: a coloring agent (A) that is decolorized after firing of zirconia; and a metal ion solution (B), wherein, when zirconia is colored with the coloring solution and then subjected to firing, the color difference of the zirconia before and after the firing satisfies ?L*?5.8, ?a*?2.4, and ?b*?4.3.

Abstract: The present invention provides a dental product comprising a base material formed of a zirconia sintered body, and having high aesthetic quality with enhanced fracture toughness and with reduced chipping and cracking in the porcelain layer. The present invention also provides a method for manufacturing such a dental product. The present invention relates to a dental product comprising: a base material formed of a zirconia sintered body, and a porcelain layer, wherein the porcelain of the porcelain layer has a suitable firing temperature of 900° C. or more, and the porcelain layer has a fracture toughness value of 1.20 MPa·m0.5 or more.