Abstract: Disclosed is a film-shaped adhesive. An embodiment of the film-shaped adhesive contains metal particles and has a shear viscosity at 110° C. of 30000 Pa·s or less. Another embodiment of the film-shaped adhesive contains metal particles and has a loss modulus at 110° C. of 200 kPa or less. Another embodiment of the film-shaped adhesive contains metal particles, a thermosetting resin, a curing agent, and an elastomer, in which a content of the metal particles based on the total amount of the metal particles, thermosetting resin, curing agent, and elastomer is 70.0% by mass or more, and a total content of the thermosetting resin and the curing agent is 13.0% by mass or more.

Abstract: The present disclosure provides a semiconductor device. The semiconductor device includes a semiconductor chip; a support member having the semiconductor chip mounted thereon; and a bonding adhesive member provided between the semiconductor chip and the support member and adhering the semiconductor chip and the support member. The bonding adhesive member includes a sintered body of silver particles.

Abstract: A two-part curable urethane-based composition comprising a main agent (A); and a curing agent (B), wherein the main agent (A) contains a urethane prepolymer (a), an isocyanurate modified product of a polyisocyanate compound (b), and a silane coupling agent (c) in a specified ratio, the curing agent (B) contains a polyol (d) having a hydroxyl value of 50 to 500 mgKOH/g and an amine catalyst (e) in a specified amount, a mixing mass ratio of the main agent (A) to the curing agent (B) is 3:1 to 10:1, and an equivalent ratio of NCO group/OH group in the main agent (A) and the curing agent (B), respectively, is 1.0 to 5.0.

Abstract: A two-part curable urethane composition comprising a main agent (A) and a curing agent (B), wherein the main agent (A) contains a urethane prepolymer (a), an isocyanurate-modified polyisocyanate compound (b), and a silane coupling agent (c) at a specified ratio by mass; and the curing agent (B) contains a polyether polyol (d), a polyether polyol having 4 or more hydroxy groups (e), and an amine catalyst (f) at a specified ratio by mass.

Abstract: A two-part curable urethane-based composition comprising a main agent (A); and a curing agent (B), wherein the main agent (A) contains a urethane prepolymer (a), an isocyanurate modified product of a polyisocyanate compound (b), and a silane coupling agent (c) in a specified ratio, the curing agent (B) contains a polyol (d) having a hydroxyl value of 50 to 500 mgKOH/g and an amine catalyst (e) in a specified amount, a mixing mass ratio of the main agent (A) to the curing agent (B) is 3:1 to 10:1, and an equivalent ratio of NCO group/OH group in the main agent (A) and the curing agent (B), respectively, is 1.0 to 5.0.

Abstract: A two-part curable urethane composition comprising a main agent (A) containing a urethane prepolymer (a), and a curing agent (B) containing a polyether polyol (b) having a weight average molecular weight of 8000 or more and an amine catalyst (c), wherein the urethane prepolymer (a) is a reaction product of a polyether polyol (a-1) having a weight average molecular weight of 8000 or more and a diisocyanate (a-2), at least one of the main agent (A) and the curing agent (B) contains a carbon black (d) at a specified ratio by mass, and at least one of the main agent (A) and the curing agent (B) contains a silane coupling agent (e) at a specified ratio by mass.

Abstract: A two-part curable urethane composition comprising a main agent (A) and a curing agent (B), wherein the main agent (A) contains a urethane prepolymer (a), an isocyanurate-modified polyisocyanate compound (b), and a silane coupling agent (c) at a specified ratio by mass; and the curing agent (B) contains a polyether polyol (d), a polyether polyol having 4 or more hydroxy groups (e), and an amine catalyst (f) at a specified ratio by mass.