Abstract: The present invention relates to a process for preparing zeolite crystals continuously, comprising the continuous introduction of a composition capable of generating zeolite crystals into at least one crystallization reaction zone subjected to stirring means, giving said composition a flow characterized by a relative Reynolds number Rer of between 40 and 50 000, and the continuous recovery of the crystals formed according to a flow characterized by a net Reynolds number Ren of between 1 and 1500.

Abstract: The present invention relates to process for synthesizing zeolite X crystals comprising at least one step of adding seeding agent(s) into a synthesis gel and at least one step of forming zeolite X crystals at a temperature strictly greater than 120° C., preferably equal to or greater than 130° C.

Abstract: The present invention relates to process for synthesizing zeolite X crystals comprising at least one step of adding seeding agent(s) into a synthesis gel and at least one step of forming zeolite X crystals at a temperature strictly greater than 120° C., preferably equal to or greater than 130° C.

Abstract: The present invention relates to a process for preparing zeolite crystals continuously, comprising the continuous introduction of a composition capable of generating zeolite crystals into at least one crystallization reaction zone subjected to stirring means, giving said composition a flow characterized by a relative Reynolds number Rer of between 40 and 50 000, and the continuous recovery of the crystals formed according to a flow characterized by a net Reynolds number Ren of between 1 and 1500.

Abstract: A method for preparing a paste-like composition including carbon-based conductive fillers, at least one polymeric binder, at least one solvent, and at least one polymeric dispersant being different from the binder. Also, the paste that can result from said method, and to the uses thereof, in pure or diluted form, in particular for the manufacture of Li-ion batteries and super-capacitors.

Abstract: A masterbatch in agglomerated solid form including carbon nanofibers and/or nanotubes and/or carbon black, the content of which is between 15 wt % and 40 wt %, preferably between 20 wt % and 35 wt %, relative to the total weight of the masterbatch; at least one solvent; at least one polymer binder, which represents from 1 wt % to 40 wt %, preferably from 2 wt % to 30 wt % relative to the total weight of the masterbatch. Also, a concentrated masterbatch, characterized in that it is obtained by eliminating all or part of the solvent from the masterbatch described previously. Also, a process for preparing said masterbatches and to the uses of the latter, especially in the manufacture of an electrode or of a composite material for an electrode.

Abstract: The present invention relates to zeolite materials in the form of agglomerates comprising at least one mesoporous zeolite and having both the characteristics of mesoporous zeolites, the properties associated with microporosity and the mechanical properties of zeolite agglomerates without mesoporous zeolite. The invention also relates to the process for preparing the said zeolite materials in the form of agglomerates.

Abstract: The present invention relates to zeolite materials in the form of agglomerates comprising at least one mesoporous zeolite and having both the characteristics of mesoporous zeolites, the properties associated with microporosity and the mechanical properties of zeolite agglomerates without mesoporous zeolite. The invention also relates to the process for preparing the said zeolite materials in the form of agglomerates.

Abstract: A method for preparing a paste-like composition including carbon-based conductive fillers, at least one polymeric binder, at least one solvent, and at least one polymeric dispersant being different from the binder. Also, the paste that can result from said method, and to the uses thereof, in pure or diluted form, in particular for the manufacture of Li-ion batteries and supercapacitors.

Abstract: The present invention relates to a masterbatch in agglomerated solid form comprising: a) carbon nanofibers and/or nanotubes and/or carbon black, the content of which is between 15 wt % and 40 wt %, preferably between 20 wt % and 35 wt %, relative to the total weight of the masterbatch; b) at least one solvent; c) at least one polymer binder, which represents from 1 wt % to 40 wt %, preferably from 2 wt % to 30 wt % relative to the total weight of the masterbatch. The present invention also relates to a concentrated masterbatch, characterized in that it is obtained by eliminating all or part of the solvent from the masterbatch described previously. It also relates to a process for preparing said masterbatches and to the uses of the latter, especially in the manufacture of an electrode or of a composite material for an electrode.