Abstract: The present invention relates to a process for the production of polyethylene terephthalate copolyester from terephthalic acid, isophthalic acid and ethylene glycol, comprising the steps of: a) preparing a catalyst composition comprising a zinc compound being present such that the elemental zinc content is in a range of about 50 to about 500 ppm, preferably about 200 to about 500 ppm, most preferably about 180 to about 260 ppm, based on the copolyester, b) placing the catalyst composition, terephthalic acid, isophthalic acid and ethylene glycol in a vessel, and c) reacting the terephthalic acid, isophthalic acid and ethylene glycol in an esterification step and a polycondensation step to obtain polyethylene terephthalate copolyester; to the copolyester obtained thereby and its use, as well as to a catalyst composition suitable in the inventive process.

Abstract: The present invention relates to a catalyst composition for producing polyethylene terephthalate from terephthalic acid and ethylene glycol, comprising: (i) an antimony compound, being present such that the elemental antimony is in a range of about 15 ppm to less than 150 ppm; (ii) a zinc compound, being present such that the elemental zinc is in a range of about 40 to about 160 ppm; as well as a process for the preparation thereof.

Abstract: The present invention relates to an orientated polyolefin composition comprising an olefin (co)polymer having a weight average molecular weight (Mw) from 30,000 to 1,000,000 and a high molecular weight tail extending to molecular weights above 1,000,000, and has a microstructure which is substantially parallel chain extended cores of the component polymer(s) and associated lamellar overgrowths extending in planes normal to the cores. The lamellar overgrowths an adjacent cores intermesh and are capable of sustaining a haul off tension of at least 10 MPa without breaking during its extrusion.The orientated polyolefin composition is produced by extruding an olefin copolymer through a die under a pressure of about 5-10 MPa, at a temperature above the self-blocking temperature thereof and by hauling off the extrudate at a tension of at least 10 MPa without breaking. The extrudates so produced have a high modulus.

Abstract: An orientated polyolefin composition comprising an olefin (co)polymer having a weight average molecular weight (Mw) from 30,000 to 1,000,000 and a high molecular weight tail extending to molelcular weights above 1,000,000, and has a microstructure which is substantially parallel chain extended cores of the component polymer(s) and associated lamellar overgrowths extending in planes normal to the cores in which the lamellar overgrowths on adjacent cores intermesh and are capable of sustaining a haul off tension of at least 10 MPa without breaking during its extrusion, is produced by extruding an olefin copolymer through a die under a pressure of about 5-10 MPa, at a temperature above the self-blocking temperature thereof and by hauling off the extrudate at a tension of at least 10 MPa without breaking. The extrudates so produced have a high modulus.