Abstract: Disclosed are a liquid colored oil and a colored polyamide fiber. The liquid colored oil contains a colorant and a base oil agent. The base oil agent is a liquid at normal temperature and normal pressure, and a solubility parameter (SP) value thereof is 7.5 to 15.0. The colored polyamide fiber contains the aforementioned liquid colored oil. The liquid color oil can be stably added into polymers and dye them during the spinning process. The colored polyamide fiber has excellent spinning and dyeing properties.

Abstract: The present invention discloses a fabrication method and use of a ?40 mm large-size and high-contrast fiber optic image inverter, belonging to the field of manufacturing of fiber optic imaging elements. The light-absorbing glass for preparing the ?40 mm large-size and high-contrast fiber optic image inverter consists of the following components in molar percentage: SiO2 60-69.9, Al2O3 1.0-10.0, B2O3 10.1-15.0, Na2O 1.0-8.0, K2O 3.0-10.0, MgO 0.1-1.0, CaO 0.5-5.0, ZnO 0-0.1, TiO2 0-0.1, ZrO2 0.1-1.0, Fe2O3 3.0-6.5, Co2O3 0.1-0.5, V2O5 0.51-1.5 and MoO3 0.1-1.0. The fiber optic image inverter has the advantages of low crosstalk of stray light, high resolution and high contrast.

Abstract: The present invention discloses a glass with high refractive index for fiber optic imaging elements with medium-expansion and fabrication method therefor, the glass comprising the following components in percentage by weight: SiO2 5-9%, Al2O3 0-1%, B2O3 23-28%, CaO 0-3%, BaO 6-12%, La2O3 30-34%, Nb2O5 4-8%, Ta2O5 0-1%, Y2O3 0-1%, ZnO 4-9%, TiO2 4-8%, ZrO2 4-6%, SnO2 0-1%. The present invention further provides a fabrication method for the glass with a high refractive index, comprising: putting raw materials quartz sand, aluminum hydroxide, boric acid or boric anhydride, calcium carbonate, barium carbonate or barium nitrate, lanthanum oxide, niobium oxide, tantalum oxide, yttrium oxide, zinc oxide, titanium dioxide, zirconium oxide and stannic oxide, etc. into a platinum crucible according to the requirement of dosing, melting at a high temperature, cooling and fining, leaking and casting to form a glass rod, and then annealing, cooling and chilling the molded glass rod.

Abstract: A method for determining the usage amount of detergent, and a dishwasher, a processor, a storage medium and a computer program product. The method for determining the usage amount of detergent includes acquiring an internal image of a dishwasher captured by an image acquisition device; according to the internal image, determining whether there is a target object in the dishwasher; when it is determined that there is a target object, generating a position table of the target object; determining the dirtiness of the target object according to the position table; and determining the usage amount of detergent for the dishwasher according to the dirtiness. The dirtiness of a target object needing to be cleaned in a dishwasher is determined by means of an image acquisition device, and the usage amount of detergent for the dishwasher is then determined according to the dirtiness.

Abstract: A cleaning method and cleaning apparatus for a dishwasher, and a dishwasher. The cleaning method for a dishwasher includes acquiring a first image of tableware in a dishwasher, identifying the type of dirt on the tableware according to the first image, determining a corresponding washing mode according to the type of dirt, controlling the dishwasher to successively clean the tableware according to the washing mode, each time after the cleaning is completed, acquiring a second image of the tableware in the dishwasher, and comparing the first image with the second image, to determine the effectiveness of the washing mode. In this way, the problem in the prior art of it being impossible to accurately identify the type of dirt can be solved, and an appropriate washing mode is matched for the current type of dirt, to realize thorough cleaning, and less time is consumed, the efficiency is high, and less water energy and electric energy are used.

Abstract: A fiber optic imaging element includes medium-expansion and a fabrication method including: (1) matching a core glass rod with a cladding glass tube to perform mono fiber drawing; (2) arranging the mono fibers into a mono fiber bundle rod, and then drawing the mono fiber bundle rod into a multi fiber; (3) arranging the multi fiber into a multi fiber bundle rod, and then drawing the multi fiber bundle rod into a multi-multi fiber; (4) cutting the multi-multi fiber, and then arranging the multi-multi fiber into a fiber assembly buddle, then putting the fiber assembly buddle into a mold of heat press fusion process, and performing the heat press fusion process to prepare a block of the fiber optic imaging element with medium-expansion; and (5) edged rounding, cutting and slicing, face grinding and polishing the prepared medium-expansion block into a billet.

Abstract: The present invention discloses a glass with high refractive index for fiber optic imaging elements with medium-expansion and fabrication method therefor, the glass comprising the following components in percentage by weight: SiO2 5-9%, Al2O3 0-1%, B2O3 23-28%, CaO 0-3%, BaO 6-12%, La2O3 30-34%, Nb2O5 4-8%, Ta2O5 0-1%, Y2O3 0-1%, ZnO 4-9%, TiO2 4-8%, ZrO2 4-6%, SnO2 0-1%. The present invention further provides a fabrication method for the glass with a high refractive index, comprising: putting raw materials quartz sand, aluminum hydroxide, boric acid or boric anhydride, calcium carbonate, barium carbonate or barium nitrate, lanthanum oxide, niobium oxide, tantalum oxide, yttrium oxide, zinc oxide, titanium dioxide, zirconium oxide and stannic oxide, etc. into a platinum crucible according to the requirement of dosing, melting at a high temperature, cooling and fining, leaking and casting to form a glass rod, and then annealing, cooling and chilling the molded glass rod.

Abstract: A fiber optic imaging element includes medium-expansion and a fabrication method including: (1) matching a core glass rod with a cladding glass tube to perform mono fiber drawing; (2) arranging the mono fibers into a mono fiber bundle rod, and then drawing the mono fiber bundle rod into a multi fiber; (3) arranging the multi fiber into a multi fiber bundle rod, and then drawing the multi fiber bundle rod into a multi-multi fiber; (4) cutting the multi-multi fiber, and then arranging the multi-multi fiber into a fiber assembly buddle, then putting the fiber assembly buddle into a mold of heat press fusion process, and performing the heat press fusion process to prepare a block of the fiber optic imaging element with medium-expansion; and (5) edged rounding, cutting and slicing,