Abstract: The present invention relates to a biodegradable polyester and use thereof, including components: A) acid components containing following repeating units: 50 to 58 mol % of terephthalic acid A1; 30 to 40 mol % of sebacic acid A2; and 2 to 20 mol % of an aliphatic dibasic acid A3 with a carbon chain length of 6 or less; B) butanediol. In the present invention, in the case of a high content of the terephthalic acid, the biodegradable polyester prepared by introducing an aliphatic dibasic acid unit having a carbon chain length of 6 or less can satisfy the degradation performance and rigidity and improve the tenacity of the material simultaneously.

Abstract: A biodegradable polyester and use thereof includes components: A) acid components containing following repeating units: 40 to 48 mol % of terephthalic acid A1; 38.5 to 50 mol % of sebacic acid A2; and 2 to 20 mol % of an aliphatic dibasic acid A3 with a carbon chain length of 6 or less; B) butanediol. In the case of low content of the terephthalic acid unit, by introducing the aliphatic dibasic acid unit with the carbon chain length of 6 or less, mechanical properties of the material can be significantly improved, and the mechanical property retention is better especially when stored in a humid environment.

Abstract: A biodegradable polyester and use thereof includes components: A) acid components containing following repeating units: 40 to 48 mol % of terephthalic acid A1; 38.5 to 50 mol % of sebacic acid A2; and 2 to 20 mol % of an aliphatic dibasic acid A3 with a carbon chain length of 6 or less; B) butanediol. In the case of low content of the terephthalic acid unit, by introducing the aliphatic dibasic acid unit with the carbon chain length of 6 or less, mechanical properties of the material can be significantly improved, and the mechanical property retention is better especially when stored in a humid environment.

Abstract: The present invention relates to a biodegradable polyester and use thereof, including components: A) acid components containing following repeating units: 50 to 58 mol % of terephthalic acid A1; 30 to 40 mol % of sebacic acid A2; and 2 to 20 mol % of an aliphatic dibasic acid A3 with a carbon chain length of 6 or less; B) butanediol. In the present invention, in the case of a high content of the terephthalic acid, the biodegradable polyester prepared by introducing an aliphatic dibasic acid unit having a carbon chain length of 6 or less can satisfy the degradation performance and rigidity and improve the tenacity of the material simultaneously.

Abstract: The present invention discloses a poly(terephthalate-co-sebacate) resin composition, comprising the following components: a. poly(terephthalate-co-sebacate); and b. an alkane, which is at least one selected from the group consisting of hexadecane, heptadecane, octadecane, nonadecane and eicosane; wherein a weight content of the alkane is 5 ppm-1000 ppm based on a total weight of the poly(terephthalate-co-sebacate) resin composition. The present invention controls the content of alkane in the composition within a range of 5 ppm-1000 ppm by adding an alkane, which not only enables the poly(terephthalate-co-sebacate) resin to have obviously improved blow molding properties, a film thickness range of less than 0.3 ?m, and a relative deviation of film thickness of less than 2.

Abstract: The present invention discloses a PBS resin composition and a preparation method thereof. The composition comprises: a. PBS resin; b. element titanium; c. element phosphorus, wherein a weight ratio range of titanium to phosphorus is 0.6-10:1, preferably 0.7-4:1, and more preferably 1.25-1.5:1. A weight content of the element titanium is 20-200 ppm, and a weight content of the element phosphorus is 15-70 ppm. By adding a titanium-containing compound and a phosphorus-containing compound and controlling the range of the weight ratio of the element titanium to the element phosphorus in the PBS resin composition to be 0.6-10:1, the present invention obtains a PBS resin composition. After treating in a 95° C.-distilled water bath for 12 hours and drying at 90° C. for 3 hours, a change of the melt flow index of the PBS resin composition is less than 50.0 g/10 min, and the PBS resin composition possesses an obviously improved hydrolysis property.

Abstract: The present invention discloses a PBAT resin composition comprising following components: (a) poly(butyleneadipate-co-terephthalate); (b) iron element; wherein, based on a total weight of the PBAT resin composition, a weight content of the iron element is 1 ppm-500 ppm. By adding iron-containing compounds into the composition and controlling the content of the iron element in a range of 1 ppm-500 ppm in the composition, a speed of reaction of aromatic structure in the PBAT resin under a hot and humid condition can be postponed, so that after the prepared PBAT resin composition is aged in boiling water for 24 hours and 48 hours, a variation of b-value is less than 2. The PBAT resin composition has obviously improved color stability in resistance to boiling water aging.

Abstract: The present invention discloses a PBS resin composition and a preparation method thereof. The composition comprises: a. PBS resin; b. element titanium; c. element phosphorus, wherein a weight ratio range of titanium to phosphorus is 0.6-10:1, preferably 0.7-4:1, and more preferably 1.25-1.5:1. A weight content of the element titanium is 20-200 ppm, and a weight content of the element phosphorus is 15-70 ppm. By adding a titanium-containing compound and a phosphorus-containing compound and controlling the range of the weight ratio of the element titanium to the element phosphorus in the PBS resin composition to be 0.6-10:1, the present invention obtains a PBS resin composition. After treating in a 95° C.-distilled water bath for 12 hours and drying at 90° C. for 3 hours, a change of the melt flow index of the PBS resin composition is less than 50.0 g/10 min, and the PBS resin composition possesses an obviously improved hydrolysis property.

Abstract: The present invention discloses a poly(terephthalate-co-sebacate) resin composition, comprising the following components: a. poly(terephthalate-co-sebacate); and b. an alkane, which is at least one selected from the group consisting of hexadecane, heptadecane, octadecane, nonadecane and eicosane; wherein a weight content of the alkane is 5 ppm-1000 ppm based on a total weight of the poly(terephthalate-co-sebacate) resin composition. The present invention controls the content of alkane in the composition within a range of 5 ppm-1000 ppm by adding an alkane, which not only enables the poly(terephthalate-co-sebacate) resin to have obviously improved blow molding properties, a film thickness range of less than 0.3 ?m, and a relative deviation of film thickness of less than 2.

Abstract: The present invention discloses a PBAT resin composition comprising following components: (a) poly(butyleneadipate-co-terephthalate); (b) iron element; wherein, based on a total weight of the PBAT resin composition, a weight content of the iron element is 1 ppm-500 ppm. By adding iron-containing compounds into the composition and controlling the content of the iron element in a range of 1 ppm-500 ppm in the composition, a speed of reaction of aromatic structure in the PBAT resin under a hot and humid condition can be postponed, so that after the prepared PBAT resin composition is aged in boiling water for 24 hours and 48 hours, a variation of b-value is less than 2. The PBAT resin composition has obviously improved color stability in resistance to boiling water aging.