Abstract: The invention relates to a chain guide, respectively a chain tensioner for use in a lubricated sliding system, comprising a surface layer or bearing or comprising a sliding element comprising a surface layer, the surface layer being mainly made of a polymeric material containing a matrix polymer and optionally other components dispersed in said matrix polymer, wherein the matrix polymer consists of a semi-crystalline polyamide (SCPA) having a tensile modulus at 140° C. of at least 800 MPa (measured by the method according to ISO 527-1A). The invention also relates to a power train drive system comprising an engine, a transmission differential and a drive shaft system, a drive chain and a plastic component comprising a sliding element in contact with the lubricated drive chain, wherein the chain guide, the chain tensioner, respectively the sliding element has a coefficient of friction (CoF), measured in lubrication oil at 140° C. at a nominal contact pressure of 1 MPa and a speed of 1 m/s, of at most 0.07.

Abstract: The present invention relates to a polymer composition, consisting of (A) 30-90 wt. % of at least one thermoplastic polymer comprising at least a semi-crystalline semi-aromatic polyamide (SSPA-1) in an amount in the range of 30-90 wt. %; (B) 10-70 wt. % of at least one reinforcing agent, and (C) 0-25 wt. % of one or more other components; wherein the SSPA-1 consists of (A-1-a) 90-100 wt. % of repeat units derived from (i) an aromatic dicarboxylic acid and (ii) diamines, and (A-1-b) 0-10 wt. % of repeat units derived from other monomers; the diamines (ii) consist of 80-95 mole % of a linear aliphatic diamine, 5-20 mole % of 2-methyl-pentamethylene diamine, and 0-10 mole % of other diamines; and the SSPA-1 has a melting temperature (Tm) of at least 300° C. The invention further relates to a molded part made of the composition, a process for making the composition and a process for making the molded part.

Abstract: Thermoplastic compositions are disclosed which include: a) a polyamide component comprising at least three amide monomer units and b) a stabilizer, wherein at least one of the at least three amide monomer units is an aliphatic amide monomer unit having a carbon to nitrogen ratio (C/N) equal to, or above 6.5, in that at least two of the at least three amide monomer units are semi-aromatic amide monomer units which polymerized provide at least one semi-crystalline semi-aromatic polyamide having a melting temperature of at least 290° C. as measured by DSC at a heating rate of 10° C./min according to standard ISO 11357-3 (2009), and in that the amount of aliphatic amide monomer unit is in the range from 20 to 60 wt. % relative to the total weight of the at least three amide monomer units in the polyamide components and the total amount of semi-aromatic amide monomer units is in the range from 40 to 80 wt.

Abstract: The present invention relates to a thermoplastic composition comprising: a) a polyamide component comprising at least three amide monomer units and b) a stabilizer characterized in that at least one of the at least three amide monomer units is an aliphatic amide monomer unit having a carbon to nitrogen ratio (C/N) equal to, or above 6.5, in that at least two of the at least three amide monomer units are semi-aromatic amide monomer units which polymerized provide at least one semi-crystalline semi-aromatic polyamide having a melting temperature of at least 290° C. as measured by DSC at a heating rate of 10° C./min according to standard ISO 1 1357-3 (2009), and in that the amount of aliphatic amide monomer unit is in the range from 20 to 60 wt. % relative to the total weight of the at least three amide monomer units in the polyamide components and the total amount of semi-aromatic amide monomer units is in the range from 40 to 80 wt.

Abstract: The present invention relates to a polymer composition, consisting of (A) polymer comprising at least (A-1) a first semi-crystalline semi-aromatic polyamide (SSPA); and (A-2) a functionalized polymer; (B) 5-69 wt. % of reinforcing agent; and (C) 0-25 wt. % of one or more other components; wherein the SSPA is present in an amount in the range of 30-90 wt. %; has a melting temperature (Tm) of at least 300° C., measured by DSC according to ISO-11357-1/3, 2011 with heating and cooling rate of 10° C./min; and consists of: (A-1-a) 90-100 mole % of repeat units derived from (i) aromatic dicarboxylic acid and (ii) diamines, and (A-1-b) 0-10 mole % of repeat units derived from other monomers; and the diamines (ii) consist of 80-95 mole % of linear aliphatic diamine, 5-20 mole % of 2-methyl-pentamethylene diamine, and 0-10 mole % of other diamines; wherein the functionalized polymer (A-2) comprises a functionalized semi-crystalline polyolefin in an amount of 1-15 wt. %; and wherein the weight percentages (wt.

Abstract: The present invention relates to a polymer composition, consisting of (A) 30-90 wt. % of at least one thermoplastic polymer comprising at least a semi-crystalline semi-aromatic polyamide (SSPA-1) in an amount in the range of 30-90 wt. %; (B) 10-70 wt. % of at least one reinforcing agent, and (C) 0-25 wt. % of one or more other components; wherein the SSPA-1 consists of (A-1-a) 90-100 wt. % of repeat units derived from (i) an aromatic dicarboxylic acid and (ii) diamines, and (A-1-b) 0-10 wt. % of repeat units derived from other monomers; the diamines (ii) consist of 80-95 mole % of a linear aliphatic diamine, 5-20 mole % of 2-methyl-pentamethylene diamine, and 0-10 mole % of other diamines; and the SSPA-1 has a melting temperature (Tm) of at least 300° C. The invention further relates to a molded part made of the composition, a process for making the composition and a process for making the molded part.

Abstract: The invention relates to a chain guide, respectively a chain tensioner for use in a lubricated sliding system, comprising a surface layer or bearing or comprising a sliding element comprising a surface layer, the surface layer being mainly made of a polymeric material containing a matrix polymer and optionally other components dispersed in said matrix polymer, wherein the matrix polymer consists of a semi-crystalline polyamide (SCPA) having a tensile modulus at 140° C. of at least 800 MPa (measured by the method according to ISO 527-1A). The invention also relates to a power train drive system comprising an engine, a transmission differential and a drive shaft system, a drive chain and a plastic component comprising a sliding element in contact with the lubricated drive chain, wherein the chain guide, the chain tensioner, respectively the sliding element has a coefficient of friction (CoF), measured in lubrication oil at 140° C. at a nominal contact pressure of 1 MPa and a speed of 1 m/s, of at most 0.07.

Abstract: The invention relates to a chain guide, respectively a chain tensioner for use in a lubricated sliding system, comprising a surface layer or bearing or comprising a sliding element comprising a surface layer, the surface layer being mainly made of a polymeric material containing a matrix polymer and optionally other components dispersed in said matrix polymer, wherein the matrix polymer consists of a semi-crystalline polyamide (SCPA) having a tensile modulus at 140° C. of at least 800 MPa (measured by the method according to ISO 527-1A). The invention also relates to a power train drive system comprising an engine, a transmission differential and a drive shaft system, a drive chain and a plastic component comprising a sliding element in contact with the lubricated drive chain, wherein the chain guide, the chain tensioner, respectively the sliding element has a coefficient of friction (Co F), measured in lubrication oil at 140° C. at a nominal contact pressure of 1 MPa and a speed of 1 m/s, of at most 0.07.

Abstract: The present invention relates to a thermoplastic composition comprising: a) a polyamide component comprising at least three amide monomer units and b) a stabilizer characterized in that at least one of the at least three amide monomer units is an aliphatic amide monomer unit having a carbon to nitrogen ratio (C/N) equal to, or above 6.5, in that at least two of the at least three amide monomer units are semi-aromatic amide monomer units which polymerized provide at least one semi-crystalline semi-aromatic polyamide having a melting temperature of at least 290° C. as measured by DSC at a heating rate of 10° C./min according to standard ISO 1 1357-3 (2009), and in that the amount of aliphatic amide monomer unit is in the range from 20 to 60 wt. % relative to the total weight of the at least three amide monomer units in the polyamide components and the total amount of semi-aromatic amide monomer units is in the range from 40 to 80 wt.

Abstract: The invention relates to a high molecular weight branched polyamide polymer comprising (a) blocks predominantly consisting of AA-BB repeat units, (b) blocks predominantly consisting of AB repeat units, and (c) branching units. The invention also relates to a process for the preparation of the high molecular weight branched polyamide polymer, comprising (1) a melt-mixing step wherein an essentially linear polyamide prepolymer (X-1), predominantly consisting of AA-BB repeat units, an essentially linear polyamide (pre)polymer (X-2), predominantly consisting of AB repeat units, and a branching agent are provided to and mixed and heated in a melt mixing apparatus, thereby forming a mixed melt, and the mixed melt being cooled, thereby forming a solid mixture; and (2) a solid state post condensation step wherein the solid mixture is post-condensed at elevated temperature in the solid state, thereby forming a high molecular weight branched polyamide polymer.

Abstract: The invention relates to a branched polyamide prepolymer obtained or obtainable by polymerization of a polyamide forming monomer mixture, comprising AA-BB repeat units and branching units derived from diamines (monomer A) dicarboxylic acids (monomer B), and/or a salt of A and B, and a higher functional monomer (monomer C) present in a molar amounts defined by formula I and formula II: MC=(Q/FC)*(MA+MB) (Formula I) and R=((MA*2)+(MC*FCA))/((MB*2)+(MC*FCB)) (Formula II) wherein—MA, MB and MC represent the molar amounts of repeat units derived from the monomers A, B and C, respectively; —FC represent the functionality of monomer C, and is equal to FC-A+FC-B; —FC-A is the number of the amino functional groups comprised by monomer C; —FC-B is the number of carboxyl functional groups or precursor groups thereof comprised by monomer C; —Q is a number in the range of 0.06-1.00; and —R is a number in the range of 0.7-1.

Abstract: The invention relates a heat stabilized thermoplastic polymer composition comprising polyamide polymer and a heat stabilizer system, as well as moulded parts made thereof. The thermoplastic polymer composition comprises (A) a blend of at least two polyamide polymers comprising a first polyamide (a.1) being a semi-crystalline polyamide with a melting temperature of at least 240° C. and a second polyamide (a.2) being either polyamide 6 or a copolyamide of polyamide-6 and another polyamide, (B) a heat stabilizer system; and (C) a polyarylene sulfide polymer, wherein (A) and (C) are present in a weight ratio in the range of 90:10-20:80.

Abstract: The invention relates to a branched polyamide prepolymer obtained or obtainable by polymerization of a polyamide forming monomer mixture, comprising AA-BB repeat units and branching units derived from diamines (monomer A) dicarboxylic acids (monomer B), and/or a salt of A and B, and a higher functional monomer (monomer C) present in a molar amounts defined by formula I and formula II: MC=(Q/FC)*(MA+MB) (Formula I) and R=((MA*2)+(MC*FCA))/((MB*2)+(MC*FCB)) (Formula II) wherein—MA, MB and MC represent the molar amounts of repeat units derived from the monomers A, B and C, respectively;—FC represent the functionality of monomer C, and is equal to FC-A+FC-B;—FC-A is the number of the amino functional groups comprised by monomer C;—FC-B is the number of carboxyl functional groups or precursor groups thereof comprised by monomer C;—Q is a number in the range of 0.06-1.00; and—R is a number in the range of 0.7-1.

Abstract: The invention relates to a sliding element for use in a chain transmission apparatus, comprising a sliding contact section for engagement in sliding contact with a chain, wherein the sliding contact section consists of a plastic material comprising a matrix polymer and dispersed therein graphite platelets comprising platelet particles having a thickness of at most 250 nm. The invention relates to an engine comprising a first sliding element in sliding contact with a second element, wherein at least a sliding contact section is made of such a plastic material comprising such thin graphite platelets. The invention further relates to a chain transmission apparatus, comprising a chain, and a sliding element comprising (i) a sliding contact section engaged in sliding contact with the chain and (ii) a main body reinforcing and supporting the sliding contact section, wherein the sliding contact section consists of such a plastic material.

Abstract: The invention relates to a high molecular weight branched polyamide polymer comprising (a) blocks predominantly consisting of AA-BB repeat units, (b) blocks predominantly consisting of AB repeat units, and (c) branching units. The invention also relates to a process for the preparation of the high molecular weight branched polyamide polymer, comprising (1) a melt-mixing step wherein an essentially linear polyamide prepolymer (X-1), predominantly consisting of AA-BB repeat units, an essentially linear polyamide (pre)polymer (X-2), predominantly consisting of AB repeat units, and a branching agent are provided to and mixed and heated in a melt mixing apparatus, thereby forming a mixed melt, and the mixed melt being cooled, thereby forming a solid mixture; and (2) a solid state post condensation step wherein the solid mixture is post-condensed at elevated temperature in the solid state, thereby forming a high molecular weight branched polyamide polymer.

Abstract: The invention relates to a chain guide, respectively a chain tensioner for use in a lubricated sliding system, comprising a surface layer or bearing or comprising a sliding element comprising a surface layer, the surface layer being mainly made of a polymeric material containing a matrix polymer and optionally other components dispersed in said matrix polymer, wherein the matrix polymer consists of a semi-crystalline polyamide (SCPA) having a tensile modulus at 140° C. of at least 800 MPa (measured by the method according to ISO 527-1A). The invention also relates to a power train drive system comprising an engine, a transmission differential and a drive shaft system, a drive chain and a plastic component comprising a sliding element in contact with the lubricated drive chain, wherein the chain guide, the chain tensioner, respectively the sliding element has a coefficient of friction (Co F), measured in lubrication oil at 140° C. at a nominal contact pressure of 1 MPa and a speed of 1 m/s, of at most 0.07.