Abstract: The present invention provides magnesium or magnesium alloys having high formability at room temperature, the magnesium or magnesium alloys having a grain size ?2 microns. The present invention also provides a method for manufacturing the magnesium or magnesium alloys having high formability at room temperature. The magnesium or magnesium alloys having high formability at room temperature are prepared by simple processing means. The present invention overcomes a problem of poor formability at room temperature.

Abstract: A high strength and corrosion-resistant magnesium alloy material, comprising 0.01-1.2 wt % of Ge and 0.01-1.2 wt % of Zn. A high strength and corrosion-resistant magnesium alloy material, comprising the following chemical elements in percentage by weight: Ge: 0.01-1.2%; Zn: 0.01-1.2%; at least one of Mn, Ca, Zr, Sr, and Gd, with a total weight percentage of ?3%, wherein the percentage by weight of a single element is ?0.8%; and the balance of Mg and other inevitable impurities. A method for fabricating the above mentioned high strength and corrosion-resistant magnesium alloy material, comprising the steps of: smelting, solid solution heat treatment, and extrusion, wherein in the extrusion step, the extrusion temperature is 180-350° C., the extrusion rate is 0.1-10 mm/s, and the extrusion ratio is 10:1-30:1.

Abstract: The present invention provides magnesium or magnesium alloys having high formability at room temperature, the magnesium or magnesium alloys having a grain size ?2 microns. The present invention also provides a method for manufacturing the magnesium or magnesium alloys having high formability at room temperature. The magnesium or magnesium alloys having high formability at room temperature are prepared by simple processing means. The present invention overcomes a problem of poor formability at room temperature.

Abstract: A method of strengthening a dilute magnesium alloy sheet includes providing a dilute magnesium alloy sheet, which includes a magnesium alloy consisting essentially of (wt %): >0 to 3.0 of Zn; >0 to 1.5 of Ca; 0 to 1.0 of Zr; 0 to 1.3 of a rare earth element or mixture of the same; 0 to 0.3 of Sr; 0 to 0.7 of Al, the balance of Mg and other unavoidable impurities, wherein the total weight % of alloying elements is less than 3%; subjecting the dilute magnesium alloy sheet to plastic deformation, in which the tensile plastic strain should exceed 0.5%, but be less than 8% to form a pre-deformed magnesium alloy sheets; and subjecting the pre-deformed magnesium alloy sheets to an ageing treatment in a temperature range of 80 to 250° C. for at least 1 minute, thereby forming a strengthened magnesium alloy sheet.

Abstract: A method of strengthening a dilute magnesium alloy sheet includes providing a dilute magnesium alloy sheet, which includes a magnesium alloy consisting essentially of (wt %): >0 to 3.0 of Zn; >0 to 1.5 of Ca; 0 to 1.0 of Zr; 0 to 1.3 of a rare earth element or mixture of the same; 0 to 0.3 of Sr; 0 to 0.7 of Al, the balance of Mg and other unavoidable impurities, wherein the total weight % of alloying elements is less than 3%; subjecting the dilute magnesium alloy sheet to plastic deformation, in which the tensile plastic strain should exceed 0.5%, but be less than 8% to form a pre-deformed magnesium alloy sheets; and subjecting the pre-deformed magnesium alloy sheets to an ageing treatment in a temperature range of 80 to 250° C. for at least 1 minute, thereby forming a strengthened magnesium alloy sheet.

Abstract: Formable magnesium based wrought alloys include a magnesium based wrought alloy consisting essentially of (wt %): 0.1 to 2.0 of Zn; 0.05 to 1.5 of Ca; 0.1 to 1.0 of Zr; 0 to 1.3 of a rare earth element or mixture of the same of which includes Gd or Y; 0 to 0.3 of Sr, Al: 0 to 0.7; the balance of Mg and other unavoidable impurities.