Process for preparing antimicrobial plastic bodies having improved long-time performance

Abstract

The present invention relates to processes for preparing an antimicrobial plastic body, said processes comprising molding a precursor and being characterized in that prior to molding at least one component of the precursor is treated with a metal colloid.

Description

[0001] The invention relates to processes for preparing antimicrobial metal-containing plastic bodies, in particular articles for medical requirements. These articles are in particular used in the form of catheters.

[0002] A considerable disadvantage of plastic articles for medical requirements, in particular of catheters for long-term and short-term use, is that the plastics used are easily infected by germs which are often multi-resistant and form a biofilm on the surface of the plastic body or on the outer and interior surface of the catheter. Prophylactic impregnation of the surfaces by means of antibiotics has to be ruled out due to the high selection of resistant microorganisms involved.

[0003] Thus, in the past years numerous attempts have been made to impregnate the plastic surfaces with silver ions originating from, e.g., silver nitrate, acetate or chloride. Among all heavy metal ions, silver ions have a very broad antimicrobial spectrum and high toxicity towards microorganisms in that they, e.g., bind to the cell wall via SH groups, block the respiratory chain, stop cell proliferation via DNA binding, but have low toxicity towards animal cells. In this context, however, sufficient microbial activity could not be observed in various clinical studies. Moreover, the etching effect and the poor water solubility, respectively, of silver salts cause further problems in use.

[0004] When metal surfaces such as silver are contacted with physiological NaCl solution, metal ions (silver ions) will be released depending on the size of the metal surface. Admixing a polymer such as polyurethane with a metal powder such as silver powder, however, will not be successful since due to the small surface area relatively high concentrations of metal powder will be necessary, which causes mechanical problems in the plastic material. The critical surface area required for antimicrobial activity, thus, cannot be obtained by admixing metal powder.

[0005] EP-A-0 711 113 discloses a new technology in which metallic silver is vapor deposited on polyurethane films which are compounded in comminuted form. This made it possible to achieve uniform distribution of silver particles in polymer material and, thus, obtain a surface area sufficiently large for bacteriostatic activity. The antimicrobial activity of said plastic bodies has been very well established as regards reduction and prevention of adherence, biofilm formation and long-time performance as well as toxicity and compatibility. The applicability of the aforesaid plastic bodies is, however, limited due to the time-consuming and costly preparation process, in particular caused by the vapor deposition of silver.

[0006] U.S. Pat. No. 5,180,585 furthermore describes an antimicrobial composition comprising inorganic particles having a first microbicidal layer and a second layer which protects the underlying first layer. The preparation process is relatively complex.

[0007] Thus, the object underlying the present invention is to provide a process for preparing antimicrobially active plastic bodies which do not exhibit the aforesaid disadvantages, i.e. can easily be prepared and provide sufficient concentration of silver ions at the surface.

[0008] This problem is solved by means of a process which is characterized in that prior to molding the plastic body at least one component of the precursor of the molded article is treated with a silver colloid.

[0009] Many polymer compounds commonly used in the medical field can be used as the starting material for the plastic body. Among these are in particular polyethylene, polypropylene, crosslinked polysiloxanes, polyurethanes, (meth)acrylate-based polymers, cellulose and cellulose derivatives, polycarbonates, ABS, tetrafluoroethylene polymers, and polyethylene terephthalates as well as the corresponding copolymers. Polyurethane, polyethylene and polypropylene as well as polyethylene-polypropylene copolymers are particularly preferred. The metal used is preferably silver, copper, gold, zinc or cerium. Among these metals, silver is particularly preferred.

[0010] Apart from colloidal metal, one or several polymer materials are used in the preparation of the plastic bodies according to the invention. Further additives can also be added to the mixture of colloidal metal and plastic(s). These are, in particular, inorganic particles such as barium sulfate, calcium sulfate, strontium sulfate, titanium oxide, aluminium oxide, silicon oxide, zeolites, mica, talcum, kaolin etc. In this context, barium sulfate which can simultaneously act as a X-ray contrast medium for specific fields of application is particularly preferred.

[0011] Prior to molding, one or several polymer components and/or one or several of the inorganic additives are treated with the colloidal metal solution.

[0012] After mixing of the starting materials which have (in part) been treated with a colloidal metal, the resulting mixture is further processed in order to obtain a molded plastic article. This can be done in mixers, kneaders, extruders, injection molding machines or (hot) presses.

[0013] The metal colloids with which the plastic materials or inorganic particles are treated are suitably prepared by reducing metal salt solutions. In order to stabilize the resulting colloid, protective agents such as gelatin, silica or starch may be used.

[0014] In one embodiment of the present invention, a preferred metal silver colloid is prepared by slowly blending an ammoniacal silver nitrate solution in gelatin with a suitable reducing agent. The reducing agent preferably is selected from aldehydes (e.g. acetaldehyde), aldoses (e.g. glucose), quinones (e.g. hydroquinone), inorganic complex hydrides (sodium or potassium boranate), reducing nitrogen compounds (hydrazine, polyethylene imine) and ascorbic acid.

[0015] Plastic precursors such as pellets and/or said inorganic particles such as barium sulfate are then treated with said colloidal silver solution, dried and molded into the respective shape. Applying said silver colloid onto the starting materials and subsequent drying can be repeated several times so that in this way very high silver concentrations can be introduced into the plastic material. This is of particular advantage if barium sulfate is coated with silver since in this way the plastic pellets do not necessarily have to be coated in advance.

[0016] The suspension can also be freed from solvent by filtration and it can subsequently be freed from all low-molecular organic compounds by first washing it with about 5% ammonia solution and then several times with distilled water. As described above, after drying in air the filter residue will give a homogeneous material. This process can also be repeated several times.

[0017] The use of e.g. gelatin, (fumed) silica or starch as a colloidal stabilizer can be omitted if silver is adsorbed by the inorganic particles, since the microcrystalline silver particles produced during reduction bind to the surface of said inorganic particles via adsorption and, thus, the formation of a continuous silver coating on the solid is avoided. Water soluble adjuvant chemicals used can be removed with water.

[0018] By varying or omitting the colloidal stabilizers as well as the reducing agents, the particle size of the silver and, thus, the mobility of the resulting silver ions can be controlled over a wide range and, moreover, by using low-molecular aldehydes as the reducing agents which partially crosslink gelatin, very strong adhesion to the polymer can be achieved.

[0019] In the following, the process according to the invention will be exemplified by way of examples.

EXAMPLE 1

Preparation of the Silver Colloid

[0020] 1.0 g gelatin (DAB) are dissolved in 100 ml distilled water at 40° C. whilst stirring. Subsequently, 1.0 g (5.88 mmol) AgNO3 p.a. are added thereto and the resulting solution is blended with 1.0 ml (14.71 mmol) water containing 25% NH3.

[0021] For the preparation of the silver colloid, 258.7 mg (5.88 mmol, 330 &mgr;l ) acetaldehyde, dissolved in 50 ml distilled water, are slowly dripped into the above solution at 40° C. over a period of time of 30 min.

EXAMPLE 2

Coating of Polyurethane Pellets

[0022] 10 min after the dripping according to Example 1 has been stopped, about 50 mg polyurethane pellets made of Tecothane TT-1085A are added and first vigorously stirred for 2 h at 40° C. and then for 3 h at room temperature so that they are coated with colloidal silver.

[0023] The silver colloid is separated by rapid filtration over a folded filter of a suitable pore size, the pellets are once again washed with the filtrate and the still wet pellets are transferred into a evaporating dish. After superfluous silver colloid solution which does not adhere to the polymer has been removed, the resulting product is dried for 10 h at 70° C.

EXAMPLE 3

Adsorption of Colloidal Silver on Barium Sulfate

[0024] a) 0.666 g gelatin and then 6.66 g AgNO3 are subsequently dissolved in 500 ml distilled water at 50° C. About 8.5 ml 25% aqueous NH3 solution are added until the reaction is slightly alkaline.

[0025] A solution of 3.53 g anhydrous &agr;-D-glucose in 150 ml distilled water is slowly dripped in at 50° C. whilst stirring vigorously and as soon as about half of the glucose solution has been dripped in, the resultant silver colloid is blended with 333 g BaSO4. After the dripping has been stopped, the suspension is further turbinated for about 2 h at 50° C. and then freed from its volatile components by evaporation and drying at 70° C. The material is comminuted in a hand-held mortar.

[0026] b) The procedure is analogous to Example 3a), with the exception that 6.66 g fumed silica (Degussa, Aerosil 200) are used instead of gelatin. The particle size of the colloidal silver was in the range of from 10 to 50 nm, as determined via a scanning electron micrograph.

EXAMPLE 4

Alternative Adsorption of Colloidal Silver on Barium Sulfate

[0027] The procedure is analogous to Example 3a), with the exception that 1.2 l distilled water, 2 g gelatin, 20 g AgNO3 and 26 ml 25% NH3 solution are used. As the reducing agent, a solution of 10.59 g glucose in 400 ml distilled water is used and blended with 333 g BaSO4 in analogy with Example 3a). The suspension is then further turbinated for 3 h at 50° C. and kept for about 8 h at 70° C. until the reaction is complete. The Ag-colloid adsorbed on BaSO4 is freed from water and the components soluble therein (gelatin, gluconic acid, NH4NO3 and NH3) by filtering the suspension which still should be as warm as possible and subsequently washing the residue four times with distilled water. Drying takes place at 70° C. and comminution is effected as in Example 3a).

[0028] The residual amount of organic material (gelatin, gluconic acid, glucose) of the material obtained according to Example 4 was determined by means of two independent methods with the proviso that under the conditions used gelatin and gluconic acid have comparable solubility in water.

[0029] By Combustion Analysis

[0030] In this context the C and H values are below the measuring tolerance indicated by the manufacturer of the apparatus of 0.3%, i.e. with a finished compounded polyurethane material comprising 20% BaSO4 and 0.8% Ag, the total amount of organic residues can be calculated to be theoretically at most 0.182 wt % (lowest value that can be detected by the apparatus). Thus, the actual value should be considerably lower.

[0031] By Thermogravimetry

[0032] When comparing the material obtained according to Example 4 with a reference sample prepared in an identical way, but not washed (weight loss about 3.2%) and pure BaSO4, a total weight loss of at most 0.28 wt % (gelatin: 0.045 wt %, gluconic acid: 0.235 wt %) or better can be observed. Thus, the finished compounded polyurethane comprising 20% BaSO4 and 0.8% Ag exhibits a total content of organic residues of ≦0.056 wt % (gelatin: ≦0.009 wt %, gluconic acid: ≦0,047 wt %). Due to its considerably higher sensitivity, thermogravimetry is preferable over combustion analysis.

EXAMPLE 5

Determination of Antibacterial Activity

[0033] In order to determine whether the plastic bodies according to the invention can be infected with germs, five cylindrical samples each of the respective plastic (diameter 3 mm, length 13 mm) were incubated with a composition containing Staphylococcus epidermis in a Trypcase-Soy-Broth nutrient solution at 175° C. The following plastic bodies were examined (no. 1 is commercially available and untreated, nos. 2 and 3 are according to the invention):

[0034] Specimen 1: section taken from a PU catheter obtained from the company Arrow (ES 04701)

[0035] Specimen 2: according to Example 2 of the present invention

[0036] Specimen 3: according to Example 3 of the present invention.

[0037] The 5 specimens were each subjected to four test sequences under the following conditions:

[0038] Test sequence 1: initial concentration of Staphylococcus epidermis 5×107 CFU/ml

[0039] Test sequence 2: initial concentration of Staphylococcus epidermis 108 CFU/ml Test sequence 3: as in test sequence 1, but measured in physiological buffer solution at 37° C. after previous incubation for 5 hours.

[0040] Test sequence 4: as in test sequence 1, the plastic bodies having been treated with natural urine filtered to be sterile at 37° C. for 4 hours.

[0041] Table 1 shows the number of infected plastic bodies which was determined by visual control. 1 TABLE 1 Number of infected specimens Test Test Test Test Specimen Sequence Sequence Sequence Sequence Type 1 2 3 4 Comparison 1 3 5 4 5 Invention 2 0 0 0 0 3 0 3 0 0

[0042] After compounding, the catheter materials are not impaired in their mechanical properties required for therapeutical purposes (roughness, homogeneity and elasticity). The process can easily be adapted to varying requirements in the production process, since antimicrobial activity is maintained irrespective of whether the silver is introduced into the polymer material by coating the polyurethane pellets (Example 2) or via the X-ray contrast medium (Examples 3 and 4).

[0043] The plastic articles according to the invention show significantly higher antimicrobial activity with respect to adherence and biofilm formation as well as considerably improved long-time performance as compared with prior art materials at comparably lower toxicity.

[0044] The preparation processes according to the invention can easily be controlled, are economical and suited for large scale production. Example 4 additionally provides a process for removing all “adjuvant chemicals” from the inorganic contrast medium so that the grant of a protective certificate on the process should be possible.

EXAMPLE 6

Dependence of Antimicrobial Activity on Time

[0045] Catheters (The Amounts are Based on the Finished Compounded Material)

[0046] 1) polyurethane catheters 20% BaSO4+0.8% Ag, length 1.0 cm (Example 4)

[0047] 2a) silicone catheters 25% BaSO4+1% Ag, length 1 cm, thickness 1.3 mm and width 2 mm (Example 4)

[0048] 2b) silicone catheters 25% BaSO4+0.33% Ag+0.33% SiO2 (Example 3b) silicone wall sections, length 1 cm, thickness 1 mm and width 2 mm

[0049] 3) control Argen Tec 1 lumen catheter (Sicuris) Extr. 1/99 20% BaSO4+0.9-1% Ag

[0050] Sterilization: Storage in a hot-air cabinet at 90° C. for 3 hours. Previous tests showed that after this period of time the samples are free of germs. (even before that time samples are largely not infected with germs)

[0051] Germs: S. epidermidis (ref.: Infection Suppl. 6/99)

[0052] E. coli

[0053] Nutrient medium: Trypcase Soja

[0054] Way of proceeding:

[0055] samples are incubated with 5×107 germs at room temperature in a suspension of 0.45% NaCl with 2.5% glucose for 8 hours

[0056] the germ suspension is subsequently removed by centrifugation

[0057] washing two times (2 min of renewed suspension in physiological sodium chloride solution whilst swiveling)

[0058] transferring the samples into sterile sodium chloride solution in a Petri dish

[0059] sampling every hour, after 6 hours every 2 hours and transferring the samples into Trypcase Soja Medium after slight swiveling in physiological sodium chloride solution

[0060] incubation for 24 to 36 hours

[0061] evaluation of the sample for sterility (turbidity=measurement of the end point).

[0062] Results of Tests with S. epidermidis

[0063] All samples are tested five times (+++++) 2 Results of tests with S. epodermidis All samples are tested five times (+++++) Time: H Sample 1 Sample 2a Sample 2b Control 0 +++++ +++++ +++++ +++++ 1 +++++ +++++ +++++ +++++ 2 +++++ +++++ +++++ +++++ 3 ++++− ++++− +++++ +++++ 4 ++++− ++++− +++++ +++++ 5 ++−−− ++−−− ++++− +++++ 6 −−−−− +−−−− ++−−− +++++ 8 −−−−− −−−−− −−−−− +++++ 10 −−−−− −−−−− −−−−− +++++ 12 −−−−− −−−−− −−−−− ++++− 16 −−−−− −−−−− −−−−− +++−− 18 −−−−− −−−−− −−−−− +++−− + = broth turbid after 36 hours − = broth clear (sterile) after 36 hours

[0064] Discussion

[0065] In this test the antimicrobial activity of solids depending on time could be examined. It is shown that silver-filled samples exhibit antimicrobial activity already after 6 hours and a contaminated catheter can be made sterile again within this period of time even at a unphysiologically high inoculum. Lower Ag concentration as in sample 2b will also have a positive result. 3 Results of tests with E. coli All samples are tested five times (+++++) Time: H Sample 1 Sample 2a Sample 2b Control 0 +++++ +++++ +++++ 1 +++++ +++++ +++++ 2 +++++ +++++ +++++ 3 ++++− +++++ +++++ 4 ++++− +++++ +++++ 5 ++++− ++++− +++++ 6 +++−− ++++− +++++ 8 ++−−− +++−− +++++ 10 +−−−− +−−−− +++++ 12 −−−−− −−−−− +++++ 16 −−−−− −−−−− ++++− 18 −−−−− −−−−− ++++−

[0066] The results for S. epidermidis are equally good even after the silver has been eluted in physiological NaCl solution for 1, 2 and 3 weeks and the results are identical to those in Table 1.

[0067] The examination for cytotoxicity was carried out by the company Toxikon, Bedford Mass., U.S.A. It was shown that the samples prepared are not toxic and fulfil the requirements of the elution test ISO 10993.

Claims

1. A process for preparing an antimicrobial plastic body, said process comprising molding a precursor and being characterized in that prior to molding at least one component of the precursor is treated with a metal colloid.

2. The process as claimed in claim 1 wherein the precursor consists of one or several polymer materials.

3. The process as claimed in claim 2 wherein said precursor consists of polyurethane.

4. The process as claimed in any one of claims 1 to 3 wherein apart from polymeric materials further additives are added to the plastic precursor.

5. The process as claimed in claim 4 wherein said additives consist of inorganic particles.

6. The process as claimed in claim 5 wherein said inorganic particles comprise barium sulfate, calcium sulfate, strontium sulfate, titanium oxide, aluminium oxide, silicon oxide, zeolites, mica, talcum or kaolin.

7. The process as claimed in claim 6 wherein said inorganic particles comprise barium sulfate and/or fumed silica.

8. The process as claimed in any one of claims 1 to 7 wherein one or several of the components of the precursor are treated with said colloidal metal.

9. The process as claimed in any one of claims 4 to 7 wherein said plastic as well as said inorganic particles are treated with said colloidal metal.

10. The process as claimed in any one of claims 4 to 7 wherein said inorganic particles are treated with said metal colloid.

11. The process as claimed in any one of claims 1 to 10 wherein said metal colloid is colloidal silver.

12. The process as claimed in any one of claims 1 to 11 wherein said treated precursor is given its final shape by mixing, kneading, extruding, injection molding or (hot) press molding.

13. A plastic body obtainable according to any one of claims 1 to 12.

14. The plastic body as claimed in claim 13 wherein said colloidal silver has a particle size of from 10 to 50 nm.

15. The plastic body as claimed in claim 13 or 14 in the form of a catheter.