Anti-microbial carpet underlay and method of making

Abstract

A carpet underlay including an effective amount of an antimicrobial compound. A rebonded carpet pad may include foam particles bonded together by a binder including zinc pyrithione. The underlay may include a laminating film on one or both sides of the pad. The laminating film may include zinc pyrithione as an effective antimicrobial.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application claims the benefit under U.S.C. § 119 of U.S. provisional application Ser. No. 60/506,688 filed Sep. 26, 2003 and entitled “Anti-Microbial Carpet Pad and Method of Making,” hereby incorporated herein by reference for all purposes.

FIELD OF THE INVENTION

This invention relates to carpet underlay and more particularly to a carpet underlay which includes an anti-microbial agent.

BACKGROUND OF THE INVENTION

Carpet, especially wall-to-wall carpet, is normally installed with an underlay, often in the form of a foam pad or cushion. Moisture, dirt, food particles, and other debris tend to filter through the carpet to the pad. These conditions provide a breeding ground for various bacteria and mold that may produce undesirable odors, cause degradation of the carpet and/or pad, and/or contribute to a poor indoor air quality environment for occupants of the premises.

A typical carpet pad consists of ground polyurethane foam particles of a specific size range that are rebonded back together to form a continuous foam pad of various densities and thickness. Typically, carpet pad ranges in density from four to eight pounds per cubic foot. Rebonded pad is made from recycled polyurethane foam, typically from scraps of foam reclaimed from padding used in furniture, bedding, and automobile seating. The scraps are often of different sizes and colors. The rebonded foam is produced by grinding or chopping the scraps, mixing the chopped scraps with a binder, curing the binder, and slicing the resulting block of rebonded foam particles into a desired pad thickness. The binder may typically form ten percent of the weight of the final rebonded pad. Various films or webs may be bonded to one or both sides of the pad for various purposes.

SUMMARY OF THE INVENTION

A carpet underlay including an effective amount of an antimicrobial compound.

In one embodiment, a carpet underlay comprises a rebonded pad comprising particles of foam joined together with a binder. The binder includes an effective amount of an anti-microbial compound.

In one embodiment, a carpet underlay comprises a film including an effective amount of an antimicrobial compound. The film may be laminated to one or both surfaces of a carpet pad.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross sectional view of a carpet undrlay according to one embodiment of the present invention.

FIG. 2 is a block diagram of a binder mixing system used in making rebonded pad for testing the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

FIG. 1 is a cross sectional illustration of an antimicrobial carpet underlay 10 which may be made according to one embodiment of the present invention. The underlay 10 includes a rebonded pad portion 12 including a number of small pieces of foam 14 bonded together by binder 16. The foam pieces 14 may typically be ground or chopped scraps of polyurethane foam used in making furniture. The underlay 10 may also include a film 18 bonded to at least one surface of the pad 12, in this case the upper surface of the pad 12. The film 18 is typically preferred to facilitate laying carpet on top of the underlay 10 and for resisting the flow of fluids into the pad 12, e.g. when fluids are spilled on carpet installed over the pad 12. A film 18 may also be laminated to the lower side of the pad 12 if desired. In the present invention, the carpet underlay 10 is resistant to the growth of bacteria and mold on and within the underlay 10. This antimicrobial resistance is achieved by adding an effective amount of an antimicrobial compound to the pad 12 and/or to the film 18, as described in more detail below.

In one embodiment, an effective biocide, or antimicrobial, compound known as zinc pyrithione (e.g. the material sold under the trademark ZINC OMADINE by Arch Chemicals Inc.) is incorporated into rebonded carpet pad 12 by the following method. The chemical name for this compound is Bis(1-hydroxy-2(1H)-pyridinethionato-O,S)-(T-4)Zinc. The zinc pyrithione in powdered form is mixed with a triol polyol of a molecular weight typically ranging from 3000 to 3500 to form a 20% strength antimicrobial/polyol mixture concentrate. Then, the 20% antimicrobial/polyol mixture concentrate is added to a binder stream at a 3.90% to 6.50% addition level to render a zinc pyrithione concentration of between 7500 to 12500 ppm in the binder 16. The antimicrobial/polyol mixture concentrate and binder stream are preferably held at between about 90 and about 100 degrees F. during mixing and use. The binder 16 is typically composed of ⅓ aromatic oil, ⅓ triol polyol, and ⅓ polymeric MDI. The binder is added to ground foam particles, mixed together, compressed, injected with steam, and dried in the form of a large block of rebonded foam particles. The block is then sliced into thicknesses suitable for carpet pad, e.g. three-eighth to five-eighth inch, to produce the rebonded foam pad 12. The binder to ground foam weight ratio is approximately 1:10. The final concentration of Zinc Pyrithione in the rebonded pad 12 is therefore from about 750 ppm to about 1250 ppm.

If desired, the particular concentration of zinc pyrithione in the antimicrobial/polyol mixture concentrate may be selected to be more or less than the 20% concentration used in this embodiment. The addition level of the antimicrobial/polyol mixture concentrate in the binder 16 may then be adjusted to achieve a zinc pyrithione concentration of at least about 7500 ppm and preferably between about 7500 to about 12500 ppm in the binder 16.

If desired, a binder 16 to ground foam weight ratio of more or less than 1:10 may be used. If other ratios are used, the particular concentration of zinc pyrithione in the antimicrobial/polyol mixture concentrate and/or the addition level of the antimicrobial/polyol mixture concentrate in the binder 16 may then be adjusted to achieve a final concentration of Zinc Pyrithione in the rebonded pad 12 from about 750 ppm to about 1250 ppm

FIG. 2 illustrates a mixing system used in making binder 16 for testing the present invention. A method for making binder 16 will be described with reference to FIG. 2. A mix tank 20 included a thirty-gallon drum and a vortex type mixer. Eighty pounds of polyol and twenty pounds of powdered zinc pyrithione were placed in tank 20 and mixed for at least three hours. A transfer pump 22 was used to pump the mixture from mix tank 20 to a run tank 24, which also includes a vortex mixer. The antimicrobial/polyol mixture concentrate in the run tank 24 was mixed constantly during production. If the mixer is turned off for any significant period of time, it should be restarted at least two hours prior to use in production of rebonded pad 12.

During production of rebonded pad 12, a variable speed Watson Marlow pump 26 was used to flow the antimicrobial/polyol mixture concentrate from the run tank 24 at a controllable rate. The rate is controlled by a control panel 28 and a variable frequency drive 30. The discharge side of pump 26 is connected to the vacuum side of a binder pump 32. A tank 34 of binder also has an outlet connected to the vacuum side of a binder pump 32. The discharge side of pump 32 is connected to a static mixer 36. The outlet 38 of mixer 36 is coupled to a blender where polyurethane particles 14 are mixed with binder 16 to produce the finished rebonded polyurethane pad 12.

During the operation of the system of FIG. 2, it is preferred that the antimicrobial/polyol mixture concentrate in the mix tank 20 and run tank 24 be maintained at a temperature of between about 90 and about 100 degrees F. during mixing and production operations. Likewise, the binder tank 34 is preferable maintained within the same temperature range.

It is sometimes desirable to include laminating film 18 on one or both surfaces of carpet pad 12. For example, such a film 18 may facilitate laying and stretching of carpet by allowing the carpet to slide easily on top of the pad 12 and avoiding undesirable movement or buckling of the pad 12. The film may also prevent fluids spilled on carpet from penetrating into the pad 12. In one embodiment of the present invention, an antimicrobial laminating film 18 is laminated onto one or both surfaces of a carpet pad. The carpet pad may or may not include an antimicrobial compound as disclosed above.

The anti-microbial laminating film 18 of this embodiment inhibits the growth of certain bacteria and fungus when used in combination with prime polyurethane foam pad or rebonded polyurethane foam pad 12 as carpet underlay. The anti-microbial film may be thermally laminated to the top and/or bottom surfaces of prime polyurethane foam pad or re-bonded polyurethane flexible foam pad 12 where it acts as a barrier to inhibit the growth of microbes that accumulate on the surfaces of carpet underlay. This film 18 may also inhibit the growth of microorganisms in other products where this film can be used as a lamination barrier.

In this embodiment, a 0.45 to 0.50 mil monolayer blown film 18 includes between 500 and 1500 ppm of the antimicrobial compound zinc pyrithione (e.g. the material sold under the trademark ZINC OMADINE by Arch Chemicals Inc.). The chemical name for this compound is Bis(1-hydroxy-2(1H)-pyridinethionato-O,S)-(T-4)Zinc. The zinc pyrithione powder is incorporated at 10% by weight into a LLDPE, linear low density polyethylene, resin concentrate supplied by PolyChem Alloy, Inc. under the trademark POLYSEPT 554Z. The chemical description of the resin concentrate is Mercaptopyridine-N-oxide in Polypropylene. This resin concentrate has a specific melt index of 20 grams/10 mins. and 0.93 density. About 1% to about 3% by weight of this concentrate is then blended with a LLDPE/Copolymer resin mixture. Due to thermal breakdown of zinc pyrithione during processing of the film, the initial 10% concentration of zinc pyrithione in the concentrate may be effectively reduced to less than 6%. After mixing with the resin mixture and processing it into a film, the net effective concentration of zinc pyrithione in the processed film is about 500 ppm to 1500 ppm. Suitable copolymer resins may be EVA, EMA, or EMM. The copolymer resin consists of approximately 60-70% by weight of the total mixture. The remaining mixture is 30-40% LLDPE by weight, including the 1-3% LLDPE concentrate treated with zinc pyrithione. The blended resins may then be extruded at between 450 and 550 degrees F. with a blow up ratio, i.e. bubble diameter to die diameter, of between 1.8 and 2.5:1. It is preferred that the extrusion temperature be kept below 500 degrees F. to minimize thermal breakdown of the zinc pyrithione.

It is apparent that zinc pyrithione powder may be incorporated at more or less than 10% by weight into the resin concentrate. If other addition levels are selected, the percentage of the concentrate blended with the LLDPE/Copolymer resin mixture may be adjusted to achieve a net effective concentration of zinc pyrithione in the processed film of from about 500 ppm to 1500 ppm

The anti-microbial treated film may be thermally laminated (e.g. at about 250-450 degrees F., 0.5 sec dwell time) to one or both sides of a prime polyurethane foam pad or rebonded pad 12 which may typically be from about three-eighth inch to about five-eighth inch thick or other desired thickness. Other laminating methods may be used if desired, e.g. by use of an adhesive. The anti-microbial film may be laminated to an anti-microbial treated pad or non-anti-microbial treated pad. The anti-microbial film may also be laminated to another anti-microbial treated or untreated film for lamination to anti-microbial treated pad or non-anti-microbial treated pad.

Biocidal effectiveness of the rebonded carpet pad 12 and/or film 18 according the present invention may be determined by measuring inhibition of growth of bacterial and/or fungus using AATCC (American Association of Textile Chemists and Colorists) 174, ASTM E2180-1, and ASTM D 3273 test protocols compared to non-treated control standards. The AATCC 174 protocol was developed for determining the antimicrobial activity of new carpet materials.

A number of specimens of carpet underlay 10 were made by methods described above, with various concentrations of zinc pyrithione in the binder 16 and film 18 for testing to determine levels that provide an effective antimicrobial effect. The specimens included a film 18 on one side as illustrated in FIG. 1. This allowed testing of the foam side of the specimens to indicate antimicrobial effect of the pad 12 without film 18 and testing of the film side to indicate antimicrobial effect of the pad 12 with film 18. The AATCC 174 test method provides for testing both unwashed and washed samples. Washed samples were treated according to the MTCC 138 protocol. The test results are summarized as follows.

The AATCC 174 test method includes three parts. Part I is a qualitative test for antibacterial activity. Test specimens are placed into contact with a nutrient agar which has been streaked with a bacterial culture. The specimens are then incubated. After incubation, a clear area of interrupted growth underneath and along the sides of the test specimen indicates antibacterial activity of the specimen. Standard strains of bacteria are used, with Staphylococcus aureus and Klebsiella pneumoniae being the representative organisms.

In the MTCC 174, Part I tests various washed and unwashed specimens were tested. An unwashed foam side specimen with 751 ppm of zinc pyrithione passed the test with a one millimeter zone of inhibition for Klebsiella pneumoniae and a two millimeter zone of inhibition for Staphylococcus aureus. All unwashed and washed foam side specimens with a concentration of 1096 ppm or more of zinc pyrithione inhibited the growth of Klebsiella pneumoniae from underneath and along the sides of the specimen.

The AATCC 174, Part II test provides a quantitative procedure for the evaluation of the degree of antibacterial activity. Test specimens are inoculated with the test microorganisms. After incubation, the bacteria are eluted from specimens by shaking in 100 milliliters of liquid. The number of bacteria present in the liquid is determined and the percent reduction produced by the specimen is calculated.

In the MTCC 174, Part II tests, washed foam side specimens containing 751 and 1096 ppm of zinc pyrithione provided a 90% reduction in the numbers of both Staphylococcus aureus and Klebsiella pneumoniae. In all unwashed and washed film and foam side specimens containing a concentration of 500 ppm or more of zinc pyrithione in the film and 1096 ppm of zinc pyrithione in the pad, there was a reduction of at least 66% in Staphylococcus aureus with an average reduction of 92%.

The AATCC 174, Part III protocol provides a qualitative test for antifungal activity. Specimens are subjected to the growth of a common fungus, Aspergillus niger, on Sabouraud Dextrose agar. Prewet specimens are inoculated and incubated at 28 degrees C. for seven days. Specimens are then assessed for growth of the fungus.

In the AATCC 174, Part III tests, washed and unwashed foam side samples with a concentration of 1096 ppm of zinc pyrithione in the pad produced no observable fungus growth. No growth was observed on washed and unwashed film side samples when the concentration of zinc pyrithione in the film was 1500 ppm or greater.

30 Inhibitory mold activity was also tested by the ASTM E2180-01 test method. Good inhibitory activity for Aspergillus niger was observed when film side specimens had a total minimum combined concentration of 1600 ppm of zinc pyrithione. The total combined concentration is the sum of the concentration in the pad 12 of a specimen and the concentration in the film 18 of the specimen. The tests indicate that a minimum of 500 ppm may be preferred in the film 18, with a preferred complement minimum of 1100 ppm in the pad 12. Alternatively, a minimum concentration of 750 ppm may be preferred in the pad 12 with a preferred complement minimum of 850 ppm in the film 18. Good results were achieved for some, but not all, specimens with a total combined concentration of 1251 ppm, i.e. 751 ppm in the pad 12 and 500 ppm in the film 18. Therefore, the preferred minimum combined concentration is about 1600 ppm.

Mold susceptibility tests were also performed under the ASTM D3273 test method. No Aspergillus niger mold colonization was observed on film 18 side specimens when the specimens had a total minimum combined concentration of about 1600 ppm zinc pyrithione. The tests indicate that a minimum of 500 ppm may be preferred in the film 18, with a preferred complement minimum of 1100 ppm in the pad 12. Alternatively, a minimum concentration of 750 ppm may be preferred in the pad 12 with a preferred complement minimum of 850 ppm in the film 18.

The above described tests indicate that an effective antimicrobial carpet underlay 10 can be made by incorporating 7500 to 12500 ppm of zinc pyrithione into binder used to bind foam particles to make rebonded carpet pad. The net concentration in the foam pad 12 is from 750 to 1250 ppm of zinc pyrithione when the binder to foam weight is 1:10. If different ratios of binder to foam are used, it is preferred to adjust the concentration in the binder stream to achieve at least about 750 ppm of zinc pyrithione in the final foam pad 12.

The tests also indicate that an effective antimicrobial film can be made by incorporating 500 to 1500 ppm of zinc pyrithione in the film 18. As noted above, the initial concentration is preferably adjusted to account for thermal degradation which occurs during film processing. Thus, the initial ten percent concentration of zinc pyrithione in the resin concentrate may be reduced to an effective five to six percent after processing.

The tests also show that when both a foam pad 12 and a film 18 including a biocide are combined to form a carpet underlay, lower concentrations of zinc pyrithione may be used than may be necessary if only the pad 12 or the film 18 contains the biocide. In general, in a carpet underlay having a biocide treated pad 12, but an untreated film 18, the pad 12 preferably has a biocide concentration near the upper end of the range tested, e.g. at least about 1100 to 1250 ppm of zinc pyrithione. For an underlay having an untreated pad 12, and a treated film 18, the film 18 preferably has a biocide concentration near the upper end of the range tested, e.g. at least about 1100 to 1500 ppm of zinc pyrithione. When both the pad 12 and film 18 are treated, it is preferred that the combined concentrations for foam pad 12 and film 18 be at least about 1600 ppm.

In the above disclosure, the concentrations of biocide in the foam pad 12 and film 18 have been discussed in terms of ranges having a lower limit and an upper limit. It is apparent that it is preferred to include concentrations at or above the lower limits to achieve an effective antimicrobial activity in the products. That is, concentrations above the ranges tested should also be effective. Concentrations should be kept below a level at which the biocide may affect the mechanical integrity of the product. Since the biocide is a relatively high cost part of the product, normal practice should be to avoid using more of the biocide than is needed to achieve effective biocidal or antimicrobial activity.

The particular choice of an effective amount of the biocide also depends upon the particular application in which the carpet pad will be used. In some applications, there is a requirement that carpet products exhibit effective antimicrobial activity after being washed. For those applications, it may be desirable to use a concentration at or near the upper limits of the ranges given above. In the tests reported above, the specimens at the upper ends of the ranges provided effective antimicrobial activity after washing. If the application does not require washing, a lower concentration of biocide provides an effective biocidal activity.

In the above description of making the rebonded foam pad 12, zinc pyrithione was initially mixed in powder form with a polyol. The resulting mixture is basically a suspension of particles in a liquid. As noted in the description of FIG. 2, it is desirable to continuously operate a mixer in run tank 24 to insure that the zinc pyrithione remains uniformly mixed with the polyol. It may be desirable to first dissolve the zinc pyrithione in a fluid which is miscible with a polyol. Such a process is described in U.S. Pat. No. 5,114,984 issued to Branch et al. on May 19, 1992. In that patent, a pyrithione salt is dissolved in an alkanolamine which is miscible with a polyol, which the Branch patents indicates may then be used to make an antimicrobially effective polyurethane. Such a solution of zinc pyrithione in polyol may also be suitable for mixing with the binder described above for use in the present invention.

While the present invention has been disclosed in terms of specific structures, chemical compositions and mixtures, and methods of making carpet underlay, it is apparent that various changes and substitutions of materials and steps may be made within the scope of the present invention as defined by the appended claims.

Claims

1. A carpet underlay comprising a pad comprising:

foam particles bound together with a binder comprising an effective amount of an anti-microbial compound.

2. A carpet underlay according to claim 1, wherein the anti-microbial compound comprises zinc pyrithione.

3. A carpet underlay according to claim 2, wherein the binder comprises at least about 7500 ppm of the anti-microbial compound.

4. A carpet underlay according to claim 2, wherein the binder comprises from about 7500 ppm to about 12500 ppm of the anti-microbial compound.

5. A carpet underlay according to claim 4, wherein the binder comprises one tenth of the weight of the pad, whereby the pad comprises from about 750 to about 1250 ppm of the anti-microbial compound.

6. A carpet underlay according to claim 2, wherein the pad comprises at least about 750 ppm of the anti-microbial compound.

7. A carpet underlay according to claim 2, wherein the pad comprises from about 750 to about 1250 ppm of the anti-microbial compound.

8. A carpet underlay according to claim 1, further comprising a film laminated to the pad.

9. A carpet underlay according to claim 8, wherein the film is thermally laminated to the pad.

10. A carpet underlay according to claim 8, wherein the film comprises an effective amount of an anti-microbial compound.

11. A carpet underlay according to claim 10, wherein the anti-microbial compound comprises zinc pyrithione.

12. A carpet underlay according to claim 11, wherein the film comprises at least about 500 ppm of zinc pyrithione.

13. A carpet underlay according to claim 11, wherein the film comprises from about 500 ppm to about 1500 ppm of zinc pyrithione.

14. A carpet underlay according to claim 11, wherein the pad comprises at least about 1100 ppm zinc pyrithione and the film comprises at least about 500 ppm zinc pyrithione.

15. A carpet underlay according to claim 11, wherein the pad comprises at least about 750 ppm zinc pyrithione and the film comprises at least about 850 ppm zinc pyrithione.

16. A carpet underlay according to claim 11, wherein the concentration of zinc pyrithione in the pad plus the concentration of zinc pyrithione in the film comprises at least about 1600 ppm.

17. A carpet underlay comprising:

a foam pad, and

an LLDPE laminating film comprising an effective amount of an anti-microbial compound laminated to the foam pad.

18. A carpet underlay according to claim 17, wherein the antimicrobial compound comprises zinc pyrithione.

19. A carpet underlay according to claim 18, wherein the laminating film comprises at least about 500 ppm of zinc pyrithione.

20. A carpet underlay according to claim 18, wherein the laminating film comprises from about 500 ppm to about 1500 ppm of zinc pyrithione.

21. A carpet underlay according to claim 18, wherein the foam pad comprises a rebonded polyurethane foam pad.

22. An LLDPE laminating film comprising an effective amount of an anti-microbial compound.

23. A laminating film according to claim 22, wherein the antimicrobial compound comprises zinc pyrithione.

24. A laminating film according to claim 23, comprising at least about 500 ppm of zinc pyrithione.

25. A laminating film according to claim 23, comprising from about 500 ppm to about 1500 ppm of zinc pyrithione.

26. A method for making rebonded carpet pad, comprising:

mixing zinc pyrithione with a polyol to form an antimicrobial polyol mixture concentrate,

blending the antimicrobial polyol mixture concentrate with a binder stream, and

selecting a percentage of zinc pyrithione mixed with the polyol and the addition ratio of the antimicrobial polyol mixture concentrate with the binder stream to provide an overall concentration of zinc pyrithione in the binder of at least about 7500 ppm

27. A method for making rebonded carpet pad according to claim 26, further comprising:

mixing zinc pyrithione with a triol polyol to a 20% strength antimicrobial polyol mixture concentrate, and

blending the 20% strength antimicrobial polyol mixture concentrate with a binder stream at at least a 3.90% addition level.

28. A method according to claim 27, further comprising blending the 20% strength antimicrobial polyol mixture concentrate with a binder stream at a 3.90% to 6.5% addition level.

29. A method according to claim 26, further comprising:

mixing the binder with foam particles.

30. A method according to claim 29, wherein the ratio of binder to foam particles is about 1:10 and results in an overall concentration of zinc pyrithione in the carpet pad of at least about 750 ppm.

31. A method according to claim 29, further comprising shaping the mixture of binder and foam particles into a block, curing the binder and slicing the block to form carpet pad.

32. A method according to claim 31, further comprising laminating a film to at least one side of the carpet pad.

33. A method according to claim 32, wherein the film comprises an effective amount of an anti-microbial compound.

34. A method of making an anti-microbial film comprising:

incorporating zinc pyrithione into an LLDPE resin concentrate,

mixing the resin concentrate with an LLDPE copolymer resin mixture to form a resin blend,

extruding the resin blend into a film, and

selecting a percentage of zinc pyrithione incorporated into the LLDPE resin concentrate and a percentage of resin concentrate in the resin blend to provide a concentration of zinc pyrithione in the film of at least about 500 ppm.

35. A method of making an anti-microbial film according to claim 34, further comprising:

selecting a percentage of zinc pyrithione incorporated into the LLDPE resin to be at least about 10% by weight, and

selecting a percentage of resin concentrate in the resin blend to be at least about 1% by weight.

36. A method according to claim 34, wherein the LLDPE copolymer resin mixture comprises about 60% to 70% by weight copolymer and about 30% to about 40% LLDPE by weight, including the resin concentrate.

37. A method according to claim 34, further comprising extruding the resin blend at a temperature of from about 450 to 550 degrees F. with a blow up ratio of between 1.8 and 2.5:1.

38. A method according to claim 37, further comprising extruding the resin blend at a temperature of from about 450 to 500 degrees F.