Methods of treating non-sputtered regions of PVD target constructions to form particle traps
The invention includes PVD targets having non-sputtered regions (such as, for example, sidewalls), and particle-trapping features formed along the non-sputtered regions. In particular aspects, the particle-trapping features can comprise a pattern of bent projections forming receptacles, and can comprise microstructures on the bent projections. The targets can be part of target/backing plate constructions, or can be monolithic. The invention also includes methods of forming particle-trapping features along sidewalls of a sputtering target or along sidewalls of a target/backing plate construction. The features can be formed by initially forming a pattern of projections along a sidewall. The projections can be bent and subsequently exposed to particles to form microstructures on the bent projections.
This patent claims priority to U.S. Provisional Patent Application 60/396,543, which was filed Jul. 16, 2002.
TECHNICAL FIELDThe invention pertains to methods of forming particle traps along non-sputtered regions of a physical vapor deposition (PVD) target construction, and pertains to PVD target constructions having projections along at least one non-sputtered region.
BACKGROUND OF THE INVENTIONDeposition methods are utilized for forming films of material across substrate surfaces. Deposition methods can be utilized in, for example, semiconductor fabrication processes to form layers ultimately utilized in fabrication of integrated circuitry structures and devices. An exemplary deposition method is physical vapor deposition (PVD), which includes sputtering processes.
A physical vapor deposition operation is described with reference to a sputtering apparatus 110 in
Substrate 118 can comprise, for example, a semiconductor wafer, such as, for example, a single crystal silicon wafer. A metal-containing film can be over a surface of the substrate in particular applications. Target 10 can comprise, for example, one or more of nickel, tantalum, titanium, copper, aluminum, silver, gold, niobium, platinum, palladium, tungsten and ruthenium, including one or more alloys of the various metals. Exemplary targets can comprise one or more of various mixtures, compounds or alloys including, for example, Ti/N, Ti/Nb, Ti/W and Ti/Al. The target can be a monolithic target, or can be part of a target/backing plate assembly.
Material is sputtered from a surface of target 10 and directed toward substrate 118. The sputtered material is represented by arrows 122.
Generally, the sputtered material will leave the target surface in a number of different directions. This can be problematic, and it is preferred that the sputtered material be directed relatively orthogonally to an upper surface of substrate 118. Accordingly, a focusing coil 126 is provided within chamber 112. The focusing coil can improve the orientation of sputtered materials 122, and is shown directing the sputtering materials relatively orthogonally to the upper surface of substrate 118.
Coil 126 is retained within chamber 112 by pins 128 which are shown extending through sidewalls of the coil and also through sidewalls 114 of chamber 112. Pins 128 are retained within retaining screws 132 in the shown configuration. The schematic illustration of
Spacers 140 extend around pins 128, and are utilized to space coil 126 from sidewalls 114.
Problems can occur in deposition processes if particles are formed, in that the particles can fall into a deposited film and disrupt desired properties of the film. Accordingly, it is desired to develop traps which can alleviate problems associated with particles falling into a desired material during deposition processes.
Some efforts have been made to modify PVD targets to alleviate particle formation. For instance, bead blasting has been utilized to form a textured surface along sidewalls of a target with the expectation that the textured surface will trap particles formed along the surface. Also, knurling and machine scrolling have been utilized to form textures on target surfaces in an effort to create appropriate textures that will trap particles.
Although some of the textured surfaces have been found to reduce particle formation, the particle formation is frequently not reduced to a desired level. In some instances, the texturing on a sidewall surface of a target can ultimately lead to formation of very large particles. Specifically, films of sputtered material form on the textured surface over time, and at some point the films peel away from the target. The films can fall onto a substrate during a PVD process to cause a defect in a layer deposited during the PVD process. This problem is frequently encountered with textures which have been formed through machine scrolling and/or knurling.
Another problem is that the formation of a textured surface can itself introduce contaminants. For instance, bead-blasting typically utilizes particles blasted at the target with high energy to texture a surface of the target. Some of the particles from for the blasting can be imbedded in the target during the blasting process, remain with the target as it is inserted in a PVD chamber, and then fall from the target during a sputtering process to become problematic contaminants during the sputtering.
It would be desired to develop a new texture which can be formed on sidewalls or other non-sputtered surfaces of a PVD target construction to better alleviate particle formation than prior art textures, and it would be particularly desirable if the new texture could eliminate undesired peeling of materials from sidewalls and other non-sputtered surfaces of a target construction during PVD processing. It would also be desired to reduce, and preferably eliminate sputtering process contamination resulting from embedded bead-blasted particles in sputtering target constructions.
SUMMARY OF THE INVENTIONIn one aspect, the invention includes a method of treating a non-sputtered surface (such as, for example, a sidewall, flange, or non-sputtered region of a sputtering face) of a PVD target construction. A pattern of projections is formed along the non-sputtered surface. The projections are bent. The projections are also exposed to particles to form microstructures on the projections. The projections can be exposed to the particles either before or after the bending of the projections.
In one aspect, the invention includes a PVD target construction having a sidewall proximate a sputtering face. The sidewall forms a lateral periphery of the target construction. The target construction includes a pattern of curved projections along the sidewall. The projections form cavities which open laterally along the sidewall.
In one aspect, the invention includes a PVD target construction having a sidewall proximate a sputtering face, and comprising a repeating pattern of receptacles along the sidewall. The receptacles have inner surfaces, and the target construction further comprises microstructures on the inner surfaces of the receptacles.
BRIEF DESCRIPTION OF THE DRAWINGSPreferred embodiments of the invention are described below with reference to the following accompanying drawings.
This disclosure of the invention is submitted in furtherance of the constitutional purposes of the U.S. Patent Laws “to promote the progress of science and useful arts” (Article 1, Section 8).
The invention encompasses new textures which can be formed on one or more surfaces of a PVD target or target/backing plate assembly, and utilized for trapping sputtered materials which redeposit on the target or assembly. In a particular aspect, curved projections (such as, for example, a bent scroll pattern) are formed on non-sputtered surfaces of a target or target/backing plate assembly to form particle trapping areas. The non-sputtered surfaces can include sidewall surfaces, flange surfaces and/or non-sputtered surfaces along a sputtering face. The projections can be exposed to particles to roughen surfaces of the projections. The projections can be considered to form a macro-scale roughness of a trapping area, and the roughened surfaces of the projections can be considered to form a micro-scale roughness of the trapping area. Thus, the invention can include patterns which have both macro-scale and micro-scale roughness, and which are utilized in trapping areas.
The utilization of both macro-scale and micro-scale patterns can be advantageous. The macro-scale pattern and micro-scale pattern can significantly reduce material fall off from a target and/or backing plate surface. Also, the formation of a micro-scale rough surface on the macro-scale pattern can effectively reduce problems that may otherwise be associated with cyclic thermal stresses occurring during cyclic sputtering processes. Specifically, a macro-scale pattern alone (such as, for example, a long machined scroll) can trap re-deposited materials to form a long film within a trapping region. Thermal stresses (such as stress associated with, for example, a different thermal expansion coefficient of the redeposited film versus the base material of the target and/or backing plate), can lead to peeling of the film from the target and/or backing plate. As the film peels from the target and/or backing plate, it can fall onto a substrate underlying the target to undesirably form particles within a layer sputter-deposited on the substrate during a PVD process. Additionally or alternatively, the peeling film can fall directly onto an electrostatic chuck provided to support the substrate, which can create system failure. In particular aspects the invention encompasses bead-blasting and/or steel brushing and/or other treatment of a macro-scale pattern to form microstructures on the pattern which pattern, and can thus alleviate, or even prevent, peeling of redeposited film materials from the trapping area.
Particular aspects of the invention are described with reference to
Sputtering face 12 will generally have both a region from which materials are sputtered in a PVD operation and a region from which materials are not sputtered in the PVD operation. The non-sputtering region can encompass, for example, a region proximate sidewall 14 corresponding to a laterally peripheral region of face 12.
As discuss above, a problem with utilizing target construction 10, or other target configurations, in sputtering operations is that some materials sputtered from face 12 can redeposit on other surfaces of the target construction (such as non-sputtered regions including the sidewalls 14, flange 16 and non-sputtered regions of face 12). The re-deposited material can ultimately fall from the target construction as particles during a PVD operation. The particles can deposit within a layer sputter-deposited during the PVD operation to detrimentally effect properties of the layer, and/or can fall onto an electrostatic chuck provided to support a substrate. It is therefore desired to develop methods for treating the sidewalls and/or flange and/or other non-sputtered surfaces of the target to avoid particle contamination of a sputter-deposited layer.
In accordance with an aspect of the present invention, surfaces of face 12 (the non-sputtered surfaces), sidewall 14 and/or flange 16 are treated by new methodologies to alleviate particle formation. The treated regions can, for example, extend partially or entirely across the regions indicated by brackets 18 in
Referring again to
If the sputtering surface 12 (
It can be advantageous that the cavities 23 open upwardly in the orientation in which target construction 10 is ultimately to be utilized in a sputtering chamber (such as, for example, the chamber 12 of
The curved projections 22 of
In particular aspects, curved projections 22 can be considered to have bases 25 where the curved projections join to sidewall 14, and sidewall 14 can be considered to have a surface 15 extending between the bases of the curved projections. The curved projections will typically have a maximum height above the sidewall surface 15 of from about 0.0001 inches to about 0.01 inches.
The particles used to form the microstructures can comprise, for example, one or more of silicon carbide, aluminum oxide, solid H2O (ice), or solid carbon dioxide. If the particles comprise a non-volatile material, a cleaning step can be introduced after formation of divots 32 to remove the particles. For instance, if the particles comprise silicon carbide or aluminum oxide, a cleaning step can be utilized wherein projections 22 are exposed to a bath or stream of cleaning material and/or are brushed with an appropriate brushing tool (such as a wire brush). A suitable stream can be a stream comprising solid H2O or solid carbon dioxide particles. If the particles initially utilized to form divots 32 consist essentially of, or consist of, volatile particles (such as solid ice or solid CO2), then the cleaning step described above can be omitted. In a particular aspect, the bead-blasting media is 24 grit Al2O3 media, and the bead-blasting is conducted to, for example, from about 1 to about 4000 micro-inch RA, preferably from about 50 to about 2000 micro-inch RA, and typically from about 100 to about 300 micro-inch RA.
The bead-blasting of the present invention can be conducted at much lower pressures than the pressures typical of prior art processes, which can reduce a likelihood that bead-blasted particles will become embedded in structures treated with the: present invention. Specifically, prior art bead-blasting is typically conducted at pressures of at least about 80 pounds per square inch (psi) (i.e., is conducted by pushing particulates at a structure with impact pressures imparted by the particulates on the structure averaging at least about 80 psi). In contrast, bead-blasting of the present invention can be conducted at pressures of less than or equal to 20 psi. To further reduce a likelihood of bead-blasted particles remaining imbedded or otherwise associated with a surface treated in accordance with the present invention, the surface can be cleaned after the bead-blasting by mechanically brushing the surface (utilizing, for example, a wire brush), and/or by spraying the surface with a volatile cleaning agent (e.g., by blasting the surface with CO2), and/or by spraying the surface with a non-volatile cleaning agent.
The sidewall 14 shown at the processing stage of
Although the exemplary aspect of the invention described herein forms the microstructures on projections 22 after bending the projections, it is to be understood that the invention encompasses other aspects (not shown) in which the microstructures are formed prior to bending the projections. Specifically, projections 22 can be subjected to bead-blasting at the processing stage of
The projections 22 of
Construction 200 comprises a target 202 bonded to a backing plate 204. The target and backing plate join at an interface 206 in the shown assembly. The bond between target 202 and backing plate 204 can be any suitable bond, including, for example, a solder bond or a diffusion bond. Target 202 can comprise any desired material, including metals, ceramics, etc. In particular aspects, the target can comprise one of more of the materials described previously relative to the target 10 of
Construction 200 has a similar shape to the target construction 10 of
A difference between construction 200 of
The target 202 of construction 200 can be treated to form particle traps along sidewall regions and/or non-sputtered regions of the sputtering face before or after the target is bonded to the backing plate. Similarly, the backing plate 204 of the construction can be treated to form particle traps along sidewall regions and/or flange regions before or after the backing plate is bonded to the target. Typically, both the target and the backing plate will have one or more surfaces treated to form particle traps, and the treatment of the target and/or backing plate of construction 200 will occur after bonding the target to the backing plate so that the target and backing plate can be concurrently treated with the same processing tool.
In compliance with the statute, the invention has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the invention is not limited to the specific features shown and described, since the means herein disclosed comprise preferred forms of putting the invention into effect. The invention is, therefore, claimed in any of its forms or modifications within the proper scope of the appended claims appropriately interpreted in accordance with the doctrine of equivalents.
Claims
1. A method of treating a non-sputtered region of a PVD target, comprising:
- forming a pattern of projections along the non-sputtered region;
- bending the projections; and
- exposing the projections to a pressurized stream of particles to form microstructures on the projections.
2. The method of claim 1 wherein the target is a monolithic target.
3. The method of claim 1 further comprising bonding the target to a backing plate to incorporate the target into a target/backing plate construction.
4. The method of claim 3 wherein the bonding the target to the backing plate occurs prior to forming the pattern of projections along the non-sputtered region.
5. The method of claim 4 wherein the target has a sidewall; wherein the non-sputtered region comprises at least a portion of the sidewall of the target; wherein the backing plate has a sidewall, and further comprising forming the pattern of projections to extend along at least a portion of the sidewall of the backing plate and at least along a portion of the sidewall of the target.
6. The method of claim 1 wherein the projections are bent prior to exposing the projections to the particles.
7. The method of claim 1 wherein the projections are bent after exposing the projections to the particles.
8. The method of claim 1 wherein the pattern of projections is formed as a scroll pattern by utilizing a CNC tool to cut into the non-sputtered region of the target.
9. The method of claim 1 wherein the particles comprise one or both of solid H2O and solid CO2.
10. The method of claim 1 wherein the particles comprise one or both of silicon carbide and aluminum oxide; and wherein the exposure of the non-sputtered region to the pressurized stream comprises utilization of a pressure of less than 20 psi within the stream during the exposure.
11. The method of claim 1 wherein the particles comprise one or both of silicon carbide and aluminum oxide; and further comprising brushing the non-sputtered region after the exposure to the particles.
12. The method of claim 1 wherein the particles comprise one or both of silicon carbide and aluminum oxide; and further comprising exposing the non-sputtered region to a stream of cleaning agent after the exposure to the particles.
13. The method of claim 12 wherein the cleaning agent comprises one or both of solid H2O and solid CO2.
14. The method of claim 1 wherein the bent projections have bases, wherein the non-sputtered region of the target has a surface extending between the bases of the bent projections, and wherein the bent projections have a maximum height above the surface of from about 0.0001 inches to about 0.01 inches.
15. The method of claim 1 wherein a periodic repeat of the bent projections across the non-sputtered region occurs in a distance of from about 0.0001 inches to about 1 inch.
16-35. (canceled).
Type: Application
Filed: Nov 9, 2004
Publication Date: Apr 21, 2005
Inventor: Jaeyeon Kim (Liberty Lake, WA)
Application Number: 10/985,316