High reflectivity p-contacts for group lll-nitride light emitting diodes

Abstract

A flip-chip LED device (10) includes a plurality of group III-nitride semiconductor layers (22) defining a p/n junction and including a top p-type group III-nitride layer (28), and a p-contact (30, 30′, 30″) for flip-chip bonding the top p-type group III-nitride layer. The p-contact includes an aluminum layer (32) disposed on the top p-type group III-nitride layer (28), and an interface layer (40, 66, 72, 80) disposed between the aluminum layer and the top p-type group III-nitride layer. The interface layer reduces a contact resistance between the aluminum layer (32) and the top p-type group III-nitride layer (28). The interface layer comprises one or more group III-nitride layers.

Description

This application is a divisional of prior application Ser. No. 10/819,740, filed Apr. 7, 2004. Prior application Ser. No. 10/819,740 is incorporated herein by reference in its entirety.

BACKGROUND

The following relates to the lighting arts. It especially relates to flip-chip bonded group III-nitride light emitting diodes for lighting applications, and will be described with particular reference thereto. However, the following also finds application in conjunction with other types of group III-nitride light emitting diodes, and in other group III-nitride optoelectronic devices such as vertical cavity surface emitting lasers (VCSELs).

In the flip-chip mounting configuration, a light emitting diode with a light-transmissive substrate is bonded “face down” to bonding bumps of a mount, that is, with the epitaxial layers proximate to the mount and the light-transmissive substrate distal from the mount, to make electrical and mechanical connection to the mount. The flip-chip arrangement has a number of advantages, including improved thermal heat sinking due to the proximity of the front-side active layers to the heat sinking mount, and elimination of electrode shadowing losses.

In the case of group III-nitride light emitting devices, formation of an economical and robust p-type electrode that has good electrical and reflection properties is difficult. Aluminum has the advantage of being highly reflective; however, aluminum has a low work function and a large contact resistance with respect to p-type gallium nitride.

A nickel layer is sometimes inserted between the p-type gallium nitride and the aluminum to improve electrical characteristics. While having good electrical characteristics, such nickel/aluminum contacts still exhibit less than ideal reflectance characteristics due to light absorption in the nickel.

It is also known to employ silver in contacting p-type gallium nitride. However, silver is more expensive, and exhibits poor adhesion to p-type gallium nitride. Moreover, silver migration can occur-under certain operating conditions. The migrating silver can short the p/n junction, causing catastrophic failure of the device.

The present invention provides a new p-contact and method for making a p-contact that overcomes the above-referenced problems and others.

BRIEF SUMMARY

In accordance with one aspect of the present application, a flip-chip LED device comprises a plurality of group III-nitride semiconductor layers defining a p/n junction and including a top p-type group III-nitride layer, and a p-contact for flip-chip bonding the top p-type group III-nitride layer. The p-contact includes an aluminum layer disposed on the top p-type group III-nitride layer, and an interface layer disposed between the aluminum layer and the top p-type group III-nitride layer. The interface layer reduces a contact resistance between the aluminum layer and the top p-type group III-nitride layer. The interface layer comprises one or more group III-nitride layers.

In accordance with another aspect of the present application, a method is provided for forming a p-contact on a top p-type group III-nitride layer of a flip-chip LED device. An interface layer is formed on the top p-type group III-nitride layer. An aluminum layer is formed on the interface layer. The interface layer reduces a contact resistance between the aluminum layer and the top p-type group III-nitride layer.

In accordance with yet another aspect of the present application, a method is provided for forming a p-contact on a top p-type group III-nitride layer of a flip-chip LED device. The top p-type group III-nitride layer is exposed to hydrochloric acid. Subsequent to the exposing to hydrochloric acid, the top p-type group III-nitride layer is exposed to a piranha solution. Subsequent to the exposing to the piranha solution, an aluminum layer is disposed on the top p-type group III-nitride layer.

Numerous advantages and benefits of the present application will become apparent to those of ordinary skill in the art upon reading and understanding the present specification.

BRIEF DESCRIPTION OF THE DRAWINGS

The application may take form in various components and arrangements of components, and in various process operations and arrangements of process operations. The drawings are only for purposes of illustrating preferred embodiments and are not to be construed as limiting the application.

FIG. 1 shows a cross-sectional view of a flip-chip light emitting diode including an improved p-contact.

FIG. 2 shows a cross-sectional view of another embodiment of a p-contact which employs a tunnel junction.

FIG. 3 shows a cross-sectional view of yet another embodiment of a p-contact which employs an interposed p-InGaN layer.

FIG. 4 compares measurements of brightness of white LEDs fabricated with nickel/aluminum based contacts (left hand side) with white LEDs fabricated from the same epitaxial wafer with aluminum contacts but otherwise similar device fabrication processing (right hand side).

FIG. 5 compares measurements of the device voltage of white LEDs fabricated with nickel/aluminum based contacts (left hand side) with white LEDs fabricated from the same epitaxial wafer with aluminum contacts but otherwise similar device fabrication processing (right hand side).

DETAILED DESCRIPTION

With reference to FIG. 1, a flip-chip light emitting diode device 10 includes a light emitting diode die 12 mounted in a flip-chip fashion to a mount 14. The light emitting diode die 12 includes a light-transmissive substrate 20, which is, preferably, a substantially transparent sapphire or silicon carbide substrate. A plurality of semiconductor layers 22 are formed on the light-transmissive substrate 20 by metalorganic chemical vapor deposition (also referred to as organometallic vapor phase epitaxy and similar nomenclatures), molecular beam epitaxy, chemical beam epitaxy, or another epitaxial film deposition technique. The semiconductor layers 22 are selected from the group III-nitride layers such as GaN layers, AlN layers, InN layers, and ternary and quaternary alloys thereof. In some embodiments, the substrate is used as an epitaxy template for forming the semiconductor layers 22 and is subsequently thinned or removed in the final device. In such embodiments where the substrate is ultimately thinned or removed, the substrate can be opaque.

The semiconductor layers 22 define a light emitting structure that emits light when electrically energized. Typically, the semiconductor layers 22 include an n-type group III-nitride layer 24, such as an n-type GaN layer or aluminum gallium nitride (AlGaN) layer, an active region 26, and a top p-type group III-nitride layer 28, which is typically made of gallium nitride or a aluminum gallium nitride. Preferably, the active region 26 includes a single layer of InN, GaN, In_xGa_1-xN (0<x<1) or the like. Optionally, the active region 26 includes a plurality of layers defining, for example, a single- or multiple-quantum well or superlattice active region. A group III-nitride-based structure typically emits light in the blue to ultraviolet spectral range, with the specific emission spectrum dependent upon the layer compositions, thicknesses, presence of certain impurities, and other features. Optionally, the semiconductor layers 22 include additional layers, such as Al_xGa_1-xN cladding layers, a current-spreading layer, a buffer layer for promoting epitaxial growth, or the like. Optionally, the device die is another type of optoelectronic device, such as a vertical cavity surface emitting laser (VCSEL).

With continuing reference to FIG. 1, at least one p-electrode or p-contact 30 is formed on the top p-type group III-nitride layer 28. The p-contact 30 is generally a multiple layer stack, including an aluminum layer 32 and a bonding stack 34. The layers 32, 34 are deposited in a single deposition process or in multiple deposition processes. Substantially any suitable thin film deposition technique or combination of techniques, such as thermal evaporation, electron beam evaporation, sputtering, electroplating, or the like can be employed. Additionally, an n-type contact 36 is defined and the device is optionally protected with a dielectric layer (not shown) having windows through which the electrodes 30, 36 are exposed.

Typically, the top p-type group III-nitride layer 28 is a p-GaN layer, a p-AlGaN layer, or another relatively large-bandgap group III-nitride material. In one fabrication process, the semiconductor layers 22 are lithographically processed to remove portions of the active region 26 and the top p-type group III-nitride layer 28 to define device mesas, and the contact electrodes 30, 36 are formed. Aluminum has a relatively low work function, and forms a relatively high resistance contact to the top p-type group III-nitride layer 28.

The inventor has found that a surface preparation process involving exposure to hydrochloric acid (HCl) followed by exposure to a piranha solution reduces the high resistance of the aluminum/p-group III-nitride. A piranha solution is a solution of sulfuric acid, hydrogen peroxide, and optionally deionized water. In one specific embodiment, the surface preparation of the top p-type group III-nitride layer 28 includes: (i) a 10 minute exposure to pure hydrochloric acid (HCl) at 50° C. and a rinse in deionized water (DI); followed by (ii) a 2 minute exposure to a 10:1:1 sulfuric acid:hydrogen peroxide:water piranha solution. The exposure to the piranha solution is performed at room temperature; however, exothermic reactions during the exposure generally produce some heating. After exposure to the piranha solution, the surface of the top p-type group III-nitride layer 28 is again rinsed in DI. The HCl/piranha surface preparation of the top p-type group III-nitride layer results in a reduced contact resistance of the p-contact 30.

Without limiting the invention to any particular scientific theory of operation, it is believed that the HCl/piranha processing produces a modification of the surface of the top p-type group III-nitride layer 28 to form an interface layer 40 between the top p-type group III-nitride layer 28 and the aluminum layer 32 which reduces the electrical barrier between the top p-type group III-nitride layer 28 and the subsequently deposited aluminum 32. It is believed that this modified surface may involve more pure (i.e., less contaminated) surface of the top p-type group III-nitride layer 28, or may involve a chemical or structural modification of the surface of the top p-type group III-nitride layer 28. It is to be appreciated that while the interface layer 40 comprises one or more group III-nitride layers, those layers may be as thin as a few monolayers, may represent a more clean group III-nitride interface layer than is achieved without the HCl/piranha surface preparation, or may represent a roughened or otherwise structurally modified group III-nitride/aluminum interface layer.

With continuing reference to FIG. 1, the bonding stack 34 is preferably a multiple layer metal stack, including an adhesion layer 50, a diffusion-blocking layer 52, and a bonding layer 54. In one embodiment, the adhesion layer 50 is titanium, while the bonding layer 54 is gold, which provides a good bonding surface for a variety of bonding methods. For thermosonic bonding, thermocompression bonding, or the like, the diffusion-blocking layer 52 is preferably a platinum layer. For solder bonding, the diffusion-blocking layer 52 is preferably nickel. Of course, it is also contemplated that the bonding stack 34 might be a single layer, two layers, or more than three layers, which might include one or more materials such as gold, titanium, nickel, platinum, or other. Moreover, for certain types of bonding the aluminum layer 32 may provide a good bonding surface, in which cases the bonding stack 34 may be omitted.

The flip-chip light-emitting diode die 12 is bonded to bonding pads 56, 58 that laterally align with the contacts 30, 36. The bonding is performed by one or more solder bumps 60, 62, by thermosonic bonding to gold-coated copper bumps, or the like. Optionally, the bonding bump 60 that secures the p-type electrode 30 is an array of bonding bumps laterally distributed to conform to the area of the p-type contact 30.

With reference to FIG. 2, in another embodiment of the p-contact 30′, the semiconductor layers 22 include a tunnel junction 66 deposited on the top p-type group III-nitride layer 28 during the growth of the semiconductor layers 22. The tunnel junction includes a degenerately doped p-type group III-nitride layer 68 deposited on the p-type group III-nitride layer 28 and a degenerately doped n-type layer 70 deposited on the degenerately doped p-type group III-nitride layer 68. These degenerately doped layers 68, 70 are preferably gallium nitride layers, although some indium can also be alloyed in to form lower bandgap indium gallium nitride degenerate layers. To promote tunneling, the tunnel junction 66 is preferably thin, such as a few nanometers thickness or less for each degenerate layer 68, 70. Hence, some increased light absorption due to indium alloying may be acceptable. An n-type group III-nitride layer 72 is deposited on the tunnel junction 66, and the aluminum layer 32 is formed on the n-type gallium nitride layer 72. The bonding stack 34 is optionally formed on the aluminum layer 32 as before. Typically, the n-type group III-nitride layer 72 is an n-GaN layer. Alloying aluminum into the n-type group III-nitride layer 72 to form AlGaN reduces optical absorption in the layer, but increases the bandgap which can degrade the quality of the electrical contact. Alloying indium into the n-type group III-nitride layer 72 to form InGaN increases optical absorption in the layer, but advantageously decreases the bandgap which generally improves the quality of the electrical contact.

The p-contact 30′ operates as follows. The tunnel junction 66 provides non-rectifying and preferably quasi-ohmic electrical communication between the top p-type group III-nitride layer 28 and the n-type gallium nitride layer 72. As a consequence of the low work function of aluminum, the contact resistance between the aluminum layer 32 and the n-type gallium nitride layer 72 is relatively low, and so the overall p-contact 30′ exhibits improved electrical characteristics.

With reference to FIG. 3, in yet another embodiment of the p-contact 30″, the semiconductor layers 22 include a p-type indium gallium nitride (InGaN) layer 80 deposited on the top p-type group III-nitride layer 28 during the growth of the semiconductor layers 22. To minimize light absorption in the lower bandgap p-type InGaN layer 80, the layer 80 is preferably kept thin, such as a few nanometers or tens of nanometers thick. The aluminum layer 32 is formed on the p-type InGaN layer 80. The bonding stack 34 is optionally formed on the aluminum layer 32 as before.

The p-contact 30″ operates as follows. The low bandgap InGaN 80 reduces the electrical barrier between the InGaN 80 and the aluminum layer 32 versus direct deposition of the aluminum on gallium nitride. The reduced barrier provides more quasi-ohmic electrical communication between the top p-type group III-nitride layer 28 and the aluminum layer 32, and so the overall p-contact 30″ exhibits improved electrical characteristics.

In either p-contact 30′, 30″, the HCl/piranha surface processing is optionally applied prior to forming the aluminum layer 32, to further improve electrical characteristics of the p-contact.

With reference to FIGS. 4-5, white LED lamps having traditional nickel/aluminum based p-contacts are experimentally compared with LED lamps in which the nickel/aluminum based p-contact was replaced with the aluminum based p-contact 30. The devices with nickel/aluminum and aluminum p-contacts were fabricated from dice cleaved from the same epitaxial wafer having blue light-emitting epitaxial layers, using identical fabrication processes except for the p-contact fabrication. The dice were similarly mounted, epoxy-encapsulated, and phosphorized using a yellow phosphor that converts some of the blue electroluminescence into yellow light to approximate white light.

As shown in FIG. 4, the brightness of the white LED was increased by 50% by replacing the nickel/aluminum p-contact with the aluminum p-contact. As shown in FIG. 5, the HCl/piranha surface processing limits the increase in the device forward voltage due to electrical resistance to about 0.3V. Overall, the luminous efficiency (output lumens/input electrical power) increased on average by 34%.

The preferred embodiments have been described. Obviously, modifications and alterations will occur to others upon reading and understanding the preceding detailed description. It is intended that the application be construed as including all such modifications and alterations insofar as they come within the scope of the appended claims or the equivalents thereof.

Claims

1. A flip-chip LED device comprising:

a plurality of group III-nitride semiconductor layers defining a p/n junction and including a top p-type group III-nitride layer; and

a p-contact for flip-chip bonding the top p-type group III-nitride layer, the p-contact including:

an aluminum layer disposed on the top p-type group III-nitride layer, and

an interface layer disposed between the aluminum layer and the top p-type group III-nitride layer and reducing a contact resistance therebetween, the interface layer comprising one or more group III-nitride layers.

2. The flip-chip LED device as set forth in claim 1, wherein the p-contact further comprises:

a bonding stack including at least one layer disposed adjacent to the aluminum layer, the bonding stack being adapted for flip-chip bonding the flip-chip LED device to an associated bonding pad.

3. The flip-chip LED device as set forth in claim 1, wherein the interface layer of the p-contact is formed by a process comprising:

exposing the top p-type group III-nitride layer to hydrochloric acid; and

subsequent to the exposing to hydrochloric acid, exposing the top p-type group III-nitride layer to a piranha solution.

4. The flip-chip LED device as set forth in claim 1, wherein the top p-type group III-nitride layer is a p-GaN layer, and the interface layer of the p-contact comprises:

a p-InGaN layer.

5. The flip-chip LED device as set forth in claim 1, wherein the interface layer of the p-contact comprises:

a tunnel junction.

6. The flip-chip LED device as set forth in claim 5, wherein the interface layer of the p-contact further comprises:

an n-type group III-nitride layer disposed between the tunnel junction and the aluminum layer of the p-contact.

7. The flip-chip LED device as set forth in claim 1, wherein the interface layer of the p-contact comprises:

a degenerately doped p-type group III-nitride layer adjacent the top p-type group III-nitride layer; and

a degenerately doped n-type group III-nitride layer adjacent the degenerately doped p-type group III-nitride layer.

8. The flip-chip LED device as set forth in claim 7, wherein the interface layer of the p-contact further comprises:

an n-type group III-nitride layer adjacent the degenerately doped n-type group III-nitride layer.