Gloves with enhanced anti-cuff-slip surface
An elastomeric article encompassing an enclosure with an interior surface having at least two regions or zones is described. The first region has a higher coefficient of friction than the second region, in which an average coefficient of friction (COF) ratio between the first and second regions of the wearer-contact surface ranges from about 1:1.2 to about 1:3.8 or 4.0. The first region has either the same or smaller surface area than the second region, and is situated at or near an opening to the enclosure. The second region is coated with a hydrogel-based donning layer. A process of making the elastomeric article is also provided. Examples of elastomeric articles according to the invention include surgeons' gloves that exhibit good lubricity and donning characteristics, and have an improved cuff-slippage control.
Latest Patents:
The present invention relates to elastomeric articles. In particular, the invention relates to certain work, medical, or surgical gloves that have a modified surface, which reduces cuff-slip down, for enhanced protection of wearers.
BACKGROUNDTight-fitting elastomeric articles, such as examination, medical, or surgical gloves, are usually made from either natural rubber or synthetic latex materials. Typically, such natural or synthetic latex materials are tacky and have a high coefficient of friction. This does not allow for easy introduction of a hand into the glove. Hence, some sort of surface treatment is required on the inner surface of the glove to facilitate donning, which may also involve lubricating the interior surface to enable ease of donning by a wearer because of undue clinging or friction between the surface of the article and that of the wear's skin. Traditionally, powdered lubricants have been applied to the inside surface of the glove to reduce friction between the skin and the glove. Unfortunately, the use of powdered lubricants may not be appropriate for specific situations, such as the case of surgical gloves. Specifically, if some of the powder escapes from the inside of the glove into the surgical environment, as for example if the glove is torn during the surgery, the powder may enter the surgical wound and cause further complications for the patient.
As a result, other solutions have been developed to aid in the donning of elastomeric gloves. Polymeric lubricant coatings have been developed to modify the interior surface of the gloves in an effort to provide a safe and effective donning for medical practitioners. To date, the surface modification coating that has had the best success and that is most accepted is a hydrogel polymeric coating.
Several kinds and ways of applying lubricating coatings, such as silicones or hydrogels, have been developed in the past; many with great success at alleviating the problem of donning. Coating the inner surface of elastomeric gloves with lubricant or donning layers, however, is believed to have unintentionally aggravated the tendency of the cuff regions of gloves to slip or roll down along the wrist during use. The problem is particularly burdensome with surgical gloves, in view of the critical nature of the surgeon's activities, and also in view of the danger that sterile field on the gloves may be compromised by attempts to re-roll the glove backup along the surgeon's arm. Surgical gloves currently on the market experience significant cuff slippage during use.
Attempts that solving the glove-cuff slippage problem have traditionally focused on changing the physical shape or design of the glove. For instance, some commercially available gloves are provided with relatively thick, circumferential or longitudinal bands, ribs, fluting, or beaded cuffs, in an attempt to minimize cuff roll-down. Alternatively, others have suggested applying an adhesive strip to inside of the cuff, and still others have suggested employing rather cumbersome straps and pegs to secure the cuff tightly to the wear's wrist and forearm. Some manufactures have remedied this issue by narrowing the diameter of gloves at the cuff opening or its immediate area, which has resulted in more constrictive force on the arms producing discomfort and often a compression band on the skin. Hence, these efforts have not been very successful.
A need exists for a better alternative that does not constrict the glove cuff, nor substantially change the gross physical configuration of the glove from designs which medical, surgical, or laboratory workers have become accustomed. The present invention satisfies this need and can provide such an alternative.
SUMMARY OF THE INVENTIONThe present invention pertains to the development of elastomeric articles, such as medical, surgical, or work gloves, that have a natural rubber latex or synthetic polymer latex substrate with a final interior surface that is differentiated into at least two major zones or regions, each with a different surface characteristic. At least one zone, a first region, of the elastomeric article is directed to achieving improved anti-slip or anti-roll-down characteristics when worn by a user against fabric or skin. To the extent that this first region of a glove has anti-slip properties, the surface of the glove is modified to have a higher coefficient of friction (COF) relative to the other, second region. In some embodiments, the higher COF may be achieved by either providing a more tacky surface in the first region or generating a slicker surface in the second region, each of which may involve the application or removal of a coating, such as of a hydrogel or other lubricating cover, to the respective zone. According to certain embodiments, the surface of the first region can be left substantially bare of any coating. That is, the elastomeric material (e.g., natural rubber or synthetic polymer) surface is exposed, or the region can be coated with a layer of adhesive or tackifying material (e.g., rubber cement). The difference in relative coefficient of friction helps prevent the glove from slipping down off of a sleeve of a surgical gown or other garment surface. Hence, the anti-slip first region preferably should be situated at or near the cuff portion of the glove. The difference in relative coefficients of friction between the two regions or zones of the inner, wearer-contacting surface can be expresses as a ratio in a range of at least about 1:1.2, up to about 4.5, more typically about 1:1.3 to about 1:3.8, preferably, about 1:1.4 to about 1:3.35. The first region, depending on the physical dimensions or size of the glove, can cover a distance or width that extends inwardly, from the terminal edge of the glove cuff, about 1 inch (2 cm) to about 5 or 6 inches (˜12-13 cm), and around laterally over a surface area that encompasses the entire periphery of the cuff area.
Just as the first region of the glove, absent a slick coating, will exhibit a relatively more tacky surface, it is envisioned that the second region of the glove includes a donning layer, such as a hydrogel or lubricating silicone layer, which will exhibit a low friction, sleek surface. This may be accomplish in the second region through application of a variety of different kinds of donning coatings that, for example, may either completely or partially cover the surface to assist donning requirements.
In another aspect, the present invention also pertains to an online method of fabricating an elastomeric article having a surface with differentiated coefficients of friction. That is, one can create the different surfaces while the elastomeric article is still on its mould, according to a dipped-goods technique. The method encompasses: forming or providing a natural or synthetic rubber latex substrate; subjecting the latex substrate to a first water leach; applying an aqueous AlSO4-containing solution to a surface of the latex substrate; applying a donning coating over a part of the AlSO4-coated surface, such that a region of about at least 1 inch (˜2.5 cm) from a terminal edge of the latex substrate remains uncoated with the donning coating. After the donning coating is dried and cured, second layer of AlSO4 is applied over the donning coating, followed by at least a second water leach. This application seals the donning coating, and prepared the coated latex substrate surface for exposure to a dilute solution of an oxidizing agent under alkaline conditions of about pH 9-11. The oxidizing agent can be a hypochlorite (e.g., NaOCl) solution, which is adapted to impart a sleek or smooth finish to the donning coating.
Additional features and advantageous of the present invention will be revealed in the following detailed description. Both the foregoing summary and the following detailed description and examples are merely representative of the invention, and are intended to provide an overview for understanding the invention as claimed.
BRIEF DESCRIPTION OF FIGURES
In general the present invention is directed to an elastomeric article. As used herein, the term “elastomeric article” refers to an article formed predominantly from an elastic or elastomeric polymer latex. An “elastomeric polymer” refers to a polymeric or rubber latex material that is capable of being stretched or expanded, and upon release of the stretching or expanding force, will return to substantially (e.g., ±5%) its previous size and configuration. An article according to the present invention, for example, may include clean-room, surgical, work, and/or industrial gloves, that general exhibit a tendency to slip down over time when worn or used. Hence, the present invention is adapted to combat this problem, by providing, in part, a glove with at least two zones on its inner surface with differentiated surface characteristics. One of the zones is adapted to prevent slippage of the article when in contact with either human skin, or a fabric material by engaging with the skin or fabric material.
In the present invention, as a general observation an inner surface of a glove that has a higher coefficient of friction is more desirable because of friction to retain the glove against the material of a garment. Yet, this observation has caveats that were surprisingly unexpected. Gloves, especially surgeon's gloves, should not restrict the natural movement and flex of a wearer's hands and wrist. Hence, the glove should not be too stiff and the coefficient of friction ratio should not be too large. In our experience, generally, a COF ratio that exceeds about 1:4.0 or 4.1 can overly restrict the ability of the user to freely move and flex the user's hands and wrists. Further, a high COF will hinder the ability of the wearer to easily don the glove, especially under damp-skin conditions. The wear's hand will catch against the high friction surface of the cuff region. To strike a balance between maintaining a natural feel, without binding the movement of hands and wrists, and better donning, while preventing the glove-cuff from slipping down, an optimized range for the COF ratio is between about 1:1.4 up to about 1:3.4 or 3.5, preferably about 1:2.0-3.0.
As depicted in
According to the present invention, the donning coat covers only partially the interior surface of a glove. That is, in an embodiment, a region of one to several inches (e.g., 1-5 or 6 inches) at or about the cuff portion of a glove is left free of a hydrogel coating, which covers the hand-donning portion around and/or below the wrist to the finger tips. The area of rubber film without hydrogel coating provides a tacky surface to adhere to gown fabric and this prevents the glove from slipping under normal use by the wearer. The tacky surface may also provide a seal against fluids draining under and into the glove, and afford more protection to the user. This is more easily illustrated, as shown in
In another aspect, the present invention pertains in part to fabrication of elastomeric gloves according to either a post formation tumbling process or an online process for increasing the relative difference in coefficient of friction of the cuff portion and hand-donning portion of an elastomeric glove. The term “online process” refers to a mechanically automatable or automation-friendly course of production, in which gloves do not need to be removed from their moulds during the manufacture and treatment steps. An elastic glove, is customarily fabricated by dipping processes, which, typically, involve the use of a hand-shaped mould, also known as a former. According to either approach of the method, a hand-shaped former, is first dipped in a coagulant solution bath to coat the mould. The mould can be composed of a variety of materials, such as either metal or ceramics, and can have a roughened or textured surface, or a smooth surface. The coagulant is allowed to dry before dipping the mould into an emulsion of a natural rubber or synthetic polymer latex, which is applied to cover the mould. The mould dwells in the latex for a short time period, about 1-5 minutes, to deposit a film layer of predetermined thickness. The latex film is allowed to partially dry. A bead may be formed at the terminal edge of the latex film. The latex film is soaked in hot water at about 40-80° C. to leach out impurities. The leached latex film, while still on the former, is then either sprayed with or dipped into a dilute solution of AlSO4 (e.g., ActiveBond™ by Delta Polymer, Inc.) with a total solids content of about 0.2-3.5%, desirably about 2-3%, to apply a uniform layer to the latex substrate surface. Afterwards, the glove is dried at a temperature in a range of about 60-150° C., preferably about 100-140° C.
In some embodiments, a hydrogel-based donning coat is applied to the dried latex film to cover the portion of the glove that will be in contact with the hand. AlSO4, it is believed, acts as a gelling coagulant for the hydrogel polymer and to enhance its attachment to the rubber substrate of the glove. Examples of possible suitable hydrogel polymer coatings are described in various references, such as U.S. Pat. Nos. 4,548,844 and 4,575,476. both to Podell et al., and U.S. Pat. No. 4,499,154 to James et al. all disclose gloves with a continuous inner layer of such hydrogel polymers; or U.S. patent application Ser. Nos. 10/978,343, and 11/023,743. The hydrogel solution can be about 1-5% total solids contect (TSC). The hydrogel layer is allowed only to cover part of the original latex surface. The hydrogel dip is maintained at a level that is at least 1-2 inches below the upper terminal edge or bead of the glove cuff. Preferably, the dip-level is lower by about 3-6 inches, depending on the overall length and configuration of the glove. That is, a glove with a longer cuff region desirably will have a proportionately larger area that is left uncoated with the hydrogel polymer. After the hydrogel coating is applied to the glove surface, a second layer of AlSO4 is applied over the hydrogel layer. It is believed that this second layer provides an acidic surface to the hydrogel layer.
To control self-blocking or sticking of the latex substrate to itself and to facilitate stripping of the glove from its mould, one applies a layer or coating of a fine powdered release agent, such as calcium or magnesium carbonate (CaCO3, MgCO3)), magnesium or zinc stearate (Mg(C18H35O2)2, Zn(C18H35O2)2), from a slurry dip over the entire glove to serve as an inorganic release agent.
Another way to obtain differentiation on a rubber surface (i.e., to achieve a two-zone effect without hydrogel coating) involves treating only part of the inner surface. That is, to partially chlorinate part of the donning side, and the area of the inner surface that is left un-chlorinated is treated with a silicone lubricant to generate a higher COF than the chlorinated surface.
In contrast to current, conventional processes that use gaseous chlorine at acidic pH levels to halogenate the hydrogel layer, an attribute of the present invention involves exposing the gloves, while still on the former, to bath of an alkaline solution of an oxidizing agent, such as sodium hypochlorite bleach. The solution will have a pH ≧8 or 9. It is believed that the hypochlorite works as a dilute chlorinating agent for the hydrogel coating and uncoated rubber surface, and imparts a sleek finish to the hydrogel coating for improved donning properties. In other words, sodium hypochlorite is used as a processing aid to create a smoother and sleeker hydrogel coating for easier donning characteristics. This process step involves no chlorine gas to enhance the relative smoothness of the coated surface for better donning characteristics and relatively lower coefficient of friction. Further, when processing online, with the donning layer exposed to out side, the sodium hypochlorite modifies only the donning side and one can avoid exposing the gripping region or outer surface of the glove. In other words, as the glove is still on the former, one can easily control the area and size of glove surface that is exposed to chlorine by controlling to what level or how far the glove substrate is submerged into the bleach solution. The hypochlorite coated area can be coterminous with the hydrogel coated region Further the present process will provide precise control at level of chlorination needed to facilitate the donning requiring. The present online process will improve, batch to batch, the consistency of the halogenation process compared to current process using gas and off line process. After at least a second aqueous leaching, which removes most of the second AlSO4 application and powdered release agents, the glove is dried and cured at temperatures in a range of about 90-150° C. for about 20-40 minutes.
Afterwards, the method may further comprising stripping the latex substrate from a mould, inverting the latex substrate, and applying a lubricating layer over the outside of the glove in an off-line processing. A lubricating layer formed from a silicone, such as a polydimethyl siloxane emulsion, can be applied at about 0.1-1.3 or 1.5 weight percent in an aqueous tumble inversion-rinse. Desirably, the silicone emulsion is applied to the glove in an amount of about 0.2-0.25% by vol. (˜0.080-0.150% by wt.). In some embodiments, the silicone emulsion may have a total solids content (TSC) of not less than about 20% and up to about 60%. An example of a desirable silicone emulsion is a pre-emulsified formulation known as DC 365 (35% TSC), available commercially from Dow Corning Corporation (Midland, Mich.). DC 365 is believed to contain about 40-70 mass % water, about 30-60 mass % methyl-modified polydimethylsiloxane, and about 1-5 mass % octylphenoxy polyethoxy ethanol. Other examples of pre-emulsified silicone formulations that may be suitable for use with the present invention are available commercially from GE silicones (Waterford, N.Y.) under the trade names SM 2140 (50% TSC), SM 2169, and AF-60. SM 2140 is believed to contain about 30-60 mass % water, about 30-60 mass % amino-modified polydimethylsiloxane, about 1-5% mass % trimethyl-4-nonyloxypolyethyleneoxy ethanol, and minor percentages of acetaldehyde, formaldehyde, and 1,4 dioxane. SM 2169 is believed to contain about 30-60 mass % water, about 60-80 mass % polydimethylsiloxane, about 1-5 mass % polyoxyethylene lauryl ether, and a small amount of formaldehyde. AF-60 is believed to contain polydimethylsiloxane, acetylaldehyde, and small percentages of emulsifiers. If desired, these pre-emulsified silicones may be diluted with water or other solvents prior to use.
Silicone emulsions function as a lubricant on polymer-coated surfaces, but on surfaces not coated with polymer, the silicone emulsion enhances overall tackiness. Hence, the polymer-coated sections of the glove become even more slick, which is good for donning, while the areas of the substrate where there is no polymer coating the silicone emulsion provides a desired grip level, such that the inner surface of the glove will adhere to a gown material when worn. The silicone emulsion is applied to both hydrogel-coated and non-coated areas of the glove substrate.
After the glove has been stripped from its mould, the latex substrate may be further subject to a series of at least two consecutive rinses with heated water (˜27° C. or 30-40-88° C.). In so-called backend processing operations, the glove is treated with an effective amount of chlorine to halogenated the gripping side. A chlorine-containing aqueous solution (at ˜30-75 ppm) can be used to process the grip side of the glove, followed with wash in a dilute hydrochloric acid (HCl) solution (about 0.1-0.85% by volume, desirable about 0.2 or 0.25-0.37%) to remove any release agent power that may remain after the water rinses. HCl dissolves the CaCO3 to produce a salt, which is then washed away by water to produce a powder-free product.
Alternatively, a batch of gloves can be tumbled in softened or deionized water as a pre-rinse. We envision, according to another aspect of the invention, a one-step treatment involving exposing the gloves to a combined mixture containing HCl+chlorine+silicone emulsion in either a bath or atomizing stray in a tumble process. The combined HCl-chlorine-silicone treatment can produce in one step several different surface effects, which ordinarily would require several different process steps. The silicone attaches to the non-polymer coated surface and the chlorine attaches to the partial polymer-coated areas of the glove, and the HCl helps remove excess CaCO3 powder that may be present. Then, the gloves are again rinsed two times in softened water, followed by rinse four times in deionized water. The batch of gloves is then dried at about 70° C. to about 80° C.
The chlorine and HCl treatment is believed to impart a smooth and sleek finish, enhancing the donning properties of the hydrogel-coated rubber surface. Generally, the higher the percentage chlorine content, the slicker the finished rubber surface becomes with an attending reduction in COF. Subsequently, one may further immerse and tumble rinse the glove for an additional third or fourth time to remove either powder residues or latex proteins in natural rubber-based gloves. Further, one may rinse up to an additional two more times in deionized water baths. Finally, another layer of silicone emulsion (e.g., DC 365) is applied in aqueous treatment via a tumble inversion-rinse, and the glove is dried.
When comparing the two versions of the present process treatment, the online approach tends to produce more consistent results, hence it is a more cost-effective and desirable process than the tumble approach.
EXAMPLES Example 1According to the online process the hand-shaped former is dipped in a coagulant bath to coat the mould. A natural or synthetic rubber latex is applied by dipping into a bath and partial dried on the mould. A bead may be formed at the cuff. While the latex substrate is on the former, the glove is subject to a first water leach. An AlSO4 (e.g., Active Bond™) solution (˜1%) is applied by either spraying or dipping of the glove into an aqueous bath for about 1-3 minutes, over the entire surface of the glove, up to and including the glove cuff. AlSO4 functions as a primer that helps enhance subsequent surface modifications. A donning coat, such as a hydrogel or polyurethane layer, is applied over part of the AlSO4-coated surface. The AlSO4 on the surface of the hydrogel layer is unreacted with the hydrogel. Typically, an area with a width of about 1 or 2 inches to up to about 5 or 7 inches (˜2.5-13 or 16 cm), down from the end of the glove cuff or bead, if present, is left uncoated with the donning coat. Preferably, the region left uncoated is about 1-2 inches (˜2.5-5 cm). The donning coated is dried and cured. The glove is subject to a second water leach and dried. The entire glove can then be either immersed in a bath or sprayed with a hypochlorite (NaOCl) solution and dried. Online treatment with NaOCl can simplify the post processing, by removing the chlorination process conventionally performed in tumblers. The water rinse removes the AlSO4 treatment, hence the AlSO4 does not react with the hypochlorite.
According to the present invention, chlorination process takes place under alkaline conditions of pH ˜9-10 or 11, which are gentler and more conducive for online fabrication. Under acidic conditions, the hydrochlorous acid (HOCl) will tend to dissociate and release chlorine gas, which can be quite caustic and harsh, hence not useful in an online process. In our process, it is believed that the NaOCl affects the hydrogel or polyurethane coating only to make it slick for donning. This is done in a dip tank with the online process. The percentage chlorine is present in a range of about 0.2-1.0%. Typically, chlorine is at about 0.3% (3000 ppm of Cl2). The available amount of chlorine in NaOCl is about 6%. According to some embodiments, the effective amount of chlorine is about 6% of 0.3%, or about 0.018%.
The hydrogel coating can be slickened with exposure to an oxidizing agent, such as a solution of sodium hypochlorate, which is desirably applied co-terminus with the hydrogel donning coated region. Afterwards, the cured glove is soaked in hot water at about 40-80° C. for about 0.5 to 3 or 4 minutes. After drying for a few minutes 3-6 minutes, the glove can be dipped in a slurry of calcium carbonate (2-5%) suspended in water. When the slurry is dried, the glove can be removed from the ceramic mould. The stripping and inversion of the glove will make the partial-hydrogel-coated surface to become the interior surface of the glove to facilitate donning.
A suitable silicone emulsion, such as commercially available formulations from Dow Corning (DC 365) or General Electric (AF60) can be applied to increase the coefficient of friction on the uncoated latex surface.
Example 2In an alternate tumbling process, a surgical glove made from an elastic latex can be manufactured by dipping the former into a coagulant solution. As with the previously described steps, a former is coated with a layer of either natural rubber or synthetic latex and allowed to partial dry. A bead may be formed at the end of the latex substrate. A first water leach is applied, followed with a coating of AlSO4 over the entire exposed surface of the latex substrate on the former. A partial hydrogel coating is applied only over the hand and wrist regions of the mould, dried and cured. A band or region of latex is left uncoated. This band can have a width of about 1-6 inches, preferably about 1-2 inches (2.5-5 cm), from the terminal edge or bead, if present. The glove is subjected to a second water leach and dried. The entire glove is then dipped into a CaCO3 slurry, and dried. Afterwards, the glove is stripped from the mould and inverted. The subsequent process steps and chemical treatments are conducted in a tumbling drum, such as in a washing machine. Another coating of AlSO4 is applied in a tumble inversion-rinse over the entire glove and dried. A first treatment with silicone emulsion in water is then applied. After at least two rinses in water, the glove is subject to a rinse in HCL solution, followed by another at least two rinses in softened water, and two more rinses in deionized water. Finally, a second treatment with silicone emulsion is applied and the glove is dried.
Section III—Coefficient of FrictionIt is believed that the modification of the inner surface of a glove, according to the present invention can greatly reduce the tendency for elastomeric gloves to slip when worn, especially when in contact with an article of protective clothing. A portion of the glove, not coated with donning layer, but a tacky surface engages with the material of the protective clothing. As such, one creates a good glove-gown interface region. In other words, due to the combination the silicone emulsion over the latex substrate which generates a higher COF at the cuff region than over the hand-donning region of the glove. The cuff sticks to gown surface and reduces slip down.
Two different tests were utilized in the determination of the coefficient of friction:
(1) Classical Inclined Plane and Weight Method: This test measures coefficient of friction via a determination of the angle at which the test sample, weighted down in a standard manner, slides down an inclined plane. The test is generally described in Principles of Physics, by J. B. Marion et al., chapter 7-1, Saunders College Publishing, New York, N.Y., 1984.
(2) Kawabata Method: This test is described in Standardization Analysis of Hand Evaluation, by Sueo Kawabata; July, 1980, 2nd Edition, pp 31-35, 48-50. As compared to the Classical Method, the Kawabata test is more reliable for measuring the coefficient of friction on rough surfaces or surfaces with small areas. In this method, the test material is moved from left to right while a contacting element (of specific dimensions, and under constant force) touches the surface of the material. A transducer connected to the detector is used to measure frictional force as the test material is moved.
Tests using the Classical Method were repeated five times on each sample to determine mean value. Tests using the Kawabata method were repeated six times: two times for each sample. The Kawabata COF data for two sizes (i.e., 6.5 & 7.5 inches) and 3 measurements of each size for each product sample were taken. The coefficient of friction is determined on the cuff and palm areas of the samples. In the test zone A is defined as the surface of the glove within 1.25 to 2 inches from the cuff edge or bead, and zone B is the surface of the donning areas of the glove, in particular the palm region. Table 1 summaries the mean average values of the Kawabata test results.
The above results clearly demonstrate that gloves produced according to the present processing method exhibit an enhanced friction characteristics as compared to the untreated counterparts. The Kawabata test demonstrated enhanced friction for samples 1, 4, 5, 7, 10, and 11. Since low friction is the fundamental cause of slippage at the cuff-sleeve interface, it appears clear that the increases in the relative COF set forth in Table 1 will provide a reduction in slippage without associated discomfort, such as over-constriction on the forearm, which tend to be associated with anti-slippage schemes that employ compression.
Table 1 also demonstrates that in some instances, relatively low levels of the treatment agent (e.g., samples 3, 12) were effective in significantly reducing the COF. As mentioned above, the use of lower levels is often desirable in view of costs, and in view of the tendency for gloves with high levels of the tackifying agent to sometimes become stiff. As mentioned before for gloves, COF ratios of over about 4.0:1 tend to hinder donning, and overly tether the glove cuff to the user's forearm area and can restrict the free movement or flex of the hands during use. This, however, is not to disclaim the potential advantages of a high COF differential for other applications which may appreciate a surface with a higher coefficient or more tacky grip.
The present invention can be adapted to any base rubber latex material formulation or dipping process. Hence, a variety of products may employ the present technique. Such products may include medical exam, surgical, or work gloves, condoms, as well as any article that may require at least a two zone differentiated surface having a contrast in coefficient of friction, such as for better wearability.
The present invention has been described both in general and in detail by way of examples. Persons skilled in the art will understand that the invention is not limited necessarily to the specific embodiments disclosed. Modifications and variations may be made without departing from the scope of the invention as defined by the following claims or their equivalents, including equivalent components presently known, or to be developed, which may be used within the scope of the present invention. Hence, unless changes otherwise depart from the scope of the invention, the changes should be construed as being included herein.
Claims
1. A flexible article comprising: a substrate body formed largely from an elastomeric material, said substrate body having a first surface and a second surface; said first surface is differentiated into at least a first and a second zone, each zone having a coefficient of friction, such that the coefficient of friction for said first zone is greater than the coefficient for said second zone, according to an average ratio in a range from about 1.2:1 to about 4.5:1 said first zone is absent a donning layer, and said second zone has said donning layer.
2. The elastomeric article according to claim 1, wherein said average coefficient of friction ratio is about 1.4:1 to about 3.8:1 for said first zone to said second zone.
3. The elastomeric article according to claim 2, wherein said average coefficient of friction ratio is about 1:5 to about 2.8:1 for said first zone to said second zone.
4. The elastomeric article according to claim 2, wherein said average coefficient of friction ratio is about 1.6:1 to about 2.5:1 for said first zone to said second zone.
5. The elastomeric article according to claim 1, wherein said first zone has a surface that is a bare elastomeric material or coated with a tackifying material.
6. The elastomeric article according to claim 1, wherein said first region is part of a surface adapted to prevent slippage of said article when in contact with either human skin, or a fabric material.
7. The elastomeric article according to claim 1, wherein aid article is made from either a natural rubber latex or synthetic polymer latex material.
8. An glove comprising: an elastomeric substrate body with an inner surface having a first and a second region, said first region having a higher coefficient of friction relative to said second region, according to a ratio in a range from about 1.2:1 to about 3.5:1, and said second region being either substantially larger or about equal in surface area than said first region, and having at least a partially coating of a donning material layer.
9. The glove according to claim 8, wherein said first zone forms part of a glove cuff.
10. The glove according to claim 8, wherein said second zone forms at least part of a hand-donning portion of said glove.
11. The glove according to claim 8, wherein said inner surface is subject to an oxidizing agent.
12. The glove according to claim 8, wherein said inner surface is subject to a partial halogenation, such that said first region is un-chlorinated and said second regions is chlorinated.
13. The glove according to claim 8, wherein said donning material includes at least one of the following polymeric materials: hydrogel-based polymer, polyurethanes, polyacrylates, polyvinyl alcohol condensation product, poly(styrene-butadiene-styrene) (SBS), or poly(styrene-ethylene-butadiene-styrene) (SEBS).
14. The glove according to claim 8, wherein said first region forms at least part of an inner surface at or about a cuff portion of said glove.
15. The glove according to claim 10, wherein said first region is adapted to exhibit a tendency to retard cuff slippage off of a wearer's wrist or forearm.
16. The glove according to claim 10, wherein said inner surface contacts an article of protective clothing and tends to engage with a material of said protective clothing.
17. The glove according to claim 8, wherein said second region forms at least part of a surface that contacts a wearer's skin.
18. A method of fabricating an elastomeric article having a surface with at least two regions with differentiated coefficients of friction, the method comprises: providing a natural rubber or synthetic polymer latex substrate on a mould; subjecting said latex substrate to a first water leach; applying an aqueous AlSO4-containing solution to a surface of said latex substrate; applying a donning coating over a part of said AlSO4-coated surface, leaving a zone of about at least 1 inch (˜2.2 cm) from a terminal edge of said latex substrate uncoated with said donning coating; drying and curing said donning coating; subjecting said latex substrate to a second water leach; applying a second layer of AlSO4 over said donning coating; and exposing said latex substrate to a dilute solution of an oxidizing agent under alkaline conditions of about pH ≧8.
19. The method according to claim 18, wherein said pH is about 9-11.
20. The method according to claim 18, wherein said donning coating includes a hydrogel material.
21. The method according to claim 18, wherein said oxidizing agent is a hypochlorite (NaOCl) solution.
22. The method according to claim 18, wherein said hypochlorite solution is adapted to impart a sleek finish to said hydrogel material.
23. The method according to claim 18, further comprises applying a coating of powdered release agent to reduce self-blocking of said region absent the donning coating.
24. The method according to claim 18, further comprising stripping said latex substrate from said mould, inverting said latex substrate, and applying a lubricating layer formed from a silicone emulsion.
25. The method according to claim 18, wherein said silicone emulsion imparts either a tackifying effect to said zone absent said donning coating or a slickening effect to said donning coating.
26. The method according to claim 18, further comprising treating said latex substrate to a first and second consecutive rinse with water, and a chlorine-containing water at ˜30-75 ppm vol., and a dilute hydrochloric (HCl) solution of about 0.1-0.85% by volume to remove any remaining powdered release agent after said first and second water rinses.
27. The method according to claim 18, further comprising subjecting said latex substrate to a medium including a combination of HCl+chlorine+silicone emulsion in one process step to achieve tacky a surface on non-donning-material coated surface and a sleek surface on donning material-coated surface.
28. The method according to claim 18, further comprising applying another layer of silicone emulsion treatment.
29. The method according to claim 18, wherein said elastomeric article has at least a first and a second zone on an inner surface, in which said first zone has a relative higher coefficient of friction, according to an average ratio in the range of about 1.4:1 to about 3.5:1.
30. The method according to claim 29, wherein said average ratio of coefficient of friction between first and second regions is about 1.8:1 to about 3.0:1.
Type: Application
Filed: Mar 31, 2005
Publication Date: Oct 5, 2006
Applicant:
Inventors: Shantilal Modha (Alpharetta, GA), Lin-Sun Woon (Alpharetta, GA)
Application Number: 11/094,959
International Classification: A41D 19/00 (20060101);