Corneal mask formed of degradation resistant polymer and providing reduced corneal deposits
Disclosed are masks configured to be implanted in a cornea of a patient. In one embodiment, the body of the mask has a light transmitting portion, a light blocking portion disposed about the light transmitting portion, and an outer periphery surrounding the light blocking portion. The mask is adapted to reside between two intracorneal layers of a cornea. In a preferred embodiment, the mask is formed from a material comprising a highly fluorinated polymeric material and an opacification agent and is resistant to degradation upon exposure to ultraviolet light. In another embodiment, the mask is formed from a material which comprises a polyanionic compound. In some embodiments, the mask includes one or more wound healing modulator compounds to aid in proper healing following implantation.
This application is a continuation-in-part of U.S. patent application Ser. No. 11/106,043, filed Apr. 14, 2005, the disclosure of which is hereby incorporated by reference in its entirety.
BACKGROUND OF THE INVENTION1. Field of the Invention
This application is related to corneal inlay devices. More particularly, this application is directed to corneal inlays that are configured not to degrade over the useful life of the inlay, and that can include one or more compounds to aid in proper healing following implantation and/or include one or more materials which reduce the amount of corneal deposits formed thereon as compared to a mask without such material.
2. Description of the Related Art
A normally functioning human eye is capable of selectively focusing on either near or far objects through a process known as accommodation. Accommodation is achieved by inducing deformation in a lens located inside the eye, which is normally referred to as the “intraocular lens”. Such deformation is induced by muscles called ciliary muscles. As some individuals age, the ability to accommodate diminishes and these individuals cannot see up close without vision correction. If far vision also is deficient, such individuals are prescribed bifocal lenses.
While this approach is sometimes satisfactory, some have proposed implanting devices inside the eye to improve accommodation for older patients. One such implant is a pin-hole imaging device that can be implanted in the cornea of an eye. While this type of device has been discussed in various contexts, and a need for the device has been identified, no such device is currently on the market.
Several factors make a successful device of this type elusive. In particular, the device needs to improve the depth of field of a patient's vision and, because it is surgically implanted, the device has to have a very long life-span. No known device has been proposed that has an adequate life-span.
Because corneal implants are exposed to a great deal of sunlight during their lifetime, resistance to degradation of the polymer due to UV exposure is important. In the contact lens and IOL arts, commercially available stabilizers have been added to the lenses to prevent degradation of the lenses due to this exposure and also to exposure to UV light used as a means of sterilization. Stabilizers dissipate the energy of ultraviolet rays to prevent degradation of the lens material. The stabilizers may be physically combined with the polymer or they may be part of a monomer which is copolymerizable with the polymeric material which forms the lens. Copolymerization reduces extractability, a problem with many stabilizers that are merely physically combined with a polymer.
SUMMARY OF THE INVENTIONNotwithstanding the foregoing, there remains a need for a mask, such as a corneal inlay device, that is sufficiently resistant to degradation of the type described above and for this and other similar applications.
In preferred embodiments, a mask includes a polyanionic compound and/or a wound healing modulator compound. In accordance with a preferred embodiment, there is provided a mask configured to be implanted in a cornea of a patient. The mask comprises a body formed from a polymeric material, the body having a light transmitting portion, a light blocking portion disposed about the light transmitting portion, an anterior surface, and a posterior surface, the anterior surface configured to reside adjacent a first intracorneal layer, the posterior surface configured to reside adjacent a second intracorneal layer, wherein the polymeric material includes one or more polyanionic compounds and/or wound healing modulator compounds, preferably loaded into the polymeric material.
In accordance with a preferred embodiment, there is provided a mask configured to be implanted in a cornea of a patient. The mask comprises a body formed from a material comprising a polymeric material, preferably a highly fluorinated polymeric material, the body having a light transmitting portion, a light blocking portion disposed about the light transmitting portion, an anterior surface, and a posterior surface, the anterior surface configured to reside adjacent a first intracorneal layer, the posterior surface configured to reside adjacent a second intracorneal layer, wherein the material comprising a polymeric material has loaded therein one or more polyanionic compounds. In a preferred embodiment, the total weight of the one or more polyanionic compounds is about 10% to 20% by weight.
The material forming the light blocking portion of the body may be of a type which comprises an opacification agent selected from the group consisting of organic dyes organic pigments, inorganic dyes, and inorganic pigments. In one preferred embodiment, the opacification agent comprises carbon. In a preferred embodiment, the mask includes at least one wound healing modulator compound.
In preferred embodiments, the mask includes an outer periphery surrounding the light blocking portion.
In accordance with a preferred embodiment, there is provided a mask comprising an aperture, preferably having a major axis of about 2.2 mm or less and an annular body extending between the aperture and an outer periphery of the mask. In a preferred embodiment, the annular body has an anterior surface and a posterior surface and is formed of a material comprising a polymeric material, preferably a highly fluorinated polymeric material, an opacification agent, and one or more polyanionic compounds and/or wound healing modulator compounds. The opacification agent is preferably present in sufficient quantity to prevent at least a substantial portion of light incident on the anterior surface from being transmitted from the anterior surface to the posterior surface. In a preferred embodiment, the anterior surface is configured to reside adjacent a first intracorneal layer of a cornea, and the posterior surface is configured to reside adjacent a second intracorneal layer. Other preferred embodiments may include one or more of the following features: a mask which does not substantially alter the curvature of a cornea following application of the mask to a cornea; an annular body that has a substantially constant thickness between the anterior and posterior surfaces, preferably of about 20 microns or less.
In accordance with a preferred embodiment, there is provided a mask configured to be implanted in a cornea of a patient. The mask comprises a body formed from a polymeric material, the body having a light transmitting portion, a light blocking portion disposed about the light transmitting portion, an anterior surface configured to reside adjacent a first intracorneal layer, a posterior surface configured to reside adjacent a second intracorneal layer, and at least one polyanionic compound and/or wound healing modulator. A wound healing modulator, if present, is preferably bound to at least one of the anterior surface and the posterior surface.
Preferred embodiments of the embodiments discussed above may have one or more additional properties. Preferred wound healing modulator compounds include, without limitation, antibiotics, antineoplastics including antimitotics, antimetabolics and antibiotic types, anti-inflammatories, immunosupressants, and antifungals. Preferred compounds include, but are not limited to, fluorouracil, mitomycin C, paclitaxel, NSAIDs (e.g. ibuprofen, naproxen, flurbiprofen, carprofen, suprofen, ketoprofen), and cyclosporins. Other preferred compounds include proteoglycans, glycosaminoglycans, and salts and derivatives thereof, as well as other carbohydrates and/or proteins. The wound healing modulator compound may be loaded into the polymer and/or adsorbed or coated onto at least one surface. In one embodiment, at least a portion of the wound healing modulator compound is adsorbed to a carbon opacification agent. In preferred embodiments, the polymeric material is UV-resistant, and preferably comprises a highly fluorinated polymeric material such as polyvinylidene fluoride (PVDF).
In preferred embodiments, the total weight of the one or more polyanionic compounds is about 0.1% by weight to about 50% by weight, including about 5% by weight to about 20% by weight, about 12% by weight to about 17% by weight, about 0.5% by weight to about 4% by weight, and about 5% by weight to about 15% by weight. Preferred polyanionic compounds include carbohydrates, proteins, natural proteoglycans, and/or the glycosaminoglycan moieties of proteoglycans, as well as derivatives (such as sulfated derivatives) and salts of compounds such as those in the recited categories. Preferred polyanionic compounds include one or more of dermatan sulfate, chondroitin sulfate, keratan sulfate, heparan sulfate, heparin, dextran sulfate, hyaluronic acid, pentosan polysulfate, xanthan, carrageenan, fibronectin, laminin, chondronectin, vitronectin, poly L-lysine salts, and anionic, preferably sulfated, carbohydrates such as alginate may also be used, as well as salts and derivatives of the listed compounds. Examples of preferred anionic compounds and combinations of polyanionic compounds include keratan sulfate/chrondroitin sulfate-proteoglycan, dermatan sulfate proteoglycan, and dextran sulfate.
BRIEF DESCRIPTION OF THE DRAWINGS
This application is directed to masks for improving the depth of focus of an eye of a patient and methods and apparatuses for making such masks. The masks generally employ pin-hole vision correction and have nutrient transport structures in some embodiments. The masks may be applied to the eye in any manner and in any location, e.g., as an implant in the cornea (sometimes referred to as a “corneal inlay”). The masks can also be embodied in or combined with lenses and applied in other regions of the eye, e.g., as or in combination with contact lenses or intraocular lenses. In some applications, discussed further below, the masks are formed of a stable material, e.g., one that can be implanted permanently.
I. Overview of Pin-Hole Vision Correction
As discussed above, mask that has a pinhole aperture may be used to improve the depth of focus of a human eye. As discussed above, presbyopia is a problem of the human eye that commonly occurs in older human adults wherein the ability to focus becomes limited to inadequate range.
The eye 10 also includes a ring of pigmented tissue known as the iris 22. The iris 22 includes smooth muscle for controlling and regulating the size of an opening 24 in the iris 22, which is known as the pupil. An entrance pupil 26 is seen as the image of the iris 22 viewed through the cornea 12 (See
The eye 10 resides in an eye-socket in the skull and is able to rotate therein about a center of rotation 30.
Turning now to
Turning now to
II. Masks Employing Pin-Hole Correction
The mask 34 preferably has a constant thickness, as discussed below. However, in some embodiments, the thickness of the mask may vary between the inner periphery (near the aperture 38) and the outer periphery.
The annular region 36 is at least partially and preferably completely opaque. The opacity of the annular region 36 prevents light from being transmitted through the mask 32 (as generally shown in
For example, in one embodiment, the material used to make mask 34 may be naturally opaque. Alternatively, the material used to make the mask 34 may be substantially clear, but treated with a dye or other pigmentation agent to render region 36 substantially or completely opaque. In still another example, the surface of the mask 34 may be treated physically or chemically (such as by etching) to alter the refractive and transmissive properties of the mask 34 and make it less transmissive to light.
In still another alternative, the surface of the mask 34 may be treated with a particulate deposited thereon. For example, the surface of the mask 34 may be deposited with particulate of titanium, gold or carbon to provide opacity to the surface of the mask 34. In another alternative, the particulate may be encapsulated within the interior of the mask 34, as generally shown in
Turning to
In another embodiment, the mask may be formed from co-extruded rods made of material having different light transmissive properties. The co-extruded rod may then be sliced to provide disks for a plurality of masks, such as those described herein.
Other embodiments employ different ways of controlling the light transmissivity through a mask. For example, the mask may be a gel-filled disk, as shown in
The material of the mask 34 may be any biocompatible polymeric material. Where a gel is used, the material is suitable for holding a gel. Examples of suitable materials for the mask 34 include the preferred polymethylmethacrylate or other suitable polymers, such as polycarbonates and the like. Of course, as indicated above, for non-gel-filled materials, a preferred material may be a fibrous material, such as a Dacron mesh.
The mask 34 may also be made to include a medicinal fluid or material, such as an antibiotic or other wound healing modulator that can be selectively released after application, insertion, or implantation of the mask 34 into the eye of the patient. Release of an antibiotic or other wound healing modulator after application, insertion, or implantation provides faster and/or improved healing of the incision. The mask 34 may also be coated with other desired drugs or antibiotics. For example, it is known that cholesterol deposits can build up on the eye. Accordingly, the mask 34 may be provided with a releasable cholesterol deterring drug. The drug may be coated on the surface of the mask 34 or, in an alternative embodiment, incorporated into the polymeric material (such as PMMA) from which the mask 34 is formed.
Thus, as shown in
Nano-devices or nanites are crystalline structures grown in laboratories. The nanites may be treated such that they are receptive to different stimuli such as light. In accordance with one aspect of the present invention, the nanites can be imparted with energy where, in response to a low light and high light environments, they rotate in the manner described above and generally shown in
Nanoscale devices and systems and their fabrication are described in Smith et al., “Nanofabrication,” Physics Today, February 1990, pp. 24-30 and in Craighead, “Nanoelectromechanical Systems,” Science, Nov. 24, 2000, Vol. 290, pp. 1502-1505, both of which are incorporated by reference herein in their entirety. Tailoring the properties of small-sized particles for optical applications is disclosed in Chen et al. “Diffractive Phase Elements Based on Two-Dimensional Artificial Dielectrics,” Optics Letters, Jan. 15, 1995, Vol. 20, No. 2, pp. 121-123, also incorporated by reference herein in its entirety.
Masks 34 made in accordance with the present invention may be further modified to include other properties.
The masks described herein may be incorporated into the eye of a patient in different ways. For example, as discussed in more detail below in connection with
When used as a corneal implant, layers of the cornea 12 are peeled away to allow insertion of the mask 34. Typically, the optical surgeon (using a laser) cuts away and peels away a flap of the overlying corneal epithelium. The mask 34 is then inserted and the flap is placed back in its original position where, over time, it grows back and seals the eyeball. In some embodiments, the mask 34 is attached or fixed to the eye 10 by support strands 72 and 74 shown in
In certain circumstances, to accommodate the mask 34, the surgeon may be required to remove additional corneal tissue. Thus, in one embodiment, the surgeon may use a laser to peel away additional layers of the cornea 12 to provide a pocket that will accommodate the mask 34. Application of the mask 34 to the cornea 12 of the eye 10 of a patient is described in greater detail in connection with
Removal of the mask 34 may be achieved by simply making an additional incision in the cornea 12, lifting the flap and removing the mask 34. Alternatively, ablation techniques may be used to completely remove the mask 34.
Further mask details are disclosed in U.S. Pat. No. 4,976,732, issued Dec. 11, 1990 and in U.S. patent application Ser. No. 10/854,033, filed May 26, 2004, both of which are incorporated by reference herein in their entirety.
III. Preferred UV-Resistant Polymeric Mask Materials
Because the mask has a very high surface to volume ratio and is exposed to a great deal of sunlight following implantation, the mask preferably comprises a material which has good resistance to degradation, including from exposure to ultraviolet (UV) or other wavelengths of light. Polymers including a UV absorbing component, including those comprising UV absorbing additives or made with UV absorbing monomers (including co-monomers), may be used in forming masks as disclosed herein which are resistant to degradation by UV radiation. Examples of such polymers include, but are not limited to, those described in U.S. Pat. Nos. 4,985,559 and 4,528,311, the disclosures of which are hereby incorporated by reference in their entireties. In a preferred embodiment, the mask comprises a material which itself is resistant to degradation by UV radiation. In one embodiment, the mask comprises a polymeric material which is substantially reflective of or transparent to UV radiation.
Alternatively, the mask may include a component which imparts a degradation resistive effect, or may be provided with a coating, preferably at least on the anterior surface, which imparts degradation resistance. Such components may be included, for example, by blending one or more degradation resistant polymers with one or more other polymers. Such blends may also comprise additives which provide desirable properties, such as UV absorbing materials. In one embodiment, blends preferably comprise a total of about 1-20 wt. %, including about 1-10 wt. %, 5-15 wt. %, and 10-20 wt. % of one or more degradation resistant polymers. In another embodiment, blends preferably comprise a total of about 80-100 wt. %, including about 80-90 wt. %, 85-95 wt. %, and 90-100 wt. % of one or more degradation resistant polymers. In another embodiment, the blend has more equivalent proportions of materials, comprising a total of about 40-60 wt. %, including about 50-60 wt. %, and 40-50 wt. % of one or more degradation resistant polymers. Masks may also include blends of different types of degradation resistant polymers, including those blends comprising one or more generally UV transparent or reflective polymers with one or more polymers incorporating UV absorption additives or monomers. These blends include those having a total of about 1-20 wt. %, including about 1-10 wt. %, 5-15 wt. %, and 10-20 wt. % of one or more generally UV transparent polymers, a total of about 80-100 wt. %, including about 80-90 wt. %, 85-95 wt. %, and 90-100 wt. % of one or more generally UV transparent polymers, and a total of about 40-60 wt. %, including about 50-60 wt. %, and 40-50 wt. % of one or more generally UV transparent polymers. The polymer or polymer blend may be mixed with other materials as discussed below, including, but not limited to, opacification agents, polyanionic compounds and/or wound healing modulator compounds. When mixed with these other materials, the amount of polymer or polymer blend in the material which makes up the mask is preferably about 50%-99% by weight, including about 60%-90% by weight, about 65-85% by weight, about 70-80% by weight, and about 90-99% by weight.
Preferred degradation resistant polymers include halogenated polymers. Preferred halogenated polymers include fluorinated polymers, that is, polymers having at least one carbon-fluorine bond, including highly fluorinated polymers. The term “highly fluorinated” as it is used herein, is a broad term used in its ordinary sense, and includes polymers having at least one carbon-fluorine bond (C—F bond) where the number of C—F bonds equals or exceeds the number of carbon-hydrogen bonds (C—H bonds). Highly fluorinated materials also include perfluorinated or fully fluorinated materials, materials which include other halogen substituents such as chlorine, and materials which include oxygen- or nitrogen-containing functional groups. For polymeric materials, the number of bonds may be counted by referring to the monomer(s) or repeating units which form the polymer, and in the case of a copolymer, by the relative amounts of each monomer (on a molar basis).
Preferred highly fluorinated polymers include, but are not limited to, polytetrafluoroethylene (PFTE or Teflon®), polyvinylidene fluoride (PVDF or Kynar®), poly-1,1,2-trifluoroethylene, and perfluoroalkoxyethylene (PFA). Other highly fluorinated polymers include, but are not limited to, homopolymers and copolymers including one or more of the following monomer units: tetrafluoroethylene —(CF2—CF2)—; vinylidene fluoride —(CF2—CH2)—; 1,1,2-trifluoroethylene —(CF2—CHF)—; hexafluoropropene —(CF(CF3)—CF2)—; vinyl fluoride —(CH2—CHF)— (homopolymer is not “highly fluorinated”); oxygen-containing monomers such as —(O—CF2)—, —(O—CF2—CF2)—, —(O—CF(CF3)—CF2)—; chlorine-containing monomers such as —(CF2—CFCl)—. Other fluorinated polymers, such as fluorinated polyimide and fluorinated acrylates, having sufficient degrees of fluorination are also contemplated as highly fluorinated polymers for use in masks according to preferred embodiments. The homopolymers and copolymers described herein are available commercially and/or methods for their preparation from commercially available materials are widely published and known to those in the polymer arts.
Although highly fluorinated polymers are preferred, polymers having one or more carbon-fluorine bonds but not falling within the definition of “highly fluorinated” polymers as discussed above, may also be used. Such polymers include co-polymers formed from one or more of the monomers in the preceding paragraph with ethylene, vinyl fluoride or other monomer to form a polymeric material having a greater number of C—H bonds than C—F bonds. Other fluorinated polymers, such as fluorinated polyimide, may also be used. Other materials that could be used in some applications, alone or in combination with a fluorinated or a highly fluorinated polymer, are described in U.S. Pat. No. 4,985,559 and in U.S. Pat. No. 4,538,311, both of which are hereby incorporated by reference herein in their entirety.
The preceding definition of highly fluorinated is best illustrated by means of a few examples. One preferred UV-resistant polymeric material is polyvinylidene fluoride (PVDF), having a structure represented by the formula: —(CF2—CH2)n—. Each repeating unit has two C—H bonds, and two C—F bonds. Because the number of C—F bonds equals or exceeds the number of C—H bonds, PVDF homopolymer is a “highly fluorinated” polymer. Another material is a tetrafluoroethylene/vinyl fluoride copolymer formed from these two monomers in a 2:1 molar ratio. Regardless of whether the copolymer formed is block, random or any other arrangement, from the 2:1 tetrafluoroethylene:vinyl fluoride composition one can presume a “repeating unit” comprising two tetrafluoroethylene units, each having four C—F bonds, and one vinyl fluoride unit having three C—H bonds and one C—F bond. The total bonds for two tetrafluoroethylenes and one vinyl fluoride are nine C—F bonds, and three C—H bonds. Because the number of C—F bonds equals or exceeds the number of C—H bonds, this copolymer is considered highly fluorinated.
Certain highly fluorinated polymers, such as PVDF, have one or more desirable characteristics, such as being relatively chemically inert and having a relatively high UV transparency as compared to their non-fluorinated or less highly fluorinated counterpart polymers. Although the applicant does not intend to be bound by theory, it is postulated that the electronegativity of fluorine may be responsible for many of the desirable properties of the materials having relatively large numbers of C—F bonds.
In preferred embodiments, at least a portion of the highly fluorinated polymer material forming the mask comprises an opacification agent which imparts a desired degree of opacity. In one embodiment, the opacification agent provides sufficient opacity to produce the depth of field improvements described herein, e.g., in combination with a transmissive aperture. In one embodiment, the opacification agent renders the material opaque. In another embodiment, the opacification agent prevents transmission of about 90 percent or more of incident light. In another embodiment, the opacification agent renders the material opaque. In another embodiment, the opacification agent prevents transmission of about 80 percent or more of incident light. Preferred opacification agents include, but are not limited to organic dyes and/or pigments, preferably black ones, such as azo dyes, hematoxylin black, and Sudan black; inorganic dyes and/or pigments, including metal oxides such as iron oxide black and ilminite, silicon carbide and carbon (e.g. carbon black, submicron powdered carbon). The foregoing materials may be used alone or in combination with one or more other materials. The opacification agent may be applied to one or more surfaces of the mask on all or some of the surface, or it may be mixed or combined with the polymeric material (e.g. blended during the polymer melt phase). Although any of the foregoing materials may be used, carbon has been found to be especially useful in that it does not fade over time as do many organic dyes, and that it also aids the UV stability of the material by absorbing UV radiation In one embodiments, carbon may be mixed with polyvinylidene fluoride (PVDF) or other polymer composition comprising highly fluorinated polymer such that the carbon comprises about 2% to about 20% by weight of the resulting composition, including about 10% to about 15% by weight, including about 12%, about 13%, and about 14% by weight of the resulting composition.
Some opacification agents, such pigments, which are added to blacken, darken or opacify portions of the mask may cause the mask to absorb incident radiation to a greater degree than mask material not including such agents. Because the matrix polymer that carries or includes the pigments may be subject to degradation from the absorbed radiation, it is preferred that the mask, which is thin and has a high surface area making it vulnerable to environmental degradation, be made of a material which is itself resistant to degradation such as from UV radiation, or that it be generally transparent to or non-absorbing of UV radiation. Use of a highly UV resistant and degradation resistant material, such as PVDF, which is highly transparent to UV radiation, allows for greater flexibility in choice of opacification agent because possible damage to the polymer caused by selection of a particular opacification agent is greatly reduced.
A number of variations of the foregoing embodiments of degradation resistant constructions are contemplated. In one variation, a mask is made almost exclusively of a material that is not subject to UV degradation. For example, the mask can be made of a metal, a highly fluorinated polymer, or another similar material. Construction of the mask with metal is discussed in more detail in U.S. application Ser. No. 11/000,562 filed Dec. 1, 2004 and entitled “Method of Making an Ocular Implant” and also in U.S. application Ser. No. 11/107,359 filed Apr. 14, 2005 with the title “Method of Making an Ocular Implant”, both of which are incorporated herein in their entirety by reference. As used in this context, “exclusively” is a broad term that allows for the presence of some non-functional materials (e.g., impurities) and for an opacification agent, as discussed above. In other embodiments, the mask can include a combination of materials. For example, in one variation, the mask is formed primarily of any implantable material and is coated with a UV resistant material. In another variation, the mask includes one or more UV degradation inhibitors and/or one or more UV degradation resistant polymers in sufficient concentration such that the mask under normal use conditions will maintain sufficient functionality in terms of degradation to remain medically effective for at least about 5 years, preferably at least about 10 years, and in certain implementations at least about 20 years.
IV. Additives to Reduce Corneal Deposits and/or Promote Proper Healing
In some circumstances, corneal implants are associated with deposits on the cornea. Loading of one or more polyanionic compounds into the polymeric material of a corneal implant may reduce and/or substantially eliminate deposits on the cornea, possibly by attracting and/or retaining growth factors.
In a preferred embodiment the one or more polyanionic compounds include carbohydrates, proteins, natural proteoglycans, and/or the glycosaminoglycan moieties of proteoglycans, as well as derivatives (such as sulfated derivatives) and salts of compounds such as those in the aforementioned categories. Preferred polyanionic compounds include one or more of dermatan sulfate, chondroitin sulfate, keratan sulfate, heparan sulfate, heparin, dextran sulfate, hyaluronic acid, pentosan polysulfate, xanthan, carrageenan, fibronectin, laminin, chondronectin, vitronectin, poly L-lysine salts, and anionic, preferably sulfated, carbohydrates such as alginate may also be used, as well as salts and derivatives of the listed compounds. Examples of preferred anionic compounds and combinations of polyanionic compounds include keratan sulfate/chrondroitin sulfate-proteoglycan, dermatan sulfate proteoglycan, and dextran sulfate.
In one embodiment, a polyanionic compound comprises acidic sulfate moieties and the sulfur content is greater than about 5% by weight, preferably greater than about 10% by weight. In an even more preferred embodiment, the average molecular weight of a polyanionic compound is about 40,000 to 500,000 Daltons.
In a preferred embodiment, the total weight of the one or more polyanionic compounds in the loaded polymeric material is about 0.1% by weight to about 50% by weight, including about 5% by weight to about 20% by weight, about 12% by weight to about 17% by weight, about 0.5% by weight to about 4% by weight, and about 5% by weight to about 15% by weight. It should be noted that the percentages recited herein in relation to polyanionic compounds, opacification agents and wound healing modulator compounds are percent by weight with 100% being the total weight of the entire mask composition including all additives.
In one embodiment, the body of the mask is formed from a polymeric material having one or more polyanionic compounds loaded therein. Loading of a polyanionic compound is performed by mixing the polyanionic compound with the resin and any other additives of the polymeric material prior to molding or casting of the body of the mask. Although some of a polyanionic compound that is loaded into the polymeric material may be on the surface of the mask, loading is to be distinguished from coating in that a coated material would not have polyanionic material throughout the bulk of the mask.
The loaded polymeric material is preferably made by suspending or dissolving polymer, one or more polyanionic compounds and any other additives (such as wound healing modulators, as described below) in a solvent or solvent system, and then casting a film whereby the solvent or solvent system is removed such as by evaporation. Preferred casting methods include spin casting and other methods, including those known in the art, which can form a thin material of relatively even thickness. Although other methods of making thin substrates, such as extrusion, may be used, solvent casting is generally preferred because it does not need to be done at high temperatures that may cause degradation of some polyanionic compounds. The polymer, polyanionic compound, and/or other additives may be ground or milled, such as by ball milling, to reduce the particle size of the material prior to suspending, dissolving or melting as part of making the mask.
In methods using solvent casting, preferred solvents include those which are capable of dissolving the polymeric material, polyanionic compounds, and/or other additives. A suitable solvent or solvent system (i.e. combination of two or more solvents) may be chosen by one skilled in the art based upon known solubilities for a given polymeric material and/or routine experimentation based upon chemical principles. In solvent casting methods, the temperature of the solvent or solution should be no higher than the boiling point of the solvent or solvent system, and is preferably about 10° C. to about 70° C. During or after casting of the solution to form a film, the temperature may be elevated, including above the boiling point.
In one embodiment, a mask, such as an inlay, comprising PVDF, dextran sulfate, and carbon was made by spin casting. 100 grams of PVDC (about 71% by weight) in the form of pellets was dissolved in 400 grams of dimethylacetamide. 17 grams of carbon (about 12% by weight) and 24 grams of dextran sulfate (about 17% by weight) are ball milled to reduce particle size and then added to the PVDF/DMA solution. The percentages by weight are the percentages of the solids portion, that is the portion that is not the solvent. The solution was at room temperature (approximately 17° C. to about 25° C.). The solution was then spin cast to form a film.
In one embodiment, the device includes a wound healing modulator. When present, the wound healing modulator is on at least one surface or it may be loaded into the polymeric material. A wound healing modulator is defined as a compound that assists in proper healing of a wound, such as by increasing the rate of healing, decreasing inflammation, moderating or suppressing immune response, decreasing scarring, decreasing cell proliferation, reducing infection, encouraging transdifferentiation of keratocytes into cells that lay down collagen, and the like. Wound healing modulators include, without limitation, antibiotics, antineoplastics including antimitotics, antimetabolics and antibiotic types, anti-inflammatories, immunosupressants, and antifungals. Preferred compounds include, but are not limited to, fluorouracil, mitomycin C, paclitaxel, NSAIDs (e.g. ibuprofen, naproxen, flurbiprofen, carprofen, suprofen, ketoprofen), and cyclosporins. Other preferred compounds include proteoglycans, glycosaminoglycans, and salts and derivatives thereof, as well as other carbohydrates and/or proteins, including those disclosed above.
A wound healing modulator may be included in the mask by loading it into the polymeric material as discussed above with respect to the polyanionic compounds. It may also be included by binding it to one or more surfaces of the device. The “binding” of the wound healing modulator to the device may occur by phenomena that do not generally involve chemical bonds, including adsorption, hydrogen bonding, van der Waals forces, electrostatic attraction, ionic bonding, and the like, or it may occur by phenomena that do include chemical bonds. In a preferred embodiment, the total weight of the one or more wound healing modulator compounds in the loaded polymeric material is about 0.1% by weight to about 50% by weight, including about 5% by weight to about 20% by weight, about 12% by weight to about 17% by weight, about 0.5% by weight to about 4% by weight, and about 5% by weight to about 15% by weight.
In one embodiment, carbon, gold or other material on a surface of the mask acts as an adsorbent or otherwise participates in the binding of one or more wound healing modulators to the implant. The material on the surface of the mask that participates in binding the wound healing modulator may be part of the bulk material of the implant (distributed throughout the implant or which migrates to the surface during and/or following formation of the implant) and/or deposited on a surface of the mask, such as an opacification agent as described elsewhere infra. The implant is then exposed to one or more wound healing modulators, such as by dipping in a solution (including dispersions and emulsions) comprising at least one wound healing modulator, to allow wound healing modulator(s) to bind to the implant. The solvent used to assist in applying and binding the wound healing modulator to the implant is preferably biocompatible, does not leave a harmful residue, and/or does not cause dissolution or swelling of the polymeric material of the mask. If more than one wound healing modulator is used, binding may be performed by dipping in a single solution containing all desired wound healing modulators or by dipping the implant in two or more successive solutions, each of which contains one or more of the desired wound healing modulators. The process of binding wound healing modulator to the implant may be done at any time. In one embodiment, at least some of the wound healing modulator is bound to the implant as part of the manufacturing process. In another embodiment, a medical practitioner, such as an ophthalmologist, binds at least some of the wound healing modulator to the implant just prior to implantation.
In alternate embodiments, one or more wound healing modulators are bound to the implant using any suitable method for binding drugs or other useful compounds to implants and medical devices and/or using methods for making drug delivery devices which deliver a drug locally in the area of implantation or placement over a period of time.
V. Masks Configured to Reduce Visible Diffraction Patterns
Many of the foregoing masks can be used to improve the depth of focus of a patient. Various additional mask embodiments are discussed below. Some of the embodiments described below include nutrient transport structures that are configured to enhance or maintain nutrient flow between adjacent tissues by facilitating transport of nutrients across the mask. The nutrient transport structures of some of the embodiments described below are configured to at least substantially prevent nutrient depletion in adjacent tissues. The nutrient transport structures can decrease negative effects due to the presence of the mask in adjacent corneal layers when the mask is implanted in the cornea, increasing the longevity of the masks. The inventors have discovered that certain arrangements of nutrient transport structures generate diffraction patterns that interfere with the vision improving effect of the masks described herein. Accordingly, certain masks are described herein that include nutrient transport structures that do not generate diffraction patterns or otherwise interfere with the vision enhancing effects of the mask embodiments.
In one embodiment, the mask 100 includes a body 104 that has an anterior surface 108 and a posterior surface 112. In one embodiment, the body 104 is capable of substantially maintaining natural nutrient flow between the first corneal layer and the second corneal layer. In one embodiment, the material is selected to maintain at least about ninety-six percent of the natural flow of at least one nutrient (e.g., glucose) between a first corneal layer (e.g., the layer 1210) and a second corneal layer (e.g., the layer 1220). The body 104 may be formed of any suitable material, including at least one of an open cell foam material, an expanded solid material, and a substantially opaque material. In one embodiment, the material used to form the body 104 has relatively high water content.
In one embodiment, the mask 100 includes and a nutrient transport structure 116. The nutrient transport structure 116 may comprise a plurality of holes 120. The holes 120 are shown on only a portion of the mask 100, but the holes 120 preferably are located throughout the body 104 in one embodiment. In one embodiment, the holes 120 are arranged in a hex pattern, which is illustrated by a plurality of locations 120′ in
Preferably the mask 100 is symmetrical, e.g., symmetrical about a mask axis 136. In one embodiment, the outer periphery 124 of the mask 100 is circular. The masks in general have has a diameter within the range of from about 3 mm to about 8 mm, often within the range of from about 3.5 mm to about 6 mm, and less than about 6 mm in one embodiment. In another embodiment, the mask is circular and has a diameter in the range of 4 to 6 mm. In another embodiment, the mask 100 is circular and has a diameter of less than 4 mm. The outer periphery 124 has a diameter of about 3.8 mm in another embodiment. In some embodiments, masks that are asymmetrical or that are not symmetrical about a mask axis provide benefits, such as enabling a mask to be located or maintained in a selected position with respect to the anatomy of the eye.
The body 104 of the mask 100 may be configured to coupled with a particular anatomical region of the eye. The body 104 of the mask 100 may be configured to conform to the native anatomy of the region of the eye in which it is to be applied. For example, where the mask 100 is to be coupled with an ocular structure that has curvature, the body 104 may be provided with an amount of curvature along the mask axis 136 that corresponds to the anatomical curvature. For example, one environment in which the mask 100 may be deployed is within the cornea of the eye of a patient. The cornea has an amount of curvature that varies from person to person about a substantially constant mean value within an identifiable group, e.g., adults. When applying the mask 100 within the cornea, at least one of the anterior and posterior surfaces 108, 112 of the mask 100 may be provided with an amount of curvature corresponding to that of the layers of the cornea between which the mask 100 is applied.
In some embodiments, the mask 100 has a desired amount of optical power. Optical power may be provided by configuring the at least one of the anterior and posterior surfaces 108, 112 with curvature. In one embodiment, the anterior and posterior surfaces 108, 112 are provided with different amounts of curvature. In this embodiment, the mask 100 has varying thickness from the outer periphery 124 to the aperture 128.
In one embodiment, one of the anterior surface 108 and the posterior surface 112 of the body 104 is substantially planar. In one planar embodiment, very little or no uniform curvature can be measured across the planar surface. In another embodiment, both of the anterior and posterior surfaces 108, 112 are substantially planar. In general, the thickness of the inlay may be within the range of from about 1 micron to about 40 micron, and often in the range of from about 5 micron to about 20 micron. In one embodiment, the body 104 of the mask 100 has a thickness 138 of between about 5 micron and about 10 micron. In one embodiment, the thickness 138 of the mask 100 is about 5 micron. In another embodiment, the thickness 138 of the mask 100 is about 8 micron. In another embodiment, the thickness 138 of the mask 100 is about 10 micron.
Thinner masks generally are more suitable for applications wherein the mask 100 is implanted at a relatively shallow location in (e.g., close to the anterior surface of) the cornea. In thinner masks, the body 104 may be sufficiently flexible such that it can take on the curvature of the structures with which it is coupled without negatively affecting the optical performance of the mask 100. In one application, the mask 100 is configured to be implanted about 5 um beneath the anterior surface of the cornea. In another application, the mask 100 is configured to be implanted about 52 um beneath the anterior surface of the cornea. In another application, the mask 100 is configured to be implanted about 125 um beneath the anterior surface of the cornea. Further details regarding implanting the mask 100 in the cornea are discussed above in connection with
A substantially planar mask has several advantages over a non-planar mask. For example, a substantially planar mask can be fabricated more easily than one that has to be formed to a particular curvature. In particular, the process steps involved in inducing curvature in the mask 100 can be eliminated. Also, a substantially planar mask may be more amenable to use on a wider distribution of the patient population (or among different sub-groups of a broader patient population) because the substantially planar mask uses the curvature of each patient's cornea to induce the appropriate amount of curvature in the body 104.
In some embodiments, the mask 100 is configured specifically for the manner and location of coupling with the eye. In particular, the mask 100 may be larger if applied over the eye as a contact lens or may be smaller if applied within the eye posterior of the cornea, e.g., proximate a surface of the lens of the eye. As discussed above, the thickness 138 of the body 104 of the mask 100 may be varied based on where the mask 100 is implanted. For implantation at deeper levels within the cornea, a thicker mask may be advantageous. Thicker masks are advantageous in some applications. For example, they are generally easier to handle, and therefore are easier to fabricate and to implant. Thicker masks may benefit more from having a preformed curvature than thinner masks. A thicker mask could be configured to have little or no curvature prior to implantation if it is configured to conform to the curvature of the native anatomy when applied.
The aperture 128 is configured to transmit substantially all incident light along the mask axis 136. The non-transmissive portion 132 surrounds at least a portion of the aperture 128 and substantially prevents transmission of incident light thereon. As discussed in connection with the above masks, the aperture 128 may be a through-hole in the body 104 or a substantially light transmissive (e.g., transparent) portion thereof. The aperture 128 of the mask 100 generally is defined within the outer periphery 124 of the mask 100. The aperture 128 may take any of suitable configurations, such as those described above in connection with
In one embodiment, the aperture 128 is substantially circular and is substantially centered in the mask 100. The size of the aperture 128 may be any size that is effective to increase the depth of focus of an eye of a patient suffering from presbyopia. For example, the aperture 128 can be circular, having a diameter of less than about 2.2 mm in one embodiment. In another embodiment, the diameter of the aperture is between about 1.8 mm and about 2.2 mm. In another embodiment, the aperture 128 is circular and has a diameter of about 1.8 mm or less. In another embodiment, the diameter of the aperture is about 1.6 mm. Most apertures will have a diameter within the range of from about 1.0 mm to about 2.5 mm, and often within the range of from about 1.3 mm to about 1.9 mm.
The non-transmissive portion 132 is configured to prevent transmission of radiant energy through the mask 100. For example, in one embodiment, the non-transmissive portion 132 prevents transmission of substantially all of at least a portion of the spectrum of the incident radiant energy. In one embodiment, the non-transmissive portion 132 is configured to prevent transmission of substantially all visible light, e.g., radiant energy in the electromagnetic spectrum that is visible to the human eye. The non-transmissive portion 132 may substantially prevent transmission of radiant energy outside the range visible to humans in some embodiments.
As discussed above in connection with
In one embodiment, the non-transmissive portion 132 prevents transmission of about 90 percent of incident light. In another embodiment, the non-transmissive portion 132 prevents transmission of about 92 percent of all incident light. The non-transmissive portion 132 of the mask 100 may be configured to be opaque to prevent the transmission of light. As used herein the term “opaque” is intended to be a broad term meaning capable of preventing the transmission of radiant energy, e.g., light energy, and also covers structures and arrangements that absorb or otherwise block all or less than all or at least a substantial portion of the light. In one embodiment, at least a portion of the body 104 is configured to be opaque to more than 99 percent of the light incident thereon.
As discussed above, the non-transmissive portion 132 may be configured to prevent transmission of light without absorbing the incident light. For example, the mask 100 could be made reflective or could be made to interact with the light in a more complex manner, as discussed in U.S. Pat. No. 6,551,424, issued Apr. 29, 2003, which is hereby incorporated by reference herein in its entirety.
As discussed above, the mask 100 also has a nutrient transport structure that in some embodiments comprises the plurality of holes 120. The presence of the plurality of holes 120 (or other transport structure) may affect the transmission of light through the non-transmissive portion 132 by potentially allowing more light to pass through the mask 100. In one embodiment, the non-transmissive portion 132 is configured to absorb about 99 percent or more of the incident light from passing through the mask 100 without holes 120 being present. The presence of the plurality of holes 120 allows more light to pass through the non-transmissive portion 132 such that only about 92 percent of the light incident on the non-transmissive portion 132 is prevented from passing through the non-transmissive portion 132. The holes 120 may reduce the benefit of the aperture 128 on the depth of focus of the eye by allowing more light to pass through the non-transmissive portion to the retina.
Reduction in the depth of focus benefit of the aperture 128 due to the holes 120 is balanced by the nutrient transmission benefits of the holes 120. In one embodiment, the transport structure 116 (e.g., the holes 120) is capable of substantially maintaining natural nutrient flow from a first corneal layer (i.e., one that is adjacent to the anterior surface 108 of the mask 100) to the second corneal layer (i.e., one that is adjacent to the posterior surface 112 of the mask 100). The plurality of holes 120 are configured to enable nutrients to pass through the mask 100 between the anterior surface 108 and the posterior surface 112. As discussed above, the holes 120 of the mask 100 shown in
The holes 120 of
The transport structure 116 is configured to maintain the transport of one or more nutrients across the mask 100. The transport structure 116 of the mask 100 provides sufficient flow of one or more nutrients across the mask 100 to prevent depletion of nutrients at least at one of the first and second corneal layers (e.g., the layers 1210 and 1220). One nutrient of particular importance to the viability of the adjacent corneal layers is glucose. The transport structure 116 of the mask 100 provides sufficient flow of glucose across the mask 100 between the first and second corneal layers to prevent glucose depletion that would harm the adjacent corneal tissue. Thus, the mask 100 is capable of substantially maintaining nutrient flow (e.g., glucose flow) between adjacent corneal layers. In one embodiment, the nutrient transport structure 116 is configured to prevent depletion of more than about 4 percent of glucose (or other biological substance) in adjacent tissue of at least one of the first corneal layer and the second corneal layer.
The holes 120 may be configured to maintain the transport of nutrients across the mask 100. In one embodiment, the holes 120 are formed with a diameter of about 0.015 mm or more. In another embodiment, the holes have a diameter of about 0.020 mm. In another embodiment, the holes have a diameter of about 0.025 mm. In another embodiment, the holes have a diameter of about 0.027 mm. In another embodiment, the holes 120 have a diameter in the range of about 0.020 mm to about 0.029 mm. The number of holes in the plurality of holes 120 is selected such that the sum of the surface areas of the hole entrances 140 of all the holes 100 comprises about 5 percent or more of surface area of the anterior surface 108 of the mask 100. In another embodiment, the number of holes 120 is selected such that the sum of the surface areas of the hole exits 164 of all the holes 120 comprises about 5 percent or more of surface area of the posterior surface 112 of the mask 100. In another embodiment, the number of holes 120 is selected such that the sum of the surface areas of the hole exits 164 of all the holes 120 comprises about 5 percent or more of surface area of the posterior surface 112 of the mask 112 and the sum of the surface areas of the hole entrances 140 of all the holes 120 comprises about 5 percent or more of surface area of the anterior surface 108 of the mask 100. In another embodiment, the plurality of holes 120 may comprise about 1600 microperforations.
Each of the holes 120 may have a relatively constant cross-sectional area. In one embodiment, the cross-sectional shape of each of the holes 120 is substantially circular. Each of the holes 120 may comprise a cylinder extending between the anterior surface 108 and the posterior surface 112.
The relative position of the holes 120 is of interest in some embodiments. As discussed above, the holes 120 of the mask 100 are hex-packed, e.g., arranged in a hex pattern. In particular, in this embodiment, each of the holes 120 is separated from the adjacent holes 120 by a substantially constant distance, sometimes referred to herein as a hole pitch. In one embodiment, the hole pitch is about 0.045 mm.
In a hex pattern, the angles between lines of symmetry are approximately 43 degrees. The spacing of holes along any line of holes is generally within the range of from about 30 microns to about 100 microns, and, in one embodiment, is approximately 43 microns. The hole diameter is generally within the range of from about 10 microns to about 100 microns, and in one embodiment, is approximately 20 microns. The hole spacing and diameter are related if you want to control the amount of light coming through. The light transmission is a function of the sum of hole areas as will be understood by those of skill in the art in view of the disclosure herein.
The embodiment of
The inventors have discovered a variety of techniques that produce advantageous arrangements of a transport structure such that diffraction patterns and other deleterious visual effects do not substantially inhibit other visual benefits of a mask. In one embodiment, where diffraction effects would be observable, the nutrient transport structure is arranged to spread the diffracted light out uniformly across the image to eliminate observable spots. In another embodiment, the nutrient transport structure employs a pattern that substantially eliminates diffraction patterns or pushes the patterns to the periphery of the image.
Other embodiments may be provided that vary at least one aspect, including one or more of the foregoing aspects, of a plurality of holes to reduce the tendency of the holes to produce visible diffraction patterns or patterns that otherwise reduce the vision improvement that may be provided by a mask with an aperture, such as any of those described above. For example, in one embodiment, the hole size, shape, and orientation of at least a substantial number of the holes may be varied randomly or may be otherwise non-uniform.
The outer peripheral region 305 may extend from an outer periphery 324 of the mask 300 to a selected outer circumference 326 of the mask 300. The selected outer circumference 325 of the mask 300 is located a selected radial distance from the outer periphery 324 of the mask 300. In one embodiment, the selected outer circumference 325 of the mask 300 is located about 0.05 mm from the outer periphery 324 of the mask 300.
The inner peripheral region 306 may extend from an inner location, e.g., an inner periphery 326 adjacent an aperture 328 of the mask 300 to a selected inner circumference 327 of the mask 300. The selected inner circumference 327 of the mask 300 is located a selected radial distance from the inner periphery 326 of the mask 300. In one embodiment, the selected inner circumference 327 of the mask 300 is located about 0.05 mm from the inner periphery 326.
The mask 300 may be the product of a process that involves random selection of a plurality of locations and formation of holes on the mask 300 corresponding to the locations. As discussed further below, the method can also involve determining whether the selected locations satisfy one or more criteria. For example, one criterion prohibits all, at least a majority, or at least a substantial portion of the holes from being formed at locations that correspond to the inner or outer peripheral regions 305, 306. Another criterion prohibits all, at least a majority, or at least a substantial portion of the holes from being formed too close to each other. For example, such a criterion could be used to assure that a wall thickness, e.g., the shortest distance between adjacent holes, is not less than a predetermined amount. In one embodiment, the wall thickness is prevented from being less than about 20 microns.
In a variation of the embodiment of
In one embodiment, each of the holes 420 has a hole entrance 460 and a hole exit 464. Each of the holes 420 extends along a transport axis 466. The transport axis 466 is formed to substantially prevent propagation of light from the anterior surface 408 to the posterior surface 412 through the holes 420. In one embodiment, at least a substantial number of the holes 420 have a size to the transport axis 466 that is less than a thickness of the mask 400. In another embodiment, at least a substantial number of the holes 420 have a longest dimension of a perimeter at least at one of the anterior or posterior surfaces 408, 412 (e.g., a facet) that is less than a thickness of the mask 400. In some embodiments, the transport axis 466 is formed at an angle with respect to a mask axis 436 that substantially prevents propagation of light from the anterior surface 408 to the posterior surface 412 through the hole 420. In another embodiment, the transport axis 466 of one or more holes 420 is formed at an angle with respect to the mask axis 436 that is large enough to prevent the projection of most of the hole entrance 460 from overlapping the hole exit 464.
In one embodiment, the hole 420 is circular in cross-section and has a diameter between about 0.5 micron and about 8 micron and the transport axis 466 is between 5 and 85 degrees. The length of each of the holes 420 (e.g., the distance between the anterior surface 408 and the posterior surface 412) is between about 8 and about 92 micron. In another embodiment, the diameter of the holes 420 is about 5 micron and the transport angle is about 40 degrees or more. As the length of the holes 420 increases it may be desirable to include additional holes 420. In some cases, additional holes 420 counteract the tendency of longer holes to reduce the amount of nutrient flow through the mask 400.
In one embodiment, at least one of the holes 520 extends along a non-linear path that substantially prevents propagation of light from the anterior surface to the posterior surface through the at least one hole. In one embodiment, the mask 500 includes a first hole portion 520a that extends along a first transport axis 566a, the second mask layer 514 includes a second hole portion 520b extending along a second transport axis 566b, and the third mask layer 515 includes a third hole portion 520c extending along a third transport axis 566c. The first, second, and third transport axes 566a, 566b, 566c preferably are not collinear. In one embodiment, the first and second transport axes 566a, 566b are parallel but are off-set by a first selected amount. In one embodiment, the second and third transport axes 566b, 566c are parallel but are off-set by a second selected amount. In the illustrated embodiment, each of the transport axes 566a, 566b, 566c are off-set by one-half of the width of the hole portions 520a, 520b, 520c. Thus, the inner-most edge of the hole portion 520a is spaced from the axis 536 by a distance that is equal to or greater than the distance of the outer-most edge of the hole portion 520b from the axis 536. This spacing substantially prevents light from passing through the holes 520 from the anterior surface 508 to the posterior surface 512.
In one embodiment, the first and second amounts are selected to substantially prevent the transmission of light therethrough. The first and second amounts of off-set may be achieved in any suitable fashion. One technique for forming the hole portions 520a, 520b, 520c with the desired off-set is to provide a layered structure. As discussed above, the mask 500 may include the first layer 510, the second layer 514, and the third layer 515.
In any of the foregoing mask embodiments, the body of the mask may be formed of a material selected to provide adequate nutrient transport and to substantially prevent negative optic effects, such as diffraction, as discussed above. In various embodiments, the masks are formed of an open cell foam material. In another embodiment, the masks are formed of an expanded solid material.
As discussed above in connection with
In a first step of one technique, a plurality of locations 220′ is generated. The locations 220′ are a series of coordinates that may comprise a non-uniform pattern or a regular pattern. The locations 220′ may be randomly generated or may be related by a mathematical relationship (e.g., separated by a fixed spacing or by an amount that can be mathematically defined). In one embodiment, the locations are selected to be separated by a constant pitch or spacing and may be hex packed.
In a second step, a subset of the locations among the plurality of locations 220′ is modified to maintain a performance characteristic of the mask. The performance characteristic may be any performance characteristic of the mask. For example, the performance characteristic may relate to the structural integrity of the mask. Where the plurality of locations 220′ is selected at random, the process of modifying the subset of locations may make the resulting pattern of holes in the mask a “pseudo-random” pattern.
Where a hex packed pattern of locations (such as the locations 120′ of
In one technique, an outer peripheral region is defined that extends between the outer periphery of the mask and a selected radial distance of about 0.05 mm from the outer periphery. In another embodiment, an inner peripheral region is defined that extends between an aperture of the mask and a selected radial distance of about 0.05 mm from the aperture. In another embodiment, an outer peripheral region is defined that extends between the outer periphery of the mask and a selected radial distance and an inner peripheral region is defined that extends between the aperture of the mask and a selected radial distance from the aperture. In one technique, the subset of location is modified by excluding those locations that would correspond to holes formed in the inner peripheral region or the outer peripheral region. By excluding locations in at least one of the outer peripheral region and the inner peripheral region, the strength of the mask in these regions is increased. Several benefits are provided by stronger inner and outer peripheral regions. For example, the mask may be easier to handle during manufacturing or when being applied to a patient without causing damage to the mask.
In another embodiment, the subset of locations is modified by comparing the separation of the holes with minimum and or maximum limits. For example, it may be desirable to assure that no two locations are closer than a minimum value. In some embodiments this is important to assure that the wall thickness, which corresponds to the separation between adjacent holes, is no less than a minimum amount. As discussed above, the minimum value of separation is about 20 microns in one embodiment, thereby providing a wall thickness of no less than about 20 microns.
In another embodiment, the subset of locations is modified and/or the pattern of location is augmented to maintain an optical characteristic of the mask. For example, the optical characteristic may be opacity and the subset of locations may be modified to maintain the opacity of a non-transmissive portion of a mask. In another embodiment, the subset of locations may be modified by equalizing the density of holes in a first region of the body compared with the density of holes in a second region of the body. For example, the locations corresponding to the first and second regions of the non-transmissive portion of the mask may be identified. In one embodiment, the first region and the second region are arcuate regions (e.g., wedges) of substantially equal area. A first areal density of locations (e.g., locations per square inch) is calculated for the locations corresponding to the first region and a second areal density of locations is calculated for the locations corresponding to the second region. In one embodiment, at least one location is added to either the first or the second region based on the comparison of the first and second areal densities. In another embodiment, at least one location is removed based on the comparison of the first and second areal densities.
The subset of locations may be modified to maintain nutrient transport of the mask. In one embodiment, the subset of location is modified to maintain glucose transport.
In a third step, a hole is formed in a body of a mask at locations corresponding to the pattern of locations as modified, augmented, or modified and augmented. The holes are configured to substantially maintain natural nutrient flow from the first layer to the second layer without producing visible diffraction patterns.
VI. Methods of Applying Pinhole Aperture Devices
The various masks discussed herein can be used to improve the vision of a presbyopic patient as well as patient's with other vision problems. The masks discussed herein can be deployed in combination with a LASIK procedure, to eliminate the effects of abrasions, aberrations, and divots in the cornea. It is also believed that the masks disclosed herein can be used to treat patients suffering from macular degeneration, e.g., by directing light rays to unaffected portions of retina, thereby improving the vision of the patient. Whatever treatment is contemplated, more precise alignment of the central region of a mask that has a pin-hole aperture with the line of sight or visual axis of the patient is believed to provide greater clinical benefit to the patient. Other ocular devices that do not require a pin-hole aperture can also benefit from the alignment techniques discussed below. Also, various structures and techniques that can be used to remove an ocular devices are discussed below.
A. Alignment of the Pinhole Aperture with the Patient's Visual Axis
Alignment of the central region of the pinhole aperture 38, in particular, the optical axis 39 of the mask 34 with the visual axis of the eye 10 may be achieved in a variety of ways. In one technique, an optical device employs input from the patient to locate the visual axis in connection with a procedure to implant the mask 34. This technique is described in more detail in U.S. patent application Ser. No. 11/000,562, filed Dec. 1, 2004, the entire contents of which is hereby expressly incorporated by reference herein.
In other embodiments, systems and methods identify one or more visible ocular features that correlate to the line of sight. The one or more visible ocular feature(s) is observed while the mask is being applied to the eye. Alignment using a visible ocular feature enables the mask to perform adequately to increase depth of focus. In some applications, a treatment method enhances the correlation of the visible ocular feature and the line of sight to maintain or improve alignment of the mask axis and the line of sight.
Accurate alignment of the mask is believed to improve the clinical benefit of the mask. However, neither the optical axis of the mask nor the line of sight of the patient is generally visible during the surgical procedures contemplated for implanting masks. However, substantial alignment of the optical axis of the mask and the line of sight may be achieved by aligning a visible feature of the mask with a visible feature of the eye, e.g., a visible ocular feature. As used herein, the term “visible ocular feature” is a broad term that includes features viewable with a viewing aid, such as a surgical microscope or loupes, as well as those visible to the unaided eye. Various methods are discussed below that enhance the accuracy of the placement of the mask using a visible ocular feature. These methods generally involve treating the eye to increase the correlation between the location of the visible ocular feature and the line of sight or to increase the visibility of the ocular feature.
In a step 1000, an eye is treated to affect or alter, preferably temporarily, a visible ocular feature. In some embodiments, the feature of the eye is altered to increase the correlation of the location of the ocular feature to the line of sight of the eye. In some cases, the treatment of step 1000 enhances the visibility of the ocular feature to the surgeon. The ocular feature may be any suitable feature, such as the pupil or any other feature that correlates or can be altered by a treatment to correlate with the line of sight of the patient. Some techniques involve the alignment of a feature of a mask with the pupil or a portion of the pupil. One technique for enhancing the visibility of the pupil or the correlation of the location of the pupil with the line of sight involves manipulating the size of the pupil, e.g., increasing or decreasing the pupil size.
In connection with the method of
The pupil size may be decreased by any suitable technique, including pharmacologic manipulation and light manipulation. One agent used in pharmacologic manipulation of pupil size is pilocarpine. Pilocarpine reduces the size of the pupil when applied to the eye. One technique for applying pilocarpine is to inject an effective amount into the eye. Other agents for reducing pupil size include: carbachol, demecarium, isoflurophate, physostigmine, aceclidine, and echothiophate.
Pilocarpine is known to shift the location of the pupil nasally in some cases. This can be problematic for some ocular procedures, e.g., those procedures directed at improving distance vision. The applicant has discovered, however, that such a shift does not significantly reduce the efficacy of the masks described herein.
While the alignment of the masks described herein with the line of sight is not significantly degraded by the use of pilocarpine, an optional step of correcting for the nasal shift of the pupil may be performed.
In one variation, the treatment of the step 1000 involves increasing pupil size. This technique may be more suitable where it is desired to align a visible mask feature near an outer periphery of the mask with the pupil. These techniques are discussed further below.
As discussed above, the treatment of the step 1000 can involve non-pharmacologic techniques for manipulating a visible ocular feature. One non-pharmacologic technique involves the use of light to cause the pupil size to change. For example, a bright light can be directed into the eye to cause the pupil to constrict. This approach may substantially avoid displacement of the pupil that has been observed in connection with some pharmacologic techniques. Light can also be used to increase pupil size. For example, the ambient light can be reduced to cause the pupil to dilate. A dilated pupil may provide some advantages in connection with aligning to a visible mask feature adjacent to an outer periphery of a mask, as discussed below.
In a step 1004, a visible feature of a mask is aligned with the ocular feature identified in connection with step 1000. As discussed above, the mask may have an inner periphery, an outer periphery, and a pin-hole aperture located within the inner periphery. The pin-hole aperture may be centered on a mask axis. Other advantageous mask features discussed above may be included in masks applied by the methods illustrated by
One technique involves aligning at least a portion of the inner periphery of a mask with an anatomical landmark. For example, the inner periphery of the mask could be aligned with the inner periphery of the iris. This may be accomplished using unaided vision or a viewing aid, such as loupes or a surgical microscope. The mask could be aligned so that substantially the same spacing is provided between the inner periphery of the mask and the inner periphery of the iris. This technique could be facilitated by making the iris constrict, as discussed above. A viewing aid may be deployed to further assist in aligning the mask to the anatomical landmark. For example, a viewing aid could include a plurality of concentric markings that the surgeon can use to position the mask. Where the inner periphery of the iris is smaller than the inner periphery of the mask, a first concentric marking can be aligned with the inner periphery of the iris and the mask could be positioned so that a second concentric marking is aligned with the inner periphery of the mask. The second concentric marking would be farther from the common center than the first concentric marking in this example.
In another technique, the outer periphery of the mask could be aligned with an anatomical landmark, such as the inner periphery of the iris. This technique could be facilitated by dilating the pupil. This technique may be enhanced by the use of a viewing aid, which could include a plurality of concentric markings, as discussed above. In another technique, the outer periphery of the mask could be aligned with an anatomical landmark, such as the boundary between the iris and the sclera. This technique may be facilitated by the use of a viewing aid, such as a plurality of concentric markings.
In another technique, the mask can be aligned so that substantially the same spacing is provided between the inner periphery of the mask and the inner periphery of the iris. In this technique, the pupil preferably is constricted so that the diameter of the pupil is less than the diameter of the pin-hole aperture.
Alternatively, an artifact can be formed in the mask that gives a visual cue of proper alignment. For example, there could be one or more window portions formed in the mask through which the edge of the pupil could be observed. The window portions could be clear graduations or they could be at least partially opaque regions through which the pupil could be observed. In one technique, the surgeon moves the mask until the pupil can be seen in corresponding window portions on either side of the pin-hole aperture. The window portions enable a surgeon to align a visible ocular feature located beneath a non-transparent section of the mask with a feature of the mask. This arrangement enables alignment without a great amount of pupil constriction, e.g., where the pupil is not fully constricted to a size smaller than the diameter of the inner periphery.
Preferably the alignment of the ocular feature with one or more visible mask features causes the mask axis to be substantially aligned with the line of sight of the eye. “Substantial alignment” of the mask axis with the eye, e.g., with the line of sight of the eye (and similar terms, such as “substantially collinear”) can be said to have been achieved when a patient's vision is improved by the implantation of the mask. In some cases, substantial alignment can be said to have been achieved when the mask axis is within a circle centered on the line of sight and having a radius no more than 5 percent of the radius of the inner periphery of the mask. In some cases, substantial alignment can be said to have been achieved when the mask axis is within a circle centered on the line of sight and having a radius no more than 10 percent of the radius of the inner periphery of the mask. In some cases, substantial alignment can be said to have been achieved when the mask axis is within a circle centered on the line of sight and having a radius no more than 15 percent of the radius of the inner periphery of the mask. In some cases, substantial alignment can be said to have been achieved when the mask axis is within a circle centered on the line of sight and having a radius no more than 20 percent of the radius of the inner periphery of the mask. In some cases, substantial alignment can be said to have been achieved when the mask axis is within a circle centered on the line of sight and having a radius no more than 25 percent of the radius of the inner periphery of the mask. In some cases, substantial alignment can be said to have been achieved when the mask axis is within a circle centered on the line of sight and having a radius no more than 30 percent of the radius of the inner periphery of the mask. As discussed above, the alignment of the mask axis and the line of sight of the patient is believed to enhance the clinical benefit of the mask.
In a step 1008, the mask is applied to the eye of the patient. Preferably the alignment of the optical axis of the mask and the line of sight of the patient is maintained while the mask is applied to the eye of the patient. In some cases, this alignment is maintained by maintaining the alignment of a mask feature, e.g., a visible mask feature, and a pupil feature, e.g., a visible pupil feature. For example, one technique maintains the alignment of at least one of the inner periphery and the outer periphery of the mask and the pupil while the mask is being applied to the eye of the patient.
As discussed above, a variety of techniques are available for applying a mask to the eye of a patient. Any suitable technique of applying a mask may be employed in connection with the method illustrated in
Thereafter, in one technique, the mask is placed on a layer of the cornea such that at least one of the inner periphery and the outer periphery of the mask is at a selected position relative to the pupil. In variations on this technique, other features of the mask may be aligned with other ocular features. Thereafter, the hinged corneal flap is placed over the mask.
Additional techniques for applying a mask are discussed above in connection with
Many additional variations of the foregoing methods are also possible. The alignment methods involving alignment of visible features may be combined with any of the techniques discussed above in connection with optically locating the patient's line of sight. One technique involves removing an epithelial sheet and creating a depression in the Bowman's membrane or in the stroma. Also, the mask can be placed in a channel formed in the cornea, e.g., in or near the top layers of the stroma. Another useful technique for preparing the cornea involves the formation of a pocket within the cornea. These methods related to preparation of the cornea are described in greater detail above.
Some techniques may benefit from the placement of a temporary post-operative covering, such as a contact lens or other covering, over the flap until the flap has healed. In one technique, a covering is placed over the flap until an epithelial sheet adheres to the mask or grows over an exposed layer, such as the Bowman's membrane.
B. Methods of Applying a Mask
Having described method for locating the visual axis of the eye 10 or a visible ocular feature that indicates the location thereof, and for visually marking the visual axis, various methods for applying a mask to the eye will be discussed.
In accordance with a still further embodiment of the invention, a mask is surgically implanted into the eye of a patient interested in increasing his or her depth of focus. For example, a patient may suffer from presbyopia, as discussed above. The mask may be a mask as described herein, similar to those described in the prior art, or a mask combining one or more of these properties. Further, the mask may be configured to correct visual aberrations. To aid the surgeon surgically implanting a mask into a patient's eye, the mask may be pre-rolled or folded for ease of implantation.
The mask may be implanted in several locations. For example, the mask may be implanted underneath the cornea's epithelium sheet, beneath the cornea's Bowman membrane, in the top layer of the cornea's stroma, or in the cornea's stroma. When the mask is placed underneath the cornea's epithelium sheet, removal of the mask requires little more than removal of the cornea's epithelium sheet.
In another embodiment, a mask of sufficient thinness, i.e., less than substantially 20 microns, may be placed underneath epithelium sheet 1210. In another embodiment, a mask or an optic having a thickness less than about 20 microns may be placed beneath Bowman's membrane 1320 without creating a depression in the top layer of the stroma.
In an alternate method for surgically implanting a mask in the eye of a patient, the mask may be threaded into a channel created in the top layer of the stroma. In this method, a curved channeling tool creates a channel in the top layer of the stroma, the channel being in a plane parallel to the surface of the cornea. The channel is formed in a position corresponding to the visual axis of the eye. The channeling tool either pierces the surface of the cornea or, in the alternative, is inserted via a small superficial radial incision. In the alternative, a laser focusing an ablative beam may create the channel in the top layer of the stroma. In this embodiment, the mask may be a single segment with a break, or it may be two or more segments. In any event, the mask in this embodiment is positioned in the channel and is thereby located so that the central axis of the pinhole aperture formed by the mask is substantially collinear with the patient's visual axis to provide the greatest improvement in the patient's depth of focus.
In another alternate method for surgically implanting a mask in the eye of a patient, the mask may be injected into the top layer of the stroma. In this embodiment, an injection tool with a stop penetrates the surface of the cornea to the specified depth. For example, the injection tool may be a ring of needles capable of producing a mask with a single injection. In the alternative, a channel may first be created in the top layer of the stroma in a position corresponding to the visual axis of the patient. Then, the injector tool may inject the mask into the channel. In this embodiment, the mask may be a pigment, or it may be pieces of pigmented material suspended in a bio-compatible medium. The pigment material may be made of a polymer or, in the alternative, made of a suture material. In any event, the mask injected into the channel is thereby positioned so that the central axis of the pinhole aperture formed by the pigment material is substantially collinear with the visual axis of the patient.
In another method for surgically implanting a mask in the eye of a patient, the mask may be placed beneath the corneal flap created during keratectomy, when the outermost 20% of the cornea is hinged open. As with the implantation methods discussed above, a mask placed beneath the corneal flap created during keratectomy should be substantially aligned with the patient's visual axis, as discussed above, for greatest effect.
In another method for surgically implanting a mask in the eye of a patient, the mask may be aligned with the patient's visual axis and placed in a pocket created in the cornea's stroma.
Further details concerning alignment apparatuses are disclosed in U.S. application Ser. No. 10/854,032, filed May 26, 2004, incorporated by reference herein in its entirety. Further variations on techniques involving pharmacologic manipulation for alignment or other purposes are discussed in U.S. application Ser. No. 11/257,505, filed Oct. 24, 2005, which is hereby incorporated by reference herein in its entirety.
VII. Further Methods of Treating a Patient
As discussed above in, various techniques are particularly suited for treating a patient by applying masks such as those disclosed herein to an eye. For example, in some techniques, a visual cue in the form of a projected image for a surgeon is provided during a procedure for applying a mask. In addition, some techniques for treating a patient involve positioning an implant with the aid of a marked reference point. These methods are illustrated by
In one method, a patient is treated by placing an implant 1400 in a cornea 1404. A corneal flap 1408 is lifted to expose a surface in the cornea 1404 (e.g., an intracorneal surface). Any suitable tool or technique may be used to lift the corneal flap 1408 to expose a surface in the cornea 1404. For example, a blade (e.g., a microkeratome), a laser or an electrosurgical tool could be used to form a corneal flap. A reference point 1412 on the cornea 1404 is identified. The reference point 1412 thereafter is marked in one technique, as discussed further below. The implant 1400 is positioned on the intracorneal surface. In one embodiment, the flap 1408 is then closed to cover at least a portion of the implant 1400.
The surface of the cornea that is exposed is a stromal surface in one technique. The stromal surface may be on the corneal flap 1408 or on an exposed surface from which the corneal flap 1408 is removed.
The reference point 1412 may be identified in any suitable manner. For example, the alignment devices and methods described above may be used to identify the reference point 1412. In one technique, identifying the reference point 1412 involves illuminating a light spot (e.g., a spot of light formed by all or a discrete portion of radiant energy corresponding to visible light, e.g., red light). As discussed above, the identifying of a reference point may further include placing liquid (e.g., a fluorescein dye or other dye) on the intracorneal surface. Preferably, identifying the reference point 1412 involves alignment using any of the techniques described herein.
As discussed above, various techniques may be used to mark an identified reference point. In one technique the reference point is marked by applying a dye to the cornea or otherwise spreading a material with known reflective properties onto the cornea. As discussed above, the dye may be a substance that interacts with radiant energy to increase the visibility of a marking target or other visual cue. The reference point may be marked by a dye with any suitable tool. The tool is configured so that it bites into a corneal layer, e.g., an anterior layer of the epithelium, and delivers a thin ink line into the corneal layer in one embodiment. The tool may be made sharp to bite into the epithelium. In one application, the tool is configured to deliver the dye as discussed above upon being lightly pressed against the eye. This arrangement is advantageous in that it does not form a larger impression in the eye. In another technique, the reference point may be marked by making an impression (e.g., a physical depression) on a surface of the cornea with or without additional delivery of a dye. In another technique, the reference point may be marked by illuminating a light or other source of radiant energy, e.g., a marking target illuminator and projecting that light onto the cornea (e.g., by projecting a marking target).
Any of the foregoing techniques for marking a reference point may be combined with techniques that make a mark that indicates the location of an axis of the eye, e.g., the visual axis or line-of-sight of the eye. In one technique, a mark indicates the approximate intersection of the visual axis and a surface of the cornea. In another technique, a mark is made approximately radially symmetrically disposed about the intersection of the visual axis and a surface of the cornea.
As discussed above, some techniques involve making a mark on an intracorneal surface. The mark may be made by any suitable technique. In one technique a mark is made by pressing an implement against the instracorneal surface. The implement may form a depression that has a size and shape that facilitate placement of a mask. For example, in one form the implement is configured to form a circular ring (e.g., a thin line of dye, or a physical depression, or both) with a diameter that is slightly larger than the outer diameter of a mask to be implanted. The circular ring can be formed to have a diameter between about 4 mm and about 5 mm. The intracorneal surface is on the corneal flap 1408 in one technique. In another technique, the intracorneal surface is on an exposed surface of the cornea from which the flap was removed. This exposed surface is sometimes referred to as a tissue bed.
In another technique, the corneal flap 1408 is lifted and thereafter is laid on an adjacent surface 1416 of the cornea 1404. In another technique, the corneal flap 1408 is laid on a removable support 1420, such as a sponge. In one technique, the removable support has a surface 1424 that is configured to maintain the native curvature of the corneal flap 1408.
In one technique, the corneal flap 1408 is closed by returning the corneal flap 1408 to the cornea 1404 with the implant 1400 on the corneal flap 1408. In another technique, the corneal flap 1408 is closed by returning the corneal flap 1408 to the cornea 1404 over the implant 1400, which previously was placed on the tissue bed (the exposed intracorneal surface).
When the intracorneal surface is a stromal surface, the implant 1400 is placed on the stromal surface. At least a portion of the implant 1400 is covered. In some techniques, the implant 1400 is covered by returning a flap with the implant 1400 thereon to the cornea 1404 to cover the stromal surface. In one technique, the stromal surface is exposed by lifting an epithelial layer to expose stroma. In another technique, the stromal surface is exposed by removing an epithelial layer to expose stroma. In some techniques, an additional step of replacing the epithelial layer to at least partially cover the implant 1400 is performed.
After the flap 1408 is closed to cover at least a portion of the implant 1400, the implant 1400 may be repositioned to some extent in some applications. In one technique, pressure is applied to the implant 1400 to move the implant into alignment with the reference point 1412. The pressure may be applied to the anterior surface of the cornea 1404 proximate an edge of the implant 1400 (e.g., directly above, above and outside a projection of the outer periphery of the implant 1400, or above and inside a projection of the outer periphery of the implant 1400). This may cause the implant to move slightly away from the edge proximate which pressure is applied. In another technique, pressure is applied directly to the implant. The implant 1400 may be repositioned in this manner if the reference point 1412 was marked on the flap 1408 or if the reference point 1412 was marked on the tissue bed. Preferably, pushing is accomplished by inserting a thin tool under the flap or into the pocket and directly moving the inlay.
After the implant 1500 is positioned in the pocket 1508, the implant 1500 may be repositioned to some extent in some applications. In one technique, pressure is applied to the implant 1500 to move the implant into alignment with the reference point 1512. The pressure may be applied to the anterior surface of the cornea 1504 proximate an edge of the implant 1500 (e.g., directly above, above and outside a projection of the outer periphery of the implant 1500, or above and inside a projection of the outer periphery of the implant 1500). This may cause the implant 1500 to move slightly away from the edge at which pressure is applied. In another technique, pressure is applied directly to the implant 1500.
The various methods and techniques described above provide a number of ways to carry out the invention. Of course, it is to be understood that not necessarily all objectives or advantages described may be achieved in accordance with any particular embodiment described herein. Thus, for example, those skilled in the art will recognize that the devices may be made that achieve or optimize one advantage or group of advantages as taught herein without necessarily achieving other objectives or advantages as may be taught or suggested herein.
Furthermore, the skilled artisan will recognize the interchangeability of various features from different embodiments. Similarly, the various features and steps discussed above, as well as other known equivalents for each such feature or step, can be mixed and matched by one of ordinary skill in this art to perform methods in accordance with principles described herein.
Although the invention has been disclosed in the context of certain embodiments and examples, it will be understood by those skilled in the art that the invention extends beyond the specifically disclosed embodiments to other alternative embodiments and/or uses and obvious modifications and equivalents thereof. Accordingly, the invention is not intended to be limited by the specific disclosures of preferred embodiments herein, but instead by reference to claims attached hereto.
Claims
1. A mask configured to be implanted in a cornea of a patient, the mask comprising:
- a body formed from a polymeric material, the body having a light transmitting portion, a light blocking portion disposed about the light transmitting portion, an outer periphery surrounding the light blocking portion, an anterior surface, and a posterior surface, the anterior surface configured to reside adjacent a first intracorneal layer, the posterior surface configured to reside adjacent a second intracorneal layer, wherein the polymeric material includes one or more polyanionic compounds loaded into the polymeric material.
2. The mask of claim 1, wherein the total weight of the one or more polyanionic compounds is about 5% by weight to about 20% by weight.
3. The mask of claim 1, wherein the total weight of the one or more polyanionic compounds is about 12% by weight to about 17% by weight.
4. The mask of claim 1, wherein the one or more polyanionic compounds comprise proteoglycans or glycosaminoglycans.
5. The mask of claim 1, wherein the one or more polyanionic compounds includes at least one compound selected from the group consisting of dermatan sulfate, chondroitin sulfate, keratan sulfate, heparan sulfate, heparin, dextran sulfate, hyaluronic acid, pentosan polysulfate, xanthan, carrageenan, fibronectin, laminin, chondronectin, vitronectin, poly L-lysine salts, and alginate.
6. The mask of claim 1, wherein the one or more polyanionic compounds comprises dextran sulfate.
7. The mask of claim 1, wherein the polymeric material comprises a highly fluorinated polymeric material.
8. The mask of claim 7, wherein the highly fluorinated polymeric material comprises polyvinylidene fluoride (PVDF).
9. The mask of claim 1, wherein the material forming the light blocking portion of the body comprises an opacification agent selected from the group consisting of organic dyes organic pigments, inorganic dyes, and inorganic pigments.
10. The mask of claim 9, wherein the opacification agent comprises carbon.
11. The mask of claim 10, further comprising at least one wound healing modulator compound.
12. The mask of claim 11, wherein at least a portion of the wound healing modulator compound is adsorbed to the carbon.
13. The mask of claim 11, wherein the wound healing modulator compound is selected from the group consisting of antibiotics, antineoplastics, antimitotics, antimetabolics, anti-inflammatories, immunosupressants, and antifungals.
14. The mask of claim 13, wherein the wound healing modulator compound is selected from the group consisting of fluorouracil, mitomycin C, paclitaxel, ibuprofen, naproxen, flurbiprofen, carprofen, suprofen, ketoprofen, and cyclosporins.
15. The mask of claim 1, wherein the light transmitting portion comprises a substantially circular aperture that is sized to transmit a fraction of the light incident on the anterior surface.
16. The mask of claim 1, wherein the body comprises a plurality of holes extending at least partially between the anterior surface and the posterior surface.
17. The mask of claim 1, wherein the polymeric material includes a UV absorbing component.
18. A mask configured to be implanted in a cornea of a patient, the mask comprising:
- a body formed from a material comprising a highly fluorinated polymeric material, the body having a light transmitting portion, a light blocking portion disposed about the light transmitting portion, and outer periphery surrounding the light blocking portion, an anterior surface, and a posterior surface, the anterior surface configured to reside adjacent a first intracorneal layer, the posterior surface configured to reside adjacent a second intracorneal layer, wherein the material comprising a highly fluorinated polymeric material has loaded therein one or more polyanionic compounds.
19. The mask of claim 18, wherein the one or more polyanionic compounds comprise proteoglycans or glycosaminoglycans.
20. The mask of claim 18, wherein the one or more polyanionic compounds are selected from the group consisting of dermatan sulfate, chondroitin sulfate, keratan sulfate, heparan sulfate, heparin, dextran sulfate, hyaluronic acid, pentosan polysulfate, xanthan, carrageenan, fibronectin, laminin, chondronectin, vitronectin, poly L-lysine salts, and alginate.
21. The mask of claim 18, wherein the one or more polyanionic compounds comprises dextran sulfate.
22. The mask of claim 18, wherein the total weight of the one or more polyanionic compounds is about 10% by weight to about 20% by weight.
23. The mask of claim 18, wherein the highly fluorinated polymeric material comprises PVDF.
24. The mask of claim 18, wherein the material forming the light blocking portion of the body comprises an opacification agent selected from the group consisting of organic dyes organic pigments, inorganic dyes, and inorganic pigments.
25. The mask of claim 24, wherein the opacification agent is carbon.
26. The mask of claim 25, further comprising at least one wound healing modulator compound.
27. The mask of claim 26, wherein at least a portion of the wound healing modulator compound is adsorbed to the carbon.
28. The mask of claim 26, wherein the wound healing modulator compound is selected from the group consisting of antibiotics, antineoplastics, antimitotics, antimetabolics, anti-inflammatories, immunosupressants, and antifungals.
29. The mask of claim 28, wherein the wound healing modulator compound is selected from the group consisting of fluorouracil, mitomycin C, paclitaxel, ibuprofen, naproxen, flurbiprofen, carprofen, suprofen, ketoprofen, and cyclosporins.
30. The mask of claim 18, wherein the light transmitting portion comprises a substantially circular aperture that is sized to transmit a fraction of the light incident on the anterior surface.
31. The mask of claim 18, wherein the material further comprises a second polymeric material.
32. The mask of claim 31, wherein the second polymeric material includes a UV absorbing component.
33. A mask comprising:
- an aperture having a major axis of about 2.2 mm or less; and
- an annular body extending between the aperture and an outer periphery of the mask, the annular body having an anterior surface and a posterior surface, the annular body being formed of a material comprising:
- a highly fluorinated polymeric material;
- an opacification agent, the opacification agent being present in sufficient quantity to prevent at least a substantial portion of light incident on the anterior surface from being transmitted from the anterior surface to the posterior surface; and
- one or more polyanionic compounds and/or wound healing modulator compounds.
34. The mask of claim 33, wherein the total weight of the one or more polyanionic compounds is about 5% by weight to about 20% by weight.
35. The mask of claim 33, wherein the total weight of the one or more polyanionic compounds is about 12% by weight to about 17% by weight.
36. The mask of claim 33, wherein the one or more polyanionic compounds comprise proteoglycans or glycosaminoglycans.
37. The mask of claim 33, wherein the one or more polyanionic compounds are selected from the group consisting of dermatan sulfate, chondroitin sulfate, keratan sulfate, heparan sulfate, heparin, dextran sulfate, hyaluronic acid, pentosan polysulfate, xanthan, carrageenan, fibronectin, laminin, chondronectin, vitronectin, poly L-lysine salts, and alginate.
38. The mask of claim 33, wherein the one or more polyanionic compounds comprises dextran sulfate.
39. The mask of claim 33, wherein the highly fluorinated polymeric material comprises PVDF.
40. The mask of claim 33, wherein the opacification agent is selected from the group consisting of organic dyes organic pigments, inorganic dyes, and inorganic pigments.
41. The mask of claim 40, wherein the opacification agent is carbon.
42. The mask of claim 41, further comprising at least one wound healing modulator compound.
43. The mask of claim 42, wherein at least a portion of the wound healing modulator compound is adsorbed to the carbon.
44. The mask of claim 42, wherein the wound healing modulator compound is selected from the group consisting of antibiotics, antineoplastics, antimitotics, antimetabolics, anti-inflammatories, immunosupressants, and antifungals.
45. The mask of claim 44, wherein the wound healing modulator compound is selected from the group consisting of fluorouracil, mitomycin C, paclitaxel, ibuprofen, naproxen, flurbiprofen, carprofen, suprofen, ketoprofen, and cyclosporins.
46. The, mask of claim 33, wherein the anterior surface is configured to reside adjacent a first intracorneal layer of a cornea, and the posterior surface is configured to reside adjacent a second intracorneal layer.
47. The mask of claim 46, wherein the mask does not substantially alter the curvature of a cornea following application of the mask to a cornea.
48. The mask of claim 33, wherein the annular body has a substantially constant thickness between the anterior and posterior surfaces.
49. The mask of claim 33, wherein the annular body has a thickness between the anterior and posterior surfaces of about 20 microns or less.
50. The mask of claim 33, wherein the annular body has a thickness between the anterior and posterior surfaces of about 8 microns.
51. A mask configured to be implanted in a cornea of a patient, the mask comprising:
- a body formed from a polymeric material, the body having a light transmitting portion, a light blocking portion disposed about the light transmitting portion, an outer periphery surrounding the light blocking portion, an anterior surface configured to reside adjacent a first intracorneal layer, a posterior surface configured to reside adjacent a second intracorneal layer, and at least one wound healing modulator loaded in the polymeric material and/or bound to at least one of the anterior surface and the posterior surface.
52. The mask of claim 51, wherein at least the light blocking portion comprises carbon.
53. The mask of claim 52, wherein at least a portion of the wound healing modulator compound is adsorbed to the carbon.
54. The mask of claim 51, wherein the wound healing modulator compound is selected from the group consisting of antibiotics, antineoplastics, antimitotics, antimetabolics, anti-inflammatories, immunosupressants, and antifungals.
55. The mask of claim 54, wherein the wound healing modulator compound is selected from the group consisting of fluorouracil, mitomycin C, paclitaxel, ibuprofen, naproxen, flurbiprofen, carprofen, suprofen, ketoprofen, and cyclosporins.
56. The mask of claim 51, wherein the polymeric material is UV-resistant and/or includes a UV absorbing component.
57. The mask of claim 56, wherein the polymeric material comprises a highly fluorinated polymeric material.
58. The mask of claim 57, wherein the highly fluorinated polymeric material comprises polyvinylidene fluoride (PVDF).
59. The mask of claim 51, wherein the light transmitting portion comprises a substantially circular aperture that is sized to transmit a fraction of the light incident on the anterior surface.
60. The mask of claim 51, wherein the body comprises a plurality of holes extending at least partially between the anterior surface and the posterior surface.
61. The mask of claim 51, wherein polymeric material comprises one or more polyanionic compounds.
62. The mask of claim 61, wherein the total weight of the one or more polyanionic compounds is about 5% by weight to about 20% by weight.
63. The mask of claim 61, wherein the one or more polyanionic compounds comprise proteoglycans or glycosaminoglycans.
64. The mask of claim 61, wherein the one or more polyanionic compounds includes at least one compound selected from the group consisting of dermatan sulfate, chondroitin sulfate, keratan sulfate, heparan sulfate, heparin, dextran sulfate, hyaluronic acid, pentosan polysulfate, xanthan, carrageenan, fibronectin, laminin, chondronectin, vitronectin, poly L-lysine salts, and alginate.
65. The mask of claim 61, wherein the one or more polyanionic compounds comprises dextran sulfate.
Type: Application
Filed: Apr 13, 2006
Publication Date: Nov 23, 2006
Inventor: Thomas Silvestrini (Alamo, CA)
Application Number: 11/404,048
International Classification: A61F 2/14 (20060101); G02C 7/16 (20060101); A61F 2/16 (20060101);