Elastic Laminates and Methods of Manufacturing Same
A method for forming an elastic laminate comprising: bonding a first nonwoven to an elastic film to form a laminate; activating the laminate to form an activated laminate; and bonding a consolidated nonwoven to the elastic film of the activated laminate to form the elastic laminate.
Latest Tredegar Film Products Corporation Patents:
This application claims priority to U.S. Provisional Application No. 60/740,036, filed Nov. 28, 2005, which is hereby incorporated by reference.
FIELD OF INVENTIONThe present invention relates generally to elastic laminates and their methods of manufacture, and, more particularly, to breathable elastic laminates having nonwoven surfaces on both sides.
BACKGROUND OF INVENTIONBreathable elastic laminates are used in the manufacture of many goods, including, for example, disposable articles such as diapers, feminine sanitary articles, and bandages. These applications require that the laminate be strong, stretchable, and soft to the touch. Improving one of these features, however, tends to diminish the others. Consequently, previously-introduced laminates tend to represent a compromise among softness, elasticity, and strength.
For example, one prior art laminate comprises an apertured elastic laminate produced by vacuum laminating a carded polypropylene nonwoven to a multilayer coextruded elastic film. The laminate is then activated in the cross direction using intermeshing gears. This construction has the advantage of a soft feel, but is limited to two layers (nonwoven and film) and lacks high peel strength.
Another prior art product comprises an apertured elastic film which is activated in the cross direction (CD) and is ultrasonically bonded on each side to a consolidated nonwoven. Although this laminate tends to be strong, it has a harsher feel than desired, requires substantial ultrasonic energy to bond the layers, and, because it has three layers, it tends to lack the level of stretch obtainable from a laminate with just a single layer of nonwoven.
Therefore, there is a need for a breathable laminate that is soft on either side yet stretchable and strong. The present invention fulfills this need among others.
SUMMARY OF INVENTIONThe invention relates to an elastic laminate having soft, nonwoven surfaces on both sides, yet is stretchable and strong. Specifically, the elastic laminate comprises an elastic inner layer and two outer nonwoven layers, in which each nonwoven layer is rendered extensible through a different method. That is, one nonwoven layer is activated, while the other is consolidated.
Applicants have discovered unexpectedly that the laminate of the present invention has an exceptional degree of cross direction stretch, offers a pleasant, soft feel, and can be bonded ultrasonically at full line speed to obtain an exceptionally strong interlayer bond. Without being bound to any particular theory, applicants hypothesize that the high level of stretch results from “elasticizing” the two nonwoven layers using two different techniques—i.e., activation and consolidation. This approach synergistically combines the strengths of the two technologies, resulting in a laminate having the high tensile strength and a strong bond characteristic of a consolidated/ultrasonically bonded nonwoven, and the softness and tear resistance characteristic of an activated nonwoven. Furthermore, this approach appears to minimize the observed tendency of one nonwoven layer to constrain the extensibility of the other nonwoven layer in the same laminate.
Accordingly, one aspect of the invention is an elastic laminate having two outer nonwoven layers which are rendered extensible using two different techniques. In a preferred embodiment, the elastic laminate comprises: (1) an elastic layer having a first and second side; (2) an activated nonwoven layer bonded to the elastic layer on the first side; and (3) a consolidated nonwoven layer bonded to the elastic layer on the second side.
Another aspect of the invention is a method for producing the laminate described above. In a preferred embodiment, the method comprises: (1) bonding a first nonwoven to an elastic film to form a laminate; (2) activating the laminate to form an activated laminate; and (3) bonding a consolidated nonwoven to the elastic film of the activated laminate to form the elastic laminate.
DESCRIPTION OF DRAWINGS
The present invention relates to an elastic laminate and a method for making it. Briefly, referring to
Referring to
Referring back to
The form of an elastic layer 12 can vary and may include, for example, elastic strands, elastic nonwoven, elastic film, elastic adhesive, elastic tacky polymeric web, elastic scrim, etc. For the sake of simplicity, unless otherwise noted, these different forms are referred to collectively herein as “elastic film.” In certain preferred embodiments, a monolayer elastic film is used. It should be understood, however, that the present invention in not limited to a monolayer film and, in certain applications, a film having multiple layers may be used. For example, it may be advantageous to have an elastic core between two skin layers to enhance bonding to the nonwoven layers or to facilitate processability. Suitable skin layers are well known and include, for example, polyethylene which may be more or less elastic than the elastic material. The thickness of the elastic film may vary according to the application, although the individual layers of the films are typically thin (e.g., the elastic core is usually, but not necessarily, less than 100 microns, and skin layers, if used, are usually less than 20 microns).
Preferably, the elastic film is breathable or is modified to be breathable in conventional ways. Such ways include, for example, aperturing, slitting, or impregnating with granular particles to create microvoids upon stretching of the elastic film.
The first nonwoven layer 16 provides a soft and breathable surface once activated (discussed below) on the first side 14 of the elastic layer. Suitable nonwovens are capable of being activated and are less elastic than the elastic layer 12. Suitable nonwovens include loose fibers and webs prepared using know techniques such as, for example, air laying, spun bond, spun lace, bonded melt blown, thermobond, bonded carded. The nonwoven material may be homogeneous or contain a variety of woven materials including bi-component fibers (e.g. having an inner core of one material and an outer core of a second material), fibers of different morphologies, geometries, and surface finishes. Suitable nonwovens materials include, for example, fibrous polyolefins such as polyethylenes and polypropylenes, and natural fibers such as cotton and cellulose.
The consolidated nonwoven 17, like the first nonwoven 16, provides a soft and breathable covering to the second side 15 of the elastic layer 12. Unlike the first nonwoven, the consolidated nonwoven is rendered extensible through a consolidation method rather than an activation method. The consolidation method is discussed in detail below.
The laminate 10 may be used in any application requiring a soft, stretchable, breathable material, and especially well suited for disposable articles given its relatively low cost. Suitable applications include, for example, absorbent articles, including adult, child or infant incontinent products (diapers, including parts such as diaper ears, tabs, and/or side panels, briefs, etc.); wraps, including sterile and nonsterile (e.g. bandages with and without absorbent sections,) as well as other disposable and/or multiple use products; e.g., articles proximate to a human or animal body, such as (e.g., garments, apparel, including undergarments, under- and outer-wear, for example, undershirts, bras, briefs, panties, etc., bathing suits, overalls, socks, head coverings and bands, hats, mitten and glove liners, medical clothing, etc.) bed sheets; medical drapes; packaging materials; protective covers; household; office; medical or construction materials; wrapping materials; etc. therapeutic devices and wraps.
The method of making the laminate is described below with reference to
The first nonwoven source 70 provides the first nonwoven 50. In this embodiment, the first nonwoven source 70 comprises a roll of material, however, any suitable source may be used, including forming the material in situ.
The first nonwoven 50 is brought into contact with elastic film 60 and bonded thereto. In this embodiment, the molten or semimolten phase of elastic film 60 facilitates bonding with the first nonwoven 50. The first nonwoven 50 may also be bound, in whole or part, to the elastic layer using other conventional methods, such as hot pin aperturing, adhesive bonding, thermal bonding, ultrasonic bonding, and combination thereof.
Optionally, the elastic film 60 is modified to render it breathable. One preferred approach for aperturing the elastic layer is shown in
The pressure differential source 30 is well known. In a preferred embodiment, the pressure differential source 30 comprises a vacuum (not shown) and an aperture definition device 120. In this embodiment, aperture definition device 120 comprises a screen with 20 apertures per linear inch in a square pattern, referred to herein as 20 square. Other screen geometries may be used to vary the amount of open area, aperture size, geometries, patterns, and other attributes. Furthermore, more than one aperture definition device may be used, for example, a device in one area may provide one pattern of apertures, and a device in another area may provide another desired pattern.
In certain embodiments, it may be desired to modify the elastic layer to make it breathable before it is bonded to the first nonwoven layer. Furthermore, it may preferable to use other known aperturing techniques such as pin rolls, slitting, hydrojets, or lasers, instead of or in addition to a pressure differential source to impart permeability or breathability to the laminate. It should also be understood that modifying the elastic film to render it breathable is not required if the elastic film comprises elastic strands or scrim in which case it is already breathable.
Pressure source 35 provides pressure to the materials. A nip roll is used in the preferred embodiments, although any suitable source may be used as a pressure source. Additionally, some embodiments may dispense with a pressure source, or use a pressure differential source as a pressure source as well. Moreover, pressure source 35 is shown here upstream of the pressure differential source, although it may be located adjacent to the pressure differential source 30 or down stream of the pressure differential source 30.
Once the elastic layer is bound to the first nonwoven, it is activated. Referring back to
Returning now to the embodiment of
In one embodiment, the second nonwoven 55 is consolidated on-line. Consolidation may be performed using various techniques such as heat consolation, cold drawing, or combing. Preferably, heat consolidation is used which is disclosed, for example, in U.S. Pat. No. RE 35,206, which is hereby incorporated by reference. As shown in
The consolidated nonwoven 91 is brought into contact with activated laminate 75 through rollers 81 and 82 and bonded using known techniques. Preferably, the consolidated nonwoven 91 and laminate 75 are bonded ultrasonically in the ultrasonic bonding area 85. It has been found that this bonding can be performed quickly at normal line speeds, e.g., 70 mpm.
Varying the materials and method conditions may vary the characteristics of the laminate. For example, selection of particular elastic and/or nonwovens, or selective processing of those materials, can result in optimization of desired properties such as bond strength, softness, elasticity, breathability, etc. Examples of method variables that may be used to modify laminate characteristics include modifying the phase of the elastic layer prior to bonding; modifying the pressure differential applied by a pressure differential source; modifying pressure imposed by a pressure source; modifying apertures in a nonwoven; modifying apertures provided in an aperture definition device; various secondary treatments of the laminate and/or components of the laminate (e.g. plasma treatment), modifying stretching of a laminate following lamination, and combinations thereof. A laminate may also be modified in any suitable fashion, for example, a laminate may be sewn, bonded, printed, cut, shaped, glued, fluted, sterilized, etc.
Although the present invention has been described with respect to various specific embodiments, various modifications will be apparent from the present disclosure and are intended to be within the scope of the following claims.
Claims
1. A method for forming an elastic laminate comprising:
- bonding a first nonwoven to an elastic film to form a laminate;
- activating said laminate to form an activated laminate; and
- bonding a consolidated nonwoven to said elastic film of said activated laminate to form said elastic laminate.
2. The method of claim 1, wherein said elastic film is apertured.
3. The method of claim 2, wherein said elastic film is bonded to said first nonwoven and apertured essentially simultaneously.
4. The method of claim 3, wherein said first nonwoven and said elastic film are apertured essentially simultaneously.
5. The method of claim 3, wherein vacuum lamination is used to bond said first nonwoven to said elastic film and to aperture said elastic film.
6. The method of claim 2 wherein the elastic film is apertured after the first bonding step.
7. The method of claim 2, wherein the elastic film is apertured before the first bonding step.
8. The method of claim 1, wherein activating said laminate comprises activating said laminate in the cross direction.
9. The method of claim 8, wherein said laminate is activated using intermeshing gear activation.
10. The method of claim 1, wherein said consolidated nonwoven is extensible in said cross direction.
11. The method of claim 1, wherein at least one of said bonding steps comprises ultrasonic bonding.
12. The method of claim 11, wherein said bonding of said consolidated nonwoven is performed ultrasonically.
13. The method of claim 1, wherein said bonding of said consolidated nonwoven is performed at essentially the same line speed as said activation step.
14. An elastic laminate comprising:
- an elastic layer having a first side and a second side;
- an activated nonwoven layer bonded to said elastic layer on said first side; and
- a consolidated nonwoven layer bonded to said elastic layer on said second side.
15. The elastic laminate of claim 14, wherein said elastic layer is breathable.
16. The elastic laminate of claim 15, wherein said elastic layer is apertured.
17. The elastic laminate of claim 14, wherein said activated nonwoven layer is a carded nonwoven.
18. The elastic laminate of claim 17, wherein said activated nonwoven layer is polypropylene.
19. The elastic laminate of claim 14, wherein said activated nonwoven layer is extensible in a first direction, and said consolidated nonwoven layer is extensible in said first direction.
Type: Application
Filed: Nov 28, 2006
Publication Date: May 31, 2007
Applicant: Tredegar Film Products Corporation (Richmond, VA)
Inventors: Jeffrey Middlesworth (Wauconda, IL), Bryan Matte (Kenosha, WI)
Application Number: 11/563,953
International Classification: B32B 5/02 (20060101);