POLYAMIDE MOULDING COMPOUND AND USE THEREOF

Abstract

The present invention relates to polyamide moulding compounds which have very low distortion with good mechanical properties. This is achieved by a combination of transparent polyamide with fibrous reinforcing materials and also particulate fillers. The moulding compounds according to the invention are used for the production of any moulded articles, semi-finished products or finished products.

Description

The present invention relates to polyamide moulding compounds which have very low distortion with good mechanical properties. This is achieved by a combination of transparent polyamide with fibrous reinforcing materials and also particulate fillers. The moulding compounds according to the invention are used for the production of any moulded articles, semi-finished products or finished products.

Polyamides are widespread nowadays as structural elements for the interior and exterior sphere, which can be attributed essentially to the outstanding mechanical properties.

An improvement in the mechanical properties, such as strength and rigidity, can be achieved in particular by the addition of fibrous reinforcing materials, e.g. glass fibres. However frequently increased distortion of the moulded parts is associated with the addition of fibrous reinforcing materials. The consequence of this is that only small contents of fibrous reinforcing materials, or rather only isotropic fillers, such as glass balls, can be used if distortion is regarded as a critical parameter for the moulded part The moulding compounds obtained in this way then have only a low modulus of elasticity in tension in the moulded part.

The addition of particulate fillers effects, on the one hand, a reduction in the distortion but leads, on the other hand, to an impairment with respect to the mechanical properties, such as strength and breaking elongation.

Starting herefrom, it was the object of the present invention to provide polyamide moulding compounds with which there can be produced moulded articles with good mechanical properties and at the same time low distortion and which do not have the previously described disadvantages of the state of the art.

This object is achieved with respect to the polyamide moulding compound by the features of claim 1, with respect to the moulded articles by the features of claim 15 and with respect to use by the features of claim 20. The further dependent claims reveal advantageous developments.

The polyamide moulding compound according to the invention comprises 40 to 79% by weight at least of a transparent polyamide, 15 to 49% by weight at least of a fibrous reinforcing material and 6 to 30% by weight of a particulate filler. In addition, further additives can be contained as complement to 100% by weight. Preferred compositions comprise 40 to 69% by weight, preferably 40 to 55% by weight, of the transparent polyamide, 25 to 49% by weight, preferably 30 to 49% by weight, of the fibrous reinforcing material, 6 to 30% by weight of the particulate filler and also if necessary, as complement to 100% by weight, at least one further additive. However there should not be understood as additives within the scope of the present invention polyamide oligomers.

A particular feature of the present invention is that good mechanical properties can be achieved by moulded articles produced herefrom by the claimed combination on the one hand and the moulded articles according to the invention have at the same time a substantially lower distortion in comparison with known moulded articles.

With respect to the fibrous reinforcing materials, basically no restrictions exist. Preferably, these are selected from the group comprising glass fibres, carbon fibres, metal fibres, aramide fibres, whiskers and mixtures thereof. There should be understood by whiskers needle-like monocrystals comprising metals, oxides, borides, carbides, nitrides, polytitanate, carbon etc. with a generally polygonal cross-section, e.g. potassium nitanate-, aluminium oxide-, silicon carbide-whiskers. In general, whiskers have a diameter of 0.1 to 10 μm and a length in the mm to cm range. At the same time, they have high tensile strength. Whiskers can be produced by deposition from the gas phase in the solid (VS mechanism) or from a three-phase system (VLS mechanism).

The glass fibres preferably have a diameter of 5 to 20 μm and particularly preferred of 5 to 10 μm. Preferably, glass fibres with a round, oval or rectangular cross-section are used. The glass fibres thereby comprise preferably E-glass. The glass fibres can thereby be added as endless fibres or as cut glass fibres, the fibres being able to be equipped with a suitable sizing system and a bonding agent or bonding agent system, e.g. on a silane basis.

All the fillers known to the person skilled in the art are possible as particulate fillers. There are included herein in particular particulate fillers selected from the group comprising talcum, mica, silicates, quartz, titanium dioxide, wollastonite, kaolin, silicic acids, magnesium carbonate, magnesium hydroxide, chalk, ground or precipitated calcium carbonate, lime, feldspar, barium sulphate, permanently magnetic or magnetisable metals or alloys, glass balls, hollow glass balls, hollow spherical silicate fillers and mixtures thereof.

Transparent polyamides in the sense of the present invention are polyamides which have a defined light transmission.

In particular the polyamides, the light transmission of which is at least 70%, are included herein if the polyamide is present in the form of a plate, e.g. a round plate, with a thickness of 2 mm. Round plates of 75×2 mm are produced on an Arburg injection moulding machine in the polished mould, the cylinder temperature being between 240 and 340° C. and the mould temperature between 20 and 140° C. The measurement of the light transmission is implemented according to ASTM D 1003-61 on the measuring apparatus Haze Gard plus by the Byk Gardner company with CIE light type C at 23° C. The light transmission value is thereby indicated in % of the irradiated light quantity.

Preferably transparent polyamides which have a light transmission of at least 86%, particularly preferred of at least 90%, are used.

No restrictions exist with respect to the composition of the transparent polyamides so that all the transparent polyamides or mixtures thereof which are known to the person skilled in the art can be used. There are included herein in particular the polyamides which are produced from at least one diamine and at least one dicarboxylic acid and/or at least one amino acid or a lactam. There are preferred hereby as diamine aliphatic and/or cycloaliphatic diamines with 6 to 17 C-atoms and/or diamines (C₆-C₁₇) with partially aromatic structures. There are used preferably as dicarboxylic acids aliphatic and/or aromatic dicarboxylic acids with 6 to 12 C-atoms. The amino acids are selected preferably from the group of α, Ω amino acids with 6 to 12 C-atoms. The lactams are preferably selected from the group of lactams with 6 to 12 C-atoms.

The transparent polyamides have a relative viscosity of 1.36-1.80, preferably 1.36-1.74, particularly preferred 1.41-1.69. The relative viscosity is thereby determined according to DIN EN ISO 307, in 0.5% m-cresol solution at 20° C.

The transparent polyamides have a glass transition temperature (Tg) of at least 120° C., preferably at least 130° C. The glass transition temperature is thereby determined by means of differential scanning calorimetry (DSC) at a heating rate of 20° C./min according to the ISO standard 11357-1/-2. The temperature at the turning point is indicated.

Transparent, amorphous polyamides are preferred. There are included herein in particular the polyamides which, in the dynamic differential scanning calorimetry (DSC) according to ISO 1357-1/-2, at a heating rate of 20° C./min, have a melting heat of at most 5 J/g, preferably at most 3 J/g and particularly preferred at most 1 J/g.

The transparent amorphous polyamides are produced preferably from at least one diamine and at least one dicarboxylic acid and/or at least one amino acid or a lactam. Aliphatic and/or cycloaliphatic diamines with 6 to 17 C-atoms and/or diamines (C₆-C₁₇) with partially aromatic structures are preferred as diamine. There are used preferably as dicarboxylic acids aliphatic and/or aromatic dicarboxylic acids with 6 to 12 C-atoms. The amino acids are selected preferably from the group α, ω amino acids with 6 to 12 C-atoms. The lactams are selected preferably from the group of lactams with 6 to 12 C-atoms

The transparent amorphous polyamides have a relative viscosity of 1.36-1.80, preferably 1.36-1,74, particularly preferred 1.41-1.69. The relative viscosity is thereby determined according to DIN EN ISO 307, in 0.5% m-cresol solution at 20° C.

The transparent amorphous polyamides have a glass transition temperature (Tg) of at least 120° C., preferably at least 130° C. The glass transition temperature is thereby determined by means of differential scanning calorimetry (DSC) at a heating rate of 20° C./min according to the ISO standard 11357-1/-2. The temperature at the turning point is indicated.

Preferred transparent amorphous polyamides are selected from the following group: PA 6I, PA 6I/6T, PA MXDI/6I, PA MXDI/MXDT/6I/6T, PA MXDI/12I, PA MXDI, PA MACM12, PA MACMI/12, PA MACMI/MACMT/12, PA 6I/MACMI/12, PA 6I/6T/MACMI/MACMT, PA 6I/6T/MACMI/MACMT/12, PA MACM6/11, PA MACMI/MACM12 and mixtures thereof. The MACM can thereby be replaced by PACM up to 55% by mol, in particular up to 50% by mol.

In specially preferred embodiments there are used as base material MACM-containing transparent amorphous polyamides or mixtures thereof which have respectively a relative viscosity of 1.41-1.69, preferably 1.49-1.69. Their glass transition temperature is at least 130° C., preferably at least 145° C.

In a further particular embodiment, a transparent amorphous polyamide is used as base material from the group MACM 12, MACMI/12 and mixtures thereof which have respectively a relative viscosity of 1.41-1.69, preferably 1.49-169. Their glass transition temperature is at least 130° C., preferably at least 145° C.

Of course the thermoplastic polyamide moulding compounds according to the invention can contain in addition normal additives which are known in general to the person skilled in the art and are selected from the group comprising impact strength modifiers, preferably so-called MBS or core-outer layer impact strength modifiers, e.g. based on methacrylate-butadiene-styrene, bonding agents, halogen-containing flameproofing agents, halogen-free flameproofing agents, stabilisers, age-protecting agents, antioxidants, antiozonants, light protection agents, UV stabilisers, UV absorbers, UV blockers, inorganic heat stabilisers, organic heat stabilisers, conductivity additives, carbon black, optical lighteners, processing aids, nucleation agents, crystallisation accelerators, crystallisation inhibitors, flow aids, lubricants, mould-release agents, softeners, pigments, colourants, marking materials and mixtures thereof.

The polyamide moulding compounds according to the invention can contain, for specific purposes, in addition also other polymers, such as polyolefins, AN polymers, functionalised copolyolefins and ionomers.

Further embodiments provide that the polyamide moulding compound contains from 21 to 60% by weight, preferably from 31 to 60% by weight, specially preferred from 45 to 60% by weight, particularly preferred from 45 to 55% by weight, of the fibrous reinforcing materials and the particulate fillers in total.

The reinforcing materials are always present in at least the same quantity (% by weight) as the fillers.

The invention comprises in addition moulded articles produced with the above-described moulding compound. These moulded articles preferably have a distortion of ≦2.7 %, particularly preferred ≦2.3%. It should be emphasised thereby that, despite this low distortion, the mechanical properties of the moulded articles remain unaffected. Thus the moulded article preferably has a modulus of elasticity in tension of ≧8000 MPa, in particular ≧10000 MPa. With respect to the tensile strength, values ≧100 MPa, and in particular ≧140 MPa are preferred. The polyamide moulding compound preferably has a breaking elongation of ≧1.5%, particularly preferred ≧2.0%.

Finally the invention also relates to the use of the above-described moulding compounds for the production of distortion-free moulded articles. The moulded articles are hereby selected preferably from the group comprising precisely fitting parts, mutually moveable parts, functional elements, operating elements, tracking elements, adjustment elements, carrier elements, frame elements, switches and housings in the field of electrics, electronics, energy and drive technology, mechanical engineering, automobiles, furniture, sport, sanitary, hygiene, medical technology, transport means, telecommunications, entertainment electronics, domestic appliances or electrical tools, produced by injection moulding, extrusion or other shaping technologies, e.g. functional carriers in the cockpit area of an automobile, frame components of a sewing machine, mobile phone housings.

The production of the polyamide moulding compounds according to the invention can be effected on normal compounding machines, such as e.g. single or twin-screw extruders or screw kneaders. As a rule, initially the polymer component is melted and the reinforcing material and/or filler is fed into the melt at any points of the extruder, e.g. by means of a side feeder. The compounding is effected preferably at set cylinder temperatures of 260° C. to 320° C. The polymer component and the reinforcing material and/or filler can however also all be metered into the feed.

The present invention is intended to be explained in more detail with reference to the subsequent examples without wishing to restrict the latter by the special embodiments shown here.

The moulding compounds were produced on a twin-screw extruder of the company Werner & Pfleiderer, type ZSK 25. Both the polyamide granulates and the mineral were thereby metered into the feed via separate scales. The glass fibre was conveyed into the polymer melt via a side feeder 6 housing units before the nozzle.

The temperature of the first housing was set at 100° C., that of the remaining housings at 280° C. A speed of rotation of 200 rpm and a throughput of 10 kg/h was used and degassed atmospherically. The strands were cooled in the water bath, cut and the obtained granulate was dried at 120° C. for 24 h.

The thus produced moulding compounds were processed as follows into test bodies and tested.

Processing

The standard test bodies were produced on an injection moulding machine of the Arburg company, model Allrounder 320-210-750 Hydronica. In the case of moulding compounds without PA 66, a material temperature of 275-300° C. and a mould temperature of 80° C. was used. In the case of moulding compounds with PA 66, 300-308° C. and 100° C.

“Visitor card holders” were produced on an injection moulding machine of the Ferromatik company, model K85 D-S/2F, at set cylinder temperatures of 270-290° C. and a mould temperature of 80-100° C.

Tests

Distortion:

The distortion was determined by means of an injection-moulded “Visitor card holder” (see FIG. 1 in this respect). After storage of 14 days in a normal atmosphere (23° C., 50% relative humidity), the width is measured and compared to the mould dimension (width of the cavity: 90.2 mm). The greater the difference, the greater is the distortion.

Modulus of elasticity in tension:

ISO 527 at a tension rate of 1 mm/min

ISO-test bar, standard: ISO/CD 3167, type A1, 170×20/10×4 mm, temperature 23° C.

Tensile Strength and Breaking Elongation:

ISO 527 at a tension rate of 50 mm/min

ISO-test bar, standard: ISO/CD 3167, type A1, 170×20/10×4 mm, temperature 23° C.

Impact Strength According to Charpy:

ISO 179/1eU

ISO-test bar, standard: ISO/CD 3167, type B1, 80×10×4 mm, temperature 23° C.

Notch-Impact Strength According to Charpy:

ISO 179/1eA

ISO-test bar, standard: ISO/CD 3167, type B1, 80×10×4 mm, temperature 23° C.

All the test bodies, apart from the “Visitor card holders”, were used in the dry state. For this purpose, the test bodies were stored after the injection moulding for at least 48 h at room temperature in dry surroundings.

EXAMPLES AND COMPARATIVE EXAMPLES

The following abbreviations are used in the following:

ABS Acrylnitrile-butadiene-styrene-copolymer

IPS Isophthalic acid (I)

LC-12 Laurinlactam

MACM Bis-(4-amino-3-methyl-cyclohexyl)methane

PC Polycarbonate

TPS Terephthalic acid (T)

RV Relative viscosity

The materials used in the examples are listed in Table 1.

TABLE 1
		Relative		Light
		viscosity at		transmission
		20° C. m-cresol,		(2 mm plates)
Material	Trade name	0.5%	Characterisation	[%]	Manufacturer
MACM12	—	1.67	*—/50/—/—/50	93.5	—
MACMI/12	—	1.55	*—/32.4/32.4/—/34.6	92	—
6I/6T/MACMI/MACMT	—	1.45	*42.9/7.6/44.5/5.0/—	91	—
6I/6T	—	1.41	*50.2/—/33.2/16.6/—	91	—
PC/ABS	Bayblend T88-	—	—	—	Bayer AG,
	4N**				Germany
PA 66	Ultramid S2701	2.70 in	—	—	BASF AG,
		H2SO4, 1%			Germany
PA6	GRILON A28	2.75 in	—	—	EMS-CHEMIE
		H2S04, 1%			AG, Switzerland
Glass fibres	Vetrotex 995	—	E-Glass	—	Saint-Gobain
	EC10-4.5		Diameter 10 mic		Vetrotex, France
			Length 4.5 mm
Calcium carbonate	MILLICARB-OG	—	Calcium carbonate,	—	Omya AG,
			ground		Switzerland
Kaolin	Quality China	—	Aluminium silicate	—	ECC
	Clay				International,
					Great Britain
**20% by weight glass fibres
*HMD/MACM/IPS/TPS/LC-12 in mol %

Table 2 shows the composition of examples 1 to 5 according to the invention and the herewith associated test results with respect to the distortion and mechanical properties.

Table 3 shows the composition of examples 6 to 10 according to the invention with associated distortion and mechanical properties.

Table 4 shows the composition of the comparative examples 11 to 16 with associated test results.

Table 5 shows the composition of the comparative examples 17 to 19 with associated test results.

TABLE 2
Examples	Number
Materials	Unit	1	2	3	4	5
MACM12	% by	40	55	40	40	50
	weight
MACMI/12	% by	—	—	—	—	—
	weight
6I/6T/MACMI/MACMT	% by	—	—	—	—	—
	weight
6I/6T	% by	—	—	—	—	—
	weight
Glass fibres	% by	30	30	30	40	40
	weight
Calcium carbonate	% by	30	15	—	20	10
	weight
Kaolin	% by	—	—	30	—	—
	weight
Tests		1	2	3	4	5
Distortion	%	2.05	1.59	2.05	2.09	2.70
Modulus of elasticity in	MPa	10230	8110	10630	11760	10260
tension
Tensile strength	MPa	144	141	110	149	147
Breaking elongation	%	2.5	3.2	1.6	2.3	2.6
Impact strength	kJ/m2	34	56	16	37	45
Notch-impact strength	kJ/m2	8	11	4	9	11

TABLE 3
Examples	Number
Materials	Unit	6	7	8	9	10
MACM12	% by	—	—	—	40	45
	weight
MACMI/12	% by	—	—	50	—	—
	weight
6I/6T/MACMI/MACMT	% by	50	—	—	—	—
	weight
6I/6T	% by	—	50	—	—	—
	weight
Glass fibres	% by	40	40	40	49	49
	weight
Calcium carbonate	% by	10	10	10	11	6
	weight
Kaolin	% by	—	—	—	—	—
	weight
Tests		6	7	8	9	10
Distortion	%	1.69	1.27	2.28	2.19	2.51
Modulus of elasticity in	MPa	14020	14630	11420	13770	13040
tension
Tensile strength	MPa	208	221	164	165	150
Breaking elongation	%	2.2	2.4	2.4	2.2	2.1
Impact strength	kJ/m2	37	36	37	40	38
Notch-impact strength	kJ/m2	8	9	9	11	13

TABLE 4
Comparative examples	Number
Materials	Unit	11*	12	13	14	15	16
PC/ABS	% by	80	—	—	—	—	—
	weight
MACM12	% by	—	70	—	—	—	—
	weight
PA66	% by	—	—	60	40	51	43
	weight
PA6	% by	—	—	—	—	9	6
	weight
Glass	% by	20	30	30	30	30	30
fibres	weight
Calcium	% by	—	—	10	—	10	—
carbonate	weight
Kaolin	% by	—	—	—	30	—	30
	weight
Tests		11	12	13	14	15	16
Distortion	%	2.75	3.33	6.09	5.14	6.56	3.99
Modulus of	MPa	5900	6450	11380	13650	10850	15010
elasticity
in tension
Tensile	MPa	77	122	187	131	187	137
strength
Breaking	%	2.0	3.9	3.2	1.5	3.7	1.4
elongation
Impact	kJ/m2	—	61	82	24	95	27
strength
Notch-	kJ/m2	—	11	10	3	12	4
impact
strength
*Bayblend T88-4N

TABLE 5
Comparative examples	Number
Materials	Unit	17	18	19
PC/ABS	% by weight	—	—	—
MACM12	% by weight	60	—	—
PA66	% by weight	—	50	45
PA6	% by weight	—	—	—
Glass fibres	% by weight	40	40	49
Calcium	% by weight	—	10	6
carbonate
Kaolin	% by weight	—	—	—
Tests		17	18	19
Distortion	%	3.27	5.32	5.11
Modulus of	MPa	8730	14208	16520
elasticity in
tension
Tensile	MPa	146	217	241
strength
Breaking	%	3.4	3.0	2.7
elongation
Impact	kJ/m2	64	92	105
strength
Notch-impact	kJ/m2	14	13	16
strength

The “Visitor card holders” produced from the moulding compounds of the examples according to the invention show without exception a lower distortion than those made of the moulding compounds of the comparative examples.

The test bodies made of the moulding compound no. 11 with an amorphous PC/ABS blend as basis (Bayblend T88-4N, a commercial product by Bayer AG) show in fact the lowest distortion in the comparative examples but even this is still higher than that of the test bodies made of the moulding compounds according to the invention.

The test bodies made of the comparative moulding compounds (nos. 13-16 and 18, 19) which are based on partially crystalline polyamides have a significantly higher distortion still.

Even the test bodies made of solely reinforced comparative moulding compounds with an amorphous polyamide as basis (nos. 12 and 17) have higher distortion than those of the moulding compounds according to the invention with reinforcing materials and fillers.

The comparative examples show in addition that high moduli of elasticity in tension generally are accompanied by high distortion.

In this context, the moulding compound no. 11 in fact provides the test bodies with the lowest distortion within the comparative examples but these also have the lowest modulus of elasticity in tension.

Without further elaboration, it is believed that one skilled in the art can, using the preceding description, utilize the present invention to its fullest extent. The preceding preferred specific embodiments are, therefore, to be construed as merely illustrative, and not limitative of the remainder of the disclosure in any way whatsoever.

In the foregoing and in the examples, all temperatures are set forth uncorrected in degrees Celsius and, all parts and percentages are by weight, unless otherwise indicated.

The entire disclosures of all applications, patents and publications, cited herein and of corresponding European application No. 06 014 372.4, filed Jul. 11, 2006, are incorporated by reference herein.

The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples.

From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention and, without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions.

Claims

1. Polyamide moulding compound comprising 40 to 79% by weight at least of a transparent polyamide, 15 to 49% by weight at least of a fibrous reinforcing material and 6 to 30% by weight of a particulate filler and also if necessary, as complement to 100% by weight, at least one further additive, polyamide oligomers being excluded as additive.

2. Polyamide moulding compound according to claim 1,

characterised in that it comprises 40 to 69% by weight, preferably 40 to 55% by weight, of the transparent polyamide, 25 to 49% by weight, preferably 30 to 49% by weight, of the fibrous reinforcing material and 6 to 30% by weight of the particulate filler and also if necessary, as complement to 100% by weight, at least one further additive.

3. Polyamide moulding compound according to claim 1,

characterised in that the at least one fibrous reinforcing material is selected from the group comprising glass fibres, carbon fibres, metal fibres, aramide fibres, whiskers and mixtures thereof.

4. Polyamide moulding compound according to claim 3,

characterised in that the glass fibres have a diameter of 5 to 20 μm, in particular 5 to 10 μm.

5. Polyamide moulding compound according to claim 3,

characterised in that the glass fibres have a round, oval or rectangular cross-section.

6. Polyamide moulding compound according to claim 3,

characterised in that glass fibres made of E-glass are contained.

7. Polyamide moulding compound according to claim 1,

characterised in that the at least one particulate filler is selected from the group comprising talcum, mica, silicates, quartz, titanium dioxide, wollastonite, kaolin, silicic acids, magnesium carbonate, magnesium hydroxide, chalk, ground or precipitated calcium carbonate, lime, feldspar, barium sulphate, permanently magnetic or magnetisable metals or alloys, glass balls, hollow glass balls, hollow spherical silicate fillers and mixtures thereof.

8. Polyamide moulding compound according to claim 1,

characterised in that the at least one transparent polyamide is selected from the group of polyamides, the light transmission of which, measured according to ASTM D 1003-61 on a plate comprising the polyamide with a thickness of 2 mm, is at least 70%, preferably at least 86%, particularly preferred at least 90%.

9. Polyamide moulding compound according to claim 1,

characterised in that the at least one transparent amorphous polyamide is selected from the group of polyamides which, in the differential scanning calorimetry, DSC according to ISO 1357-1/-2 at a heating rate of 20° C./min, have a melting heat of at most 5 J/g, preferably at most 3 J/g and particularly preferred at most 1 J/g.

10. Polyamide moulding compound according to claim 1,

characterised in that the transparent polyamide is an amorphous polyamide which was obtained from respectively at least one polyamide-forming diamine and/or dicarboxylic acid and/or amino acid or lactam.

11. Polyamide moulding compound according to claim 9,

characterised in that there are selected as diamine aliphatic and/or cycloaliphatic diamines with 6 to 17 C-atoms and/or diamines with partially aromatic structures with 6 to 17 C-atoms, as dicarboxylic acid aliphatic and/or aromatic dicarboxylic acids with 6 to 12 C-atoms and as amino acid α, ω amino acids with 6 to 12 C-atoms.

12. Polyamide moulding compound according to claim 1,

characterised in that the polyamides are selected from the group of homo- and/or copolyamides based on PA 6I, PA 6I/6T, PA MXDI/6I, PA MXDI/MXDT/6I/6T, PA MXDI/12I, PA MXDI, PA MACM12, PA MACMI/12, PA MACMI/MACMT/12, PA 6I/MACMI/12, PA 6I/6T/MACMI/MACMT, PA 6I/6T/MACMI/MACMT/12, PA MACM6/11, PA MACMI/MACM12, MACM being able to be replaced by PACM up to 55% by mol, in particular up to 50% by mol.

13. Polyamide moulding compound according to claim 1,

characterised in that the additives are selected from the group comprising impact strength modifiers, bonding agents, halogen-containing flameproofing agents, halogen-free flameproofing agents, stabilisers, age-protecting agents, antioxidants, antiozonants, light protection agents, UV stabilisers, UV absorbers, UV blockers, inorganic heat stabilisers, organic heat stabilisers, conductivity additives, carbon black, optical lighteners, processing aids, nucleation agents, crystallisation accelerators, crystallisation inhibitors, flow aids, lubricants, mould-release agents, softeners, pigments, colourants, marking materials and mixtures thereof.

14. Polyamide moulding compound according to claim 1,

characterised in that the polyamide moulding compound contains from 21 to 60% by weight of the fibrous reinforcing materials and the particulate fillers in total.

15. Moulded article, produced from a polyamide moulding compound according to claim 1.

16. Moulded article according to claim 14,

characterised in that the moulded article has a distortion of less than or equal to 2.7%, in particular less than or equal to 2.3%.

17. Moulded article according to claim 14,

characterised in that the moulded article has a modulus of elasticity in tension of greater than or equal to 8000 MPa, in particular greater than or equal to 10000 MPa.

18. Moulded article according to claim 14,

characterised in that the moulded article has a tensile strength of greater than or equal to 100 MPa, in particular 140 MPa.

19. Moulded article according to claim 14,

characterised in that the polyamide moulding compound has a breaking elongation of greater than or equal to 1.5%, in particular 2.0%.

20. Use of the polyamide moulding compound according to claim 1 for the production of distortion-free moulded articles.

21. Use according to the claim 1,

characterised in that the moulded articles are selected from the group comprising fibres, films, pipes, hollow bodies or other semi-finished products or finished products from injection moulding, extrusion, pultrusion, injection blowing or other shaping technologies.