MOLDING OF POLYPROPYLENE WITH ENHANCED REHEAT CHARACTERISTICS
Bottles, containers and other articles are formed from polypropylene compositions that include a reheating agent, such as antimony, carbon black, graphite, titanium, copper, manganese, iron, tungsten, graphite, infra-red absorbing dyes or other infra-red absorbing material. The reheating time for the polypropylene composition is shortened for injection stretch blow molding or thermoforming, and the polypropylene granule composition with reheating agent has an L* value of at least 80% of the L* value for a polypropylene granule control without added reheating agents as measured by the Gardner color test. The reheating agent may be incorporated into the polypropylene composition by in situ chemical reduction of a metal compound, such as antimony triglycolate, with a reducing agent, such as hypophosphorous acid. In addition, the polypropylene composition with reheating agent may be derived from a polypropylene masterbatch with high concentrations of reheating agent.
Latest INVISTA NORTH AMERICA S.AR.L. Patents:
This invention relates to the manufacture of bottles, containers and other articles from polypropylene polymer compositions, in particular by injection stretch blow molding and thermoforming techniques.
BACKGROUND OF THE INVENTIONPolyester compositions, such as polyethylene terephthalate or copolymers thereof (hereinafter collectively referred to as “PET”), are well known packaging materials. For example, in U.S. Pat. No. 4,340,721, a PET composition is used to manufacture beverage bottles and other containers (hereinafter referred to as “bottles”) by various molding methods.
In current practice PET bottles of the size and shape for most beverage applications are usually made by an injection stretch blow molding technique. Injection stretch blow molding has two main steps. First, the PET, in the form of granules, is melted in an injection molding machine and the melt injected into a cooled mold to form a precursor to the final bottle known as a “preform”. Commonly, the preform has a threaded neck with a shortened bottle body shape length about 8 to 20 cm and a material thickness between 3 mm and 6 mm. Second, the preform is transferred to a stretch blow molding machine where its external surfaces are reheated by infra-red (IR) lamps. Once the preform has reached a desired temperature, it is stretched and blown to form the final bottle.
The time it takes to reheat the preform is the rate-limiting factor for the overall process. The preform starts at ambient temperature and has to be heated to above the glass transition temperature of the polyester (generally to about 110° C.) so that the preform becomes sufficiently flexible to permit the stretch-blow step to work. In general, polyester polymers have a poor ability to absorb IR radiation. Hence, as well as extending the overall production time, the preform reheating step also requires a significant amount of energy. To address this problem, certain prior patents have taught that adding black materials and/or metal particles to PET compositions can reduce the time and energy required for reheating. Hence, prior patents teach adding carbon black (U.S. Pat. No. 4,476,272), iron oxide (U.S. Pat. No. 4,250,078), and antimony and other metal particles (U.S. Pat. Nos. 5,419,936 and 5,529,744) to reduce PET preform reheating time. Antimony metal particles were indicated as preferred because such particles preferentially absorb radiation at or near the infra-red wavelengths emitted by the IR lamps in most stretch blow mold machines, e.g., 500 nm to 2000 nm. Furthermore, as described in U.S. Pat. Nos. 5,419,936 and 5,529,744, antimony compounds are usually present in the polyester composition itself (as the catalyst for melt polymerization) and can be converted to antimony metal particles, with the desired IR absorption characteristics, by the addition of a reducing agent in the melt polymerization stage of manufacture.
Although PET has found widespread application for beverage bottles, the cost of raw materials for making PET is much higher than for some non-PET polymers. Therefore, the industry continually seeks to switch from PET to lower cost alternatives. Whilst seeking these alternatives, container manufacturers do not wish to invest substantial resources in new capital equipment to process a new polymer material, but would prefer to adapt their existing PET injection blow molding equipment for use with the new material.
One possible alternative to PET for use in injection stretch blow molding of beverage bottles is polypropylene. U.S. Pat. No. 6,258,313 teaches that injection stretch blow molding of a polypropylene preform is possible if the preform is heated simultaneously both from the outside and inside. Nevertheless, it has heretofore been more difficult to produce satisfactory beverage bottles from polypropylene by this method. First, polypropylene has a lower density and specific heat than PET and hence exhibits a significantly narrower processing window. Second, polypropylene suffers from the same limitations as PET in terms of its poor ability to absorb IR radiation. Furthermore, polypropylene generally has greater opacity than PET, which detracts from its aesthetic appearance. The industry thus continues to seek ways to improve the IR absorption properties of polypropylene such that it can be used to make beverage bottles on the same injection stretch blow molding equipment as PET and/or used to make other thermoformed articles.
SUMMARY OF THE INVENTIONIn a first aspect, the invention is a method for injection stretch blow molding a polypropylene bottle from a preform that comprises a polypropylene composition containing a reheating agent. The reheating agent may be one or more metal particles of antimony, titanium, copper, manganese, iron and tungsten, where antimony is most preferred. The reheating agent also may be particles of carbon black, graphite, infra-red absorbing dyes or other infra-red absorbing material.
The preform is reheated, usually by heating with one or more heating lamps, to a desired reheat temperature. The time for reheating the preform is shorter than the time for reheating a control preform of equivalent dimensions formed from the polypropylene composition without a reheating agent. The polymer granules used to make the preform have an L* value of at least about 80% of an L* value of the polymer granules used to make the control preform. The L* values are measured by the Gardner color test. For example, where the control polypropylene composition granules have an L* value of about 75, the granules used to manufacture the preform according to the invention have an L* value of about 60 or above. The closer the L* value is to the L* value of the control, the more the final bottle will resemble the color/aesthetics of a bottle made from the control polypropylene.
Preferably, the reheating agent is incorporated into the polypropylene in the form of particles having particle sizes in the range of about 10 nanometers (nm) to about 100 micrometers, and more preferably in the range of 10 nm to 10 microns. Preferably, the reheating agent particles are incorporated into the polypropylene in an amount in the range of about 2 ppm to 1000 ppm, more preferably from 2 ppm to 350 ppm, most preferably from 2 ppm to 50 ppm. The reheating agent particles also may be incorporated into the polypropylene composition in the form of particles having sizes in the range of 10 nm to 100 microns and in an amount in the range of 50 ppm to 25,000 ppm to form a polypropylene masterbatch. The masterbatch then may be blended with other polypropylene compositions (possibly free of reheating agents or containing different reheating agents or different proportions of the same reheating agents) to form a polypropylene composition with desired proportion(s) of reheating agent(s).
In addition, the reheating agent may be generated within the polypropylene composition by in situ chemical reduction of a metal compound with a reducing agent.
Thus, the metal compound can contain one or more of antimony, titanium, copper, manganese, iron and tungsten, and the reducing agent can be one or more organic phosphorous acids or inorganic phosphorous acids, or tannic, gallic, and pyrogallic acids, or hydrazine, or sulphites, or tin II salts, nickel hydroxide or any organic or inorganic compound with an electrochemical potential sufficient to reduce the metal compounds to the metallic state. Preferably, the metal compound is antimony triglycolate and the reducing agent is hypophosphorous acid.
The preforms, polypropylene bottles and other polypropylene articles made from the polypropylene compositions with reheating agents are also claimed. Examples of other polypropylene articles include three-dimensional articles, such as cups or serving trays or food containers, and two-dimensional articles, such as sheets. Depending upon the desired aesthetics of the final articles, the L* values for the polypropylene granules with reheating agents used to form these other polypropylene articles may be outside the preferred range for L* for compositions used to form bottle preforms that are injection stretch blow molded into bottles.
BRIEF DESCRIPTION OF THE DRAWINGSThe present invention will be described in the following detailed description with reference to the following drawings:
The present invention is directed to polypropylene compositions that are useful in the production of stretch blow molded containers, particularly bottles, with good color quality and transparency. Such compositions may also be used to make other polypropylene containers and polypropylene articles with other two-step techniques, such as thermoforming. The polypropylene compositions contain as reheating agents certain metal particles that intrinsically absorb radiation in the wavelength region of 500 nm to 2000 nm, which are the typical wavelengths of the radiation from infra-red lamps used in IR heating in PET injection stretch blow molding. The metal particles are present in sufficient amount to reduce the reheating time that would otherwise be required to reheat a preform of a polypropylene composition to the desired temperature during injection stretch blow molding or thermoforming. Such polypropylene compositions with reheating agents still have acceptable color and clarity for the desired end use applications.
Referring first to
As shown in
When the preform 10 reaches a desired temperature, the reheated preform 10 is then ready for stretch blow molding. Referring next to
Reheating agents added to the polypropylene composition to reduce reheating time according to the invention include antimony (Sb), manganese (Mn), iron (Fe), carbon black, graphite, infra-red dyes, titanium (Ti), tungsten (W), and copper (Cu). Antimony and carbon black are preferred reheating agents, and antimony is particularly preferred. The reheating agents preferably are added to the polypropylene composition in amounts from about 2 ppm to about 1000 ppm, more preferably about 2 ppm to 350 ppm, and most preferably from about 2 ppm to 50 ppm, and with particle sizes in the range of about 10 nm to about 100 microns, most preferably in the range 10 nm to 10 microns.
The reheating agents may be incorporated into the polypropylene compositions in a number of ways. As one alternative, the reheating agents may be directly mixed with the polypropylene granules prior to introducing the mixture to an injection mold to form the preform. As another more preferred alternative, the reheat agents can be directly mixed with the polypropylene granules and passed through a twin screw compounding extruder or similar piece of equipment to form a well dispersed and distributed polypropylene compound before being introduced to an injection moulding machine. As an alternate more preferred alternative, the reheating agents can be generated within the polypropylene composition by in situ chemical reduction of a metal compound with a reducing agent. As a fourth and even more preferred alternative, the reheating agents can be incorporated into the polypropylene composition by one of the alternatives above, but in high concentrations to form masterbatch granules. Then, such masterbatch granules may be blended with polypropylene granules having a different concentration of reheating agent or no reheating agent or a concentration of a different reheating agent to form a desired polypropylene composition containing one or more reheating agents in desired concentrations. For example, the polypropylene masterbatch may incorporate reheating agent(s) in the form of particles having sizes in the range of 10 nm to 100 microns, preferably less than 10 microns, and in an amount in the range of 50 ppm to 25,000 ppm, preferably less than 1250 ppm.
The degree of reheating agent distribution and dispersion in the polypropylene composition affects the reheating efficacy. That is to say, the more evenly distributed and more widely dispersed the reheating agents in the polymer, the better the reheating efficacy. Similarly, better distribution and dispersion of reheating agents in the polymer improves the aesthetics of the polymer.
In one of the more preferred embodiments, the reheating agent is formed by an in situ chemical reduction of a metal compound with a reducing agent. The metal compound preferably contains one or more of antimony, titanium, copper, manganese, iron and tungsten, and the reducing agent preferably is selected from the group consisting of one or more of organic phosphorous acids, inorganic phosphorous acids, tannic, gallic, and pyrogallic acids, hydrazine, sulphites, tin II salts and nickel hydroxide, or any organic or inorganic compound with an electrochemical potential sufficient to reduce the metal compounds to the metallic state.
Antimony as reheating agent preferably is formed by an in situ chemical reduction of an antimony compound with a reducing agent, such as hypophosphorous acid or other organic phosphorous acid or inorganic phosphorous acid. Preferred antimony compounds include antimony triglycolate (ATG), antimony triacetate (ATA) or antimony trioxide (ATO). The hypophosphorous acid reduces antimony compounds to antimony, which is dispersed in the polypropylene composition. The antimony particles appear to be more uniformly dispersed when introduced into the polypropylene composition in this manner. In particular, we discovered that the antimony particles deposited by the reaction of ATA, ATO or ATG with hypophosphorous acid and/or phosphorous acid have a particularly favorable particle size and are particularly well dispersed in the polypropylene.
The present invention provides a method of making polypropylene containers, such as bottles, and other polypropylene articles that have aesthetic characteristics close to polypropylene compositions without reheating agents. At the same time, the method also reduces the energy requirements for reheating compared to polypropylene compositions without reheating agents. One immediate advantage is cost savings though reduced cycle time or energy savings. Yet another advantage of the present invention is that polypropylene can be used at a higher temperature than PET in subsequent processing, such as pasteurization or cleaning. In addition, polypropylene is recyclable to the same extent as PET.
The following examples further illustrate the present invention. All parts and percentages are expressed by weight unless otherwise specified.
EXAMPLESTwo methods for measuring the reheat temperature were used to assess reheating times for polypropylene compositions containing different reheating agents. First, injection molded plaques were formed from the polypropylene compositions and through heat times for such plaques were measured according to the procedure described below. Second, plaques were molded from the polypropylene compositions and surface reheat times for such plaques were measured according to the procedure described below.
Preparing the Polypropylene Masterbatch Compositions
Polypropylene polymer granules with a size of about 2.5 to 4.0 mm in length and 2.0 to 3.0 mm in diameter were mixed with reheating agents according to the following steps. First, about 5-7 kg polypropylene polymer was mixed with liquid paraffin (about 20 ml) in a plastic bag. The polymer in the bag was tumbled to coat the polymer granules with a thin film of oil. Next, the reheating agents were added to the bag and the admixture was tumbled again. Then, the coated polypropylene polymer granules were compounded using an APV MP2030 twin screw extruder, followed by a Boston Mathews single screw extruder fitted with a 4-section cavity transfer mixer. The resultant compound was then injection molded to form plaques for further testing.
Procedure for Measuring Plaque Through Heating Temperature
Polypropylene plaque through heating temperature measurements were made as follows:
A polypropylene plaque of one hundred millimeters (100 mm) in diameter and four millimeters (4 mm) in cross-sectional thickness was used to evaluate the reheating time for various polypropylene compositions. Each polypropylene plaque of a polymer composition containing a reheating agent and each plaque of the corresponding control composition were made by a standard injection molding method using NB90 Negri Bossi 90te injection molding equipment available from Negri Bossi of Milan Italy. All of the sample and control plaques were made to exactly the same dimension—100 mm in diameter and 4 mm in cross-sectional thickness. The plaques were clean and free of surface contaminants, and had flat upper and lower surfaces.
As illustrated schematically in
The measuring apparatus was calibrated by using control plaques with a defined composition. These control plaques were tested repeatedly and showed consistent reheat measurements. Then, the reheating times for plaques that were tested for comparison were expressed in reference to the control. Two measurements were used: (1) time (seconds) to heat the plaque to 80° C.; and (2) temperature of the plaque after 300 seconds heating time. We have found that for proper comparison the plaques used in this method should have the same starting ambient temperature. Newly molded plaques should be cooled down to room temperature for a sufficient amount of time before testing. In our tests, freshly molded plaques were allowed to cool down at room temperature for at least 30 minutes before the reheating test was conducted.
Referring to
For the reheating test in
Introducing reheating agents in polypropylene compositions can result in undesired coloration of the final container, article or bottle product. The extent of coloration induced by reheating agents varies depending on the type and the amount of agents used. For a given reheating agent, the less amount of the agent is used, the less coloration will be in the final product. If the amount of the reheating agent used is low enough to minimize the unwanted coloration to an accepted level, that amount may not be sufficient to reduce reheating time. The challenge, therefore, is to find a reheating agent that can effectively reduce the reheating time and still produce a final container, article or bottle with minimum coloration.
We used a color measurement (L*) from the Gardner calorimeter to evaluate coloration of polypropylene compositions caused by different reheating agents. The color measurement (L*) reflects the absorption and scattering of light by the testing material. The Gardner BYK Color-View spectrophotometer Model No. 9000 is available from BYK Gardner, Inc., Columbia, Md. USA. L* values for polypropylene plaques made from polypropylene compositions containing different reheating agents in different amounts were measured.
The L* measurements shown in
Table 1 below summarizes the energy savings due to the reduction of reheating time and the relative color aesthetics of these certain tested polypropylene compositions.
Blowing Trial Details
The preforms for the blowing trial were made on a laboratory scale combined injection moulding and blowing machine. The preforms were injection moulded with typical polypropylene processing conditions—the melt temperature was 220° C., the mould temperature was 15° C., and the cycle time was 27 seconds. We then used a separate laboratory blowing machine which had been designed specifically for polypropylene. This blowing machine had two heating ovens, each having 10,000 watts heating capacity and each fitted with forced air ventilation. Several spinning preform holders were used to index the preforms through two ovens separated by an air gap. Each preform was indexed through the first oven in about 60 to 80 seconds. Then, the preform was indexed through an air space to allow the heated preform to equilibrate for about 60 to 80 seconds. Next, the preform was indexed through a second oven for about 60 to 80 seconds, and then, after a further 10-second period indexing in air, it was delivered to the blowing station.
For the energy saving experiment, the machine indexing speed was set at a constant 750 bottles per hour output, and the oven settings were adjusted (reduced) for each sample to provide an optimum injection moulded bottle. Energy savings were then calculated based on the lesser amount of heating energy required to reheat the bottles formed from a polypropylene composition that contained reheating agents versus the amount of heating energy required to reheat the control bottle. In Table 1, energy savings are expressed as a percentage.
For the cycle time saving experiment, both ovens were set to a constant 8900 watts output (for a combined 17,800 watts output). The cycle time was then increased until the preforms were heated sufficiently to allow the optimum blowing of the bottle. The increased cycle time of each sample was calculated against the control cycle time and expressed as a percentage.
The results in Table 1 indicate that the use of 10 ppm Sb produced from antimony triglycolate with hypophosphorous acid reduced the preform reheating energy and cycle time to the same level as 5 ppm carbon black, but the color and visual aesthetics of the polypropylene granule containing antimony was much better than the granules that contained carbon black. Thus, the resulting bottles formed from the polypropylene composition with antimony had better color and visual aesthetics than did the bottles formed from the polypropylene composition containing 5 ppm or 10 ppm carbon black.
The preforms with reheating agents as compared to the control preforms produced energy savings in the range of about 10% to 30%, preferably 15 % to 20%, and cycle time savings in the range of about 25% to 35% (see Table 1). Thus, the polypropylene compositions with reheating agents shorten reheating time and still produce bottles with acceptable color and visual aesthetics.
We further explored the reheating and aesthetic characteristics of different types of antimony reagents. More specifically, we tested antimony triglycolate, antimony trioxide and antimony triacetate at different concentrations. We additionally explored the reheating and aesthetic characteristics of other reheating agents. We also tested different methods for mixing the reheating agents with the polypropylene, namely, by direct application to the polypropylene granules, and by mixing polypropylene granules with masterbatch granules containing high concentrations of reheating agents. For reducing agents, different phosphorous acids with different dosages were also tested. See Tables 2 and 3 below for a summary of these results.
We found that adding antimony as a reheating agent was preferred to carbon black in view of the aesthetics. We further found that adding antimony compounds in combination with phosphoric acid, preferably hypophosphoric acid, more thoroughly disperses the metal particles in the polypropylene composition. Lastly, the antimony triglycolate, antimony trioxide or antimony triacetate with hypophosphoric acid combinations that resulted in from 2 ppm to 350 ppm antimony metal particles in the polypropylene composition achieved the best results for reheat performance and color aesthetics.
Procedure for Measuring Plaque Surface Reheat Temperature
Plaques injection molded from polypropylene compositions as specified in Tables 1, 2 and 3 were rotated while heated by radiation emitted by an IR heating lamp (a 175 Watt lamp model IR-175C-PAR from Phillips at 2400°K) (See, e.g.,
The plaques tested contained various reheating agents, such as antimony (Sb), manganese (Mn), iron (Fe), titanium (Ti), tungsten (W), copper (Cu), graphite, infra-red dye and carbon black, in various amounts. The results are reported in Tables 2 and 3 below. For the compositions set forth in Tables 2 and 3, the controls were plaques made from polypropylene without reheating additives. All of the reheating agents tested improved the plaque surface reheating time as compared with the control polypropylene. However, certain of the reheating agents when incorporated into polypropylene granules (and plaques) had L* values much lower than the target L* (80% of the control), and thus may not be as suitable for use in injection stretch blow molding of bottles. These compositions still may have utility when making other polypropylene articles with thermoforming techniques.
Data for surface reheating times for certain of the polypropylene compositions that included reheating agent, compared to the control C1, is shown graphically in
M/b: masterbatch.
N: nucleated.
M: milled.
ATG: antimony triglycolate.
ATA: antimony triacetate.
TNPP: trisnonylphenyl phosphite.
H3PO3 = phosphorous acid,
H2PO3 = Hypophosphorous acid
Polypropylene compositions with reheating agents according to the invention preferably result in at least a 10% reduction in reheating time, more preferably at least a 25% reduction in reheating time, and most preferably at least a 35% reduction in reheating time, as compared to the reheating time for the control composition. Thus, from Tables 2 and 3, the polypropylene compositions with reheating agents that had reheat times to 80° C. of 375 seconds and under, and particularly 300 seconds and under were most advantageous.
The invention has been illustrated by detailed description and examples of the preferred embodiment. Various changes in form and detail will be within the skill of persons skilled in the art. Therefore, the invention must be measured by the claims and not by the description of the examples or the preferred embodiments.
Claims
1. A method for injection stretch molding a polypropylene bottle, comprising:
- (a) forming a preform from a polypropylene composition containing a reheating agent, wherein the reheating agent comprises one or more metal particles, and wherein said metal particles are selected from the group consisting of one or more of antimony, titanium, copper, manganese, iron and tungsten;
- (b) reheating the preform to a desired temperature, wherein the time for the preform to reach the desired temperature is less than the time for reheating to the desired temperature a control preform of equivalent dimensions that is formed from the polypropylene composition without the reheating agent; and
- (c) injection stretch blow molding the reheated preform to form the bottle; wherein the polypropylene composition containing a reheating agent when it is in a granule form prior to forming the preform has an L* value as measured by the Gardner color test of at least about 80% of an L* value of the polypropylene composition in granule form in the absence of the reheating agent.
2. (canceled)
3. A method for injection stretch molding a polypropylene bottle, comprising:
- (a) forming a preform from a polypropylene composition containing a reheating agent, wherein the reheating agent comprises carbon black, graphite or an infra-red dye in the form of particles incorporated into the polypropylene composition in an amount in the range of 2 ppm to 1000 ppm;
- (b) reheating the preform to a desired temperature, wherein the time for the preform to reach the desired temperature is less than the time for reheating to the desired temperature a control preform of equivalent dimensions that is formed from the polypropylene composition without the reheating agent; and
- (c) injection stretch blow molding the reheated preform to form the bottle;
- wherein the polypropylene composition containing a reheating agent when it is in a granule form prior to forming the preform has an L* value as measured by the Gardner color test of at least about 80% of an L* value of the polypropylene composition in granule form in the absence of the reheating agent.
4. The method of claim 1, wherein the reheating agent is incorporated into the polypropylene composition in the form of particles having sizes in the range of 10 nm to 100 microns and in an amount in the range of 2 ppm to 1000 ppm.
5. The method of claim 1 or 3, wherein the reheating agent is incorporated into the polypropylene composition in the form of particles having sizes in the range of 10 nm to 10 microns and in an amount in the range of 2 ppm to 50 ppm.
6. The method of claim 1, wherein the reheating agent is generated within the polypropylene composition by in situ chemical reduction of a metal compound with a reducing agent.
7. The method of claim 6, wherein the metal compound contains one or more of antimony, titanium, copper, manganese, iron and tungsten, and the reducing agent is selected from the group consisting of one or more of organic phosphorous acids, inorganic phosphorous acids, tannic, gallic, and pyrogallic acids, hydrazine, sulphites, tin II salts and nickel hydroxide.
8. The method of claim 6, wherein the metal compound is antimony triglycolate and the reducing agent is hypophosphorous acid.
9. The method of claim 1, wherein the reheating agent is incorporated into the polypropylene composition in the form of particles having sizes in the range of 10 nm to 100 microns and in an amount in the range of 50 ppm to 25,000 ppm to form a polypropylene masterbatch.
10. A polypropylene bottle made according to the method of claim 1 or 3.
11.-33. (canceled)
34. The method of claim 3, wherein the reheating agent is incorporated into the polypropylene composition in the form of particles having sizes in the range of 10 nm to 100 microns.
35. The method of claim 3, wherein the reheating agent is incorporated into the polypropylene composition in an amount in the range of from 2 ppm to 350 ppm.
36. The method of claim 3, wherein the reheating agent is incorporated into the polypropylene composition in an amount in the range of from 2 ppm to 50 ppm.
37. The method of claim 6, wherein the metal compound is antimony trioxide.
38. The method of claim 6, wherein the metal compound is antimony trioxide and the reducing agent is hypophosphorous acid.
39. A method for injection stretch molding a polypropylene bottle, comprising:
- (d) forming a preform from a polypropylene composition containing a reheating agent selected from metal particles that intrinsically absorb radiation in the wavelength region of 500 nm to 2000 nm;
- (e) reheating the preform to a desired temperature, wherein the time for the preform to reach the desired temperature is less than the time for reheating to the desired temperature a control preform of equivalent dimensions that is formed from the polypropylene composition without the reheating agent; and
- (f) injection stretch blow molding the reheated preform to form the bottle;
- wherein the polypropylene composition containing a reheating agent when it is in a granule form prior to forming the preform has an L* value as measured by the Gardner color test of at least about 80% of an L* value of the polypropylene composition in granule form in the absence of the reheating agent.
40. The method of claim 39, wherein the reheating agent is incorporated into the polypropylene composition in the form of particles having sizes in the range of 10 nm to 100 microns and in an amount in the range of 2 ppm to 1000 ppm.
41. The method of claim 39, wherein the reheating agent is incorporated into the polypropylene composition in the form of particles having sizes in the range of 10 nm to 10 microns and in an amount in the range of 2 ppm to 50 ppm.
42. The method of claim 39, wherein the reheating agent is generated within the polypropylene composition by in situ chemical reduction of a metal compound with a reducing agent.
43. The method of claim 39, wherein the reheating agent is incorporated into the polypropylene composition in the form of particles having sizes in the range of 10 nm to 100 microns and in an amount in the range of 50 ppm to 25,000 ppm to form a polypropylene masterbatch.
Type: Application
Filed: Oct 24, 2007
Publication Date: Feb 28, 2008
Applicant: INVISTA NORTH AMERICA S.AR.L. (Wilmington, DE)
Inventors: Michael Neal (Martan), David Harrison (Redcar), Stephen Jenkins (Stokesley), J. Davis (Billingham)
Application Number: 11/877,751
International Classification: B29D 22/00 (20060101);