INSITU REMOVAL OF CHELATOR FROM ANIONIC POLYMERIZATION REACTIONS

Abstract

A process for producing polymers having at least one high vinyl end segment is provided. The process comprises: (a) forming a living prepolymer high vinyl initiator with a vinyl content greater than about 45% using a vinyl modifier, (b) adding a R1R2R3aluminum or R1R2R3boron compound to nullify the effect of the vinyl modifier, and (c) initiating polymerization of diene monomers using said living prepolymer high vinyl initiator so as to form a polymer product with at least one high vinyl end segment, where R1, R2, and R3 are selected from the group consisting of C1-C12 alkyl, C2-C12 alkene, C2-C12 alkyne, phenyl, and alkyl-substituted phenyl, and may all be identical or may all be separately selected but cannot be H. The polymers having at least one high vinyl end segment may be coupled to produce a polymer having a high vinyl end segment on all ends.

Description

FIELD OF THE DISCLOSURE

The disclosure relates to methods for producing polymer compositions with high vinyl end segments.

BACKGROUND OF DISCLOSURE

Polymers and copolymers of conjugated dienes such as polybutadiene, polyisoprene, and styrene-butadiene rubbers possess physical properties which make them suitable for many important applications such as synthetic rubbers and as additives to other polymeric systems such as, for example, high impact polystyrene (HIPS). HIPS can be manufactured by polymerizing styrene in the presence of 5-10% dissolved polybutadiene or butadiene copolymer. During the polymerization of the styrene, the polybutadiene or butadiene copolymer is grafted onto the styrene polymer chain. To increase the grafting efficiency of the polybutadiene, it is desirable for the polybutadiene to have end segments having a high vinyl content rather than cis or trans configurations. The vinyl content refers to alkenyl groups configured pendant to the polymer backbone, as opposed to cis and trans configurations which contain the alkenyl groups within the polymer backbone. The terms vinyl content and vinyl bond content are used interchangeably herein.

Polymers with high vinyl end segments canbe produced by initiating polymerization and allowing the reaction to proceed to near completion. As the polymerization reaction approaches completion, additional monomer and a vinyl modifier are added. The vinyl modifer increases the number of vinyl configured bonds that are formed during polymerization, hence leading to increased vinyl content. The final segment of the polymer thus has a higher vinyl bond content than the beginning segment. The vinyl concentration of the end segment can be controlled to levels as high as about 70%. However, if one wishes both ends of the polymer, or the ends of a star branched polymer, to have high vinyl content with the remaining segments having low vinyl content, this method will not work because coupling reactions result in high vinyl in the center of the polymer chain or star branched polymer.

To produce linear or branched polymers with all ends having a high vinyl content, an organo-dilithium initiator can be used to polymerize a low vinyl middle segment. Subsequently, additional monomer and a vinyl modifier are added to produce ends having a high vinyl content. This method avoids the need for a coupling agent. However, organo-dilithium initiators are expensive and unstable.

Alternatively, linear or branched polymers with all ends having a high vinyl content may be produced by first forming a living prepolymer high vinyl initiator by anionic polymerization of monomer units in the presence of a vinyl modifier. The living prepolymer high vinyl initiator is then utilized to initiate polymerization of additional monomer units, thus producing a polymer having a high vinyl end and a low vinyl end. The low vinyl end is formed as a result of the extra monomer units lowering the concentration of the vinyl modifier. The polymers are then coupled between the low vinyl ends, producing a polymer with each end containing a high vinyl segment. However, if this method is used in a batch polymerization process, the transition from high vinyl to low vinyl is gradual since the change results from the decrease in concentration of the vinyl modifier upon addition of additional monomer. Since the transition is gradual, the higher the desired vinyl content in the end segment is, the higher the vinyl content in the middle portion of the polymer chain will be. Further, dilution of the modifier is not an effective method when chelating modifiers are used.

The above method may also be used in a continuous process, wherein the living prepolymer high vinyl initiator is made continuously in one reactor and fed to a second reactor where the bulk of the polymer is made. In comparison to a batch process, a continuous process utilizing the above method can produce a more abrupt change in vinyl content. However, the abrupt change is caused by using a higher temperature in the second reactor, which lessens the effectiveness of the vinyl modifier.

There remains a need for a process to produce polymers having high vinyl segments on all ends, which does not require the use of expensive and unstable organo-dilithium initiators. Furthermore, there remains a need for a process in which a higher vinyl content may be obtained on the end segments without increasing the vinyl content of the middle segment. Additionally, there remains a need for a process that is capable of providing a more abrupt change in vinyl content without the need for a temperature differential to lessen the effectiveness of the vinyl modifier.

SUMMARY OF DISCLOSURE

A process for producing polymers having at least one high vinyl end segment is provided. The process comprises: (a) forming a living prepolymer high vinyl initiator with a vinyl content greater than about 45% using a vinyl modifier, (b) adding a R₁R₂R₃aluminum or R₁R₂R₃boron compound to nullify the effect of the vinyl modifier, and (c) initiating polymerization of diene monomers using said living prepolymer high vinyl initiator so as to form a polymer product with at least one high vinyl end segment, where R₁, R₂, and R₃ are selected from the group consisting of C1-C12 alkyl, C2-C12 alkene, C2-C12 alkyne, phenyl, and alkyl-substituted phenyl, and may all be identical or may all be separately selected but cannot be H.

The process may further comprise using a coupler to couple the polymer product with a high vinyl end segment to produce a further product with at least two high vinyl end segments.

A method of producing an engineered plastic selected from the group consisting of high impact polystyrene, styrene-maleic anhydride copolymer, methylmethacrylate-butadiene-styrene copolymer, transparent impact polystyrene, and acrylonitrile butadiene styrene copolymer is also provided. The method comprises the steps of: (a) (1) forming a living prepolymer high vinyl initiator with a vinyl content greater than about 45% using a vinyl modifier, (2) adding a R₁R₂R₃aluminum or R₁R₂R₃boron compound to nullify the effect of the vinyl modifier, and (3) initiating polymerization of diene monomers using said living prepolymer high vinyl initiator so as to form a polymer product with at least one high vinyl end segment, where R₁, R₂, and R₃ are selected from the group consisting of C1-C12 alkyl, C2-C12 alkene, C2-C12 alkyne, phenyl, and alkyl-substituted phenyl, and may all be identical or may all be separately selected but cannot be H; (b) adding the polymer product with at least one high vinyl end segment to a solvent comprising at least one vinyl monomer; (c) optionally adding at least one additional inert solvent; (d) optionally adding additive selected from the group consisting of extender oils, modifiers, and antioxidants; (e) initiating polymerization of the vinyl monomer by the use of an initiator and/or heat, wherein steps (b)-(d) can be performed in any order.

An additional process for producing polymers having at least one high vinyl end segment is provided. The process comprises: (a) forming a living prepolymer high vinyl initiator with a vinyl content greater than about 45% using a vinyl modifier, (b) adding a R₁R₂R₃aluminum or R₁R₂R₃boron compound to nullify the effect of the vinyl modifier, and (c) initiating polymerization of diene monomers using said living prepolymer high vinyl initiator so as to form a polymer product with at least one high vinyl end segment, where R₁, R₂, and R₃ are selected from the group consisting of C1-C12 alkyl, C2-C12 alkene, C2-C12 alkyne, phenyl, and alkyl-substituted phenyl, and may all be identical or may all be separately selected but cannot be H, where step (c) is conducted at a maximum temperature that is no more than 20° C. higher than the maximum temperature at which steps (a) and (b) are conducted.

The process may further comprise using a coupler to couple the polymer product with a high vinyl end segment to produce a further product with at least two high vinyl end segments.

DETAILED DESCRIPTION

Preparation of the living prepolymer high vinyl initiator is carried out by adding an initiator to a mixture of monomers in the presence of a vinyl modifier. Any initiator known in the art as suitable for the polymerization of conjugated dienes may be used. Suitable initiators include anionic initiators. Organo-lithium initiators are exemplary anionic initiators, but other anionic initiators are well known to those of skill in the art and may be utilized. Preferred organo-lithium initiators have the formula RLi_x, wherein R represents a hydrocarbyl radical of about 1 to about 20, preferably about 2 to about 8 carbon atoms per R group and x is an integer from 1 to about 4. Typical R groups include aliphatic and cycloaliphatic groups. Specific examples of R groups for substitution in the above formulas include primary, secondary, and tertiary groups, such as n-propyl, isopropyl, n-butyl, isobutyl, t-butyl, and mixtures thereof.

Specific examples of suitable lithium initiators include n-butyl lithium, p-tolyllithium, 4-phenylbutyl lithium, 4-butylcyclohexyl lithium, lithium dialkyl amines, lithium dialkyl phosphines, lithiumalkyl aryl phosphine, lithium diaryl phosphines and mixtures thereof.

The anionic initiator is employed in an amount designed to result in the desired molecular weight of the polymer. The ratio of millimoles of the anionic initiator per hundred grams of the anionically polymerizable monomer ranges between 0.1 millimoles to 100 millimoles, or between 0.2 millimoles to 20 millimoles, or between 0.5 millimoles to 4 millimoles.

Initiator is added to a mixture of monomers in a suitable hydrocarbon solvent in the presence of a vinyl-modifier. Exemplary monomers include conjugated dienes and vinyl monomers. Exemplary conjugated dienes include 1,3-butadiene, isoprene (2-methyl-1,3-butadiene), 2-ethyl-1,3-butadiene, 2,3-dimethyl-1,3-butadiene, piperylene (1,3-pentadiene), 2-methyl-1,3-pentadiene, 3-methyl-1,3-pentadiene, 4-methyl-1,3-pentadiene, 2,4-dimethyl-1,3-pentadiene, 1,3-hexadiene, and the like. Exemplary vinyl monomers include 1,2-diphenyl-4-methyl-1-hexene, styrene, α-methylstyrene, p-methylstyrene, vinyl toluene, vinyl anthracene, vinyl pyridines such as 2-vinylpyriene and 4-vinylpyridine, vinyl naphthalene such as 1-vinylnaphthalene, 2-vinylnaphthalene, 1-α-methylvinylnaphthalene, 2-α-methylvinylnaphthalene, and the like, and mixtures thereof.

Suitable solvents used in the preparation of the living prepolymer high vinyl initiator include hydrocarbon solvents such as pentane, hexane, heptane, octane, nonane, decane, cyclopentane, cyclohexane, cycloheptane, cyclooctane, and mixtures thereof.

A vinyl modifier is added to increase the 1,2-addition reaction of the diene monomer in the preparation of the living prepolymer high vinyl initiator. Such modifying agents are known in the art. These modifying agents may be employed in amounts generally ranging from about 1:100 to about 100:1 molar ratio of the modifier to anionic initiator. This yields a living prepolymer with molecular weight of about 500 to about 5,000. The 1,2-addition product can be increased from about the 5-15% range to as high as about 90-100% of the diene monomer units being incorporated into the living prepolymer high vinyl initiator. The preferred vinyl content of the living prepolymer high vinyl initiator is greater than about 45%, more preferably greater than about 50%.

Exemplary vinyl modifiers include one or more of hexamethylphosphoric acid triamide, N,N,N′,N′-tetramethylethylene diamine, ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, tetrahydrofuran, 1,4-diazabicyclo[2.2.2]octane, diethyl ether, triethylamine, tri-n-butylamine, tri-n-butylphosphine, p-dioxane, 1,2-dimethoxy ethane, dimethyl ether, methyl ethyl ether, ethyl propyl ether, di-n-propyl ether, di-n-octyl ether, anisole, dibenzyl ether, diphenyl ether, dimethylethylamine, bis-oxalanyl propane, dipiperidino ethane, tri-n-propyl amine, trimethyl amine, triethyl amine, N,N-dimethyl aniline, N-ethylpiperidine, N-methyl-N-ethyl aniline, and N-methylmorpholine.

The number average molecular weight (M_n) of the living prepolymer high vinyl initiator is in the range of about 100 to 20,000, preferably in the range of about 250 to 5000, and most preferably in the range of about 500 to 2500.

After forming the living prepolymer high vinyl initiator, a R₁R₂R₃aluminum or R₁R₂R₃boron compound is added to the living prepolymer high vinyl initiator. In the above formulas, R₁, R₂, and R₃ are selected from the croup consisting of C1-C12 alkyl, C2-C12 alkene, C2-C12 alkyne, phenyl, and alkyl-substituted phenyl, and may all be identical or may all be separately selected but cannot be H. Exemplary R₁R₂R₃aluminum or R₁R₂R₃boron compounds include trialkyl compounds. Suitable trialkyl compounds include triethylaluminum, trimethylaluminum, and triisobutylaluminum.

The purpose of adding the R₁R₂R₃aluminum or R₁R₂R₃boron compound is to nullify the effect of the vinyl modifier. One advantage of nullifying the effect of the vinyl modifier is that additional monomers may be subsequently polymerized into a low vinyl content configuration by simply combining the mixture of living prepolymer high vinyl initiator and R₁R₂R₃aluminum or R₁R₂R₃boron compound with additional monomer and a suitable solvent. The living prepolymer high vinyl initiator initiates the polymerization of the monomers by continuing living anionic polymerization. Thus, a living polymer with one high vinyl end segment is produced.

Preferred monomer units that may be added to the living prepolymer high vinyl initiator are conjugated dienes and vinyl-substituted aromatic hydrocarbons. The polymers with one high vinyl end segment can contain more than one monomer unit, in a random or block configuration. Suitable conjugated dienes include one or more of 1,3-butadiene, isoprene, 2,3-dimethyl-1,3-butadiene, and 1,3-pentadiene. Preferred conjugated dienes are 1,3-butadiene and/or isoprene.

Suitable vinyl-substituted aromatic hydrocarbons include one or more of styrene, α-methylstyrene, 1-vinyl naphthalene, 2-vinyl naphthalene, 1-α-methy vinyl naphthalene, 2-α-methyl vinyl naphthalene, as well as alkyl, cycloalkyl, aryl, alkaryl, and aralkyl derivatives thereof, in which the total number of carbon atoms in the combined hydrocarbon is generally not greater than 12, as well as any di- or tri-vinyl substituted aromatic hydrocarbons. One preferred vinyl-substituted aromatic hydrocarbon is styrene. If the di- or tri-vinyl substituted aromatic hydrocarbons are used, the resulting polymer has a branched and/or crosslinked structure.

Suitable solvents in this step include one or more of pentane, hexane, heptane, octane, nonane, decane, cyclopentane, cyclohexane, cycloheptane, cyclooctane.

The polymerization temperature can vary over a broad range from about −50° C. to about 200° C., or from about −20° C. to about 140° C. One advantage of using the R₁R₂R₃aluminum or R₁R₂R₃boron compound to nullify the effect of the vinyl modifier is that the polymerization temperature does not have to be significantly higher than the temperature at which the living prepolymer high vinyl initiator is formed to create a lower vinyl content. Accordingly, the polymerization temperature may optionally be no more than 20° C. higher than the temperature(s) at which the living prepolymer high vinyl initiator is formed or the R₁R₂R₃aluminum or R₁R₂R₃boron compound is added. The pressure used preferably is sufficient to maintain the fluidity of the substantially liquid phase under the conditions of the polymerization reaction.

The polymerization reaction is generally conducted for a time sufficient to obtain at least about 80% and preferably about 99% conversion of charged monomer units. The M_n of the uncoupled polymer is in the range of about 20,000 to 500,000, more preferably in the range of about 30,000 to 400,000, and most preferably in the range of about 40,000 to about 300,000.

The living prepolymer high vinyl end segment accounts for a minor portion of the total weight of the polymer composition. For example, the living prepolymer high vinyl end segment may account for less than about 15% of the total weight of the polymer composition, or less than about 10% of the total weight, or less than about 5%. Therefore, the vinyl content of the living prepolymer high vinyl end segment has very little effect on the total vinyl content of the polymer composition. The preferred vinyl content of the total polymer composition is less than about 35%, and preferably less than about 30%.

The living polymer with one high vinyl end segment may be produced by a batch or a continuous process. To make the living polymer in a continuous mode, the living prepolymer high vinyl initiator is made continuously in one reactor and fed to a second reactor where the living polymer with one high vinyl end segment is produced.

The living polymer with one high vinyl end segment produced above may then be coupled to other living polymers having one high vinyl end segment. Coupling results in a polymer having a high vinyl end segment on all ends of the polymer chain. A wide variety of coupling agents can be used to couple the living polymers. A di-coupling agent will result in a linear polymer with both end segments having high vinyl content. A tri-coupling agent will result in a star-shaped polymer with all three end segments having high vinyl content, and a tetra-coupling agent will result in a star-shaped polymer with all four end segments having high vinyl content.

Suitable coupling agents include, but are not limited to, SnCl₄, alkyl SiCl₃, CO₂, CCl₄, SiCl₄, PNCl₂, divinylbenzene, butyl benzoate, CCl₃COOEt, and mixtures thereof.

The appropriate amount of coupling agent is calculated based on the amount needed to react with the number of initiator atoms present in the polymer. For example, with a tetrafunctional coupling agent, such as SnCl₄, one-fourth of the molecular weight of SnCl₄ is calculated as required for each atom of initiator present. As a by-product, the initiator, e.g., Li⁺, is removed by reaction with chlorine and precipitated from the reaction solution as LiCl.

Other additives known in the art can be added. Stabilizers, antioxidants, conventional fillers, reinforcing agents, reinforcing resins, pigments, fragrances, and the like are examples of some such additives. Specific examples of useful antioxidants and stabilizers include 2-(2′-hydroxy-5′-methylphenyl)benzotriazole, nickel di-butyl-di-thiocarbamate, tris(nonylphenyl) phosphite, 2,6-di-t-butyl-4-methylphenol, and the like. Exemplary conventional fillers and pigments include silica, carbon black, titanium dioxide, iron oxide, and the like. These compounding ingredients are incorporated in suitable amounts depending upon the contemplated use of the product, preferably in the range of 1-350 parts by weight of additives or compounding ingredients per 100 parts by weight of the polymer composition.

A reinforcing agent may be defined as material added to a resinous matrix to improve the strength of the polymer. Most reinforcing materials are inorganic or organic products of high molecular weight. Various examples include glass fibers, asbestos, boron fibers, carbon and graphite fibers, whiskers, quartz and silica fibers, ceramic fibers, metal fibers, natural organic fibers, and synthetic organic fibers. Other elastomers and resins are also useful to enhance specific properties like damping properties, adhesion, and processability.

The polymer compositions of the present disclosure are useful as additives in the preparation of engineered plastics. Engineered plastics may be prepared by adding either the uncoupled polymer containing a high vinyl end segment or the coupled polymer having all ends containing a high vinyl segment to a suitable solvent which contains at least one vinyl monomer. Optionally, at least one additional inert solvent may be also be used. The polymer/solvent mixture may also optionally contain additives selected from the group consisting of extender oils, modifiers, and antioxidants. Polymerization of the vinyl monomer is initiated by the use of an initiator and/or heat. Exemplary engineered plastics that may be made by this process include, but are not limited to, high impact polystyrene, styrene-maleic anhydride copolymer, methylmethacrylate-butadiene-styrene copolymer, transparent impact polystyrene, and acrylonitrile butadiene styrene copolymer.

Suitable initiators include free radical initiators. Exemplary free radical initiators include dilauroyl peroxide lauroyl acid, dioctanoyl peroxide caprylic acid, didecanoyl peroxide n-decanoic acid, di-n-propionyl peroxide propionic acid, bis(3,5,5-trimethyl hexanoyl) 3,5,5-trimethyl peroxide hexanoic acid, dibenzoyl peroxide benzoic acid, bis(2,4-dichlorobenzoyl) 2,4 dichlorobenzoic acid peroxide, bis(o-methybenzoyl)peroxide o-methyl benzoic acid, acetyl cyclohexane sulphonyl cyclohexane sulphonic peroxide acid, t-butylperoxypivalate pivalic acid, t-butyl peroxy-2-ethylhexanoate 2-ethyl caproic acid, t-butyl peroxy isobutyrate isobutyric acid, and t-butyl peroxybenzoate benzoic acid.

Suitable vinyl monomers for preparing engineered plastics include, but are not limited to, styrene, divinyl benzene, α-methylstyrene, 1-vinyl naphthalene, 2-vinyl naphthalene, 1-α-methy vinyl naphthalene, and 2-α-methyl vinyl naphthalene.

Suitable solvents in this step include, but are not limited to, one or more of pentane, hexane, heptane, octane, nonane, decane, cyclopentane, cyclohexane, cycloheptane, cyclooctane.

Any extender oil, modifier, and antioxidant may be used. Such materials are well known to those skilled in the art. Examples of such materials are listed above.

The present invention will be described in more detail with reference to the following examples. The following examples are presented for purposes of illustration only and are not to be construed in a limiting sense.

EXAMPLES

Examples 1 and 2 were produced by charging bottles with hexane and a 21.4% blend of 1,3-butadiene in hexane to obtain a concentration of 1,3-butadiene as shown in Table 1. n-butyl lithium and bis-oxalyanyl propane were added to both bottles in the amounts shown in Table 1. Triethylaluminum was added to Example 2 in the amount shown in Table 1. The polymerization was conducted for 18 hours at 50° C. The polymers were precipitated in isopropanol and drum-dried. The analytical results in Table 1 show that the triethylaluminum in Example 2 effectively nullified the effect of the bis-oxalyanyl propoane to produce a polybutadiene with a significantly lower vinyl content than Example 1. Mw represents the weight average molecular weight, and Mn represents the number average molecular weight. Mw and Mn values are obtained from a calibrated GPC (Gel Permeation Chromatography) instrument.

	TABLE 1
	Example 1	Example 2
% 1,3-butadiene in hexane	14.3%	14.2%
n-butly lithium (mmol)	0.616	0.616
bis-oxalanyl propane (mmol)	0.21	0.21
triethylaluminum (mmol)	0.00	0.25
R.I.	1.5104	1.5158
% vinyl (R.I.)	63%	26%
1H NMR % vinyl	61.2%	21.7%
Mn (GPC)	69,000	73,200
Mw/Mn	1.1105	1.2168

Example 3 was prepared by charging a bottle with hexane and a 21.4% blend of 1,3-butadiene in hexane to obtain a concentration of 1,3-butadiene as shown in Table 2. n-butyl lithium and bis-oxalyanyl propane were added to the bottle. Example 3 was polymerized at 0° C. for 4 hours to prepare a living prepolymer high vinyl initiator. Example 4 was prepared by charging Example 3 into a 1 gallon reactor containing 1,3-butadiene in hexane in the concentration shown in Table 2. The 1 gallon reactor also contained triethylaluminum. The polymerization was conducted at 12-68° C. for 2 hours. The results in Table 2 show that triethylaluminum nullified the effect of the bis-oxalyanyl propane to produce a polybutadiene having a low vinyl content.

	TABLE 2
	Example 3	Example 4
% 1,3-butadiene in hexane	10.7%	14.4%
n-butly lithium (mmol)	1.00	1.00
bis-oxalanyl propane (mmol)	0.47	0.47
triethylaluminum (mmol)	0.00	0.54
R.I.	1.5	1.5165
% vinyl (R.I.)	66%	21%
1H NMR % vinyl	84.7%	14.4%
Mn (GPC)	3,600	62,700
Mw/Mn	1.0862	1.1797

Claims

1. A process comprising:

a. forming a living prepolymer high vinyl initiator with a vinyl content greater than about 45% using a vinyl modifier,

b. adding a R1R2R3aluminum or R1R2R3boron compound, and

c. Initiating polymerization of diene monomers using said living prepolymer high vinyl initiator so as to form a polymer product with at least one high vinyl end segment,

wherein said polymer product has an overall vinyl content of less than 35%, and where R1, R2, and R3 are selected from the group consisting of C1-C12 alkyl, C2-C12 alkene, C2-C12 alkyne, phenyl, alkyl-substituted phenyl and may all be identical or may all be separately selected but cannot be H.

2. A process as claimed in claim 1 wherein the R1R2R3aluminum or R1R2R3boron compound are trialkyl compounds.

3. A process as claimed in claim 1 wherein the R1R2R3aluminum compound is triethylaluminum.

4. A process as claimed in claim 1 wherein step (a) comprises combining an anionic initiator, monomer and a vinyl modifier, wherein said monomer comprises at least one conjugated diene monomer.

5. A process as claimed in claim 4 wherein said anionic initiator is an organolithium compound.

6. A process as claimed in claim 4 wherein said monomer comprises 1,3-butadiene.

7. A process as claimed in claim 1 wherein the vinyl modifier comprises at least one of hexamethylphosphoric acid triamide, N,N,N′,N′-tetramethylethylene diamine, ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, tetrahydrofuran, 1,4-diazabicyclo[2.2.2]octane, diethyl ether, triethylamine, tri-n-butylamine, tri-n-butylphosphine, p-dioxane, 1,2-dimethoxy ethane, dimethyl ether, methyl ethyl ether, ethyl propyl ether, di-n-propyl ether, di-n-octyl ether, anisole, dibenzyl ether, diphenyl ether, dimethylethylamine, bis-oxalanyl propane, tri-n-propyl amine, trimethyl amine, triethyl amine, N,N-dimethyl aniline, N-ethylpiperidine, N-methyl-N-ethyl aniline, and N-methylmorpholine.

8. A process as claimed in claim 4 wherein said monomer further comprises at least one vinyl monomer.

9. (canceled)

10. (canceled)

11. A process as claimed in claim 1 wherein said polymerization in step (c) further comprises the use of at least one vinyl monomer.

12. (canceled)

13. A process comprising:

a. forming a living prepolymer high vinyl initiator with a vinyl content greater than about 45% using a vinyl modifier,

b. adding a R1R2R3aluminum or R1R2R3boron compound, and

c. initiating polymerization of diene monomers using said living prepolymer high vinyl initiator so as to form a polymer product with a high vinyl end segment,

wherein said polymer product has an overall vinyl content of less than 35%, and where R1, R2, and R3 are selected from the group consisting of C1-C12 alkyl, C2-C12 alkene, C2-C12 alkyne, phenyl, alkyl-substituted phenyl, and mixtures thereof and may all be identical or may all be separately selected but cannot be H

where step (c) is conducted at a maximum temperature that is no more than 20° C. higher than the maximum temperature at which steps (a) and (b) are conducted.

14. A process as claimed in claim 13 wherein the R1R2R3aluminum or R1R2R3boron compound are trialkyl compounds.

15. A process as claimed in claim 13 wherein the R1R2R3aluminum compound is triethylaluminum.

16. A process as claimed in claim 13 wherein step (a) comprises combining an anionic initiator, monomer and a vinyl modifier, wherein said monomer includes one or more conjugated diene monomers.

17. A process as claimed in claim 16 wherein said initiator is an organolithium compound.

18. A process as claimed in claim 16 wherein said monomer comprises 1,3-butadiene.

19. A process as claimed in claim 13 wherein the vinyl modifier comprises at least one of hexamethylphosphoric acid triamide, N,N,N′,N′-tetramethylethylene diamine, ethylene glycol dimethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, tetrahydrofuran, 1,4-diazabicyclo[2.2.2]octane, diethyl ether, triethylamine, tri-n-butylamine, tri-n-butylphosphine, p-dioxane, 1,2-dimethoxy ethane, dimethyl ether, methyl ethyl ether, ethyl propyl ether, di-n-propyl ether, di-n-octyl ether, anisole, dibenzyl ether, diphenyl ether, dimethylethylamine, bis-oxalanyl propane, tri-n-propyl amine, trimethyl amine, triethyl amine, N,N-dimethyl aniline, N-ethylpiperidine, N-methyl-N-ethyl aniline, and N-methylmorpholine.

20. A process as claimed in claim 16 wherein said monomer further comprises at least one of vinyl monomer.

21. (canceled)

22. (canceled)

23. A process as claimed in claim 13 wherein said polymerization in step (c) further comprises the use of at least one vinyl monomer.

24. A process comprising:

a. forming a living prepolymer high vinyl initiator with a vinyl content greater than about 45% using a vinyl modifier,

b. adding a R1R2R3aluminum or R1R2R3boron compound, and

c. initiating polymerization of diene monomers using said living prepolymer high vinyl initiator so as to form a polymer product with at least one high vinyl end segment,

wherein said polymer product has an overall vinyl content of less than 35%, and said polymer product with a high vinyl end segment from step (c) is coupled to produce a further product with at least two high vinyl end segments, and R1, R2, and R3 are selected from the group consisting of C1-C12 alkyl, C2-C12 alkene, C2-C12 alkyne, phenyl, alkyl-substituted phenyl and may all be identical or may all be separately selected but cannot be H.

25. A process as claimed in claim 24, wherein a di-coupling, tri-coupling, tetra-coupling, quatra-coupling, penta-coupling or hexa-coupling agent is used for the coupling.

26. A process as claimed in claim 24 wherein said polymerization in step (c) further comprises the use of at least one vinyl monomer.

27. A method comprising the steps of:

(a) adding the polymer produced in any of claims 1-8, 11, or 24-26 to a solvent comprising at least one vinyl monomer;

(b) optionally adding at least one additional inert solvent;

(c) optionally adding additives selected from the group consisting of extender oils, modifiers, and antioxidants,

(d) initiating polymerization of the vinyl monomer by the use of an initiator and/or heat,

wherein steps a, b and c can be performed many order;

whereby the result of steps (a)-(d) is production of an engineered plastic; and

wherein the engineered plastic is selected from the group consisting of high impact polystyrene, styrene-maleic anhydride copolymer, methylmethacrylate-butadiene-styrene copolymer, transparent impact polystyrene, and acrylonitrile butadiene styrene copolymer.

28. A process comprising:

a. forming a living prepolymer high vinyl initiator with a vinyl content greater than about 45% using a vinyl modifier,

b. adding a R1R2R3aluminum or R1R2R3boron compound, and

c. initiating polymerization of diene monomers using said living prepolymer high vinyl initiator so as to form a polymer product with a high vinyl end segment

wherein said polymer product has an overall vinyl content of less than 35%, and said polymer product with a high vinyl end segment from step (c) is coupled to produce a further product with at least two high vinyl end segments, and R1, R2, and R3 are selected from the group consisting of C1-C12 alkyl, C2-C12 alkene, C2-C12 alkyne, phenyl, alkyl-substituted phenyl, and mixtures thereof and may all be identical or may all be separately selected but cannot be H

where step (c) is conducted at a maximum temperature that is no more than 20° C. higher than the maximum temperature at which steps (a) and (b) are conducted.

29. A process as claimed in claim 28, wherein a di-coupling, tri-coupling, tetra-coupling, quatra-coupling, penta-coupling or hexa-coupling agent is used for the coupling.

30. A process as claimed in claim 28 wherein said polymerization in step (c) further comprises the use of at least one vinyl monomer.

31. A process comprising:

a. adding an anionic initiator to a mixture of monomers in the presence of a vinyl modifier to form a living polymer with a vinyl content greater than about 45%;

b. adding a R1R2R3aluminum or R1R2R3boron compound to the mixture in step (a) when said living polymer has a number average molecular weight in the range of about 100 to about 20,000;

c. allowing said living polymer to obtain a number average molecular weight in the range of about 20,000 to about 500,000; and

d. optionally, coupling said living polymer;

wherein said living polymer produced in step (c) has an overall vinyl content of less than 35%, and p1 where R1, R2, and R3 are selected from the group consisting of C1-C12 alkyl, C2-C12 alkene, C2-C12 alkyne, phenyl, alkyl-substituted phenyl and may all be identical or may all be separately selected but cannot be H.