METHOD FOR PROVIDING HERMETIC ELECTRICAL FEEDTHROUGH

Abstract

A method for fabricating the hermetic electrical feedthrough. The method comprises providing a ceramic sheet having an upper surface and a lower surface, forming at least one via hole in said ceramic sheet extending from said upper surface to said lower surface, inserting a conductive thickfilm paste into said via hole, laminating the ceramic sheet with paste filled via hole between an upper ceramic sheet and a lower ceramic sheet to form a laminated ceramic substrate, firing the laminated ceramic substrate to a temperature to sinter the laminated ceramic substrate and cause the paste filled via hole to form metalized via and cause the laminated ceramic substrate to form a hermetic seal around said metalized via, and removing the upper ceramic sheet and the lower ceramic sheet material from the fired laminated ceramic substrate to expose an upper and a lower surface of the metalized via.

Description

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. provisional Patent Application Ser. No. 60/946,086, filed Jun. 25, 2007 for “Method and Apparatus for Providing Hermetic Electrical Feedthrough” by Jerry Ok and Robert J. Greenberg, the disclosure of which is incorporated herein by reference. This application is related to U.S. patent application Ser. No. 09/823,464, filed Mar. 30, 2001 for “Method and Apparatus for Providing Hermetic Electrical Feedthrough” by Jerry Ok and Robert J. Greenberg, the disclosure of which is incorporated herein by reference.

FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

The present disclosure was made with support from the United States Government under Grant number R24EY12893-01, awarded by the National Institutes of Health. The United States Government has certain rights in the invention.

FIELD

The present disclosure relates generally to a method and apparatus for providing electrical feedthroughs and more particularly to a method and apparatus suitable for forming hermetic electrical feedthroughs through a ceramic sheet.

BACKGROUND

Various approaches are described in the literature for fabricating hermetically sealed electrical circuit housings suitable for extended operation in corrosive environments, e.g., in medical devices implanted in a patient's body. For such applications, a housing must be formed of biocompatible and electrochemically stable materials and typically must include a wall containing multiple hermetic electrical feedthroughs. A hermetic electrical feedthrough is comprised of electrically conductive material which extends through and is hermetically sealed in the wall material.

One known approach uses an assembled pin feedthrough consisting of a conductive pin that is bonded chemically at its perimeter through brazing or the use of oxides, and/or welded, and/or mechanically bonded through compression to a ceramic body. Typically, gold is used as a braze material that wets the feedthrough pin and the ceramic body resulting in a hermetic seal. Wetting to the ceramic body requires a deposited layer of metal such as titanium. This layer acts additionally as a diffusion barrier for the gold.

Other alternative feedthrough approaches use a metal tube cofired with a green ceramic sheet. The hermeticity of the metal/ceramic interface is achieved by a compression seal formed by material shrinkage when the assembly is fired and then allowed to cool. The use of a tube inherently limits the smallest possible feedthrough to the smallest available tubing. Acceptable results have been reported only when using tubes having a diameter >40 mils in ceramic substrates at least 70 mils thick.

SUMMARY

According to a first aspect, a method of fabricating a hermetic electrical feedthrough is disclosed, the method comprising: providing a ceramic sheet having an upper surface and a lower surface; forming at least one via hole in said ceramic sheet extending from said upper surface to said lower surface; inserting a conductive thickfilm paste into said via hole; laminating the ceramic sheet with paste filled via hole between an upper ceramic sheet and a lower ceramic sheet to form a laminated ceramic substrate; firing the laminated ceramic substrate to a temperature to sinter the laminated ceramic substrate and cause the paste filled via hole to form metalized via and cause the laminated ceramic substrate to form a hermetic seal around said metalized via; and removing the upper ceramic sheet and the lower ceramic sheet material from the fired laminated ceramic substrate to expose an upper and a lower surface of the metalized via.

According to a second aspect, a method of fabricating a hermetic electrical feedthroughs is disclosed, the method comprising: providing a plurality of ceramic sheets having an upper surface and a lower surface; forming a plurality of via holes in each of the ceramic sheets extending from said upper surface to said lower surface of each ceramic sheet; inserting a conductive thickfilm paste into the via holes of each ceramic sheet; stacking the plurality of ceramic sheets on top of each other, wherein the via holes filled with conductive thickfilm paste of each ceramic sheet is substantially aligned with the via holes filled with conductive thickfilm paste of the other ceramic sheets; sandwiching the stacked ceramic sheets between an upper ceramic sheet and a lower ceramic sheet; laminating stacked plurality of ceramic sheets with the lower ceramic sheet and the upper ceramic sheet to form a laminated ceramic substrate; firing the laminated ceramic substrate to a temperature to sinter the laminated ceramic substrate and cause the paste filled via holes to form metalized vias and cause the laminated ceramic substrate to form a hermetic seal around the metalized vias; and removing the upper ceramic sheet and the lower ceramic sheet material from the fired laminated ceramic substrate to expose an upper and a lower surface of the metalized vias.

Further embodiments are shown in the specification, drawings and claims of the present application.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 depicts a top view of a finished feedthrough assembly in accordance with the present disclosure comprised of a ceramic sheet having electrically conductive vias extending therethrough;

FIG. 2 depicts a sectional view taken substantially along the plane 2-2 of FIG. 1 showing the electrically conductive vias ends flush with the surfaces of the ceramic sheet;

FIG. 3 depicts a flow diagram illustrating a possible series of process steps for fabricating a feedthrough assembly in accordance with the present disclosure;

FIGS. 4A-4M respectively depict the fabrication stages of a feedthrough assembly in accordance with the process flow illustrated in FIG. 3, wherein FIG. 4A depicts a sectional view of a ceramic sheet; FIGS. 4B-C depict via holes being punched in the sheet of FIG. 4A; FIGS. 4D-E depict exemplary stencil printing with vacuum pull down process; FIG. 4F depicts paste inserted into the via holes; FIGS. 4G-H depict exemplary multilayer lamination process; FIG. 41 shows an exemplary laminated substrate; FIGS. 4J-K depict lapping/grinding process; and FIGS. 4L-M depict dicing of the substrate to form multiple feedthrough assemblies.

In the following description, like reference numbers are used to identify like elements. Furthermore, the drawings are intended to illustrate major features of exemplary embodiments in a diagrammatic manner. The drawings are not intended to depict every feature of every implementation nor relative dimensions of the depicted elements, and are not drawn to scale.

DETAILED DESCRIPTION

The present disclosure is directed to a method and apparatus suitable for forming hermetic electrical feedthroughs in a ceramic sheet (or substrate) having a possible thickness of ≦40 mils. More particularly, the disclosure is directed to a method and apparatus for forming a structure including a hermetic electrical feedthrough which is both biocompatible and electrochemically stable and suitable for implantation in a patient's body.

Electrical feedthroughs in accordance with the present writing are intended to function in corrosive environments, e.g., in medical devices intended for implantation in a patient's body. In such applications, it is generally critical that the device housing be hermetically sealed which, of course, requires that all feedthroughs in the housing wall also be hermetic. In such applications, it is also generally desirable that the weight and size of the housing be minimized and that all exposed areas of the housing be biocompatible and electrochemically stable. Biocompatiblity assures that the implanted device has no deleterious effect on body tissue. Electrochemical stability assures that the corrosive environment of the body has no deleterious effect on the device. Ceramic and platinum materials are often used in implantable medical devices because they typically exhibit both biocompatibility and electrochemical stability.

Embodiments constructed in accordance with the present disclosure are able to achieve very high feedthrough density. For example, in applications where miniaturization is important, the feedthrough pitch, i.e., center-to-center distance between adjacent feedthroughs may be from 10 mils to 40 mils.

Attention is initially directed to FIGS. 1 and 2 which depict a preferred feedthrough assembly 8 in accordance with the present disclosure comprising a thin ceramic sheet 10 of ceramic material having multiple electrical feedthroughs 12 extending therethrough terminating flush with the upper and lower surfaces 14, 16 of sheet 10. The sheet 10 typically comprises a wall portion of a housing (not shown) for accommodating electronic circuitry. The feedthroughs 12 function to electrically connect devices external to the housing, e.g., adjacent to surface 14, to electronic circuitry contained within the housing, e.g., adjacent to surface 16. “Thin ceramic sheet” as used herein refers to a sheet having a finished thickness dimension of ≦40 mils, i.e., 1 mm. The apparatus in accordance with the disclosure is particularly suited for use in corrosive environments such as in medical devices implanted in a patient's body.

The present disclosure is directed to providing electrical feedthroughs that are compatible with thin ceramic sheets (or substrates) having a finished thickness of ≦40 mils, and with feedthroughs that are hermetic, biocompatible, and electrochemically stable. In one exemplary embodiment, the ceramic sheet 10 may be formed of 90% aluminum oxide (AlO₂) and the feedthroughs 12 may have a diameter of ≦20 mils and may be composed of paste containing, for example, platinum.

Attention is now directed to FIGS. 3 and 4A-4M which depict the possible process steps for fabricating the finished feedthrough assembly 8 illustrated in FIGS. 1 and 2.

Initially, a green ceramic sheet/tape/substrate 20 (FIG. 4A), formed, for example, of >90% aluminum oxide (AlO₂) is selected as represented by step 21 in FIG. 3. In an exemplary embodiment, the sheet 20 may have a thickness of 40 mils or less. “Green ceramic sheet/tape/substrate” as used herein refers to an unfired ceramic sheet, tape or substrate.

Via holes 26 are formed into the sheet 20 as represented by FIGS. 4B-4C and step 28 in FIG. 3. In an exemplary embodiment, each via hole 26 may be punched in to the sheet 20 using, for example, programmable punch tool 27. In one exemplary embodiment, a plurality of via holes 26 may be punched at the same time. It is to be understood that other methods may be used to form via holes 26. For Example, via holes 26 may be formed using solvent etching, laser ablation, and/or via holes 26 may be drilled.

Step 37 of FIG. 3 calls for selecting a conductive thickfilm paste 17 to fill in via holes 26 depicted in FIG. 4C. “Thickfilm paste” as used herein refers to a material containing inorganic particles dispersed in a vehicle comprising an organic resin and a solvent. Types of different pastes are disclosed in U.S. Pat. No. 5,601,638, the disclosure of which is incorporated herein by reference.

In one exemplary embodiment, a stencil printing with vacuum pull down process may be used to fill via holes 26 with the conductive paste 17 as represented by FIGS. 4D-4E and step 39 in FIG. 3. During the stencil printing with vacuum pull down process, the sheet 20 may sandwiched between a stencil layer 19 and a vacuum base 80. As a squeegee 18 roles the conductive paste 17 across the stencil layer 19, a vacuum chuck 81 of the vacuum base 80 pulls the conductive paste 17 through holes 82 of the stencil layer 19 and into the via holes 26 as shown in FIGS. 4D-4E.

Step 40 of FIG. 3 calls for determining if additional green ceramic sheet/tape/substrates with paste filled via holes are required. If additional green ceramic sheet/tape/substrates with paste filled via holes are required (“Yes” in step 40), steps 21, 28, 37 and 39 are repeated. If additional green ceramic sheet/tape/substrates with paste filled via holes are not required (“No” in step 40), step 41 of FIG. 3 is performed.

Upon completion of the stencil printing with vacuum pull down process and step 40, the sheet 20 with via holes 26 filled with conductive paste 17 shown in FIG. 4F may go through a multilayer lamination process as represented by FIGS. 4G-4H and step 41 in FIG. 3.

In the multilayer lamination process, the sheet 20 of FIG. 4F may be laminated with, for example, sheets 91 and 92 as shown in FIG. 4G. The sheets 91 and 92 may contain conductive paste filled vias 26 that are similar to the conductive paste filled vias 26 of the sheet 20 and the sheets 91 and 92 may be formed using steps 21, 28, 37 and 39 of FIG. 3 as described above.

During the multilayer lamination process, a) the sheets 20, 91 and 92 are stacked on top of each other with conductive paste filled vias 26 of each sheet being aligned on top of each other; b) stacked sheets 20, 91 and 92 are sandwiched between two unpunched green ceramic sheets/tapes/substrates 95 and 96; and c) the sheets 20, 91 and 92 and the sheets 95 and 96 are laminated together using a heatpress 98 to create laminated substrate 100 shown in FIG. 41.

Although FIGS. 4G and 4H laminate three sheets 20, 91 and 92 with conductive paste filled vias 26, one skilled in the art can appreciate that this disclosure is not limited to three sheets and that a single sheet 20 with conductive paste filled vias may be laminated together with the sheets 95 and 96 without the additional sheets 91 and 92. Although FIGS. 4G and 4H appreciate that this disclosure is not limited to three sheets and that additional sheets with conductive paste filled vias may also be laminated together with sheets 20, 91 and 92.

Step 44 of FIG. 3 calls for the laminated substrate 100 to be fired. Firing of the laminated substrate 100 encompasses different aspects of forming bonds in ceramic (evaporation, binder burnout, sintering, etc.). The unpunched ceramic layers 95 and 96 of the laminated substrate 100 help to constrain the conductive paste within via holes 26 and allow for compression during the firing step 44. The unpunched ceramic layers 95 and 96 of the laminated substrate 100 also help to isolate the conductive paste filled vias 26 from the firing atmosphere during the step 44 which may be the key to hermetic and low resistance paste filled vias 26. An exemplary firing schedule includes ramping the laminated substrate 100 of FIG. 41 up to 600° C. at a rate of 1° C./minute, then ramping up to 1600° C. at a rate at 5° C./minute, followed by a one hour dwell and then a cool-to-room-temperature interval.

During the firing and subsequent cooling during the step 44, the ceramic material of the laminated substrate 100 shrinks thereby shrinking via holes 26 around the paste 17 to form a seal. The fine aluminum oxide suspension permits uniform and continuous sealing around the surface of the paste 17. Additionally, at the maximum firing temperature, e.g., 1600° C., the paste 17 being squeezed by the ceramic exhibits sufficient flow to enable the paste 17 to flow and fill any crevices in the ceramic. This action produces a hermetic paste/ceramic interface. Furthermore, the firing step 44 may also cause hermeticity through bonding mechanisms like, for example, sintering, glass melt/wetting, alloying, compounding and/or diffusion solution formation. “Sintering” as used herein is a term used to describe the consolidation of the ceramic material during firing. Consolidation implies that within the ceramic material, particles have joined together into an aggregate that has strength. The term sintering may be used to imply that shrinkage and densification have occurred; although this commonly happens, densification may not always occur. □ “Sintering” is also a method for making objects from powder, by heating the material (below its melting point) until its particles adhere to each other. “Sintering” is traditionally used for manufacturing ceramic objects, and has also found uses in such fields as powder metallurgy. “Alloying” as used herein refers to an alloy that is a homogeneous hybrid of two or more elements, at least one which is a metal, and where the resulting material has metallic properties. “Compounding” as used herein refers to a chemical compound that is a substance consisting of two or more elements chemically-bonded together in a fixed proportion by mass. “Diffusion solution formation” as used herein refers is the net movement of particles from an area of high concentration to an area of low concentration. A solid solution is a solid-state solution of one or more solutes in a solvent. Such a mixture is considered a solution rather than a compound when the crystal structure of the solvent remains unchanged by addition of the solutes, and when the mixture remains in a single homogeneous phase. Also, the firing step 44 may also cause solidification of the metalized vias 26 and the ceramic material of the laminated substrate 100 to prevent leaks.

Step 48 of FIG. 3 calls for lapping or grinding the upper and lower surfaces of the fired laminated substrate 100 to remove materials 50 and 51, depicted in FIG. 4J, in order to expose the upper and lower faces of the metalized vias 26. The upper and lower surfaces of the fired laminated substrate 100 may also go through the polishing step 49 so that the metalized vias 26 are flush with the surrounding ceramic material.

After lapping and/or grinding, the fired laminated substrate 100 may be subjected to a hermeticity test, e.g., frequently a helium (He) leak test as represented by step 56 in FIG. 3.

In one exemplary embodiment, sheet/substrate 20 may contain several patterns 24a-d of the via holes 26 as shown in FIG. 4L. In this exemplary embodiment, the fired laminated substrate 100 would contain several patterns 24a-d of the metal filled via holes 26 and the fired laminated substrate 100 would be subjected to a singulation or dicing step 58 to provide multiple feedthrough assemblies 60A, 60B, 60C, 60D shown in FIG. 4M.

Although some embodiments described above employ a ceramic sheet of >90% aluminum oxide (AlO₂), alternative embodiments may use other ceramic materials, e.g., zirconium. Because the firing temperature of the ceramic can be tailored within certain limits, the conductive paste 17 may comprise any of the noble metals and/or any of the refractory metals, for example, platinum, titanium, gold, paliadum, tantalum, niobium.

As used in this specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the content clearly dictates otherwise. The term “plurality” includes two or more referents unless the content clearly dictates otherwise. Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the disclosure pertains.

From the foregoing, it should now be appreciated that electrical feedthrough assemblies and fabrication methods thereof have been described suitable for use in medical devices intended for implantation in a patient's body. Although a specific structure and fabrication method has been described, it is recognized that variations and modifications will occur to those skilled in the art coming within the spirit and scope of the invention as defined by the appended claims.

Claims

1. A method of fabricating a hermetic electrical feedthrough, the method comprising:

providing a ceramic sheet having an upper surface and a lower surface;

forming at least one via hole in said ceramic sheet extending from said upper surface to said lower surface;

inserting a conductive thick film paste into said via hole;

laminating the ceramic sheet with paste filled via hole between an upper ceramic sheet and a lower ceramic sheet to form a laminated ceramic substrate;

firing the laminated ceramic substrate to a temperature to sinter the laminated ceramic substrate and cause the paste filled via hole to form a metalized via and cause the laminated ceramic substrate to form a hermetic seal around said metalized via; and

removing the upper ceramic sheet and the lower ceramic sheet material from the fired laminated ceramic substrate to expose an upper and a lower surface of the metalized via.

2. The method of claim 1, wherein said ceramic sheet is formed of material comprised of at least 90% aluminum oxide.

3. The method of claim 1, wherein said ceramic sheet is formed of material comprised of at least 92% aluminum oxide.

4. The method of claim 1, wherein said ceramic sheet after said firing and material removal steps is less than or equal to 40 mils thick.

5. The method of claim 1, wherein said ceramic sheet after said firing and material removal steps is less than 15 mils thick.

6. The method of claim 1, wherein said paste comprises platinum.

7. The method of claim 1, wherein the metalized via has a diameter of less than or equal to 20 mils.

8. The method of claim 1, wherein the metalized via has a diameter of less than or equal to 10 mils.

9. The method of claim 1, wherein the ceramic sheet is unfired.

10. The method of claim 1, wherein forming at least one via hole in said ceramic sheet comprises punching the via hole using a punch tool, etching the via hole using a solvent etching, using laser ablation or drilling the via hole.

11. The method of claim 1, wherein inserting a conductive thick film paste into said via hole comprises:

disposing the ceramic sheet with the via hole between a stencil layer and a vacuum base, wherein the stencil layer includes at least one though hole that is aligned above the via hole;

roll the conductive thickfilm paste across the stencil layer; and

pull the conductive thickfilm paste into the via hole though the hole in the stencil layer with a vacuum created by the vacuum base.

12. The method of claim 1, wherein laminating the ceramic sheet with paste filled via holes between the upper ceramic sheet and the lower ceramic sheet to form the laminated ceramic substrate comprises:

placing the ceramic sheet with paste filled via holes together with the upper ceramic sheet and the lower ceramic sheet in a heatpress; and

applying heat and pressure by the heatpress until the laminated ceramic substrate is formed.

13. The method of claim 1, wherein firing the laminated ceramic substrate comprises evaporation, binder burnout and sintering of the laminated ceramic substrate.

14. The method of claim 1, wherein said ceramic material comprises aluminum oxide, zirconium oxide or mixture thereof.

15. The method of claim 1, wherein said ceramic material comprises less than 99% aluminum oxide.

16. The method of claim 1, wherein the fired laminated ceramic substrate has a thickness of less than 20 mils after removing the upper ceramic sheet and the lower ceramic sheet material.

17. The method of claim 1, wherein the fired laminated ceramic substrate has a thickness of 15-20 mils after removing the upper ceramic sheet and the lower ceramic sheet material.

18. The method of claim 1, wherein said conductive thickfilm paste comprises a material selected from the group consisting of platinum, titanium, gold, palladium, tantalum, and niobium.

19. The method of claim 1, wherein said conductive thickfilm paste comprises noble metal, refractory metal or mixture thereof.

20. A method of fabricating a hermetic electrical feedthrough, the method comprising:

providing a plurality of ceramic sheets having an upper surface and a lower surface;

forming a plurality of via holes in each of the ceramic sheets extending from said upper surface to said lower surface of each ceramic sheet;

inserting a conductive thickfilm paste into the via holes of each ceramic sheet;

stacking the plurality of ceramic sheets on top of each other, wherein the via holes filled with conductive thickfilm paste of each ceramic sheet are substantially aligned with the via holes filled with conductive thickfilm paste of the other ceramic sheets;

sandwiching the stacked ceramic sheets between an upper ceramic sheet and a lower ceramic sheet;

laminating the stacked plurality of ceramic sheets with the lower ceramic sheet and the upper ceramic sheet to form a laminated ceramic substrate;

firing the laminated ceramic substrate to a temperature to sinter the laminated ceramic substrate and cause the paste filled via holes to form metalized vias and cause the laminated ceramic substrate to form a hermetic seal around the metalized vias; and

removing the upper ceramic sheet and the lower ceramic sheet material from the fired laminated ceramic substrate to expose an upper and a lower surface of the metalized vias.