ELECTRICALLY CONDUCTIVE YARN WITH REDUCED TORSIONS

Abstract

A yarn (100) comprising one or more bundles (110, 120, 130), each of said one or more bundles comprising at least thirty metal fibres is described. The metal fibres (140) comprise stainless steel and a metal which is electrically more conductive than stainless steel. The yarn is twisted with a predetermined number of torsions per meter, said predetermined number of torsions per meter is smaller than 80 per meter and larger than 10 per meter. By doing so, an improved flexlife of the yarn can be obtained.

Description

TECHNICAL FIELD

The present invention relates to an electrically conductive yarn comprising one or more bundles of metal fibres and to its various uses.

BACKGROUND ART

Yarns comprising one or more bundles of metal fibres are known. Such yarns are e.g. applied in vehicle seat heating systems or heatable textiles. In these applications, the yarns are used as an electrical resistance and provided, in use, with an electric current to obtain the required heating effect. In many of the applications of such yarns, the yarns are subjected to different stress and/or strain conditions. In particular, the yarns may be repeatedly loaded under tensile and/or bending or torsion stresses, e.g. when applied in a car seat heating. When repeatedly subjected to such stresses, metal fibres of the yarn may break, eventually resulting in the failure of the yarn. As a result, the yarn may no longer provide its function as a heating element in e.g. a car seat heating.

DISCLOSURE OF INVENTION

In general, there is a desire to increase the life time of systems or components. In case of the application of yarns comprising bundles of metal fibres, the life time of the yarn is affected by its resistance against repeated bending, which is generally called the flexlife. Therefore, in order to improve the life time of yarns comprising one or more bundles of metal fibres, it is an object of the present invention to design a yarn having an improved resistance against bending and/or fretting and/or wear, which improved resistance is called an improved flexlife. Within the meaning of the present invention, flexlife is to be understood as “the resistance to rupture of the yarn under repetitive bending conditions”.

According to the invention, this object is achieved by a yarn for car seat heating comprising one or more bundles, each bundle comprising at least thirty metal fibres, said metal fibres comprising stainless steel and a metal which is electrically more conductive than stainless steel, such as e.g. copper or a copper alloy, said yarn comprising a predetermined number of torsions per meter, characterized in that said predetermined number of torsions per meter is smaller than 80 per meter and larger than 10 per meter.

Examples of a metal “which is electrically more conductive than stainless steel” are e.g. copper, aluminium, nickel, silver, gold or any alloy thereof.

The bundles comprise and at least 30 metal fibers. Preferably, all the fibers in the bundle are metal fibers. Even more preferably, all the fibers in the bundles are metal fibers comprising stainless steel and a metal which is electrically more conductive than stainless steel.

The metal fibres can be single drawn or bundle drawn. For a single drawn fibre the diameter reduction is done by means of a series of dies for one fibre. For bundle drawn fibres the diameter reduction is done by means of a single series of dies for the whole bundle, as e.g. described in U.S. Pat. No. 3,379,000, U.S. Pat. No. 3,394,213, U.S. Pat. No. 2,050,298 or U.S. Pat. No. 3,277,564. In case of the bundle drawing operation, the cross section of a fiber has usually a pentagonal or hexagonal shape as is shown in FIG. 2 of U.S. Pat. No. 2,050,298, and the circumference of the fiber cross section is usually serrated as opposed to a single drawn fiber, which has a circular cross section. This difference in fiber cross section resulted in the use of the term “equivalent diameter” of a fiber which is to be understood as the diameter of an imaginary circle having a surface area equal to the surface area of the radial cross section of the fiber.

The number of torsions per meter may vary from 10 per meter until 80 per meter, e.g. from 20 per meter until 70 per meter, e.g. from 30 per meter until 60 per meter. As used herein, the term “number of torsions” must be understood to be the amount of twist or torsion used to obtain the electrically conductive yarn, or stated otherwise, the number of turns about the axis of the yarn. In case only one bundle is present in the yarn, the number of torsions is the amount of torsion applied on this individual bundle. In case two or more bundles are present in the yarn, the number of torsions is the amount of twist used to combine the bundles into the yarn.

As such, a yarn according to the present invention encompasses the following examples:

• • A yarn comprising one single bundle comprising 1000 fibres, the bundle having 50 torsions per meter.
  • A yarn comprising two bundles, each comprising 275 fibres, the bundles being twisted with one another with 50 torsions per meter.

With respect to the second example, preferably the individual bundles have no torsions on their own.

It has been observed in various experiments that the number of torsions per meter as applied in a yarn comprising one or more bundles of metal fibres affects the flexlife of the yarn. More specifically, it has been observed that an important increase in flexlife is achieved when the number of torsions per meter is kept below 80.

In general, a much higher number of torsions per meter is applied in yarn in order to obtain the various elements of the yarn (i.e. the fibres in a bundle or bundles) closely together. However, as surprisingly has been observed in the present invention, this high number of torsions may adversely affect the flexlife of the yarn. As a consequence, the life expectancy of the application comprising the yarn may be reduced. By selecting the number of torsions per meter according to the present invention, an increase of the flexlife of the yarns, and consequently an increased life time of the system wherein the yarns are applied, can be realised. Examples of applications wherein the flexlife of the yarns plays an important role are e.g. the use in heating applications such as a car seat heating. In order to keep the different elements of the yarn from spreading too far apart, it has been observed that a minimum number of approx. 10 torsions per meter is sufficient.

As a matter of example only, it has been observed by experiments that in particular embodiments of the yarns according to the present invention the flexlife can be 10,000 cycles or more. The fibres as applied in yarns according to the present invention comprise multiple layers of metal and at least they comprise both stainless steel and a metal which is electrically more conductive than stainless steel, such as e.g. copper or copper alloy. By applying such a fibre, advantage can be made of the properties of both the stainless steel and the metal which is electrically more conductive than stainless steel. The fibres as applied in the yarns according to the invention thus combine the favourable strength properties of a stainless steel and the electrical resistance properties of such electrically more conductive metal such as e.g. copper.

The equivalent diameter of the individual metal fibres is typically smaller than 50 μm, e.g. smaller than 40 μm, e.g. smaller than 20 μm. The fibre diameter is typically greater than 1 μm, e.g. greater than 2 μm, e.g. greater than 6 μm. It has been observed that a reduced fibre diameter also has a positive effect on the flexlife.

The metal fiber yarn can further be coated with a suitable coating, preferably PVC, PVA, PTFE (polytetrafluoroethylene, also called Teflon) FEP (copolymers of tetrafluoromethylene and hexafluoropropylene), MFA (perfluoroalkoxy polymer) or polyurethane lacquer.

A yarn according to the invention is advantageously used in car seat heating, but also in textile products in general or for heating applications in general.

BRIEF DESCRIPTION OF FIGURES IN THE DRAWINGS

FIG. 1 schematically shows a cross-sectional view of a yarn according to the present invention;

FIGS. 2a and 2b schematically illustrate two possible ways of twisting multiple bundles about one another to obtain a yarn according to the present invention;

FIG. 3 schematically illustrates the flexlife of a yarn as a function of the number of torsions per meter;

FIG. 4 schematically illustrates the application of a yarn according to the present invention as a heating element for a car seat.

MODE(S) FOR CARRYING OUT THE INVENTION

Yarns according to the present invention comprise one or more bundles of metal fibres, each bundle comprising at least 30 metal fibres. FIG. 1 schematically depicts a cross-sectional view of a yarn 100 according to the present invention. The yarn 100 comprises three bundles 110, 120 and 130 each comprising more than 30 metal fibres 140.

In the present invention, metal is to be understood as encompassing both metals and metal alloys (such as stainless steel) or compositions. As an example, the metal fibres as applied in the present invention may comprise a stainless steel core enclosed by copper or a copper alloy. Alternatively, the metal fibres as applied in a yarn according to the present invention may have a copper core surrounded by a stainless steel mantle. Such fibres provide improved electrical properties combined with the corrosion and oxidation resistance of stainless steel. Said stainless steel is preferable chosen out of AISI 300 series such as AISI 302, 304, 316 or 316L, or AISI 400 series such as AISI 430, AISI 625 or AISI 904.

In accordance with the present invention, the fibres forming the bundles may either be bundle-drawn fibres or single drawn fibres.

The metal fibres as applied in the yarns according to the present invention preferably have an equivalent diameter being less than 50 micrometer, but more than 0.5 micrometer, preferably between 1 micrometer and 35 micrometer, yet preferably between 7 and 21 micrometer. The equivalent diameter of a fibre is to be understood as the diameter of an imaginary circle, having the same area as the cross section of the fibre.

Preferably, the bundles of fibres as applied in the yarns according to the present invention are obtained from a bundle-drawing process. The latter process may advantageously be applied as it enables the manufacturing of thinner fibres compared to a single-drawing process. In addition, the bundle-drawing process can be considered a more economical process as it results in a plurality of fibres being obtained at the same time. With respect to bundle drawing of metal fibres, reference can be made to U.S. Pat. No. 3,394,213, U.S. Pat. No. 2,050,298 or U.S. Pat. No. 3,277,564.

The yarns according to the present invention may advantageously be applied to obtain a textile product, e.g. a braided, woven, knotted or knitted textile product.

The metal fibres as applied in the yarns according to the present invention may comprise a core of a material having a higher electric conductivity compared to steel or steel alloys. Preferred materials for forming such a core are copper or copper alloys.

When such materials are to be used for forming the metal fibres, bundles of such materials may equally be obtained by grouping a plurality of single-drawn wires or filaments, or, preferably, as in the present invention, using a bundle-drawing process, as e.g. described in JP-A-5-177243 and WO-A-2006/120045 obtaining metal fibres with multiple layers. As such, a bundle of metal fibres having a copper or copper alloy core and a mantle of e.g. stainless steel can be obtained. In a preferred embodiment, the stainless steel mantle may comprise AISI 316L steel or AISI 625 or AISI 904.

Said bundles may advantageously be applied in yarns according to the present invention for such applications where the electrical conductivity is important, such as electrical heating applications. Such applications can e.g. include heatable textiles wherein the electrically conductive yarn functions as a resistive heating element. Such textiles can e.g. be part of a heating device which is integrated in a car seat, usually between a foamed part of the seat and the seat upholstery.

A further application where the electrical conductivity is important and where the yarns according to the invention may advantageously be applied is the use as leadwire connecting different electronic devices to each other such as batteries, PCB's or monitoring devices.

With respect to the twisting of the two or more bundles as applied in embodiments of the yarns according to the present invention, different options exist. Two options are illustrated in FIGS. 2a and 2b.

FIG. 2a schematically depicts two bundles A and B and a reference line L on the outer surface of each bundle (if the bundle is untwisted, then the reference point is a fibre L the fibre being located on the circumference of the bundle). One way of twisting the different bundles A and B is by bending the bundles about each other, substantially without applying any torsion on the individual bundles. As such, the twisting of the two or more bundles does not result in a (additional) torsion of the individual bundles. This is illustrated on the left side of FIG. 2b. As can be seen, reference line L (or fibre L) substantially remains in the position relative to the circumference (or other fibres) of the bundle. This process is sometimes referred to as “cabling” and can be carried out by means of tubular twisting machines.

As an alternative, the bundles of the yarns can be twisted by applying a torsional force on the two or more bundles. By doing so, the individual bundles also have a torsion on their own, or get an additional torsion. This is illustrated on the right side of FIG. 2b. This process is sometimes referred to as “bunching” and can be carried out by double-twisting machines.

The flexlife improvement that can be obtained by yarns according to the present invention is further illustrated by the graph shown in FIG. 3. FIG. 3 schematically indicates the flexlife FL as a function of the number of torsions per meter N. As can be seen on the graph, an important flexlife improvement is obtained when the number of torsions per meter is kept below 80. By a further reduction of the number of torsions per meter, the flexlife can be increased even further. However, as already mentioned above, in order to keep the different bundles of the yarn from spreading too far apart, it has been observed that a minimum number of approx. 10 torsions per meter should be observed. A good compromise between an improved flexlife and avoiding the bundles from spreading too far apart is found when the number of torsions per meter is between 30 and 60.

Yarns according to the present invention may advantageously be applied as a heating element for a car seat. This is illustrated in FIG. 4. FIG. 4 schematically shows a car seat 500 provided with a textile product 510 comprising yarns in accordance with the present invention as electrical electrodes 511. Carbon wires 512 may be coupled to an electric device (not shown) that is arranged to provide, in use, the required current to the textile product by means of two cables 513, each being coupled to an electrode 511 to which the carbon wires 512 are coupled. This arrangement is called a parallel car seat heating element.

Alternatively, a serial car seat heating embodiment can be provided, where the yarns according to the present invention function as the heat resisting elements.

The improvement with respect to the flexlife that can be realised by yarns according to the invention is illustrated by the following test results.

The following table 1 shows, as an example, the experimentally determined flexlife of the following yarns.

The yarns are indicated as:

a/b×c/d

wherein

a equals the equivalent diameter of the fibres,

b represents the number of bundles,

c represents the number of fibres per bundle and

d represents the number of torsions per meter.

	TABLE 1
		Av. # of cycles
	yarn	(Flexlife)	Tex	Flex Factor
	14/1 × 275/40	2702	340	7.9
	14/1 × 275/100	2368	340	7.0
	14/1 × 275/150	2420	340	7.1
	14/4 × 90/40	3593	445	8.1
	14/4 × 90/100	2526	445	5.7
	14/4 × 90/150	1989	445	4.5
	12/2 × 275/50	4800	499	9.6
	12/2 × 275/120	3627	499	7.3
	12/2 × 275/175	3089	499	6.2
	12/3 × 275/50	6446	749	8.6
	12/3 × 275/120	5727	749	7.6
	12/3 × 275/175	5082	749	6.8
	14/3 × 275/50	6871	1020	6.7
	14/3 × 275/100	4784	1020	4.7
	14/3 × 275/175	4013	1020	3.9

The flexlife can be determined by subjecting a sample length of a yarn to a repeated bending over a bending radius of about 0.60 mm to 0.80 mm and under an axial load. The bending degree in such a test is generally taken as 180°. During the test, a micro-current is arranged to run through the yarn sample, the yarn sample forming part of an electrical circuit. Once all fibres of the sample are broken, the electric circuit is also broken and the counting of the number of bendings is stopped.

Flexlife must be compared for yarns having a same tex number (tex is being expressed in g/1000m). In table 1, it is clear that for yarns with approximately same tex numbers the flexlife is better for smaller diameters of fibers. The flexfactor, which is the ratio of the number of flex life cycles to the Tex of the yarn, is therefore an appropriate means for comparing the “flexlife” of a yarn. By examining the flexfactor, as in table 1, it is clear that lower torsions applied on a yarn, as well as smaller diameters of fibers in the yarn provide a better “flexlife”.

Although various specific applications of the yarns according to the invention are mentioned, the present invention is in no way restricted to the applications mentioned.

Claims

1. An electrically conductive yarn comprising one or more bundles, each bundle comprising at least thirty metal fibres, said metal fibres comprising stainless steel and a metal which is electrically more conductive than stainless steel, said yarn comprising a predetermined number of torsions per meter, characterized in that said predetermined number of torsions per meter is smaller than 80 per meter and larger than 10 per meter.

2. A yarn according to claim 1, wherein said metal fibres are single-drawn or bundle-drawn.

3. A yarn according to claim 1, the yarn comprising two or more bundles.

4. A yarn according to claim 1, wherein said metal which is electrically more conductive than stainless steel is copper.

5. A yarn according to claim 1, wherein said predetermined number of torsions is between 30 torsions per meter and 60 torsions per meter.

6. A yarn according to claim 1 wherein the number of bundles times the number of fibres per bundle is larger than 250.

7. A yarn according to claim 1, wherein said metal fibres are untwisted in some or all of said bundles.

8. A yarn according to claim 1, wherein said metal fibres are twisted in some or all of said bundles.

9. A yarn according to claim 1, wherein said metal fibres comprise a copper core and a stainless steel mantle.

10. A yarn according to claim 1 wherein said yarn has an isolating coating such as PTFE (Polytetrafluoroethylene).

11. A yarn according to claim 1, said yarn additionally comprising a polymer elongated element, said polymer elongated element twisted with said one or more bundles of metal fibres.

12. A heating element comprising an electrically conductive yarn as in claim 1.

13. The use of an electrically conductive yarn as in claim 1 as resistive heating elements in heatable textile applications.

14. The use of an electrically conductive yarn as in claim 13, wherein said heatable textile application is car seat heating.

15. The use of an electrically conductive yarn as in claim 1 in a leadwire.