HYDROGEN ELIMINATION AND THERMAL ENERGY GENERATION IN WATER-ACTIVATED CHEMICAL HEATERS
A hydrogen suppressing, flameless, heat generating chemical composition including magnesium, a hydrogen suppressor or eliminator, particulate carbon, an alloying metal selected from the group consisting of: iron, cobalt, nickel, zinc, aluminum and mixtures thereof, a metallic salt including a cation and an anion, wherein the anion is selected from the group consisting of silicate, carbonate, bicarbonate, phosphate, borate, perborate, percarbonate, perphosphate, persulfate, nitrate, nitrite, ferrate, permanganate, and stannate and combinations thereof, and water. The magnesium or magnesium-containing alloy, hydrogen suppressor or eliminator, particulate carbon, alloying metal, metallic salt and water are each present in a proportional amount to generate sufficient heat to heat water, medical supplies and/or consumable rations.
This application is a Continuation-in-Part of application Ser. No. 12/701,990, filed on Feb. 8, 2010, which is a Continuation-in-Part of application Ser. No. 12/322,596, filed on Feb. 4, 2009, which is a Continuation-in-Part of application Ser. No. 12/069,995, filed on Feb. 14, 2008, which is a Continuation-in-Part of application Ser. No. 11/657,852, filed on Jan. 25, 2007, which claims the benefit of Provisional Application Ser. No. 60/764,213, filed on Feb. 1, 2006, which applications are incorporated herein by reference.
STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENTThe U.S. Government has a paid-up license in this invention and the right in limited circumstances to require the patent owner to license others on reasonable terms as provided for by the terms of Contract Nos. W911QY-06-C-0021, W911QY-07-P-0335 and W911QY-08-C-0096 awarded by the Department of Defense.
BACKGROUND OF THE INVENTIONFlameless Chemical Heaters (FCH), also known as Flameless Ration Heaters (FRH), are used in Meal, Ready-to-Eat (MRE) packaging to provide hot meals to soldiers in the field or for warming or heating medical supplies or food rations in confined spaces (e.g., tents, underwater shelters) or in remote locations where there is no heat source. These FCHs or FRHs are generally based on the reaction of magnesium with water to form magnesium hydroxide and hydrogen which releases about 85 kcal of energy per mole of magnesium. Equation [1] below sets forth this reaction.
Mg+2H2O→Mg(OH)2+H2+Δ [1]
There are two types of MREs. The first is an individual meal for the soldier. The second one is a family-style meal for a group of 10-20 soldiers, called the Unitized Group Ration-Express (UGR-E). Both of these MREs use a Flameless Ration Heater (FRH) as the heat source for the hot meal. The temperature of a 250 gram individual MRE entrée can be raised by 100° F. in about 10 minutes using a 14 g FRH. Typically, the process of heating food consists of adding about 40 ml of water to the FRH by the military or other user, in order to activate the chemical reaction that produces the heat. Presently, the FRH consists of a magnesium, iron and salt mixture. The iron is used to activate the reaction of magnesium with water, whereas the salt prevents the formation of a magnesium oxide film on the magnesium metal surface. The reaction products are magnesium hydroxide and hydrogen. With the individual MRE, the liberation of up to 13 liters of hydrogen gas has not been a substantial safety problem.
The Unitized Group Ration-Express (UGR-E) is a complete meal in a box and can feed small groups of eighteen soldiers. Again, the food is heated by using a proportionally larger FRH that is activated by the addition or distribution of water. The problem associated with the release of hydrogen is significantly magnified with group meals. For a UGR-E weighing 28 pounds and requiring approximately 400 g of heater material, the amount of hydrogen released is typically 13.5 cubic feet or 380 liters. Thus, the concern is that generation of this large quantity of hydrogen in a confined space will exceed the Lower Explosive Limit of 4%.
Accordingly, there is a need for an improved system for the elimination, or at least minimization of hydrogen generation in magnesium/water based flameless heaters.
SUMMARY OF THE INVENTIONIt is therefore a principal object of the invention to eliminate or suppress the cogeneration of hydrogen in all types of magnesium-based FCHs, to prevent the release of hydrogen into the atmosphere and preventing potentially explosive situations by means of a novel process.
Thus, one principal aspect of the invention includes useful methods for generating energy for flameless heating, such as for foodstuffs, water, medical supplies, etc., especially in the case of outdoor applications for camping, emergency, military applications all without the cogeneration of hazardous hydrogen by the steps of:
(i) forming a reaction mixture including magnesium or magnesium-containing alloy, a hydrogen eliminator or suppressor and particulate carbon; and,
(ii) adding a metallic salt and water to the reaction mixture, the metallic salt includes a cation and an anion and the anion is selected from the group consisting of silicate, carbonate, bicarbonate, phosphate, borate, perborate, percarbonate, perphosphate, persulfate, nitrate, nitrite, ferrate, permanganate, and stannate and combinations thereof.
The metallic salt and water are added either sequentially or together and the reaction mixture, metallic salt and water in combination generate sufficient thermal energy for heating an article or substance while simultaneously eliminating or suppressing the generation of hydrogen. Thus, the metallic salt may be added to the reaction mixture prior to the addition of water, the water may be added to the reaction mixture prior to the addition of the metallic salt, the metallic salt and water may be added to the reaction mixture simultaneously or the metallic salt and water may form a solution which is in turn added to the reaction mixture.
This inventor discovered a new class of useful hydrogen suppressors or eliminators for flameless heaters.
Accordingly, it is still a further principal object of the invention to provide novel methods and compositions of matter for the flameless generation of thermal energy, including heater devices and meal, ready-to-eat packaged meals wherein the methods and compositions not only suppress or eliminate the cogeneration of potentially hazardous hydrogen, but surprisingly, were discovered to provide a substantially accelerated temperature rise for more prompt heating of the packaged meal compared to other state-of-the-art flameless chemical heaters.
Generally, for purposes of this invention the expression “hydrogen suppressor” as appearing in the specification and claims is intended to mean any metal-containing oxidizing agent that is suitable for at least minimizing, and more preferably, eliminating the cogeneration of hydrogen in the presence of magnesium or a magnesium-containing alloy. The metal of the metal-containing oxidizing agent, more specifically, is one having multiple valences, and includes as a preferred group, oxides of transition metals, such as manganese and/or oxides of ruthenium, and more particularly, manganese dioxide and ruthenium dioxide, to name but a few.
It should be understood, there are other representative examples of reactants in addition to oxides of manganese and ruthenium as hydrogen suppressors or eliminators, which when mixed with magnesium and reacted with water at least minimize, and more preferably totally suppress the cogeneration of hydrogen, while effectively generating the desired thermal energy. Generally, the useful hydrogen suppressors or eliminators are transition metal oxides that avoid the cogeneration of hydrogen in the reaction with magnesium or magnesium alloys. Representative examples include noble metals, such as platinum, iridium and rhodium. Other multivalent transition metal oxides include such members as iron, cobalt, nickel, silver, gold, tin, zirconium, hafnium, tantalum, lead, copper, and so on.
Useful magnesium-containing alloys for the above reaction mixture can also include at least one alloying element, such as iron, cobalt, nickel, zinc, aluminum and mixtures thereof.
The subject invention also contemplates optional additives in practicing the flameless heating methods disclosed herein comprising at least one member selected from hydrogen overvoltage suppressors, promoters, flowing agents and reaction activators.
The subject invention also contemplates the addition of a combination of metallic salts to the composition of step (i). For example, the metallic salt added to the composition of step (i) may include a plurality of unique metallic salts. Such compositions including a plurality of metallic salts are within the spirit and scope of the claimed invention.
As previously mentioned, it is still a further principal object of the invention to provide novel hydrogen suppressing or eliminating flameless, thermal energy generating chemical compositions. The compositions comprise reaction mixtures having at least: magnesium; a hydrogen suppressor or eliminator; particulate carbon; an alloying metal selected from the group consisting of: iron, cobalt, nickel, zinc, aluminum and mixtures thereof; a metallic salt including a cation and an anion, wherein the anion is selected from the group consisting of silicate, carbonate, bicarbonate, phosphate, borate, perborate, percarbonate, perphosphate, persulfate, nitrate, nitrite, ferrate, permanganate, and stannate and combinations thereof; and, water. Moreover, in some embodiments, the cation is selected from the group consisting of an alkaline metal and an alkali metal, while in other embodiments, the cation is selected from the group consisting of sodium, calcium, magnesium and potassium. Still yet further, the composition may comprise iron thereby providing greater control of the mass of the present invention composition needed to generate a desired amount of heat energy, while maintaining a desired level of hydrogen generation.
Generally, the reactants are present in proportional amounts sufficient to generate heat for promptly raising the temperature of substances, products or articles, such as water, medical supplies, consumable rations, and the like, to the desired temperature within a reasonable time period. As previously pointed out, it was surprisingly and unexpectedly discovered the novel hydrogen suppressor or eliminator compositions of the present invention provide a substantially accelerated temperature rise over known flameless heat generating compositions comprising magnesium and water. Moreover, it was also surprisingly and unexpectedly discovered that the introduction of a metallic salt of the present invention provides more desirable heater performance characteristics, i.e., rate of heating and amount of hydrogen generation.
As previously mentioned, the hydrogen suppressing or eliminating flameless heat generating compositions may have other optional reactants, such as a hydrogen overvoltage suppressors, reaction promoters, flowing agents and reaction activators.
In addition to magnesium metal, the hydrogen suppressing, flameless heat generating reaction mixtures may also be prepared from alloys of magnesium, prepared from alloying metals, such as iron, cobalt, nickel, zinc, aluminum and mixtures of the same, or may also be prepared with other metals such as iron. Such alloys are known among skilled artisans, and are commercially available through ordinary channels of commerce.
Besides magnesium, the flameless heat generating reaction mixtures, like the previously described methods, also comprise at least one hydrogen eliminator/suppressor, such as oxides of manganese and/or ruthenium, and more particularly, manganese dioxide and/or ruthenium dioxide in a sufficient amount to suppress the generation of hydrogen. This includes other transition metal oxides like those previously discussed in connection with the methods of the invention.
It is yet a further principal object of the invention to provide for heater devices, such as trays and pouches comprising the hydrogen suppressing, flameless, heat generating compositions, particularly for heating water, food rations, including medical supplies especially useful for camping and military applications. This is especially intended to include Meal, Ready-to-Eat military ration packaging comprising the above flameless heater devices.
It is still yet a further principal object of the invention to provide bags or pouches arranged to maximize the performance of the present invention hydrogen suppressing, flameless, heat generating compositions while maintaining the ability to transport such bags or pouches without undue settling of the present invention composition within the bag or pouch. It should be appreciated that undue settling detrimentally affects the performance of the present invention heater devices.
For a further understanding of the invention and its characterizing features reference should now be made to the accompanying drawings wherein:
The invention relates to novel methods and reaction mixtures/compositions for the generation of flameless heat mainly without the co-generation of potentially hazardous hydrogen previously associated with prior art methods and compositions. The methods of the invention employ at least one transition metal oxide powder, such as an oxide of manganese and/or ruthenium, for example, mixed with powdered magnesium or magnesium-containing alloy to generate flameless heat, free of, or with minimal cogeneration of hydrogen. The methods of the present invention can in part be demonstrated by the following representative reaction scheme set forth in Equation [2]:
Mg°+2MnO2+H2O→Mn2O3+Mg(OH)2+Δ [2]
It should be appreciated that thermodynamically, Equations [1] and [2] are sanctioned to proceed and generate the same amount of heat when the reactants are mixed in proportions dictated by the stoichiometry. Thus, the amount of heat generated by 1 gram of Mg via Equation [1] is the same as 5.37 grams of the reactants via Equation [2].
The reaction according to Equation [2] eliminates or suppresses hydrogen generation, or at least minimizes its cogeneration, while providing accelerated temperature rise over prior methods, i.e., more spontaneous heat generation than the known Mg+H2O reaction of Equation [1], as will be demonstrated by the methods below currently used in flameless chemical heaters or flameless ration heaters. It may be noted that the addition of CuCl2, NaNO3, and trichloroacetic acid to magnesium were believed to eliminate the hydrogen evolution reaction. However, NaNO3 and trichloroacetic acid are not effective in fully suppressing hydrogen generation, and CuCl2 in the MREs is not acceptable because of environmental and health considerations.
The novel chemical compositions of the present invention react and generate sufficient heat for promptly heating water, medical supplies, consumable rations, and the like, without simultaneously generating hydrogen, or in the alternative, without simultaneously generating unacceptable levels of hydrogen. Methods of the invention rely on a metallic element, e.g., magnesium or alloy thereof, a hydrogen suppressor or eliminator, a metallic salt and water, the latter of which acts as a reactant and a medium for the reaction. Generally, the hydrogen suppressor or eliminator is a transition metal oxide, and include inter-alia noble and non-noble metal oxides. Other useful representative oxides include PtO, IrO2, RhO2, Fe2O3, CO3O4, NiO, Ag2O, Au2O3, CuO, TiO2, ZrO2, HfO2, Ta2O5 and PbO2.
Optional additives for the hydrogen suppressing flameless heat generating chemical compositions and methods may include a hydrogen overvoltage suppressor, a promoter, flowing agent, activators, and the like.
The metallic element in the chemical composition that generates heat is magnesium or magnesium alloy containing from about 0.001% to about 10% iron, cobalt, nickel, zinc, aluminum, either singly or in combination with each other. A preferred composition is pure or substantially pure magnesium with small or trace amounts of other metals, e.g., <0.001% to about 0.1% of the alloying elements, iron, cobalt, nickel, zinc and aluminum. One preferred hydrogen suppressor in the chemical composition is MnO2 and RuO2. A preferred hydrogen suppressor may be either γ-MnO2 or β-MnO2, both known oxides, made either electrolytically or chemically by known methods, or from a naturally occurring ore that is treated. A most preferred hydrogen suppressor is γ-MnO2. The amount of MnO2 in the chemical composition is in ranges from about 1 to about 10 times the stoichiometric amount required for the Mg+MnO2 reaction with water, the preferred amount being 1-10 times the stoichiometry.
The hydrogen overvoltage suppressor in the chemical composition may be a metal sulfide, the metal preferably being Fe, Co, Ni, or a highly electrically conductive carbon, present in amounts ranging from about 0.001 to about 1%. The promoter in the chemical composition is preferably a carbon in particulate or powder form, present in an amount ranging from about 0.001 to about 20 percent-by-weight. The filler or flowing agent includes such representative members as silicon dioxide and calcium carbonate, and is present in an amount ranging from about 0.001 to about 10 percent-by-weight. They are effective in also promoting the reaction rate of the flameless heater reaction mixtures. Activators for the reaction mixtures include alkali metal halides, such as NaCl, magnesium halide salts, such as MgCl2, MgBr2, including Mg(ClO4)2, and so on. Additionally, activators for the reaction mixtures include thermally and electrically conducting, high surface area synthetic graphite and other conducting carbon materials. An example of a suitable synthetic graphite includes Asbury 4827, produced by Asbury Graphite Mills, Inc., of Asbury, N.J., while suitable conducting carbons include Asbury TC 307, also produced by Asbury Graphite Mills, Inc., KETJENBLACK® (such as EC600JD), produced by Akzo Nobel Polymer Chemicals LLC, of Chicago, Ill., BLACK PEARLS® 2000 or 1300, both produced by Cabot Corporation, Alpharetta, Ga. The amount of activator can vary in the range from about 0.001 to about 50%. One preferred activator is MgCl2, the other being electrically conductive carbon.
The reaction scheme set forth supra is an electrochemical corrosion reaction, the anodic reaction being the oxidation of Mg to form Mg2+ ions, the cathodic reaction being the reduction of MnO2 to Mn2O3 and the electron transfer processes proceeding on the surface of MnO2. It is for this reason that there is no need for a conducting electrolyte, such as a salt solution, to activate the reaction described supra. However, Mg is prone to form MgO and therefore, the reaction described supra does not proceed to completion unless an electrically conducting material such as carbon is added to the Mg/MnO2 mixture and blended thoroughly to establish/provide good electrical connectivity between MnO2 and Mg sites.
MgCl2 serves the same purpose but in a different way. Thermodynamic potential-pH diagrams for an Mg/water system at various temperatures show that the pH at which Mg2+ is in equilibrium with Mg(OH)2 shifts to lower pH values as the temperature increases. Thus, when MgCl2 is added, the temperature rises to as high as 120-150° C., and facilitates the solubility of Mg(OH)2 at pH=7, which is the pH of the water added to the reactants. Note that at pH=7 and at 25° C., the stable species is Mg2+, whereas at pH=7 and at 90° C., there is an equilibrium between these two species. This is the reason why addition of MgCl2 promotes the accessibility of the blocked MgO sites. The pH value at which Mg2+ is in equilibrium with Mg(OH)2 is strongly dependent on the activity of Mg2+ ions in the solution. It has been found that the higher the activity, the lower the pH value. We generally added MgCl2 corresponding to an activity of >>1.
It will be understood, activators, e.g., MgCl2 and carbon, may be introduced into the flameless heater compositions of the invention by various methods. For example, one method provides for blending/mixing an activator, such as MgCl2 and/or carbon in particulate form into the milled magnesium and hydrogen suppressor or eliminator when preparing the reaction mixture, before introducing the water reactant. Alternatively, an aqueous solution of the MgCl2, e.g., 5 to 7 M solution of the activator in the water reactant (45 to 60 wt % solution), can be prepared and introduced together as a salt solution into the milled Mg and hydrogen suppressor or eliminator reaction mixture. However, the former method of blending the activator with the milled Mg and hydrogen suppressor or eliminator is generally more preferred because it is more effective in suppressing hydrogen than the latter method. Moreover, the addition of the metallic salt of the present invention may occur in the same fashion as the introduction of the activators. For example, the metallic salt may be either milled with the Mg and hydrogen suppressor, or alternatively, may be used to form an aqueous solution which is later added to the Mg and hydrogen suppressor mixture. Still further, the metallic salt may be incorporated via either means as a pure metallic salt, or alternatively, a plurality of suitable metallic salts in combination.
Example 1In order to demonstrate the details of the invention based on a Mg/MnO2+H2O system according to the equation [2] above, the following experiment was conducted.
A 99.98% pure Mg metal sample of 500μ particle size from Superior Metal Powders, Franklin, Pa., was used in this test, and contained trace amounts, i.e., 85 ppm Al, 4 ppm Cu, 300 ppm Fe, 250 ppm Mn, 50 ppm Na, 150 ppm Si, 100 ppm Zn and 50 ppm Ca. In addition, a 30μ size γ-MnO2 powder from Tronox, LLC, Henderson, Nev., was used with a purity of 99%. The γ-MnO2 contained trace amounts, i.e., 8600 ppm S, 2600 ppm Ca, <100 ppm Mg, <1000 ppm Al, <100 ppm Si, <100 ppm Cl, 700 ppm K, <1000 ppm Cr and <100 ppm Sn.
The above Mg and γ-MnO2 powders were used to make a batch sample in a stoichiometric ratio according to equation [2], above. Approximately 500 g of the 300μ particle size MnO2 and 69.44 g of 50μ Mg were combined and placed in a mill. In this case the mill was a Vibrokinetic Energy (VKE) Mill, from Microgrinding System, Inc., Little Rock, Ark., model 624 (diameter=6″ and tube length=24″). This mill was operated with 36 stainless steel rods (6 with a diameter=1″, 30 with a diameter= 7/16″) with a length of 24″. The sample mixture was introduced into the mill via a 2″ diameter feed. All the screws and openings were tightened and secured prior to running the mill for 6 hours. At the end of the 6 hour milling period, the sample remained in the mill over night to cool. The sample was removed with a Nalgene scoop, transferred to a 600 ml stainless steel beaker and stored in a desiccator with calcium sulfate as the dehydrating agent.
Following
First, filter cloth 12 was cut into a 6″×8″ sheet. The filter cloth was then made hydrophilic. One of two procedures and surfactants may be used in making the porous filter cloth hydrophilic. One method employs a “dip and nip” technique. This method requires taking the porous hydrophobic cloth and dipping it into a 5% aqueous solution of surfactant. The excess surfactant is then squeezed off by passing the cloth through a pair of nip rollers. The second method provides for applying one or more dabs of a surfactant such as Pluronic-25R2 surfactant, from BASF Corp., Florham Park, N.J., on one or both sides of the cloth. Alternative procedures for making the filter cloth hydrophilic are discussed infra.
Hydrophilic porous filter cloth 12 was then fabricated into bag 10 by folding the treated 6″×8″ sheet in half. The bottom 4″ of side 14 and 6″ of side 16 were heat sealed to form the pocket or bag 10 with opening 22 on the top 4″ of side 18 left open to allow for filling before applying the final heat seal. The heat seals were made using a Uline 8″ impulse Sealer (H-163). 100 g of the milled and dried Mg/MnO2 powder 20 described supra was then placed in the Unilayer 270 polypropylene bag 10 and opening 22 on the top sealed closed. This sealed flameless ration heater reaction mixture bag 10 was then placed in green non-porous “poly” bag 24 (
60 ml of water 31 (
In order to compare the performance of the hydrogen suppressing, flameless heat generating composition prepared according to Example 1, a second sample of the known flameless heat generating composition comprising Mg and H2O only was prepared.
8 g of 500μ Mg/Fe, from Innotech Products, Inc., Cincinnati, Ohio as presently used in a U.S. Army ration heater, was prepared according to the recipe in U.S. Pat. No. 5,611,329. This sample was placed in a “non-woven” bag material from Innotech Product, Inc. The Innotech bag material was a roll configured into four, 1″ compartments distributed through the length of the roll. 6″ of this material was cut from the roll and the bottom was heat sealed with a Uline, 8″ impulse sealer (H-163). Each of the four compartments was filled with 2 g of the Mg/Fe and the ration heater was heat sealed closed (not shown).
The completed flameless ration heater was placed in a green polyethylene bag, from the U.S. Army, with a 250 g water pouch. After thirty seconds, 40 ml of an aqueous solution of 0.25 M sodium chloride was poured between the water pouch and the flameless ration heater. The top of the green bag was folded over and the green bag with its contents was placed in a “chipboard” box (not shown). For approximately 30 seconds, the box system was held horizontally with the ration heater at the bottom. Then, the system was set at a slight incline to prevent water loss, and allowed to react for 30 minutes. The temperature variation was recorded as a function of time and shown in
100 g of 500μ Mg/Fe, from Innotech Products, Inc., Cincinnati, Ohio, as presently used in a U.S. Army ration heater, was prepared according to the recipe set forth in U.S. Pat. No. 5,611,329. This sample was placed in an 8″×11″ bag made from the “non-woven” bag material from Innotech Product, Inc., that was configured into four, 2″ compartments distributed through the length of the roll. Each of the four compartments was filled with 25 g of 500μ Mg/Fe and the ration heater was heat sealed closed.
This completed ration heater was placed in a UGR-E heating tray, over which a 3500 g “water pouch” was placed. This assembly was placed in a card board box and then 330 ml of 1.5% NaCl solution was added. The card board box was then closed and the edges sealed with a tape. The temperature variation was recorded as a function of time over a 60 minute period, and shown in
In order to demonstrate a further embodiment of a chemical heater composition which includes a metal halide activator, a further experiment was performed with the reactants: Mg+MnO2+MgCl2 by means of the following protocol.
The milling procedure for the Mg/MnO2 mixture was the same as that stated in Example 1. 45 g of the milled Mg/MnO2 mixture was mixed with 15 g of 325 mesh MgCl2, from Sigma-Aldrich, Inc., St. Louis, Mo. This Mg/MnO2/MgCl2 mixture was placed in a dual layer bag consisting of two different filter cloth materials made of polyester fibers (Finon C305NW) and polypropylene fibers (Unilayer 270). Finon C305NW is made of polyester fibers with a thickness of 7 mils (0.1778 mm) and a weight of 50.9 g/m2, with an air permeability of 1,778 l/m2/sec and a Mullen Burst of 50 psi. This dual layer configuration is essential with Mg/MnO2/MgCl2 mixtures to provide thermal stability to the bag via the polyester fabric and the depth loading characteristic via the polypropylene, 6-ply, Unilayer. Both of the bag materials from Midwest Filtration were received in 8″×11″ sheets and cut into 6″×8″ sheets. To make these materials hydrophilic, the “dip and nip” process of Example 1 was employed. To configure the pouch, the Finon polyester material was placed aside the smooth surface of the Unilayer polypropylene and both are folded in half to make a 4″×6″ pouch with the polyester inside the Unilayer polypropylene (not shown). A Uline 8″ impulse Sealer (H-163) was used to heat seal the two materials together. The 6″ side, parallel to the fold and one of the 4″ sides were sealed prior to adding the reaction mixture. An additional seal, parallel to the 6″ side and down the center of the pouch was also added to make the pouch into two compartments. 30 g of the Mg/MnO2/MgCl2 mixture was added to each of the compartments. The pouch was heat sealed closed and placed in a green “polybag” with a 250 g water test pouch as a surrogate for a ration. 40 ml of water was added to the green bag on the same side as the ration heater. The top of the bag was folded over and the whole system was placed in a “chipboard” box. For approximately 30 seconds, the box was held horizontally with the ration heater under the water pouch. Then the pouch was set at a slight incline for thirty minutes, as in Example 1. The temperature variation was recorded as a function of time and shown in
The performance of the FRH composition of the Example 3 was also tested relative to the Example 2 with the results demonstrated by
As described above, bag 10 may be constructed in a variety of ways. As set forth in Example 1, bag 10 may be fabricated from porous filter cloth, such as Unilayer 270. In this example, the filter cloth is a 6-ply sonic bonded polypropylene laminate. Additionally, as set forth in Example 3, a dual layer bag consisting of two different filter cloth materials may be fabricated from polyester fibers, such as Finon C305NW, and polypropylene fibers, such as Unilayer 270. Furthermore, it has been found that bag 10 may also be fabricated from multiple layers, e.g., four to six layers, of polyester fibers, such as Finon C305NW. Still further, it has been found that bag 10 may also be fabricated from a white sonic-bond filter media containing six layers of 0.5 oz/yd2 SMS (spunbond/melt blown/spunbond) polypropylene, such as Uniloft 300S (UL300S) manufactured by MidWest Filtration Company. Uniloft 300S has a basis weight of 3.0 oz/yd2, a nominal thickness of 20 mils, a Frazier air permeability of 29 cfm/ft2 and a Mullen Burst of 80 psi. Similar to the previously described fabrications, the multiple layers can be sonically bonded and made hydrophilic by the “dip and nip” or dabbing process of Example 1. Each of these fabrications provides varying levels of thermal stability and depth loading capability so that fine particles are prevented from blocking the pores and preventing entry of water from outside to the reactants inside the bag material. In the dual layer configuration, the polyester fiber provides thermal stability to the bag while the polypropylene provides the depth loading characteristic. Moreover, porous filter cloth fabricated from polymeric fibers allows the transmission of water, and the release of gases while precluding the blockage of pores by the solid reactants and/or products owing to its depth loading characteristics.
It has been found that when Unilayer-based ration heater pouches are used in combination with the present invention, a very small seepage of carbon and/or MnO2 fines occurs before and after the reaction. Such leakage leads to an unappealing aesthetic appearance of the heater and stains the hands of the person handling the heater. It has been found that these issues may be eliminated by employing a dual composite fabric consisting of an inner layer of 1.5 oz, Unipro 260-SMS (spunbond/meltblown/spunbond filter media containing 100% polypropylene), and an outer layer of Unilayer 135 which is a 3-ply bonded polypropylene fiber cloth. The temperature-time profiles of the present invention in combination with the Unilayer 270 and the Unilayer 135/Unipro-SMS arrangements described above are shown in
An ideal material for housing the heater chemicals should exhibit good thermal stability, permits facile activation fluid entry into the bag and steam release from the bag, and has more than enough depth loading capability to confine the MnO2 and C fines (from the reactants mixture). The last attribute prevents blockage of pores which restrict the entry of the activation fluid into the reactants inside the housing material. The leakage of fines does not affect the heat transfer characteristics, but displays dirtiness and stains the hands of the person touching the heater.
Hydrogen GenerationThe amount of hydrogen generated by the FRH reaction mixtures of Examples 1, 3 and 20 was measured on a comparative basis with the FRH reaction mixture of the prior art (Example 2) by collecting off-gases and analyzing for hydrogen content by means of gas chromatography. The results are provided in Table 1 below:
The following example demonstrates the method for removing residual moisture (3.3% H2O) from electrolytic manganese dioxide to near zero level for improving useful shelf-life of the reaction mixture.
In performing the process, 500 g of MnO2 is placed in an oven set to 400° C. for 2 hours and then heated at 110° C. for 24 hours. This MnO2 sample is mixed with Mg powder and milled following the procedure disclosed in Example 1. The remaining steps of the process correspond to those disclosed in Example 1, containing Mg+MnO2.
Example 5The following example demonstrates the method for removing residual moisture (3.3% H2O) from electrolytic MnO2 to near zero level in preparing a reaction mixture comprising Mg and MnO2 (water-free), plus MgCl2 activator for improving useful shelf-life of the reaction mixture.
In performing the process, 500 g of MnO2 is placed in an oven set to 400° C. for 2 hours and then heated at 110° C. for 24 hours. This MnO2 sample is then mixed with Mg powder and milled following the procedure in Example 1. The remaining steps of the process are the same as those disclosed in Example 3, containing Mg+MnO2+MgCl2.
Example 6The following example was performed to demonstrate the procedure for preparing a homogeneous reaction mixture that maximizes electrical contact of all the MnO2 with Mg in the reaction mixture.
In performing the process, 300 g of 60μ γ-MnO2, from Tronox, LLC, was mixed with the Mg powder and milled according to the procedure in Example 1. The remaining process steps corresponded to those disclosed in Example 1.
Example 7The following example was performed to demonstrate the procedure employed in preparing a reaction mixture comprising Mg+MgCl2 with small particle size (60μ) MnO2.
In performing the process, 300 g of 60μ γ-MnO2, from Tronox, LLC, was mixed with Mg powder and milled following the procedure in Example 3. The remaining steps are the same as that described in Example 3.
Example 8The following example demonstrates preparation of a reaction mixture according to present invention comprising magnesium with manganese dioxide except with very small average particle size of 0.8μ.
In performing the process, 300 g of 0.8μ MnO2 available from Sigma Aldrich can be mixed with Mg powder and milled following the procedure in Example 1, above. The remaining steps of the process can follow those disclosed in best mode Example 1.
Example 9The following example also demonstrates preparation of a flameless heater reaction mixture according to the present invention, but with ultra fine particulates of MnO2 (0.8μ γ-MnO2) hydrogen suppressant, plus MgCl2 activator.
In preparing the reaction mixture, 300 g of 0.8μ MnO2, from Sigma Aldrich, is mixed with Mg powder and milled following the procedure of Example 3, above. The remaining steps for preparation of the reaction mixture correspond to those also described in best mode Example 3.
Example 10The following best mode example also demonstrates a further aspect of the invention except the improved flameless heater composition is prepared with two (2) times the stoichiometric amount of manganese dioxide.
In preparing the composition, 600 g of MnO2 from Tronox, LLC, is mixed with Mg particles and milled as described in working Example 1, supra. The remaining steps correspond to those also described in Example 1.
Example 11The following best mode example also demonstrates a further aspect of the invention for preparing flameless heater compositions prepared with two (2) times the stoichiometric amount of manganese dioxide in combination with magnesium chloride activator.
In preparing the reaction mixture/composition, 600 g of MnO2 from Tronox, LLC, is mixed with the Mg particles and milled as described in Example 1. The remaining steps correspond to those also described in Example 3.
Example 12The following example demonstrates a further alternative embodiment of the invention comprising Mg+MnO2+1% Zn° metal, wherein an additional alloying metal, i.e., zinc, is introduced into the composition to form surface alloyed magnesium metal particulates during the milling step.
In preparing the reaction mixture/composition, 500 g of 300μ MnO2 (same as the MnO2 disclosed in Example 1, procedure for Mg+MnO2), 69.44 g of 500μ Mg (same as the Mg° described in Example 1 procedure for Mg+MnO2) and 5 g Zn° particles, from Sigma Aldrich with a purity of 99.99%, were combined, placed in the VKE mill and milled for 6 hours. The remaining procedure is the same as that described in Example 1, procedure for Mg°±MnO2.
This inventor found that the milling process is effective for: (i) mixing the ingredients to form a homogeneous reactive composition; (ii) assures desired intimate electrical contact between the ingredients, i.e., Mg+MnO2+Zn° metal; (iii) is an effective means of forming surfaces alloyed with added metals, such as zinc, cobalt, nickel, iron, aluminum and mixtures of the same; and, (iv) also promotes better surface adhesion of the MnO2 to the magnesium or alloyed magnesium.
Example 13This example discloses a flameless heating composition of the invention comprising a combination of both oxides of manganese and ruthenium in a 30% RuO2, 70% MnO2 proportional range.
In preparing the composition, 48.61 g of 500μ Mg (same as disclosed in Example 1), 350 g of 300μ particle size of MnO2 (same as the MnO2 disclosed in Example 1 procedure for Mg+MnO2) and 150 g RuO2, 99.99% pure from Sigma Aldrich (12036-10-1), were combined, placed in the VKE mill and milled for 6 hours. The remaining procedure is the same as that described in Example 1.
Example 14This example discloses a flameless heating composition of the invention similar to Example 13, except the combination of oxides of manganese and ruthenium have been reversed wherein RuO2 is present in 70% range, and the MnO2 is present in a proportional range of 30%.
In preparing the composition, 20.83 g of 500μ Mg (same Mg disclosed in Example 1 and the procedure for milling Mg+MnO2), 150 g of 300μ of MnO2 (same MnO2 disclosed in Example 1 and milling procedure for Mg+MnO2 in Example 1) Mg, and 350 g RuO2 (same as the RuO2 described in Example 13, Mg+30% RuO2+70% MnO2), were combined, placed in the VKE mill and milled for 6 hours. The remaining procedure is the same as that disclosed in Example 1.
Example 15This best mode example demonstrates a flameless heating composition of the invention comprising RuO2 as the sole hydrogen suppressing agent.
In preparing the composition, 45.50 g of 500μ Mg (same as the Mg disclosed in Example 1) and 500 g RuO2, (same as the RuO2 disclosed in Example 13), were combined, placed in the VKE mill and milled for 6 hours. The remaining procedure is the same as that described in Example 1.
Example 16This example demonstrates a further embodiment of the invention wherein the flameless heater mixture includes in addition to Mg and MnO2, 10% by-weight carbon to promote the rate of reaction and the generation of heat.
In preparing the reaction mixture/composition, 69.44 g of 500μ Mg (Same type of Mg disclosed in Example 1), 500 g MnO2 (same as the MnO2 disclosed in Example 1) and 50 g carbon from Cabot Corp., Boston, Mass., available under the trademark Vulcan XC72R, Lot: GP-3860 were combined and placed in the VKE mill and milled for 6 hours. The remaining procedure for this composition follows the same protocols as disclosed in Example 1, above.
Example 17A further embodiment of the invention is presented wherein 1% Na2S is introduced into the flameless heater composition Mg+MnO2 composition as a hydrogen overvoltage suppressor. A metal sulfide may be incorporated into the composition as a fail safe in the event hydrogen is unexpectedly generated.
The flameless heater composition was prepared by mixing 69.44 g of 500μ Mg (same Mg disclosed in Example 1), 500 g of MnO2 (same MnO2 disclosed in Example 1) and 5 g Na2S (from Sigma Aldrich), and placing the mixture in the VKE mill and milling for 6 hours. The remaining procedure corresponds to that described in Example 1, above.
Example 18Another embodiment of the flameless heater compositions of the invention includes the introduction of a filler/flowing agent, such as 2% SiO2 to the magnesium/manganese dioxide.
This embodiment may be prepared by combining 69.44 g of 500μ Mg (the same Mg disclosed in Example 1) with 500 g MnO2 (the same MnO2 disclosed in Example 1) and 10 g of 20μ SiO2 (from Sigma Aldrich, purity=99.5%) and placing the mixture in the VKE mill and milling for 6 hours. The remaining procedure for preparing corresponds to that disclosed in Example 1.
Example 19A similar flameless heater composition to that of Example 18 may be prepared using 2% CaCO3 filler/flowing agent with the magnesium and manganese dioxide.
The reaction mixture/composition may be prepared by combining 69.44 g of 500μ Mg (same Mg as disclosed in Example 1), 500 g MnO2 (same MnO2 as disclosed in Example 1) and 10 g of 20n CaCO3 (from Sigma Aldrich, purity=99.0%), and placing the mixture in the VKE mill and milling for 6 hours. The remaining procedure corresponds to that described in Example 1.
Example 20A 99.98% pure magnesium powder of 200-300μ particle size from Superior Metal Powders and containing 60 ppm Al, 50 ppm Cu, 300 ppm Fe, 700 ppm Mn, 50 ppm Si, 50 ppm Zn and 80 ppm Sn was used in this test. The 70-80μ γ-MnO2, from Tronox, LLC, with a purity of 99% and contained 1.2% SO42−, 2600 ppm Na, 190 ppm Al, 310 ppm C, 35 ppm Fe and 400 ppm K. These two materials were used to make a batch sample, in a stoichiometric ratio according to Equation [1] above, along with 5% Asbury 4827 carbon, a synthetic graphite of <20-<30μ particle size, containing 1440 ppm Al, 865 ppm Ca, 2150 ppm Fe, 300 ppm Mg, 200 ppm Na and 2900 ppm Si.
Approximately 1100 g of a mixture containing 919.2 g MnO2, 52.2 g C and 130 g Mg was weighed and placed in the Vibrokinetic Energy (VKE) Mill, from Microgrinding System, Inc., model 624 (diameter=6″ and tube length=24″). This mill is run with 36 stainless steel rods (6 with a diameter=1″, 30 with a diameter= 7/16″) with a length of 24″ as a stainless steel rod. The sample mixture is loaded into the mill via the 2″ diameter feed. All screws and openings are tightened and secured prior to running the mill for 1.5 hours. At the end of 1.5 hours, the sample is left in the mill for 20 minutes to cool. The sample is removed with a Nalgene scoop, transferred to a 1000 ml stainless steel beaker and stored in a desiccator with calcium sulfate as the dehydrating agent.
A Unilayer 270 bag material from Midwest Filtration is used to contain the milled Mg/MnO2 mixture. First, the bag material is cut into a 16.5″×11″ sheet and folded in half to make a 8.25″×11″ bag. Prior to adding the sample, one of the 8.25″ sides and the 11″ side is heat sealed to form a pocket. The task is done with a Uline, 8″, Impulse Sealer (H-163). 450 g of the milled Mg/MnO2 mixture is placed in the Unilayer Pocket and sealed closed. This completed ration heater is placed in a UGR-E tray, over which the 3500 g “water pouch” is placed. This assembly is placed in a card board box and then 350 ml of water is added. The card board box is then closed and the edges sealed with a tape. The temperature variation was recorded as a function of time over a 60 minute period, and is presented in
The reaction set forth in Equation [2] above suppresses hydrogen; however, it does not proceed to provide as much heat as the composition set forth in the instant invention. See for example, the results labeled 64 on
As described above, reactions of Mg+MnO2 with water can proceed via either Equation [1] and/or Equation [2] to provide heat. The reaction which dominates the generation of heat can be determined by measuring the amount of hydrogen generated during the course of the reaction using the setup shown in
It has been found, according to the data set forth in Table 2, that the reaction mixture which includes Mg+MnO2 does proceed as dictated by thermodynamics, but not at a rate that is needed to heat rations with a comparable weight of Mg. Therefore, the temperature has not reached a desirable value, e.g., 60° C. However, even under these conditions, a reaction according to Equation [1] is occurring, as evidenced by the amount of H2 generated. It has been further found that when carbon is included in the reaction mixture, i.e., Mg+MnO2+C, heat is produced as a result of the reactions set forth in both Equations [1] and [2]. This is evidenced by the amount of H2 produced. The reaction of Equation [1] is a parallel reaction occurring during the course of the reaction of Equation [2]. It is believed that the reaction of Equation [1] can be suppressed by: a) blocking the Mg reaction sites thereby preventing the reaction of Mg with water from the bulk; and/or, b) consuming the hydrogen as it is formed. The foregoing means for suppressing the reaction of Equation [1] are discussed here below.
The Mg reaction sites can be blocked by forming insoluble Mg species on the Mg sites as the reaction of Mg with water is initiated. The individual steps involved in the reaction of Equation [1] are as follows:
Mg→Mg2++2e [3]
2H2O+2e→H2+2OH− [4]
The insoluble species of Mg include but are not limited to magnesium silicate, magnesium bicarbonate, magnesium phosphate, magnesium borate, magnesium perborate, magnesium percarbonate, magnesium perphosphate and magnesium persulfate. Thus, when sodium salts of anions such as silicate, carbonate, bicarbonate, phosphate, borate, perborate, percarbonate, perphosphate and persulfate (individually or in combination) are added to the Mg+MnO2+C mixtures, these anions combine with Mg2+ formed via Equation [3] to form insoluble Mg compounds on Mg reaction sites. As a result, the reaction of Equation [3] is pushed in the reverse direction, which in turn suppresses the reaction of Equation [4]. Since the reaction of Equation [1] is suppressed, the reaction of Equation [2] proceeds without hindrance, since the reaction of Equation [2] is a surface reaction. It should be noted that Equation [2] is an electrochemical corrosion reaction wherein the anodic reaction is the oxidation of Mg to form Mg2′ ions, the cathodic reaction is the reduction of MnO2 to Mn2O3 and the electron transfer processes proceed on the surface of MnO2. It should be emphasized that alkali and alkaline earth salts with anions such as chloride, bromide, fluoride, hydroxide, acetate, citrate, etc., will not suppress the hydrogen evolution reaction because they do not form insoluble films of Mg on the Mg surfaces. The foregoing sodium salts may be added to the present invention composition as an activating solution/fluid, or alternatively, the salts may be added to the composition as a dry component, wherein the salts dissolve upon the introduction of water to the composition. Moreover, the sodium salts may be added individually or as a combination of a plurality of salts.
Example 21A 99.98% pure magnesium powder of 200-300μ particle size from Superior Metal Powders and containing 60 ppm Al, 50 ppm Cu, 300 ppm Fe, 700 ppm Mn, 50 ppm Si, 50 ppm Zn and 80 ppm Sn was used in this example. The 70-80μ γ-MnO2 was from Tronox, LLC with a purity of 99% and contained 1.2% SO42−, 2600 ppm Na, 190 ppm Al, 310 ppm C, 35 ppm Fe and 400 ppm K. These two materials were used to make a batch sample, in a stoichiometric ratio according to Equation [1] along with 5% Asbury 4827 carbon, a synthetic graphite of <20-<30μ particle size, containing 1440 ppm Al, 865 ppm Ca, 2150 ppm Fe, 2900 ppm Si, 300 ppm Mg, 200 ppm Na and 2900 ppm Si.
Approximately 1100 g of the mixture containing 919.2 g MnO2, 52.2 g C, 130 g Mg was weighed and placed in the Vibrokinetic Energy (VKE) Mill, from Microgrinding System, Inc., Model 624 (diameter=6″ and tube length=24″). This mill ran using 36 stainless steel rods (6 with a diameter=1″, 30 with a diameter= 7/16″) with a length of 24″ as a stainless steel rod. The sample mixture was loaded into the mill via the 2″ diameter feed. All the screws and openings were tightened and secured prior to running the mill for 1.5 hours. At the end of 1.5 hours, the sample was left in the mill for 20 minutes to cool. The sample was removed with a Nalgene scoop, transferred to a 1000 ml stainless steel beaker and stored in a desiccator with calcium sulfate as the dehydrating agent.
A composite Unilayer 135/Unipro-SMS bag material from Midwest filtration was used to contain the milled Mg/MnO2/C mixture. First, the bag material was cut into a 16.5″×11″ sheet and folded in half to make a 8.25″×11″ bag. Prior to adding the sample, one of the 8.25″ sides and the 11″ side is heat sealed to form a pocket. The task was done with a Uline 8″ impulse Sealer (Model H-163). 450 g of the milled Mg/MnO2/C was placed in the Unilayer Pocket and sealed closed. This completed ration heater was placed in a UGR-E tray, over which a 3500 g “water pouch” was placed. This assembly was placed in a card board box and then 350 ml of 2.3% sodium silicate water was added. The card board box was then closed and the edges sealed with a tape. The temperature variation was recorded as a function of time over a 60 minute period, and presented in
An analysis of the gases produced, following the methodology described earlier, showed the percent hydrogen evolved compared to that expected if all the Mg has directly reacted with H2O to be ˜10%. This translates to approximately a 95% reduction in the amount of hydrogen generated when compared to a 110 g Mg/Fe heater that is presently used in UGR-E heaters.
Moreover, the hydrogen from the foregoing reactions can be consumed as it is formed. An alternate approach to suppress hydrogen generation is to react it as it is formed by oxidizing it to form protons as:
H2+2e→2H+ [5]
This scheme requires the presence of species that can be reduced. The reducible species are cations such as Cu2+, Ni2+ or anions such as nitrate, nitrite, ferrate, permanganate, and stannate. Cu2+, Ni2+ will be reduced to metallic Cu or Ni, which are carcinogenic and cannot come in contact with food products. The reducible species with perborate and percarbonate additions is H2O2 formed by the hydrolysis of these species. Tests have shown that nitrate and nitrite completely suppress H2 generation, but the reduced product in both cases is ammonia which smells and hence is not acceptable with food products. Permanganate and ferrate are reduced to MnO2 and Fe3+, respectively. These species are colored and hence stain the bag material and the bottom of the food tray. While these suppressants can be used to prevent hydrogen evolution, they are not preferred because of aesthetic aspects, especially with foods and food products.
Example 22This example comprises a comparison of a variety of compositions including the instant invention and several known compositions. The first composition includes: 4 g of a Mg/Fe mixture, 40.25 g of CuCl2 (which is equivalent to 51 g of CuCl2.2H2O), 7.7 g of Citric acid and 34.2 g of sodium citrate which equals 86.15 g of total composition. This composition is Example 1 from U.S. Pat. No. 5,517,981 (hereinafter Taub). The second, third and fourth compositions each includes: 1.56 g of Mg, 11.18 g of MnO2 and 2.25 g of carbon.
The first composition was activated with 11 mL of water, the second composition was activated with 11 mL of water having 1.5% NaCl, the third composition was activated with 11 mL of water and the fourth composition was activated with 11 mL of water having 2.3% sodium silicate.
It should be appreciated that the reaction of Taub provides heat according to the reaction of Equation [6].
Mg+CuCl2→MgCl2+Cu [6]
The reaction of Equation [6] has a heat of reaction of 101 kcal/mole verses 85.88 kcal/mole for the reaction of Equation [1]. Moreover, the Taub reaction produces metallic Cu fines which block the cloth bag which houses the reaction mixture thereby preventing steam from getting out of the bag and which in turn heat the water pouch. As the water pouch is heavy, i.e., weighing approximately 3.5 kg, the steam was prevented from escaping to heat the water. Once the water pouch was removed, the bag expanded as the steam was not able to get out. Furthermore, the Taub composition developed blackish green color as the reaction proceeded making the heater bag appear undesirable. Lastly, the Taub composition results in Cu which is a known carcinogenic material and hence not permitted near food.
Lastly, it should be noted that the nature of the wetting agent employed to impart hydrophilicity to a given polymeric filter media and the manner in which it is applied impacts the temperature-time profile and the fines retention characteristics of the composite bag materials for housing the heater chemicals. Pluronic 25R2, a BASF product, which is a polyoxypropylene-polyoxypolyethylene block copolymer is generally used to wet polyester media. Eccowet D-75B, a product of Eastern Color & Chemical Company, which is a sodium sulfo-succinate solution in propylene glycol is used for polypropylene based media. It has been found that a proper wetting agent should be used for a given polymeric material, as otherwise, the heat generation profiles will be significantly altered.
Tests have also shown that the manner by which the wetting agents are applied to a given material makes a difference in the temperature profiles and the appearance of the heater bag after use. Pluronic is applied by lightly dabbing it on the bag with a brush or adding measured number of drops in select locations on the heater bag, whereas Eccowet is impregnated on the cloth by soaking it in a 1-5% solution of the wetting agent, squeezing the excess solution and drying it at 90-100° C. The procedure used for Eccowet is not applicable with Pluronic, since this leads to lowered temperature profiles and unacceptable seepage of black fines.
Compositions Including IronAs described supra, the present invention composition may include iron. For example, iron may be compounded with the magnesium to form alloyed magnesium. It has been found that forming an intermediate blend of a present invention composition that includes additional iron provides added control over some desired characteristics of the composition, e.g., material weight which in turn affects material cost. In other words, the overall material mass may be reduced thereby reducing the material cost; however, this reduction in material mass must also be balanced against the percentage of hydrogen generated during the reaction in order to avoid unacceptable or unsafe levels of hydrogen gas for a given space. Thus, the ratio of magnesium to iron must be selected such that the amount of hydrogen released does not cause the level of hydrogen in a given space to reach a flammable level.
The reaction of Mg/MnO2/C/Na2SiO3 with solutions of Na2CO3 promotes the reaction in accordance with Equation [2] above, whereas activation by NaCl solutions promotes the reaction in accordance with Equation [1] above, without interfering with the reaction of Equation [2]. To minimize material mass and cost without jeopardizing heat generation, iron is milled with Mg/MnO2/C/Na2SiO3/Na2CO3 and the composition is activated with NaCl solutions. By controlling the amount of iron added, the composition mass and the amount of hydrogen generated can be controlled, as shown in
Powder compositions have a tendency to shift or settle during shipping or periods of storage, resulting in non-uniform distribution within the bags. It has been found that the bags used to hold the compositions must be configured to minimize such changes as the non-uniform distribution will affect the thermal performance of the heater. Additionally, the configuration of the bag, such as the pocket configurations described infra, affects how the composition performs, e.g., how much heat energy is generated, as the reaction is dependent on such factors as the extent of activating solution reaching the composition components. Several embodiments of bag configurations are disclosed herein which assist with maintaining the present invention composition in a particular location, while promoting the generation of heat energy. It should be appreciated that some bags, e.g., small bags, are left as a single pocket, as depicted by bag 200 in
An embodiment of a present invention bag configuration includes the introduction of an x-frame formed from a fluted and ribbed material (See
A variety of other configurations are also possible and may be formed using the method employing the fluted and ribbed material described above, or alternatively, formed using a heat seal or adhesive bond. Such configurations are depicted in
The following example is used in comparative testing the results of which is set forth herebelow.
This composition is prepared according to the following procedure. 114.74 g of Mg from ESM, Inc., 820.26 g of MnO2 (AB grade) from Tronox, LLC, 157.30 g of Carbon (Grade 4827) from Ashbury Graphite Mills, Inc., and 7.70 g of Sodium Silicate (Grade S-25, anhydrous) from OxyChem were weighed for a total of 1.1 kg into a 2 liter Nalgene container. The mixture was shaken to allow mixing of the individual components, and then placed into a VKE-626 mill, which was then operated for 90 minutes, turned off, and allowed to cool for 30 minutes. The composition was removed from the mill by removing the mill end cap, taking out the mixing rods, and then scooping out the material into an electrically grounded, 3 liter stainless steel container.
This composition may be activated with 330 ml of a 1.5% sodium carbonate solution, which generated approximately 2-3 cubic feet of H2 when activating a 450 g UGR-E heater unit. It should be appreciated that the foregoing composition may also be activated with a variety of alternate solutions, as described herebelow.
Example 24The following example is used in comparative testing the results of which is set forth herebelow.
This composition is prepared according to the following procedure. 391.82 g of Mg from ESM, Inc., 610.61 g of MnO2 (AB grade) from Tronox, LLC, 51.15 g of Carbon (Grade 4827) from Ashbury Graphite Mills, Inc., 5.17 g of Sodium Silicate (Grade S-25, anhydrous) from OxyChem, and 8.03 g of Fe powder (99.9% pure, 325 mesh) from Reade Advanced Materials were weighed for a total of 1.1 kg into a 2 liter Nalgene container. The mixture was shaken to allow mixing of the individual components, and then placed into a VKE-626 mill, which was then operated for 90 minutes, turned off, and allowed to cool for 30 minutes. The composition was removed from the mill by removing the mill end cap, taking out the mixing rods, and then scooping out the material into an electrically grounded, 3 liter stainless steel container.
This composition may be activated with 335 ml of a 1.5% sodium chloride solution, which generated approximately 6 cubic feet of H2 when activating a 170 g UGR-E heater unit. It should be appreciated that the foregoing composition may also be activated with a variety of alternate solutions, as described herebelow.
Several different variations of heater compositions of Examples 23 and 24 were used in the testing of the thermal performance of the various compartmentalizations. Single compartment bag 300, having 450 g of the heater composition of Example 23 activated with 330 ml of an NaCl solution, is shown as line 302 in
Compartmentalizing by heat sealing the bags provides rigidity to the bags. However, performance test data, as shown in
Framed compartments formed in accordance with the method described above and using fluted and ribbed material provide differences in performance for the following reasons. The adhesive used to bond the frame provided a bond with a high peel adhesion at ambient temperatures, but became weak as the temperature increased to 40-50° C. A consequence of this temperature dependent peel adhesion behavior was that while there was a seal restricting the movement of the chemicals at room temperature, it was no longer present as the heater reaction proceeded. As a result, the temperature profiles were not as adversely affected as in the presence of a heat seal, which promoted the initial heating rates but lowered the final temperatures. In short, the frame formed from a fluted and ribbed material provides the necessary compartmentalization for shipping and storage, while such compartmentalization is removed upon use due to the breakdown of the adhesion. Furthermore, such a frame, e.g., frame 400, is formed from at least two discreet pieces of fluted and ribbed material, e.g., strips 402. Strips 402 include fluting 404 and ribs 406. Frame 400 is formed by passing a first strip 402 through fluting 404 of a second strip 402. Depending on the desired angle α and angle β, the thickness of each strip 402 may be cut such that rotation within fluting 404 permits such angles α and β. Angles α and β may be, for example, 77° and 103°, respectively. It should be appreciated that fluting 404 permits the passage of the activating solution. Thus, frame 400 substantially maintains the present invention composition within the compartments, while permitting the activating solution to pass freely throughout the entire heater unit. Moreover, for heater bags containing larger quantities of the present invention heater composition, e.g., UGR-E heater bags having 450 g of a heater composition, the frame structure outperforms the heat sealed
Vacuum sealed bags were sturdy, but lost rigidity when the vacuum was released.
As described above, the present invention heater units may be placed within a tray during use, such as heater unit 450 placed within tray 452 as shown in
An six compartment bag having 165 g of a 35.35% Mg/1.45% Fe/55.1% MnO2/4.62% C/0.475% Na2SiO3/3% Na2CO3 heater composition activated with a 330 ml of 1.5% solution of NaCl solution, is shown as lines 500, 502, 504 and 506 in
The presence of the aluminum foil lid stock slightly affected the performance of the heater units. Additionally, the heater composition, the nature of the bag material and the wetting agent affect the temperature profiles, while negative effects have been found to be mitigated by using a different lid stock material used to enclose the heater unit.
As described supra, the bag material must be made hydrophilic in order to permit the in flow of activating fluid and the out flow of steam thereby promoting the chemical reactions described above. As further described above, the bag material may be made hydrophilic by applying one or more drops of a hydrophilizing solution to one or both outer surfaces of a present invention heater bag. It should be appreciated that “a hydrophilizing solution” as used herein is intended to mean a solution that is applied to the bag material in order to rendered that portion of the bag material hydrophilic. It is believed that the application of the hydrophilizing solution via drops leads to greater consistency in performance due to the inconsistencies inherent during dabbing or brushing. It has been found that the type wetting agent and the manner of its application to the bag material influences the performance and the cleanliness of the heater unit. It should be appreciated that cleanliness is intended to mean the aesthetic appearance of the heater unit, before, during and after its use, as well as whether composition material or reaction products are permitted to escape the heater unit.
The embodiments of hydrophilizing solutions depicted in
Furthermore, the effectiveness of various types of hydrophilizing solutions was also tested. Using single compartment heater bags formed from UL300S material, filled with 450 g of Mg/MnO2/C and activated with 315 ml of 2.0% Na2SiO3, the performance of various hydrophilizing solutions is shown in
While the invention has been described in conjunction with various embodiments, they are illustrative only. Accordingly, many alternatives, modifications and variations will be apparent to persons skilled in the art in light of the foregoing detailed description, and it is therefore intended to embrace all such alternatives and variations as to fall within the spirit and broad scope of the appended claims.
Claims
1. A hydrogen suppressing, flameless, heat generating chemical composition comprising:
- magnesium;
- a hydrogen suppressor or eliminator;
- particulate carbon;
- an alloying metal selected from the group consisting of: iron, cobalt, nickel, zinc, aluminum and mixtures thereof;
- a metallic salt comprising a cation and an anion, wherein said anion is selected from the group consisting of silicate, carbonate, bicarbonate, phosphate, borate, perborate, percarbonate, perphosphate, persulfate, nitrate, nitrite, ferrate, permanganate, and stannate and combinations thereof; and,
- water, wherein said magnesium or magnesium-containing alloy, hydrogen suppressor or eliminator, particulate carbon, alloying metal, metallic salt and water are each present in a proportional amount to generate sufficient heat to heat water, medical supplies and/or consumable rations.
2. The hydrogen suppressing, flameless, heat generating chemical composition according to claim 1, further comprising at least one member selected from the group consisting of a hydrogen overvoltage suppressor, a flowing agent and a reaction activator.
3. The hydrogen suppressing, flameless, heat generating composition according to claim 1, wherein the alloying metal is present in an amount from about 0.001 to about 10 percent by-weight
4. The hydrogen suppressing, flameless, heat generating chemical composition according to claim 1, wherein said hydrogen suppressor comprises oxides of manganese and/or ruthenium.
5. The hydrogen suppressing, flameless, heat generating chemical composition according to claim 4, wherein said oxide of manganese is γ-MnO2 or β-MnO2.
6. The hydrogen suppressing, flameless, heat generating chemical composition according to claim 4, wherein the oxide of manganese is present in an amount ranging from 0.5 to about 10 times the stoichiometric amount required for the magnesium and the oxide of manganese reaction with water to occur.
7. The hydrogen suppressing, flameless, heat generating chemical composition according to claim 2, wherein the hydrogen overvoltage suppressor is a metal sulfide and the activator is an inorganic salt.
8. The hydrogen suppressing, flameless, heat generating composition according to claim 2, wherein the reaction activator is selected from the group consisting of: alkali metal halides, magnesium halide salts, thermally and electrically conducting, high surface area synthetic graphite, conducting carbon, conducting graphite, carbon and mixtures thereof, and the reaction activator is present in an amount from about 0.001 to about 50 percent by-weight.
9. The hydrogen suppressing, flameless, heat generating composition according to claim 8, wherein the reaction activator is mixed with milled magnesium-manganese dioxide mixtures prior to activating the heater reaction with water.
10. The hydrogen suppressing, flameless, heat generating composition according to claim 8, wherein the reaction activator is the synthetic graphite, the synthetic graphite is Asbury 4827.
11. The hydrogen suppressing, flameless, heat generating composition according to claim 8, wherein the reaction activator is the conducting carbon, the conducting carbon is Ketjenblack, Black Pearls® 2000, Black Pearls® 1300 or Asbury TC 307.
12. The hydrogen suppressing, flameless, heat generating composition according to claim 1, wherein said cation is selected from the group consisting of an alkaline metal and an alkali metal.
13. The hydrogen suppressing, flameless, heat generating composition according to claim 1, wherein said cation is selected from the group consisting of sodium, calcium, magnesium and potassium.
14. The hydrogen suppressing, flameless, heat generating composition according to claim 1, wherein the metallic salt and water are added either sequentially or together.
15. A heater device comprising the hydrogen suppressing, flameless, heat generating chemical composition according to claim 1.
16. The heater device of claim 15 wherein the hydrogen suppressing, flameless, heat generating chemical composition is enclosed within a bag, the bag comprising a plurality of compartments.
17. The heater device of claim 16 wherein the bag comprises a filter cloth, said filter cloth comprises a spunbond/melt blown/spunbond polypropylene media.
18. The heater device of claim 16 wherein the compartments are formed by a heat seal.
19. The heater device of claim 16 wherein the compartments are formed by a frame, the frame formed by at least one piece of a fluted and ribbed material, the frame bonded to the bag by an adhesive.
20. The heater device of claim 16 wherein the bag comprises at least one drop of a hydrophilizing fluid on at least one side of the bag.
21. A meal, ready-to-eat package comprising the flameless heater device according to claim 15.
Type: Application
Filed: Oct 14, 2011
Publication Date: Feb 9, 2012
Inventor: Tilak V. Bommaraju (Grand Island, NY)
Application Number: 13/273,830
International Classification: C10L 8/00 (20060101); F24J 1/00 (20060101);