PROCESS FOR PRODUCING ULTRAFINE POWDERS BASED ON POLYAMIDES, ULTRAFINE POLYAMIDE POWDERS AND THEIR USE
Process for preparing ultrafine powders based on polyamides by contacting polyamides having a relative solution viscosity ηrel in the range from 1.5 to 2.0, measured in 0.5% m-cresol solution at 25° C., with an alcoholic medium in the presence of inorganic particles suspended therein under the action of pressure and/or temperature to generate an at least partial solution, and then precipitating the polyamide from the at least partial solution; the resulting ultrafine polyamide powders have a specific BET surface area of 5-100 m2/g; a fineness d50 of less than 70 μm; an apparent density AD from 250 to 1000 g/l; and a particle content of 0.1 to 80% by weight of inorganic particles based on the total weight of the polyamide powder; which powders are equally suitable for coatings and for mouldings and components with improved mechanical properties.
Latest EVONIK DEGUSSA GmbH Patents:
This is a divisional application of U.S. application Ser. No. 12/089,998, filed Apr. 11, 2008, which is a 371 of PCT/EP06/067308 filed on Oct. 12, 2006.
The present invention is in the field of fine polyamide powder.
In particular, the invention relates to a process for preparing ultrafine powders based on polyamides by contacting polyamides having a relative solution viscosity ηrel in the range from 1.5 to 2.0, measured in 0.5% m-cresol solution at 25° C., with an alcoholic medium in the presence of inorganic particles under the action of pressure and/or temperature to generate an at least partial solution, and then precipitating the polyamide from the at least partial solution. The invention also includes fine polyamide powders which have a high BET surface area and an apparent density which is within the range of standard precipitated polyamide powders, and also the use of the fine polyamide powders.
Powders based on polyamide, for example for coatings or for obtaining mouldings, are notable for their high chemical resistance and very good mechanical properties. Powders which are obtained by reprecipitation from ethanolic solution, for example according to DE-A 2905547, are superior with regard to their processing performance to those products which are obtained from a grinding process, for example according to DE-A 1570392, since the precipitation leads to rounder and hence better fluidizable particles. Moreover, ground powders as obtained, for particles. Moreover, ground powders as obtained, for example, also according to DE-C 2855920 have a broad particle size distribution, which in turn causes a high level of classifying complexity. A further advantage of the precipitated powders is the wide range of variation in the molecular weight (ηrel=1.5-2.0), while ground powders are producible in an economically viable manner only at an ηrel<1.7.
The fine polyamide powders should ideally satisfy a whole series of requirements. For instance, it would be desirable to amalgamate a high BET surface area with a large apparent density combined with sufficient fineness of the powders.
For example, a high BET surface area would be desirable in many cases in order to improve the adhesion of the powder with respect to surfaces to be coated, or in order thus to lead to improved incorporation of pigments or additives of all types.
In the so-called laser sintering process for producing components from fine polyamide powders too, a high BET surface area is advantageous, since the possibility of adhesion between the powder particles can thus be increased.
Unfortunately, however, the advantages of a high BET surface area have to date necessarily been associated with an apparent density which complicates frictionless processing in existing processes. Normally, high apparent density and high BET surface area are two contradictory requirements. Powders based on polyamide which satisfy both requirements cannot be prepared according to the current state of the art. Although DE-A 19708956 describes fine polyamide powders with high apparent density which have been obtained by a two-stage precipitation process, these powders still have a low BET surface area.
Although combinations of polyamide powders with inorganic pigments (e.g. titanium dioxide) have a high apparent density, they are neither fine powders nor exhibit a high BET surface area.
The mere presence of particulate substances during the reprecipitation of polyamides is just as unlikely to lead to the desired combination of properties. Thus, DE-A 3510690 discloses polyamide powders which are obtained by a precipitation process from ethanol, according to the examples of said DE-A 3510690, inter alia, in the presence of white pigment (particulate titanium dioxide). However, measurements show that powders obtained according to this example have either relatively good apparent densities in conjunction with very low BET surface area, or sufficient BET surface area but at the expense of a no longer sufficiently high apparent density. A fine polyamide powder having a combination of high BET surface area and an apparent density between 250 and 1000 g/l is not made obtainable by DE-A 3510690.
In view of the prior art detailed, it is an object of the invention to specify a process for preparing fine powders based on polyamide which, with sufficient fineness, couple a high BET surface area with sufficiently good processibility, i.e. an apparent density within the desired range.
It is a further object to provide fine polyamide powders having a high BET surface area in combination with sufficiently high apparent density.
It is another object to specify possible uses of the inventive fine polyamide powders. Thus, the fine powders based on polyamide should, by simple known processes, make available components and mouldings which possess increased strength values such as modulus of elasticity or tensile strength, but also very good impact resistance properties.
These objects, and further objects which are not specified in detail but which are immediately evident from the discussion of the prior art, are solved by a process having the features of Claim 1. With regard to the product, the independent claim of the appropriate category specifies a solution to the object of the invention. With regard to the possible uses, solutions are disclosed by the appropriate claims.
By using, in a process for preparing ultrafine powders based on polyamides by contacting polyamides having a relative solution viscosity ηrel in the range from 1.5 to 2.0, measured in 0.5% m-cresol solution at 25° C., with an alcoholic medium in the presence of inorganic particles under the action of pressure and/or temperature to generate an at least partial solution, and then precipitating the polyamide from the at least partial solution, a suspension of the inorganic particles in the alcoholic medium, it is possible in a manner which is not directly foreseeable to make available for the first time fine powders based on polyamide which satisfy the property profile discussed at the outset.
In the context of the invention, processible fine polyamide powders with high apparent density and high BET surface area can be obtained by performing the polyamide precipitation (reprecipitation of the polyamide) in an alcoholic suspension which contained inorganic particles. In contrast to DE-A 3510690, in which, for example, a precipitation was also performed in the presence of particles (white pigment), a suspension of the particles is generated in the process according to the invention and the reprecipitation of the polyamide is performed in the presence of this suspension of the particles. A surprising result obtained here is an optimally processible fine polyamide powder having the desired properties with regard to BET surface area and apparent density.
The inventive procedure results in fine polyamide powders in combination with inorganic particles.
The use of inorganic particles which are present in suspension in an alcoholic medium is of particular significance for the process of the invention. In a preferred process variant, the process is characterized in that a suspension is used which comprises inorganic particles having a mean particle size d50 in the range from 0.001 to 0.8 μm, measured in suspension in the alcoholic medium as the volume-weighted median value of the peak analysis by means of static or dynamic light scattering, suspended in the alcoholic medium. Even more preferably, suspensions of inorganic particles are used, the particles having a size d50 in the range from 0.005 to 0.5 μm and most preferably in the range from 0.01 to 0.3 μm. The particle size as specified is determined by known measurement methods by means of static or dynamic light scattering in the suspension. The values obtained via light scattering processes may be isolated particles or else agglomerates of primary particles in the suspension. What is important for the invention is that the particles actually present in the suspension, whether they be primary particles or agglomerates, have a d50 value within the range specified. The particle size can be measured, for example, with a Zetasizer 3000 Hsa (Malvern Instruments, UK). When the particle size is above a d50 value of 0.8 μm, the risk that no fine powders result is great. In the reprecipitation, the result under some circumstances might then be excessively large polyamide powder particles.
The nature of the compounds usable as inorganic particles in the context of the invention can vary over a wide range. Processes of great interest are those in which a suspension is used which comprises inorganic particles selected from the group consisting of Al2O3, TiO2, ZrO2, SiO2, ZnO, Bi2O3, CeO2, ITO (indium oxide doped with tin(IV) oxide), ATO (tin(IV) oxide doped with antimony oxide), IZO (indium oxide doped with zinc oxide), boron nitride, boron carbide, mixed oxides and spinels, suspended in the alcoholic medium. Particular preference is given to the use of aluminium oxide (Al2O3).
In this connection, the aluminium oxide may preferably be of pyrogenic origin. Pyrogenic means that corresponding aluminium oxide powder is obtained by reacting a suitable starting material in a flame. Pyrogenic processes include flame oxidation and flame hydrolysis. A particular process used for the industrial scale preparation of aluminium oxide is the flame hydrolysis of aluminium chloride in a hydrogen/oxygen flame. In general, the aluminium oxide particles prepared in this way are present in the form of aggregated primary particles, the primary particles being free of pores and bearing hydroxyl groups on their surface. In the reaction of aluminium chloride to give aluminium oxide, a by-product formed is hydrochloric acid which adheres to the aluminium oxide particles. Commonly, a majority of the hydrochloric acid is removed from the particles by a treatment with steam.
Aluminium oxide powders particularly suitable for the invention include: AEROXIDE® Alu C, AEROXIDE® Alu 65, AEROXIDE®Alu 130, all Degussa AG, SpectrAl™ 100 Fumed Alumina, SpectrAl™ 51 Fumed Alumina, SpectrAl™ 81 Fumed Alumina, all Cabot Corp.
An appropriate process variant envisages the use of a suspension which is obtainable by suspending inorganic particles having a specific surface area in the range from 5 to 200 m2/g in the alcoholic medium.
The inorganic particles are used in the form of a suspension in alcoholic medium. To obtain a suspension, the particles are distributed finely in the alcoholic medium. This is done by processes known per se. Particular preference is given to processes which enable a high energy input. Such processes are described, for example, in German Patent Application 103 60 766 or German Patent Application 10 2005 032 427.4.
In a preferred embodiment, the process of the invention is characterized in that a suspension is used which is obtainable by suspending the inorganic particles in the alcoholic medium with introduction of an energy input of greater than 1000 kJ/m3. This generally gives rise to very usable suspensions of the particles in the alcohol. The energy input addressed can be accomplished by known units. Suitable units may be: planetary kneaders, rotor-stator machines, stirred ball mills, roll mills and the like.
A particularly suitable procedure has been found to be one in which the suspension is first prepared with an energy input of less than 1000 kJ/m3 to form a presuspension, the presuspension is divided into at least two substreams, these substreams are placed under a pressure of at least 500 bar in a high-energy mill, decompressed through a nozzle and allowed to meet one another in a gas- or liquid-filled reaction chamber, and the high-energy grinding is optionally repeated once or more than once.
The amount of inorganic particles in the suspension can vary over a wide range. Depending on the particle type, size of the inorganic particles and specific nature of the alcoholic medium, relatively small or relatively large solids contents may be advisable. In general, it will, however, be appropriate to use very solids-rich suspensions for the purposes of the invention. In an advantageous process modification, a suspension is used which has a content of particles in the range from 10 to 60% by weight based on the total weight of the suspension. Suspensions which are usable particularly favourably include those having a solids content of from 15 to 50% by weight, even more appropriately from 20 to 50% by weight.
The suspensions of inorganic particles in alcoholic media involved in the process according to the invention should be highly stable. In the context of the invention, particularly stable is understood to mean the stability of the suspension against sedimentation and reagglomeration within a period of one month, generally of at least six months.
To achieve particularly stable suspensions, it has also been found to be particularly advantageous when, in the distribution of the inorganic particles in the alcoholic medium, additives are present which can stabilize the suspension.
Such additives are, for example, phosphoric acid and its mono- or dibasic phosphates, phosphoric esters, phosphonic acids, organically modified phosphonic acid, sulphuric acid and derivatives thereof, nitric acid, genrerally organic mineral acids. In addition, it is also possible to use organic compounds having acidic protons, for example carboxylic acids or phenols. Basic organic compounds, for example based on amines, are also suitable.
The suspensions utilizable for the invention are generated in an alcoholic medium. This may be a pure alcohol, a mixture of a plurality of alcohols or else alcohols having a content of water or other substances which essentially do not disadvantageously influence the desired reprecipitation of the polyamides. The alcoholic medium of the inventive suspensions preferably has a content of less than 50% by weight of nonalcoholic substances (preferably water), more preferably less than 10% by weight and particularly appropriately less than 1% by weight of extraneous, nonalcoholic substances. Useful substances for the invention are generally all types of alcohols or mixtures thereof which permit reprecipitation of the polyamides under the desired conditions (pressure and temperature). In the individual case, it is possible for the person skilled in the art to adjust the system to specific requirements without any great complication. For the process of the invention, the alcoholic medium used for the reprecipitation of the polyamide and/or the suspension of the inorganic particles is preferably one or more alcohols which have a numerical ratio of oxygen atoms to carbon atoms in the range from 1:1 to 1:5.
Typical alcohols for preparing the suspension of the inorganic particles are those having a ratio of oxygen to carbon of 1:1, 1:2, 1:3, 1:4 and 1:5, preferably those having an oxygen to carbon ratio of 1:2 and 1:3, more preferably having an oxygen to carbon ratio of 1:2. Very particularly appropriately, ethanol is used in the preparation of a suspension of the inorganic particles, and in the reprecipitation of the polyamides.
The polyamides reprecipitable in accordance with the invention (i.e., therefore, compounds usable as starting materials) are the entire range of known and available substances. Polyamides usable with preference as the starting material for the process of the invention include nylon-11, nylon-12 and polyamides having more than 12 aliphatically bonded carbon atoms per carboxamide group, preferably nylon-12. It is also possible to use the corresponding copolyamides or mixtures of homo- and copolyamides which contain at least 70 percent by weight of the units mentioned. As comonomers, they may accordingly contain from 0 to 30 percent by weight of one or more comonomers, such as caprolactam, hexamethylenediamine, 2-methylpentane-1,5-diamine, octamethylene-1,8-diamine, dodeca-methylenediamine, isophoronediamine, trimethylhexa-methylenediamine, adipic acid, suberic acid, azelaic acid, sebacic acid, dodecanedioic acid, aminoundecanoic acid. The homo- and copolyamides referred to hereinafter as polyamides are used in the form of granules or pellets, which possess a relative solution viscosity between 1.5 and 2.0 (measured in 0.5% m-cresol solution at 25° C. to DIN 53 727), preferably between 1.70 and 1.95. They can be prepared by polycondensation, hydrolytic or acidolytic or activated anionic polymerization by known processes. Preference is given to using unregulated polyamides with NH2/COOH end group ratios=from 40/60 to 60/40. The use polyamide may contain not more than 0.2 percent by weight of H3PO4. Preference is given to using H3PO4-free polyamides. However, it may also be appropriate to use regulated polyamides, preferably those in which the NH2/COOH end group ratio of 90:10 and 80:20 or 10:90 and 20:80 is present.
The solution of the polyamides for reprecipitation can be prepared in all known ways. What is advantageous is substantially complete dissolution of the polyamide in the alcoholic medium in the presence of the suspension of inorganic particles. The dissolution can be promoted by use of pressure and/or temperature. The procedure is appropriately to initially charge the polyamide in the alcoholic medium and to dissolve it over the time needed under the action of elevated temperature. The suspension of the inorganic particles can be added before, during or after the dissolution of the polyamide. Appropriately, the suspension of the inorganic particles is initially charged at the same time as the polyamide. The dissolution operation is favourably promoted by the use of appropriate stirrer units. The precipitation of the polyamide can likewise be supported by use of pressure and/or temperature. For instance, a lowering of the temperature and/or distillative removal (preferably under reduced pressure) of the solvent, i.e. of the alcoholic medium, lead to the precipitation of the polyamide. However, it is also possible to support the precipitation by addition of an antisolvent (precipitant).
The invention also provides an ultrafine powder based on polyamides, obtainable by contacting polyamides having a relative solution viscosity ηrel in the range from 1.5 to 2.0, measured in 0.5% m-cresol solution at 25° C., with a suspension of inorganic particles in an alcoholic medium under the action of pressure and/or temperature to generate an at least partial solution, and then precipitating the polyamide from the at least partial solution, the polyamide powder being characterized by a specific BET surface area in the range of 5-100 m2/g, preferably 10-25 m2/g; a fineness d50 of less than 70 μm; an apparent density AD in the range from 250 to 1000 g/l; and a particle content of 0.1 to 80% by weight, preferably from 1 to 60% by weight, of inorganic particles based on the total weight of the polyamide powder.
The BET surface area is determined to DIN 66131 by absorption of nitrogen according to Brunauer-Emmett-Teller.
The fineness d50 is determined by light scattering in a laser beam with a Malvern Mastersizer S Version 2.18.
The apparent density is determined to DIN 53644.
The particle content is determined by an ash/ignition residue determination to DIN EN ISO 3451 Part 1 and Part 4.
The solution viscosity was determined in 0.5% meta-cresol solution to DIN 307.
Preferred precipitated powders have apparent densities in the range from 250 to 800 g/l and more preferably between 300 and 500 g/l. Within these ranges, there is optimal processibility.
The fine polyamide powders of the invention feature a unique combination of properties. In addition to the properties mentioned, they also possess a relatively narrow particle size distribution, which is evident from the examples. Owing to their outstanding properties, the powders are suitable for a whole series of applications.
One preferred use of the ultrafine powder based on polyamides comprises the use as a coating composition. The powders give rise to impeccable coatings by all known and suitable coating processes. It is possible to produce either fluidized-bed sintering powders or electrostatic powders. Thus, even in the coating of difficult metal parts, the precipitated powders exhibit excellent properties with regard to stretchability and edge coatings, and also stability toward alkaline aqueous solutions. The mechanical strength of the coatings is at an excellent level.
The precipitated powders of the invention are equally outstandingly suitable for the production of mouldings and components. Materials made from inventive fine polyamide powders otherwise also have outstanding mechanical properties. For instance, the inventive fine powders exhibit not only increased strength values such as modulus of elasticity or tensile strength, but also very good impact strength properties.
The invention therefore also encompasses the use of the ultrafine powder based on polyamides to produce mouldings and/or components of various shapes and structures. In this case, one possibility is to proceed from the powder itself and to produce the mouldings or components directly by known deformation processes, preferably by injection moulding, extrusion or blow moulding.
Alternatively, the powders can also first be granulated and then processed thermoplastically, again by processes known per se, i.e. essentially by means of injection moulding, extrusion or blow moulding.
The invention will be illustrated in detail below with reference to examples and comparative examples.
Tests
Preparation of suspensions of the inorganic particles in alcoholic medium (ethanol) to be used in the process of the invention
Suspension 1 (S1):
A 100 1 stainless steel batch vessel is initially charged with 77 kg of ethanol. Subsequently, with running Ystral Conti-TDS 3 (stator slot: 4 mm ring and 1 mm ring, rotor/stator distance approx. 1 mm) under shear conditions, 23 kg of AEROXIDE® Alu C (BET 100 m2/g) from Degussa are introduced into the batch vessel. Once the addition has ended, shearing is continued at 3000 rpm for another 30 min.
This presuspension is conducted in two passes through the Sugino Ultimaizer HJP-25050 high-energy mill at a pressure of 2500 bar and diamond dies of diameter 0.25 mm and thereby intensively ground further.
The addition of 85% phosphoric acid, so as to attain a concentration of 2% pure H3PO4 based on the Al2O3, was effected during the preparation of the presuspension in the dissolver.
After the suspension, a mean particle size d50 of 0.18 μm was determined by dynamic light scattering (Zetasizer 3000 Hsa from Malvern Instruments, UK). The volume-weighted median value of the peak analysis is reported.
Suspension 2 (S2):
A 100 1 stainless steel batch vessel is initially charged with 44 kg of ethanol and 1.00 kg of H3PO4 (85%). Subsequently, with running Ystral Conti-TDS 3 (stator slot: 4 mm ring and 1 mm ring, rotor/stator distance approx. 1 mm) under shear conditions, 21 kg of AEROXIDE® Alu C (BET 100 m2/g) from Degussa are introduced into the batch vessel. Once approx. 18 kg of AEROXIDE® Alu C had been added, a further 0.13 kg of H3PO4 (85%) was added, in order again to achieve a low viscosity. Once the addition has ended, shearing is continued at 3000 rpm for another 30 min. At shear time 25 min, a further 1.2 kg of H3PO4 (85%) are added, so that a concentration of 11% H3PO4 (85%) based on the Al2O3 is achieved.
This presuspension is conducted in two passes through the Sugino Ultimaizer HJP-25050 high-energy mill at a pressure of 2500 bar and diamond dies of diameter 0.25 mm and thereby intensively ground further.
After the suspension, a particle size d50 of 0.14 μm was determined by dynamic light scattering (Zetasizer 3000 Hsa from Malvern Instruments, UK). The volume-weighted median value of the peak analysis is reported.
Suspension 3 (S3):
A 100 1 stainless steel batch vessel is initially charged with 77 kg of ethanol. Subsequently, with running Ystral Conti-TDS 3 (stator slot: 4 mm ring and 1 mm ring, rotor/stator distance approx. 1 mm) under shear conditions, 23 kg of AEROXIDE® Alu C (BET 100 m2/g) from Degussa are introduced into the batch vessel. Once the addition has ended, shearing is continued at 3000 rpm for another 30 min.
This presuspension is conducted in two passes through the Sugino Ultimaizer HJP-25050 high-energy mill at a pressure of 2500 bar and diamond dies of diameter 0.25 mm and thereby intensively ground further.
The phosphoric acid was added during the preparation of the suspension in the dissolver. After passage through the high-energy mill, for further stabilization, Cublen P 50 (a commercial product from Schwarz and Zschimmer GmbH, a 50% solution of 2-phosphonobutane-1,2,4-tricarboxylic acid in water) was added in such an amount that a concentration of 2% by weight of Cublen P 50 based on the amount of Al2O3 is achieved.
After the suspension, a particle size d50 of 0.13 μm was determined by static light scattering (Zetasizer 3000 Hsa from Malvern Instruments, UK). The volume-weighted median value of the peak analysis is reported.
Suspension 4 (S4):
A 100 1 stainless steel batch vessel is initially charged with 77 kg of ethanol. Subsequently, with running Ystral Conti-TDS 3 (stator slot: 4 mm ring and 1 mm ring, rotor/stator distance approx. 1 mm) under shear conditions, 23 kg of AEROXIDE® Alu C (BET 100 m2/g) from Degussa are introduced into the batch vessel. Once the addition has ended, shearing is continued at 3000 rpm for another 30 min.
This presuspension is conducted in two passes through the Sugino Ultimaizer HJP-25050 high-energy mill at a pressure of 2500 bar and diamond dies of diameter 0.25 mm and thereby intensively ground further.
For stabilization, 85% phosphoric acid is now added with intensive mixing to the suspension obtained, so that a concentration of 2% pure H3PO4, based on the amount of Al2O3, is achieved, and Cublen P 50 (a commercial product from Schwarz and Zschimmer GmbH, a 50% solution of 2-phosphonobutane-1,2,4-tricarboxylic acid in water) is added in such an amount that a concentration of 2% by weight of Cublen P 50 based on the amount of Al2O3 is achieved.
After the suspension, a particle size d50 of 0.06 μm was determined by static light scattering (Zetasizer 3000 Hsa from Malvern Instruments, UK). The volume-weighted median value of the peak analysis is reported.
Suspension 5 (S5):
A 100 1 stainless steel batch vessel is initially charged with 77 kg of ethanol. Subsequently, with running Ystral Conti-TDS 3 (stator slot: 4 mm ring and 1 mm ring, rotor/stator distance approx. 1 mm) under shear conditions, 23 kg of VP zirconium oxide PH from Degussa are introduced into the batch vessel. Once the addition has ended, shearing is continued at 3000 rpm for another 30 min.
This presuspension is conducted in two passes through the Sugino Ultimaizer HJP-25050 high-energy mill at a pressure of 2500 bar and diamond dies of diameter 0.25 mm and thereby intensively ground further.
The phosphoric acid was again added during the suspension in the dissolver, while the amount of 2% by weight of Cublen P 50 (a commercial product from Schwarz and Zschimmer GmbH, a 50% solution of 2-phosphonobutane-1,2,4-tricarboxylic acid in water), based on the overall suspension, is added for subsequent stabilization.
After the suspension, a particle size d50 of 0.08 μm was determined by static light scattering (Zetasizer 3000 Hsa from Malvern Instruments, UK). The volume-weighted median value of the peak analysis is reported.
Preparation of fine polyamide powders with high apparent density and low BET surface area (noninventive comparative example A-D).
COMPARATIVE EXAMPLE A Two-Stage Reprecipitation of Unregulated PA 1250 kg of unregulated PA 12 prepared by hydrolytic polymerization and having a relative solution viscosity of 1.62 and an end group content of 75 mmol/kg of COOH and 69 mmol/kg of NH2 are brought to 145° C. in a 0.8 m3 stirred tank together with 310 1 of ethanol, denatured with 2-butanone and water content 1%, within 5 hours, and left at this temperature for 1 hour with stirring (paddle stirrer, d=80 cm, speed=49 rpm). Subsequently, the jacket temperature is reduced to 124° C. and, while continuously distilling off the ethanol, the internal temperature is brought to 125° C. with the same stirrer speed at a cooling rate of 25 K/h. From now on, the jacket temperature is kept 2 K-3 K below the internal temperature at the same cooling rate. The internal temperature is brought to 117° C. with the same cooling rate and then kept constant for 60 minutes. Thereafter, distillative removal is continued at a cooling rate of 40 K/h and the internal temperature is thus brought to 111° C. At this temperature, precipitation sets in, noticeable by the evolution of heat. The distillation rate is increased to such an extent that the internal temperature does not rise above 111.3° C. After 25 minutes, the internal temperature falls, which indicates the end of precipitation. Further distillative removal and cooling via the jacket brings the temperature of the suspension to 45° C., and the suspension is then transferred to a paddle dryer.
The ethanol is distilled off at 70° C./400 mbar, and the residue is then dried at 20 mbar/86° C. for 3 hours.
COMPARATIVE EXAMPLE B Two-Stage Reprecipitation of PA 1010In accordance with Example A, 50 kg of a PA 1010 specimen which has been obtained by polycondensation of 1,10-decanediamine and sebacic acid and has the following data is reprecipitated: ηrel=1.84, [COOH]=62 mmol/kg, [NH2]=55 mmol/kg.
The precipitation conditions are altered compared to Example A as follows:
Dissolution temperature: 155° C., nucleation temperature/time: 128° C./60 min
Precipitation temperature: 120° C., precipitation time: 1 hour, stirrer speed: 90 rpm
COMPARATIVE EXAMPLE C Two-Stage Reprecipitation of PA 1212In accordance with Example A, 50 kg of a PA 1212 granule specimen which has been obtained by polycondensation of 1,10-decanediamine and dodecanedioic acid and has the following data is reprecipitated: ηrel=1.80, [COOH]=3 mmol/kg, [NH2]=107 mmol/kg.
The precipitation conditions are altered compared to Example A as follows:
Dissolution temperature: 155° C., nucleation temperature: 123° C., nucleation time: 60 min
Precipitation temperature: 117° C., precipitation time: 60 minutes, stirrer speed: 110 rpm
COMPARATIVE EXAMPLE D One-Stage Reprecipitation of Unregulated PA 12 According to DE-A 3510690 in the Presence of White Pigment50 kg of unregulated PA 12 prepared by a hydrolytic polymerization and having a relative solution viscosity of 1.62 and an end group content of 75 mmol/kg of COOH and 69 mmol/kg of NH2, and also 3 kg of titanium dioxide pigment (Kerr-McGee R-FK 3), together with 310 1 of ethanol denatured with 2-butanone and water content 1%, are brought to 152° C. in a 3 m3 stirred tank (d=160 cm) within 5 hours and left at this temperature with stirring (paddle stirrer, d=80 cm, speed=80 rpm) for 1 hour. The jacket temperature is then reduced to 124° C. and, while continuously distilling off the ethanol, the internal temperature is brought to 125° C. with a cooling rate of 25 K/h at the same stirrer speed. From now on, the jacket temperature is kept 2 K-3 K below the internal temperature at the same cooling rate until, at 108° C., precipitation, recognizable by the evolution of heat, sets in. The distillation rate is increased to such an extent that the internal temperature does not rise above 109.7° C. After 20 minutes, the internal temperature declines, which indicates the end of the precipitation. Further distillative removal and cooling via the jacket brings the temperature of the suspension to 45° C., and the suspension is then transferred to a paddle dryer.
The ethanol is distilled off at 70° C./500 mbar, and the residue is then dried at 20 mbar/86° C. for 3 hours.
The preparation of fine polyamide powders with high apparent density and high BET surface area is illustrated hereinafter with reference to examples. The results are compiled in Table 1.
EXAMPLE 1 One-Stage Reprecipitation of Unregulated PA 12 Analogously to DE-A 3510690, but with use of Suspension S150 kg of unregulated PA 12 prepared by a hydrolytic polymerization and having a relative solution viscosity of 1.62 and an end group content of 75 mmol/kg of COOH and 69 mmol/kg of NH2, together with 290 1 of ethanol denatured with 2-butanone and water content 1% and 17.4 kg of S1, are brought to 145° C. in a 0.8 m3 stirred tank within 5 hours and left at this temperature with stirring (paddle stirrer, d=80 cm, speed=85 rpm) for 1 hour. The jacket temperature is then reduced to 124° C. and, while continuously distilling off the ethanol, the internal temperature is brought to 125° C. with a cooling rate of 25 K/h at the same stirrer speed. From now on, the jacket temperature is kept 2 K-3 K below the internal temperature at the same cooling rate until, at 109° C., precipitation, recognizable by the evolution of heat, sets in. The distillation rate is increased to such an extent that the internal temperature does not rise above 109.3° C. After 20 minutes, the internal temperature declines, which indicates the end of the precipitation. Further distillative removal and cooling via the jacket brings the temperature of the suspension to 45° C., and the suspension is then transferred to a paddle dryer. The ethanol is distilled off at 70° C./500 mbar, and the residue is then dried at 20 mbar/86° C. for 3 hours.
EXAMPLE 2 One-Stage Reprecipitation of Unregulated PA 12 with Addition of Suspension S2The procedure was analogous to Example 1. 17.4 kg of suspension S2 were used.
EXAMPLE 3 One-Stage Reprecipitation of Unregulated PA 12 with Addition of Suspension S2The procedure was analogous to Example 1. 34.8 kg of suspension S2 were used. The amount of ethanol in the batch was reduced from 290 1 to 275 1.
EXAMPLE 4 One-Stage Reprecipitation of Unregulated PA 12 with Addition of Suspension S3The procedure was analogous to Example 1. 17.4 kg of suspension S3 were used.
EXAMPLE 5 One-Stage Reprecipitation of Unregulated PA 12 with Addition of Suspension S3The procedure was analogous to Example 1. 34.8 kg of suspension S3 were used. The amount of ethanol in the batch was reduced from 290 1 to 275 1.
EXAMPLE 6 One-Stage Reprecipitation of Unregulated PA 12 with Addition of Suspension S4The procedure was analogous to Example 1. 17.4 kg of suspension S4 were used.
EXAMPLE 7 One-Stage Reprecipitation of Unregulated PA 12 with Addition of Suspension S5The procedure was analogous to Example 1. 17.4 kg of suspension S5 were used.
EXAMPLE 8 One-Stage Reprecipitation of Unregulated PA 1010 with Addition of Suspension S2In accordance with Example 1, 50 kg of a PA 1010 specimen obtained by polycondensation of 1,10-decanediamine and sebacic acid and having the following characteristic data are reprecipitated: ηrel=1.84, [COOH]=62 mmol/kg, [NH2]=55 mmol/kg.
Compared to Example 1, the precipitation conditions were modified as follows:
Precipitation temperature: 120° C., precipitation time: 2 hours, stirrer speed: 90 rpm
17.4 kg of suspension S2 were used.
EXAMPLE 9 One-Stage Reprecipitation of Unregulated PA 1012 with Addition of Suspension S2In accordance with Example 1, 50 kg of a PA 1012 granule specimen obtained by polycondensation of 1,10-decanediamine and dodecanedioic acid and having the following characteristic data are reprecipitated: ηrel=1.76, [COOH]=46 mmol/kg, [NH2]=65 mmol/kg.
Compared to Example 1, the precipitation conditions were modified as follows:
Dissolution temperature: 155° C., precipitation temperature: 123° C., precipitation time: 40 minutes, stirrer speed: 110 rpm
17.4 kg of suspension S2 were used.
EXAMPLE 10 One-Stage Reprecipitation of Unregulated PA 1012 with Addition of Suspension S2In accordance with Example 1, 400 kg of a PA 1012 granule specimen obtained by polycondensation of 1,10-decanediamine and dodecanedioic acid and having the following characteristic data are reprecipitated: ηrel=1.80, [COOH]=3 mmol/kg, [NH2]=107 mmol/kg.
Compared to Example 1, the precipitation conditions were modified as follows:
Dissolution temperature: 155° C., precipitation temperature: 117° C., precipitation time: 60 minutes, stirrer speed: 110 rpm
17.4 kg of suspension S2 were used.
Preparation and Characterization of Granule
The powders from Examples 1 and 3 and Comparative Example A were melted, extruded and granulated in a Coperion ZSK 25 twin-screw extruder at 220° C. and a throughput of 8 kg/h.
Subsequently, standard specimens were produced by injection moulding and the tensile test to ISO 527 and the impact resistance to ISO 179 le/U at 23° C. and −40° C. were determined.
The results are summarized in Table 2.
Modulus of elasticity, tensile strength, breaking strength, yield stress and elongation at break were determined in the tensile test to ISO 527.
Impact resistance was determined to ISO 179 le/U.
It is evident that specimens obtained with polyamide powders prepared in accordance with the invention possess a higher modulus of elasticity and also higher tensile strength values.
Claims
1. An ultrafine powder based on a polyamide, obtainable by contacting the polyamide having a relative solution viscosity ηrel in a range from 1.5 to 2.0, measured in a 0.5% m-cresol solution at 25° C., with a suspension of inorganic particles in an alcoholic medium under the action of pressure and/or temperature to generate an at least partial solution, and then precipitating the polyamide from the at least partial solution, wherein a specific BET surface area is in a range of 5-100 m2/g; a fineness d50 is less than 70 μm; an apparent density AD is in a range from 250 to 1000 g/l; and a particle content is from 0.1 to 80% by weight of the inorganic particles based on the total weight of the polyamide powder.
2. A coating composition comprising the ultrafine powder based on the polyamides according to claim 1.
3. A moulding comprising the ultrafine powder based on the polyamides according to claim 1.
4. A method for producing the moulding of claim 3, comprising an injection extrusion or blow of the moulding.
5. A method for producing the moulding of claim 3, comprising producing a granule and subsequent thermoplastic, and further injecting, extruding or blowing the moulding.
6. The ultrafine powder according to claim 1, wherein the suspension of the inorganic particles is at least one selected from the group consisting of Al2O3, TiO2, ZrO2, SiO2, ZnO, Bi2O3, CeO2, ITO, ATO, IZO, boron nitride, boron carbide, mixed oxides and spinels, suspended in the alcoholic medium.
7. The ultrafine powder according to claim 1, wherein the suspension of the inorganic particles is at least one of Al2O3.
8. The ultrafine powder according to claim 1, wherein the specific BET surface area in a range of 10-25 m2/g.
9. The ultrafine powder according to claim 1, wherein the apparent density AD in a range from 250 to 800 g/l.
10. The ultrafine powder according to claim 1, wherein the particle content is from 1 to 60% by weight of the inorganic particles based on the total weight of the polyamide powder.
11. The process according to claim 1, wherein the apparent density AD in a range from 300 to 500 g/l.
Type: Application
Filed: Jun 12, 2012
Publication Date: Oct 18, 2012
Applicant: EVONIK DEGUSSA GmbH (Essen)
Inventors: Harald Häger (Luedinghausen), Franz-Erich Baumann (Duelmen), Wolfgang Lortz (Waechtersbach), Christoph Batz-Sohn (Hanau-Mittelbuchen)
Application Number: 13/494,082
International Classification: C08L 77/00 (20060101); B29C 47/00 (20060101); B29C 45/00 (20060101); C09D 177/00 (20060101); B29C 49/00 (20060101);