HIGH-THERMAL CONDUCTIVITY ADSORBENTS FOR RAPID ABSORPTION OF HEAT PULSES AND A PRESSURE-CASCADE BURST DESORPTION SYSTEM USING THE SAME
A composite adsorbent and heat burst desorption system using the same. The composite adsorbent material includes a backbone and a filler. The backbone comprises a first material having a high thermal conductivity and a plurality of pore. The filler, within the pores of the backbone, comprises a second material having a large specific surface area.
Latest Government of the United States as Represented by the Secretary of the Air Force Patents:
- APPARATUS AND METHOD FOR HOLDING OPTICAL FIBER AND FIBER ARRAYS VIA VACUUM FOR FIBER ALIGNMENT AND ATTACHING
- SYSTEMS AND METHODS FOR MAPPING HARDWARE FIFO TO PROCESSOR ADDRESS SPACE
- ENDOVASCULAR VARIABLE AORTIC CONTROL CATHETER
- ENDOVASCULAR VARIABLE AORTIC CONTROL CATHETER
- Systems and methods for determining feature resolution of image data
Pursuant to 37 C.F.R. §1.78(a)(4), this application claims the benefit of and priority to prior filed co-pending Provisional Application Ser. No. 61/720,416, filed Oct. 31, 2012, which is expressly incorporated herein by reference.
RIGHTS OF THE GOVERNMENTThe invention described herein may be manufactured and used by or for the Government of the United States for all governmental purposes without the payment of any royalty.
FIELD OF THE INVENTIONThe present invention relates generally to the rapid absorption of heat pulses and, more particularly, to adsorbents and systems for rapid absorption of heat pulses.
BACKGROUND OF THE INVENTIONTechnological advances in electronics, avionics, and automotive industries are often accompanied by a further need for energy storage. However, the energetic needs of these platforms often result in high thermal output. At times, the thermal output may include large bursts of heat (ranging from about 100 kW to about 1 MW) over a relatively short period of time (about 10 seconds to about 100 seconds). Conventional systems of managing the heat produced by these platforms have included micro- and meso-porous materials (e.g., activated carbons, zeolites, silica, and alumina gels) having large specific surface areas (ranging from about 1000 m2/g to about 2000 m2/g). However, some of these materials (zeolites and silica gels) have poor thermal conductivity due to low intrinsic thermal conductivity or poor consolidation of powders.
Certain gases and vapors (e.g., NH3, CO2, MeOH, and H2O), known and used as adsorbates, adsorb onto solid adsorbents, such as the micro- and meso-porous materials with large heats of adsorption. Exemplary heats of desorption, on an adsorbate-mass basis, are shown below in Table 1. However, these systems (solid/vapor desorption systems) have conventionally been used as refrigerators or heat pumps that function on a continuous, low instantaneous, cooling power basis. Therefore, these conventional systems have not been suitable for use in adequately adsorbing rapid bursts of heat, particularly over the lifetime of the platform.
Other conventional approaches to thermal management have incorporated macroporous foams (e.g., graphitic, aluminum, and copper foams), having high effective thermal conductivities (ranging from about 20 W/m·K to about 200 W/m·K). Yet, macroporous foams are incapable of adsorbing large quantities of adsorbates due to low specific surface areas (ranging from about 10 m2/g to about 100 m2/g).
Thus, there remains a need for large high-thermal conductivity adsorbents, particularly for use in systems configured to manage large thermal loads and accommodate short periods of rapid cooling. Furthermore, and in particularly for uses with respect to deployed military platforms, new devices are needed that are light weight, compact, low cost, low maintenance, and safe to operate (with respect to toxicity, flammability, and reactivity).
SUMMARY OF THE INVENTIONThe present invention overcomes the foregoing problems and other shortcomings, drawbacks, and challenges of conventional heat adsorption materials and systems. While the invention will be described in connection with certain embodiments, it will be understood that the invention is not limited to these embodiments. To the contrary, this invention includes all alternatives, modifications, and equivalents as may be included within the spirit and scope of the present invention.
According to one embodiment of the present invention, a composite adsorbent includes a backbone and a filler. The backbone comprises a first material having a high thermal conductivity and a plurality of pore. The filler, within the pores of the backbone, comprises a second material having a large specific surface area.
Another embodiment of the present invention is directed to a heat burst desorption system for absorbing rapid heat bursts from a heat load. The system includes an adsorbent bed containing an adsorbent and an adsorbate supply containing an adsorbate. The adsorbate is configured to adsorb onto the surface of the adsorbent with a large heat of adsorption. The system operates in an absorption mode and a recharge mode. In the absorption mode, when heat is transferred from the heat load to the adsorbent bed, the adsorbent bed is fluidically coupled to an exhaust such that adsorbate desorbs from surface of the adsorbent and is vented. In the recharge mode, heat is rejected from the system along a second transfer path, the adsorbent bed is fluidically coupled to the adsorbate supply such that adsorbate adsorbs onto the surface of the adsorbent.
According to still another embodiment of the present invention, a method of absorbing rapid heat bursts from a heat load includes decompressing an adsorbent bed, containing an adsorbent, when heat is generated. When heat generation cases, the adsorbent bed is recharged with an adsorbate, which is configured to adsorb onto a surface of the adsorbent.
Yet another embodiment of the present invention is directed to a composite adsorbent having a thermally-conductive backbone and a filler. The backbone includes a first material having plurality of pore therein and the filler is within those pores. A second material, comprising the filler, has a large specific surface area.
In accordance with another embodiment of the present invention, an adsorbent includes a plurality of thermally-conductive elements. Elements of the plurality interface with other elements of the plurality to form a three-dimensional network. The elements may include carbon nanotubes, multi-wall carbon nanotubes, metallic nanowires, semiconducting nanowires, graphene, or a combination thereof.
An embodiment of the present invention includes a composite adsorbent having a backbone and a filler. A first material, which comprises the backbone, includes a plurality of pores therein and a thermal conductivity greater than about 20 W/m·K. A second material, which comprises the filler, has a specific surface area greater than about 1000 m2/g.
The above and other objects and advantages of the present invention shall be made apparent from the accompanying drawings and the descriptions thereof.
The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments of the present invention and, together with a general description of the invention given above, and the detailed description of the embodiments given below, serve to explain the principles of the present invention.
Turning now to the figures, and in particular to
In Block 20 of the flowchart 10, an outermost layer of the material comprising the backbone 12 is exfoliated and fills pores 18 of the backbone 12. One method of exfoliation, according to one exemplary embodiment, places the porous backbone 12 into an acidic bath such that ionic solvent may intercalate into the pores 18. The intercalating species (illustrated as intercalating solvent 22) may include, for example, SO4, NO3, or other like ionic groups. With the intercalating solvent 22 permeated throughout the backbone 12, the backbone 12 may then be rapidly heated such that outermost layers exfoliate from the backbone 12 and reside within the pores 18 as exfoliate filler 24.
If desired, the backbone 12 and/or the exfoliate filler 24 may be surface treated so as to further tune adsorbate-adsorbent interaction within the composite adsorbent 16 (Block 26). For instance, polar ionic species (e.g., acidic functional groups, nitrates, and sulfates) may be added to change the polarity of the adsorbent surface of the backbone 12. Additionally, or alternatively, liquid, vapor, or plasma treatments may be used to further modify the adsorbent surface of the backbone 12 or of the filler 24.
A second method of forming a composite adsorbent 28, also shown in the flowchart of
As residual solution is evaporated from the backbone 12, whether by supercritical or freeze drying, an aerogel or cryogel 30 forms, respectively, within the pores 18 (Block 36). If necessary, or desired, a reactive gas species may be directed through the filler 30 to develop a desired distribution of porosity (Block 38). And, as described previously with respect to the composite adsorbent 16 of
In some instances, high thermal conductivity may be required to extend in three dimensions. A three-dimensional adsorbent 40 suitable for such uses and according to one embodiment of the present invention is shown and described with respect to
Each element 42 may be a carbon nanotubes (CNTs), a multi-wall CNT, a metallic or semiconducting nanowire, graphene, or other 2D structured material. The three-dimensional adsorbent forms a three-dimensional network to transmit heat over a large volume while providing a porous-like structure between adjacent ones of the elements 42. The illustrative structure permits significant adsorption of adsorbate species without restricting the flow of adsorbate molecules, the necessity of which is described in greater detail below.
One approach of synthesizing embodiments of the three-dimensional adsorbents 40 may include template-assisted growth from graphene. In this approach, two-dimensional graphene is grown on all outer surfaces of a connected network of metal, e.g., Ni, after which the metal is dissolved to leave the residual, covalently bonded CNT network.
While the three-dimensional adsorbent 40 may have large inherent thermal conductivity, the high interfacial density may suggest to those of ordinary skill in the art that the effective conductivity of the three-dimensional adsorbent 40 will be dominated by thermal interfacial resistance at nodes 44 formed at the intersection of connected individual elements 42. Small interfacial thermal resistance is likely to require strong bonding forces at the nodes 44 (e.g., covalent, ionic, or metallic bonds), which minimize the scattering of photons at those interfaces. Mechanisms to promote these nodes 44 may include introduction of metallic nanoparticles (which act as hubs connecting multiple tubes/wires), covalent bonding between individual elements (e.g., branching, covalently bonded CNT structures), or other similar mechanisms. Large specific surface areas of the three-dimensional adsorbent 40 may be derived from the large intrinsic specific surface areas of individual elements 42. Given that very little area is consumed by the nodes 44, the three-dimensional adsorbent 40 will, for the large part, maintain the specific surface area of the individual elements 42, which maximizes the area for gas or vapor molecules to adsorb to the adsorbent.
Composite materials, as described in the various embodiments of the present invention herein, are light-weight and have a high-thermally conductive. Generally, the high-dielectric porous backbone provides the desired high thermal conductivity while filler materials provide a large surface area, which promotes adsorbate interaction. By minimizing the thermal interfacial resistance between the backbone and the filler, heat transfer through the composite material is highly efficient.
The composite materials, according to the various embodiments of the present invention, may be utilized in improving systems configured to quickly absorb bursts of heat. That is, these composite materials, when used with suitable gas or vapor adsorbates, rapidly absorb large pulses of heat. In that regard, and with reference now to
The fraction of the adsorbate to be used during system operation is determined by minimum and operating pressures. Exemplary pressures for the adsorbate tank 52 may range from about 50 bar to 100 bar; however, these pressure ranges are not considered to be limiting. Ideally, the adsorbate may be stored in the liquid phase to minimize the overall volume of the system.
The adsorbate tank 52 is fluidically coupled to an adsorbent bed 58 containing a composite adsorbent 60 according to embodiments of the present invention. The adsorbent bed 58 is operable over a range of pressures, for example, pressures ranging from about 10 bar to 50 bar, or, as necessary, to atmospheric pressure; however, these pressure ranges are not considered to be limiting. In any event, the adsorbent bed 58 may generally be under a lower pressure after discharge and a higher pressure after recharged, as provided in detail below. In some embodiments, the adsorbent bed 58 may not be pressured over the condensation pressure of the adsorbent 60 as depressurization may lead to rapid expansion within the adsorbent bed 58, which is likely to irreversibly damage the adsorbent 60. Furthermore, the maximum pressure of the adsorbent bed 58 may be intrinsically linked to the minimum pressure of the storage tank 52, as the storage tank 52 is maintained at a higher pressure than the adsorbent bed 58 in order to effectively recharge the adsorbent 60.
In use, the system 50 is operable in an absorption mode, during which heat is absorbed from the heat load 56, and in a recharge mode, during which the system 50 prepares for subsequent heat absorption by transferring absorbed heat to a cooling loop 62 of, for example, a fuel tank (not shown). More specifically, and in the absorption mode illustrated in
Between heat burst generations, the system 50 is operated in a recharging mode to prepare for a subsequently generated heat burst. In that regard, the exhaust valve 64 is closed so that the adsorbent bed 58 may be re-pressurized from the adsorbate tank 52 via valve 66. Because adsorption is essentially the inverse process to desorption, some quantity of heat may be generated at the adsorbent bed 58, which must be rejected for the adsorption process to continue. However, generated heat is offset by the quantity of heat consumed by evaporating and/or decompressing adsorbate 54 from the tank 52. If the net effect is heat generation, the heat may be dissipated by some other element on the platform, including, for example, the cooling loop 62 of a fuel tank (not shown) or to the ambient environment by way of an air-heat exchanger. However, the rate of available heat rejection may limit the duty cycle of the system 50.
The skilled artisan will, with the benefit of the disclosure provided herein, note the particular benefit of a pressure cascade to store adsorbate gas/vapor, to control adsorption/desorption, and to regulate venting of the adsorbate 54.
The heat burst desorption system described according to the embodiments of the present invention herein may be configured to manage large thermal loads (about 100 kW to about 1 MW) with a rapid response time (less than about 1 second). Recharging capabilities are possible with a duty cycle of about 5% to about 50%, and, generally, the systems may be operational for extended periods of time, for example, missions ranging from 100 sec to 10,000 sec.
While the present invention has been illustrated by a description of various embodiments, and while these embodiments have been described in some detail, they are not intended to restrict or in any way limit the scope of the appended claims to such detail. Additional advantages and modifications will readily appear to those skilled in the art. The various features of the invention may be used alone or in any combination depending on the needs and preferences of the user. This has been a description of the present invention, along with methods of practicing the present invention as currently known. However, the invention itself should only be defined by the appended claims.
Claims
1. A composite adsorbent comprising:
- a backbone comprising a first material having a high thermal conductivity and having a plurality of pores therein; and
- a filler within pores of the plurality of the backbone and comprising a second material having a large specific surface area.
2. The composite adsorbent of claim 1, wherein the thermal conductivity of the first material comprising the backbone is greater than about 20 W/m·K.
3. The composite adsorbent of claim 1, wherein the specific surface area of the second material comprising the filler is greater than about 1000 m2/g.
4. The composite adsorbent of claim 1, wherein the first material comprising the backbone is a graphitic foam, an aluminum foam, a copper foam, a three-dimensional network of carbon nanotubes, a three-dimensional network of multi-walled carbon nanotubes, a three-dimensional network of metallic or semiconducting nanowires, grapheme, or a combination thereof.
5. The composite adsorbent of claim 1, wherein the second material comprising the filler is an aerogel or a cryogel.
6. The composite adsorbent of claim 1, wherein a surface of the first material comprising the backbone, a surface of the second material comprising the filler, or both is chemically modified.
7. The composite adsorbent of claim 6, wherein the chemical modification includes introduction of a polar ionic species.
8. The composite adsorbent of claim 1, wherein the second material comprising the filler comprises exfoliated outer layer of the first material comprising the backbone.
9. A heat burst desorption system for absorbing rapid heat bursts from a heat load, the system comprising:
- an adsorbent bed containing an adsorbent;
- an adsorbate supply containing an adsorbate, the adsorbate configured to adsorb onto a surface of the adsorbent with a large heat of adsorption;
- a first heat transfer path thermally coupling the adsorbent bed to the heat load; and
- a second heat transfer path thermally coupling the adsorbent supply to a cooling loop,
- wherein the system is operable in an absorption mode and recharge mode: (i) when the system is in the absorption mode, the adsorbent bed is fluidically coupled to an exhaust such that adsorbate desorbs from surface of the adsorbent and vented when heat is transferred on the first heat transfer path, and (ii) when the system is in the recharge mode, the adsorbent bed is fluidically coupled to the adsorbate supply such that adsorbate adsorbs onto the surface of the adsorbent and heat is transferred on the second heat transfer path.
10. A method of absorbing rapid heat bursts from a heat load, the method comprising:
- decompressing an adsorbent bed comprising an adsorbent when heat is generated by the heat load; and
- recharging the adsorbent bed with an adsorbate when heat generation ceases, the adsorbate configured to adsorb onto a surface of the adsorbent.
11. The method of claim 10, wherein the adsorbent is the composite adsorbent of claim 1.
12. The method of claim 10, wherein heat generated while recharging the adsorbent bed is rejected from the adsorbent bed.
13. The method of claim 12, wherein the rejected heat is transferred to a cooling loop.
14. A composite adsorbent comprising:
- a thermally-conductive backbone comprising a first material having a plurality of pores therein; and
- a filler within pores of the plurality of the backbone and comprising a second material having a large specific surface area.
15. The composite adsorbent of claim 14, wherein a thermal conductivity of the first material comprising the backbone is greater than about 20 W/m·K.
16. The composite adsorbent of claim 14, wherein the specific surface area of the second material comprising the filler is greater than about 1000 m2/g.
17-21. (canceled)
Type: Application
Filed: Oct 31, 2013
Publication Date: May 1, 2014
Applicant: Government of the United States as Represented by the Secretary of the Air Force (Wright-Patterson AFB, OH)
Inventors: Patrick J. Shamberger (Centerville, OH), Ajit Roy (Beavercreek, OH)
Application Number: 14/068,005
International Classification: F28D 17/02 (20060101); F28D 17/04 (20060101);