MULLITE-CONTAINING INVESTMENT CASTING CORE
An investment casting core includes a mullite-containing core body. The body can be made by providing a mullite-containing powder, forming the powder into a green body, and sintering the green body to form the mullite-containing core body.
Latest UNITED TECHNOLOGIES CORPORATION Patents:
This disclosure relates to investment casting and, more particularly, to investment casting cores.
Investment casting is known and used to cast metallic components with relatively complex geometries. For example, gas turbine engine components, such as airfoils that have internal passages, are made by investment casting. To form the internal passages or other relatively complex geometrical features, a core is provided which represents a positive projection of negative features that are to be formed in the casting process. A wax material is then provided around the core in the shape of the component to be cast. A shell is then formed around the wax and the wax is removed to form a cavity between the core and the surrounding shell into which molten metal is poured to form the shape of the component. After solidification of the metal, the core is removed using known techniques to provide the cast component.
SUMMARYAn investment casting core according to an exemplary aspect of the present disclosure includes a mullite-containing core body.
In a further non-limiting embodiment of any of the foregoing examples, the mullite-containing core body has, by weight, 40% or greater of mullite.
In a further non-limiting embodiment of any of the foregoing examples, the mullite-containing core body has, by weight, 40-90% of mullite.
In a further non-limiting embodiment of any of the foregoing examples, the mullite-containing core body has a material selected from the group consisting of alumina, silica, magnesia, yttria, calcia, zirconium silicate and combinations thereof.
In a further non-limiting embodiment of any of the foregoing examples, the mullite-containing core body has, by weight, 40-90% of mullite and 60-5% of silica.
In a further non-limiting embodiment of any of the foregoing examples, the mullite-containing core body has a material selected from the group consisting of magnesia, yttria, calcia and combinations thereof.
In a further non-limiting embodiment of any of the foregoing examples, the mullite-containing core body has zirconium silicate.
A further non-limiting embodiment of any of the foregoing examples includes a metallic core body joined to the mullite-containing core body.
In a further non-limiting embodiment of any of the foregoing examples, the metallic core body is selected from the group consisting of molybdenum, tungsten, tantalum, rhenium, niobium and combinations thereof.
In a further non-limiting embodiment of any of the foregoing examples, the mullite-containing core body has, by weight, 80-90% mullite, 15-5% silica, 2.5-10% alumina, 0-2.5% zircon, 0-5% of one or more of: calcia, magnesia and yttria.
In a further non-limiting embodiment of any of the foregoing examples, the mullite-containing core body has a multi-modal or bi-modal grain size distribution.
A method of making an investment casting core according to an exemplary aspect of the present disclosure includes providing a mullite-containing powder, forming the mullite-containing powder into a green body, and sintering the green body to form a mullite-containing core body.
A further non-limiting embodiment of any of the foregoing examples includes providing the mullite-containing powder in a blend with a binder, and the forming includes molding the blend into the green body.
In a further non-limiting embodiment of any of the foregoing examples, the mullite-containing powder has at least a bi-modal particle size distribution of mullite particles.
In a further non-limiting embodiment of any of the foregoing examples, the mullite-containing powder has a material selected from alumina, silica, magnesia, yttria, calcia, zirconium silicate and combinations thereof in a powder with at least a bi-modal particle size distribution.
A further non-limiting embodiment of any of the foregoing examples includes joining the mullite-containing core body to a metallic core body.
A further non-limiting embodiment of any of the foregoing examples includes selecting a composition of the mullite-containing powder to obtain a coefficient of thermal expansion in the mullite-containing core body that matches a coefficient of thermal expansion of the metallic core body.
A method of investment casting according to an exemplary aspect of the present disclosure includes casting a metallic component at least partially around an investment casting core that has a mullite-containing core body.
A further non-limiting embodiment of any of the foregoing examples includes the mullite-containing core body that has a material selected from the group consisting of alumina, silica, magnesia, yttria, calcia, zirconium silicate and combinations thereof.
A further non-limiting embodiment of any of the foregoing examples includes a metallic core body joined to the mullite-containing core body.
The various features and advantages of the present disclosure will become apparent to those skilled in the art from the following detailed description. The drawings that accompany the detailed description can be briefly described as follows.
The core 20 includes a mullite-containing core body 22. A “body” is a main or central foundational part, distinct from subordinate features, such as coatings or the like that are supported by the underlying body and depend primarily on the shape of the underlying body for their own shape.
In the investment casting of metallic components, such as from a superalloy material, the mechanical characteristics of a core influence the quality of the investment casting process and component. As an example, when molten metallic material is cast around a core, solidification of the metallic material exerts a force on the core. If the Young's Modulus is to high, the core will resist the solidification forces and may undesirably cause high internal stresses in the cast component or “hot tearing” of the component. In this regard, the mullite-containing core body 22 has a composition that provides “crushability” of the core 20 during investment casting. That is, the core 20 is tailored to “crush” under the solidification forces to reduce internal stresses and hot tearing.
In one example, the mullite-containing core body 22 has a composition that has, by weight, 40% or greater of mullite. In a further example, the mullite-containing core body 22 has, by weight, 40-90% of mullite.
In further examples, additional materials are used with the mullite to adjust a coefficient of thermal expansion (“CTE”) of the mullite-containing core body 22 and/or as processing aids. For example, the mullite-containing core body 22 has one or more materials selected from: alumina, silica, magnesia, yttria, calcia, zirconium silicate or combinations thereof. The alumina, silica, magnesia, yttria and calcia may be added to adjust the CTE. The yttria, calcia and zirconium silicate may be added as processing aids (yttria and calcia) to facilitate sintering when making the mullite-containing core body 22 or as grain growth inhibitors (zirconium silicate). In one further example, the mullite-containing core body 22 has, by weight, 40-90% of mullite and 60-5% silica. In further examples, the mullite-containing core body can also include up to 25% by weight of alumina, up to 5% by weight of magnesia, up to 5% by weight of yttria, up to 5% by weight of calcia and up to 10% by weight of zirconium silicate. Further, the mullite-containing core body 22 can have a grain size that has a grain size distribution that is equal to or approximately equal to a powder size distribution, such as a bi-modal or multi-modal particle size distribution as discussed below. This, the grain size distribution can be multi-modal or bi-modal.
The core 20 has a shape that corresponds to negative features that are to be formed in the investment cast component, such as gas turbine engine airfoils. In this regard, the illustrated core 20 has elongated limbs 24 and branches 26 that extend off of the limbs 24. It is to be understood, however, that the core 20 may alternatively have different geometries than shown, depending upon the features that are to be formed in the investment cast component.
In a further example, the core 20 can be a multi-material core that, in addition to the mullite-containing core body 22, also has a metallic core body 28 that is joined with the mullite-containing core body 22. For example, the metallic core body 28 is a refractory metal core. In one example, the refractory metal is selected from molybdenum, tungsten, tantalum, rhenium, niobium and combinations thereof.
The metallic core body 28 can be joined to the mullite-containing core body 22 using an adhesive material. For instance, the adhesive material is applied the joining surface of the mullite-containing core body 22, the metallic core body 28 or both in the form of slurry, such as a colloidal silica-based slurry. The colloidal silica based adhesive slurry will be comprised of materials of similar composition to the main core body: mullite, alumina, zirconia silicate to act as filler material as well as to ensure compatibility with the main body core. Upon drying of the slurry, the colloidal silica serves as a binder adhesive to secure the mullite-containing core body 22 and the metallic core body 28 together. Alternatively, other types of adhesives and ceramic materials could be used including adhesive systems based upon, ethyl silicate, sodium silicate, collidial alumina, colloidal yttria, colloidal zirconia.
The composition of the mullite-containing core body 22 can be tailored with regard to CTE to closely match the CTE of the metallic core body 28. For example, for the given refractory metals described above, mullite provides a relatively close match in CTE. The mullite composition can be modified with the alumina, silica, magnesia or combinations thereof to modify the CTE of the mullite-containing core body 22 in accordance with the CTE of the selected refractory metal of the metallic core body 28. In one example, the CTE of the mullite-containing core body 22 is within about 2% of the CTE of the metallic core body 28. The close match between the coefficients of thermal expansion provides a more durable joint with improved dimensional stability and thus the ability to achieve tighter tolerances and increased quality.
In a further example, step 32 includes providing the mullite-containing powder in a blend with a binder and then in step 34 molding the blend to form the green body. For example, the binder can be a thermoplastic material, a wax material or a wax material with viscosity modifiers, such as stearate. In one example, the blend includes approximately 10-20% by weight of the binder material and a remainder of the mullite-containing powder.
The composition of the mullite-containing powder can be tailored according to the desired composition of the mullite-containing core body 22. That is, the mullite-containing powder can include mullite powder and powders of any or all of the other above-described materials of alumina, silica, magnesia, yttria, calcia and zirconium silicate.
In a further example, the mullite-containing powder has at least a bi-modal particle size distribution. The bi-modal distribution provides a blend of coarse and fine particles that facilitate forming the green body with relatively large sections and also with relatively thin sections. That is, the multi-modal particle size distribution facilitates filling a mold to form a relatively complex green body shape. Powders of the added materials in addition to the mullite can also include a multi-modal particle size distribution for similar purposes. Given this description, one of ordinary skill in the art will be able to determine a bimodal or multi-modal distribution to meet their particular needs. As examples, multi-modal distributions are described in “Fitting Bimodal Particle Size Distribution Curves” J. M. Dallavalle et. al., Ind. Eng. Chem., 1951, 43 (6), pp 1377-1380, incorporated herein by reference, and Reed, James, Introduction to the principles of ceramic processing, New York, A Wiley-Interscience publication, 1995, also incorporated herein by reference.
As also shown in
Although a combination of features is shown in the illustrated examples, not all of them need to be combined to realize the benefits of various embodiments of this disclosure. In other words, a system designed according to an embodiment of this disclosure will not necessarily include all of the features shown in any one of the Figures or all of the portions schematically shown in the Figures. Moreover, selected features of one example embodiment may be combined with selected features of other example embodiments.
The preceding description is exemplary rather than limiting in nature. Variations and modifications to the disclosed examples may become apparent to those skilled in the art that do not necessarily depart from the essence of this disclosure. The scope of legal protection given to this disclosure can only be determined by studying the following claims.
Claims
1. An investment casting core comprising:
- a mullite-containing core body; and
- a metallic core body joined to the mullite-containing core body, and the mullite-containing core body has a coefficient of thermal expansion that is within 2% of a coefficient of thermal expansion of the metallic core body.
2. The investment casting core as recited in claim 1, wherein the mullite-containing core body has, by weight, 40% or greater of mullite.
3. The investment casting core as recited in claim 1, wherein the mullite-containing core body has, by weight, 40-90% of mullite.
4. The investment casting core as recited in claim 1, wherein the mullite-containing core body has a material selected from the group consisting of alumina, silica, magnesia, yttria, calcia, zirconium silicate and combinations thereof.
5. The investment casting core as recited in claim 1, wherein the mullite-containing core body has, by weight, 40-90% of mullite and 60-5% of silica.
6. The investment casting core as recited in claim 1, wherein the mullite-containing core body has a material selected from the group consisting of magnesia, yttria, calcia and combinations thereof.
7. The investment casting core as recited in claim 1, wherein the mullite-containing core body has zirconium silicate.
8. (canceled)
9. The investment casting core as recited in claim 1, wherein the metallic core body is selected from the group consisting of molybdenum, tungsten, tantalum, rhenium, niobium and combinations thereof.
10. The investment casting core as recited in claim 1, wherein the mullite-containing core body has, by weight, 80-90% mullite, 15-5% silica, 2.5-10% alumina, 0-2.5% zircon, 0-5% of one or more of: calcia, magnesia and yttria.
11. The investment casting core as recited in claim 1, wherein the mullite-containing core body has a multi-modal or bi-modal grain size distribution.
12. A method of making an investment casting core, the method comprising:
- providing a mullite-containing powder;
- forming the mullite-containing powder into a green body;
- sintering the green body to form a mullite-containing core body; and
- joining the mullite-containing core body to a metallic core body, and selecting a composition of the mullite-containing powder to obtain a coefficient of thermal expansion of the mullite-containing core body that matches a coefficient of thermal expansion of the metallic core body.
13. The method as recited in claim 12, including providing the mullite-containing powder in a blend with a binder, and the forming includes molding the blend into the green body.
14. The method as recited in claim 12, wherein the mullite-containing powder has at least a bi-modal particle size distribution of mullite particles.
15. The method as recited in claim 12, wherein the mullite-containing powder has a material selected from alumina, silica, magnesia, yttria, calcia, zirconium silicate and combinations thereof in a powder with at least a bi-modal particle size distribution.
16. (canceled)
17. (canceled)
18. A method of investment casting, the method comprising:
- casting a metallic component at least partially around an investment casting core that has a mullite-containing core body and a metallic core body joined to the mullite-containing core body. the mullite-containing core body having a coefficient of thermal expansion that is within 2% of a coefficient of thermal expansion of the metallic core body.
19. The method as recited in claim 18, wherein the mullite-containing core body has a material selected from the group consisting of alumina, silica, magnesia, yttria, calcia, zirconium silicate and combinations thereof.
20. The method as recited in claim 18, further comprising a metallic core body joined to the mullite-containing core body.
21. The investment casting core as recited in claim 1, wherein the mullite-containing core body includes yttria.
22. The investment casting core as recited in claim 1, wherein the mullite-containing core body includes calcia.
23. The method as recited in claim 18, wherein the mullite-containing core body includes yttria.
24. The method as recited in claim 18, wherein the mullite-containing core body includes calcia.
25. The method as recited in claim 12, wherein the mullite-containing core body includes yttria.
26. The method as recited in claim 12, wherein the mullite-containing core body includes calcia.
27. The investment casting core as recited in claim 1, wherein the metallic core body is adhesively joined to the mullite-containing core body.
Type: Application
Filed: Dec 28, 2012
Publication Date: Jul 3, 2014
Applicant: UNITED TECHNOLOGIES CORPORATION (Hartford, CT)
Inventor: Mario P. Bochiechio (Vernon, CT)
Application Number: 13/729,077
International Classification: B22C 1/00 (20060101); B22C 9/10 (20060101);