HIGHLY CORROSION-RESISTANT COPPER TUBE

A copper tube which can exhibit an improved resistance against ant nest corrosion, and which is suitably usable in air-conditioning equipment and refrigerating equipment, to advantageously extend a service life of the equipment produced by using the copper tube. The copper tube contains 0.05-1.0% by weight of P (phosphate) and the balance consisting of Cu (copper) and inevitable impurities.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description
CROSS REFERENCE TO RELATED APPLICATION

This application is a continuation of the International Application No. PCT/JP2014/052418 filed on Feb. 3, 2014, which claims the benefit under 35 U.S.C. §119(a)-(d) of Japanese Application No.2013-055963 filed on Mar. 19, 2013, the entireties of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a highly corrosion-resistant copper tube, and more particularly relates to a copper tube suitably usable as a heat transfer tube and a refrigerant tube in air-conditioning equipment and refrigerating equipment, for example.

2. Description of Related Art

A tube made of a phosphorous deoxidized copper (JIS-H3300-C1220T) having excellent properties in terms of corrosion resistance, brazability, heat conductivity and bending workability, for example, has been mainly used as the heat transfer tube in the air-conditioning equipment, the refrigerant tube in the refrigerating equipment and the like.

However, it is recognized that the above-described phosphorous deoxidized copper tube used in the air-conditioning equipment and the refrigerating equipment suffers from generation of so-called “ant nest corrosion” (or “formicary corrosion”) which is an unusual corrosion that progresses in the form of an ants' nest from the surface of the tube in a direction of its wall thickness. The ant nest corrosion is considered to be generated in a damp environment by a corrosive medium in the form of a lower carboxylic acid such as a formic acid and an acetic acid. Further, it is recognized that such corrosion is also generated in the presence of a chlorine-based organic solvent such as 1,1,1-trichloroethane, particular kinds of lubricating oil, and formaldehyde, for example. It is known that generation of the ant nest corrosion is particularly remarkable where the phosphorous deoxidized copper tube is used as a conduit in the air-conditioning equipment and the refrigerating equipment, which conduit is liable to dewing. Once the ant nest corrosion is generated, it progresses rapidly and penetrates through the wall of the copper tube in a short time, giving rise to a problem that the equipment becomes unworkable.

Under the above-described circumstances, JP-A-6-122932 proposes a corrosion-resistant high-strength copper tube, and discloses that resistance of the copper tube against the ant nest corrosion is improved since the copper tube contains 0.0025-0.01 wt % of phosphate (P) and the balance consisting of Cu and conventionally contained impurities, which copper tube may have an oxygen concentration not higher than 20 wtppm. Namely, based on the fact that generation of the ant nest corrosion is reduced in an oxygen-free copper tube having an extremely low P content, the P content of the copper tube proposed in the above-indicated publication is reduced as compared with that of the phosphorous deoxidized copper tube, so that the copper tube has a higher resistance against the ant nest corrosion than the phosphorous deoxidized copper tube.

However, the copper tube obtained by reducing the P content has not yet achieved a sufficiently high resistance against the ant nest corrosion which is comparable to that of the oxygen-free copper tube. Therefore, it is desired to develop a copper tube which can exhibit a higher resistance against the ant nest corrosion than the conventional copper tube, even in a severe corrosive environment.

SUMMARY OF THE INVENTION

The present invention was made in view of the background art described above. It is therefore an object of the invention to provide a copper tube which can exhibit a higher resistance against the ant nest corrosion, and which has an excellent anti-corrosion property and which is suitably usable in the air-conditioning equipment and the refrigerating equipment. Another object of the invention is to advantageously extend a service life of equipment produced by using such a copper tube.

The inventors of the present invention made intensive studies on the ant nest corrosion generated in the copper tube used in the air-conditioning equipment, the refrigerating equipment and the like, and found that the copper tube having a higher resistance against the ant nest corrosion can be practically and advantageously obtained by setting the P content of the copper tube to be higher than that of the conventional phosphorous deoxidized copper tube. The present invention was completed based on this finding.

Based on the above-described finding, the present invention provides a heat transfer tube used in a damp environment in air-conditioning equipment and exposed to a corrosive action caused by a corrosive medium consisting of a lower carboxylic acid, which corrosive action progresses in the form of an ants' nest from a surface of the heat transfer tube in a direction of its wall thickness, wherein the heat transfer tube is a highly corrosion-resistant copper tube having a high resistance against ant nest corrosion and comprising 0.10-1.0% by weight of P (phosphate) and the balance consisting of Cu and inevitable impurities. The present invention also provides a refrigerant tube used in a damp environment in refrigerating equipment and exposed to a corrosive action caused by a corrosive medium consisting of a lower carboxylic acid, which corrosive action progresses in the form of an ants' nest from a surface of the refrigerant tube in a direction of its wall thickness, wherein the refrigerant tube is a highly corrosion-resistant copper tube having a high resistance against ant nest corrosion and comprising 0.10-1.0% by weight of P and the balance consisting of Cu and inevitable impurities.

In the present invention, the P content of the highly corrosion-resistant copper tube is set within a range of 0.10-1.0% by weight, which P content is higher, by a predetermined amount, than that of the conventional phosphorous deoxidized copper tube, which is within a range of about 0.015-0.040% by weight. By using the above-described highly corrosion-resistant copper tube as the heat transfer tube for air-conditioning equipment and the refrigerant tube for refrigerating equipment, the resistance of the heat transfer tube against the ant nest corrosion and the resistance of the refrigerant tube against the ant nest corrosion are significantly improved. It is particularly surprising that the heat transfer tube and the refrigerant tube according to the present invention have a higher resistance against the ant nest corrosion than the conventional oxygen-free copper tube.

In a preferable form of each of the heat transfer tube for air-conditioning equipment and the refrigerant tube for refrigerating equipment according to the invention, each of the heat transfer tube and the refrigerant tube comprises not lower than 0.15% by weight of P.

In further preferable form of each of the heat transfer tube for air-conditioning equipment and the refrigerant tube for refrigerating equipment according to the invention, each of the heat transfer tube and the refrigerant tube comprises not higher than 0.8% by weight of P. In other preferable form of the heat transfer tube for air-conditioning equipment and the refrigerant tube for refrigerating equipment according to the invention, each of the heat transfer tube and the refrigerant tube comprises not higher than 0.5% by weight of P.

In still other preferable form of each of the heat transfer tube for air-conditioning equipment and the refrigerant tube for refrigerating equipment according to the invention, a total amount of the inevitable impurities is not higher than 0.05% by weight.

The present invention also provides a method for improving a corrosion resistance of a copper tube used in a damp environment in air-conditioning equipment or refrigerating equipment, against ant nest corrosion which is generated in the damp environment by a corrosive medium consisting of a lower carboxylic acid, and progresses from a surface of the copper tube, wherein the resistance of the copper tube against the ant nest corrosion is improved by forming the copper tube by using a material comprising 0.10-1.0% by weight of P and the balance consisting of Cu and inevitable impurities. In a preferable form of the method for improving the corrosion resistance of the copper tube according to the invention, the material of the copper tube comprises 0.3-1.0% by weight of P. In other preferable form of the method for improving the corrosion resistance of the copper tube according to the invention, a total amount of the inevitable impurities contained in the material of the copper tube is not higher than 0.05% by weight.

According to the present invention, the practical copper tube which is superior to the conventional copper tube in its anti-corrosion property in terms of the resistance against the ant nest corrosion can be provided. Further, by using the copper tube according to the present invention as the heat transfer tube in the air-conditioning equipment and the refrigerant tube in the refrigerating equipment, the service life of those equipment can be extended.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic cross sectional view showing an apparatus used for a corrosion resistance test in illustrated Examples; and

FIG. 2 is a graph showing a relationship between a P content of copper tubes obtained in the Examples and a maximum corrosion depth of those copper tubes.

DETAILED DESCRIPTION OF THE INVENTION

A highly corrosion-resistant copper tube according to the invention has a major characteristic that its phosphate (P) content is held within a range of 0.05-1.0% by weight and higher than that of the conventional copper tube. It is considered that owing to such a high P content, the type of corrosion generated in the copper tube shifts from a selective corrosion which progresses in a direction perpendicular to the axial direction of the copper tube (i.e., in a direction of the wall thickness of the copper tube) to a surface corrosion which progresses in a direction parallel to the axial direction of the copper tube (i.e., in a direction extending along the surface of the copper tube). In particular, by setting the P content of the copper tube so as to be not lower than 0.10% by weight, and preferably not lower than 0.15% by weight, generation of the selective corrosion is effectively reduced or prevented, and the copper tube can exhibit corrosion resistance which is considerably higher than that of the conventional copper tube.

Where the P content of the copper tube is as low as 0.05% by weight, the selective corrosion is generated, but a rate of progress of the selective corrosion in the copper tube can be effectively reduced as compared with that in the conventional copper tube, so that the copper tube is recognized to have a higher resistance against the ant nest corrosion. Therefore, the P content of the copper tube is set so as to be not lower than 0.05% by weight, in the present invention. On the other hand, the upper limit of the P content of the copper tube needs to be set at 1.0% by weight, since the P content higher than 1.0% by weight causes almost no change in the resistance of the copper tube against the ant nest corrosion, and even causes deterioration of workability of the copper tube during its production, giving rise to a problem of cracking of the copper tube, for example. From the standpoint of practical production of the copper tube, the P content of the copper tube is preferably set so as to be not higher than 0.8% by weight, and more preferably not higher than 0.5% by weight.

The highly corrosion-resistant copper tube according to the present invention is made of a material having the P content described above with the balance consisting of Cu (copper) and inevitable impurities. A total amount of the inevitable impurities such as Fe, Pb and Sn contained in the copper tube is generally controlled so as to be not higher than 0.05% by weight.

The intended copper tube is produced by using a Cu material having the above-described composition according to the invention, by a method similar to the conventional method. For example, the copper tube is produced by steps of casting an ingot or a billet, and extruding and drawing the ingot or billet. Dimensions such as the outside diameter and the wall thickness of the thus obtained copper tube are adequately determined depending on the intended application of the copper tube. Where the copper tube according to the invention is to be used as a heat transfer tube, the copper tube may have a smooth internal surface, or may advantageously have various kinds of internal grooves formed in its internal surface by various known processes, as is well known in the art.

EXAMPLES

To clarify the present invention more specifically, some examples according to the present invention will be described. It is to be understood that the invention is by no means limited by the details of the illustrated examples, but may be embodied with various changes, modifications and improvements which are not described herein, and which may occur to those skilled in the art, without departing from the spirit of the invention.

Initially, various kinds of copper tube having compositions including respective P contents indicated in Table 1 given below, with the balance consisting of Cu and inevitable impurities were produced as in production of the conventional copper tube, such that each copper tube has an outside diameter of 9.52 mm and a wall thickness of 0.41 mm. The thus produced copper tubes were subjected to an ant nest corrosion test, as described below. Further, a Cu material containing 1.5% by weight of P and the balance consisting of Cu and inevitable impurities was used to produce a copper tube having dimensions similar to those of the above-described copper tubes, but the intended copper tube could not be obtained due to cracking of the tube. A phosphorous deoxidized copper tube and an oxygen-free copper tube each having the same dimensions as those of the above-described copper tubes were provided as comparative copper tubes.

TABLE 1 Copper tube P content No. Kind of copper tube (% by weight) 1 Copper tube according to the invention 0.11 2 Copper tube according to the invention 0.19 3 Copper tube according to the invention 0.30 4 Copper tube according to the invention 0.40 5 Copper tube according to the invention 0.50 6 Copper tube according to the invention 1.00 7 Phosphorous deoxidized copper tube 0.03 8 Oxygen-free copper tube <0.004

Each of the thus provided various kinds of copper tube was subjected to the ant nest corrosion test by using a test apparatus shown in FIG. 1. A plastic container 2 shown in FIG. 1 has a capacity of 2 L and can be hermetically sealed with a cap 4. Silicone plugs 6 are attached to the cap 4 such that the plugs 6 extend through the cap 4. Copper tubes 10 to be subjected to the corrosion test were inserted into the plastic container 2 by a predetermined length, such that the copper tubes 10 extend through the respective silicone plugs 6. Lower open ends of the copper tubes 10 were dosed with silicone plugs 8. 100 mL of a formic acid aqueous solution having a predetermined concentration was accommodated in the plastic container 2, such that the copper tubes 10 do not contact with the aqueous solution.

The ant nest corrosion test was conducted by using three kinds of formic acid aqueous solutions 12 having respective concentrations of 0.01%, 0.1% and 1%. The copper tubes 10 were set with respect to each of the plastic containers 2 in which the respective formic acid aqueous solutions 12 were accommodated, and the plastic container 2 was left within a constant temperature bath at a temperature of 40° C. The plastic container 2 with the copper tubes 10 was taken out of the bath for two hours each day, and held at the room temperature (15° C.), to cause dewing on surfaces of the copper tubes 10 by the difference between the temperature of the constant temperature bath and the room temperature. The copper tubes 10 were subjected to the corrosion test under the above-described conditions for 20 days.

Each of the copper tubes subjected to the corrosion test using each of the formic acid aqueous solutions having the respective concentrations was examined in its cross section, and measured of its maximum corrosion depth. Results of the measurement are indicated in Table 2 given below. Further, a relationship between the maximum corrosion depth of the copper tubes subjected to the corrosion test using the 0.1% formic acid aqueous solution and the P content of the respective copper tubes is indicated in a graph of FIG. 2.

TABLE 2 Copper Maximum corrosion depth (mm) tube Formic acid Formic acid Formic acid No. concentration: 0.01% concentration: 0.1% concentration: 1% 1 0.10 0.25 2 0.06 0.11 0.12 3 0.08 0.04 0.08 4 0.04 0.05 0.07 5 0.03 0.04 0.10 6 <0.03 0.05 7 0.15 0.40 >0.40 8 0.05 0.30 >0.40

As is apparent from the results in Table 2, in the corrosion test conducted by using the formic acid aqueous solution having the concentration of 0.01%, the ant nest corrosion was not generated and only slight corrosion on the surfaces of the copper tubes was recognized in the copper tubes Nos. 1-6 having P contents within a range of 0.1-1.0% by weight, and the copper tube No. 8 which is the oxygen-free copper tube. On the other hand, in the corrosion test conducted by using the formic acid aqueous solutions having the respective concentrations of 0.1% and 1%, the ant nest corrosion was recognized in both of the copper tube No. 7 which is the phosphorous deoxidized copper tube, and the copper tube No. 8 which is the oxygen-free copper tube, and corrosion was recognized in the copper tubes Nos. 1-6 having the P contents within the range of 0.1-1.0% by weight. However, the corrosion generated in the copper tubes Nos. 1-6 was not the ant nest corrosion, and maximum corrosion depths of the copper tubes Nos. 1-6 are smaller than those of the phosphorous deoxidized copper tube and the oxygen-free copper tube.

Further, as indicated in FIG. 2, the copper tubes having P contents higher or lower than the P content of 0.03% by weight of the phosphorous deoxidized copper tube (No. 7) have smaller maximum corrosion depths than the phosphorous deoxidized copper tube (No. 7). It is particularly noted that the copper tubes (Nos. 1-6) according to the present invention having higher P contents than the phosphorous deoxidized copper tube (No. 7) are superior to the oxygen-free copper tube (No. 8) in their maximum corrosion depths.

Claims

1. A heat transfer tube used in a damp environment in air-conditioning equipment and exposed to a corrosive action caused by a corrosive medium consisting of a lower carboxylic acid, which corrosive action progresses in the form of an ants' nest from a surface of the heat transfer tube in a direction of its wall thickness, wherein the heat transfer tube is a highly corrosion-resistant copper tube having a high resistance against ant nest corrosion and comprising 0.10-1.0% by weight of P and the balance consisting of Cu and inevitable impurities.

2. The heat transfer tube according to claim 1, comprising not lower than 0.15% by weight of P.

3. The heat transfer tube according to claim 1, comprising not higher than 0.8% by weight of P.

4. The heat transfer tube according to claim 1, comprising not higher than 0.5% by weight of P.

5. The heat transfer tube according to claim 1, wherein a total amount of the inevitable impurities is not higher than 0.05% by weight.

6. A refrigerant tube used in a damp environment in refrigerating equipment and exposed to a corrosive action caused by a corrosive medium consisting of a lower carboxylic acid, which corrosive action progresses in the form of an ants' nest from a surface of the refrigerant tube in a direction of its wall thickness, wherein the refrigerant tube is a highly corrosion-resistant copper tube having a high resistance against ant nest corrosion and comprising 0.10-1.0% by weight of P and the balance consisting of Cu and inevitable impurities.

7. The refrigerant tube according to claim 6, comprising not lower than 0.15% by weight of P.

8. The refrigerant tube according to claim 6, comprising not higher than 0.8% by weight of P.

9. The refrigerant tube according to claim 6, comprising not higher than 0.5% by weight of P.

10. The refrigerant tube according to claim 6, wherein a total amount of the inevitable impurities is not higher than 0.05% by weight.

11. A method for improving a corrosion resistance of a copper tube used in a damp environment in air-conditioning equipment or refrigerating equipment, against ant nest corrosion which is generated in the damp environment by a corrosive medium consisting of a lower carboxylic acid, and progresses from a surface of the copper tube, wherein the resistance of the copper tube against the ant nest corrosion is improved by forming the copper tube by using a material comprising 0.10-1.0% by weight of P and the balance consisting of Cu and inevitable impurities.

12. The method for improving the corrosion resistance of the copper tube according to claim 11, wherein the material of the copper tube comprises 0.3-1.0% by weight of P.

13. The method for improving the corrosion resistance of the copper tube according to claim 11, wherein a total amount of the inevitable impurities contained in the material of the copper tube is not higher than 0.05% by weight.

Patent History
Publication number: 20150377568
Type: Application
Filed: Sep 10, 2015
Publication Date: Dec 31, 2015
Inventors: Kozo KAWANO (Nagoya-Shi), Shinobu SUZUKI (Nagoya-Shi)
Application Number: 14/849,955
Classifications
International Classification: F28F 21/08 (20060101); F28F 1/00 (20060101);