SLIDING RESIN COMPOSITION, AND SLIDING MEMBER
A resin composition used for a sliding member to improve seizing resistance. The sliding resin composition includes: a resin binder; a solid lubricant; and aggregates of particles. A coupling force between the particles in the aggregates is smaller than a threshold stress of the resin binder so that the aggregates exposed at a surface of the resin binder are partially detached with a force smaller than the threshold stress of the resin binder. The aggregates of the particles harder than the resin binder are used as a protecting and reinforcing agent, and the amount of the particles contained in the sliding resin composition is 1 vol. % or more but 20 vol. % or less of the entire sliding resin composition. The particles harder than the resin binder have an average particle diameter of between 10 nm and 100 nm that is smaller than that of the solid lubricant.
The present invention relates to a sliding resin composition and improvement of a sliding member using the composition.
BACKGROUND ARTThe sliding surface of a bearing applied to the engine of a vehicle is required to have high abrasion resistance and seizing resistance. As one of solutions to this requirement, a technique has been proposed in which the sliding surface of a bearing is coated with a resin composition (see Patent Documents 1 and 2).
In this technique disclosed in these prior art literatures, a layer of a resin composition is formed by coating the inner peripheral surface (sliding surface) of a semi-cylindrical base material layer with the resin composition.
Such a sliding resin composition (hereinafter, sometimes simply referred to as “resin composition”) contains a resin binder, a solid lubricant, and protecting and reinforcing particles. When a load is applied to the resin composition, the solid lubricant itself is deformed (e.g., cleaved), more specifically, slip occurs between its crystal planes so that the stress of the resin composition is relaxed (Patent Document 1). On the other hand, for example, nano-ordered silica particles (20 to 50 nm in diameter) are used as the protecting and reinforcing particles to improve the abrasion resistance of the entire resin composition (Patent Document 2).
Refer to Patent Documents 3 to 5 as other prior art literatures that disclose techniques relating to the present invention.
CITATIONS LISTPatent Document 1: JP 2013-72535 A
Patent Document 2: JP 2007-517165 A
Patent Document 3: JP 2006-116458 A
Patent Document 4: JP 2007-92995 A
Patent Document 5: JP 2008-95725 A
SUMMARY OF INVENTION Technical ProblemsCurrent car engines tend to frequently repeat start and stop to improve fuel efficiency. Further, the viscosity of engine oil has been reduced to reduce the shear resistance of the oil. In the case of such an engine, an oil film between a shaft and a bearing tends to be insufficient so that sliding under boundary lubrication conditions often occurs. As a result, the friction coefficient during sliding increases so that a load applied to a resin composition layer that is in contact with the shaft in the bearing increases.
When a load applied to the resin composition layer increases, there is a possibility that the resin composition layer is deformed beyond its limitation so that a resin composition itself is broken or a resin composition is separated from a base material. As a result, solid contact occurs between the base material (alloy layer) of the bearing and the shaft so that welding occurs between the base material of the bearing and the shaft due to excessive heat generation, which may cause seizing.
The techniques disclosed in Patent Documents 1 and 2 are intended to improve the resin composition layer to improve seizing resistance.
However, the resin composition layer of the bearing is required to have higher seizing resistance for the following reasons.
In recent years, diesel engines for heavy trucks and the like as well as gasoline engines have also been required to frequently repeat start and stop to achieve lower fuel consumption. As compared to a bearing for gasoline engine, a heavier specific load is applied to a bearing for diesel engine at a lower peripheral speed, which makes it more difficult to maintain an oil film between a shaft and the bearing. Further, a vehicle with a diesel engine generally travels a longer distance between maintenances than a vehicle with a gasoline engine, which increases the possibility of entry of foreign dirt into between a shaft and a bearing. This also makes it difficult to maintain an oil film. Further, a cast iron shaft having a rougher surface than a conventional one has used to reduce the cost of the shaft, which also makes it difficult to maintain an oil film.
A heavy load is applied to a bearing for diesel engine, and therefore a resin composition constituting the sliding surface of the bearing is, of course, required to have high abrasion resistance.
Solutions to ProblemsIn order to solve such a problem, it is an object of the present invention to provide a resin composition to be used for, for example, a bearing for a vehicle engine to improve its seizing resistance.
In order to achieve the above object, a first aspect of the present invention provides a sliding resin composition, comprising:
a resin binder; a solid lubricant; and a protecting and reinforcing agent, wherein
the protecting and reinforcing agent comprises aggregates of particles, and wherein
a coupling force between the particles in the aggregates is smaller than a threshold stress of the resin binder so that the aggregates exposed at the surface of the resin binder are partially detached by a force smaller than the threshold stress of the resin binder.
As for the thus defined sliding resin composition according to the first aspect, when a load applied to the aggregates exposed at a sliding surface of the resin composition is larger than the coupling force between the particles constituting the aggregates but is smaller than the threshold stress of the resin binder, the aggregates are partially disintegrated and detached while the shape of the resin binder is maintained so that minute recesses are formed in the sliding surface. The recesses serve as lubricant oil retaining parts that contribute to maintaining an oil film on the sliding surface. This improves seizing resistance.
The threshold stress described above refers to the maximum stress that, when a load is applied to each component of the resin composition, each component can withstand without plastic deformation or breakage. When having a smaller threshold stress, each component is more easily disintegrated and is brittler.
It is considered that the particles are aggregated in a manner that high-order particles (secondary or higher particles) are formed by, for example, directly coupling single particles (i.e., primary particles) to form secondary particles and further coupling the secondary particles to form tertiary particles, or in a manner that primary particles are coupled by the resin binder, or in a manner that coupling of primary particles is supported by the resin binder.
When a load applied to the aggregates exposed at the sliding surface of the resin composition exceeds a threshold stress of the aggregates so that coupling between the particles is broken, minute recesses are formed in the sliding surface. The recesses serve as lubricant oil retaining parts that contribute to maintaining an oil film on the sliding surface.
Further, when a load is applied to the aggregates, the aggregates are deformed due to the occurrence of slip between the particles before the resin binder is deformed, and finally the aggregates are disintegrated. In other words, when a load applied to the resin composition exceeds the threshold stress of the aggregates, slip irreversibly occurs between the particles constituting the aggregates, and when the slip further increases, the aggregates themselves are disintegrated so that some of the particles coupled to form the aggregates are detached. The threshold stress of the aggregates is set to be smaller than that of the resin binder, which makes it possible to relax the stress of the resin binder.
According to a second aspect of the present invention, the particles constituting the aggregates may be harder than the resin binder. This allows the entire sliding resin composition to have high abrasion resistance. Hereinafter, the particles that constitute the aggregates and are harder than the resin binder are sometimes referred to as “protecting and reinforcing primary particles”.
The hardness of each component serves as an indicator of abrasion resistance, and can be expressed as, for example, Vickers hardness.
The hardness of the protecting and reinforcing primary particles is 10 to 100 times higher than that of the resin binder in terms of Vickers hardness.
The solid lubricant contained in the resin composition reduces the friction coefficient of the surface of the resin composition to improve the slip properties thereof. In general, molybdenum disulfide, tungsten disulfide, boron nitride, graphite, or the like is used as the solid lubricant. All these materials are softer (smaller hardness) and brittler (smaller threshold stress) than the resin binder.
According to a third aspect of the present invention, the threshold stress of each of the three components constituting the resin composition, that is, the resin binder, the solid lubricant, and the protecting and reinforcing agent is defined as follows.
-
- Solid lubricant≦Protecting and reinforcing agent<Resin binder
As for the thus defined resin composition according to the third aspect, when a heavy load is applied to the resin composition, the solid lubricant and the protecting and reinforcing agent are deformed or disintegrated before the resin binder is deformed because the solid lubricant and the protecting and reinforcing agent are brittler than the resin binder. Therefore, the stress of the resin binder is relaxed, and as a result, the shape of the resin binder, which can be said to be the skeleton of the sliding resin composition, is maintained.
The amount of the particles constituting the aggregates and contained in the resin composition is 1 vol. % or more but 20 vol. % or less of the entire resin composition. When the amount of the particles contained is 1 vol. % or more of the entire resin composition, the amount of the aggregates exposed at the sliding surface is sufficient so that lubricant oil retaining parts can be sufficiently formed. When the particles are harder than the resin binder to improve the abrasion resistance of the resin composition, the abrasion resistance of the resin composition can be sufficiently improved. On the other hand, when the amount of the particles contained is 20 vol. % or less of the entire resin composition, the viscosity of the resin binder is suitable for production.
The particles to be aggregated have a smaller diameter than the solid lubricant. Here, the diameter of the particles and the diameter of the solid lubricant are referred to as diameters in a measured view, and the diameters of all the particles are substantially smaller than the diameters of all the particles of the solid lubricant. For example, the particles and the solid lubricant appearing in the cross-section of the sliding resin composition perpendicular to the sliding surface of the sliding resin composition may be approximated by ellipses. In this case, the long axis of the ellipses is defined as a particle diameter. If the diameter of the particles is larger than that of the solid lubricant, the aggregates of the particles have a larger diameter, and therefore it may inhibit the function of the solid lubricant.
Based on the above, a fourth aspect of the present invention is defined as follows.
In the resin composition according to any one of the above first to third aspects, the protecting and reinforcing agent includes aggregates of particles that are harder than the resin binder and have a smaller diameter than the solid lubricant, and occupies 1 vol. % or more but 20 vol. % or less of the entire sliding resin composition.
It is to be noted that the amount of the protecting and reinforcing agent contained (vol. %=volume %) can be determined not only by comparison of the volumes of raw materials but also by ICP chemical analysis of a bulk of the resin composition.
A fifth aspect of the present invention is defined as follows.
In the resin composition according to the fourth aspect, the particles have an average particle diameter of 10 nm or more but 100 nm or less.
As for the thus defined resin composition according to the fifth aspect, when the particles having an average particle diameter of 10 nm or more but 100 nm or less are used, the single particles (i.e., primary particles) are easily aggregated together in the resin composition.
The particle diameter of the primary particles can be defined, for example, as follows. The primary particles appearing in the cross-section of the sliding resin composition perpendicular to the sliding surface of the sliding resin composition are approximated by ellipses, and the long axis of the ellipses is defined as a particle diameter.
When the amount of the particles is set to a value within the above range and the average particle diameter of the particles is set to 10 nm or more, it is possible to prevent excessive aggregation of the particles contained in the resin composition. If the average particle diameter is less than 10 nm, there is a fear that excessive aggregation of the particles occurs. If excessive aggregation of the particles occurs, an area where the aggregates are absent increases in the resin composition, and therefore the resin composition may not be sufficiently improved by the aggregates.
Further, when the amount of the particles contained is set to a value within the above range and the average particle diameter of the particles is set to 100 nm or less, appropriate aggregates can be reliably formed without excessive dispersion of the particles. On the other hand, if the average particle diameter exceeds 100 nm, the particles may be excessively dispersed singly in the resin composition. In this case, it also may cause the aggregates do not sufficiently perform their desired function of maintaining the lubricity of the sliding surface by partially detaching the aggregates exposed at the sliding surface to form recesses that serve as lubricant oil retaining parts.
When the aggregates of the particles are appropriately deformed or disintegrated, accumulation of stress in the resin binder can be efficiently prevented, and therefore the resin binder is not significantly broken at once. As a result, the seizing resistance of the resin composition is improved.
From another viewpoint, the average particle diameter of the particles that should be aggregated to form aggregates may be 15 nm or more but 50 nm or less.
A sixth aspect of the present invention is defined as follows.
In the sliding resin composition according to the fifth aspect, when the average particle diameter of the aggregates of the protecting and reinforcing primary particles is defined as A and a standard deviation of the average particle diameter is defined as σ, A−1σ is 60 nm or more and A+1σ is 400 nm or less.
The shape of the aggregates is not limited to a sphere. Therefore, in this description, the diameter of the aggregates appearing in a measured view in a cutting surface obtained by cutting the sliding resin composition in a direction perpendicular to the sliding surface of the sliding resin composition is used. More specifically, the aggregates observed are approximated by ellipses, and the long axis of the ellipses is defined as the diameter of the aggregates. A heavier load is applied to the sliding resin composition in a direction perpendicular to the sliding surface of the sliding resin composition. This is the reason why the cutting surface perpendicular to the sliding surface is defined as a measured view. Further, the width of the aggregates subjected to a load in the perpendicular direction (=the length of the aggregates projected onto the sliding surface) significantly relates to the threshold stress of the aggregates. This is the reason why the long axis of approximate ellipses of the aggregates is defined as the diameter of the aggregates.
As for the thus defined sliding resin composition according to the sixth aspect, the aggregates have an appropriate size, and are therefore evenly dispersed in the resin composition. This allows the aggregates to be evenly exposed at the sliding surface of the resin composition. Therefore, when a load is applied to the resin composition, the exposed aggregates are partially disintegrated to form lubricant oil retaining parts.
When the A−1σ is 60 nm or more, the degree of aggregation of the particles in the resin composition is sufficient. Therefore, when some of the aggregates are exposed at the sliding surface of the resin composition, the areas of exposed portions of the aggregates are enough to form lubricant oil retaining parts. When the A+1σ is 400 nm or less, the degree of dispersion of the aggregates of the particles is sufficient, and therefore there is no region where the aggregates are unevenly distributed in the sliding surface of the resin composition.
As a result, lubricant oil retaining parts can be evenly distributed in the entire sliding surface of the resin composition.
A seventh aspect of the present invention is defined as follows.
In the sliding resin composition according to any one of the first to sixth aspects, the aggregates have an aspect ratio of 10 or less.
The aspect ratio of the aggregates is defined as follows. The aggregates appearing in a measured view in a cutting surface obtained by cutting the sliding resin composition in a direction perpendicular to the sliding surface of the sliding resin composition are approximated by ellipses, and the ratio between the long axis and the short axis of the ellipses is defined as an aspect ratio (long axis/short axis).
When the aspect ratio of the aggregates is 10 or less, in other words, when the shape of the aggregates is closer to a sphere, the area of the aggregates exposed at the sliding surface of the resin composition is stable. A general aggregate is approximated by an ellipse. Therefore, when the aggregates have an aspect ratio of 10 or less, the area of the aggregates appearing in the sliding surface of the resin composition is stable irrespective of the orientation of long axis of the aggregates.
This sliding member 1 has a structure in which a resin coating layer 7 including a sliding resin composition is laminated on a base material layer 2.
In the sliding member 1 including a cylindrical or semi-cylindrical bearing, the base material layer 2 thereof includes a cylindrical or semi-cylindrical steel plate layer 3. If necessary, an alloy layer 5 made of an alloy of Al, Cu, Sn, or the like is provided on the surface (inner peripheral surface) of the steel plate layer 3. Although not shown, the base material layer 2 may be one having, on the surface of the alloy layer 5, a Sn-, Bi-, or Pb-group plating layer or a layer having a resin. The layer having a resin is different from the resin coating layer 7.
In order to improve adhesion between the base material layer 2 and the resin coating layer 7, the inner peripheral surface of the base material layer 2 may be subjected to surface roughening. The surface roughening may be performed by chemical surface treatment such as combination of alkaline etching and pickling or mechanical surface treatment such as shot blasting.
The constituent material of the steel plate layer 3 is not limited to steel, and may be, for example, an alloy of aluminum, copper, and tungsten.
The sliding resin composition constituting the resin coating layer 7 includes a resin binder 10, a solid lubricant 11, and aggregates 20 of protecting and reinforcing primary particles 13.
In the resin composition, the resin binder 10 binds the resin coating layer 7 to the base material layer 2 and fixes the solid lubricant 11. A resin material used for the resin binder 10 may be appropriately selected depending on, for example, the intended use of the sliding member 1. When the sliding member 1 is used for vehicle engines, the resin material may be at least one of polyimide resins, polyamideimide resins, epoxy resins, phenol resins, polyamide resins, fluorine resins, and elastomers, and may be a polymer alloy.
The thickness of the resin coating layer 7 may be arbitrarily designed, and may be, for example, 1 μm or more but 20 μm or less.
A method for laminating the resin coating layer 7 may also be arbitrarily selected. Examples of the method to be used include pad printing, screen printing, air spray painting, airless spray painting, electrostatic painting, tumbling, squeezing, rolling, and roll coating.
The material of the solid lubricant 11 may also be appropriately selected depending on the intended use of the sliding member. For example, the material of the solid lubricant 11 may be at least one selected from molybdenum disulfide, tungsten disulfide, h-boron nitride, polytetrafluoroethylene, melamine cyanurate, carbon fluoride, phthalocyanine, graphene nanoplatelets, fullerene, ultrahigh molecular weight polyethylene (manufactured by Mitsui Chemicals, Inc. under the trade name of “MIPELON”), and Nε-lauroyl-L-lysine (manufactured by Ajinomoto Co., Inc. under the trade name of “AMIHOPE”).
The amount of the solid lubricant 11 contained in the resin composition may be arbitrarily selected depending on the intended use of the sliding member. For example, when the amount of the entire resin composition constituting the resin coating layer 7 is defined as 100 vol. %, the amount of the solid lubricant 11 contained in the resin composition may be 20 vol. % or more but 70 vol. % or less.
In order to improve the slip properties of the resin coating layer 7, the (0, 0, L) plane orientation intensity ratio of the solid lubricant 11 is preferably 75% or more.
As shown in
The abrasion resistance of the resin coating layer 7 itself is improved by using, as the protecting and reinforcing primary particles 13, ultrafine particles that are harder than the material of the resin binder 10 and have a smaller diameter than the solid lubricant 11, preferably, a nano-order diameter (see Patent Document 2).
In order to directly achieve such a purpose, the protecting and reinforcing primary particles 13 are preferably dispersed more evenly in the resin coating layer 7. More specifically, it is preferred that the protecting and reinforcing primary particles 13 be dispersed without coupling together as much as possible, that is, the protecting and reinforcing primary particles 13 be dispersed as primary particles.
However, as a result of study by the present inventors, when a heavy load is applied to the resin coating layer 7, as shown in
On the other hand, according to this invention, as shown in
Therefore, when a heavy load is applied to the resin coating layer 7, part of stress generated in the resin coating layer 7 is relaxed by deformation or disintegration of the aggregates 20, which prevents the resin coating layer 7 from being significantly broken at once.
At this time, as shown in
From the viewpoint of improving the abrasion resistance of the resin coating layer 7 itself, the constituent material of the protecting and reinforcing primary particles 13 is harder than the resin binder 10 and has a smaller diameter than the solid lubricant. The constituent material of the protecting and reinforcing primary particles 13 may be arbitrarily selected depending on the intended use of the sliding member, and more specifically, may be, for example, microparticles of gold, silver, silicon oxide (silica), aluminum oxide, zinc oxide, tin oxide, or zirconium oxide.
For the purpose of forming lubricant oil retaining parts shown in
The protecting and reinforcing primary particles 13 may have an average particle diameter of 10 nm or more but 100 nm or less.
The average particle diameter of the protecting and reinforcing primary particles 13 can, of course, be determined from the specifications of raw material particles, but can also be determined in the following manner even in a state where the protecting and reinforcing primary particles 13 are contained in the resin coating layer 7. More specifically, for example, the resin coating layer is cut in an axial direction perpendicular to the sliding surface of the resin coating layer to obtain a cutting surface, and an image of a predetermined range of any portion in the cutting surface of the resin coating layer (hereinafter, sometimes referred to as “axial-direction cutting surface”) is taken. The thus obtained image is analyzed by image analysis software to approximate the primary particles in the image by ellipses (particle-equivalent ellipses). In this analysis software, an ellipse having the same area and primary and secondary moments as those of a target object (primary particle) is defined as the particle-equivalent ellipse.
Such protecting and reinforcing primary particles can be formed by, for example, a crushing method using a ball mill, a jet mill, or the like, an aggregation method (reductive method) including aggregation caused by reduction using a reducing agent or by electrochemical reduction, a pyrolysis method including thermal decomposition, a physical vapor deposition method such as evaporation in plasma gas, a laser vaporization method including rapid laser vaporization, or a chemical vapor deposition method comprising a chemical reaction in a vapor phase. A reaction field for production of the protecting and reinforcing particles may be either a gas phase or a liquid phase.
When the amount of the entire resin composition constituting the resin coating layer 7 is defined as 100 vol. %, the amount of the protecting and reinforcing primary particles 13 contained in the resin composition, that is, the amount of the aggregates 20 contained in the resin composition may be 1 vol. % or more but 20 vol. % or less.
This makes it possible to evenly form lubricant oil retaining parts in the sliding surface of the resin composition and to control the viscosity of the resin composition to be suitable for production.
When the average particle diameter of the obtained aggregates is defined as A and the standard deviation of the average particle diameter is defined as σ, A−1σ is 60 nm or more and A+1σ is 400 nm or less.
The average particle diameter of the aggregates can be determined by the same method as used for the protecting and reinforcing primary particles.
The size of the aggregates can be adjusted by appropriately adjusting the method of surface treatment of the protecting and reinforcing primary particles and the degree of surface treatment, the type of dispersion medium for dispersing the protecting and reinforcing primary particles and the viscosity of the dispersion medium, and the concentration of the primary particles in the dispersion medium, and further homogenizing this dispersion system.
The aggregates 20 have an aspect ratio of 10 or less. Here, the aspect ratio of the aggregates 20 can be determined by the same image processing as used for the protecting and reinforcing primary particles.
The aspect ratio can be adjusted by adjusting energy added when the protecting and reinforcing primary particles are dispersed in a solvent. For example, when a bead mill is used as a dispersion device, aggregates having a smaller aspect ratio are formed by reducing the rotation speed of the bead mill to reduce energy added to the particles.
On the other hand, as shown in
From the viewpoint of improving the abrasion resistance of the resin composition constituting the resin coating layer 7, hard particles that form substantially no aggregates may be added to the resin composition.
Such hard particles preferably have a size larger than 100 nm. Examples of the material of the hard particles include oxides such as aluminum oxide, chromium oxide, cerium oxide, zirconium oxide, titanium oxide, silicon oxide, and magnesium oxide, nitrides such as silicon nitride and cubic boron nitride, carbides such as silicon carbide, and diamond. When the amount of the entire resin composition constituting the resin coating layer 7 is defined as 100 vol. %, the amount of the hard particles contained in the resin composition may be 1 vol. % or more but 5 vol. % or less. When the material of the hard particles is different from that of the protecting and reinforcing particles, the properties of the resin coating layer 7 can be easily controlled. When the hard particles are made of the same material as the protecting and reinforcing particles, the sliding member can be inexpensively produced.
When the amount of the entire resin composition is defined as 100 vol. %, metal particles of Sn, Bi, Pb, In, or the like may be added in an amount of 1 vol. % or more but 5 vol. % or less.
Hereinbelow, a method for producing the sliding member 1 will be described.
In this embodiment, a solution is prepared by dissolving the resin binder in a solvent, and another solution is prepared by dispersing the protecting and reinforcing primary particles in the solvent. When the protecting and reinforcing primary particles are mixed to prepare the latter, energy required for mixing (e.g., the rotation speed of a mixing blade) is adjusted to adjust the shape, that is, the aspect ratio of the aggregates. The above two solutions are mixed together, and the solid lubricant and an additive used depending on the intended use are mixed therewith to prepare a coating liquid. If necessary, the amount of the solvent is controlled to adjust the viscosity of the coating liquid to be within a preferred range. Then, the coating liquid is applied onto the base material layer 2. Then, the coating liquid is allowed to stand for a predetermined time (leveling step), and is then subjected to a drying step to remove the solvent therefrom by heating so as to be cured to form the resin coating layer 7 including the sliding resin composition.
EXAMPLESHereinbelow, the present invention will be described with reference to the following examples suitable for a semi-cylindrical sliding member.
An aluminum bearing alloy layer was pressure-welded to the surface of a back metal layer formed from a semi-cylindrical steel member. Finishing for bearing inner surface is performed on the inner peripheral surface of the alloy layer, and then degreasing and removal of foreigndirt were performed.
Then, surface roughening treatment was performed by shot blasting.
Onto the inner peripheral surface of this intermediate, a coating liquid containing aggregates having a controlled aspect ratio was applied by spraying so as to have a thickness of about 5 μm. Then, the coating liquid was subjected to a leveling step for a predetermined time and a drying step, and was then subjected to a curing step at 200° C. to 300° C. for 30 min to 120 min. In this way, a sliding member (bearing) was produced which had a resin coating layer 7 including a resin composition of each of Examples and Comparative Examples shown in Table 1.
The thus obtained sliding members (bearings) were subjected to a seizing test under the following conditions.
- Rotation speed: 1500 rpm
- Lubricant oil: VG22
- Oil supply rate: 150 mL/min
- Material of shaft: S55C
A specific load was increased step by step to determine a specific load for seizing.
The results are shown in Table 1.
The content of each component (vol. %), the diameter of protecting and reinforcing primary particles, the size of aggregates, and the aspect ratio of aggregates shown in Table 1 were determined by observing the axial-direction cutting surface of each of the resin coating layers 7. More specifically, an image of an arbitrary portion (with a certain area) in the cutting surface was taken, and the obtained image was analyzed with image analysis software (Image-pro plus ver. 4.5) to calculate each of these values.
The following can be seen from the results shown in Table 1.
In each of the resin coating layers 7 of Examples 1 to 15, aggregates 20 of protecting and reinforcing primary particles were dispersed in a resin binder 10, and some of the aggregates 20 were exposed at the sliding surface of the resin coating layer 7. In Comparative Example 1, aggregates 20 were not formed.
Example 14 and Example 15 of Group I do not satisfy the requirement “(1) the amount of the protecting and reinforcing primary particles contained in the resin composition is 1 vol. % or more but 20 vol. % or less of the entire resin composition”, and therefore the specific loads for seizing thereof are higher than that of Comparative Example 1, but are relatively lower than those of Examples of other groups.
Example 12 and Example 13 of Group II satisfy the requirement “(1) the amount of the protecting and reinforcing primary particles contained in the resin composition is 1 vol. % or more but 20 vol. % or less of the entire resin composition”, and therefore the specific loads for seizing thereof are higher than those of Examples of Group I.
Examples 6 to 11 of Group III satisfy the requirement “(1) the amount of the protecting and reinforcing primary particles contained in the resin composition is 1 vol. % or more but 20 vol. % or less of the entire resin composition” and the requirement “(2) the average particle diameter of the protecting and reinforcing primary particles is 10 nm or more but 100 nm or less”, and therefore the specific loads for seizing thereof are higher than those of Example 12 and Example 13 of Group II.
Example 5 of Group W satisfies the above requirements (1) and (2) and the requirement “(3) the size A−1σ of the aggregates is 60 nm or more and the size A+1σ of the aggregates is 400 nm or less”, and therefore the specific load for seizing thereof is higher than those of Examples 6 to 11 of Group III.
Examples 1 to 4 of Group V satisfy the above requirements (1) to (3) and the requirement “(4) the aspect ratio of the aggregates is 10 or less”, and therefore the specific load for seizing thereof is higher than that of Example 5 of Group IV.
According to study by the present inventors, one or two or more of the following properties of the resin composition has/have an influence on the seizing resistance of the resin composition.
(1) Tilt Angle of Long Axis of Aggregates
When the aggregates are used as protecting and reinforcing particles, the angle between the long axis of the aggregates and the sliding surface is 45 degrees or less.
Here, the long axis of the aggregates refer to the long axis of the aggregates appearing in a measured view in a cutting surface obtained by cutting the sliding resin composition in a direction perpendicular to the sliding surface of the sliding resin composition. For example, the observed aggregates are approximated by ellipses, and the long axis of the ellipses is defined as the long axis of the aggregates.
It is to be noted that the angles of long axes of all the aggregates are not always the same, and therefore the average of the angles of long axes of the aggregates observed in the cutting surface is set to the 45 degrees or less.
When the angle between the long axis of the aggregates and the sliding surface is 45 degrees or less, in other words, when the long axis of the aggregates is closer to parallel to the sliding surface, the aggregates reliably receive a load applied in a direction perpendicular to the sliding surface, and the load acts as a shearing force in a short axis direction so that the aggregates are more reliably deformed or disintegrated.
Further, when the long axis of the aggregates is closer to parallel to the sliding surface, the aggregate is more largely exposed at the sliding surface. This makes it easy to partially detach the exposed sliding body to form micro recesses that serve as lubricant oil retaining parts.
(2) Relationship I Between Aggregates and Solid Lubricant
Ten percent or more of the aggregates are closely attached to the solid lubricant or are present in the vicinity of the solid lubricant.
When the aggregates are closely attached to the solid lubricant, the solid lubricant that is first deformed, cleaved, or disintegrated by the application of a load influences the aggregates that are closely attached to the solid lubricant.
For example, when the aggregates are closely attached to the ends of particles of the cleavable solid lubricant so as to cover them, the cleavage of the solid lubricant generates a force that shears the aggregates so that the deformation of the aggregates is induced. That is, the solid lubricant that relaxes the stress of the resin binder and the aggregates work together so that the solid lubricant having a small threshold stress is first deformed due to an increase in load, and then the aggregates having a relatively large threshold stress are deformed. In this way, stress relaxation follows to load increase without any gap.
Further, also when the aggregates are closely attached to the sides of particles of the solid lubricant, the solid lubricant is first deformed by the application of a load, which influences the resin binder surrounding the solid lubricant so that the resin binder is slightly deformed. That is, a large stress is locally generated in the vicinity of the solid lubricant in the rein binder. At this time, when the aggregates are closely attached to the solid lubricant, the stress locally generated in the resin binder can reliably be relaxed.
As can be seen from the above description, the aggregates may be present in the vicinity of the solid lubricant to relax stress locally generated in the resin composition. In this case, the distance between the solid lubricant and the aggregates is equal to or less than the average particle diameter of the protecting and reinforcing primary particles (10 nm or more but 100 nm or less). When the aggregates are present at such a distance within the above range from the solid lubricant, stress locally generated in the vicinity of the solid lubricant in the resin composition due to the deformation of the solid lubricant can reliably be relaxed.
When 10% or more of the aggregates are closely attached to the solid lubricant or are present in the vicinity of the solid lubricant, deformation of the solid lubricant directly influences the 10% or more of the aggregates. Therefore, even when a load is increased, the solid lubricant and the aggregates work together to continuously relax stress without any gap.
Here, the percentage (%) of the aggregates that are closely attached to the solid lubricant or are present in the vicinity of the solid lubricant is determined in the following manner.
The counted number of the aggregates that are closely attached to the solid lubricant or are present in the vicinity of the solid lubricant is compared to the counted total number of the aggregates appearing in a predetermined measured view in a cutting surface obtained by cutting the sliding resin composition in a direction perpendicular to the sliding surface of the sliding resin composition.
(3) Relationship II Between Aggregates and Solid Lubricant
The amount of the aggregates to which the ends of two or more particles of the solid lubricant are coupled is 5.0% or more.
When the aggregates are closely attached to the tips of particles of the solid lubricant, the solid lubricant that is first deformed, cleaved, or disintegrated by the application of a load influences the aggregates that are closely attached to the tips of particles of the solid lubricant.
For example, when the aggregates are closely attached to the ends of particles of the cleavable solid lubricant so as to cover them, the cleavage of the solid lubricant generates a force that shears the aggregates so that the deformation of the aggregates is induced. That is, the solid lubricant that relaxes the stress of the resin binder and the aggregates work together so that the solid lubricant having a small threshold stress is first deformed due to an increase in load, and then the aggregates having a relatively large threshold stress are deformed. In this way, stress relaxation follows to load increase without any gap.
Further, when one aggregate is closely attached to the tips of two or more particles of the solid lubricant to couple them, a force generated by deformation of each of the particles of the solid lubricant is concentrated on the one aggregate, and therefore a force applied to the aggregate due to the deformation of the solid lubricant is increased so that the aggregate is more reliably deformed or disintegrated.
Further, an assembly of two or more particles of the solid lubricant coupled by the aggregate functions as one piece of the solid lubricant because, as described above, the aggregate is easily deformed or disintegrated. In other words, the assembly covers a wider range of the resin binder to relax the stress of the resin binder. This makes it possible to more reliably prevent the disintegration or detachment of the rein binder.
The amount of the aggregates coupling the ends of two or more particles of the solid lubricant is set to 5.0% or more of all the aggregates. When the amount of the aggregates coupling the ends of two or more particles of the solid lubricant is set to 5.0% or more, deformation of two or more particles of the solid lubricant directly influences the aggregates, and therefore the aggregates are more reliably deformed or disintegrated to perform the function of stress relaxation. Therefore, even when a load is increased, the solid lubricant and the aggregates work together to continuously relax stress without any gap.
(4) Relationship III Between Aggregates and Solid Lubricant
The average particle diameter of the aggregates is 40% or less of the average particle diameter of the solid lubricant.
When the average particle diameter of the aggregates is 40% or less of the average particle diameter of the solid lubricant, the aggregates are sufficiently smaller than the solid lubricant. This makes it possible to promote the dispersion of the aggregates in the resin composition to ensure the effect of the aggregates on relaxing the stress of the resin binder in the entire resin composition.
(5) Relationship Between Particles Constituting Aggregates
The value of D90/D10 of the protecting and reinforcing primary particles constituting the aggregates is set to 5 or less, wherein D10 is a particle diameter when a cumulative height of particle diameters is 10%, and D90 is a particle diameter when a cumulative height of particle diameters is 90%.
Here, a cumulative height of particle diameters refers to an integrated quantity in a particle diameter distribution curve, and D10 refers to a particle diameter when a cumulative percentage reaches 10% from the lower side of the distribution curve, and D90 refers to a particle diameter when a cumulative percentage reaches 90% from the lower side of the distribution curve. Therefore, when the value of D90/D10 is smaller, the particle diameter distribution of the particles is sharper.
When the value of D90/D10 is set to 5 or less, the particles have a sharp particle diameter distribution, that is, have a uniform particle diameter.
The present invention is not limited to the above description of the embodiment according to the present invention. Various modified embodiments are also included in the present invention as long as they are easily conceivable by those skilled in the art and do not depart from the scope of the claims.
The above embodiment has been described with reference to a case where the sliding member is a bearing, but the present invention is applicable also to other sliding members.
REFERENCE SIGNS LIST
- 1: Sliding member
- 2: Base material layer
- 3: Back metal layer
- 5: Alloy layer
- 7: Resin coating layer
- 10: Resin binder
- 11: Solid lubricant
- 13: Protecting and reinforcing particle
- 20: Aggregate
- 30: Recess
Claims
1. A sliding resin composition comprising: a resin binder; a solid lubricant; and a protecting and reinforcing agent, wherein
- the protecting and reinforcing agent comprises aggregates of particles, and wherein
- a coupling force between the particles in the aggregates is smaller than a threshold stress of the resin binder so that the aggregates exposed at a surface of the resin binder are partially detached with a force smaller than the threshold stress of the resin binder.
2. The sliding resin composition according to claim 1, wherein the particles are harder than the resin binder.
3. The sliding resin composition according to claim 1, wherein the resin binder, the solid lubricant, and the aggregates have the following relationship in terms of threshold stress:
- solid lubricant≦aggregates<resin binder.
4. The sliding resin composition according to claim 1, wherein the particles are harder than the resin binder, have a smaller particle diameter than the solid lubricant, and occupy 1 vol. % or more but 20 vol. % or less of the entire sliding resin composition.
5. The sliding resin composition according to claim 4, wherein the particles have an average particle diameter of 10 nm or more but 100 nm or less.
6. The sliding resin composition according to claim 5, wherein, when an average particle diameter of the aggregates is defined as A and a standard deviation of the average particle diameter is defined as σ, A−1σ is 60 nm or more and A+1σ is 400 nm or less.
7. The sliding resin composition according to claim 1, wherein the aggregates have an aspect ratio of 10 or less.
8. A sliding resin composition comprising: a resin binder; a solid lubricant; and a protecting and reinforcing agent comprising aggregates of particles, wherein
- the particles have a smaller diameter than the solid lubricant and are contained in an amount of 1 vol. % or more but 20 vol. % or less of the entire composition, and wherein
- the aggregates have an aspect ratio of 10 or less.
9. The sliding resin composition according to claim 8, wherein the particles are harder than the resin binder.
10. The sliding resin composition according to claim 8, wherein the particles have an average particle diameter of 10 nm or more but 100 nm or less.
11. The sliding resin composition according to claim 10, wherein, when an average particle diameter of the aggregates is defined as A and a standard deviation of the average particle diameter is defined as σ, A−1σ is 60 nm or more and A+1σ is 400 nm or less.
12. A sliding member comprising: a base material layer; and a coating layer that is laminated on the base material layer and comprises the sliding resin composition according to claim 1.
13. The sliding member according to claim 12, wherein the base material layer has a semi-cylindrical portion.
14. A sliding member comprising: a base material layer; and a coating layer that is laminated on the base material layer and comprises the sliding resin composition according to claim 8.
Type: Application
Filed: May 15, 2015
Publication Date: Mar 30, 2017
Inventors: Hiroki KOBAYAKAWA (Inuyama-shi, AichiInuyama-shi, Aichi), Erina YASUDA (Inuyama-shi, Aichi)
Application Number: 15/311,278