Water-Soluble Or Water-Swellable Polymers As Water Loss Reducers In Cement Slurries

This invention relates to water-soluble or water-swellable polymers, containing a) 25-35 mol. % of one or more recurrent structural units of formula (1), where R1 and R2 represent hydrogen, methyl or ethyl, A represents a linear or branched C1-C12-alkylene, and Q+ stands for H+, NH4+, Li+, Na+, K+, ½Ca++, ½Mg++, ½Zn++, ⅓Al+++, or organic ammonium ions of the formula [HNR5R6R7]+, b) 3 to 8 mol. % of one or more recurrent structural units of formula (2), where R1 represents hydrogen, methyl, or ethyl, X+ stands for H+, NH4+, Li+, Na+, K+, ½Ca++, ½Mg++, ½Zn++, ⅓Al+++, or organic ammonium ions of the formula [HNR5R6R7]+, B is a linear or branched alkylene group with 1 to 6 carbon atoms, and n is a whole number between 0 and 5, and c) 57 to 72 mol. % of a (meth)acrylamide.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description

The present invention relates to water-soluble or water-swellable polymers based on acryl-, methacryl- or ethacrylamidoalkylsulfonic acid or salts thereof and carboxyalkyl acrylate, methacrylate or ethacrylate or oligomers of these carboxyl compounds, and acrylamides or alkylacrylamides, to a process for preparing these polymers and to the use thereof as water loss reducers in cement slurries for cementing deep wells for reducing the water loss at the wellbore wall (fluid loss additives).

In deep wells for developing mineral oil and natural gas deposits, the use of cement slurries has long been known. Once the wellbore has reached a certain depth, what are called feed tubes are introduced into the wellbore. For this purpose, the feed tubes have to be fixed, meaning that a cement slurry is pumped into the cavity between the rock and the feed tubes and hardens to give a solid rock. The cement rock which forms has to be impermeable to gases and liquids, in order that no gas and/or oil can flow out of the reservoir rock into other sections or up to the surface. High demands are made on the cement slurry to be pumped. It should have good pumpability, i.e. minimum viscosity, and nevertheless not exhibit any separation. The release of water from the cement slurry to the porous rock during the pumping operation should be low, in order that no thick filtercakes form at the wellbore wall, which would increase the pump pressure because of the annular space constriction to such a high degree that the porous rock breaks up. Moreover, the cement slurry, in the case of excessive water release, would not set optimally and would become permeable to gas and oil. On the other hand, the cement shell which forms in the annular space must attain sufficient strength very quickly, and no shrinkage, which leads to flow channels for gas, oil and water, may occur in the course of setting. Optimal adjustment of the properties of the cement slurry is possible only by means of additives. The most important additives are retardants, accelerators, dispersants and water loss reducers.

Effective water loss reducers used in practice for cement and gypsum slurries are a wide variety of different polymers, copolymers and combinations thereof. The first effective products, which are still being used even now, were cellulose ethers based on hydroxyethyl cellulose and carboxymethyl hydroxyethyl cellulose. Owing to thermal instability, these lose efficiency at wellbore temperatures above 100° C. (212° F.). If the temperature rises to about 120° C. to 150° C., thermal breakdown of these biogenic substances commences. As a result, many different fully synthetic thermally stabilized polymers have been developed and are still being used nowadays at the different temperatures and salinities of the cement slurry.

Polymers as additives for reducing the water loss from cement slurries are well known in the literature, although many have very limited activity in the temperature range between 30° C. (86° F.) and 200° C. (392° F.).

U.S. Pat. No. 2,614,998 describes the use of partly hydrolyzed polyacrylamide (polyacrylamide-co-acrylic acid) as water loss-reducing polymer. However, these polymers can lead to significant delays in the setting time of the cement and show only low efficacy at high temperatures.

U.S. Pat. No. 2,865,876, U.S. Pat. No. 2,905,565 and U.S. Pat. No. 3,052,628 describe the use of sulfonated polymers as additives. The polymers and copolymers described therein differ distinctly in terms of composition from the copolymers of the invention and have gained no technical significance at all.

U.S. Pat. No. 5,472,051 describes copolymers of acryloyldimethyltaurate and acrylic acid having molecular weights of less than 5000 g/mol. However, these polymers can lead to severe delays in the setting time of the cement and, because of the molecular weight, show high water losses at high temperatures.

WO-99026991 and EP-1045869 teach copolymers of acryloyldimethyltaurate and acrylamide, but these polymers, in direct comparison with the copolymers of the invention, exhibit poorer performance properties below a temperature of 50° C. (122° F.) (comparative example 1).

U.S. Pat. No. 4,015,991 describes a polymer prepared by polymerization of acryloyldimethyltaurate and acrylamide in water, wherein at least 20% of the acrylamide units have to be hydrolyzed subsequently to acrylic acid or a salt of acrylic acid. The copolymer described in the examples of U.S. Pat. No. 4,015,991 has formed through the polymerization of 116.4 g (0.56 mol) of acryloyldimethyltaurate and 14.7 g (0.207 mol) of acrylamide in water. After at least 20% of the acrylamide units have been hydrolyzed to acrylic acid, U.S. Pat. No. 4,015,991 claims the following copolymer:

where
x is 73.8 mol %
y is max. 21.8 mol %
z is at least 4.4 mol %, depending on y.

However, the disadvantage of this polymer is an unwanted influence on the cement properties (reduction in hardened cement strength) and the delaying effect on the solidification of the cement. A further problem is the restricted temperature range for use as a water loss-reducing polymer. At 176.7° C. (350° F.), it is demonstrably inactive (comparative examples 5 and 6). U.S. Pat. No. 4,015,991 showed that it is not possible by aqueous polymerization of acryloyldimethyltaurate and acrylamide without a hydrolysis step to produce any copolymer suitable for application purposes.

EP-0116671 discloses the introduction of 5%-60% by weight of vinylamides (e.g. N-vinylmethylacetamide) into acryloyldimethyltaurate-containing polymers. In this way, the high-temperature range of the application was significantly extended. However, these polymers have poorer performance properties at temperatures below a temperature of 50° C. (122° F.).

U.S. Pat. No. 5,025,040 describes copolymers of acryloyldimethyltaurate, acrylamide and at least 20% N-vinylimidazole.

U.S. Pat. No. 4,931,489 discloses copolymers of substituted acrylamides and N-vinylimidazoles, without the use of acryloyldimethyltaurate.

EP-0217608, U.S. Pat. No. 4,555,269 and EP-0157055 describe a copolymer of acryloyldimethyltaurate and dimethylacrylamide in a molar ratio of 1:4 to 4:1 as a fluid loss additive for salt-containing (about 10% by weight) cement slurries and the use of acryloyldimethyltaurate and acrylic acid in a molar ratio of 1:4 to 4:1 for the same purpose.

Polymers based on acryloyldimethyltaurate or salts thereof are already known. No solution satisfactory for application purposes for a temperature range between 30° C. (86° F.) and 200° C. (392° F.) on the basis of the monomers disclosed in U.S. Pat. No. 4,015,991 has been described to date.

Polymers based on acryloyldimethyltaurate, acrylic acid and acrylamide are likewise known:

EP-0244981 discloses polymers based on acryloyldimethyltaurate, acrylic acid and acrylamide as a soil-repellent sealing formulation. These polymers are prepared by the free-radical polymerization of the monomers in an aqueous medium. Polymers prepared according to examples 1-8 in EP-0244981, because of their polymer architecture (comparative examples 2, 3 and 4), demonstrably do not bring about any reduction in water loss when they are used as additive in cement slurries.

Polymers based on sulfonates and acrylamide, according to U.S. Pat. No. 4,800,071, are employed as filtration aids in order to remove sparingly soluble calcium salts from aqueous phosphoric acid solutions. No use of these polymers as water loss reducers in cement slurries for cementing deep wells has been disclosed.

U.S. Pat. No. 4,342,653 discloses polymers based on acryloyldimethyltaurate and acrylamide. These polymers are used as precipitation aids for aqueous dispersions. The precipitation aids described should have between 1 and 35 mol % of repeat units of acryloyldimethyltaurate, and a Brookfield viscosity of at least 2·10−3 Pa·s. The example adduced in U.S. Pat. No. 4,342,653 features an acrylamide content of 94 mol %. Such a high molar acrylamide content does not lead to any reduction in water loss in cement slurries.

JP-11310751 describes polymers based on 10-90 mol % of acryloyldimethyltaurate, 0-90 mol % of acrylamide and 0-30 mol % of further copolymerizable monomers suitable for paper coatings, adhesives and emulsion-based adhesives. These polymers are prepared by the free-radical polymerization of the monomers in an aqueous medium. Polymers prepared by the process in JP-11310751, because of their polymer architecture, do not bring about any reduction in water loss when they are used as additive in cement slurries.

JP-63060240 discloses polymers based on acryloyldimethyltaurate, acrylamides and sodium acrylate, which are used as precipitants in gold suspensions or gels for gold separation. The polymer specified in the example contains 13.3 mol % of AMPS, 13.3 mol % of sodium acrylate and 73.4 mol % of acrylamide, and was prepared with the aid of an aqueous free-radical polymerization. However, the disadvantage of these polymers is an unwanted influence on the cement properties (reduction in hardened cement strength) and the delaying effect on the solidification of the cement. As an additive in cement slurries, the polymer also does not exhibit any effects which contribute to reduction in water loss in cement slurries.

Additives on the market which are used as water loss reducers in cement slurries for cementing deep wells are acryloyldimethyltaurate and copolymers thereof (e.g. HOSTAMER® 4707 from Clariant). However, these in turn have the disadvantage that they lead to an increase in water loss below a temperature of 180° C. (356° F.).

The multitude of polymers developed for reduction of water release makes it clear that it is always problematic to formulate a cement slurry which is optimal for application purposes for a temperature range between 30° C. (86° F.) and 200° C. (392° F.). A significant influence on the suitability thereof is exerted by the temperature of the wellbore section which is being prepared for cementing. The polymers optimized for different temperatures constitute major logistical problems because a certain stock of extra water loss-reducing polymers always has to be kept at sites all over the world.

It was therefore an object of the present invention to provide substances which can help to achieve improved control of liquid loss in the cement slurries for cementing wellbores at temperatures between 80° F. and 300° F.

It has now been found that, surprisingly, the performance properties required can be achieved through the copolymerization of acryl-, methacryl- or ethacrylamidoalkylsulfonic acid or salts thereof and with carboxyalkyl acrylate, methacrylate or ethacrylate or oligomers of these carboxyl compounds, and with acrylamides or alkylacrylamides, when the polymerization process is altered and the subsequent hydrolysis is dispensed with, and hence a novel polymer which has not been described to date is prepared. This polymer also does not have any set-delaying properties below 50° C.

The present invention provides water-soluble or water-swellable polymers having a k value of 100 to 300, measured in 0.5% by weight solution in distilled water, containing

  • a) 25-35 mol % of one or more recurrent structural units of the formula (1)

    • in which
    • R1, R2 are hydrogen, methyl or ethyl,
    • A is linear or branched C1-C12-alkylene, and
    • Q+ is H+, NH4+, Li+, Na+, K+, ½Ca++, ½Mg++, ½Zn++, ⅓Al+++, organic ammonium ions of the formula [HNR5R6R7]+ where R5, R6 and R7 may each independently be hydrogen, a linear or branched alkyl group having 1 to 22 carbon atoms, a linear or branched, mono- or polyunsaturated alkenyl group having 2 to 22 carbon atoms, a C6-C22-alkylamidopropyl group, a linear monohydroxyalkyl group having 2 to 10 carbon atoms or a linear or branched dihydroxyalkyl group having 3 to 10 carbon atoms, and where at least one of the R5, R6 and R7 radicals is not hydrogen, or mixtures of these ions,
  • b) 3 to 8 mol % of one or more recurrent structural units of the formula (2)

    • in which
    • R1 is hydrogen, methyl or ethyl,
    • X+ is H+, NH4+, Li+, Na+, K+, ½ Ca++, ½ Mg++, ½ Zn++, ⅓ Al+++, organic ammonium ions of the formula [HNR5R6R7]+ where R5, R6 and R7 may each independently be hydrogen, a linear or branched alkyl group having 1 to 22 carbon atoms, a linear or branched, mono- or polyunsaturated alkenyl group having 2 to 22 carbon atoms, a C6-C22-alkylamidopropyl group, a linear monohydroxyalkyl group having 2 to 10 carbon atoms or a linear or branched dihydroxyalkyl group having 3 to 10 carbon atoms, and where at least one of the R5, R6 and R7 radicals is not hydrogen, or mixtures of these ions,
    • B is a chemical bond, or a linear or branched alkylene group having 1 to 6 carbon atoms, and
    • n is an integer from 0 to 5,
      and
  • c) 57 to 72 mol % of one or more recurrent structural units of the formula (3)

    • in which
    • R1 is hydrogen, methyl or ethyl, and
    • R3 and R4 are each independently hydrogen, methyl, ethyl, n-propyl, isopropyl or butyl.

The invention further provides for the use of the polymers of the invention as water loss reducers for cement formulations. Preferably, 0.05% to 5% by weight of the polymers, based on the weight of the cement formulation, is used in cement formulations.

In a polymer of the invention, it is possible in each case for different structural units of the formula (1) and/or of the formula (2) and/or of the formula (3) to be present. A polymer of the invention may, for example, contain several structural units of the formula (1) which differ from one another by different counterions Q+. A polymer of the invention may, for example, also contain several structural units of the formula (2) which differ from one another by different counterions X+. A polymer of the invention may, for example, also contain several structural units of the formula (3) which differ by different R1, R3 and R4 radicals. The R1 radicals in the structural units of the formulae (1), (2) and (3) may be identical or different in all the structural units.

The weight-average molecular weights of these polymers are preferably 300 000 to 5 000 000, more preferably 500 000 to 4 000 000, especially 600 000 to 2 500 000 g/mol. The weight-average molecular weights can be determined with the aid of gel permeation chromatography (GPC). The procedure for determining the weight-average molecular weight with the aid of GPC is described in detail in “Makromolekulare Chemie: Eine Einführung” [Macromolecular Chemistry: An Introduction] by Bernd Tieke, Wiley-VCH, 2nd fully revised and extended edition (Sep. 9, 2005) ISBN-10: 3527313796 in chapter 3. The polymers were analyzed against a polystyrenesulfonate standard.

Indicators used for the molecular weight are the relative viscosity and the k value. To determine the k value, the copolymer is dissolved in distilled water in a concentration of 0.5% by weight and the outflow time at 20° C. is determined by means of an Ubbelohde viscometer. This value gives the absolute viscosity of the solution (ηc). The absolute viscosity of the solvent is (η0). The ratio of the two absolute viscosities gives the relative viscosity:

Z = n c n 0

The relative viscosity Z and the concentration C can be used to determine the k value by means of the following equation:

Lg z = ( 75 * k 2 1 + 1.5 kc + k ) * c

The k value of the polymers of the invention is from 100 to 300, preferably from 150 to 270 and especially preferably from 180 to 250.

In the structural units of the formula (1), R1 is preferably hydrogen or methyl and more preferably hydrogen.

In the structural units of the formula (1), A is preferably a structural unit of the formula —C(CH3)2—CH2—.

The structural units of the formula (1) are preferably derived from monomers from the group consisting of acryloyldimethyltaurate, acryloyl-1,1-dimethyl-2-methyltaurate, acryloyltaurate, acryloyl-N-methyltaurate, preferably acryloyldimethyltaurate.

Preferably, the neutralization level of the structural units of the formula (1) is from 50.0 to 100 mol %, more preferably from 80.0 to 100 mol %, especially preferably from 90.0 to 100 mol % and exceptionally preferably from 95.0 to 100 mol %.

In the structural units of the formula (1), Q is partly H+ if neutralization is incomplete. In the case of partial or complete neutralization, Q+ is preferably selected from NH4+, Ca2+ and Na+ and mixtures of these ions. More preferably, the counterion Q other than H+ is NH4+.

In the structural units of the formula (2), R1 is preferably hydrogen or methyl and more preferably hydrogen.

In the structural units of the formulae (2), B is preferably a chemical bond or a structural unit of the formula —CH2—CH2—.

In the structural units of the formula (2), n is preferably 0 to 5 and more preferably 0 to 3 and especially preferably 0 or 1.

Preferably, the proportion of structural units of the formula (2) in which n is 0 within component b) of the polymers of the invention is at least 70.0 mol %, more preferably at least 80.0 mol %, especially preferably at least 90.0 mol %, exceptionally preferably at least 95.0 mol %.

More preferably, in the structural units of the formula (2), B is a chemical bond or the —CH2CH2— group.

In a further preferred embodiment, in the structural units of the formula (2), B is a chemical bond or the —CH2CH2— group and n is an integer from 1 to 5, and preferably from 1 to 3 and more preferably 1.

In the structural units of the formula (2), X is partly H+ if neutralization is incomplete. In the case of partial or complete neutralization, X is preferably selected from NH4+, Ca2+ and Na+ and mixtures of these ions. More preferably, the counterion X that is not H+ is NH4+

In a further particularly preferred embodiment of the invention, X+ is H+.

In a further particularly preferred embodiment of the invention, the polymers of the invention contain several different structural units of the formula (2), where the counterions X+ in some structural units of the formula (2) are defined as H+ and the counterions X+ in the other structural units of the formula (2) are defined differently than H+, and preferably as NH4+.

In a further particularly preferred embodiment of the invention, the polymers of the invention contain several different structural units of the formula (2) which differ in terms of R1, b and/or n.

These structural units are preferably derived from monomers from the group consisting of methacrylic acid, acrylic acid, carboxyethyl acrylate and higher oligomers of the formula (2) in which n is an integer of 2 or more.

Especially preferably, the structural units are derived from methacrylic acid, acrylic acid and carboxyethyl acrylate. Particular preference is given to methacrylic acid and acrylic acid.

The structural units of the formula (3) are preferably derived from monomers from the group consisting of acrylamide, N-methylacrylamide, N-ethylacrylamide, N,N-diethylmethacrylamide, N,N-diethylacrylamide, N,N-dimethylmethacrylamide, N,N-dimethylacrylamide, N-isopropylacrylamide, N-tert-butylacrylamide and N-butylacrylamide, preferably acrylamide, methacrylamide, N,N-diethylacrylamide, N,N-dimethylacrylamide, isopropylacrylamide, more preferably acrylamide, methacrylamide, N,N-dimethylacrylamide, especially preferably acrylamide.

In a further embodiment of the invention, the polymers of the invention preferably contain

  • a) 27.5 to 32.5 mol % of structural units of the formula (1),
  • b) 4.5 to 7.5 mol % of structural units of the formula (2), and
  • c) 60 to 68 mol % of structural units of the formula (3).

In a further preferred embodiment of the invention, the structural units of the formula (1) are derived from acryloyldimethyltaurate, those of the formula (2) are derived from acrylic acid and those of the formula (3) are derived from acrylamide.

Particularly preferred polymers of the invention contain structural units of

  • a) 25 to 35 mol % of acryloyldimethyltaurate, and
  • b) 3 to 8 mol % of acrylic acid, and
  • c) 57 to 72 mol % of acrylamide.

A further embodiment of particularly preferred polymers of the invention contains structural units of

  • a) 27.5 to 32.5 mol % of acryloyldimethyltaurate, and
  • b) 4.5 to 7.5 mol % of acrylic acid, and
  • c) 60 to 68 mol % of acrylamide.

In a further preferred embodiment of the invention, the polymers of the invention do not contain any cationic structural units.

The distribution of the different structural units in the polymers of the invention may be random, blockwise or in alternating or gradient form. The polymers of the invention are generally prepared by free-radical polymerization.

Free-radical polymerizations are common knowledge to those skilled in the art and are described in detail in standard literature works, for example in “Makromolekulare Chemie: Eine Einführung” by Bernd Tieke, Wiley-VCH, 2nd fully revised and extended edition (Sep. 9, 2005) ISBN-10: 3527313796.

The polymers of the invention are preferably prepared by means of free-radical precipitation polymerization in a polar solvent or solvent mixture. This involves dissolving or dispersing the corresponding monomers, for example, in the polar solvent or solvent mixture and initiating the polymerization in a manner known per se, for example by adding a free radical-forming compound. It is possible here, for example, for the initially charged monomers to be polymerized “directly”. Alternatively, they may also be neutralized prior to the polymerization, for example by reacting acidic groups in monomers used with bases prior to the polymerization, forming the counterions Q+ of the structural units of formula (1) or X+ of the structural units of formula (2). Instead of the neutralization of the monomers prior to the polymerization, however, it is also possible to neutralize the polymers with the bases on completion of polymerization.

The present invention therefore further provides a process for preparing the polymers of the invention, wherein monomers from which the structural units of components a) to c) derive are free-radically polymerized in a polar solvent or solvent mixtures comprising such solvents, and the monomers are optionally neutralized prior to the polymerization, or the polymer is neutralized after the polymerization, with ammonia or organic amines or an Li+-, Na+-, K+-, Ca++-, Mg++-, Zn++- or Al+++-containing base, preferably with the corresponding hydroxides or carbonates and more preferably with hydroxides.

Useful polymerization initiators include all free radical-forming substances; as well as typical diazo compounds and peroxy compounds, initiation is also possible by means of redox initiators, a photoinitiator or by means of high-energy radiation (UV, neutrons, plasma). In contrast to aqueous free-radical polymerization, there is only a minor dependence of the product on the type and amount of the initiator system used.

In a preferred embodiment of the process for preparing the polymers of the invention, the free-radical precipitation polymerization is effected in a polar solvent or solvent mixture which is characterized in that the solvent or solvent mixture has a boiling point of 60 to 110° C., preferably of 60 to 85° C., more preferably of 70 to 85° C.

In a further preferred embodiment of the process for preparing the polymers of the invention, the polar solvent contains:

  • d) water
    and
  • e) one or more further polar solvents, preferably alcohols, dialkyl ketone and cyclic ethers, more preferably alcohols, dialkyl ketone and especially preferably alcohols.

In a further preferred embodiment of the process for preparing the polymers of the invention, component e) contains one or more polar solvents selected from the group of methanol, ethanol, 1-propanol, 2-propanol, 2-methyl-2-propanol, 2-butanol, dimethyl ketone, diethyl ketone, tetrahydropyran, tetrahydrofuran, 2-methyltetrahydrofuran, 1,3-dioxane, 1,4-dioxane, preferably ethanol, 1-propanol, 2-propanol, 2-methylpropan-2-ol, 2-butanol, dimethyl ketone, tetrahydrofuran, 2-methyltetrahydrofuran, 1,3-dioxane, more preferably 2-propanol, 2-methylpropan-2-ol, dimethyl ketone, tetrahydrofuran, 2-methyltetrahydrofuran, 1,3-dioxane, especially preferably 2-methylpropan-2-ol, dimethyl ketone and exceptionally preferably 2-methylpropan-2-ol.

In the process for preparing the polymers of the invention, it is possible for various polar solvents of component e) to be present. One polar solvent of the invention in component e) may, for example, comprise 2-methylpropan-2-ol. A further solvent of the invention in component e) may, for example, comprise a mixture of 2-methylpropan-2-ol and dimethyl ketone. A further solvent of the invention in component e) may, for example, comprise a mixture of 2-methylpropan-2-ol and tetrahydrofuran.

In a particular embodiment of the process for preparing a polymer of the invention, the polar solvent mixture contains 0.5% to 20% by weight, preferably 0.5% to 10% by weight and more preferably 1% to 8% by weight of water and exceptionally preferably 2% to 5% by weight of water.

In a further particular embodiment of the process for preparing a polymer of the invention, the polar solvent mixture contains 5% to 99.5% by weight, preferably 10% to 99.5% by weight and more preferably 30% to 99.5% by weight of 2-methylpropan-2-ol.

In a further particular embodiment of the process for preparing a polymer of the invention, the polar solvent mixture contains 0.5% to 20% by weight of water, 7.5% to 92% by weight of 2-methylpropan-2-ol and 7.5% to 92% by weight of dimethyl ketone, preferably 0.5% to 7.5% by weight of water, 20% to 89.5% by weight of 2-methylpropan-2-ol and 10% to 79.5% by weight of dimethyl ketone.

In an exceptionally preferred process for preparing an inventive polymer, 27.5 to 32.5 mol % of acryloyldimethyltaurate, 4.5 to 7.5 mol % of acrylic acid and 60 to 68 mol % of acrylamide are free-radically polymerized in a polar solvent mixture, preferably a mixture of 1% to 8% by weight of water and 92% to 99% by weight of 2-methylpropan-2-ol, and the monomers are optionally neutralized prior to the polymerization, or the polymer is neutralized after the polymerization, with ammonia, ammonium carbonate, sodium hydroxide, sodium carbonate, preferably with ammonia.

The polymers are obtained as a white voluminous precipitate in the polar solvent mixture. For isolation, it is possible to use all the customary evaporation and drying isolation processes. More particularly, the polar solvent mixture can be removed from the product by a pressure filtration or distillation. A small residue of the polar solvent mixture is of no concern, either for safety reasons or for application reasons.

The invention further provides a method for cementing deep wells using a cement slurry containing the polymer of the invention in a concentration of 0.01% to 5% bwoc (by weight of cement), preferably 0.05% to 0.9% bwoc. Further components of the cement slurry are waters of different salinity and cement. In addition, it is possible to use dispersants, retardants, accelerators, extenders, foamers, defoamers, weighting agents, density-reducing additives and tensile strength-increasing fibers or silicate derivatives as auxiliary additives.

The invention further provides a method for cementing deep wells using a cement slurry containing a mixture of the inventive polymer and starch in a concentration of 0.01% to 5% bwoc (by weight of cement), preferably 0.05% to 0.9% bwoc. Further components of the cement slurry are waters of different salinity and cement. In addition, it is possible to use dispersants, retardants, accelerators, extenders, foamers, defoamers, weighting agents, density-reducing additives and tensile strength-increasing fibers or silicate derivatives as auxiliary additives.

The term “starch” is understood to mean an organic compound. Starch is a polysaccharide having the formula (C6H10O5)n which consists of α-D-glucose units joined to one another via glycosidic bonds. Starch may consist of:

    • 0% to 100% by weight of amylose, linear chains having a helical (screw) structure, having only α-1,4-glycosidic linkages, and
    • 0% to 100% by weight of amylopectin, highly branched structures, having α-1,6-glycosidic and α-1,4-glycosidic linkages. However, the amylopectin of starch, with about one α-1,6-glycosidic bond after about 30 α-1,4-glycosidic linkages, is less highly branched than that of glycogen (about 1 α-1,6-glycosidic bond for every 10 α-1,4-glycosidic bonds).

In this part of the world, starch is usually obtained from potatoes or cereals, but also from numerous other plants, such as rice (broken rice from rice dehusking factories) and corn. Another starch-providing plant of international significance is manioc (tapioca). In industrial starch production, various technologies are used according to the raw material.

In a particular embodiment of the invention, the starch can be thermally modified in an upstream step. The starch can physically bind several times its own weight of water, swell up and gelatinize under the action of heat. When heated with water, the starch swells at 47-57° C., the layers break up and gelatinized starch forms at 55-87° C. (potato starch at 62.5° C., wheat starch at 67.5° C.), having different stiffening capacity according to the starch type. The use of natural, non-pregelatinized starch has the advantage that, during the pumping of a cement slurry, this cement slurry is rheologically stabilized when the temperature increases.

In a further particular embodiment of the invention, the starch may be in a chemically modified form. Modified starch, according to which properties are to be modified, is produced by various chemical conversion processes. In the case of some modified starches, several conversion processes are conducted in succession (e.g. acetylated oxidized starch). Modified starches modified by chemical conversion processes are understood to mean:

    • acid-treated starch by reaction with acids (for example with hydrochloric acid, phosphoric acid or sulfuric acid)
    • alkali-modified starch by reaction with alkalis (for example with sodium hydroxide solution or potassium hydroxide solution)
    • bleached starch by treatment with peroxyacetic acid, hydrogen peroxide, sodium hypochlorite, sodium chlorite, sulfur dioxide, sulfites, potassium permanganate or ammonium persulfate
    • enzymatically modified starch by treatment with amylases
    • oxidized starch by oxidation (for example with sodium hypochlorite)
    • monostarch phosphate by esterification with phosphorous ester groups (for example phosphoric acid, sodium phosphate or potassium phosphate, phosphonic acid or pentasodium triphosphate)
    • distarch phosphate by esterification with sodium trimetaphosphate or phosphorus oxychloride
    • phosphated distarch phosphate by combination of the processes for preparing monostarch phosphate and distarch phosphate
    • acetylated starch by esterification (for example with anhydrides)
    • hydroxypropyl starch by reaction with propylene oxide
    • sodium octenylsuccinate starch by reaction of starch with octenylsuccinic anhydride.

The most commonly desired improvements are in resistance to heat, cold and/or pH changes (acids).

The invention therefore further provides mixtures comprising the abovementioned starch and/or modifications thereof and the polymers of the invention. These mixtures preferably contain:

  • 25% to 75% by weight of starch and
  • 25% to 75% by weight of the polymers of the invention.

In a particular embodiment, the mixtures contain

  • 25% to 75% by weight of a chemically modified starch and
  • 25% to 75% by weight of the polymers of the invention.

In a further particular embodiment, the mixtures contain

  • 25% to 75% by weight of a thermally modified starch and
  • 25% to 75% by weight of the polymers of the invention.

An inventive mixture of starch and the polymers of the invention can be obtained during the polymerization process after the actual polymerization and before the drying operation or isolation operation.

A further inventive mixture of starch and the polymers of the invention can be obtained by the mixing of the pulverulent starch with the pulverulent polymer of the invention.

EXAMPLES

In polymerization processes A to B described below, typical preparation processes for the polymers of the invention are described.

In the examples, there was variation of the polar solvent used, with the aid of which the polymers of the invention can be prepared. With the aid of polymerization methods A1 to A5 and B1 to B3, further polymers of the invention were prepared by the variation of the monomers. These polymers and polymerization processes used for the synthesis thereof are summarized in table 1a) to table 1i).

  • Polymerization process A1: Polymerization in 2-methylpropan-2-ol/water (3.5%) as polar solvent

In a 2 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube, 772 g of anhydrous 2-methyl-propan-2-ol are admixed with 28 g of distilled water. The reaction vessel is within a thermostatted heating bath.

This reaction vessel is blanketed with nitrogen gas and, in a gentle nitrogen countercurrent, 113.2 g of acryloyldimethyltaurate are introduced. The acryloyldimethyltaurate does not dissolve completely in the 2-methylpropan-2-ol/water mixture and is partly in the form of a dispersion of solids. The pH of this mixture is below pH 1. Through the gas inlet tube, gaseous ammonia is introduced above the liquid phase until the pH of the dispersion is between 7 and 8. On attainment of the desired pH range, the mixture is stirred for another 1 hour and the pH is recorded continuously. The reaction vessel is blanketed with nitrogen and 79.2 g of acrylamide and 7.6 g of acrylic acid are introduced. After the acrylamide has been introduced, the pH is checked again and optionally corrected into the pH range of 7 to 8. A constant nitrogen stream is passed through the solution for at least 1 hour. After this inertization time, the residual oxygen is checked by means of an oxygen electrode. Should the measured value of residual oxygen in the liquid phase exceed the value of 1 ppm, another inertization is necessary until this value is attained. Thereafter, in a gentle nitrogen stream, 2 g of 2,2′-azobis(2,4-dimethylvaleronitrile) are added and the reaction tank is heated to 40° C. Shortly after attainment of an internal temperature of 40° C., the introduction of nitrogen gas is ended and commencement of the polymerization reaction is observed, which can be identified by a temperature increase of 10-35° C. About 5-15 minutes after onset of the polymerization reaction, the temperature maximum has been exceeded and the temperature in the reaction vessel is increased by means of the heating bath up to the boiling point of the 2-methylpropan-2-ol/water mixture. Under gentle reflux, the now viscous mixture is stirred for a further two hours. The reaction product, present in the form of a viscous suspension of polymer in the 2-methylpropan-2-ol/water mixture, is removed by filtration and subsequent drying in a vacuum drying cabinet.

  • Yield: 215.4 g of polymer 1
  • Dry content (IR drier, 15 minutes at 120° C.): 94%
  • K value (0.5% solution in distilled water): 212
  • pH (0.5% solution in distilled water): 4.76
  • Polymerization process A2: Polymerization in 2-methylpropan-2-ol/water (2%)

In a 2 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube, 784 g of anhydrous 2-methylpropan-2-ol are admixed with 16 g of distilled water. The reaction vessel is within a thermostatted heating bath. The further steps of polymerization process A2 are conducted analogously to polymerization process A1.

With the aid of polymerization method A2, further polymers of the invention were prepared by varying the monomers. These polymers are summarized in table 1.

  • Polymerization process A3: Polymerization in 2-methylpropan-2-ol/water (4.5%)

In a 2 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube, 764 g of anhydrous 2-methylpropan-2-ol are admixed with 36 g of distilled water. The reaction vessel is within a thermostatted heating bath. The further steps of polymerization process A3 are conducted analogously to polymerization process A1.

  • Polymerization process A4: Polymerization in 2-methylpropan-2-ol/water (1.5%)

In a 2 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube, 788 g of anhydrous 2-methylpropan-2-ol are admixed with 12 g of distilled water. The reaction vessel is within a thermostatted heating bath. The further steps of polymerization process A4 are conducted analogously to polymerization process A1.

  • Polymerization process A5: Polymerization in 2-methylpropan-2-ol/water (7.5%)

In a 2 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube, 748 g of anhydrous 2-methylpropan-2-ol are admixed with 52 g of distilled water. The reaction vessel is within a thermostatted heating bath. The further steps of polymerization process A5 are conducted analogously to polymerization process A1.

  • Polymerization process B1: Polymerization in 2-methylpropan-2-ol, dimethyl ketone and water as polar solvent (50:50, 3.4% water)

In a 2 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube, 384 g of anhydrous 2-methylpropan-2-ol and 384 g of dimethyl ketone are admixed with 26.4 g of distilled water. The reaction vessel is within a thermostatted heating bath.

This reaction vessel is blanketed with nitrogen gas and, in a gentle nitrogen countercurrent, 130 g of acryloyldimethyltaurate are introduced. The acryloyldimethyltaurate does not dissolve completely in the 2-methylpropan-2-ol/dimethyl ketone/water mixture and is partly in the form of a dispersion of solids. The pH of this mixture is below pH 1. Through the gas inlet tube, gaseous ammonia is introduced above the liquid phase until the pH of the dispersion is between 7 and 8. On attainment of the desired pH range, the mixture is stirred for another 1 hour and the pH is recorded continuously. The reaction vessel is blanketed with nitrogen and 60 g of acrylamide and 10 g of acrylic acid are introduced. After the acrylamide has been introduced, the pH is checked again and optionally corrected into the pH range of 7 to 8. A constant nitrogen stream is passed through the solution for at least 1 hour. After this inertization time, the residual oxygen is checked by means of an oxygen electrode. Should the measured value of residual oxygen in the liquid phase exceed the value of 1 ppm, another inertization is necessary until this value is attained. Thereafter, in a gentle nitrogen stream, 2.05 g of 2,2′-azobis(2,4-dimethylvaleronitrile) are added and the reaction tank is heated to 40° C. Shortly after attainment of an internal temperature of 40° C., the introduction of nitrogen gas is ended and commencement of the polymerization reaction is observed, which can be identified by a temperature increase of 10 to 35° C. About 5-15 minutes after onset of the polymerization reaction, the temperature maximum has been exceeded and the temperature in the reaction vessel is increased by means of the heating bath up to the boiling point of the 2-methylpropan-2-ol/water mixture. Under gentle reflux, the now viscous mixture is stirred for a further two hours. The reaction product, present in the form of a viscous suspension of polymer in the 2-methylpropan-2-ol/water mixture, is removed by filtration and subsequent drying in a vacuum drying cabinet.

  • Polymerization process B2: Polymerization in 2-methylpropan-2-ol, dimethyl ketone and water as polar solvent (75:25, 3.0% water)

In a 2 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube, 582 g of anhydrous 2-methylpropan-2-ol and 194 g of dimethyl ketone are admixed with 24 g of distilled water. The reaction vessel is within a thermostatted heating bath. The further steps of polymerization process B2 are conducted analogously to polymerization process B1.

  • Polymerization process B3: Polymerization in 2-methylpropan-2-ol, dimethyl ketone and water as polar solvent (25:75, 5.0% water)

In a 2 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube, 194 g of anhydrous 2-methylpropan-2-ol and 582 g of dimethyl ketone are admixed with 24 g of distilled water. The reaction vessel is within a thermostatted heating bath. The further steps of the polymerization process are conducted analogously to polymerization process B1.

TABLE 1a) Examples of polymers of the invention prepared by polymerization processes A1 to A5 and B1 to B3 ACDMT Acrylic acid Acrylamide V-65 ® Polymer Process g mol % g mol % g mol % g % by wt. k value 2 A1 110.0 29.6 10.00 7.7 80.0 62.7 2.00 1.0 215 4 A1 113.2 30.9 7.60 6.0 79.2 63.1 2.00 1.0 210 6 A1 98.0 32.0 6.40 6.0 65.0 61.9 1.90 1.1 208 7 A1 119.0 32.5 5.70 4.5 79.2 63.0 2.25 1.1 200 8 A1 104.5 28.5 9.60 7.5 80.4 64.0 2.25 1.2 204 12 A2 110.0 29.6 10.00 7.7 80.0 62.7 2.25 1.1 192 13 A2 113.2 30.9 7.60 6.0 79.2 63.1 2.20 1.1 188 14 A2 119.0 32.5 5.70 4.5 79.2 63.0 2.20 1.1 179 16 A3 113.2 30.9 7.60 6.0 79.2 63.1 2.20 1.1 216 18 A3 110.0 29.6 10.00 7.7 80.0 62.7 2.25 1.1 222 20 A4 90.0 25.1 6.20 5.0 86.0 69.9 2.18 1.2 176

TABLE 1b) Examples of polymers of the invention prepared by polymerization processes A1 to A5 and B1 to B3 ACDMT Acrylic acid Acrylamide V-65 ® Polymer Process g mol % g mol % g mol % g % by wt. k value 25 B1 109.5 29.5 9.70 7.5 80.3 63.0 2.30 1.2 203 26 B1 100.0 28.5 6.10 5.0 80.0 66.5 2.10 1.1 211 28 B1 113.2 31.0 7.60 6.0 79.0 63.0 2.20 1.1 213 31 B2 99.5 34.5 8.00 8.0 56.8 57.5 1.80 1.1 219 33 B2 110.0 34.3 3.40 3.0 69.0 62.7 2.00 1.1 227 34 B2 119.0 32.5 5.70 4.5 79.2 63.0 2.25 1.1 228 35 B2 110.0 29.6 10.00 7.7 80.0 62.7 2.25 1.1 221 36 B2 113.2 30.9 7.60 6.0 79.2 63.1 2.25 1.1 227 38 B3 113.2 30.9 7.60 6.0 79.2 63.1 2.20 1.1 216 40 B3 110.0 29.6 10.00 7.7 80.0 62.7 2.25 1.1 218

TABLE 1c) Polymers of the invention by polymerization process A1 ACDMT Methacrylic Acrylamide V-65 ® k Polymer Process mol % acid mol % mol % g value 42 A1 30 7 63 2.00 208 44 A1 31 6 63 2.00 219

TABLE 1d) Polymers of the invention by polymerization process A1 Dimethyl- ACDMT Methacrylic acrylamide V-65 ® k Polymer Process mol % acid mol % mol % g value 47 A1 30 7 63 2.0 201 49 A1 31 6 63 2.0 198

TABLE 1e) Polymers of the invention by polymerization process A1 ACDMT CEA Acrylamide V-65 ® Polymer Process mol % mol % mol % g k value 52 A1 30 7 63 2.0 217 54 A1 31 6 63 2.0 209

TABLE 1f) Polymers of the invention by polymerization process A1 Dimethyl- ACDMT CEA acrylamide V-65 ® Polymer Process mol % mol % mol % g k value 57 A1 30 7 63 2.0 218 59 A1 31 6 63 2.0 207

TABLE 1g) Polymers of the invention by polymerization process A1 CEA ACDMT oligomer Acrylamide V-65 ® Polymer Process mol % mol % mol % g k value 62 A1 30 7 63 2.0 214 64 A1 31 6 63 2.0 205

TABLE 1h) Polymers of the invention by polymerization process A1 CEA Dimethyl- ACDMT oligomer acrylamide V-65 ® Polymer Process mol % mol % mol % g k value 67 A1 30 7 63 2.0 208 69 A1 31 6 63 2.0 218
  • ACDMT=acryloyldimethyltaurate
  • AA=acrylic acid
  • AM=acrylamide
  • CEA=carboxyethyl acrylate
  • CEA oligomer=carboxyethyl acrylate oligomer mixture with n=0 to 5
  • V-65=2,2′-azobis(2,4-dimethylvaleronitrile)/V-65 is a registered trademark of Wako Pure Chemicals Industries, Ltd
  • Comparative example 1 (not in accordance with the invention, prepared according to EP-1045869, copolymer prepared in precipitation polymerization, 44.5 mol % of acryloyldimethyltaurate and 55.5 mol % of acrylamide)

In a 3 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube, 1700 g of anhydrous 2-methylpropan-2-ol are admixed with 50 mL of distilled water. The reaction vessel is within a thermostatted heating bath.

This reaction vessel is blanketed with nitrogen gas and, in a gentle nitrogen countercurrent, 245 g of acryloyldimethyltaurate are introduced. The acryloyldimethyltaurate does not dissolve completely in the 2-methylpropan-2-ol/water mixture and is partly in the form of a dispersion of solids. The pH of this mixture is below pH 1. Through the gas inlet tube, gaseous ammonia is introduced above the liquid phase until the pH of the dispersion is between 7 and 8. On attainment of the desired pH range, the mixture is stirred for another 1 hour and the pH is recorded continuously. The reaction vessel is blanketed with nitrogen and 105 g of acrylamide are introduced. After the acrylamide has been introduced, the pH is checked again and optionally corrected into the pH range of 7 to 8. A constant nitrogen stream is passed through the solution for at least 1 hour. After this inertization time, the residual oxygen is checked by means of an oxygen electrode. Should the measured value of residual oxygen in the liquid phase exceed the value of 1 ppm, another inertization is necessary until this value is attained. Thereafter, in a gentle nitrogen stream, 2 g of AIBN are added and the reaction tank is heated to 60° C. Shortly after attainment of an internal temperature of 60° C., the introduction of nitrogen gas is ended and commencement of the polymerization reaction is observed, which can be identified by a temperature increase of 10-15° C. About 5-15 minutes after onset of the polymerization reaction, the temperature maximum has been exceeded and the temperature in the reaction vessel is increased by means of the heating bath up to the boiling point of the 2-methylpropan-2-ol/water mixture. Under gentle reflux, the now viscous mixture is stirred for a further two hours. The reaction product, present in the form of a viscous suspension of polymer in the 2-methylpropan-2-ol/water mixture, is removed by filtration and subsequent drying in a vacuum drying cabinet.

  • Yield: 365 g
  • Dry content (IR drier, 15 minutes at 120° C.): 96%
  • K value (0.5% solution in distilled water): 212
  • Comparative example 2 (not in accordance with the invention, prepared according to EP-0244981, copolymer prepared in an aqueous gel polymerization, 18.6 mol % of acryloyldimethyltaurate, 10 mol % of acrylic acid and 71.3 mol % of acrylamide)

In EP-0244981, reference is made in the examples to a gel polymerization in a conventional manner. No detailed preparation process for the polymers in EP-0244981 is described.

For comparative example 2, a 1 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube was initially charged with 390 g of distilled water, 40 g of acryloyldimethyltaurate, 7.5 g of acrylic acid and 52.5 g of acrylamide. Nitrogen gas is passed through the reaction solution for 1 hour. Thereafter, 2 g of ammonium peroxodisulfate dissolved in 10 g of distilled water are added as initiator. This mixture is heated to 40° C. until a polymerization reaction occurs after 10-15 minutes. After passing through the temperature maximum, the internal temperature is adjusted to 60° C. by means of the thermostat. A clear gel of high viscosity forms. The gel is comminuted mechanically and dried in a vacuum drying cabinet.

  • Comparative example 3 (not in accordance with the invention, prepared according to EP-0244981, copolymer prepared in an aqueous gel polymerization, 34 mol % of acryloyldimethyltaurate, 11.4 mol % of acrylic acid and 54.6 mol % of acrylamide).

For comparative example 3, a 1 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube was initially charged with 390 g of distilled water, 60 g of acryloyldimethyltaurate, 7 g of acrylic acid and 11.4 g of acrylamide. Nitrogen gas is passed through the reaction solution for 1 hour. Thereafter, 2 g of ammonium peroxodisulfate dissolved in 10 g of distilled water are added as initiator. This mixture is heated to 40° C. until a polymerization reaction occurs after 10-15 minutes. After passing through the temperature maximum, the internal temperature is adjusted to 60° C. by means of the thermostat. A clear gel of high viscosity forms. The gel is comminuted mechanically and dried in a vacuum drying cabinet.

  • Comparative example 4 (not in accordance with the invention, prepared according to EP-0244981, copolymer prepared in an aqueous gel polymerization, 10.3 mol % of acryloyldimethyltaurate, 5.9 mol % of acrylic acid and 84.9 mol % of acrylamide). Comparative example 4 was prepared analogously to comparative example 2.

For comparative example 4, a 1 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube was initially charged with 390 g of distilled water, 25 g of acryloyldimethyltaurate, 5 g of acrylic acid and 70 g of acrylamide. Nitrogen gas is passed through the reaction solution for 1 hour. Thereafter, 2 g of ammonium peroxodisulfate dissolved in 10 g of distilled water are added as initiator. This mixture is heated to 40° C. until a polymerization reaction occurs after 10-15 minutes. After passing through the temperature maximum, the internal temperature is adjusted to 60° C. by means of the thermostat. A clear gel of high viscosity forms. The gel is comminuted mechanically and dried in a vacuum drying cabinet.

  • Comparative example 5 (not in accordance with the invention, prepared according to U.S. Pat. No. 4,015,991, copolymer prepared in an aqueous gel polymerization, 10.3 mol % of acryloyldimethyltaurate, 5.9 mol % of acrylic acid and 84.9 mol % of acrylamide).

A 3 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube is initially charged with 328 g of distilled water and 116.4 g of acryloyldimethyltaurate. The acryloyldimethyltaurate is neutralized by adding 45 g of a 50% sodium hydroxide (NaOH) solution. After the neutralization reaction, a clear solution having a pH between 7 and 8 is obtained. 14.7 g of acrylamide are dissolved gradually in the solution thus neutralized. Nitrogen gas is passed through the reaction solution for 1 hour. Thereafter, 0.69 g of tert-butyl peroxypivalate and 1.0 mL of an iron ammonium sulfate solution as redox initiator pair are added. The iron ammonium sulfate solution is prepared by dissolving 0.098 g of Fe(NH4)2(SO4)2 in 500 g of water. This mixture is additionally stirred at room temperature until, after 1-2 hours, a polymerization reaction occurs. The exothermic polymerization reaction, in the case of adiabatic polymerization, increases the temperature to 50-60° C. After passing through the temperature maximum, the internal temperature is adjusted to 60° C. by means of the thermostat. A clear gel of high viscosity is formed. The gel is comminuted mechanically and dried on a roller drier.

  • Yield: 152 g of comparative polymer 5

According to the testing in U.S. Pat. No. 4,015,991, this base polymer should have only poor water-loss reducing action. In contrast, at low temperatures, 28° C., the partly hydrolyzed products should have good performance properties. These products were prepared and tested as in comparative example 6.

  • Comparative example 6 (not in accordance with the invention, prepared according to U.S. Pat. No. 4,015,991) Controlled hydrolysis of comparative polymer 5

45.3 g of comparative polymer 5 are dissolved in 1500 mL of distilled water while stirring. On completion of dissolution of the polymer, 1.68 g of potassium hydroxide which have been dissolved in 20 mL of water beforehand are added thereto. This mixture is heated to 60° C. then stirred at this temperature for one hour. The reaction product is dried again with the aid of a roller drier. In this way, 50% hydrolysis is achieved.

Examples: Synergistic Mixtures Comprising Starch and the Polymers of the Invention

For the synergistic mixtures comprising starch and the polymers of the invention, the following starch types were used:

  • Starch A: corn starch
  • Starch B: manioc starch
  • Starch C: “cook up modified starch”
  • Starch D: hydroxypropyl starch

Table 2 describes the mixtures made with the starches A to E and the polymers of the invention.

TABLE 2 Synergistic mixtures comprising starch and the polymers of the invention Mixture Starch % by wt. Polymer % by wt. 1 A 30  (4) 70 2 A 50  (4) 50 3 A 70  (4) 30 4 B 50  (4) 50 5 D 60  (4) 40 6 A 25 (42) 75 7 A 40 (42) 60 8 A 65 (42) 35 9 B 25 (42) 75 10 B 40 (42) 60 11 B 65 (42) 35 12 B 50 (52) 50 13 C 50 (52) 50 14 D 50 (52) 50 15 D 40 (52) 60 16 D 60 (52) 40 17 A 75  (7) 25 18 D 50  (7) 50 25 A 45 (26) 55 26 E 65 (26) 35 27 A 50 (49) 50 28 A 45 (49) 50 29 A 65 (49) 35 30 B 50 (49) 50 31 C 45 (49) 50 32 D 65 (49) 35 33 A 50 (54) 50 34 B 50 (54) 50 35 D 50 (54) 50

Examples: Test Results

The testing is effected according to API spec. 10. In an atmospheric consistometer, the cement slurry is stirred/conditioned at analysis temperature and then, at the same temperature, the rheology with the FANN model 35SA viscometer is measured (at high temperature, conditioning is effected at 93° C. and the viscosity is measured). At temperatures of >93° C., the water loss is measured with a stirring fluid loss apparatus (SFLA).

Table 3 shows the water loss-reducing properties of selected abovementioned examples according to API spec. 10 at 35° C. (95° F.) in a static filtration test in the Baroid HTHP filter press. It becomes clear that the water loss reduction with the polymers of the invention can be improved considerably at low temperatures compared to the comparative examples. Of course, at these low temperatures, the polymers based on acryloyldimethyltaurate and acrylamide as claimed in EP-1045869, reworked in comparative example 1, also reduce water loss. However, it becomes clear from table 1 that the water loss of comparative example 1 is nearly twice as high compared to the inventive polymer 4. The gel polymers described in EP-0244981, reworked in comparative examples 2 to 3, show a high water loss even at very low temperatures and are unsuitable for use. For this reason, comparative examples 2 to 3 were not considered in the measurements which follow. The two comparative examples from U.S. Pat. No. 4,015,991, based on partly hydrolyzed poly(acrylamide-co-acryloyldimethyltaurate), reworked in comparative examples 5 and 6, in direct comparison with polymer 4, likewise have nearly twice to three times the water loss. These polymers too appear unsuitable for use.

Formulation of the Cement Slurries:

  • 100 g of Dyckerhoff Class G
  • 44 g of distilled water
  • 0.3-0.5 g of polymer

TABLE 3 (Use test at 95° F. (35° C.)) Rheology after mixing at 75° F. (24° C.), scale divisions API at X revolutions per minute fluid Polymer Concentration Revolutions per minute (rpm) loss No. % by wt. 600 300 200 100 6 3 mL 2 (P) 0.5 95 74 46 33 6 3 60 4 (P) 0.3 108 77 44 30 5 3.5 58 8 (P) 0.3 103 73 39 28 4 3 72 13 (P) 0.3 90 72 38 25 4 3 75 16 (P) 0.3 110 87 53 36 5 3.5 95 18 (P) 0.3 95 73 45 26 4 3 85 20 (P) 0.5 88 67 47 28 4.5 3.5 66 28 (P) 0.3 87 69 39 26 5 3 65 33 (P) 0.3 98 82 59 30 6 3.5 70 36 (P) 0.3 86 63 42 30 5 3.5 68 1 (C) 0.3 94 68 39 26 5 3 115  2 (C) 0.3 290 167 118 67 7.5 4.5 470* 3 (C) 0.3 120 105 77 56 11 5 660* 4 (C) 0.3 275 151 116 59 9 6.5 270* 5 (C) 0.3 168 88 68 38 11 11.5 143* 6 (C) 0.3 225 117 84 43 7 4.5 178* (P) = inventive polymer (ex.: 30 (P) = inventive polymer 30 from Table 1a)) (C) = non-inventive comparative example (ex. 5 (C) = comparative example 5) *values are calculated, since all the water had been expressed before the test had ended.

Table 4 shows the water loss-reducing properties of selected abovementioned examples according to API spec. 10 at 121.1° C. (250° F.) in a stirred filtration test in the Fann HTHP filter press (stirring fluid loss apparatus, SFLA). In order to better show the improved properties of the polymers of the invention compared to the state of the art of the polymers claimed in EP1045869 (comparative example 1), the concentration of the polymers used was varied between 0.25% and 0.5% by weight. It becomes clear that, with the polymers of the invention at lower concentrations (0.25% by weight), water loss is reduced by 40% compared to by weight (80 mL) the claimed polymers in EP 1045869 (130 mL).

Formulation of the Cement Slurries:

  • 100 g of Dyckerhoff Class G Cement
  • 35 g of silica flour
  • 54.8 g of distilled water

Polymer in the Concentration Specified in Table 3 or 4

  • 0.3 g of dispersant (polynaphthalenesulfonate, PNS)
  • 0.5 g of retarder (lignosulfonate)

TABLE 4 (Use test at 250° F. (121.1° C.)) Rheology after mixing at 75° F. (24° C.), scale divisions API at X revolutions per minute fluid Polymer Concentration Revolutions per minute (rpm) loss No. % by wt. 600 300 200 100 6 3 mL 1 (C) 0.25 167 91 63 34 5 3.5 130 1 (C) 0.5 >300 168 117 64 7.5 5.0 52 4 (P) 0.25 170 91 63 34 5 3.5 80 4 (P) 0.5 >300 174 119 65 7 4.5 42 2 (P) 0.5 295 164 113 62 7 4.5 44 4 (P) 0.5 >300 174 119 65 7 4.5 42 13 (P) 0.5 >300 179 126 70 8 5 40 7 (P) 0.5 >300 174 123 68 7 4 43 31 (P) 0.5 >300 167 121 58 7.5 3.5 54 26 (P) 0.5 295 173 119 64 7 4.5 60 (P) = inventive polymer (ex.: 30 (P) = inventive polymer 30 from Table 1a))

Table 5 shows the water loss-reducing properties of selected abovementioned mixture of starch and the polymers of the invention according to API spec. 10 under various temperature conditions (250° F., 300° F. and 350° F.) in a stirred filtration test in the Fann HTHP filter press (stirring fluid loss apparatus, SFLA).

Formulation of the Cement Slurries:

  • 100 g of Dyckerhoff Class G Cement
  • 35 g of silica flour
  • 54.8 g of distilled water

Polymer in the Concentration Specified in Table 3 or 4

  • 0.3 g of dispersant (polynaphthalenesulfonate, PNS)
  • 0.5-1.5 g of retarder (lignosulfonate)

TABLE 5 (Use tests of the mixtures at different temperatures) Rheology after mixing at 75° F. (24° C.), API scale divisions at X revolutions per minute fluid Temp. Revolutions per minute (rpm) loss Mixture ° F. 600 300 200 100 6 3 mL 2 250 188 104 71 38 5 4 102 4 250 173 93 63 34 6 5 106 3 250 208 115 79 43 6 4.5 60 2 300 191 108 74 42 8.5 9 52 4 300 203 113 78 43 7.5 6.5 46 3 300 242 133 94 52 9 7.5 43 3 300 228 127 88 49 9 7.5 41 2 350 206 119 91 50 15 14 96 3 350 217 123 89 54 13.5 12.5 92 (P) = inventive polymer (ex.: 30 (P) = inventive polymer 30 from table 1a))

It was therefore an object of the present invention to provide polymers which can help to achieve improved control of liquid loss in the cement slurries for cementing wellbores at temperatures between 80° F. and 300° F. WO-99/26991 describes copolymers of AMPS and acrylamide. Table 4 on page 23 discloses that there is a distinct decline in the water loss-reducing properties of the polymers described within a temperature range between 100° F. and 200° F., and doubling of the water loss in some cases in the use test. The addition of acrylic acid in the polymers of the invention distinctly improves the water loss compared to the polymers of WO-99/26991. The comparative examples which follow are intended to demonstrate this.

Comparative Examples According to WO-99/26991

  • Comparative polymer 7: (not in accordance with the invention, prepared according to WO-99/26991—copolymer of acryloyldimethyltaurate 70% by weight and acrylamide 30% by weight)

In a 3 liter Quickfit flask with anchor stirrer, reflux condenser with offgas scrubber, combined thermometer/pH meter and a gas inlet tube, 50 ml of distilled water are added to 1700 g of anhydrous 2-methylpropan-2-ol. The reaction vessel is in a thermostated heating bath.

This reaction vessel is blanketed with nitrogen gas and, in a gentle nitrogen countercurrent, 245 g of acryloyldimethyltaurate are introduced. The acryloyldimethyltaurate does not dissolve completely in the 2-methylpropan-2-ol/water mixture and is partly in the form of a dispersion of solids. The pH of this mixture is below pH 1. Gaseous ammonia is introduced through the gas inlet tube above the liquid phase until the pH of the dispersion is between 7 and 8. On attainment of the desired pH, the mixture is stirred for a further 1 hour and the pH is recorded continuously. The reaction vessel is blanketed with nitrogen, and 105 g of acrylamide are introduced. After the acrylamide has been introduced, the pH is checked again and, if necessary, corrected to the range of pH 7 to 8. A constant nitrogen stream is passed through the solution for at least 1 hour. After this inertization period, the residual oxygen level is checked by means of an oxygen electrode. Should the residual oxygen value in the liquid phase exceed the value of 1 ppm, another inertization is necessary until this value is attained. Thereafter, in a gentle nitrogen stream, 1.5 g of AIBN are added and the reaction vessel is heated to 60° C. Shortly after the attainment of an internal temperature of 60° C., the introduction of nitrogen gas is ended and commencement of the polymerization reaction is observed, which can be identified by an increase in temperature of 10 to 15° C. About 5-15 minutes after onset of the polymerization reaction, the temperature maximum has been exceeded and the temperature in the reaction vessel is increased by the heating bath up to the boiling point of the 2-methylpropan-2-ol/water mixture. Under gentle reflux, the now viscous mass is stirred for a further two hours. The reaction product, in the form of a viscous suspension of polymer in the 2-methylpropan-2-ol/water mixture, is separated off by filtration and subsequent drying in a vacuum drying cabinet.

  • Yield: 362 g
  • Dry content (IR drier, 15 minutes at 120° C.): 97.5%
  • K value (0.5% solution in distilled water): 208
  • Comparative polymer 8 (not in accordance with the invention, prepared according to WO-99/26991—copolymer of acryloyldimethyltaurate 60% by weight and acrylamide 40% by weight)

The comparative example is prepared analogously to comparative polymer 7. Rather than the amounts specified in comparative polymer 7, 210 g of acryloyldimethyltaurate and 140 g of acrylamide are used.

  • Yield: 371 g
  • Dry content (IR drier, 15 minutes at 120° C.): 95.5%
  • K value (0.5% solution in distilled water): 219
  • Comparative polymer 9 (not in accordance with the invention, prepared according to WO-99/26991—copolymer of acryloyldimethyltaurate 60% by weight and acrylamide 40% by weight)

The comparative example is prepared analogously to comparative polymer 7. Rather than the amounts specified in comparative polymer 7, 280 g of acryloyldimethyltaurate and 70 g of acrylamide are used.

  • Yield: 363 g
  • Dry content (IR drier, 15 minutes at 120° C.): 96%
  • K value (0.5% solution in distilled water): 201

Examples of Test Results

Testing is effected according to API spec. 10. In an atmospheric consistometer, the cement slurry is stirred/conditioned at analysis temperature and then, at the same temperature, the rheology is measured with the FANN model 35SA viscometer (at high temperature, conditioning is effected at 93° C. and the viscosity is measured) and the water loss is measured at below 120° C. with a Baroid HTHP filter press and at above 120° C. with the stirring fluid loss test apparatus. The setting times were determined with an Autoclave Engineers HTHP consistometer. Formulation of the cement slurries: ad 100% Dyckerhoff Class G Cement, 43.7% distilled water, 0.3% polymer.

Table 6 shows the water loss-reducing properties of selected abovementioned examples according to API spec. 10 at 35° C. (95° F.) in a static filtration test in the Baroid HTHP filter press. This makes it clear that it was possible with the polymers of the invention to considerably improve the reduction in water loss at low temperatures compared to the comparative examples. Comparative example 7 differs from comparative example 1 merely by a somewhat smaller amount of initiator (1.5 g rather than 2.0); the measured K value for both polymers mentioned is identical to the value reported in WO-99/26991 and is 212. Both polymers were synthesized by the same method as a precipitation polymer in tert-BuOH.

TABLE 6 API spec. 10 at 35° C. (95° F.) of the polymers of the invention compared to compared examples 1 amd 6 to 8 Rheology after mixing at 75° F. (24° C.), scale divisions API at X revolutions per minute fluid Polymer Concentration Revolutions per minute (rpm) loss No. % by wt. 600 300 200 100 6 3 mL 2 (P) 0.5 95 74 46 33 6 3 60 4 (P) 0.3 108 77 44 30 5 3.5 58 8 (P) 0.3 103 73 39 28 4 3 72 13 (P) 0.3 90 72 38 25 4 3 75 20 (P) 0.5 88 67 47 28 4.5 3.5 66 28 (P) 0.3 87 69 39 26 5 3 65 33 (P) 0.3 98 82 59 30 6 3.5 70 36 (P) 0.3 86 63 42 30 5 3.5 68 1 (C) 0.3 94 68 39 26 5 3 115 7 (C) 0.3 96 72 41 26 4.5 3.5 109 8 (C) 0.3 113 81 47 29 6 3 121 9 (C) 0.3 87 75 54 33 6 4 116 (P) = polymer (C) = comparative example

TABLE 7 API spec. 10 at 250° F. (121.1° C.) of the polymers of the invention compared to comparative examples 1 and 6 to 8 Rheology after mixing at 75° F. (24° C.), scale divisions API at X revolutions per minute fluid Polymer Concentration Revolutions per minute (rpm) loss No. % by wt. 600 300 200 100 6 3 mL 4 (P) 0.5 >300 174 119 65 7 4.5 42 2 (P) 0.5 295 164 113 62 7 4.5 44 13 (P) 0.5 >300 179 126 70 8 5 40 7 (P) 0.5 >300 174 123 68 7 4 43 31 (P) 0.5 >300 167 121 58 7.5 3.5 54 1 (C) 0.5 >300 168 117 64 7.5 5.0 52 7 (C) 0.5 >300 175 113 67 7 5 54 8 (C) 0.5 >300 187 129 72 8 6 60 9 (C) 0.5 >300 159 110 63 7 4.5 58 (P) = polymer (C) = comparative example

In table 6, it was possible to detect an improvement in the water loss-reducing properties at 95° F. The water loss-reducing properties of comparative example 7 by direct comparison with comparative example 1 show nearly identical values and demonstrate the reproducibility of the process used. Nevertheless, the water loss of comparative polymers 1 and 6 to 9 at an average of 115 mL+/−5 mL is distinctly higher than that of the polymers of the invention. The difference in the water loss of the polymers of the invention relative to the comparative polymers was between 30 and 55 mL. This demonstrates clearly that the addition of acrylic acid leads to a technical improvement at low temperatures.

Table 7 shows the water loss-reducing properties of selected abovementioned examples according to API spec. 10 at 250° F. (121.1° C.) in a static filtration test in the Baroid HTHP filter press. In this test too, it was possible to show that the polymers of the invention have a demonstrably lower water loss at temperatures between 80° F. and 300° F. and under identical experimental conditions than the polymers of WO-99/26991. Running the comparison between comparative example 7 of WO-99/26991 and comparative example 1 (according to EP 1045869) again, the good reproducibility of the process used is shown in this test as well. The use tests conducted according to API spec. 10 at 95° F. and 250° F. demonstrate clearly that addition of acrylic acid to the polymers of the invention leads to an improvement in the water loss-reducing properties.

Claims

1. A water-soluble or water-swellable polymer having a k value of 100 to 300, measured in 0.5% by weight solution in distilled water, containing and

a) 25-35 mol % of at least one recurrent structural unit of the formula (1)
in which R1, R2 are hydrogen, methyl or ethyl, A is linear or branched C1-C12-alkylene, and Q+ is H+, NH4+, Li+, Na+, K+, ½Ca++, ½Mg++, ½Zn++, ⅓Al+++, organic ammonium ions of the formula [HNR5R6R7]+ where R5, R6 and R7 may each independently be hydrogen, a linear or branched alkyl group having 1 to 22 carbon atoms, a linear or branched, mono- or polyunsaturated alkenyl group having 2 to 22 carbon atoms, a C6-C22-alkylamidopropyl group, a linear monohydroxyalkyl group having 2 to 10 carbon atoms or a linear or branched dihydroxyalkyl group having 3 to 10 carbon atoms, and where at least one of the R5, R6 and R7 radicals is not hydrogen, or mixtures of these ions,
b) 3 to 8 mol % of at least one recurrent structural unit of the formula (2)
in which R1 is hydrogen, methyl or ethyl, X+ is H+, NH4+, Li+, Na+, K+, ½Ca++, ½Mg++, ½Zn++, ⅓Al+++, organic ammonium ions of the formula [HNR5R6R7]+ where R5, R6 and R7 may each independently be hydrogen, a linear or branched alkyl group having 1 to 22 carbon atoms, a linear or branched, mono- or polyunsaturated alkenyl group having 2 to 22 carbon atoms, a C6-C22-alkylamidopropyl group, a linear monohydroxyalkyl group having 2 to 10 carbon atoms or a linear or branched dihydroxyalkyl group having 3 to 10 carbon atoms, and where at least one of the R5, R6 and R7 radicals is not hydrogen, or mixtures of these ions, B is a chemical bond, or a linear or branched alkylene group having 1 to 6 carbon atoms, and n is an integer from 0 to 5,
c) 57 to 72 mol % of at least one recurrent structural unit of the formula (3)
in which R1 is hydrogen, methyl or ethyl, and R3 and R4 are each independently hydrogen, methyl, ethyl, n-propyl, isopropyl or butyl.

2. The polymer as claimed in claim 1, wherein the at least one structural unit of the formula (1) is derived from monomers selected from the group consisting of acryloyldimethyltaurate, acryloyl-1,1-dimethyl-2-methyltaurate, acryloyltaurate, and acryloyl-N-methyltaurate.

3. The polymer as claimed in claim 1, wherein the at least one structural unit of the formula (2) is derived from methacrylic acid, acrylic acid, carboxyethyl acrylate or higher oligomers of the formula (2) in which n is an integer of 2 or more.

4. The polymer as claimed in claim 1, wherein the at least one structural unit of the formula (3) is derived from monomers selected from the group consisting of acrylamide, N-methylacrylamide, N-ethylacrylamide, N,N-diethylmethacrylamide, N,N-diethylacrylamide, N,N-dimethylmethacrylamide, N,N-dimethylacrylamide, N-isopropylacrylamide, N-tert-butylacrylamide and N-butylacrylamide.

5. The polymer as claimed in claim 1, wherein Q+ in formula (1) is selected from the group consisting of NH4+, Na+ and mixtures of these ions and X+ in formula (2) is selected from the group consisting of H+, NH4+, Na+ and mixtures of these ions.

6. The polymer as claimed in claim 1, containing 27.5 to 32.5 mol % of the structural units (1), 4.5 to 7.5 of the structural units (2) and 60 to 68 mol % of the structural units (3).

7. The polymer as claimed in claim 1, in which the neutralization level of the structural units of the formula (1) is 95 to 100 mol %.

8. The polymer as claimed in claim 1, in which n=0 in at least 70% of all the structural units of the formula (2).

9. The polymer as claimed in claim 1, in which n is 0 or 1.

10. The polymer as claimed in claim 1, in which formula (3) is derived from acrylamide.

11. The polymer as claimed in claim 1, which contains structural units of

a) 27.5 to 32.5 mol % of acryloyldimethyltaurate,
b) 4.5 to 7.5 mol % of acrylic acid, and
c) 60 to 68 mol % of acrylamide.

12. The polymer as claimed in claim 1, in which formula (1) represents acryloyldimethyltaurate, formula (2) represents acrylic acid and formula (3) represents acrylamide.

13. A process for preparing a polymer comprising the steps of polymerizing and

a) 25-35 mol % of at least one recurrent structural unit of the formula (1)
in which R1, R2 are hydrogen, methyl or ethyl, A is linear or branched C1-C12-alkylene, and Q+ is H+, NH4+, Li+, Na+, K+, ½Ca++, ½Mg++, % Zn++, ⅓Al+++, organic ammonium ions of the formula [HNR5R6R7]+ where R5, R6 and R7 may each independently be hydrogen, a linear or branched alkyl group having 1 to 22 carbon atoms, a linear or branched, mono- or polyunsaturated alkenyl group having 2 to 22 carbon atoms, a C6-C22-alkylamidopropyl group, a linear monohydroxyalkyl group having 2 to 10 carbon atoms or a linear or branched dihydroxyalkyl group having 3 to 10 carbon atoms, and where at least one of the R5, R6 and R7 radicals is not hydrogen, or mixtures of these ions,
b) 3 to 8 mol % of at least one recurrent structural unit of the formula (2)
in which R1 is hydrogen, methyl or ethyl, X+ is H+, NH4+, Li+, Na+, K+, ½Ca++, ½Mg++, ½Zn++, ⅓Al+++, organic ammonium ions of the formula [HNR5R6R7]+ where R5, R6 and R7 may each independently be hydrogen, a linear or branched alkyl group having 1 to 22 carbon atoms, a linear or branched, mono- or polyunsaturated alkenyl group having 2 to 22 carbon atoms, a C6-C22-alkylamidopropyl group, a linear monohydroxyalkyl group having 2 to 10 carbon atoms or a linear or branched dihydroxyalkyl group having 3 to 10 carbon atoms, and where at least one of the R5, R6 and R7 radicals is not hydrogen, or mixtures of these ions, B is a chemical bond, or a linear or branched alkylene group having 1 to 6 carbon atoms, and n is an integer from 0 to 5,
c) 57 to 72 mol % of at least one recurrent structural unit of the formula (3)
in which R1 is hydrogen, methyl or ethyl, and R3 and R4 are each independently hydrogen, methyl, ethyl, n-propyl, isopropyl or butyl via free-radical precipitation polymerization in a polar solvent, and the monomers are optionally neutralized prior to the polymerization, or the polymer is optionally neutralized after the polymerization, with ammonia, ammonium carbonate or organic amines or an Li+-, Na+-, K+-, Ca++-, Mg++-, Zn++- or Al+++-containing base.

14. The process as claimed in claim 13, wherein the polar solvent has a boiling point of 60 to 110° C.

15. The process as claimed in claim 13, wherein the polar solvent is a solvent mixture of and

d) water
e) at least one further polar solvent.

16. The process as claimed in claim 13, wherein the polar solvent comprises methanol, ethanol, 1-propanol, 2-propanol, 2-methyl-2-propanol, 1-butanol, 2-butanol, dimethyl ketone, diethyl ketone, pentan-2-one, butanone, tetrahydropyran, tetrahydrofuran, 2-methyltetrahydrofuran, 1,3-dioxane or 1,4-dioxane.

17. The process as claimed in claim 13, in which the polar solvent comprises 2-methylpropan-2-ol.

18. The process as claimed in claim 13, wherein the polar solvent comprises 1% to 5% by weight of water.

19. The process as claimed in claim 13, wherein 27.5 to 32.5 mol % of acryloyldimethyltaurate, and 4.5 to 7.5 mol % of acrylic acid, 60 to 68 mol % of acrylamide is subjected to free-radical precipitation polymerization a mixture of 1% to 8% by weight of water and 92% to 99% by weight of 2-methylpropan-2-ol, and the monomers prior to the polymerization or the polymer after the polymerization are/is optionally neutralized with ammonia, ammonium carbonate, sodium hydroxide, sodium carbonate.

20. (canceled)

21. (canceled)

22. A method for cementing deep wells using a cement slurry, wherein the cement slurry comprises a polymer as claimed in claim 1.

23. The method as claimed in claim 22, in which the polymer content is 0.05% to 5% by weight, based on the cement slurry.

24. A polymer mixture containing 25% to 75% by weight of a polymer as claimed in claim 1, and 25% to 75% by weight of starch, chemically modified starch or thermally modified starch.

Patent History
Publication number: 20180171207
Type: Application
Filed: May 31, 2016
Publication Date: Jun 21, 2018
Applicant: Clariant International Ltd. (Muttenz)
Inventors: Dirk FISCHER (Hahnheim), Christoph KAYSER (Mainz), Claudia DIEMEL (Gelnhausen), Jürgen TONHAUSER (Oestrich-Winkel), Michael SCHÄFER (Gründau-Rothenbergen)
Application Number: 15/737,205
Classifications
International Classification: C09K 8/487 (20060101); C08F 220/56 (20060101); C08L 33/26 (20060101); C08L 3/02 (20060101); C08L 3/04 (20060101); C04B 24/38 (20060101); C04B 24/26 (20060101); C08L 3/08 (20060101);