LASER FILM DEBONDING METHOD

Abstract

A laser-based coating removal method debonds a film from a substrate rather than ablating the film. A laser light is transmitted through a transparent film to an underlying bonding layer for bonding the film to one or more additional films and/or a substrate. The laser light is absorbed at the bonding layer and the transparent film is released. In some embodiments, after the transparent film is released it is able to be physically removed.

Description

RELATED APPLICATIONS

This patent application claims priority under U.S.C. 119(e) of the co-pending U.S. Provisional Patent Application No. 61/929,887, filed on Jan. 21, 2014, and entitled “LASER FILM DEBONDING METHOD,” which is hereby incorporated by reference in its entirety.

FIELD OF THE INVENTION

The present invention is generally directed to systems and methods of laser removal of coatings. More specifically, the present invention is directed to a method of removing a protective film without damaging the underlying substrate.

BACKGROUND OF THE INVENTION

In the maintenance and possibly manufacturing or rework of aircraft propellers it is required that certain damaged protective films be removed and fresh films be applied to refurbish the propellers and return them to use. Such rework or repair may also be required for large turbine blades of wind powered electric generators. Damage to propellers or blades often occurs from normal use such as wear and tear from high speed impact of rain and ice particles or bird strikes to sand and gravel impact. Some aircraft runways may consist of only a “dirt” strip or a sandy beach. As such, debris can become airborn and flow into the propeller or blade wash. Propeller damage may also result from military conflict or simple maintenance accidents.

A conventional example of an aircraft propeller and coating is that of a painted metal propeller. However, more recently developed high efficiency and light weight propellers are constructed of fiberglass or carbon fiber composite substrates rather than aluminum alloys. These propellers may have a protective coating other than paint. A possible coating may be polyurethane. These coatings may range in thickness from a few thousandths of an inch to many tens of thousands. Polyurethane is a well known material also used to protect hardwood floors in homes.

To maintain the propellers, the damaged protective film first needs to be removed. This removal presents a formidable practical problem. Conventional methods such as sanding, media blasting, scrapping or chiseling are both time consuming and may cause further damage to the underlying composite substrate therefore requiring further time consuming and expensive substrate repair after the old protective film is removed. FIG. 1 illustrates an approach to remove a protective film such as paint on metal such as a painted propeller. In this approach, the film is slowly ablated by decomposing the film in multiple passes of a scanned laser beam of appropriate optical characteristics. Typically, this approach also requires much power.

SUMMARY OF THE INVENTION

A laser-based coating removal method debonds a film from a substrate rather than ablating the film. A laser light is transmitted through a transparent film to an underlying bonding layer for bonding the film to one or more additional films and/or a substrate. The laser light is absorbed at the bonding layer and the transparent film is released. In some embodiments, after the transparent film is released it is able to be physically removed.

In one aspect, a method of removing a protective film from a substrate comprises transmitting a laser light through a transparent film to an underlying bonding layer and absorbing the laser light at the bonding at the layer, wherein as the laser light is absorbed at the bonding layer, the transparent film is released. After the transparent film is released, the released film is able to be physically lifted away from the substrate. Particularly, during the method the film remains substantially intact and not melted or deformed or decomposed. Additionally, there is no substantial thermal nor structural damage to the underlying substrate. In some embodiments, the film is polyurethane. In some embodiments, the substrate comprises fiberglass composite or carbon fiber and epoxy composite or composite foam material. The laser beam may be scanned in order to substantially clean up or prepare the substrate surface for strong adhesion of a new layer of protective coating. In some embodiments, the protective film ranges from 0.001 inches to 0.300 inches thickness. In some embodiments, the laser wavelength is in the near infrared. In further embodiments, the laser wavelength is 1064 nanometers. In some embodiments, the laser scanning method is completed by a machine such as an XY table. In some of these embodiments, the XY translator table is computer controlled. In some embodiments, the scanning method is manual such that a laser work head is moved by hand by over the work piece. Alternatively, the work head may be scanned over the work piece by a robot. In some embodiments, the substrate comprises a propeller blade, such as, from an aircraft or a hovercraft or a rotor blade such from a helicopter or from a wind turbine blade. In some embodiments, the laser is a pulsed Nd:YAG laser. In some embodiments, the laser average power is at least 10 watts. In further embodiments, the laser repetition rate is at least 100 per second. In some embodiments, a laser spot size ranges from 0.1 mm to 10 mm diameter.

In a further aspect, a method of removing a protective film from a substrate comprises transmitting a laser light through a first film layer to a second film layer above the substrate and absorbing the laser light at an adhering interface between the first film layer and the second film layer, wherein as the laser light is absorbed at the interface, the first film and the second film are debonded. In some embodiments, the first film layer and the second film layer comprise polyurethane. The first film layer remains intact as the first film and the second film are debonded. In some embodiments, the protective film layers range from 0.001 inches to 0.300 inches thickness. In some embodiments, the laser wavelength is in the near infrared. In further embodiments, the laser wavelength is 1064 nanometers.

In another aspect, a method of removing one or more protective films from a substrate comprises transmitting a laser light through one or more than one transparent films and absorbing the laser light at an adhering interface between a last film above the substrate and a second to last film, wherein as the laser light is absorbed at the interface, the last film and the second to the last film are debonded. In some embodiments, the last film above the substrate and the second to last film comprise polyurethane. The second to last film remains intact as the last film and the second to the last film are debonded. In some embodiments, the protective film layers range from 0.001 inches to 0.300 inches thickness. In some embodiments, the laser wavelength is in the near infrared. In further embodiments, the laser wavelength is 1064 nanometers.

In still a further aspect, a laser-based coating removal system to remove a coating from a surface comprises a laser source configured to provide a laser pulse, a laser scanning head coupled to the laser source and configured to direct the laser pulse onto a position on the surface, wherein the laser pulse is configured with a wavelength such that the laser pulse passes through one or more transparent films and to an underlying bonding layer, and wherein as the laser light is absorbed at the bonding layer, the one or more transparent films are released. In some embodiments, the laser scanning head is machine controlled. Alternatively, the laser scanning head is manually controlled such that the work head is moved by hand over the work piece. In some embodiments, the coating ranges from 0.001 inches to 0.300 inches thickness. In some embodiments, the laser wavelength is in the near infrared. In some embodiments, the laser wavelength is 1064 nanometers. In some embodiments, the laser comprises a pulsed Nd:YAG laser. In further embodiments, the laser average power is at least 10 watts. In some embodiments, the laser repetition rate is at least 100 per second. In further embodiments, a laser spot size ranges from 0.1 mm to 10 mm diameter.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 illustrates a prior system for removing a protective film from a surface in accordance with some embodiments.

FIGS. 2 and 3 illustrate a system for removing a protective film from a surface in accordance with some embodiments.

FIGS. 4-6 illustrate a method of removing a protective film from a surface in accordance with some embodiments.

DETAILED DESCRIPTION OF THE EMBODIMENTS

Embodiments of the invention are directed to a system and method for debonding a film from a substrate rather than ablating the film. A laser light is transmitted through a transparent film to an underlying bonding layer for bonding the film to one or more additional films and/or a substrate. The laser light is absorbed at the bonding layer and the transparent film is released. In some embodiments, after the transparent film is released it is able to be physically removed.

Reference will now be made in detail to implementations of a laser-based coating removal system and method as illustrated in the accompanying drawings. The same reference indicators will be used through the drawings and the following detailed description to refer to the same or like parts. In the interest of clarity, not all of the routine features of the implementations described herein are shown and described. It will also be appreciated that in the development of any such actual implementation, numerous implementation-specific decisions be made to achieve the developer's specific goals, such as compliance with application and business related constraints, and that these specific goals will vary from one implementation to another and from one developer to another. Moreover, it will be appreciated that such a development effort might be complex and time-consuming, but would nevertheless be a routine undertaking of engineering for those of ordinary skill in the art having the benefit of this disclosure.

The present invention takes a unique and efficient approach to film removal by de-bonding the film rather than laboriously ablating it. The removal of paint by laser method is a typical example of ablating. In ablation, the film is decomposed into simpler components such as carbon dioxide and water vapor. Alternatively the film can be rather exploded or pyrolized on a microscopic level—laser spot by laser spot—from the surface in thin layers as a laser makes pass after pass to, in effect, shave away the film (paint). This process while quite useful is time and energy consuming. Indeed for thicker films greater than a few thousandths of an inch “mils” the process can be time consuming taking perhaps minutes or hours per square foot of area while requiring a relatively high powered laser, say, hundreds of watts of average power.

In the case of removing relatively thick films from large propellers which may have on the order of 10 sq. ft of area per blade and which may range from a few mils to 100 mils thickness, if an ablation method were used, the process could take many hours or days to complete.

As shown in FIG. 1, a prior art system utilizes a series of laser light pulses 115 in order to remove a coating 125 from an underlying primer 121 and substrate 120. This ablation approach however, requires multiple passes, excess energy and time.

FIG. 2 illustrates an example of a system for debonding a film from a substrate rather than slowly ablating it. As shown in FIG. 2, the system comprises a laser source 210 that directs a laser pulse 215 to a location in order to remove a film 223 from a substrate 220. The film 223 is substantially translucent which enables the laser light pulse 215 to pass through the film 223 and be absorbed by an underlying primer and/or bonding layer 221 on a surface of the substrate 220. In some embodiments, the protective film 223 comprises a coating material such as polyurethane and the substrate comprises a metal and/or a composite such as carbon fiber or fiberglass. The laser light 215 is absorbed at the underlying primer and/or bonding layer 221 which causes debonding between the film 223 and the substrate 220.

The film 223 to be de-bonded from the substrate 220 is substantially transparent to the laser light 215 such that the film transmits the photonic energy to the underlying bonding layer 221. The underlying bonding layer 221 is then be substantially or at least sufficiently absorptive of the laser energy 215 at the laser wavelength. Consequently, when the laser energy 215 is absorbed by the bonding layer 221, the bonding molecules then substantially debond or locally decompose thereby releasing the overlying film 223. Once de-bonded, the overlying film 223 for the areas exposed to the laser light 215 can then be physically lifted away free of any connection to the substrate 220. In some embodiments, only one pass of the laser light 215 is required. In some embodiments, the laser source 210 comprises a computer controlled XY translator table. However, the laser source 210 is able to comprise any appropriately desired computer controlled or manually operated laser scanning head.

The bonding layer 221 may be a primer or other adhesive layer between the substrate 220 and the overlying film 223. In some embodiments, it is also a thin upper layer of the substrate itself as long as the bonding layer 221 substantially absorbs the laser energy 215. The absorbed energy breaks the bond locally in a very thin zone while leaving the overlying film 223 intact and not damaging the substrate 220.

In some embodiments, the laser source 215 is able to transmit a laser light through a first film layer to a second film layer above the substrate in order to debond the first film layer from the second film. As shown in FIG. 3, a laser source 310 directs a laser pulse 315 to a location in order to remove the first film 327 from the second film 323 and the substrate 320.

The first film 327 and/or upper film is substantially translucent which enables the laser light pulse 315 to pass through the first film 327 and be absorbed by an underlying primer and/or bonding layer 325 which provides an interface between the first film layer 327 and the second film layer 327. The first film layer 327 and the second film layer 323 are able to be transparent to the laser light 315 as long as the underlying primer and/or bonding layer 325 is able to absorb the laser light 315 energy. For example, as described above, in some embodiments, the first film 327 and the second film 323 comprise a transparent coating layer such as polyurethane. The laser light 315 is absorbed at the underlying primer and/or bonding layer 325 which causes debonding between the first film 327 and the second film 323. The underlying or second film layer 323 does not have to be the substrate 320. When the energy is absorbed, the bond breaks between the first film 327 and the second film 323, thus interlayer debonding is possible above the substrate 320.

FIG. 4 illustrates a method of removing a protective film from a substrate in accordance with the above embodiments. The method begins in the step 410. In the step 420, a laser light is transmitted through a protective film to an underlying bonding layer. In some embodiments, the protective film is a transparent film such as polyurethane. In the step 430, the laser light is absorbed at the bonding layer between the protective film and an underlying substrate. When the laser energy is absorbed by the bonding layer the bonding molecules then substantially debond or locally decompose thereby releasing the overlying film. Once de-bonded, the overlying film for the areas exposed to the laser light can then be physically lifted away free of any connection to the substrate. The method ends in the step 440.

As described above, the laser source is able to transmit a laser light through a first film layer to a second film layer above the substrate in order to debond the first film layer from the second film. FIG. 5 illustrates a method of removing a first and/or top coating layer from an underlying second and/or bottom coating layer. The method begins in the step 510. In the step 520, a laser light is transmitted through a first film layer and to a second film layer where the light is absorbed at an adhering interface between the first film layer and the second film layer in the step 530. The first film layer and the second film layer are able to be transparent to the laser light as long as the underlying primer and/or bonding layer is able to absorb the laser light energy. When the laser energy is absorbed by the adhering interface the adhering molecules then substantially debond or locally decompose thereby releasing the overlying film. Once de-bonded, the overlying first film for the areas exposed to the laser light can then be physically lifted away free of any connection to second film and the substrate. The method ends in the step 540.

Particularly, the laser light source is able to be used to in order to remove one or more than one transparent films from a substrate. For example, FIG. 6 illustrates a method of removing one or more than one protective layer from a substrate. The method begins in the step 610. In the step 620, a laser light is transmitted through one or more than one transparent films coupled to a substrate. In the step 630, the laser light is absorbed at an adhering and/or bonding interface between a last film above the substrate and a second to last film. As described above, when the laser energy is absorbed by the bonding layer the bonding molecules then substantially debond or locally decompose thereby releasing the overlying film. Once de-bonded, the overlying film for the areas exposed to the laser light can then be physically lifted away free of any connection to the substrate. The method ends in the step 640.

The key to this laser method is that the film to be de-bonded from a substrate is substantially transparent to the laser light such that the film transmits the photonic energy to the underlying bonding layer. The underlying bonding layer must then be substantially or at least sufficiently absorptive of the laser energy at the laser wavelength. When such laser energy is absorbed by the bonding layer the bonding molecules then substantially debond or locally decompose thereby releasing the overlying film. In such a method the overlying film for areas exposed to the laser light can now be physically lifted away free of any connection to the substrate.

Adjacent areas not exposed to the laser retain their strong bond. At such a boundary line if it is desired to remove the film at the laser treated areas, the de-bonded film can simply be cut away with a sharp tool (knife, scissor, razor blade) such as in the case of a local repair depot.

In some embodiments, laser light in the near infrared range, such as, approximately 1 micron, or more specifically, 1064 nanometers wavelength will substantially transmit through such a coating material as polyurethane. In some embodiments, a Nd:YAG laser will generate this light wavelength at high enough power for practical and economic application. Good transmission may occur even for thicknesses approaching 100 mils. The laser light is further able to be absorbed by underlying layers such as the top epoxy layer in a fiberglass or carbon fiber composite substrate. The absorption produces very localized and instantaneous heating at the poly and epoxy interface such as to break the bond between the two layers. At the same time the laser energy delivered (fluence) is not so large as to heat the poly layer to melting or flowing and neither overheats nor damages the composite fiberglass or carbon fiber substrate epoxy or composite matrix. By way of example, such laser treated areas barely reach human body temperature in a practical application. The laser energy is able to de-bond the layers with no flame hazard and without smoke or the observation of other vapors.

Scanning Methods

In some embodiments, the laser beam may be scanned over the work piece by a source machine where an “XY” transport table moves a work piece under a laser work head as is generally known in the art. Alternatively, the work piece may also be scanned manually by a hand held work head. Particularly, the work piece is able to be scanned using any appropriately desired method as known in the art.

Interface Clean Up

In some embodiments, the laser system may further be used to clean up a very thin layer of decomposed primer or adhesive layer which might result in the formation of a black “soot” that is created by the local laser heating and adhesive decomposition at the interface. After the film (polyurethane) is lifted away from the substrate (essentially in one piece) a very thin black sooty layer may remain on the substrate. The adhesive may be an epoxy compound.

In case it is desired to clean up the substrate prior to applying a new fresh coat of protective film (polyurethane), traditional manual methods such as fine sand papering and solvent wipe can be employed. However, the laser may also be used to clean the interface of soot while not creating sanding debris nor chemical waste. It has been found that the laser with substantially the same power and beam scanning setting as used in the de-bonding can clean the surface perhaps better than fine grit sandpaper. Notably a thin layer of bonding compound, which may be epoxy, remains and thereby the composite substrate is still covered.

In operation, the system and method for debonding a film from a substrate is able to quickly remove such films in minutes on a large propeller blade, consumes relatively little laser energy and does not damage the substrate. A composite substrate propeller blade of approximate 6 foot length with a protective polyurethane film a few mils to 100 mils thick can have its polyurethane coating de-bonded by laser in about 5 minutes while requiring only 300 watts average laser power at the surface. The method can work with a pulsed laser as low powered as 40 watts average power, but the debonding rate will be proportionally slower. Of course, the instantaneous laser power for a pulsed laser can be many tens of kilowatts per spot. The pulse duration for each spot is relatively short, such as 100 nanoseconds by example. Pulse repetition rate may be 10,000 per second by way of example.

The present invention takes a unique and efficient approach to film removal by de-bonding the film rather than laboriously ablating it. The method transmits laser light and photonic energy to an underlying bonding layer coupling a protective film to one or more additional layers and/or a substrate. When the laser energy is absorbed by the bonding layer the bonding molecules then substantially debond or locally decompose thereby releasing the overlying film. In such a method the overlying film for areas exposed to the laser light can now be physically lifted away free of any connection to the substrate. The film is quickly removed without damaging the substrates and while consuming relatively little laser energy. Accordingly, the laser film debonding method as described herein has many advantages.

The present invention has been described in terms of specific embodiments incorporating details to facilitate the understanding of the principles of construction and operation of the invention. Such reference herein to specific embodiments and details thereof is not intended to limit the scope of the claims appended hereto. It will be apparent to those skilled in the art that modifications may be made in the embodiment chosen for illustration without departing from the spirit and scope of the invention.

Claims

1. A method of removing a protective film from a substrate comprising:

a. transmitting a laser light through the protective film to an underlying and separately applied bonding layer, wherein the bonding layer adheres the protective film to the substrate; and

b. absorbing the laser light at the bonding at the layer,

wherein as the laser light is absorbed at the bonding layer, the protective film is released.

2. The method of claim 1, wherein the protective film comprises polyurethane.

3. The method of claim 1, wherein the substrate comprises fiberglass composite or carbon fiber and epoxy composite or composite foam material.

4. The method of claim 1, wherein the protective film ranges from 0.001 inches to 0.300 inches thickness.

5. The method of claim 1, wherein the laser wavelength is in the near infrared.

6. The method of claim 1, wherein the laser wavelength is 1064 nanometers.

7. The method of claim 1, wherein the laser scanning method is machine controlled.

8. The method of claim 1, wherein the scanning method is manual such that a laser work head is moved by hand by over the work piece.

9. The method of claim 1, wherein the laser comprises a pulsed Nd:YAG laser.

10. The method of claim 1, wherein the laser average power is at least 10 watts.

11. The method of claim 1, wherein the laser repetition rate is at least 100 per second.

12. The method of claim 1, wherein a laser spot size ranges from 0.1 mm to 10 mm diameter.

13. A method of removing a protective film from a substrate comprising:

a. transmitting a laser light at a wavelength to transmit through a first protective film layer to a separately applied adhering interface between the first protective film layer and a second protective film layer; and

b. absorbing the laser light at the adhering interface between the first film layer and the second film layer,

wherein as the laser light is absorbed at the adhering interface, the first film and the second film are debonded.

14. The method of claim 13, wherein the first film layer and the second film layer comprise polyurethane.

15. The method of claim 13, wherein the first film layer remains intact as the first film and the second film are debonded.

16. The method of claim 13, wherein the protective film layers range ranges from 0.001 inches to 0.300 inches thickness.

17. The method of claim 13, wherein the laser wavelength is in the near infrared.

18. The method of claim 13, wherein the laser wavelength is 1064 nanometers.

19. A method of removing one or more protective films from a substrate comprising:

a. transmitting a laser light at a wavelength to transmit through one or more than one protective films; and

b. absorbing the laser light at a separately applied adhering interface between a last film above the substrate and a second to last film,

wherein as the laser light is absorbed at the adhering interface, the last film and the second to the last film are debonded.

20. The method of claim 19, wherein the last film above the substrate and the second to last film comprise polyurethane.

21. The method of claim 19, wherein the second to last film remains intact as the last film and the second to the last film are debonded.

22. The method of claim 19, wherein the protective film ranges from 0.001 inches to 0.300 inches thickness.

23. The method of claim 19, wherein the laser wavelength is in the near infrared.

24. The method of claim 19, wherein the laser wavelength is 1064 nanometers.

25. A laser-based coating removal system to remove a protective film from a surface, the system comprising:

a. a laser source configured to provide a laser pulse;

b. a laser scanning head coupled to the laser source and configured to direct the laser pulse onto a position on the surface, wherein the laser pulse is configured with a wavelength such that the laser pulse transmits through the protective films to an underlying and separately applied bonding layer, wherein the bonding layer adheres the protective film to the surface, and wherein as the laser light is absorbed at the bonding layer, the one or more protective films are released.

26. The system of claim 25, wherein the laser scanning head is machine controlled.

27. The system of claim 25, wherein the laser scanning head is manually controlled such that the work head is moved by hand by over the work piece.

28. The system of claim 25, wherein the protective film ranges from 0.001 inches to 0.300 inches thickness.

29. The system of claim 25, wherein the laser wavelength is in the near infrared.

30. The system of claim 25, wherein the laser wavelength is 1064 nanometers.

31. The system of claim 25, wherein the laser comprises a pulsed Nd:YAG laser.

32. The system of claim 25, wherein the laser average power is at least 10 watts.

33. The system of claim 25, wherein the laser repetition rate is at least 100 per second.

34. The system of claim 25, wherein a laser spot size ranges from 0.1 mm to 10 mm diameter.