COATED ELECTRICAL OR ELECTRONIC DEVICE PROTECTED FROM LIQUID PENETRATION

Abstract

An electrical or electronic device comprising a polymeric coating, formed by exposing;the device to pulsed plasma comprising a compound of formula (I), where R1, R2, R3 and R4 are as defined in the specification, for a sufficient period of time to allow a polymeric layer to form on the surface of the electrical or electronic device. Devices of this type are protected from contamination by liquids, in particular environmental liquids.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is continuation of U.S. application Ser. No. 15/443,114, filed Feb. 27, 2017, which is a division of U.S. application Ser. No. 12/161,181, filed Nov. 12, 2008, which issued as U.S. Pat. No. 9,617,353 on Apr. 11, 2017, which is a U.S. national stage application under 35 U.S.C. § 371 of PCT/GB2007/000149, filed Jan. 19, 2007, which claims priority of United Kingdom application 0601117.5, filed Jan. 20, 2006 and U.S. provisional application 60/762,242, filed Jan. 26, 2006, each of the foregoing of which is incorporated by reference in its entirety.

BACKGROUND OF THE INVENTION

Field of the Invention

The present invention relates to novel products in the form of electronic or electrical devices, which are treated to protect them from liquid damage, for example from environmental damage in particular from water or other liquids, as well as to processes for their production.

Description of Related Art

It is well known that electronic and electrical devices are very sensitive to damage caused by contamination by liquids such as environmental liquids, in particular water. Contact with liquids, either in the course of normal use or as a result of accidental exposure, can lead to short circuiting between electronic components, and irreparable damage to circuit boards, electronic chips etc.

The problem is particularly acute in relation to small portable electronic equipment such as mobile phones, pagers, radios, hearing aids, laptop, notebook, palmtop computers and personal, digital assistants (PDAs), which can be exposed to significant liquid contamination when moved outside. In addition, they are prone to accidental exposure to liquids, for example if dropped or splashed.

In addition, other types of electronic or electrical devices are particularly prone to for example, environmental damage because of their location, for example outdoor lighting systems, radio antenna and other forms of communication equipment.

However, most devices of this type are damaged by accidental spillage or the like. Particular examples may include desktop devices such as keyboards, or instrumentation for instance used in control rooms.

A particular problem arises in relation to devices which are used in sound reproduction and which utilise transducers such as loudspeakers, microphones, ringers and buzzers. These are particularly susceptible to damage by liquid contamination, either as a result of accidental exposure or from environmental factors such as rain or spray in use. In many cases, the membranes or diaphragms used in the devices, particularly the most economical ones, are liquid absorbent to some degree, and when exposed to water for example, will absorb considerable amounts. This affects the operability of the transducer significantly and the quality of the sound reproduction therefore suffers.

Many microphones are provided with an open-pore foamed plastic enclosure surrounding the transducer. However, these must be gas permeable and they do not provide complete protection against liquid contamination.

In the past, this problem has been addressed by introducing further water protective measures in the microphones. In many cases, these comprise water-impermeable porous membranes such as polytetrafluoroethylene (PTFE) membranes (see for example WO/01/03468 or U.S. Pat. No. 5,420,570) into the device. In all cases, these membranes will reduce the sensitivity of the transducer and therefore have an adverse impact on sound quality.

In other cases, such as that described in GB 2,364,463, more rigid protective covers are provided, which are solid and holes into which pick-up devices are inserted. This solution is costly and complex and only suitable in certain limited situations.

Plasma deposition techniques have been quite widely used for the deposition of polymeric coatings onto a range of surfaces, and in particular onto fabric surfaces. This technique is recognised as being a clean, dry technique that generates little waste compared to conventional wet chemical methods. Using this method, plasmas are generated from organic molecules, which are subjected to an electrical field. When this is done in the presence of a substrate, the radicals of the compound in the plasma polymerise on the substrate. Conventional polymer synthesis tends to produce structures containing repeat units that bear a strong resemblance to the monomer species, whereas a polymer network generated using a plasma can be extremely complex. The properties of the resultant coating can depend upon the nature of the substrate as well as the nature of the monomer used and conditions under which it is deposited.

BRIEF SUMMARY OF THE INVENTION

The applicants have found that by utilising a specific type of monomer under particular deposition conditions, electronic or electrical devices having highly liquid repellent nano-coatings thereon can be produced, which does not affect the efficacy of the device.

DETAILED DESCRIPTION OF THE INVENTION

According to the present invention there is provided an electronic or electrical device having a polymeric coating, formed by exposing said device to pulsed plasma comprising a compound of formula (I)

where R¹, R² and R³ are independently selected from hydrogen, alkyl, haloalkyl or aryl optionally substituted by halo; and R⁴ is a group X—R⁵ where R⁵ is an alkyl or haloalkyl group and X is a bond; a group of formula —C(O)O(CH₂)_nY— where n is an integer of from 1 to 10 and Y is a bond or a sulphonamide group; or a group —(O)_PR⁶(O)_q(CH₂)_t— where R⁶ is aryl optionally substituted by halo, p is 0 or 1, q is 0 or 1 and t is 0 or an integer of from 1 to 10, provided that where q is 1, I is other than 0, for a sufficient period of time to allow a protective polymeric layer to form on the surface of the electrical or electronic device.

As used herein, the expression “in a gaseous state” refers to gases or vapours, either alone or in mixture, as well as aerosols.

The expression “protective polymeric layer” refers to polymeric layers which provide some protection against liquid damage, and in particular are liquid (such as oil- and water-) repellent. Sources of liquids from which the devices are protected include environmental liquids such as water, and in particular rain, as well as any other oil or liquid, which may be accidentally spilled.

As used herein, the term “electronic or electrical device” refers includes any piece of electrical or electronic equipment which may be used, as well as components thereof such as printed circuit boards (PCBs), transistors, resistors, electronic components or semi-conductor chips. In particular however, the coating is applied to the outer surface of a fully assembled device, for example the fully assembled mobile phone, or microphone. In such cases, the polymer layer will be applied to, for example an outer casing or foam cover, as well as any exposed components such as control buttons or switches, so as to prevent any liquid reaching the components within.

The applicants have found that the polymer layer forms across the entire surface of the device, including where the device includes different substrate materials, such as a combination of different plastics (including foamed plastic), metals and/or glass surfaces, and surprisingly therefore, the entire device is made liquid repellent. Even where these are not in a water-tight relationship, for example push buttons on a mobile phone which are not fused to the surrounding casing, the polymer layer deposited in this way is sufficiently repellent to prevent liquids penetrating the device around the edge of the buttons into the device. Thus it has been found that mobile phones for example, which are generally very sensitive to liquid damage, can be fully immersed in water after the treatment of the invention, without any lasting harm.

As the coating is carried out without requiring immersion in any liquids,there is no risk to the operations of the device as a result of exposure to this procedure.

This broad applicability makes the present procedure particularly advantageous.

Particular examples of electrical and electronic devices include communications devices such as mobile phones and pagers, radios, and sound and audio systems such as loudspeakers, microphones, ringers or buzzers, hearing aids, personal audio equipment such as personal CD, tape cassette or MP3 players, televisions, DVD players including portable DVD players, video recorders, digi and other set-top boxes such as Sky, computers and related components such as laptop, notebook or palmtop computers, personal digital assistants (PDAs), keyboards, or instrumentation, games consoles in particular hand-held playstations and the like, or outdoor lighting systems.

Other particular examples may include electrical or electronic components which are particularly at risk of water contamination, such as those used in transport vehicles include aircraft and other transport equipment such as trains, automobiles in addition to other vehicles such as those used by the Military, and other devices such as washing machines and dishwashers.

In a particular embodiment, the electronic or electrical device is a microphone. By utilising the method defined above, highly advantageous microphones have been produced. In particular, the main features and benefits of using this approach are that by coating for example the casing in particular the foam cover of the microphone, the transducer is protected from liquid contamination without any loss of sound quality. Levels of protection equal to or better than those achieved using membranes are achieved without any resultant “muffling” of the sound quality, which is a feature of the use of such membranes.

When applied to the foam cover, the layer does not affect porosity of the foam. In other words, the layer is not sufficient to block the pores of the foam or to affect the air permeability in any way. However, the entire surface of the pores is made liquid repellent, and this is sufficient to ensure that liquids do not penetrate the foam.

However, similar advantages occur in relation to devices which incorporate small microphones such as communications devices and sound and audio systems as defined above, and in particular mobile phones, where coating of the finished phone may further enhance the levels of protection.

Electronic or electrical devices treated in this way are protected to a significant degree, against water and oil damage.

Precise conditions under which the plasma polymerization takes place in an effective manner will vary depending upon factors such as the nature of the polymer, the electrical or electronic device etc. and will be determined using routine methods and/or the techniques.

Suitable plasmas for use in the method of the invention include non-equilibrium plasmas such as those generated by radiofrequencies (Rf), microwaves or direct current (DC). They may operate at atmospheric or sub-atmospheric pressures as are known in the art. In particular however, they are generated by radiofrequencies (Rf).

Various forms of equipment may be used to generate gaseous plasmas. Generally these comprise containers or plasma chambers in which plasmas may be generated. Particular examples of such equipment are described for instance in WO2005/089961 and WO02/28548, the content of which is incorporated herein by reference, but many other conventional plasma generating apparatus are available.

In general, the item to be treated is placed within a plasma chamber together with the material to be deposited in gaseous state, a glow discharge is ignited within the chamber and a suitable voltage is applied, which may be pulsed.

The gas used within the plasma may comprise a vapour of the monomeric compound alone, but it may be combined with a carrier gas, in particular, an inert gas such as helium or argon. In particular helium is a preferred carrier gas as this can minimises fragmentation of the monomer.

When used as a mixture, the relative amounts of the monomer vapour to carrier gas is suitably determined in accordance with procedures which are conventional in the art. The amount of monomer added will depend to some extent on the nature of the particular monomer being used, the nature of the laboratory disposable being treated, the size of the plasma chamber etc. Generally, in the case of conventional chambers, monomer is delivered in an amount of from 50-250 mg/min, for example at a rate of from 100-150 mg/min. Carrier gas such as helium is suitably administered at a constant rate for example at a rate of from 5-90, for example from 15-30 sccm. In some instances, the ratio of monomer to carrier gas will be in the range of from 100:1 to 1:100, for instance in the range of from 10:1 to 1:100, and in particular about 1:1 to 1:10. The precise ratio selected will be so as to ensure that the flow rate required by the process is achieved.

Alternatively, the monomer may be delivered into the chamber by way of an aerosol device such as a nebuliser or the like, as described for example in WO2003/097245 and WO03/101621, the content of which is incorporated herein by reference.

In some cases, a preliminary continuous power plasma, may be struck for example for from 2-10 minutes for instance for about 4 minutes, within the chamber. This may act as a surface pre-treatment step, ensuring that the monomer attaches itself readily to the surface, so that as polymerisation occurs, the coating “grows” on the surface. The pre-treatment step may be conducted before monomer is introduced into the chamber, in the presence of only the inert gas.

The plasma is then suitably switched to a pulsed plasma to allow polymerisation to proceed, at least when the monomer is present.

In all cases, a glow discharge, is suitably ignited by applying a high frequency voltage, for example at 13.56 MHz. This is suitably applied using electrodes, which may be internal or external to the chamber, but in the case of the larger chambers are internal.

Suitably the gas, vapour or gas mixture is supplied at a rate of at least 1 standard cubic centimetre per minute (sccm) and preferably in the range of from 1 to 100 sccm.

In the case of the monomer vapour, this is suitably supplied at a rate of from 80-300 mg/minute, for example at about 120 mg per minute depending upon the nature of the monomer, whilst the pulsed voltage is applied.

Gases or vapours may be drawn or pumped into the plasma region. In particular, where a plasma chamber is used, gases or vapours may be drawn into the chamber as a result of a reduction in the pressure within the chamber, caused by use of an evacuating pump, or they may be pumped or injected into the chamber as is common in liquid handling.

Polymerisation is suitably effected using vapours of compounds of formula (I), which are maintained at pressures of from 0.1 to 200 mtorr, suitably at about 80-100 mtorr.

The applied fields are suitably of power of from 40 to 500 W, suitably at about 100 W peak power, applied as a pulsed field. The pulses are applied in a sequence which yields very low average powers, for example in a sequence in which the ratio of the time on a time off is in the range of from 1:500 to 1:1500. Particular, examples of such sequence are sequences where power is on for 20-50 μs, for example about 30 μs, and off for from 1000 μs to 30000 μs, in particular about 20000 μs. Typical average powers obtained in this way are 0.01 W.

The fields are suitably applied from 30 seconds to 90 minutes, preferably from 5 to 60 minutes, depending upon the nature of the compound of formula (I) and the electrical or electronic device etc.

Suitably a plasma chamber used is of sufficient volume to accommodate multiple electrical or electronic devices, in particular when these are small in size, for example up to 20,000 microphone heads can be processed at the same time with ease and much more is capably with the correct size equipment.

A particularly suitable apparatus and method for producing electrical or electronic devices in accordance with the invention is described in WO2005/089961, the content of which is hereby incorporated by reference.

In particular, when using high volume chambers of this type, the plasma is created with a voltage as a pulsed field, at an average power of from 0.001 to 500 w/m³, for example at from 0.001 to 100 w/m³ and suitably at from 0.005 to 0.5 w/m³.

These conditions are particularly suitable for depositing good quality uniform coatings, in large chambers, for example in chambers where, the plasma zone has a volume of greater than 500 cm³, for instance 0.5 m³ or more, such as from 0.5 m³-10 m³ and suitably at about 1 m³. The layers formed in this way have good mechanical strength.

The dimensions of the chamber will be selected, so as to accommodate the particular electrical or electronic device being treated. For instance, generally cuboid chambers may be suitable for a wide range of applications, but if necessary, elongate or rectangular chambers may be constructed or indeed cylindrical, or of any other suitable shape.

The chamber may be a sealable container, to allow for batch processes, or it may comprise inlets and outlets for electrical or electronic devices, to allow it to be utilised in a continuous process. In particular in the latter case, the pressure conditions necessary for creating a plasma discharge within the chamber are maintained using high volume pumps, as is conventional for example in a device with a “whistling leak”. However it will also be possible to process certain items at atmospheric pressure, or close to, negating the need for “whistling leaks”

The monomers used are selected from monomers of formula (I) as defined above. Suitable haloalkyl groups for R¹, R², R³ and R⁵ are fluoroalkyl groups. The alkyl chains may be straight or branched and may include cyclic moieties.

For R⁵, the alkyl chains suitably comprise 2 or more carbon atoms, suitably from 2-20 carbon atoms and preferably from 6 to 12 carbon atoms.

For R¹, R² and R³, alkyl chains are generally preferred to have from 1 to 6 carbon atoms.

Preferably R⁵ is a haloalkyl, and more preferably a perhaloalkyl group, particularly a perfluoroalkyl group of formula C_mF_2m+1 where m is an integer of 1 or more, suitably from 1-20, and preferably from 4-12 such as 4, 6 or 8.

Suitable alkyl groups for R¹, R² and R³ have from 1 to 6 carbon atoms.

In one embodiment, at least one of R¹, R² and R³ is hydrogen. In a particular embodiment R¹, R², R³ are all hydrogen. In yet a further embodiment however R³ is an alkyl group such as methyl or propyl.

Where X is a group —C(O)O(CH₂)_nY—, n is an integer which provides a suitable spacer group. In particular, n is from 1 to 5, preferably about 2.

Suitable sulphonamide groups for Y include those of formula —N(R⁷)SO₂⁻ where R⁷ is hydrogen or alkyl such as C_1-4alkyl, in particular methyl or ethyl.

In one embodiment, the compound of formula (I) is a compound of formula (II)

CH₂═CH—R⁵   (II)

where R⁵ is as defined above in relation to formula (I).

In compounds of formula (II), X in formula (I) is a bond.

However in a preferred embodiment, the compound of formula (I) is an acrylate of formula (III)

CH₂═CR⁷C(O)O(CH₂)_nR⁵   (III)

where n and R⁵ as defined above in relation to formula (I) and R⁷ is hydrogen, C_1-10 alkyl, or C_1-10haloalkyl. In particular R⁷ is hydrogen or C_1-6alkyl such as methyl. A particular example of a compound of formula (III) is a compound of formula (IV)

where R⁷ is as defined, above, and in particular is hydrogen and x is an integer of from 1 to 9, for instance from 4 to 9, and preferably 7. In that case, the compound of formula (IV) is 1H,1H,2H,2H-heptadecafluorodecylacylate.

In a further aspect, the invention provides a method for protecting an electrical or electronic device against liquid damage said method comprising exposing said device to a pulsed plasma, comprising a compound of formula (I)

where R¹, R² and R³ are independently selected from hydrogen, alkyl, haloalkyl or aryl optionally substituted by halo; and

R⁴ is a group X—R⁵ where R⁵ is an alkyl or haloalkyl group and X is a bond; a group of formula —C(O)O(CH₂)_nY— where n is an integer of from 1 to 10 and Y is a bond or a sulphonamide group; or a group —(O)_PR⁶(O)_q(CH₂)_t— where R⁶ is aryl optionally substituted by halo, p is 0 or 1, q is 0 or 1 and t is 0 or an integer of from 1 to 10, provided that where q is 1, t is other than 0, in a gaseous state for a sufficient period of time to allow a protective polymeric layer to form on the surface of the electrical or electronic device.

Liquid damage from which these devices are protected include environmental liquids such as water and in particular rain, or any other liquid, which may be accidentally spilled onto the device.

Suitably, the electrical or electronic device is placed in a plasma deposition chamber, a glow discharge is ignited within said chamber, and a voltage applied as a pulsed field.

Suitable monomers and reaction conditions for use in this method are as described above.

The invention will now be particularly described by way of example.

EXAMPLE 1

Microphones

A set of 100 microphones were placed into a plasma chamber with a processing volume of ˜300 litres. The chamber was connected to supplies of the required gases or vapours, via a mass flow controller and/or liquid mass flow meter and a mixing injector or any other vapour/gas introduction mechanism as appropriate.

The chamber was evacuated to between 3-10 mtorr base pressure before allowing helium into the chamber at 20 sccm until a pressure of 80 mtorr was reached. A continuous power plasma was then struck for 4 minutes using RF at 13.56 MHz at 300 W.

After this period, 1H,1H,2H,2H-heptadecafluorodecylacylate (CAS 27905-45-9) of formula

was brought into the chamber at a rate of 120 milligrams per minute and the plasma switched to a pulsed plasma at 30 micro seconds on-time and 20 milliseconds off-time at a peak power of 100 W for 40 minutes. On completion of the 40 minutes the plasma power was turned off along with the processing gases and vapours and the chamber evacuated back down to base pressure. The chamber was then vented to atmospheric pressure and the microphone heads removed.

It was found that the microphone heads were covered with a water and oil-repellent that protected it from challenge with water.

Claims

1. An electrical or electronic device having a polymeric coating, formed by exposing said device to pulsed plasma comprising a compound of formula (I)

where R1, R2 and R3 independently are selected from hydrogen, alkyl, haloalkyl or aryl optionally substituted by halo; and R4 is a group X—R5 where R5 is an alkyl or haloalkyl group and X is a bond; a group of formula —C(O)O(CH2)nY— where n is an integer of 1 to 10 and Y is a bond or a sulphonamide group; or a group —(O)pR6(O)q(CH2)t— where R6 is aryl optionally substituted by halo, p is 0 or 1, q is 0 or 1 and t is 0 or an integer of 1 to 10, provided that where q is 1, t is other than 0, for a sufficient period of time to allow a protective polymeric layer to form on the surface of the electrical or electronic device.

2. An electrical or electronic device according to claim 1, which is selected from communications devices, sound or audio systems devices, computers or computer-related components, outdoor lighting systems, or electrical or electronic devices used in transport vehicles, washing machines and dishwashers; or components of any of these.

3. An electrical or electronic device according to claim 2, which is a sound or audio system device.

4. An electrical or electronic device according to claim 3, which is a loudspeaker, microphone, ringer or buzzer.

5. An electrical or electronic device according to claim 4 comprising a microphone that comprises a foamed plastic cover and the polymeric layer is present thereon.

6. An electrical or electronic device according to claim 1, wherein any alkyl chains in R1, R2 or R3, have 1 to 6 carbon atoms.

7. An electrical or electronic device according to claim 1, wherein at least one of R1, R2 and R3 is hydrogen.

8. An electrical or electronic device according to claim 1, wherein R3 is an alkyl group such as methyl or propyl.

9. An electrical or electronic device according to claim 1, wherein the compound of formula (I) is a compound of formula (II)

CH2═CH—R5   (II)

where R5 is as defined in claim 1, or a compound of formula (III) CH2═CR7C(O)O(CH2)nR5   (III)

where n and R5 are as defined in claim 1 and R7 is hydrogen, C1-10 alkyl, or C1-10haloalkyl.

10. An electrical or electronic device according to claim 1, wherein R5 comprises an alkyl group having in the range of 6 to 12 carbon atoms.

11. An electrical or electronic device according to claim 1, wherein R5 comprises a perfluoroalkyl group of formula CmF2m+1 where m is an integer of 1 or more, preferably 1-20, and more preferably 4-12 such as 4, 6 or 8.

12. An electrical or electronic device according to claim 9, wherein the compound of formula (III) is a compound of formula (IV)

where R7 is as defined in claim 9, and x is an integer of 1 to 9.

13. An electrical or electronic device according to claim 12, wherein the compound of formula (IV) is 1H,1H,2H,2H-heptadecafluorodecyl acrylate.