METHODS OF 3D PRINTING ARTICLES WITH PARTICLES
The present invention generally relates to methods of printing articles using three-dimensional printing and other printing techniques, and to articles formed from such techniques, including the printing of articles containing particles. Certain embodiments are generally directed to composites comprising particles (e.g., reinforcing particles), for example, rubber particles. The particles may be used, for example, to increase slip or abrasion resistance. The composites may also contain polyurethanes or other compounds, e.g., to facilitate fabrication, e.g., using three-dimensional printing and other printing techniques. Other embodiments are directed to methods of making or using such articles. For example, in some embodiments, a composite may be prepared by mixing particles (e.g., reinforcing particles) with at least a first fluid and a second fluid within a nozzle, such as a microfluidic printing nozzle, which may be used to direct the resulting product onto a substrate.
Latest VoxeI8,Inc. Patents:
The present invention generally relates to methods of printing articles using three-dimensional printing and other printing techniques, and to articles formed from such techniques, including the printing of articles containing particles.
BACKGROUNDThe manufacture of composites may involve the expensive and environmentally hazardous synthesis and incorporation of new materials. In addition, the properties of composites may be difficult to control. Improved methods of manufacture of composites are thus needed.
SUMMARYThe present invention generally relates to methods of printing articles using three-dimensional printing and other printing techniques, and to articles formed from such techniques, including the printing of articles containing particles. The subject matter of the present invention involves, in some cases, interrelated products, alternative solutions to a particular problem, and/or a plurality of different uses of one or more systems and/or articles.
In one aspect, the present invention is generally directed to a method. In some cases, the method includes a method for printing an article, e.g., 3D-printing an article, e.g., for use in footwear. In one set of embodiments, the method includes receiving object information associated with the article; identifying a target material to be printed using the object information; identifying two or more input materials to create the target material, at least one of the two or more input materials comprising particles (e.g., reinforcing particles); identifying a set of printer settings for printing the target material; generating print instructions using the set of printer parameters; and printing the article using the print instructions.
The method, in another set of embodiments, includes flowing a first fluid through a first inlet into a nozzle; flowing a second fluid through a second inlet into the nozzle; flowing particles (e.g., reinforcing particles) into the nozzle; mixing the first fluid, the second fluid, and the particles (e.g., reinforcing particles) to form a mixture within the nozzle; and printing the mixture onto a substrate from the nozzle.
In one set of embodiments, the method includes flowing a fluid into a microfluidic printing nozzle, flowing particles (e.g., reinforcing particles) into the nozzle, mixing the fluid and the particles (e.g., reinforcing particles) within the microfluidic printing nozzle using an impeller to form a mixture, and printing the mixture onto a substrate.
In another set of embodiments, the method includes flowing a first fluid through a first inlet and a second fluid through a second inlet into a microfluidic printing nozzle, where the first fluid comprises a foam precursor and the second fluid comprises a cell-forming agent, homogenously mixing the first fluid and the second fluid to form a mixture, and printing the mixture onto a substrate.
The method, in another set of embodiments, includes flowing a fluid into a microfluidic printing nozzle, mixing the fluid with a gas within the microfluidic printing nozzle using an impeller to form a froth comprising bubbles of the gas dispersed within the fluid, and printing the froth onto a substrate.
In another set of embodiments, the method comprises acts of mixing a first fluid and a second fluid in a mixing chamber to form a foam precursor, flowing the foam precursor and a cell-forming agent into a microfluidic printing nozzle, rotating an impeller within the microfluidic printing nozzle to form a mixture of the foam precursor and the cell-forming agent, and printing the mixture onto a substrate.
The method, in still another set of embodiments comprises flowing at least two inputs into a mixing nozzle to form a first mixture comprising a blowing agent. The method may further comprise flowing at least two inputs into a mixing nozzle to form a second mixture. A first region comprising the first mixture may be deposited to form a first elastomer. A second region comprising the second mixture may be deposited to form a second elastomer. At least the first region of the article may be heated to a temperature greater than or equal to the activation temperature of the blowing agent. In some embodiments, heating at least the first region of the article causes differential expansion between the first region and the second region of the article and physical deformation of the article.
In another aspect, the present invention is generally directed to an article. In some embodiments, the article is an article for use in footwear. In some embodiments, the article includes a 3D-printed composite comprising a plurality of particles (e.g., reinforcing particles) having a largest numerical average dimension of greater than or equal to 10 microns and less than or equal to 400 microns.
In another set of embodiments, the article is a 3D-printed article for use in footwear. In some embodiments, the article includes a 3D-printed article having a gradient in a property between a first portion and a second portion, wherein the 3D-printed article is a single integrated material, and wherein the property is selected from the group consisting of average largest dimension of particles (e.g., reinforcing particles), weight percent of particles (e.g., reinforcing particles), volume percent of particles (e.g., reinforcing particles), compression strength, slip resistance, abrasion resistance, density, stiffness, heat deflection temperature, pore concentration, pore size, and coefficient of thermal expansion.
In some embodiments, the article comprises a polymeric structure. The article may comprise particles (e.g., reinforcing particles) distributed in the polymeric structure to form a gradient of the weight percent of particles (e.g., reinforcing particles) in the polymeric structure. In some embodiments, a textile is adhered to the polymeric structure.
In some embodiments, the article comprises a polymeric structure and an unexpanded chemical blowing agent in at least a portion of the polymeric structure. In some embodiments, a textile is adhered to at least a portion of the polymeric structure.
In another aspect, the present invention is generally directed to a device. In some embodiments, the device is a device for printing, e.g., 3D-printing. According to one set of embodiments, the device comprises a first microfluidic printing nozzle comprising a first mixing chamber and a first impeller disposed therein, a second microfluidic printing nozzle comprising a second mixing chamber and a second impeller disposed therein, the second nozzle further comprising an input in fluid communication with an outlet of the first nozzle, and a controller configured and arranged to independently control rotation of the first impeller and the second impeller.
In another set of embodiments, the device comprises a microfluidic printing nozzle comprising a mixing chamber and an impeller disposed therein, a heat source or a cooling source in thermal communication with the nozzle, and a controller constructed and arranged to control rotation of the impeller.
The device, in yet another set of embodiments, includes a microfluidic printing nozzle comprising a mixing chamber and an impeller disposed therein, and a controller constructed and arranged to laterally move the impeller within the microfluidic printing nozzle.
The nozzle may be controlled, for example, using a computer or other controller, in order to control the deposition of the product onto the substrate. In some cases, gases or other materials may be incorporated into the product within the nozzle, e.g., to form a foam.
Other advantages and novel features of the present invention will become apparent from the following detailed description of various non-limiting embodiments of the invention when considered in conjunction with the accompanying figures.
Non-limiting embodiments of the present invention will be described by way of example with reference to the accompanying figures, which are schematic and are not intended to be drawn to scale. In the figures, each identical or nearly identical component illustrated is typically represented by a single numeral. For purposes of clarity, not every component is labeled in every figure, nor is every component of each embodiment of the invention shown where illustration is not necessary to allow those of ordinary skill in the art to understand the invention. In the figures:
The present invention generally relates to the printing of materials using three-dimensional printing and other printing techniques, and to articles formed from such techniques. In some embodiments, the articles may be articles for use in footwear. Certain embodiments are generally directed to composites comprising particles (e.g., reinforcing particles), for example, rubber particles. The particles may be used, for example, to increase slip or abrasion resistance. The composites may also contain polyurethanes or other compounds, e.g., to facilitate fabrication, e.g., using three-dimensional printing and other printing techniques. Other embodiments are directed to methods of making or using such articles. For example, in some embodiments, a composite may be prepared by mixing particles (e.g., reinforcing particles) with at least a first fluid and a second fluid within a nozzle, such as a microfluidic printing nozzle, which may be used to direct the resulting product onto a substrate.
In some embodiments, an article that is printed (e.g., 3D-printed) may comprise a composite. In some embodiments, a composite may comprise a matrix and a plurality of particles (e.g., reinforcing particles). The matrix may include materials such as polyurethane or other suitable polymers, which may be used to facilitate manufacturing of articles. Examples of polyurethanes and other suitable polymers include those described in greater detail below. In some embodiments, the composite may comprise a foam, although this is not a requirement in every embodiment. The particles (e.g., reinforcing particles), in some cases, may provide for increased slip resistance, e.g., due to increased friction. In some cases, the particles may provide increased toughness or resistance to abrasion, for example, of a surface. In certain cases, the particles may be used for texture, for example, to produce a coarser or more bumpy surface texture to an article, to produce a certain appearance or “sheen” to the surface of an article, or the like. In some embodiments, the particles (e.g., reinforcing particles) may comprise rubber. The rubber may arise from any suitable source, and may include virgin and/or recycled rubber. The rubber may be natural rubber and/or synthetically produced rubber. Examples of rubber include, but are not limited to, ground tire rubber, recycled tire rubber, or the like. The rubber forming the particles may comprise a variety of polymers, including but not limited to, natural rubber (e.g., latex rubber), styrene butadiene (SBR), polyacrylics, polyvinyl acetate (PVA), polyvinyl chloride (PVC), polychloroprene (neoprene), polyurethanes, butyl rubbers, or the like. Combinations of these and/or other rubbers may also be used in some cases. It should be noted that in some cases, the exact composition of polymers in rubber particles is unknown. As examples, the rubber may arise from a variety of natural sources (and thus comprise a variety of different polymers), the rubber may have been recycled from different sources (e.g., tires, pencil erasers, balloons, footwear, or the like), etc. For example, in one set of embodiments, recycled rubber from sources such as discarded tires may be formed into particles using techniques such as mechanical grinding, cryogenic grinding, milling, cutting, shredding, screening, etc.
In addition, in other embodiments, other materials may be used for reinforcing particles, e.g., in addition to and/or instead of rubber particles. Non-limiting examples include silica, fumed silica, silicon carbide, titanium dioxide, fibers, carbon, carbon fiber, gypsum, glass fiber, calcium carbonates, nanorods, microrods, carbon fibers, thermoplastics, or the like. In some embodiments, the particles may comprise silicone particles, wax particles, or polytetrafluoroethylene particles, or combinations thereof. In some embodiments, the particles (e.g., reinforcing particles) may comprise a thermoplastic polyurethane that has a blowing agent inside that has yet to be expanded, or an expanded thermoplastic polyurethane. In some embodiments, the particles (e.g., reinforcing particles) comprise a blowing agent that decomposes to gas above an activation temperature. In some embodiments, the particles comprise azodicarbonamide particles, sodium bicarbonate particles, hydrazine particles, toluenesulfonylhydrazine particles, or oxybisbenzenesulfonylhydrazine particles, or combinations thereof. In some embodiments, reinforcing particles may comprise hollow or solid spheres. Such spheres may comprise, as non-limiting examples, glass or polyurethane. For example, the spheres may be hollow elastomer spheres (e.g., hollow polyurethane spheres), and the density of a composite including these spheres may be reduced relative to the density of a substantially similar composite not including these spheres.
Particles (e.g., reinforcing particles) may, in some embodiments, have a largest numerical average dimension of at least 10 microns, at least 20 microns, at least 30 microns, at least 40 microns, at least 50 microns, at least 60 microns, at least 70 microns, at least 80 microns, at least 90 microns, at least 100 microns, at least 150 microns, at least 200 microns, at least 250 microns, at least 300 microns, at least 350 microns, at least 400 microns, at least 500 microns, at least 700 microns, or at least 900 microns. In some embodiments, the particles (e.g., reinforcing particles) may have a largest numerical average dimension of at most 1000 microns, at most 900 microns, at most 700 microns, at most 500 microns, at most 400 microns, at most 350 microns, at most 300 microns, at most 250 microns, at most 200 microns, at most 150 microns, at most 100 microns, at most 90 microns, at most 80 microns, at most 70 microns, at most 60 microns, at most 50 microns, at most 40 microns, at most 30 microns, or at most 20 microns. Combinations of the above-referenced ranges are also possible (e.g., at least 10 microns and at most 1000 microns, or at least 50 microns and at most 400 microns, or at least 50 microns and at most 250 microns). The particles may be spherical and/or non-spherical. In some cases, the particles may be present in a range of sizes and/or shapes (e.g., as in the case of crumb rubber or ground tire rubber).
In some embodiments, the surfaces of the particles (e.g., reinforcing particles) may be functionalized. Functionalization is given its ordinary meaning in the art and may refer to the process of changing the surface chemistry of a material (particles, e.g., reinforcing particles, e.g., comprising rubber). In some embodiments, functionalization involves covalently and/or non-covalently attaching molecules to the material. In some embodiments, functionalization of the particles (e.g., reinforcing particles) is carried out prior to mixing the particles (e.g., reinforcing particles) with other material(s) (e.g., a first fluid, a first fluid and a second fluid, etc.). This functionalization of particles (e.g., reinforcing particles) may be carried out in order to improve, as non-limiting examples, certain aspects of the process of mixing the particles (e.g., reinforcing particles) with other materials (e.g., fluids), or properties of a three-dimensionally printed composite that results from depositing (e.g., 3D-printing) the resulting mixture onto a substrate and allowing it to solidify.
For example, by functionalizing the particles (e.g., reinforcing particles) prior to introducing the particles into a mixing nozzle, into which one or more other materials (e.g., fluids) are also introduced, the process of mixing the particles (e.g., reinforcing particles) with the one or more materials (e.g., fluids) may be improved by reducing the viscosity of the composition in the mixing nozzle. In this example, the composition in the mixing nozzle comprises the particles (e.g., reinforcing particles) and one or more materials (e.g., fluids). As another non-limiting example, functionalizing the particles (e.g., reinforcing particles) prior to introducing the particles into a mixing nozzle, into which one or more other materials (e.g., fluids) are also introduced, may improve the mechanical properties (e.g., decrease the maximum local stiffness, increase the overall toughness) of a three-dimensionally printed composite that results from depositing (e.g., 3D-printing) the resulting mixture onto a substrate and allowing it to solidify. These mechanical property improvements may be compared to a substantially similar composite comprising non-functionalized particles (e.g., reinforcing particles).
In some embodiments, functionalization of the particles (e.g., reinforcing particles) may improve the properties of the composition in the mixing nozzle and/or of the deposited (e.g., 3D-printed) solidified composite by means of, as a non-limiting example, improving the dispersion (e.g., minimizing aggregation) of the particles (e.g., reinforcing particles) in the matrix (e.g., comprising polyurethane) of the composite. This may be useful, for example, in embodiments in which the particles (e.g., reinforcing particles) are introduced into a mixing nozzle at a high loading relative to the total volume of the composition (e.g., greater than or equal to 50 volume percent of the composition in the mixing nozzle). As a non-limiting example, the surfaces of the particles (e.g., reinforcing particles) may be functionalized with a silane. Non-limiting examples of silanes include (3-aminopropyl)triethoxysilane, 3-glycidyloxy propyltriethoxysilane, 3-glycidyloxy propyltrimethoxysilane, polyether-functional trimethoxysilane, and vinylsilane. Other non-limiting examples of chemical groups with which to functionalize the surfaces of the particles (e.g., reinforcing particles) include alkyl groups, hydroxyl groups, isocyanate groups, amine groups, amide groups, aromatic groups, glycidyl groups, epoxide groups, vinyl groups, acrylate groups, and methacrylate groups. The surfaces of the particles (e.g., reinforcing particles) may be functionalized, as another non-limiting example, to facilitate bonding (e.g., covalently bonding) of the particles to the matrix material, e.g., chemically. This may result, for example, in higher strength and/or abrasion resistance than in a substantially similar composite wherein the particles (e.g., reinforcing particles) are not bound. In some cases, at least 50%, at least 75%, or at least 90% of the surfaces of the particles may be functionalized, e.g., with silanes and/or other functional moieties as discussed herein.
In some embodiments, the incorporation of particles (e.g., reinforcing particles) into a composite may result in a change (e.g., an improvement) in the performance of the composite with respect to one or more properties (e.g., abrasion resistance, slip resistance, or the like). As a non-limiting example, a composite having particles (e.g., reinforcing particles) may have greater abrasion resistance and/or greater slip resistance than a substantially similar composite lacking such particles. As another non-limiting example, a composite may have a lower overall density than a substantially similar composite lacking particles (e.g., reinforcing particles).
In some embodiments, the incorporation of a certain type of particles (e.g., reinforcing particles) into the matrix of the composite may result in a change (e.g., an improvement) in the performance of the composite with respect to one or more properties (e.g., physical properties, environmental sustainability, cost, or the like). In some cases, the use of a filler (e.g., ground tire rubber) may be beneficial in the object of environmental sustainability. As a non-limiting example, less waste may be produced in producing a composite comprising recycled materials, such as ground tire rubber particles.
In addition, certain aspects of the invention are generally directed to methods for printing an article, for example, an article comprising a composite (e.g., a composite comprising particles, e.g., reinforcing particles).
In some embodiments, printing an article (e.g., comprising a composite) may include flowing particles (e.g., reinforcing particles, e.g., comprising recycled tire rubber) into a nozzle (see, e.g.,
In some embodiments, the particles (e.g., reinforcing particles) may be present in an article, e.g., after formation, such that the article has a weight percent of particles (e.g., reinforcing particles) of at least 5 wt %, at least 10 wt %, at least 15 wt %, at least 20 wt %, at least 25 wt %, at least 30 wt %, at least 35 wt %, at least 40 wt %, at least 45 wt %, at least 50 wt %, at least 55 wt %, at least 60 wt %, at least 65 wt %, at least 70 wt %, at least 75 wt %, at least 80 wt %, or at least 85 wt % with respect to the total weight of the article. In some embodiments, the article has a weight percent of particles (e.g., reinforcing particles) of at most 90 wt %, at most 85 wt %, at most 80 wt %, at most 75 wt %, at most 70 wt %, at most 65 wt %, at most 60 wt %, at most 55 wt %, at most 50 wt %, at most 45 wt %, at most 40 wt %, at most 35 wt %, at most 30 wt %, at most 25 wt %, at most 20 wt %, at most 15 wt %, or at most 10 wt % with respect to the total weight of the article. Combinations of the above-referenced ranges are also possible (e.g., at least 5 wt % and at most 90 wt %).
In some embodiments, the particles (e.g., reinforcing particles) may be present in an article, e.g., after formation, such that the article has a volume percent of particles (e.g., reinforcing particles) of at least 5 vol %, at least 10 vol %, at least 15 vol %, at least 20 vol %, at least 25 vol %, at least 30 vol %, at least 35 vol %, at least 40 vol %, at least 45 vol %, at least 50 vol %, at least 55 vol %, at least 60 vol %, at least 65 vol %, or at least 70 vol % with respect to the total volume of the article. In some embodiments, the article has a volume percent of particles (e.g., reinforcing particles) of at most 74 vol %, at most 70 vol %, at most 65 vol %, at most 60 vol %, at most 55 vol %, at most 50 vol %, at most 45 vol %, at most 40 vol %, at most 35 vol %, at most 30 vol %, at most 25 vol %, at most 20 vol %, at most 15 vol %, or at most 10 vol % with respect to with respect to the total volume of the article. Combinations of the above-referenced ranges are also possible (e.g., at least 5 vol % and at most 74 vol %).
In some embodiments, as discussed in more detail below, printing a mixture onto a substrate may comprise depositing the mixture onto a substrate in a layer. In some embodiments, printing the mixture onto a substrate may comprise depositing the mixture onto a substrate in a plurality of layers. Printing in a plurality of layers may involve depositing the mixture onto a substrate in a first layer (e.g., along a line) and then depositing the mixture onto a substrate in a second layer (e.g., along the same line, in a perpendicular line to that of the first layer, etc.). Printing (e.g., 3D-printing) a plurality of layers may involve depositing a material in a pre-determined shape with a high degree of precision and control, using for example a robotic positioning system coupled with a controller. Those of ordinary skill in the art will be aware of systems and methods for 3D-printing, which typically involves the formation of 3-dimensional shapes, e.g., as opposed to 2-dimensional coatings that take the shape of the surface that they are applied to.
A variety of 3D-printing techniques are known to those of ordinary skill in the art, and include, but are not limited to, additive manufacturing techniques such as direct ink writing (DIW), stereolithography (SL), fused deposition modeling (FDM), laser sintering, laminated object manufacturing (LOM), doctor blading, material spraying, and material jetting. In some embodiments, for example, 3D-printing comprises depositing a first material in a first layer via additive manufacturing, removing at least some material in the first layer via subtractive manufacturing, and after removing the at least some material in the first layer, depositing a second material in the first layer via additive manufacturing. In some embodiments, additive manufacturing comprises at least one member selected from the group consisting of: direct ink writing (DIW), stereolithography (SL), fused deposition modeling (FDM), laser sintering, laminated object manufacturing (LOM), doctor blading, material spraying, and material jetting. In some embodiments, subtractive manufacturing comprises at least one member selected from the group consisting of: milling, drilling, cutting, etching, grinding, sanding, planing, and turning.
In some embodiments, 3D-printing comprises receiving, by a processing device, a 3D model of an object to be printed; receiving, by the processing device, information including at least one material property of a material to be 3D-printed; and generating, by the processing device, a set of sensor-based printer control parameters to print the object based, at least in part, on the sensor input. In some implementations, the processing device is further adapted to execute instructions for initiating 3D-printing of the object in the 3D-printer; receiving, during 3D-printing, the input from the sensor associated with the 3D-printing; and adjusting at least one printing property based on the sensor input. In some variations, the sensor is a force probe, a weight sensor, an optical camera, an imaging device, an in-line imaging device, a profilometer, a laser measurement device, a 3D scanner, or an automatic digital multimeter.
In another non-limiting implementation, 3D-printing includes obtaining model data representing a 3D model of an object. This implementation also includes processing the model data to generate a set of commands to direct a 3D-printer to extrude a material to form a physical model associated with the object. The set of commands is executable to cause an extruder (e.g., comprising a mixing nozzle) of the 3D printer to deposit a first portion of the material corresponding to a first portion of the physical model, to clean, to purge, or to clean and purge the extruder after depositing the first portion of the material, and to deposit a second portion of the material after cleaning the extruder. The second portion of the material corresponds to a second portion of the physical model.
In certain embodiments, a printed article (e.g., a 3D-printed article comprising a composite) may have a smallest dimension of greater than 10 mm, greater than 12 mm, greater than 14 mm, greater than 16 mm, greater than 18 mm, or greater than 20 mm.
In certain embodiments, a printed article (e.g., a 3D-printed article comprising a composite) may have an average largest dimension of particles (e.g., reinforcing particles) of at least 10 microns, at least 20 microns, at least 30 microns, at least 40 microns, at least 50 microns, at least 60 microns, at least 70 microns, at least 80 microns, at least 90 microns, at least 100 microns, at least 150 microns, at least 200 microns, at least 250 microns, at least 300 microns, at least 350 microns, at least 400 microns, at least 500 microns, at least 700 microns, or at least 900 microns. In some embodiments, the printed article may have an average largest dimension of particles (e.g., reinforcing particles) of at most 1000 microns, at most 900 microns, at most 700 microns, at most 500 microns, at most 400 microns, at most 350 microns, at most 300 microns, at most 250 microns, at most 200 microns, at most 150 microns, at most 100 microns, at most 90 microns, at most 80 microns, at most 70 microns, at most 60 microns, at most 50 microns, at most 40 microns, at most 30 microns, or at most 20 microns. Combinations of the above-referenced ranges are also possible (e.g., at least 10 microns and at most 1000 microns, or at least 50 microns and at most 400 microns, or at least 50 microns and at most 250 microns).
In certain embodiments, a printed article (e.g., a 3D-printed article comprising a composite) may have a compression strength of at least 0.1 MPa, at least 0.5 MPa, at least 1 MPa, at least 5 MPa, at least 10 MPa, at least 20 MPa, at least 40 MPa, at least 80 MPa, at least 100 MPa, at least 200 MPa, at least 300 MPa, or at least 400 MPa. In some embodiments, a printed article may have a compression strength of at most 500 MPa, at most 400 MPa, at most 300 MPa, at most 200 MPa, at most 100 MPa, at most 80 MPa, at most 40 MPa, at most 20 MPa, at most 10 MPa, at most 5 MPa, at most 1 MPa, or at most 0.5 MPa. Combinations of the above-referenced ranges are also possible (e.g., at least 0.1 MPa and at most 500 MPa).
In some embodiments, an article comprising a composite that is printed (e.g., 3D-printed) may comprise two or more portions, wherein one or more properties (e.g., average largest dimension of particles (e.g., reinforcing particles), average concentration of particles (e.g., reinforcing particles) e.g. weight percent of particles (e.g., reinforcing particles), surface roughness, compression strength, slip resistance, abrasion resistance, density, stiffness, heat deflection temperature, pore concentration, pore size, and coefficient of thermal expansion) of a first portion may differ from one or more properties of a second portion. In some embodiments, the difference in properties between the first portion and the second portion may comprise a gradient of the one or more properties (e.g., the property or properties may vary relatively smoothly from a first value in the first portion to a second value in the second portion). In other embodiments, there may be a sharp change in one or more of the properties at a boundary of one or more of the first portion and the second portion. In some embodiments, the article may be adhered to a textile. In some embodiments, the article may comprise a polymer. In some embodiments, the article may be a component of a shoe upper. The article may in some cases be printed directly onto a textile to make up a component of a shoe upper or article of apparel. Examples of methods of producing such particles, e.g., having differences between a first portion and a second portion, are discussed in more detail below.
In some embodiments, a method of printing an article may comprise flowing at least two inputs into a mixing nozzle to form a first mixture comprising a blowing agent. In some embodiments, one of the at least two inputs to form the first mixture comprises an isocyanate and another of the at least two inputs to form the first mixture comprises a polyol system containing the blowing agent. In some embodiments, the method further comprising flowing at least a third input comprising a polyol system into the mixing nozzle to form the first mixture. In some embodiments, the method may comprise depositing a first region comprising the first mixture to form a first elastomer.
In some embodiments, the method may comprise flowing at least two inputs into a mixing nozzle to form a second mixture. In some embodiments, one of the at least two inputs to form the second mixture comprises an isocyanate and another of the at least two inputs to form the second mixture comprises a polyol system. In some embodiments, the second mixture comprises a blowing agent. In some embodiments, the method further comprises flowing at least a third input comprising a polyol system containing a blowing agent into the mixing nozzle to form the second mixture. In some embodiments, the method may comprise depositing a second region adjacent to the first region, comprising the second mixture to form a second elastomer.
In some embodiments, the method may comprise heating at least the first region of the article (e.g., at least the first region and the second region of the article) to a temperature greater than or equal to the activation temperature of the blowing agent. In some embodiments, heating at least the first region of the article causes differential expansion between the first region and the second region of the article and physical deformation of the article.
In some embodiments, as a non-limiting example, input Part A may comprise isocyanate, input Part B′ may comprise a polyol system, and input Part B″ may comprise a polyol system with a blowing agent. When Part A and Part B′ are mixed, an elastomer results. When Part A and Part B″ are mixed, an elastomer that will expand when activated results. When Part A is mixed with Part B′ and Part B″, an elastomer that will expand to a lesser extent than pure Part A with pure Part B″ (e.g., when in the same ratio as Part A to Part B′ and Part B″ combined) results. If a fourth input were added, then stiffness as well as expansion on activation could be controlled.
In certain embodiments, a printed article (e.g., a 3D-printed article) that comprises at least two portions, at least one of which comprises a composite (e.g., a printed article that comprises at least a first portion comprising an elastomer and a second portion comprising a elastomer containing a blowing agent) may have a ratio of a property (e.g., average largest dimension of particles (e.g., reinforcing particles), average concentration of particles (e.g., reinforcing particles), surface roughness, compression strength, slip resistance, abrasion resistance, density, stiffness, heat deflection temperature, pore concentration, pore size, and/or coefficient of thermal expansion) of the second portion of the printed article to the same property of the first portion of the printed article of greater than or equal to 1.05, greater than or equal to 1.1, greater than or equal to 1.2, greater than or equal to 1.3, greater than or equal to 1.5, greater than or equal to 2, or greater than or equal to 5. In some embodiments, a ratio of the property of the second portion of the printed article to the same property of the first portion of the printed article may be less than or equal to 10, less than or equal to 5, less than or equal to 2, less than or equal to 1.5, less than or equal to 1.3, less than or equal to 1.2, or less than or equal to 1.1. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to 1.05 and less than or equal to 10).
In some embodiments, the gradient in a property (e.g., volume percent of particles, e.g., reinforcing particles) in the article may be present from the surface of the article to greater than or equal to 10 microns, greater than or equal to 20 microns, greater than or equal to 30 microns greater than or equal to 50 microns, greater than or equal to 100 microns, greater than or equal to 500 microns, greater than or equal to 1000 microns, or greater than or equal to 10000 microns below the surface of the article. In some embodiments, the gradient in the property may be present throughout the thickness of the article.
If two portions having different properties are present, the portions may differ for a variety of reasons, for example, different particle compositions, different particle shapes, different particle sizes, different densities of particles, or the like. Combinations of any of these are also possible. As a non-limiting example, if two average particle sizes are present, then each of the average particle sizes may independently be those described herein. In certain embodiments, as another example, a printed article (e.g., a 3D-printed article) that comprises at least two portions comprising particles (e.g., reinforcing particles) may have a ratio of the average largest dimension of particles (e.g., reinforcing particles) in a first portion of the printed article to the average largest dimension of particles (e.g., reinforcing particles) in a second portion of the printed article of greater than or equal to 1.05, greater than or equal to 1.1, greater than or equal to 1.2, greater than or equal to 1.3, greater than or equal to 1.5, greater than or equal to 2, or greater than or equal to 5. In some embodiments, a ratio of the average largest dimension of particles (e.g., reinforcing particles) in the second portion of the printed article to the average largest dimension of particles (e.g., reinforcing particles) in the first portion of the printed article may be less than or equal to 10, less than or equal to 5, less than or equal to 2, less than or equal to 1.5, less than or equal to 1.3, less than or equal to 1.2, or less than or equal to 1.1. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to 1.05 and less than or equal to 10).
In certain embodiments, a printed article (e.g., a 3D-printed article) that comprises at least one portion comprising a composite (e.g., a printed article that comprises at least a first portion comprising a composite) may have a weight percent of particles (e.g., reinforcing particles) in the first portion of the printed article of at least 5 wt %, at least 10 wt %, at least 15 wt %, at least 20 wt %, at least 25 wt %, at least 30 wt %, at least 35 wt %, at least 40 wt %, at least 45 wt %, at least 50 wt %, at least 55 wt %, at least 60 wt %, at least 65 wt %, at least 70 wt %, at least 75 wt %, at least 80 wt %, or at least 85 wt % with respect to the total weight of the article. In some embodiments, the first portion of the printed article has a weight percent of particles (e.g., reinforcing particles) of at most 90 wt %, at most 85 wt %, at most 80 wt %, at most 75 wt %, at most 70 wt %, at most 65 wt %, at most 60 wt %, at most 55 wt %, at most 50 wt %, at most 45 wt %, at most 40 wt %, at most 35 wt %, at most 30 wt %, at most 25 wt %, at most 20 wt %, at most 15 wt %, or at most 10 wt % with respect to the total weight of the article. Combinations of the above-referenced ranges are also possible (e.g., at least 5 wt % and at most 90 wt %).
In certain embodiments, a printed article (e.g., a 3D-printed article) that comprises at least two portions comprising a composite (e.g., a printed article that comprises at least a first portion comprising a composite and a second portion comprising a composite) may have a weight percent of particles (e.g., reinforcing particles) in the first portion of the printed article of at least 5 wt %, at least 10 wt %, at least 15 wt %, at least 20 wt %, at least 25 wt %, at least 30 wt %, at least 35 wt %, at least 40 wt %, at least 45 wt %, at least 50 wt %, at least 55 wt %, at least 60 wt %, at least 65 wt %, at least 70 wt %, at least 75 wt %, at least 80 wt %, or at least 85 wt % with respect to the total weight of the article. In some embodiments, the second portion of the printed article has a weight percent of particles (e.g., reinforcing particles) of at most 90 wt %, at most 85 wt %, at most 80 wt %, at most 75 wt %, at most 70 wt %, at most 65 wt %, at most 60 wt %, at most 55 wt %, at most 50 wt %, at most 45 wt %, at most 40 wt %, at most 35 wt %, at most 30 wt %, at most 25 wt %, at most 20 wt %, at most 15 wt %, or at most 10 wt % with respect to the total weight of the article. Combinations of the above-referenced ranges are also possible (e.g., at least 5 wt % and at most 90 wt %).
In certain embodiments, a printed article (e.g., a 3D-printed article) that comprises at least two portions comprising a composite (e.g., a printed article that comprises at least a first portion comprising a composite and a second portion comprising a composite) may have a ratio of the weight percent of particles (e.g., reinforcing particles) in the second portion of the printed article to the weight percent of particles (e.g., reinforcing particles) in the first portion of the printed article of greater than or equal to 1.05, greater than or equal to 1.1, greater than or equal to 1.2, greater than or equal to 1.3, greater than or equal to 1.5, greater than or equal to 2, or greater than or equal to 5. In some embodiments, a ratio of the weight percent of particles (e.g., reinforcing particles) in the second portion of the printed article to the weight percent of particles (e.g., reinforcing particles) in the first portion of the printed article may be less than or equal to 10, less than or equal to 5, less than or equal to 2, less than or equal to 1.5, less than or equal to 1.3, less than or equal to 1.2, or less than or equal to 1.1. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to 1.05 and less than or equal to 10).
In certain embodiments, a printed article (e.g., a 3D-printed article) that comprises at least one portion comprising a composite (e.g., a printed article that comprises at least a first portion comprising a composite) may have a compression strength in the first portion of the printed article of at least 0.1 MPa, at least 0.5 MPa, at least 1 MPa, at least 5 MPa, at least 10 MPa, at least 20 MPa, at least 40 MPa, at least 80 MPa, at least 100 MPa, at least 200 MPa, at least 300 MPa, or at least 400 MPa. In some embodiments, the first portion of the printed article may have a compression strength of at most 500 MPa, at most 400 MPa, at most 300 MPa, at most 200 MPa, at most 100 MPa, at most 80 MPa, at most 40 MPa, at most 20 MPa, at most 10 MPa, at most 5 MPa, at most 1 MPa, or at most 0.5 MPa. Combinations of the above-referenced ranges are also possible (e.g., at least 0.1 MPa and at most 500 MPa).
In certain embodiments, a printed article (e.g., a 3D-printed article) that comprises at least two portions comprising a composite (e.g., a printed article that comprises at least a first portion comprising a composite and a second portion comprising a composite) may have a compression strength in the second portion of the printed article of at least 0.1 MPa, at least 0.5 MPa, at least 1 MPa, at least 5 MPa, at least 10 MPa, at least 20 MPa, at least 40 MPa, at least 80 MPa, at least 100 MPa, at least 200 MPa, at least 300 MPa, or at least 400 MPa. In some embodiments, the second portion of the printed article may have a compression strength of at most 500 MPa, at most 400 MPa, at most 300 MPa, at most 200 MPa, at most 100 MPa, at most 80 MPa, at most 40 MPa, at most 20 MPa, at most 10 MPa, at most 5 MPa, at most 1 MPa, or at most 0.5 MPa. Combinations of the above-referenced ranges are also possible (e.g., at least 0.1 MPa and at most 500 MPa).
In certain embodiments, a printed article (e.g., a 3D-printed article) that comprises at least two portions comprising a composite (e.g., a printed article that comprises at least a first portion comprising a composite and a second portion comprising a composite) may have a ratio of compression strength in the second portion of the printed article to compression strength in the first portion of the printed article of greater than or equal to 1.05, greater than or equal to 1.1, greater than or equal to 1.2, greater than or equal to 1.3, greater than or equal to 1.5, greater than or equal to 2, or greater than or equal to 5. In some embodiments, a ratio of compression strength in the second portion of the printed article to compression strength in the first portion of the printed article may be less than or equal to 10, less than or equal to 5, less than or equal to 2, less than or equal to 1.5, less than or equal to 1.3, less than or equal to 1.2, or less than or equal to 1.1. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to 1.05 and less than or equal to 10).
In certain embodiments, a printed article (e.g., a 3D-printed article) that comprises at least two portions comprising a composite (e.g., a printed article that comprises at least a first portion comprising a composite and a second portion comprising a composite) may have a ratio of slip resistance in the second portion of the printed article to slip resistance in the first portion of the printed article of greater than or equal to 1.05, greater than or equal to 1.1, greater than or equal to 1.2, greater than or equal to 1.3, greater than or equal to 1.5, greater than or equal to 2, or greater than or equal to 5. In some embodiments, a ratio of slip resistance in the second portion of the printed article to slip resistance in the first portion of the printed article may be less than or equal to 10, less than or equal to 5, less than or equal to 2, less than or equal to 1.5, less than or equal to 1.3, less than or equal to 1.2, or less than or equal to 1.1. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to 1.05 and less than or equal to 10).
In certain embodiments, a printed article (e.g., a 3D-printed article) that comprises at least two portions comprising a composite (e.g., a printed article that comprises at least a first portion comprising a composite and a second portion comprising a composite) may have a ratio of abrasion resistance in the second portion of the printed article to abrasion resistance in the first portion of the printed article of greater than or equal to 1.05, greater than or equal to 1.1, greater than or equal to 1.2, greater than or equal to 1.3, greater than or equal to 1.5, greater than or equal to 2, or greater than or equal to 5. In some embodiments, a ratio of abrasion resistance in the second portion of the printed article to abrasion resistance in the first portion of the printed article may be less than or equal to 10, less than or equal to 5, less than or equal to 2, less than or equal to 1.5, less than or equal to 1.3, less than or equal to 1.2, or less than or equal to 1.1. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to 1.05 and less than or equal to 10).
In some embodiments, the particles (e.g., reinforcing particles) may be incorporated in order to modify the finish of the printed article. The term finish is given its ordinary meaning in the art and may refer to the appearance experienced by the viewer. As non-limiting examples, the finish may be characterized as shiny or matte.
In some embodiments, the particles (e.g., reinforcing particles) may comprise a blowing agent, e.g., solid particles that decompose, above a certain activation temperature, into a gas. In some embodiments, the activation temperature of the blowing agent may be greater than the curing temperature (e.g., the maximum temperature in the curing profile) of the matrix of the printed article by e.g. at least 2 degrees Celsius, at least 5 degrees Celsius, at least 10 degrees Celsius, at least 20 degrees Celsius, at least 30 degrees Celsius, or at least 50 degrees Celsius. In some embodiments, the activation temperature of the blowing agent may be less than the curing temperature of the matrix of the printed article by e.g. at least 2 degrees Celsius, at least 5 degrees Celsius, at least 10 degrees Celsius, at least 20 degrees Celsius, at least 30 degrees Celsius, or at least 50 degrees Celsius, or equal to curing temperature of the matrix of the printed article. The term activation temperature is given its ordinary meaning in the art and may refer to the temperature at or above which a blowing agent comprising solid particles decomposes into a gas. The term curing temperature is given its ordinary meaning in the art and may refer to the temperature at or above which the matrix of the printed article (e.g., comprising polyurethane) solidifies by e.g. crosslinking.
In some embodiments, the blowing agent may be incorporated into the printed article by introducing a fluid comprising a blowing agent concentrate as one of the inputs of a mixing nozzle (e.g., a microfluidic printing nozzle) system with a plurality of inputs. In some embodiments, the blowing agent concentrate may be made to flow into the mixing nozzle at a constant rate, such that the volume fraction of solid particles comprising blowing agent in the matrix of the printed article is constant throughout the printed object. In some embodiments, the blowing agent concentrate may be made to flow into the mixing nozzle at a varying rate, such that the volume fraction of solid particles comprising blowing agent in the matrix of the printed article varies throughout the printed object.
In some embodiments, the blowing agent concentrate is made to flow into the mixing nozzle at a varying rate as dictated by a computer. In some embodiments, the blowing agent concentrate is digitally made to flow into the mixing nozzle at a varying rate, such that a greater volume fraction of blowing agent is incorporated into at least a first portion of the printed article where shrinkage of the matrix during curing is predicted and/or known to cause warping of the printed article, and a smaller volume fraction of blowing agent is incorporated into at least a second portion of the printed article where shrinkage of the matrix during curing is predicted and/or known not to cause warping of the printed article.
In some embodiments, in the case where shrinkage of the matrix during curing is known to cause warping of at least a first portion of a printed article, measurement of the extent of warping of at least a first portion of a first printed article, in which the first printed article is printed and cured without the activation of a blowing agent, maybe conducted to determine the locations of warping. These determined locations of warping can be used to design the incorporation of varying volume fractions of blowing agent in at least a first portion and a second portion of a second printed article, in which a greater volume fraction of blowing agent is incorporated in at least the first portion of the second printed article to reduce warping (e.g., resulting from shrinkage during curing of the matrix) by means of volumetrically expanding at least the first portion of the second printed article by heating at least the first portion of the second printed article above the activation temperature of the blowing agent. The measurement of the extent of warping of the first printed article at locations throughout the first printed article may in some embodiments, as a non-limiting example, be accomplished by the inclusion of markings in the first printed article and then video-tracking of the change in position of these markings with curing.
In some embodiments, the matrix may shrink during curing by at least about 0.5% by volume, at least about 1% by volume, at least about 2% by volume, at least about 3% by volume, at least about 4% by volume, at least about 5% by volume, at least about 10% by volume, at least about 15% by volume, at least about 20% by volume, at least about 30% by volume, or at least about 40% by volume. In some embodiments, the matrix may shrink during curing by at most about 50% by volume, at most about 40% by volume, at most about 30% by volume, at most about 20% by volume, at most about 15% by volume, at most about 10% by volume, at most about 5% by volume, most about 4% by volume, at most about 3% by volume, or at most about 2% by volume.
In some embodiments, heating at least a first portion of a printed article, comprising the blowing agent, at or above the activation temperature of the blowing agent causes a volumetric expansion of the printed article. In some embodiments, the at least a first portion of the printed article may volumetrically expand (e.g., upon heating at or above the blowing agent activation temperature) by at least about 1% by volume, at least about 2% by volume, at least about 3% by volume, at least about 4% by volume, at least about 5% by volume, at least about 10% by volume, at least about 15% by volume, at least about 20% by volume, at least about 30% by volume, or at least about 40% by volume. In some embodiments, the at least a first portion of the printed article may volumetrically expand (e.g., upon heating at or above the blowing agent activation temperature) by at most about 50% by volume, at most about 40% by volume, at most about 30% by volume, at most about 20% by volume, at most about 15% by volume, at most about 10% by volume, at most about 5% by volume, most about 4% by volume, at most about 3% by volume, or at most about 2% by volume.
In some embodiments, the blowing agent incorporated into at least a first portion of a printed article may be present in a volume fraction such that the volumetric expansion provided by the blowing agent is within about 50%, within about 40%, within about 30%, within about 20%, within about 10%, within about 5%, within about 2%, within about 1%, or within about 0.5% of the volumetric shrinkage provided by the curing of the matrix.
In a non-limiting set of embodiments, the printed article (
A non-limiting set of methods of making article 1900 (
In some embodiments, the volume fraction of solid blowing agent in the printed article may be at least about 0.01 volume percent, at least about 0.1 volume percent, at least about 1 volume percent, at least about 5 volume percent, at least about 10 volume percent, at least about 20 volume percent, at least about 30 volume percent, or at least about 40 volume percent. In some embodiments, the volume fraction of solid blowing agent in the printed article may be at most about 50 volume percent, at most about 40 volume percent, at most about 30 volume percent, at most about 20 volume percent, at most about 10 volume present, at most about 5 volume percent, at most about 1 volume percent, or at most about 0.1 volume percent.
In some embodiments, solid particles of blowing agent may be incorporated into the entire printed article such that the solid particles are homogeneously dispersed in the matrix at a constant volume fraction.
In some embodiments, the surface of the printed article may be exposed to a temperature at or above both the curing temperature of the matrix and the activation temperature of the blowing agent for a brief period of time, such that only the blowing agent at the surface of the printed article is activated. In some embodiments, such treatment of the printed article results in a surface with a matte finish. In some embodiments, the surface of the printed article may be exposed to a temperature above both the curing temperature of the matrix and the activation temperature of the blowing agent by at least about 0 degrees Celsius, at least about 1 degree Celsius, at least about 2 degrees Celsius, at least about 5 degrees Celsius, at least about 10 degrees Celsius, at least about 15 degrees Celsius, at least about 20 degrees Celsius, at least about 25 degrees Celsius, at least about 30 degrees Celsius, at least about 40 degrees Celsius, or at least about 50 degrees Celsius. In some embodiments, the surface of the printed article may be exposed to a temperature above both the curing temperature of the matrix and the activation temperature of the blowing agent by at most about 60 degrees Celsius, at most about 50 degrees Celsius, at most about 40 degrees Celsius, at most about 30 degrees Celsius, and most about 25 degrees Celsius, at most about 20 degrees Celsius, at most about 15 degrees Celsius, at most about 10 degrees Celsius, at most about 5 degrees Celsius, at most about 2 degrees Celsius, or at most about 1 degree Celsius.
In some embodiments, the surface of the printed article may be exposed to a temperature at or above both the curing temperature of the matrix and the activation temperature of the blowing agent for less than or equal to about 300 seconds, less than or equal to about 240 seconds, less than or equal to about 180 seconds, less than or equal to about 120 seconds, less than or equal to about 60 seconds, less than or equal to about 30 seconds, less than or equal to about 20 seconds, less than or equal to about 10 seconds, less than or equal to about 5 seconds, less than or equal to about 2 seconds, or less than or equal to about 1 second.
In some embodiments, a concentrated hot air nozzle maybe used to locally expose the surface of at least a first portion of a printed article to a temperature at or above both the curing temperature of the matrix and the activation temperature of the blowing agent. In some embodiments, the at least a first portion that was locally exposed with a concentrated hot air nozzle has a matte finish.
In some embodiments, the particles (e.g., reinforcing particles) may comprise solid particles comprising a blowing agent that may be incorporated into at least a first portion of the printed article. In some embodiments, the solid particles comprising a blowing agent may be incorporated into the printed article in a gradient. In some embodiments, at least a second portion of the printed article is free of solid particles comprising a blowing agent. In a non-limiting set of embodiments, the surface layer of the printed article (
A non-limiting set of methods of making article 1700 (
In some embodiments, local activation of the blowing agent may be accomplished by local application of heat to at least a first portion of the printed article in which the blowing agent has been incorporated (e.g., by flowing through a mixing nozzle). In some embodiments, a printed article that has been cured may comprise bubbles (e.g., that have been formed from the activation of the blowing agent) and may additionally comprise solid particles comprising a blowing agent that were intentionally left not activated. In this case, in some embodiments, the entire printed article was heated at or above the curing temperature of the matrix, and at least a first portion of the printed article was heated at or above the activation temperature of the blowing agent. In some embodiments, at least a second portion of the printed article was heated at or above the activation temperature of the blowing agent, in which case, e.g., the solid particles comprising a blowing agent remaining as solid particles had an activation temperature above the curing temperature of the matrix.
In a non-limiting set of embodiments, the printed article (
A non-limiting set of methods of making article 1800 (
In some embodiments, a blowing agent concentrate may be one of the inputs (e.g., a first fluid) to a mixing nozzle system with a plurality of inputs. In some embodiments, the volume percent of blowing agent incorporated into a given portion of the printed article is digitally controlled. In some embodiments, the entire printed article is heated at or above the activation temperature of the blowing agent and at or above the curing temperature of the matrix, and only at least a first portion of the printed article comprising the blowing agent volumetrically expand and/or achieve a different surface texture from the at least a second portion of the printed article that is free of the blowing agent prior to heating.
In some embodiments, a hybrid approach may be taken, in which a plurality of blowing agents, each with a different activation temperature and/or a different solid particle size, may be incorporated into the printed article. In some embodiments, a low-temperature activating blowing agent may be incorporated that has an activation temperature at or below the curing temperature of the matrix and therefore that is activated during curing of the printed article. In some embodiments, a blowing agent with an activation temperature above the curing temperature of the matrix may be incorporated into the printed article and may be activated by the local application of heat during or after curing the printed article.
In some embodiments, an article that changes shape (e.g., from deposition to its solid cured and/or activated form) may be printed by controlling the ratios of two or more inputs into a mixing nozzle to deposit at least two regions each of which comprises a respective matrix (e.g., an elastomer) adjacent to one another where at least one of the regions contains a blowing agent (e.g., chemical blowing agent) that can be activated at high temperature. The first region may have the same or different components from the second region. Following deposition of the at least two regions, the blowing agent may be activated by heating at least one portion of the article comprising the blowing agent to a temperature greater than or equal to the activation temperature of the blowing agent (and, when applicable, the curing temperature of the matrix), resulting in a differential expansion between the at least two regions that causes physical deformation of the article. In some embodiments, the differential expansion is programmed to cause the article to better conform to a shoe last.
In some embodiments, the blowing agent concentration is varied between the at least two regions by controlling the ratio between two or more input materials to a mixing nozzle, one or more of which input materials comprises the blowing agent. In some embodiments, the stiffness of the matrix (e.g., elastomer) in the first region may differ from the stiffness of the matrix (e.g., elastomer) in the second region (e.g., by varying the concentration of crosslinking agent between the first region and the second region). In some embodiments, the differential expansion of the two or more regions is controlled by the stiffness difference between the two regions with respect to the matrix (e.g., elastomer) that encapsulates the blowing agent. In some embodiments, the differential expansion is controlled by both a difference in stiffness of the matrix and a difference in blowing agent concentration between the two or more regions. In some embodiments, the differential expansion is controlled by a difference between the first region and the second region of the density, blowing agent concentration, pore concentration, pore size, stiffness, heat deflection temperature, coefficient of thermal expansion, and/or filler concentration.
In certain embodiments, the printed article may have a ratio of the concentration of blowing agent in the first region prior to heating, to the concentration of blowing agent in the second region prior to heating, of greater than or equal to 1.05, greater than or equal to 1.1, greater than or equal to 1.2, greater than or equal to 1.3, greater than or equal to 1.5, greater than or equal to 2, or greater than or equal to 5. In some embodiments, a ratio of the concentration of blowing agent in the first region prior to heating, to the concentration of blowing agent in the second region prior to heating, may be less than or equal to 10, less than or equal to 5, less than or equal to 2, less than or equal to 1.5, less than or equal to 1.3, less than or equal to 1.2, or less than or equal to 1.1. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to 1.05 and less than or equal to 10).
In certain embodiments, the printed article may have a ratio of the concentration of crosslinking agent in the first region prior to heating, to the concentration of crosslinking agent in the second region prior to heating, of greater than or equal to 1.05, greater than or equal to 1.1, greater than or equal to 1.2, greater than or equal to 1.3, greater than or equal to 1.5, greater than or equal to 2, or greater than or equal to 5. In some embodiments, a ratio of the concentration of crosslinking agent in the first region prior to heating, to the concentration of crosslinking agent in the second region prior to heating, may be less than or equal to 10, less than or equal to 5, less than or equal to 2, less than or equal to 1.5, less than or equal to 1.3, less than or equal to 1.2, or less than or equal to 1.1. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to 1.05 and less than or equal to 10). In some embodiments, the activation temperature of the blowing agent may be greater than or equal to 200 degrees Celsius, greater than or equal to 250 degrees Celsius, greater than or equal to 300 degrees Celsius, greater than or equal to 350 degrees Celsius greater than or equal to 400 degrees Celsius, greater than or equal to 450 degrees Celsius, greater than or equal to 500 degrees Celsius, greater than or equal to 550 degrees Celsius, greater than or equal to 600 degrees Celsius, greater than or equal to 650 degrees Celsius, or greater than or equal to 700 degrees Celsius. In some embodiments, the activation temperature of the blowing agent may be less than or equal to 750 degrees Celsius, less than or equal to 700 degrees Celsius, less than or equal to 650 degrees Celsius, less than or equal to 600 degrees Celsius, less than or equal to 550 degrees Celsius, less than or equal to 500 degrees Celsius, less than or equal to 450 degrees Celsius, less than or equal to 400 degrees Celsius, less than or equal to 350 degrees Celsius, less than or equal to 300 degrees Celsius, or less than or equal to 250 degrees Celsius. Combinations of these activation temperatures are also possible (e.g., greater than or equal to 200 degrees Celsius and less than or equal to 750 degrees Celsius).
In some embodiments, the at least one portion of the article may be heated to a temperature greater than or equal to the activation temperature of the blowing agent (and, when applicable, the curing temperature of the matrix) for greater than or equal to 1 minute, greater than or equal to 2 minutes, greater than or equal to 5 minutes, greater than or equal to 30 minutes, or greater than or equal to 60 minutes. In some embodiments, the at least one portion of the article may be heated to a temperature greater than or equal to the activation temperature of the blowing agent for less than or equal to 120 minutes, less than or equal to 60 minutes, less than or equal to 30 minutes, less than or equal to 5 minutes, or less than or equal to 2 minutes. Combinations of these heating durations are also possible (e.g., greater than or equal to 1 minute and less than or equal to 120 minutes).
In some embodiments, an article may comprise a polymeric structure. In some embodiments, the polymeric structure may comprise a polymer. In some embodiments, the polymeric structure may comprise particles (e.g., reinforcing particles) (e.g., comprising a chemical blowing agent). In some embodiments, the polymeric structure has a gradient in volume percent of particles (e.g., reinforcing particles). At least one portion of the polymeric structure in some embodiments may be adhered to a textile. In some cases, the polymeric structure may contain in at least one portion a chemical blowing agent that has not been expanded. In some cases, the polymeric structure may contain in at least one portion pores from chemical blowing agent that has been expanded. In some embodiments, the surface roughness of the polymeric structure may be increased by heating the polymeric structure at a portion containing chemical blowing agent to a temperature greater than or equal to the activation temperature of the blowing agent.
In some embodiments, one or more materials deposited onto a substrate (e.g., by a print head such as a nozzle) may comprise reactive functional groups for a period of time after deposition. The reactive functional groups may be configured to react with other articles to which the deposited material is adjacent (e.g., articles of footwear, components of articles of footwear), such as an article onto which the material was deposited, an article added to the deposited material, an article positioned beside the deposited material, an article disposed on the same article onto which the material was deposited, and/or an article that is positioned partially above or below the deposited material and partially beside the deposited material. Reaction between the reactive functional groups in the deposited material and one or more articles to which it is adjacent may result in bond formation between the deposited material and the articles(s), and/or may increase the adhesive strength between the deposited material and the article(s). Examples of such articles include textiles, molded parts, layers, further deposited materials with the same or different chemistry, and the like. In some embodiments, the deposited material may bond with two or more articles to which it is adjacent, and may adhere these articles together through bonds formed by reaction of the reactive functional groups in the deposited material with the articles. Each article adhered together may comprise a deposited material (e.g., a 3D-printed article may be built up by successively depositing layers of materials comprising reactive functional groups on top of each other), some of the articles adhered together may comprise a deposited material (e.g., a deposited material may adhere another deposited material to which it is adjacent to a textile on which they are both disposed), or none of the articles adhered together may comprise a deposited material. In some cases, the articles adhered together may have different physical or chemical properties (e.g., different values of toughness, different values of Young's modulus).
In some embodiments, reactive functional groups that are configured to react with an article to which a deposited material is adjacent (e.g., an article of footwear, a component of an article of footwear) may also be configured to react with other reactive functional groups in the deposited material. Reaction between two complementary sets of functional groups within the deposited material may comprise curing of the material. As the deposited material cures, the number of reactive functional groups within the deposited material may be reduced and the deposited material may become less reactive with any articles to which it is adjacent. In certain cases, tuning the curing time of the deposited material by varying one or more parameters (e.g., temperature at which the deposited material is held after deposition, composition of the deposited material) may be advantageous because it may allow for tuning of the reactivity of the deposited material as a function of time. For example, the curing time may be tuned so that the deposited material is adhesive upon deposition and upon further addition of a second article to the deposited material, but is no longer adhesive during further manufacturing steps and/or when an article of which the deposited material is a part of is in use.
A variety of suitable reactive functional groups and molecules comprising reactive functional groups may be included in a deposited material. In some embodiments, a deposited material may comprise reactive functional groups that are alcohol groups and reactive functional groups that are isocyanate groups, and the alcohol groups and isocyanate groups may react to form a polyurethane. In some embodiments, a deposited material may comprise reactive functional groups that are amine groups and reactive functional groups that are isocyanate groups, and the alcohol groups and isocyanate groups may react to form a polyureas. Non-limiting examples of suitable molecules comprising alcohol groups include difunctional hydroxyl compounds such as 1,4-butanediol, hydroquinone bis(2-hydroxylethyl) ether, neopentyl glycol, diethanolamine, and methyldiethanolamine; trifunctional hydroxyl compounds such as trimethylolpropane, 1,2,6-hexanetriol, and triethanolamine; tetrafunctional hydroxyl compounds such as pentaerythritol; and polyols such as polyether polyols, polyester polyols, polytetrahydrofuran, polycaprolactone polyols, polycarbonate polyols, and polytetramethylene ether glycol-based polyols. Non-limiting examples of suitable molecules comprising amine groups include difunctional amine compounds such as diethyltoluenediamine and dimethylthiotoluenediamine. Non-limiting examples of suitable molecules comprising isocyanate groups include methylenebis(phenyl isocyanate), toluene diisocyanate, hexamethylene diisocyanate, naphthalene diisocyanate, methylene bis-cyclohexylisocyanate, and isophorone diisocyanate. Other types of reactive functional groups, and other types of molecules comprising reactive functional groups are also possible.
In some embodiments, a deposited material may be cured (and/or configured to be cured) at room temperature. In some embodiments, the deposited material may be cured (and/or configured to be cured) at a temperature above room temperature. The deposited material may be configured (and/or configured to be cured) to be cured at a temperature of greater than or equal to 70° C., greater than or equal to 80° C., greater than or equal to 90° C., or greater than or equal to 100° C. The deposited material may be cured (and/or configured to be cured) at a temperature of less than or equal to 110° C., less than or equal to 100° C., less than or equal to 90° C., or less than or equal to 80° C. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to 70° C. and less than or equal to 110° C.). Other ranges are also possible.
A deposited material may be cured (and/or configured to be fully cured) over any suitable period of time. In some embodiments, the deposited material is fully cured (and/or configured to be cured) over a period of time of greater than or equal to two hours, greater than or equal to four hours, greater than or equal to eight hours, greater than or equal to 12 hours, greater than or equal to 20 hours, greater than or equal to 24 hours, greater than or equal to 36 hours, greater than or equal to 48 hours, greater than or equal to three days, greater than or equal to four days, greater than or equal to five days, or greater than or equal to six days. In some embodiments, the deposited material is fully cured (and/or configured to be fully cured) over a period of time of less than or equal to one week, less than or equal to six days, less than or equal to five days, less than or equal to four days, less than or equal to three days, less than or equal to 48 hours, less than or equal to 36 hours, less than or equal to 24 hours, less than or equal to 20 hours, less than or equal to 12 hours, less than or equal to eight hours, or less than or equal to four hours. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to two hours and less than or equal to 20 hours, or greater than or equal to 24 hours and less than or equal to one week). Other ranges are also possible. In general, higher curing temperatures result in faster reactions between reactive functional groups. This may cause the time over which the deposited material is fully cured (and/or configured to be fully cured) to decrease. For example, a material may be fully cured over a period of time of greater than or equal to a few days and less than or equal to one week when cured at room temperature but may be fully cured over a period of time of greater than or equal to two hours and less than or equal to 20 hours at a temperature of greater than or equal to 70° C. and less than or equal to 110° C.
A deposited material may be deposited at any degree of curing. In some embodiments, the deposited material is at least 25% uncured upon deposition, at least 30% uncured upon deposition, at least 40% uncured upon deposition, at least 50% uncured upon deposition, at least 60% uncured upon deposition, at least 70% uncured upon deposition, at least 80% uncured upon deposition, or at least 90% uncured upon deposition. In some embodiments, the deposited material is at most 95% uncured upon deposition, at most 90% uncured upon deposition, at most 80% uncured upon deposition, at most 70% uncured upon deposition, at most 60% uncured upon deposition, at most 50% uncured upon deposition, or at most 40% uncured upon deposition. Combinations of the above-referenced ranges are also possible (e.g., at least 30% uncured upon deposition and at most 95% uncured upon deposition). Other ranges are also possible.
In some embodiments, an article (e.g., an article of footwear, a component of an article of footwear) is positioned adjacent to a deposited material (e.g., deposited on the deposited material, deposited adjacent the deposited material, laminated to the deposited material, etc.) before it has fully cured. The article may be positioned adjacent to the deposited material before at least 25% of the deposited material has cured, before at least 30% of the deposited material has cured, before at least 40% of the deposited material has cured, before at least 50% of the deposited material has cured, or before at least 60% of the deposited material has cured. The article may be positioned adjacent to the deposited material before at most 70% of the deposited material has cured, before at most 60% of the deposited material has cured, before at most 50% of the deposited material has cured, before at most 40% of the deposited material has cured, or before at most 30% of the deposited material has cured. Combinations of the above-referenced ranges are also possible (e.g., before at least 25% of the deposited material has cured and before at most 70% of the deposited material has cured). Other ranges are also possible.
In certain embodiments, an article (e.g., an article of footwear, a component of an article of footwear, an article of apparel such as a sports bra, a component of an article of apparel such as a sports bra) as described herein may be produced on a multi-axis deposition system, and/or a method as described herein may include at least one step that is performed on a multi-axis deposition system. In general, and as described further below, multi-axis deposition systems include a print head and a substrate. The print head may be any suitable print head configured to deposit a material onto the substrate. The substrate may be any suitable substrate onto which a material may be deposited; in some embodiments, one or more articles (e.g., a component of an article of footwear, an upper, a sock liner) may be disposed on the substrate. In certain embodiments, one or both of the print head and substrate may be translated along one or more axes and/or rotated around one or more axes. Translation and/or rotation of the print head and/or substrate may enable the position of the print head with respect to the substrate to be changed prior to, during, and/or after a printing process. In some cases, translation and/or rotation of the print head and/or the substrate may allow the print head to deposit material onto a wide variety of substrate surfaces and/or allow the print head to deposit material onto the substrate at a wide variety of angles. In some embodiments, the print head may be configured to be rotated and/or translated such that it can deposit material onto each surface of the substrate.
A print head in a multi-axis deposition system may be any suitable print head configured to deposit a material of interest onto the substrate. In some embodiments a multi-axis deposition system may comprise two or more print heads. Non-limiting examples of suitable print heads include a direct write head, a mixing nozzle, an ink jet head, a spray valve, an aerosol jet print head, a laser cutting head, a hot air gun, a hot knife, an ultrasonic knife, a sanding head, a polishing head, a UV curing device, an engraver, an embosser, and the like. In some embodiments, it may be advantageous for the multi-axis deposition system to comprise a first print head that is comprises a mixing nozzle and a second print head that does not comprise a mixing nozzle. As described elsewhere herein, in some embodiments, the print head may be configured to accept one or more material inputs (e.g., one material input, two material inputs, etc.). When two or more material inputs are present, the inputs may be substantially the same or they may differ. In some embodiments, the print head may be configured to mix two or more reactive material inputs to form a reactive mixture that may be deposited onto a substrate while the first and second material inputs are reacting and/or after the first and second material inputs have reacted. For example, the print head may be configured to mix a polyol and an isocyanate to form a reactive polyurethane mixture. Other examples of suitable reactive mixtures include reactive polyurea mixtures, reactive mixtures comprising reactive polyurethane and reactive polyurea blends, reactive mixtures comprising epoxy groups and amine groups, and reactive silicone mixtures.
A substrate in a multi-axis deposition system may be any suitable substrate capable of receiving the material deposited by the print head. In some cases, the substrate may have a shape that enables facile deposition of the material of interest in a morphology of interest by the print head. As an example, the substrate may have a shape that substantially corresponds to the morphology of interest, such as a footwear last for footwear applications (e.g., as shown in
In some embodiments, a multi-axis deposition system may comprise a substrate that is removable. The substrate may be configured to be positioned in the multi-axis deposition system during material deposition and removed after material deposition. In some embodiments, a multi-axis deposition system may comprise multiple substrates that may be added to the multi-axis deposition system prior to material deposition and/or removed from the multi-axis deposition system after material deposition. Each substrate may have a different shape (e.g., a different shoe size, a different cup size, a mold for a different type of apparel), or two or more substrates may have substantially the same shape.
As described above, one or more articles may be disposed on the substrate prior to material deposition and/or during material deposition using a multi-axis deposition system. The article(s) disposed on the substrate may be configured to be positioned on the substrate during material deposition and, optionally, removed from the substrate after material deposition. In some embodiments, a multi-axis deposition system may be configured to deposit material onto a multiple articles successively, each of which may be added to the multi-axis deposition system prior to material deposition and/or removed from the multi-axis deposition system after material deposition. For example, a textile (e.g., a non-flat textile, an upper, a woven textile, a knit textile) may be disposed on the substrate prior to material deposition, during material deposition, and/or after material deposition. In some embodiments, a multi-axis deposition system may be employed to deposit a reactive mixture as described above onto a textile to form a 3D-printed material on the textile and/or on a succession of textiles sequentially added to the substrate.
It should be noted that the print head(s) and the substrate in a multi-axis deposition system comprising both a print head and a substrate may be oriented with respect to each other in other ways than that shown in
As described above, a multi-axis deposition system may comprise one or more print heads that may be configured to be translated along one or more axes. In some embodiments, one or more print heads may be configured to be translated along one axis, along two axes, or along three axes. In certain cases, the axes may be perpendicular to each other. In other cases two or more of the axes are not perpendicular to each other (e.g., they may intersect at an angle between 45° and 90°). For example, in some embodiments the print head may be configured to be translated vertically, and/or translated in one or more directions perpendicular to the vertical direction. As another example, in some embodiments one or more print heads may be configured to be translated in a direction perpendicular to the substrate, and/or in one or more directions parallel to the substrate. As a third example, in some embodiments one or more print heads may be configured to be translated at a 45° angle with respect to the substrate. In some cases, each axis of translation may independently be controlled by separate motors. In some embodiments, one or more print heads may not be configured to be translated.
In some embodiments, one or more print heads in a multi-axis system may be configured to be rotated around one axis, around two axes, or around three axes. In some embodiments, one or more print heads may be configured to be rotated around more than three axes (e.g., around more than four axes, around more than six axes, around more than eight axes, around more than 10 axes, or around more than 12 axes). In certain cases, the axes may be perpendicular to each other. For example, in some embodiments the print head may be configured to be rotated around a vertical axis, and/or rotated around one or more axes perpendicular to the vertical axis. As another example, in some embodiments one or more print heads may be configured to be rotated around an axis perpendicular to the substrate, and/or around one or more axes parallel to the substrate. In some cases, each axis of rotation may independently be controlled by separate motors. In some embodiments, one or more print heads may not be configured to be rotated. In some embodiments, the print head may be configured to be stationary.
In some embodiments, a substrate in a multi-axis system may be configured to be translated along one axis, along two axes, or along three axes. In certain cases, the axes may be perpendicular to each other. In other cases two or more of the axes are perpendicular to each other (e.g., they may intersect at an angle between 45° and 90°). For example, in some embodiments the substrate may be configured to be translated vertically, and/or translated in one or more directions perpendicular to the vertical direction. As another example, in some embodiments the substrate may be configured to be translated in a direction perpendicular to the print head, and/or in one or more directions parallel to the print head. As a third example, in some embodiments the print head may be configured to be translated at a 45° angle with respect to the substrate. In some cases, each axis of translation may independently be controlled by separate motors. In some embodiments, the substrate may not be configured to be translated.
In some embodiments, a substrate in a multi-axis system may be configured to be rotated around one axis, around two axes, or around three axes. In certain cases, the axes may be perpendicular to each other. In some embodiments, the substrate may be configured to be rotated around more than three axes (e.g., around more than four axes, around more than six axes, around more than eight axes, around more than 10 axes, or around more than 12 axes). For example, in some embodiments the substrate may be configured to be rotated around a vertical axis, and/or rotated around one or more axes perpendicular to the vertical axis. As another example, in some embodiments the substrate may be configured to be rotated around an axis perpendicular to the print head, and/or around one or more axes parallel to the print head. In some cases, each axis of rotation may independently be controlled by separate motors. In some embodiments, the substrate may not be configured to be rotated. In some embodiments, the substrate may be configured to be stationary.
In some embodiments, a multi-axis deposition system may comprise one or more features that aid rotation and/or translation of a print head and/or a substrate. As an example, in some cases the print head may be attached to a print head arm that facilitates motion. When two or more print heads are present, each print head may be positioned separate print head arms or two or more print heads may be positioned on the same print head arm. In some cases, two or more print head arms may be attached to a single gantry. The print head arms may be capable of facilitating translation and/or rotation of the print head. In some embodiments, the print head(s) may be attached to single print head arms; in other embodiments, the print head(s) may be attached to multiple print head arms that are attached at joints that allow for rotation and/or translation. In some cases, one or more motors may facilitate motion of one or more components of the print head arm(s). As another example, in some cases the substrate may be attached to a substrate arm that facilitates motion. The substrate arm may be capable of facilitating translation and/or rotation of the substrate. In some embodiments, the substrate may be attached to a single substrate arm; in other embodiments, the substrate may be attached to multiple substrate arms that are attached at joints that allow for rotation and/or translation. In some cases, the substrate may be attached to a robot arm. In some cases, one or more motors may facilitate motion of one or more components of the substrate arm(s). In certain embodiments, the print head may be attached to a print head arm and the substrate may be attached to a substrate arm.
In
Substrate 1010 in
In some embodiments, a multi-axis system may comprise further features in addition to some or all of those described above. For example, the multi-axis system may be encased in a frame or enclosure.
Certain combinations of print head motion and substrate motion may be especially advantageous. For example, as shown in
In some embodiments, a multi-axis system may have one or more features that make it suitable for 3D-printing materials of interest. For example, the multi-axis system may be configured to deposit a material onto a substrate as a continuous stream or as a continuous filament. In other words, the substrate may be in fluid communication with the print head via the material during deposition. In certain cases, the multi-axis system may be employed to deposit a continuous stream or filament that extends from a first side of a last or a material disposed on the last (e.g., an upper, a 3D-printed material disposed on an upper) across the bottom of the last or material disposed on the last to the opposing side of the last or material disposed on the last. In some cases, the multi-axis system may be employed to print each portion of an article of footwear except for the upper.
In some embodiments, a multi-axis system may be configured to 3D-print materials with one or more advantageous properties. For example, the multi-axis system may be configured to 3D-print materials with a feature size of greater than or equal to 100 microns, greater than or equal to 200 microns, greater than or equal to 500 microns, greater than or equal to 1 mm, greater than or equal to 2 mm, greater than or equal to 5 mm, greater than or equal to 10 mm, greater than or equal to 20 mm, greater than or equal to 50 mm, greater than or equal to 1 cm, or greater than or equal to 2 cm. In some embodiments, the multi-axis system may be configured to 3D-print materials with a feature size of less than or equal to 5 cm, less than or equal to 2 cm, less than or equal to 1 cm, less than or equal to 5 mm, less than or equal to 2 mm, less than or equal to 1 mm, less than or equal to 500 microns, or less than or equal to 200 microns. Combinations of the above-referenced ranges are also possible (e.g., greater than or equal to 100 microns and less than or equal to 5 cm). Other ranges are also possible.
As discussed herein, a 3D printer may be provided that is capable of printing a material (e.g., a composite) that is formed by combing two or more other materials (e.g., a polymer and particles, e.g., reinforcing particles) to create a 3D object, such as an article of a shoe. Additionally (or alternatively), such 3D objects may comprise a gradient structure with at least one non-uniform property (e.g., color, average stiffness, average Shore A hardness, average pore size, and average density). The inventors have appreciated that existing techniques for generating printer instructions for a 3D printer, such as those implemented in conventional slicer software applications, may be unable to accurately determine appropriate printer settings (e.g., a ratio of two or more inputs to a mixing chamber and/or nozzle, a spin speed of an impeller in the mixing nozzle, sequencing of material into a mixing chamber and/or nozzle, valving to change material inputs into the mixing chamber and/or nozzle, total cumulative flowrate of all inputs to a mixing chamber, vertical position of a print head relative to the substrate, speed of movement of the print head, amount of reverse pumping following a movement command, temperature of the print head, temperature of a substrate onto which the article is printed, and the calibration setting for a material inlet pump) to properly print such materials. Accordingly, aspects of the present disclosure relate to a computer program that is configured to generate printer settings for printing such materials in uniform and/or gradient structures of a 3D object.
The computer program may be configured to receive object information, such as a design file for a 3D object (e.g., from a computer-aided design (CAD) program) and/or a print path for printing a 3D object (e.g., from a slicer application) with information indicative of target material properties at various points along the print path, and output print instructions that may be provided to a 3D printer to accurately create the 3D object. The computer program may generate the print instructions by, for example, identifying a target material that is to be deposited, identifying the input materials required to create the target material, and identifying the printer settings to print the target material using the input materials. Once the appropriate set of printer settings have been identified, print instructions may be generated using the identified set of printer settings. For example, print instructions may be generated that comprise a print path for the print head to follow and printer settings information indicative of the appropriate printer settings at a plurality of points along the print path.
The computer program may comprise a set of instructions that may be executed by a computer system comprising a processor (e.g., a hardware processor or a virtual processor) and a memory (e.g., a non-transitory computer readable medium). For example, the computer program may comprise a set of instructions stored in a non-transitory computer readable medium that programs at least one processor coupled to the non-transitory computer readable medium. It should be appreciated that the computer system may be communicatively coupled to a 3D printer and/or integrated with the 3D printer.
In some embodiments, the computer program may comprise a plurality of instructions that program at least one processor to perform a method 1000 in
In act 1002, the system may receive object information associated with a 3D object. The object information may be, for example, a design file for a 3D object to be printed. The design file may comprise information indicative of one or more properties of the 3D object such as shape, material composition, and/or color. The design file may be in any of a variety of formats. Example formats include: Drawing Interchange Format (DXF), COLLAborative Design Activity (COLLADA), STereoLithography (STL), Initial Graphics Exchange Specification (IGES), and Virtual Reality Modeling Language (VRML). Alternatively (or additionally), the object information may comprise a print path for a print head to follow to print the 3D object (e.g., generated by a slicer application) and information indicative of the desired material properties at various points along the print path. For example, the object information may comprise a print path comprising a plurality of points and metadata associated with one or more (or all of) the plurality of points indicative of a desired material property at the point (e.g., color, average stiffness, average Shore A hardness, average pore size, average density, etc.). In some implementations, the metadata may be directly associated with one or more points in the plurality of points. In other implementations, the metadata may be stored in another format and overlaid onto the print path to determine the material properties at a given point. For example, the metadata may be desired color information stored in an image comprising a plurality of pixel values that may be overlaid onto the print path. In this example, the pixel value that aligns with a given point in the print path may be the metadata associated with the respective point.
In act 1004, the system may identify a target material to be printed based on the object information. For example, the object information may comprise information regarding the target material (e.g., in metadata) and the system may directly identify the target material from the received object information.
In act 1006, the system may identify input material(s) to create the target material. For example, the 3D printer may print the target material in the object by mixing a first material with a second material. In this example, the system may identify the first and second materials. The system may identify this information by, for example, retrieving information stored in a memory of the computer system regarding the input materials required to create the target material in the object.
In act 1008, the system identifies one or more printer settings for printing the target material using the identified input materials. In some embodiments, the system may identify one or more printer settings required to print the target material at a plurality of discrete points in the object (e.g., along the print path). In instances where the printer settings deviate between discrete points (e.g., to print a gradient structure in the object), the system may employ interpolation techniques (e.g., linear interpolation and cubic interpolation) to smooth shifts in printer settings between the discrete points. In one example for illustration, the system may identify that the mixing ratio of two materials needs to be 40/60 at a first point in a gradient structure and a 50/50 ratio at a second point in the gradient structure. In this example, the system may fit a linear curve between the first and second points to create a smooth ramp between a 40/60 ratio and a 50/50 ratio. Thereby, the system may create a set of printer settings to employ along the print path as the print head moves from the first point to the second point.
In act 1012, the system may generate the print instructions using the identified printer settings in act 1008. The print instructions may comprise, for example, a print path for a print head to follow to print the 3D object along with printer settings at a plurality of points along the print path (e.g., generated in act 1008). The print instructions may be, for example, G-code instructions. Once the print instructions have been generated, the system may transmit the print instructions to a 3D printer (and/or one or more other components of a 3D printer in embodiments where the computer system is integrated with the 3D printer).
As mentioned, certain aspects of the present invention generally relate to the printing of materials, using 3-dimensional printing and other printing techniques, including the printing of foams and other materials and/or the modulation of material composition and material properties through space and/or time. In some embodiments, a foam may be prepared by mixing materials within a nozzle, such as a microfluidic printing nozzle, which may be used to direct the resulting product onto a substrate. The nozzle may be controlled, for example, using a computer or other controller, in order to control the deposition of material onto the substrate. In some cases, gases or other materials may be incorporated into the material within the nozzle, e.g., to form a foam. However, it should be understood that the present invention is not limited to only foams; for example, other materials, including composites that comprise particles (e.g., reinforcing particles), are also included in other embodiments of the invention.
For instance, certain aspects of the invention are generally directed to devices for 3D-printing. Generally, in 3D-printing, material is controllably deposited, e.g., on a substrate, to create a product. The material may be deposited in a pattern defining the product, or that can be manipulated to create the product, e.g., by removing portions of the pattern. In some cases, a printing nozzle, such as a microfluidic printing nozzle, may be used to direct material onto a substrate. The nozzle may be controlled, for example, using a computer or other controller, in order to control the deposition of material onto the substrate.
One example of an embodiment of the invention is now described with respect to
One or more fluids may flow into the nozzle, and in some embodiments, mixed within the nozzle, e.g., within a mixing chamber within the nozzle to form the material to be deposited on the substrate. In some cases, active mixing may be used to mix fluids within the nozzle. For example, as is shown in
In some embodiments, as discussed herein, the speed of the impeller may be controlled, e.g., by a computer or other electronic controller, to control the mixing and/or direction of material exiting the nozzle. For example, the controller may control a valve or other apparatus to control the exiting of material from the nozzle, for example, as the nozzle moves relative to a substrate (or equivalently, as the substrate moves relative to the nozzle). Control of nozzle mixing and the position of the nozzle relative to the substrate may thus be used to control 3D-printing of a material onto the substrate.
In addition, in some embodiments, the material within the nozzle may be subjected to heating or cooling. This may, for example, be used to control mixing and/or reaction within the material, to keep the temperature at substantially the temperature of the surrounding environment (e.g., at room temperature), to prevent the surrounding environmental conditions and/or the heat generated by friction of the impeller and exotherm of the material curing from affecting the reaction or the printing parameters, or the like. Any method may be used to heat or cool the material within the nozzle. For example, heating or cooling may be applied to the nozzle itself, and/or to material within the nozzle. Non-limiting examples include electrical heating, Peltier cooling, application of infrared light, or other techniques such as those discussed herein.
As mentioned, one or more fluids may enter the nozzle to be mixed together. The fluids may enter via a common inlet, and/or via separate inlets, for example, as is illustrated in
As a non-limiting example, in one set of embodiments, two or more fluids may be mixed together to form product on a substrate, for example, a foam or other article, such as a composite. In some cases, a material (e.g., a precursor to the foam) may be deposited on a substrate in a partially fluid state, where the material is able to harden to form the product on the substrate. For instance, the material may have a viscosity of less than 1,000,000 cP, less than 500,000 cP, less than 300,000 cP, less than 100,000 cP, less than 50,000 cP, less than 30,000 cP, less than 10,000 cP, less than 5,000 cP, less than 3,000 cP, less than 1,000 cP, less than 500 cP, less than 300 cP, less than 100 cP, less than 50 cP, less than 30 cP, or less than 10 cP. In some cases, the material may have a viscosity of at least 10 cP, at least 30 cP, at least 50 cP, at least 100 cP, at least 300 cP, at least 500 cP, at least 1,000 cP, at least 3,000 cP, at least 5,000 cP, at least 10,000 cP, at least 30,000 cP, at least 50,000 cP, at least 100,000 cP, at least 300,000 cP, at least 500,000 cP, or at least 1,000,000 cP. Combinations of any of these viscosities are also possible; for example, the viscosity of a material may be between 100 cP and 500 cP. The material may form a product passively (e.g., upon drying of the material, completion of a reaction forming the product, etc.), and/or additional steps may be taken to encourage formation of the product. As various non-limiting examples, heat may be applied to the material and/or to the substrate, light (e.g., ultraviolet light) may be applied to the material to cause a chemical reaction, etc.
In some embodiments, a foam may be prepared by mixing a polymer, a cross-linking reagent, and a cell-forming agent, e.g., within a printing nozzle such as is shown in
One example of a suitable polymer is polyurethane; one example of a cross-linking reagent is isocyanate; and one example of a cell-forming agent is water (which can react with the isocyanate to produce carbon dioxide as the foam forms). Other examples of each of these are discussed in more detail below. In addition, it should be understood that other fluids or reactants may be combined to form a foam, and the invention is not limited to only embodiments that include a polymer, a cross-linking reagent, and a cell-forming agent; see below for additional non-limiting examples. For example, as discussed below, a foam may be prepared using a polymer and a cell-forming agent, but not necessarily a cross-linking agent. In some embodiments, other additives may also be introduced, for example, surfactant, silicone surfactant, UV stabilizer, catalyst, pigment, nucleation promotors, fillers for better abrasion resistance, chemical foaming agents, etc. In addition, other products besides foam may be formed in other embodiments. For example, in some cases, a composite is formed that comprises particles (e.g., reinforcing particles); for example, the composite may include polyurethane or other polymers described herein, as well as particles (e.g., reinforcing particles) such as rubber particles. In some cases, the composite is a foam, although it need not be in other cases.
As mentioned, if more than two fluids or reactants are used, they may, in some embodiments, be introduced into the same nozzle, as is shown in
In some cases, one or more of the inputs to first nozzle 15 may be a mixing chamber, such as mixing chamber 19, having an output 38 which fluidly communicates to inlet 35 of nozzle 15 in this figure. In some cases, mixing chamber may have a similar shape to nozzle 15 (e.g., mixing chamber 19 may be a nozzle), although this is not a requirement. Mixing chamber may have, in some embodiments, one or more inputs (e.g., inputs 41 and 42). In addition, in some cases, mixing nozzle 19 may include an impeller 29, or another suitable mixing apparatus. In this example, impeller 29 causes mixing via spinning (depicted in
A more specific example is provided in
The above discussion describes certain non-limiting examples of various embodiments of the present invention that can be used to produce 3-dimensionally printed foams and other products (e.g., composites), as well as articles made using such techniques. However, other embodiments are also possible. Accordingly, more generally, various aspects of the invention are directed to various systems and methods for 3D-printing foams and other objects as described herein.
As mentioned, certain aspects of the invention are generally directed to foams. Such foams and other articles described herein may be used in a variety of applications, such as footwear. The foam, if present, may be a material comprising a matrix and pores disposed within the matrix. Pores may be randomly distributed throughout the foam, or may be positioned at regular and/or pre-determined intervals. The material present within the pores of a foam is typically of a different phase than the material forming the matrix of the foam (e.g., a foam may comprise pores that comprise gas within a matrix that comprises a liquid and/or a solid). As would be understood to one of ordinary skill in the art, in a closed-cell foam, the cells of the foam are typically isolated or separated from each other. By contrast, in an open-cell foam, the cells of the foam are interconnected with each other; for example, they may be formed in an interconnected fashion, or the cells may be ruptured or become interconnected during or after formation of the foam. These conditions are typically more violent foaming conditions than those resulting in a closed-cell foam.
The foam may be formed from a variety of polymers and gases. The gases may be introduced into materials to form the foam in a number of ways, including into the foam components prior to entrance into the mixing nozzle (e.g. frothed components), during the mixing of components (e.g., active frothing), upon exiting the print nozzle (e.g. release of pressure or spike in temperature to generate gas), generated during printing (e.g. water-blown polyurethanes), generated in a post process after printing is complete by thermally, or otherwise, activating a chemical additive within the material (e.g. blowing agent), etc. In addition, in some cases, a gas may be introduced by providing a liquid that forms a gas, e.g., upon a decrease in pressure or an increase in temperature. For instance, a liquid such as butane may be kept under pressure and/or cooled prior to introduction into the nozzle or the mixing chamber; a change in temperature and/or pressure may cause the liquid to form a gas. Without wishing to be bound by theory, closed cell foams and open cell foams may have different properties (e.g., closed cell foams may have different values of density, stiffness, hardness, and the like than otherwise equivalent open cell foams) and may be suitable for different applications. In some embodiments, closed cell foams may have properties that are better suited to footwear applications than open cell foams.
In some cases, the foams may be prepared to be lightweight, tough, elastic, and/or soft, e.g., using techniques such as those discussed herein. For example, polyurethane foams can be made into a variety of different applications such as shoe soles, cushions, pads, insulation, etc. The properties of the foam can be varied widely, as discussed herein. As an example, similar raw materials can be used to create a piece of rigid insulation, a memory foam pillow, a low density elastic foam pad for a seat cushion, or a high density foam outsole of a shoe. Further non-limiting examples of 3D printed shoes may be seen in a U.S. provisional patent application filed on Feb. 27, 2017, entitled “Systems and Methods for Three-Dimensional Printing of Footwear and Other Articles,” incorporated herein by reference in its entirety.
In some cases, foams may be prepared as discussed herein using various inputs and mixing the inputs using an active mixing nozzle, as described herein. For instance, the foam density may be varied by varying the amount of added gas, the amount of added water (e.g., in water-blown foam applications), the amount of added blowing agent, etc. As another example, the foam density constant may be held constant, but the cross-link density or isocyanate content may be varied to change properties such as the elasticity, elongation, or stiffness of the foam.
In some cases, as discussed herein, a foam precursor, prior to curing, may have different rheological properties than the starting raw materials without gas content. For example, a mixture of low viscosity fluids, gases, and/or surfactants, etc. having Newtonian flow behavior before foaming can be used to produce a precursor having non-Newtonian flow characteristics, e.g., with a yield stress, or shear-thickening or shear-thinning behavior. This may be used herein to produce a precursor having a rheological profile suitable for printing, e.g., on a substrate. Fluids such as incompressible Newtonian fluids or gases can be introduced into a nozzle (e.g., prior to mixing) in a controlled fashion and precisely metered onto a substrate during deposition. In some cases, the foaming process may start within the nozzle, and this process may affect the final mechanical properties of the foam.
Accordingly, certain aspects are generally directed to systems and methods for producing a foam or other products as discussed herein. In some cases, a foam may include a plurality of cells (which may include open and/or closed cells) within a polymer or other suitable matrix. Accordingly, certain embodiments described herein are directed to systems and methods able to 3D-print a material on a substrate that is able to form a foam. For instance, the material, at 3D-printing, may have properties that allow it to flow, e.g., from a nozzle, onto a substrate. The material may also contain a gas therein (and/or a gas precursor) that can form the cells of the foam, e.g., upon solidification of the material to form the foam.
In some embodiments of the invention, a material is formed via mixing of two, three, or more fluids to form a precursor, which is 3D-printed onto a substrate and allowed to solidify to form a foam or other product, such as a thermoplastic, an elastomer, a rigid thermoset, or the like. A variety of fluids may be reacted to form a precursor to the foam, as is discussed in further detail herein. In some embodiments, a microfluidic printing nozzle is used to prepare the material prior to deposition onto a substrate. In some embodiments, more than one fluid may be introduced into the nozzle, and the fluids can be mixed within the nozzle to produce the material to be deposited onto the substrate.
In one set of embodiments, a nozzle is used to direct a material (e.g., a precursor) onto a substrate. The nozzle can have any suitable shape. The nozzle may have any suitable shape having an outlet able to direct material at a substrate. For instance, the nozzle may be conical, pyramid-shaped, funnel-shaped, cylindrical, or the like. The nozzle may also have any suitable size. In some cases, the nozzle may include one or more mixing chambers or other regions in which two fluids come into contact with each other, and can be mixed together, e.g., actively or passively. The nozzle or the mixing chamber may have a volume that is less than 20 ml, less than 18 ml, less than 16 ml, less than 14 ml, less than 12 ml, less than 10 ml, less than 8 ml, less than 6 ml, less than 5 ml, less than 4 ml, less than 3 ml, less than 2 ml, less than 1 ml, less than 0.5 ml, less than 0.3 ml, less than 0.1 ml, etc., and/or a volume that is at least 0.1 ml, at least 0.3 ml, at least 0.5 ml, at least 1 ml, at least 2 ml, at least 3 ml, at least 4 ml, at least 5 ml, at least 6 ml, at least 8 ml, at least 10 ml, at least 12 ml, at least 14 ml, at least 16 ml, at least 18 ml, at least 20 ml, etc.
In addition, fluids may be introduced into the nozzle, and product produced within the nozzle, at relatively high rates. For example, in certain embodiments, the rate of printing of product may be at least 0.1 mL/min, at least 0.3 mL/min, at least 0.5 mL/min, at least 1 mL/min, at least 3 mL/min, at least 5 mL/min, at least 10 mL/min, at least 30 mL/min, at least 50 mL/min, at least 100 mL/min, at least 300 mL/min, at least 500 mL/min, at least 1 L/min, at least 3 L/min, at least 5 L/min, at least 10 L/min, or at least 20 L/min. In some cases, the rate of printing may be no more than 25 L/min, no more than 20 L/min, no more than 15 L/min, no more than 10 L/min, no more than 5 L/min, no more than 3 L/min, no more than 1 L/min, no more than 500 mL/min, no more than 300 mL/min, no more than 100 mL/min, no more than 50 mL/min, no more than 30 mL/min, no more than 10 mL/min, no more than 5 mL/min, no more than 3 mL/min, no more than 1 mL/min, no more than 0.5 mL/min, no more than 0.3 mL/min, or no more than 0.1 mL/min. Combinations of any these are also possible, e.g., the rate of printing may be between 5 L/min and 20 L/min. In addition, as discussed above, a fluid may contain particles (e.g., reinforcing particles) in some cases. In some cases, particles such as reinforcing particles can be introduced into the nozzle, e.g., without the presence of a fluid. For example, the particles (e.g., reinforcing particles) may enter the nozzle in a substantially dry state in certain embodiments.
Relatively small volumes such as these may be useful in certain embodiments to promote more complete mixing, e.g., such that the fluids and/or solids are substantially mixed together, and/or to promote smaller residence times within the mixer, for example, less than 30 s, less than 25 s, less than 20 s, less than 15 s, less than 10 s, or less than 5 s. In addition, relatively small volumes may be useful to more rapidly stop and/or alter the reactants (and/or additives, if present) within the nozzle or mixing chamber. In some instances, a smaller volume may be easier to control and/or alter the degree of mixing, e.g., to compensate for variable flowrates and system reactivities, or the like.
As mentioned, in certain embodiments of the invention, the nozzle may include a valve, such as a needle valve. In some cases, a valving system may be used to control fluid input into the nozzle and/or material exiting the nozzle. In certain instances, various components of the mixing system that come in contact with the material may be set up with a valving system.
The fluids and/or particles (if present) may be mixed until they are substantially mixed together in certain embodiments, e.g., having a relatively uniform appearance, or are substantially homogenous mixed. For instance, the fluids and/or particles (if present) may be mixed such that the individual fluids are evenly distributed relative to each other (e.g., upon exiting the nozzle). In some cases, after mixing, portions of the exiting mixture do not exhibit large or changing variations in relative distributions or ratios of one fluid relative to other fluids. However, in other cases, the fluids and/or particles (if present) may only be partially mixed together. In some cases, mixing within the nozzle may be passive, e.g., where the flow of fluids and/or particles (if present) into the nozzle causes the mixing of the fluids and/or particles within the nozzle. The nozzle may also contain, in some embodiments, baffles or other impediments to disrupt the flow of fluid and/or particles, e.g., to promote mixing.
As one non-limiting example, the geometry of the nozzle can be determined in certain embodiments for a given material set and flow rate such that the material exits the nozzle with a viscosity higher than the viscosities of any of the individual inputs but has not yet solidified. For instance, various polyols and the isocyanates can be selected to tune the material reactivity to suit the flow rate into the nozzle and the mixing volume, such that the materials begin to react as they are mixed and also remain fluid enough to be able to leave the nozzle at the outlet continuously. Other parameters, such as a catalyst or the temperature, may also be used to tune material reactivity. Non-limiting examples of methods of heating or cooling a nozzle are discussed in more detail below.
In some embodiments, material exiting the nozzle may pass through an opening which structures the printed line (e.g. continuously printing) or dose (e.g. dosing mode). The opening can be one of a variety of geometries including, but not limited to, circular, rectangular, star-shaped, any closed two-dimensional shape, multiple separate shapes (e.g., being fed from the same nozzle), or the like.
In addition, in some embodiments, the nozzle, mixing chamber, and/or the impeller may be at least partially coated with a non-stick surface to prevent material from building up on such surfaces. Examples of suitable coatings include, but are not limited to, polymeric coatings such as polyurethane or epoxy coatings, or ceramic coatings.
One non-limiting example of an architecture for a nozzle can be seen in
Examples of architectures for various subsystems in certain embodiments of the invention can be seen in
It should be noted that these architectures are by way of example only, and in other embodiments, other architectures may be used, for example, for nozzles, mixing chambers, pumping subsystems, or the like.
In addition, in some embodiments, the composition or one or more of the fluids and/or particles (if present) may be changed during the mixing process, e.g., to produce a change or a gradient in properties in the product. For example, the ratio of two reactants may be changed during mixing, or one reactant may be replaced with another reactant during mixing, etc. In some cases, a first fluid may be changed to a different fluid in a continuous manner, e.g., without interruption. As another non-limiting example, particles (e.g., reinforcing particles) may be added to the nozzle and/or to a fluid entering the nozzle, and changed to different particles (e.g., reinforcing particles), e.g., without interruption.
Non-limiting examples of properties that may change within a product include pore or cell size, density, stiffness, hardness, degree of cross-linking, chemical composition, or the like. The change may be a step change, or a more gradual change, e.g., producing a gradient in a property. For example, a foam or other product may exhibit a first portion having a first property (e.g., average pore size) and a second portion having a second property. Thus, for example, the product may have a first average pore size and a second portion that solidifies into a foam having a second average pore size, wherein the first average pore size is at least 10%, at least 20%, at least 30%, at least 40%, at least 50%, etc. greater than the second average pore size. There may be a gradual or abrupt change between the portions. Other examples of properties that may change within a product include, but are not limited to, average largest dimension of particles (e.g., reinforcing particles), average concentration of particles (e.g., reinforcing particles), surface roughness, compression strength, slip resistance, and abrasion resistance.
As used herein, a portion of an article may refer to any collection of points within the article (i.e., points that are within the portion of space bounded by the external surfaces of the article). Portions of the article are typically, but not always, volumes of space within the article (in some embodiments, a portion may be a surface within an article, a line within an article, or a point within an article). Portions of the article may be continuous (i.e., each point within the portion may be connected by a pathway that does not pass through any points external to the portion) or may be discontinuous (i.e., the portion may comprise at least one point that cannot be connected to at least one other point within the article by a pathway that does not pass through any points external to the portion). Portions of an article may be substantially homogeneous with respect to one or more properties (e.g., one or more properties of the portion may vary with a standard deviation of less than or equal to 1%, 2%, 5%, or 10% throughout the portion), and/or may be heterogeneous with respect to one or more properties (e.g., one or more properties of the portion may vary with a standard deviation of greater than or equal to 1%, 2%, 5%, or 10% throughout the portion).
In some embodiments, one or more properties of a mixture that is 3D-printed from a nozzle may change as a function of time and/or nozzle position with respect to the substrate. For instance, the composition of one or more components and/or the wt % of one or more components within the mixture may change as a function of time. In some embodiments, one or more physical parameters of the nozzle and/or the substrate may change as a function of time. As an example, the temperature of the nozzle and/or the substrate may change as a function of time. Without wishing to be bound by theory, the temperature of the nozzle and the temperature of the substrate may affect the types of reactions that occur between various components (e.g., cross-linking reactions, foaming reactions, reactions within the nozzle, reactions on the substrate) and/or the rates at which these reactions occur. This may in turn affect the chemical structure of the mixture (e.g., the composition of the mixture, the degree of cross-linking of the resultant foam) during and/or after printing, and/or affect one or more physical properties of the mixture (e.g., the viscosity of the mixture, the average pore size of the resultant foam, the density of the resultant foam, the stiffness of the resultant foam, the hardness of the resultant foam) during and/or after printing. In some embodiments, changes in substrate or nozzle temperature during printing may allow for different portions of the 3D-printed article (e.g., those printed at different times and/or in different positions on the substrate) to have different chemical or physical properties. In some embodiments, the portions with different chemical and/or physical properties may be printed in a single continuous process, and/or may together form a single integrated material.
In one set of embodiments, active mixing processes may be used to mix the fluids. For example, an impeller or other mixing apparatus may be used to mix fluids within the nozzle, e.g., in a mixing chamber within the nozzle. (However, it should be understood that an impeller is not necessarily required in all embodiments.) The impeller, if present, may have any shape or size able to cause the mixing of fluids. For instance, the impeller may include one or more vanes, blades, propellers, paddles, holes, and/or cavities, or the like, which may be used to cause movement (e.g., spinning) of fluids within the nozzle. In one embodiment, an impeller may include internal channels that allow a gas or fluid to enter through the impeller into the mixing chamber or nozzle. For instance, the nozzle may include a spindle having one or more openings that allow gas or other fluids to be released.
In addition, the impeller may be fabricated out of any suitable material, e.g., metal, ceramic, a polymer, or the like. In some cases, the impeller itself may be 3D-printed. The impeller may be controlled using any suitable technique, e.g., by mechanically, electrically, and/or magnetically the impeller. In some cases, more than one impeller or other mixing apparatus may be used. Non-limiting examples of other mixing apparatuses and techniques include turbines or the application of ultrasound or additional fluids into the nozzle.
In addition, in some cases, no impeller or other mixing apparatus is used; for example, passive mixing techniques, such as controlling channel geometries or input flows, may also be used. For instance, ratios and/or compositions of incoming fluids may be controlled to control mixing, e.g., within a nozzle or mixing chamber. Combinations of mixing systems may also be used in certain embodiments, including combinations of active systems, or combinations of active and passive systems, for example, including any of the active or passive systems described herein.
In some cases, an impeller (or other mixing apparatus) may sweep through the nozzle or the mixing chamber such that the closest distance between the impeller as it travels and the wall of the nozzle or mixing chamber is less than 10 mm, less than 5 mm, less than 3 mm, less than 1 mm, less than 0.5 mm, less than 0.3 mm, less than 0.1 mm, less than 0.05 mm, less than 0.0.3 mm, less than 0.01 mm, less than 0.005 mm, etc. In some cases, the impeller may come into contact with the wall, although in other cases, the impeller may be at least 1 mm, at least 3 mm, at least 5 mm, or at least 10 mm away from the wall as it travels. In some cases, the impeller or other mixing apparatus may be one that substantially conforms to the shape of the nozzle or the mixing chamber in which the impeller or other mixing apparatus is located. For instance, the impeller may, upon rotation, sweep through a volume that is at least 50%, at least 60%, at least 70%, at least 80%, at least 90%, or at least 95% of the volume of the nozzle or the mixing chamber.
The impeller, if used, may be rotated at any suitable speed. For example, the impeller may be rotated at a speed of at least 5 rpm, at least 10 rpm, at least 20 rpm, at least 30 rpm, at least 40 rpm, at least 50 rpm, etc. In some cases, much higher rotation speeds may be used, e.g., at least 100 rpm, at least 200 rpm, at least 300 rpm, at least 500 rpm, at least 750 rpm, at least 1000 rpm, at least 2000 rpm, at least 3000 rpm, at least 5000 rpm, at least 7500 rpm, or at least 10,000 rpm. Higher rpm speeds may be useful in certain embodiments to create a froth or a foam. In some (but not all) embodiments, the impeller may be rotated at an rpm speed that is at least 16 times the residency time of the material in the mixing chamber or the impeller (for example, if the residency time is 10 seconds, then the rpm speed may be at least 160 rpm). In some cases, the impeller may be rotated at variable speeds. For instance, the impeller may be rotated at different speeds to control the formation or various properties of the foam or other product, and/or the impeller may be rotated to control the rate at which a material is deposited onto a substrate from the nozzle. In addition, in some cases, the impeller may be rotated at a speed that increases or decreases with respect to time. In some cases, changing the rotation speed of the impeller with respect to time may be used to alter a property of the foam or other product, e.g., from a first portion to a second portion. An example of a system that can be used to control the speed of the impeller can be seen in Int. Pat. Apl. Pub. No. WO 2016/164562, incorporated herein by reference.
In addition, in some embodiments, the impeller may be at least partially coated with a non-stick surface to prevent material build-up, as discussed herein.
In some cases, the impeller shape has a shape that allows it to fill the majority of the volume of the mixing chamber, such that the mixing volume is relatively small. When the mixing volume is relatively small, the material may have a relatively short residency time in the mixer, and the material properties or gradient structures can be varied quickly. In some cases, the free volume of the mixing chamber or nozzle (i.e., the volume therein not occupied by the impeller) may be less than 20 ml, less than 18 ml, less than 16 ml, less than 14 ml, less than 12 ml, less than 10 ml, less than 8 ml, less than 6 ml, less than 5 ml, less than 4 ml, less than 3 ml, less than 2 ml, less than 1 ml, less than 0.5 ml, less than 0.3 ml, less than 0.1 ml, etc. Thus, for example, in some embodiments, the impeller has a conical shape, e.g., if the mixing chamber or nozzle has a conical shape. In addition, in some cases, the impeller may be positioned such that the impeller as it travels has a distance from the wall of the nozzle or mixing chamber as discussed herein.
In one set of embodiments, the position of the impeller can be controlled or altered, for example, before or during mixing. The impeller may be actuatable with respect to the position of the mixing chamber, e.g., such that the mixing volume can be changed at any point to account for variable flowrate, thus keeping the residency time in the mixing chamber constant. For example, an actuator or servo may be able to move the impeller laterally within the mixing chamber, or towards an outlet, for example, during mixing or rotation of the impeller. In addition, in some cases, the impeller speed can be varied, such that the material experiences a fixed number of impeller rotations per residency time in the mix chamber.
In certain embodiments, the impeller can be used as a valve. For example, the end of the impeller may be directed into the outlet of the nozzle to block and close the nozzle, thereby preventing or controlling flow out of the chamber. For instance, the impeller may be directed forward (into the outlet) to prevent flow, and/or moved various distances relative to the outlet to allow different flows of fluid out of the nozzle.
In one set of embodiments, the nozzle and/or the mixing chamber may be heated or cooled. In some cases, the temperature of mixing may be controlled, for instance, to allow for uniform mixing, to facilitate reaction of fluids therein (e.g., to an optimum or desired temperature), to remove excess heat (e.g., contributed by a chemical reaction, the spinning of an impeller, etc.), or the like. Various methods can be used to add heat or remove heat from the nozzle or the mixing chamber. For example, a heat source may be positioned to deliver heat to the nozzle or mixing chamber, or to one or more fluids entering therein. Examples of heat sources include electrically resistive heaters, infrared light sources, or heating fluids (e.g., which can transmit heat using a heat exchanger or the like). In some cases, more than one heat source may be used. Similarly, a variety of cooling sources can be used in some embodiments to remove heat from the nozzle or mixing chamber. Non-limiting examples include Peltier coolers or cooling fluids (e.g., which can remove heat using a heat exchanger or the like).
Heating and/or cooling may, for example, be used to control mixing and/or reaction within the material, to keep the temperature at substantially the temperature of the surrounding environment (e.g., at room temperature), to prevent the surrounding environmental conditions and/or the heat generated by friction of the impeller and exotherm of the material curing from affecting the reaction or the printing parameters, or the like. In some cases, the temperature may be altered by at least 5° C., at least 10° C., at least 15° C., at least 20° C., or by other ranges such as those discussed herein. In other embodiments, however, the temperature may be controlled or altered by no more than 20° C., no more than 15° C., no more than 10° C., no more than 5° C., etc. relative to the incoming fluids or the surrounding environmental conditions.
In addition, in some embodiments, one or more sensors may be present, e.g., within the nozzle or mixing chamber, within an outlet, within the substrate, or within sensing communication of the nozzle, mixing chamber, outlet, and/or substrate. Such sensors may be used to determine a property of the incoming fluids, the mixing process, and/or the exiting material (for example, the flowrate), e.g., qualitatively and/or quantitatively. In some cases, such information may be used to control the process, e.g., by controlling the flow of fluid into the nozzle or mixing chamber, the mixing speed (e.g., of an impeller), the flow exiting an outlet, the opening and closing of a valve at the outlet, or the like. Non-limiting examples include temperature sensors (e.g., thermocouples, infrared cameras, or the like), pressure transducers, photodiodes, colorimetric sensors, etc. In addition, more than one sensor can be used in some cases.
Fluid, or solid particles, or a semi-solid paste, may be introduced into the nozzle or mixing chamber from one, two, three, or more inputs, in one set of embodiments. The inputs may independently have the same or different distances from the outlet of the nozzle or mixing chamber. As an example, two inputs may be near the top of a nozzle or mixing chamber, e.g., to allow two fluids to mix, and additional inputs may be lower, e.g., to introduce additional components (for instance, additives) as the fluids flow down the mixing chamber. As various non-limiting examples, this may be useful to allow reactions to occur in a certain order, to build viscosity first before starting to foam, to mix surfactants before adding filler, to mix ingredients prior to adding a catalyst, or the like.
In some embodiments, one or more of the inlets may be controlled using one or more valves or other apparatuses. In some cases, the valves may be controlled using a computer or other controller, e.g., as discussed herein. Thus, for example, valves may be used to control flow into (and/or out of) the nozzle. In some cases, valves may be used to control the flow of fluids through channel intersections, e.g., to keep fluids from reacting or curing too early (e.g., by creating a cured skin at the interface of an inactive channel). Examples of valves that can be used include, but are not limited to, needle valves, ball valves, gate valves, butterfly valves, and the like. The valves can independently be controlled, e.g., by electrical actuation, pneumatic actuation, or the like. In addition, in some cases, an impeller (if present) may be used as a needle valve, e.g., in conjunction with an outlet, as discussed herein.
The entering fluid may be gas, a liquid, a viscoelastic material, and/or any other flowable or deformable material. In some cases, the fluid may also contain particles such as particles (e.g., reinforcing particles), including those discussed above. In addition, the entering fluid may include combinations of any of these in certain embodiments. In some cases, two or more fluids may be mixed prior to delivery, e.g., as discussed in detail herein. However, in some cases, two or more fluids may not be mixed prior to delivery. For instance, two or more inlets into the nozzle or mixing chamber may be used to introduce two or more separate fluids. These fluids can then be mixed in the nozzle or mixing chamber.
The fluids may be delivered using any suitable technique, and the same or different techniques may be used to delivery different fluids. For instance, fluids may be delivered passively (i.e., by gravitational flow), or actively (for example, by using pumps such as progressive cavity pumps, auger pumps, gear pumps, or the like). In some embodiments, the fluids may delivered using input channels that may have features to create turbulent flow and/or to cause passive mixing, e.g., as fluid flows through the channels. This may be useful, for example, in causing some mixing (for example, of a fluid with an additive) in order to occur prior to entry into a nozzle or mixing chamber such as described herein. In some cases, as mentioned, the nozzle may also include particles such as reinforcing particles, which may be incorporated into the final product, e.g., as a composite material.
In some cases, active mixing may be used to control the delivery of different fluids and/or particles (if present). This may be useful, for example, for mixing fluids entering in at different flowrates (e.g., as in a 4:1 or 10:1 ratio), different viscosities, or the like. For example, in some cases, fluids that may be used include fluids that have relatively high viscosities, or viscoelastic solids that exhibit a yield stress, etc.
In some cases, a gas and a liquid may be mixed within the nozzle, e.g., as discussed above, to produce a froth. The gas may be added to the nozzle, and/or generated within the nozzle. The froth may comprise bubbles or pockets of gas dispersed within the fluid. The bubbles within the froth may be dispersed relatively uniformly or homogenously, or may have a relatively small average size. For example, the average bubble size within the froth may be less than 10 mm, less than 5 mm, less than 3 mm, less than 1 mm, less than 500 micrometers, less than 400 micrometers, less than 300 micrometers, less than 200 micrometers, less than 100 micrometers, less than 50 micrometers, less than 30 micrometers, less than 10 micrometers, less than 5 micrometers, etc. in average or characteristic diameter and/or the average bubble size may be at least 1 micrometer, at least 2 micrometers, at least 3 micrometers, at least 4 micrometers, at least 5 micrometers, at least 10 micrometers, at least 30 micrometers, at least 50 micrometers, at least 100 micrometers, at least 300 micrometers, at least 500 micrometers, at least 1 mm, at least 3 mm, at least 5 mm, etc. The bubbles may also exhibit a relatively uniform distribution of sizes, for example, such that at least 80%, at least 90%, or at least 95% of the bubbles within a sample of froth have an average diameter that is between 80% and 120%, or between 90% and 110% of the average bubble diameter. The gas may be introduced as one of the fluids entering the nozzle, and/or generated through chemical reaction of fluids within the nozzle. Non-limiting examples of gases that may be used include air, carbon dioxide, nitrogen, argon, or the like. In some cases, the froth may be deposited onto a substrate, e.g., as discussed herein. The froth may, in some embodiments, comprise at least 20%, at least 30%, at least 40%, or at least 50% by volume of gas. In addition, in some cases, the froth may also contain particles (e.g., reinforcing particles).
In some cases, the nozzle may include more than one fluid that can be mixed with the gas. For example, in one embodiment, reactive fluids or fluids that contain surfactants that facilitate the introduction of the gas as bubbles in the fluids may be used. Examples of surfactants are discussed in more detail below. In some cases, mixing may occur relatively rapidly (for example, by spinning the mixing impeller at high velocity), and the froth would be in its near final form upon exiting the mixing nozzle. The froth may then be deposited or hardened to form a foam. The density of the froth (or the subsequent foam) can be varied by varying the ratio of the gas to the liquid. The mean bubble size in the froth (or the foam) can be varied, for example, by changing the impeller rotational velocity and/or the residence time in the nozzle or mixing chamber. The mechanical properties of the foam can also be changed, for example, by varying fluid compositions entering the nozzle during the formation process (for example, the ratio of isocyanate to polyol).
In some cases, producing froths or other materials containing gas within the nozzle, e.g., by mixing within the nozzle, may allow control over the froth or subsequent product that is formed. For instance, rheological properties may be controlled or altered by controlling mixing and/or the introduction of fluids within the nozzle. Froth development also may be at least somewhat independent of reaction rates, as it can be partially controlled by controlling external factors such as the mixing rate, e.g., at least in embodiments where no gas is produced by reaction (although in other embodiments, gases that contribute to the froth may desirably be produced by reaction).
In one set of embodiments, a material (for example, a froth), when deposited onto a substrate, may have a variety of rheological properties. For instance, the material may be substantially fluid and able to flow, e.g., to conform a mold or other substrate to which it is deposited. In some cases, the material may have a viscosity of less than less than 1,000 cP, less than 500 cP, less than 300 cP, less than 100 cP, less than 50 cP, less than 30 cP, or less than 10 cP. The material may also be Newtonian or non-Newtonian. In other embodiments, however, the material may exhibit some degree of solidity or elasticity, e.g., having a non-zero yield stress, and/or by exhibiting at least some resistance to a distorting influence or deforming force that is applied to the material. In some cases, the material may be sufficiently solid as to be able to define or hold a shape. For instance, the material may be sufficiently solid such that it deforms from its original shape by less than 10% (by volume) after deposition on a substrate, e.g., within 30 seconds after printing onto the substrate.
The substrate may be any suitable target for a material exiting a nozzle. In some cases, the substrate is planar, although in other cases, the substrate is non-planar. For instance, the substrate may be a mold (e.g., the mold of a shoe), to which a material may be introduced. In some cases, the material may be relatively fluid and able to conform to contours within the substrate (e.g., if the substrate is a mold). However, in other cases, the material may be relatively solid, e.g., having a defined shape, upon deposition onto the substrate, such as is discussed herein.
In some cases, the substrate may also be heated or cooled, e.g., to promote or inhibit a reaction, to cause solidification to occur, or the like. In some cases, the temperature may be altered by at least 5° C., at least 10° C., or by other ranges such as those discussed herein. Any method may be used to heat or cool the substrate. For example, heat or cooling sources may be used to apply heat or cooling to the substrate, the substrate may be contained within a heated or cooled environment, or a source of a heated or cooled fluid may be used to heat or cool the substrate, e.g., via a heat exchanger). In one embodiment, radiant light or infrared radiation may be applied to the substrate for heating.
As a non-limiting example, in one embodiment, a two-stage foaming system that implements two foaming types may be used. For example, using mechanical frothing in the nozzle may be used to mix a Newtonian liquid with a blowing agent into a printable viscoelastic foam formulation. After deposition, the polymer in the foam may be completely or partly cured. The temperature of the polymer can be raised to drive the decomposition of the blowing agent, and the subsequent expansion of the foam.
As another non-limiting example, a nozzle involving mechanical frothing may be used to create a foam having a yield stress that behaves viscoelastically. After deposition, the foam may be heated to achieve further expansion of the foam. This secondary expansion can be carried out, for example, using an agent, such as azodicarbonamide. For example, one or more inputs can be used to deliver a polyol loaded with surfactant and a blowing agent into a nozzle, which are then mixed together, e.g., such that a froth is formed.
In some aspects, two or more fluids may be mixed prior to introduction into a nozzle. In some cases, the fluids may be mixed in a second nozzle or mixing chamber (e.g., separate from the first nozzle), and in some cases, a series of mixing chambers may be used, in any arrangement, e.g., in series and/or parallel. Thus, in some embodiments, more than one stage of mixing or combining fluids may be used. As non-limiting example,
Mixing within a mixing chamber may be relatively complete, or may be partial in some cases. In addition, in some cases, no mixing may occur in a mixing chamber, other than incidental mixing or diffusion (for example, as two fluids come into contact with each other). As noted above, more vigorous mixing can occur within the printing nozzle, which may lessen the need for complete mixing to occur upstream. However, in other embodiments, more complete mixing may occur within one or more mixing chambers upstream of the printing nozzle.
In some aspects, one or more purge fluids may be used to purge one or more of the inlets, outlets, nozzles, and/or mixing chambers, etc. For example, a purge fluid may be passed through one or more of these when they are not actively being used to mix or print, and/or to clear fluids so that different fluids can be used. For instance, a purge fluid may flow through an inlet when switching the inlet from a first fluid source to a second fluid source, e.g., to purge residual fluid from the first fluid source that may be present. The purge fluid may flow through the nozzle in some cases, and/or be removed prior to the nozzle. Non-limiting examples of purge fluids include gases such as air, carbon dioxide, nitrogen, argon, or the like, and/or liquids such as water (which may be pure, contain one or more additives such as surfactants in some cases, etc.). Purge fluids could also be a non-reactive paste such as petroleum jelly or a viscous silicone oil or paraffin wax, or an aqueous or alcohol based gel such as pluronic or carbopol. Combinations of purge fluids may also be used in some embodiments.
As a non-limiting example of use of a purge fluid, a nozzle may have a first inlet and a second inlet, in which two fluids (A and B) are reacted together to produce a first product. The nozzle may also be used to produce a second product also formed from two fluids (A′ and B′), where one or both of A′ and B′ are different than A and B. Both A and A′ may be introduced using the first inlet, while B and B′ may be introduced using the second inlet. To avoid contamination of A with A′ and/or B with B′, one or more purge fluids may be introduced between introducing A and A′ to the nozzle and/or B and B′ to the nozzle. In some cases, sufficient purge fluid may be introduced to clear the entire nozzle or mixing chamber between different fluids, although in other cases, some degree of contamination may be deemed to be acceptable, e.g., the purge fluid may be used to reduce but not completely eliminate contamination. The introduction of more than one fluid into an inlet may be controlled using any suitable technique; e.g., one or more fluid sources may be able to be placed in fluid communication with an inlet, where control of such fluid communication may be controlled using one or more valves (e.g., needle valves or other valves such as those discussed herein), which in some cases may be controlled using a computer or other controller.
As a non-limiting example,
In various aspects, a variety of foams or other products (such as composites) may be produced. For example, in some embodiments, a foam may be created from a foam precursor comprising a polymer and a cross-linking agent. The polymer can comprise polyol such as a low number average molecular weight diol, high number-average molecular weight diol, a low number-average molecular weight triol, a high number-average molecular weight triol, or a high number-average molecular weight monol. For instance, a high molecular weight monol, diol, or triol may have a number-average molecular weight of greater than 300, 400, or 500, while a low molecular weight monol, diol, or triol may have a number-average molecular weight less than 300, 400, or 500. Other examples of polymers include, but are not limited to, epoxies, acrylates, cyanate esters, silicones, polyesters, phenolics, hydrogels, or the like.
In one set of embodiments, the polymer includes a polyurethane, e.g., formed by reacting the polyol with an isocyanate. The polyol may be any suitable polyhydroxy compound. For example, the polyol may be a hydroxy-terminated ester, ether or carbonate diol, or a hydroxyl-terminated polybutadiene polymer. Non-limiting examples of polyalkylene ether glycols include polyethylene ether glycols, poly-1,2-propylene ether glycols, polytetramethylene ether glycols, poly-1,2-dimethylethylene ether glycols, poly-1,2-butylene ether glycol, and polydecamethylene ether glycols. Examples of polyester polyols include polybutylene adipate and polyethylene terephthalate. Examples of polycarbonate diols include polytetramethylene carbonate diol, polypentamethylene carbonate diol, polyhexamethylene carbonate diol, polyhexane-1,6-carbonate diol and poly(1,6-hexyl-1,2-ethyl carbonate)diol. However, many other suitable polyhydroxy compounds can also be used depending upon the desired application. Any suitable polyol, polythiol or polyamine or mixture thereof that is suitable for this purpose may be used, such as, for example, mixed diols comprising a 2,4-dialkyl-1,5-pentanediol and a 2,2-dialkyl-1,3-propanediol. Specific examples of 2,4-dialkyl-1,5-pentanediols include 2,4-dimethyl-1,5-pentanediol, 2-ethyl-4-methyl-1,5-pentanediol, 2-methyl-4-propyl-1,5-pentanediol, 2,4-diethyl-1,5-pentanediol, 2-ethyl-4-propyl-1,5-pentanediol, 2,4-dipropyl-1,5-pentanediol, 2-isoptopyl-4-methyl-1,5-pentanediol, 2-ethyl-4-isoptopyl-1,5-pentanediol, 2,4-diisopropyl-1,5-pentanediol, 2-isopropyl-4-propyl-1,5-pentanediol, 2,4-dibutyl-1,5-pentanediol, 2,4-dipentyl-1,5-pentanediol, 2,4-dihexyl-1,5-pentanediol, and the like. Specific examples of 2,2-dialkyl-1,3-propanediols include 2,2-dipentyl-1,3-propanediol, 2,2-dihexyl-1,3-propanediol and the like.
In some cases, longer-chain or higher molecular weight polyols may be used to produce relatively softer materials because they have more polyol relative to isocyanate. In some cases, the isocyanate can also be underindexed compared to the number of reactive sites on the polyol to make a softer foam that behaves less elastically.
The cross-linking agent, if present, can comprise an isocyanate in some cases, and/or an isocyanate prepolymer. An isocyanate may have more than one functional isocyanate group per molecule and may be any suitable aromatic, aliphatic or cycloaliphatic polyisocyanate. In some cases, the isocyanate is a diisocyanate. One non-limiting example is an organic diisocyanate, such as methylene diphenyl diisocyanate. Additional examples of organic diisocyanates include 4,4′-diisocyanatodiphenylmethane, 2,4′-diisocyanatodiphenylmethane, isophorone diisocyanate, p-phenylene diisocyanate, 2,6-toluene diisocyanate, polyphenyl polymethylene polyisocyanate, 1,3-bis(isocyanatomethyl)cyclohexane, 1,4-diisocyanatocyclohexane, 1,6-hexamethylene diisocyanate, 1,5-naphthalene diisocyanate, 3,3′-dimethyl-4,4′-biphenyl diisocyanate, 4,4′-diisocyanatodicyclohexylmethane, 2,4′-diisocyanatodicyclohexylmethane, and 2,4-toluene diisocyanate, or combinations thereof. In some cases, an isocyanate prepolymer may be used, e.g., in addition to and/or instead of an isocyanate. For instance, where two isocyanates are added to the ends of a polyol, so it still has functionality of two, but with a higher molecular weight.
In addition, it should be understood that a cross-linking agent is not required. For example, in some embodiments a polymer (such as a thermoplastic polyurethane) can be mixed with fillers and frothed in a nozzle or a mixing chamber, then cooled upon exiting to form a foam.
In some embodiments, no foam is produced and a crosslinked product results. As a non-limiting example, a high number-average molecular weight diol may be mixed with an isocyanate (e.g., a diisocyanate, or other isocyanates described herein) and deposited onto a substrate, e.g., to produce a thermoplastic elastomer. In another embodiment, a low number-average molecular weight diol can be mixed with an isocyanate and deposited onto a substrate, e.g., to produce a rigid thermoplastic. In yet another embodiment, a high number-average molecular weight diol and a high number-average molecular weight triol can be mixed, and then the polyol mixture mixed with an isocyanate and deposited onto a substrate, e.g., to produce a flexible thermosetting elastomer with high resiliency.
In some embodiments, the foam precursor comprises a polyurethane, an epoxy, a silicone, a cyanoacrylate, an adhesive, a cyanate ester, a polyester, a polyimide, a phenolic, or another suitable material. In another embodiment, the foam precursor could comprise a decomposeable binder and particles which stabilize the bubble interface. In some cases, the particles may be sintered at the bubble interface to form a non-polymeric foam, e.g., a metal foam or a ceramic foam.
As a non-limiting example of a foam, in one embodiment, a high number-average molecular weight diol and a high number-average molecular weight triol are mixed with a surfactant, and then the polyol-surfactant mixture is mixed with an isocyanate. The foam precursor that results may be mixed with nitrogen, or another gas, and deposited onto a substrate. Mixing techniques such as those discussed herein, e.g., involving more than one stage of mixing or combining fluids, may be used.
As yet another non-limiting example, a high number-average molecular weight diol and a high number-average molecular weight monol are mixed with a surfactant, and then the polyol-surfactant mixture is mixed with an isocyanate. Mixing techniques such as those discussed herein, e.g., involving more than one stage of mixing or combining fluids, may be used. The foam precursor that results is then mixed with nitrogen, or another gas, and deposited onto a substrate. This may be used to produce memory foam, or other types of foam.
As mentioned, in some embodiments, a surfactant may be used to produce a foam or other product as discussed herein. For example, a surfactant may be used to facilitate the introduction of gas into a fluid, the subsequent stability of the bubbles that are formed, and/or the rheology of the foam can be altered or tuned using various surfactants, or altering their concentration, etc. For instance, in one embodiment, a surfactant may be used that comprises a first moiety with affinity for an air-liquid interface, e.g., to facilitate the introduction of gas into a fluid. Non-limiting examples of such surfactants include sodium stearate, sodium dodecyl sulfate, or silicone-based surfactants such as silicone polyethers. Many such surfactants are widely available commercially.
In some cases, a surfactant molecule may be used that allows production of a high yield stress foam, e.g., a foam able to maintain its shape after deposition on a substrate. For example, in some embodiments, a high-yield stress inducing surfactant is one where the end of the surfactant is more soluble in the continuous phase of the foam precursor. The surfactant may have a relatively high molecular weight, and may be non-ionic. Non-limiting examples of such surfactants include surfactants with a molecular weight of greater than or equal to 1500 Daltons. In addition, in some cases, a surfactant molecule may be used that allows production of a low yield stress foam, e.g., a foam unable to maintain its shape after deposition on a substrate, and the foam may conform to the material around it after deposition. In some embodiments, a low-yield stress inducing surfactant is one where the soluble end may be either charged or have a relatively low molecular weight, e.g., such that no entanglement between the surfactants is able to occur. Non-limiting examples of such surfactants include surfactants with a low molecular weight (e.g., silicone surfactants with a low molecular weight). In addition, in some embodiments, different types of surfactants may be used, e.g., a high yield and a low yield surfactant. By varying the relative concentration of the first surfactant and the second surfactant in the mixture, the resultant foam may vary from high yield stress to low or no yield stress, depending upon the application.
In certain embodiments, the first surfactant molecule may comprise a first moiety having an affinity for an air-liquid interface, and a second moiety that comprises a long chain that is soluble in the foam precursor and prone to entanglement. The second surfactant molecule may, in some instances, comprise the same first moiety with affinity for the air-liquid interface, and a second moiety that comprises a short chain with an electrostatic charge. The electrostatic charge may in some cases be such that the cells of the closed-cell foam repel one another and can move freely past one another.
The cell-forming agent, in some embodiments, forms cells within a material such as a foam or froth, as discussed herein. For instance, the cell-forming agent may comprise water, and/or a gaseous material such as air, carbon dioxide, nitrogen, butane, or the like. In some embodiments, the cell-forming agent comprises a blowing agent that is added that can generate a gas, e.g., chemically. The microfluidic printing nozzle may disperse the blowing agent in a material, for example a polymer, to form a two-phase mixture of blowing agent cells within the polymer. Thus, the blowing agent can comprise a material that decomposes into a gas, e.g., at an elevated temperature. In some cases, the blowing agent can comprise a gaseous material that maintains its liquid state by cooling or pressurization, and reverts to its native gas state when the pressure is released or the blowing agent is heated, which may cause the blowing agent to form a gas, e.g., to cause cells in the polymer to grow. The resultant gas may become trapped in cells within the material, e.g., forming a foam.
As an example of use of a blowing agent, the microfluidic printing nozzle may mix a blowing agent with a material, for example a polymer, which may undergo a chemical reaction to cause the formation of a gas. Chemical blowing agents may include generally low molecular weight organic compounds that decompose to release a gas such as nitrogen, carbon dioxide, or carbon monoxide. Non-limiting examples of chemical blowing agents include azo compounds such as azodicarbonamide.
Thus, in some cases, the blowing agent can be used to create foams that form cells by induction by heat, removal of pressure, or the like. For instance, a foam precursor can be mixed with the blowing agent and deposited onto a substrate or part without forming cells until after deposition, or with only partially formed cells. Thus, in some cases, material may be deposited onto a substrate, then induced to form cells by heating the material. After deposition, cells may form within the product, e.g., by induction by heat, removal of pressure, or the like.
As a non-limiting example, a foam may comprise an ethylene-vinyl acetate foam, which may be utilized in footwear or other applications. A blowing agent may be selected such that the agent phase-transitions into a gas at a temperature at which the polymer containing it is soft and malleable. In some cases, the polymer can expand (e.g., expand up to 600%) as the cells form without rupturing, and the resultant material can be cooled to form a solid foam.
As another example, water may be used in another embodiment as a cell-forming agent. For example, a water-blown foam may be produced where water and a surfactant are mixed into a polymer component, which is then mixed with isocyanate or another substance able to react with water, e.g., to produce a gas. For instance, as a non-limiting example, isocyanate chemically reacts with both water and polyol; the reaction of polyols with isocyanate may be used to increase the molecular weight of the polymer, e.g., to form a polyurethane, while the reaction of water with the isocyanate forms carbon dioxide gas. The carbon dioxide gas becomes trapped in the polymer as it solidifies, and a foam is thus created. In some cases, the amount of water may be controlled to control the properties of the resulting foam, such as density or cell size, e.g., during the reaction process.
As yet another non-limiting example, a blowing agent that decomposes very slowly with time may be selected, such that a foam may be very slowly inflated without any heating required. In some cases, this may result in a foam with improved in rebound properties (e.g., compression strength) versus a substantially similar foam where heat was applied to activate the blowing agent, resulting in a higher performing article for use in footwear.
In addition, in some embodiments, a material may be deposited onto a substrate, e.g., to fill a mold, then the mold may be sealed and the blowing agent induced to form a foam, which may then start to fill in the mold as the foam expands.
In some embodiments, additives are introduced into the mixture. They may be introduced at any suitable point, for example, directly into a nozzle or mixing chamber (e.g., through one or more separate inlets), or upstream of the nozzle or mixing chamber (e.g., using a series of mixing chambers, as described herein). In some embodiments, an additive may be added directly to another fluid (e.g., without necessarily requiring a mixing chamber). These additives can comprise particles such as reinforcing particles (e.g., as described herein), hollow glass spheres, hollow elastomer spheres (e.g., hollow polyurethane spheres), a pigment, a metal, a filler such as a thermally conductive filler, a filler having a relative dielectric constant of at least 5, an ultraviolet stabilizer, a filler concentrate, or another suitable additive. Additional examples of additives include surfactants (e.g., silicone surfactants), catalysts, nucleation promotors, fillers for better abrasion resistance, chemical foaming agents, etc. Combinations of these and/or other additives are also possible. As a non-limiting example, a 3D printed closed-cell foam may be produced that incorporates particulate additives comprising a cellular network of cell walls separating empty cells, where the cell walls comprise a polymer composite including filler particles dispersed in a polymer matrix.
As a non-limiting example, hollow glass spheres or hollow elastomer spheres (e.g., hollow polyurethane spheres) may be incorporated into polyurethanes or other polymers as discussed herein to reduce density, increase stiffness, reduce dielectric constant, provide more nucleation sites for bubble formation, or the like. For instance, hollow spheres may be used to decrease weight. Hollow spheres, for example hollow glass spheres or hollow polymer spheres can be varied, e.g., spatially, in order to change the properties of the product. Other examples of particles (e.g., reinforcing particles) that can be used, e.g., in addition to and/or instead of hollow glass spheres include, but are not limited to, rubber particles and other particles described herein.
In one aspect, a foam may be printed (e.g., via 3D-printing) into a structure defining a plurality of cells, i.e., into a foam-like structure. Thus, a foam may be printed as part of a larger foam-like structure, e.g., where the walls of the foam-like structure (e.g., defining cells of the foam-like structure themselves) are foams having cells. The foam-like structure may have open cells, closed cells, or any combination of open and closed cells, independently of the structure of the foam itself forming the foam-like structure.
In one set of embodiments, one or more methods for manufacturing 3D-printed articles as described herein may be advantageous in comparison to other methods for making articles for use in footwear. For example, a footwear manufacturer employing a method as described herein may be able to use fewer processes to create the article than would be employed in other comparable processes (e.g., the manufacturer may use a three-dimensional printer (3D printer) in a single process to make a component that would otherwise be made by a combination of several processes such as injection molding, lamination, and the like). This may allow for more rapid and/or more facile manufacturing. As another example, one or more of the methods described herein may not necessarily require the use equipment that is expensive to manufacture and whose cost is typically recovered only after repeated use (e.g., molds). Some of the methods described herein may instead employ a 3D printer to create articles whose design can be modified as desired with little or no added cost. In some embodiments, it may be economical for methods as described herein to create small batches of 3D-printed articles (e.g., batches of less than 100, less than 50, or less than 10). It is thus possible for manufacturers may employ some of the methods described herein to respond to changing market conditions, to create articles for use in footwear that are designed for individual users or groups of users, etc. In some embodiments, it may be advantageous to use one or more of the methods described herein to fabricate a 3D-printed article at the point of sale and/or to avoid long distance shipping. Other examples may be seen in U.S. Pat. Apl. Ser. No. 62/464,364, entitled “Systems and Methods for Three-Dimensional Printing of Footwear and Other Articles,” filed Feb. 27, 2017, incorporated herein by reference in its entirety.
A non-limiting example of a 3D-printed article for use in footwear is shown in
In some embodiments, a 3D-printed article may comprise two or more portions, where one or more properties (e.g., average pore size, density, stiffness, stiffness of solid components of the article, Shore A hardness, degree of cross-linking, chemical composition, color, abrasion resistance, thermal conductivity, electrical conductivity, stiffness anisotropy, elastic modulus, flexural modulus, filler content, opacity, conductivity, breathability) of a first portion may differ from one or more properties of a second portion. In some embodiments, the difference in properties between the first portion and the second portion may comprise a gradient of the one or more properties (e.g., the property or properties may vary relatively smoothly from a first value in the first portion to a second value in the second portion). In other embodiments, there may be a sharp change in one or more of the properties at a boundary of one or more of the first portion and the second portion. Other examples include, but are not limited to, average largest dimension of particles (e.g., reinforcing particles), average concentration of particles (e.g., reinforcing particles), surface roughness, compression strength, slip resistance, or abrasion resistance.
It should be understood that while
Similarly, while
In some embodiments, one or more portions may together form an 3D-printed article with one or more of the following features: macrovoids embedded within the article (e.g., a midsole) without an intersecting interface from overmolding, lamination, or ultrasonic welding; one or more open cell lattices; variations in density across geometries that would be challenging to form by molding; interpenetrating foams and elastomers that may, in some embodiments, not be separated by an interface due to molding or lamination; and/or one or more interfaces between different materials with extreme undercuts (e.g., materials with a negative draft angle, materials which cannot be injection molded using a single mold because they would be unable to slide out of the mold).
In some embodiments, a 3D-printed article (e.g., a 3D-printed article comprising two or more portions) may be a foam (e.g., a closed cell foam). For instance,
It should also be understood that certain 3D-printed articles described herein may not be foams (i.e., they may not include any pores). For instance, certain embodiments may relate to 3D-printed articles that are not foams and that comprise one or more elastomers. In addition, in some cases, an article may be printed that can then be formed into a foam, e.g., using a chemical reaction to produce a gas within the article.
As shown in
In some embodiments, a 3D-printed article as designed herein may be suitable for use as a component of one or more articles of footwear.
As described above, certain articles as described herein may be formed by a process involving one or more 3D-printing steps. In some embodiments, an article may be formed by a process involving both one or more 3D-printing steps and one or more non-3D-printing steps. For example, an article may be formed by a first 3D-printing step followed by a first non-3D-printing step which is optionally followed by one or more further 3D-printing steps or non-3D-printing steps. For example, a sole or sole component may be 3D-printed into a mold to form a first portion and then a material may be injection molded or compression molded above the first portion to form the second portion. Third, fourth, fifth, and/or higher numbered portions may then optionally be formed on the second portion (by, e.g., 3D-printing). As another example, a non-3D printing step may comprise directly bonding two materials by pressing a first material (e.g., a non-3D-printed material, an upper) into a second 3D-printed material (e.g., a 3D-printed midsole) prior to full curing of the second material. As a third example, an inkjet finishing process may be applied to deposit one or more materials (e.g., one more pigments) on a 3D-printed article or on a material disposed on a 3D-printed article (e.g., a material injection molded or compression molded on a 3D-printed article). In some embodiments, an inkjet finishing process may enhance the surface quality of the article that is subject to it.
In some cases, 3D-printed foams (e.g., closed-cell foams, open-cell foams, etc.) may be prepared as discussed herein using various inputs, as described herein. For instance, the foam density may be varied by varying the amount of added gas, the amount of added water (e.g., in water-blown foam applications), the amount of added chemical blowing agent, etc. As another example, the foam density constant may be held constant, but the cross-link density or isocyanate content may be varied to change properties such as the elasticity, elongation, or stiffness of the foam.
In some embodiments, one or more properties of a mixture that is 3D-printed from a nozzle may change as a function of time and/or nozzle position with respect to the substrate. For instance, the composition of one or more components and/or the wt % of one or more components within the mixture may change as a function of time. In some embodiments, one or more physical parameters of the nozzle and/or the substrate may change as a function of time. As an example, the temperature of the nozzle and/or the substrate may change as a function of time. Without wishing to be bound by theory, the temperature of the nozzle and the temperature of the substrate may affect the types of reactions that occur between various components (e.g., cross-linking reactions, foaming reactions, reactions within the nozzle, reactions on the substrate) and/or the rates at which these reactions occur. This may in turn affect the chemical structure of the mixture (e.g., the composition of the mixture, the degree of cross-linking of the resultant foam) during and/or after printing, and/or affect one or more physical properties of the mixture (e.g., the viscosity of the mixture, the average pore size of the resultant foam, the density of the resultant foam, the stiffness of the resultant foam, the Shore A hardness of the resultant foam) during and/or after printing. In some embodiments, changes in substrate or nozzle temperature during printing may allow for different portions of the 3D-printed article (e.g., those printed at different times and/or in different positions on the substrate) to have different chemical or physical properties. In some embodiments, the portions with different chemical and/or physical properties may be printed in a single continuous process, and/or may together form a single integrated material.
In some cases, as discussed herein, a foam precursor, prior to curing, may have different rheological properties than the starting raw materials without gas content. For example, a mixture of low viscosity fluids, gases, and/or surfactants, etc. having Newtonian flow behavior before foaming can be used to produce a precursor having non-Newtonian flow characteristics, e.g., with a yield stress, or shear-thickening or shear-thinning behavior. This may be used herein to produce a precursor having a rheological profile suitable for printing, e.g., on a substrate. Fluids such as incompressible Newtonian fluids or gases can be controlled introduced into a nozzle (e.g., prior to mixing) and precisely metered onto a substrate during deposition. In some cases, the foaming process may start within the nozzle, and controlled to control deposition of the precursor and/or the final mechanical properties of the foam.
U.S. Pat. Apl. Ser. Nos. 62/464,363 and 62/464,364 are each incorporated herein by reference in its entirety.
The following examples are intended to illustrate certain embodiments of the present invention, but do not exemplify the full scope of the invention.
Example 1Water-blown polyurethane foam. A mixing nozzle was configured to have two inputs: Input A for an isocyanate pre-polymer, and Input B for a mixture of polyols, surfactants, and water. When the two inputs were combined in the mixing chamber, the water and polyols reacted with the isocyanate to form a polyurethane matrix with a higher number-average molecular weight than the polyols and carbon dioxide that became trapped in the polyurethane matrix to form a foam. Inputs A and B were as follows:
Input A: (one or more of the following components flowed into the mixing nozzle)
Input B: (one or more of the following components flowed into the mixing nozzle, in addition to water)
Such a water-blown polyurethane foam (white, top portion) was co-printed with a non-foaming two-part polyurethane elastomer (blue, bottom portion) to form a shoe sole, as is shown in
A mean pore size of the foam was characterized by slicing through a 3D-printed filament to obtain a cross-section of the foam and then imaging the cross-section with a light microscope and using image analysis (depicted in
Silicone gradient material. A coupon with a gradient in both stiffness and color was fabricated using a two-input mixing nozzle system, as shown in
The inputs were as follows:
Input 1, A and B: (two or more of the following components flowed into the mixing nozzle)
Input 2, A′ and B′: (two or more of the following components flowed into the mixing nozzle)
Mixing cells into a hydrogel. A hydrogel structure is formed using the mixing system. A first input to the mixing nozzle comprises a cross-linking agent for the hydrogel, and a second input to the mixing nozzle comprises an uncross-linked hydrogel precursor. Additional inputs into the mixing nozzle include concentrated cell suspensions of various types, different types of cell media, and concentrates of cell growth factors and chemical signaling agents.
Example 4Printing a rigid epoxy foam. A mixing nozzle comprises a mixing/frothing chamber and at least three inputs. A first input is a gas such as nitrogen or air. A second input is a bisphenol-A-based resin such as Epon® Resin 828, with an added surfactant that stabilizes bubbles. A third input is a curing agent for epoxy resin such as a diamine like ethylenediamine. The second and third input are added to the mixing chamber to induce the epoxy resin to cross-link into a solid thermoset. The gas input flowrate can be varied along with the impeller speed to create a rigid thermosetting foam with variable dielectric properties due to air content.
Example 5Mixing therapeutics into a biodegradable matrix material. A multi-input system can be used for creating a therapeutic-impregnated matrix of material such as a pill. Inputs include: a solution of a biodegradable polymer with a high degradation rate; a solution of a biodegradable polymer with a low degradation rate; a solution of a first active therapeutic agent; a solution of a second active therapeutic agent; a sugar or flow inducing agent; or another suitable input.
A pill-like architecture can then be 3D-printed, wherein the composition of the pill can be varied spatially. For example, the external part of the pill could be 3D-printed to contain a first therapeutic agent, and the material printed has a fast degradation profile for a quick release of the first therapeutic agent. Then the internal part of the pill may be printed with a material that degrades slowly, and may contain two different types of therapeutic agents. The external surface of the pill may have a printed inert sugar coating so that no therapeutic release occurs until the pill has passed through the esophagus. This allows the possibility of combining many pills into one. By this process, a 3D-printed pill can have a customized therapeutic release profile that is specific to a patient.
The same methodology to 3D-print pills can be applied to 3D-printed implantable long-term therapeutic release depots. For example, this 3D-printing methodology can be applied towards fabricating a skin tissue graft, wherein drugs, growth factors, antibiotics, and cells can be printed with variable spatial concentration to promote the regrowth of a skin defect such as a severe burn. Printing an implantable therapeutic depot may involve an input that induces polymerization or cross-linking.
Example 6Printing a rigid epoxy foam: printing a stimuli-responsive structure from a reactive polyurethane system. A system comprising at least four inputs may be used to 3D-print a stimuli-responsive structure, the inputs comprising: an isocyanate cross-linking agent; a polyol mixture wherein the components have low stiffness; a polyol mixture wherein the components have high stiffness; and a chemical blowing agent concentrate dissolved in polyol.
For example, a tri-layer architecture can be 3D-printed to accomplish the stimuli-responsive property. As shown in
The expansion of the bottom material upon decomposition of the chemical blowing agent, coupled with the strong interface with the strain-limiting layer, causes a physical curling of the whole tri-layer structure. Selective placement of the expandable material containing the blowing agent can be utilized to programmatically define deformations in printed parts that will not occur until after the part is printed and heated.
Example 7This example illustrates the formulation and printing of an outsole material. First, a polyol concentrate was made by mixing the ingredients at the prescribed ratio (Part B Fluid) using a planetary centrifugal mixer. Next, the fillers (Outsole Formulation, Part B) were added to the polyol concentrate and mixed with a planetary centrifugal mixer under vacuum. Finally, the Part B mixture was loaded into a syringe, and used to feed into one side of the active mixing head. The same protocol was done for Part A in a separate container.
Part B Fluid: Polyol concentrate:
Part A Fluid: Isocyanate prepolymer:
BASF Lupranate 5030—polyester and MDI quasi prepolymer with NCO content of 18.9%
While several embodiments of the present invention have been described and illustrated herein, those of ordinary skill in the art will readily envision a variety of other means and/or structures for performing the functions and/or obtaining the results and/or one or more of the advantages described herein, and each of such variations and/or modifications is deemed to be within the scope of the present invention. More generally, those skilled in the art will readily appreciate that all parameters, dimensions, materials, and configurations described herein are meant to be exemplary and that the actual parameters, dimensions, materials, and/or configurations will depend upon the specific application or applications for which the teachings of the present invention is/are used. Those skilled in the art will recognize, or be able to ascertain using no more than routine experimentation, many equivalents to the specific embodiments of the invention described herein. It is, therefore, to be understood that the foregoing embodiments are presented by way of example only and that, within the scope of the appended claims and equivalents thereto, the invention may be practiced otherwise than as specifically described and claimed. The present invention is directed to each individual feature, system, article, material, kit, and/or method described herein. In addition, any combination of two or more such features, systems, articles, materials, kits, and/or methods, if such features, systems, articles, materials, kits, and/or methods are not mutually inconsistent, is included within the scope of the present invention.
In cases where the present specification and a document incorporated by reference include conflicting and/or inconsistent disclosure, the present specification shall control. If two or more documents incorporated by reference include conflicting and/or inconsistent disclosure with respect to each other, then the document having the later effective date shall control.
All definitions, as defined and used herein, should be understood to control over dictionary definitions, definitions in documents incorporated by reference, and/or ordinary meanings of the defined terms.
The indefinite articles “a” and “an,” as used herein in the specification and in the claims, unless clearly indicated to the contrary, should be understood to mean “at least one.”
The phrase “and/or,” as used herein in the specification and in the claims, should be understood to mean “either or both” of the elements so conjoined, i.e., elements that are conjunctively present in some cases and disjunctively present in other cases. Multiple elements listed with “and/or” should be construed in the same fashion, i.e., “one or more” of the elements so conjoined. Other elements may optionally be present other than the elements specifically identified by the “and/or” clause, whether related or unrelated to those elements specifically identified. Thus, as a non-limiting example, a reference to “A and/or B”, when used in conjunction with open-ended language such as “comprising” can refer, in one embodiment, to A only (optionally including elements other than B); in another embodiment, to B only (optionally including elements other than A); in yet another embodiment, to both A and B (optionally including other elements); etc.
As used herein in the specification and in the claims, “or” should be understood to have the same meaning as “and/or” as defined above. For example, when separating items in a list, “or” or “and/or” shall be interpreted as being inclusive, i.e., the inclusion of at least one, but also including more than one, of a number or list of elements, and, optionally, additional unlisted items. Only terms clearly indicated to the contrary, such as “only one of” or “exactly one of,” or, when used in the claims, “consisting of,” will refer to the inclusion of exactly one element of a number or list of elements. In general, the term “or” as used herein shall only be interpreted as indicating exclusive alternatives (i.e. “one or the other but not both”) when preceded by terms of exclusivity, such as “either,” “one of,” “only one of,” or “exactly one of.”
As used herein in the specification and in the claims, the phrase “at least one,” in reference to a list of one or more elements, should be understood to mean at least one element selected from any one or more of the elements in the list of elements, but not necessarily including at least one of each and every element specifically listed within the list of elements and not excluding any combinations of elements in the list of elements. This definition also allows that elements may optionally be present other than the elements specifically identified within the list of elements to which the phrase “at least one” refers, whether related or unrelated to those elements specifically identified. Thus, as a non-limiting example, “at least one of A and B” (or, equivalently, “at least one of A or B,” or, equivalently “at least one of A and/or B”) can refer, in one embodiment, to at least one, optionally including more than one, A, with no B present (and optionally including elements other than B); in another embodiment, to at least one, optionally including more than one, B, with no A present (and optionally including elements other than A); in yet another embodiment, to at least one, optionally including more than one, A, and at least one, optionally including more than one, B (and optionally including other elements); etc.
When the word “about” is used herein in reference to a number, it should be understood that still another embodiment of the invention includes that number not modified by the presence of the word “about.”
It should also be understood that, unless clearly indicated to the contrary, in any methods claimed herein that include more than one step or act, the order of the steps or acts of the method is not necessarily limited to the order in which the steps or acts of the method are recited.
In the claims, as well as in the specification above, all transitional phrases such as “comprising,” “including,” “carrying,” “having,” “containing,” “involving,” “holding,” “composed of,” and the like are to be understood to be open-ended, i.e., to mean including but not limited to. Only the transitional phrases “consisting of” and “consisting essentially of” shall be closed or semi-closed transitional phrases, respectively, as set forth in the United States Patent Office Manual of Patent Examining Procedures, Section 2111.03.
Claims
1. A method of printing of an article for use in footwear, comprising:
- receiving object information associated with the article;
- identifying a target material to be printed using the object information;
- identifying two or more input materials to create the target material, at least one of the two or more input materials comprising particles;
- identifying a set of printer settings for printing the target material;
- generating print instructions using the set of printer parameters; and
- printing the article using the print instructions.
2. The method of claim 1, wherein the target material comprises a composite.
3. The method of claim 1, wherein the set of printer settings comprises at least one setting selected from the group consisting of: a ratio of the two or more input materials to a mixing chamber, a spin speed of an impeller in the mixing chamber, a sequence of materials into a mixing chamber, a position of one or more valves to control material inputs into the mixing chamber, total cumulative flowrate of all inputs to a mixing chamber, vertical position of a print head relative to the substrate, speed of movement of the print head, amount of reverse pumping following a movement command, temperature of the print head, temperature of a substrate onto which the article is printed, and the calibration setting for a material inlet pump.
4. The method of claim 1, wherein the article comprises a gradient structure.
5. The method of claim 1, wherein printing the article comprises mixing at least two fluids with particles.
6. The method of claim 1, wherein printing the article comprises mixing at least three fluids with particles.
7. The method of claim 1, wherein identifying the target material to be printed using the object information comprises identifying a gradient structure using the object information.
8. A method of printing of an article, comprising:
- flowing a first fluid through a first inlet into a nozzle;
- flowing a second fluid through a second inlet into the nozzle;
- flowing particles into the nozzle;
- mixing the first fluid, the second fluid, and the particles to form a first mixture within the nozzle; and
- printing the first mixture onto a substrate from the nozzle.
9. The method of claim 8, comprising printing the first mixture onto the substrate in at least a first portion.
10. The method of claim 8, wherein the particles comprise a blowing agent.
11. The method of claim 8, wherein the mixture of the first fluid and the second fluid cures to form a matrix on the substrate containing the particles.
12. The method of claim 8, wherein the minimum activation temperature of the blowing agent is greater than the maximum temperature in the curing profile of the matrix by at least 10 degrees Celsius.
13. The method of claim 8, wherein the average activation temperature of the blowing agent is less than the curing temperature of the matrix by at least 10 degrees Celsius.
14. The method of claim 8, further comprising:
- flowing the first fluid through the first inlet into the nozzle;
- flowing the second fluid through the second inlet into the nozzle;
- mixing the first fluid and the second fluid to form a second mixture within the nozzle; and
- printing the second mixture onto a substrate from the nozzle in at least a second portion.
15-88. (canceled)
89. A method of printing an article, comprising:
- flowing at least two inputs into a mixing nozzle to form a first mixture comprising a blowing agent;
- flowing at least two inputs into a mixing nozzle to form a second mixture;
- depositing a first region comprising the first mixture to form a first elastomer;
- depositing a second region adjacent to the first region, comprising the second mixture to form a second elastomer; and
- heating at least the first region of the article to a temperature greater than or equal to the activation temperature of the blowing agent;
- wherein heating at least the first region of the article causes differential expansion between the first region and the second region of the article and physical deformation of the article.
90. The method of claim 89, wherein the second mixture comprises a blowing agent.
91. The method of claim 89, wherein one of the at least two inputs to form the first mixture comprises an isocyanate and another of the at least two inputs to form the first mixture comprises a polyol system containing the blowing agent.
92. The method of claim 91, further comprising flowing at least a third input comprising a polyol system into the mixing nozzle to form the first mixture.
93. The method of claim 89, wherein one of the at least two inputs to form the second mixture comprises an isocyanate and another of the at least two inputs to form the second mixture comprises a polyol system.
94. The method of claim 93, further comprising flowing at least a third input comprising a polyol system containing a blowing agent into the mixing nozzle to form the second mixture.
95-102. (canceled)
Type: Application
Filed: Feb 27, 2018
Publication Date: Feb 7, 2019
Applicant: VoxeI8,Inc. (Somerville, MA)
Inventors: Travis Alexander Busbee (Somerville, MA), Avin Dhoble (Waltham, MA), Noah Tremblay (Pepperell, MA), Clara H. Rhee (Somerville, MA), Sean Christopher Troiano (Somerville, MA)
Application Number: 15/907,085