TREATMENT OF THICK FINE TAILINGS INCLUDING CHEMICAL IMMOBILIZATION, POLYMER FLOCCULATION AND DEWATERING
A process for the treatment of thick fine tailings that include constituents of concern (CoCs) and suspended solids is provided. The process includes subjecting the thick fine tailings to treatments including chemical immobilization of the CoCs, polymer flocculation of the suspended solids, and dewatering. The chemical immobilization can include the addition of compounds enabling the insolubilization of the CoCs. Subjecting the thick fine tailings to chemical immobilization and polymer flocculation can facilitate production of a reclamation-ready material, which can enable disposing of the material as part of a permanent aquatic storage structure (PASS).
This application is a U.S. National Stage of International Patent Application No. PCT/CA2017/050227, filed Feb. 23, 2017, which claims priority to foreign Canadian Patent Application No. CA 2,921,835, filed on Feb. 24, 2016, the disclosures of which are incorporated by reference in their entirety.
TECHNICAL FIELDThe technical field generally relates to the treatment of thick fine tailings derived from mining operations, such as oil sands mining.
BACKGROUNDTailings derived from mining operations are often placed in dedicated disposal ponds for settling. The settling of fine solids from the water in tailings ponds can be a relatively slow process and can form a stratum of thick fine tailings.
Certain techniques have been developed for dewatering thick fine tailings. Dewatering of thick fine tailings can include contacting with a flocculant and then depositing the flocculated material onto a sub-aerial deposition area where the deposited material can release water and eventually dry. Other techniques for treating thick fine tailings include addition of gypsum and sand to produce consolidating tailings.
In the context of dewatering thick fine tailings, there are a number of challenges related to processing the material to facilitate efficient reclamation.
SUMMARYSeveral implementations of processes and systems for treating thick fine tailings, which can be used in the context of forming a permanent aquatic storage structure (PASS), are described herein.
In one implementation, there is provided a process for treating mature fine tailings (MFT) derived from oil sands extraction and including constituents of concern (CoC) comprising bitumen, naphthenic acid, arsenic and selenium.
This process includes retrieving MFT from a tailings pond and providing an in-line flow of the MFT. The process further includes adding in-line an aqueous immobilization solution into the in-line flow of MFT and in-line mixing thereof with the MFT, thereby producing a pre-treated tailings flow. The aqueous immobilization solution includes an immobilization chemical selected from multivalent inorganic salts. The pre-treated tailings flow includes immobilized bitumen-clay complexes comprising multivalent cations forming cation bridges between negatively charged bitumen droplets and negatively charged clay particles; insolubilized naphthenic acid; insolubilized arsenic; and insolubilized selenium.
The process further includes adding in-line an aqueous flocculant solution into the pre-treated tailings flow to form a flocculating material; in-line conditioning and transport of the flocculating material to produce a flocculated material in a water release zone; depositing the flocculated material onto a sub-aerial deposition area, allowing release water to separate from a solids-enriched material; and forming a permanent aquatic storage structure (PASS) for retaining the solids-enriched material and a water cap. The forming of the PASS includes forming a consolidating solids-rich lower stratum below the water cap; and retaining the immobilized bitumen-clay complexes, the insolubilized naphthenic acid, the insolubilized arsenic and the insolubilized selenium to inhibit migration of the CoCs into the water cap.
In certain implementations related to in-line addition of an aqueous immobilization solution, the aqueous immobilization solution can be neutral or acidic. In addition, the immobilization chemical can be fully dissolved in the immobilization solution prior to the in-line addition into the in-line flow of MFT. In some implementations, the in-line addition and the in-line mixing of the immobilization chemical into the MFT are performed at concentration and mixing intensity sufficient to substantially inhibit aggregation of multivalent cation hydroxides and promote charge neutralization between the negatively charged bitumen droplets and the negatively charged clay particles. In this regard, it is noted that dosages and mixing can result in the formation of cation hydroxides, although the process and the immobilization effects are not tailored in accordance with such cation hydroxide formation. The process can include the use of dosage and mixing that minimize aggregation of such cation hydroxides such that it generally does not add to the immobilization mechanisms.
The immobilization chemical can include a divalent cation or a trivalent cation. The immobilization chemical can include an aluminum cation, a ferric cation, a calcium cation, or a sulphate anion. Alternatively, immobilization chemical can include or consist of gypsum and/or alum. In certain implementations related to the concentration of the immobilization chemical, the immobilization chemical can be added in a concentration below water saturation thereof. The immobilization chemical can be selected, formulated and/or added in a concentration so as to immobilize substantially all of the bitumen, naphthenic acid, arsenic and selenium present in the MFT, optionally so as to immobilize substantially all of the CoCs present in the MFT and further optionally so as to avoid increasing flocculant dosage more than 20% or more than 10% to achieve a same steady-state deposit clay-to-water ratio (CWR) as an equivalent process excluding addition of an immobilization chemical.
Regarding the process step of in-line addition of the aqueous flocculant solution, the aqueous flocculant solution can include an anionic polymer flocculant, that can be fully dissolved in the aqueous flocculant solution prior to addition to the pre-treated tailings flow. In some implementations, the anionic polymer flocculant includes a sodium-based polymer flocculant or a calcium-based polyacrylamide-polyacrylate co-polymer with high molecular weight.
Regarding the process step of in-line conditioning of the flocculating material, this step can consist of pipeline shearing that is managed to increase a yield strength of the flocculating material to a maximum, and then decrease the yield strength to achieve the water release zone while avoiding overshearing.
Regarding PASS implementations, the process can further include managing the PASS to render the water cap suitable to supporting aquatic life. In some implementations, the managing includes supplying fresh water into the water cap, optionally construction and maintenance of reclamation landforms, optionally comprising shorelines, littoral zones, water inlets and water outlets. The managing can also include monitoring composition of the water cap, and further optionally controlling water levels of the water cap. In addition, the process can include providing an intermediate layer of coke in between the water cap and the solids-rich lower stratum. In other implementations, the deposited solids-enriched material remains in-place after deposition and forms the consolidating solids-rich lower stratum of the PASS. Alternatively, the deposited solids-enriched material is not relocated after deposition.
In another implementation, there is provided a process for treating thick fine tailings that includes CoCs and suspended solids. Optionally, the thick fine tailings include mature fine tailings derived from oil sands extraction. The process includes subjecting the thick fine tailings to chemical immobilization and polymeric flocculation to chemically immobilize the CoCs and polymerically flocculate the suspended solids, to produce treated thick fine tailings; and dewatering the treated thick fine tailings. The dewatering thereby produces an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
Regarding immobilization and flocculation process step, subjecting the thick fine tailings to chemical immobilization and polymeric flocculation can include adding an immobilization chemical to the thick fine tailings to produce a pre-treated tailings; and adding a flocculant into the pre-treated tailings to form a flocculating material. Optionally, the immobilization chemical and the flocculant are added in-line. Further optionally, the immobilization chemical is added as part of an aqueous immobilization solution, and the flocculant is added as part of an aqueous flocculant solution. In some implementations, the chemical immobilization includes insolubilization of dissolved or soluble CoCs, and optionally formation of cation bridges between negatively charged CoCs and negatively charged mineral particles.
Regarding the dewatering process step, the dewatering can include depositing the treated thick fine tailings onto a sloped sub-aerial beach. In some implementations, the dewatering includes depositing the treated thick fine tailings into a pit, such as a mined out pit, which can also be called a mine pit.
In certain implementations of the above process, the latter can further include forming a permanent aquatic storage structure (PASS) for retaining the solids-enriched component. The PASS includes a water cap; and a consolidating solids-rich lower stratum below the water cap and inhibiting migration of the CoCs into the water cap.
In another implementation, there is provided a process for treating thick fine tailings that includes CoCs and suspended solids. The process includes subjecting the thick fine tailings to chemical immobilization to immobilize the CoCs and produce a pre-treated tailings material. The process further includes subjecting the pre-treated tailings material to polymeric flocculation to flocculate the suspended solids and produce a flocculated tailings material; and dewatering the flocculated tailings material. The dewatering thereby produces an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
In another implementation, there is provided a process for treating thick fine tailings that includes CoCs and suspended solids. The process includes subjecting the thick fine tailings to polymeric flocculation to flocculate the suspended solids and produce a flocculated tailings material; and dewatering the flocculated tailings material. The dewatering thereby produces an aqueous component depleted in the suspended solids and including CoCs; and a solids-enriched component comprising the flocculated solids. The process further includes subjecting the aqueous component to chemical immobilization to immobilize the CoCs and produce a contaminant-depleted water stream and a contaminant enriched stream including the immobilized CoCs.
In another implementation, there is provided a process for treating thick fine tailings that includes CoCs and suspended solids. The process includes subjecting the thick fine tailings to polymeric flocculation to flocculate the suspended solids and produce a flocculated tailings material; subjecting the flocculated tailings material to chemical immobilization to immobilize the CoCs; and dewatering the flocculated tailings material. The dewatering produces an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
In another implementation, there is provided a process for treating thick fine tailings that includes CoCs and suspended solids. The process includes simultaneously adding an immobilization chemical and a polymer flocculent into the thick fine tailings, in order to chemically immobilize the CoCs and polymerically flocculate the suspended solids; and dewatering the thick fine tailings. The dewatering thereby produces an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
In another implementation, there is provided a process for treating thick fine tailings that includes CoCs and suspended solids. The process includes adding a polymeric compound to the thick fine tailings. The polymeric compound includes multivalent cation groups effecting chemical immobilization of the CoCs, and organic polymeric groups effecting the polymeric flocculation of the suspended solids. The process further includes dewatering the thick fine tailings to produce an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
In another implementation, there is provided a process for treating thick fine tailings that includes CoCs comprising surfactants and soluble metal, metalloid and/or non-metal compounds. The process includes adding an immobilization chemical into the thick fine tailings in order to immobilize the CoCs and produce a pre-treated tailings. The pre-treated tailings include insolubilized surfactants; and insolubilized metal, metalloid and/or non-metal compounds. The process further includes adding a flocculant into the pre-treated tailings to flocculate suspended solids and form a flocculating material; conditioning the flocculating material to produce a flocculated material; and dewatering the flocculated material. The dewatering produces an aqueous component depleted in the CoCs and suspended solids; and a solids-enriched component comprising the insolubilized surfactants, the insolubilized metal, metalloid and/or non-metal compounds and the flocculated solids.
In another implementation, there is a process for treating thick fine tailings that includes CoCs comprising hydrocarbons, surfactants and soluble metal, metalloid and/or non-metal compounds. The process includes adding an immobilization chemical into the thick fine tailings in order to immobilize the CoCs and produce a pre-treated tailings. The pre-treated tailings include immobilized hydrocarbon-mineral complexes; insolubilized surfactants; and insolubilized metal, metalloid and/or non-metal compounds. The process further includes adding a flocculant into the pre-treated tailings to flocculate suspended solids and form a flocculating material; conditioning the flocculating material to produce a flocculated material; and dewatering the flocculated material. The dewatering produces an aqueous component depleted in the CoCs and suspended solids; and a solids-enriched component comprising the immobilized hydrocarbon-mineral complexes, the insolubilized surfactants, the insolubilized metal, metalloid and/or non-metal compounds and the flocculated solids.
In another implementation, there is a process treating thick fine tailings that includes CoCs and suspended solids. The process includes adding an aluminum sulphate based compound into the thick fine tailings in order to immobilize the CoCs and produce a pre-treated tailings. The aluminum sulphate based compound is added at sufficient dosage and mixing so that aluminum cations form cation bridges between negatively charged immiscible CoCs and negatively charged clay particles, to produce immobilized complexes; and insolubilize dissolved CoCs to form insolubilized CoCs. The process further includes adding an anionic polyacrylamide based flocculant into the pre-treated tailings to flocculate the suspended solids and form a flocculating material; conditioning the flocculating material to produce a flocculated material; and dewatering the flocculated material. The dewatering produces an aqueous component depleted in the CoCs and suspended solids; and a solids-enriched component comprising the immobilized complexes, the insolubilized CoCs, and the flocculated solids.
In another implementation, there is provided a process treating thick fine tailings that includes CoCs and suspended solids. The process includes adding a calcium sulphate based compound into the thick fine tailings in order to immobilize the CoCs and produce a pre-treated tailings. The calcium sulphate based compound is added at sufficient dosage and mixing so that calcium cations form cation bridges between negatively charged immiscible CoCs and negatively charged clay particles, to produce immobilized complexes; and insolubilize dissolved CoCs to form insolubilized CoCs. The process further includes adding an anionic polyacrylamide based flocculant into the pre-treated tailings to flocculate the suspended solids and form a flocculating material; conditioning the flocculating material to produce a flocculated material; and dewatering the flocculated material. The dewatering produces an aqueous component depleted in the CoCs and suspended solids; and a solids-enriched component comprising the immobilized complexes, the insolubilized CoCs, and the flocculated solids.
In another implementation, there is provided a permanent aquatic storage structure (PASS) for storing thick fine tailings. The PASS includes a containment structure defining side walls and a bottom; a water cap within the containment structure; and a solids-rich lower stratum below the water cap. The solids-rich lower stratum includes polymercially flocculated solids and immobilized CoCs.
Regarding layering of the PASS, the solids-rich lower stratum can be formed from discharging thick fine tailings pre-treated by chemical immobilization and polymer flocculation into the containment structure. Optionally, the solids-rich lower stratum is from a deposited pre-treated material and remains in-place after deposition. In some implementations, the PASS includes an intermediate layer in between the water cap and the solids-rich lower stratum. The intermediate layer can be composed of coarse particulate material, such as coke. The coke can be derived from a bitumen processing operation.
In implementations related to the immobilized CoCs, the immobilized CoCs can include immobilized bitumen-clay complexes, insolubilized CoCs (such as insolubilized surfactants and/or insolubilized naphthenic acids, insolubilized arsenic, insolubilized selenium, and/or insolubilized heavy metals) and can further be selected from divalent and trivalent salts, including alum, gypsum or both.
In implementations related to the water cap, the PASS can include a fresh water line for introducing fresh water into the water cap; and/or a recycle water line for removing recycle water from the water cap. The water cap can have a composition suitable to support aquatic life. Optionally, the PASS includes reclamation landforms selected from shorelines and littoral zones, and/or monitoring systems configured form monitoring a composition of the water cap.
In another implementation, there is provided a system for treating thick fine tailings comprising CoCs and suspended solids. The system includes:
-
- a tailings supply pipeline for transporting the thick fine tailings;
- an immobilization addition line in fluid communication with the tailings pipeline for adding an immobilization chemical;
- a polymer flocculant injector in fluid communication with the tailings pipeline for injecting a polymer flocculant to produce a flocculation tailings material;
- a tailings conditioning pipeline in fluid communication with the polymer flocculant injector for transporting and conditioning the flocculation tailings material;
- a deposition outlet for receiving flocculation tailings material and depositing the same onto a sub-aerial deposition area; and
- a containment structure including the sub-aerial deposition area and configured to contain the flocculation tailings material and allow formation of a water cap and a solids-rich lower stratum below the water cap, the solids-rich lower stratum comprising polymercially flocculated solids and chemically immobilized CoCs.
In another implementation, there is provided a process for treating fine tailings that include CoCs that are water mobile and suspended solids. The process includes adding an immobilization chemical to react with the CoCs and enable immobilization of the same; and adding a polymer flocculant to flocculate the suspended solids. The process further includes producing a treated tailings material; and dewatering the treated tailings material. The dewatering produces a water component; and a solids-enriched component including the CoCs rendered water immobile and flocculated solids.
In implementations related to immobilization and flocculation, the immobilization chemical can include a divalent cation and/or a trivalent cation, optionally gypsum and/or alum. The immobilization chemical can be selected to immobilize bitumen by cation bridging with suspended clays, to immobilize naphthenic acids, to immobilize arsenic, and/or to immobilize and selenium. The immobilization chemical and the polymer flocculant can be each added in-line, and further optionally each added dissolved in a corresponding aqueous solution. In addition, the flocculant can include an anionic polymer flocculant, such as a sodium-based or a calcium-based polyacrylamide-polyacrylate co-polymer with high molecular weight.
In implementations related to dewatering, the dewatering can include continuously discharging the treated tailings material into a pit to allow an initial water release from the solids-enriched component; and compressing the solids-enriched component below subsequently deposited treated tailings and/or a water cap.
In certain implementations of the above process, the latter can further include forming a permanent aquatic storage structure (PASS), optionally contained in a mine pit, for retaining the solids-enriched component. The PASS includes a water cap; and a consolidating solids-rich lower stratum below the water cap and inhibiting migration of the CoCs into the water cap. The deposited solids-enriched component can remain in-place after deposition and can form the consolidating solids-rich lower stratum of the PASS.
Optionally, the process also includes managing the PASS to render the water cap suitable to supporting aquatic life. The managing can include supplying fresh water into the water cap; construction and maintenance of reclamation landforms; monitoring composition of the water cap; and/or controlling water levels of the water cap.
Regarding handling of the treated tailings material, the treated tailings material can be discharged so that the initial water release results in an initial clay-to-water ratio (CWR) in the solids-enriched component of at least 0.5, 0.6, 0.65, 0.70, 0.75, 0.80, 0.85, 0.90, 0.95 or 1. The treated tailings material can be discharged sub-aerially, and can be discharged to avoid overshearing flocs in the treated tailings material. Optionally, the treated tailings material is deliberately sheared to improve long term water release from the deposit at the expense of the initial water release, and further optionally to reach a target floc size between about 50 μm and about 200 μm to enhance long term water release. Floc size measurements can be made using various devices and techniques, such as a Focused Beam Reflectance Measurement (FBRM) device.
In another implementation, there is provided a process for treating thick fine tailings. The process includes adding an immobilization chemical to the thick fine tailings to form a pre-treated material; and subjecting the pre-treated material to pipeline shear conditioning to form a conditioned pre-treated material. The pipeline shear conditioning is provided such that the conditioned pre-treated material has target rheological characteristics. The process further includes adding a flocculant to the conditioned pre-treated material to produce a flocculated material; and dewatering the flocculated material.
In certain implementations related to shear conditioning, the pipeline shear conditioning of the process can be performed to modify a yield stress of the pre-treated material from an initial yield stress up to an upper crest yield stress, and then down to a lower yield stress that is in between the initial yield stress and the upper crest yield stress, such that the conditioned pre-treated material has the lower yield stress. Optionally, the pipeline shear conditioning is performed so that the lower yield stress represents a reduction in the yield stress of about 30% to 80% from the upper crest yield stress. Further optionally, the pipeline shear conditioning is performed so that the lower yield stress is at least about 25 Pa lower than the upper crest yield stress, or between about 10 Pa and about 15 Pa. The pipeline shear conditioning can also be performed so that the lower yield stress is on a generally flat plateau of yield stress versus time. In addition, the pipeline shear conditioning can be performed to produce a gel-state pre-treated material having increased yield stress; and then produce the conditioned pre-treated material having an ungelled state and a decreased yield stress compared to the gel-state pre-treated material. Optionally, the pipeline shear conditioning is performed such that the conditioned pre-treated material has a turbulent flow regime upon addition of the flocculant thereto. Further optionally, the pipeline shear conditioning is controlled according to shear intensity, shear duration and/or total shear energy imparted to the pre-treated material.
In certain implementations related to immobilization, adding the immobilization chemical to the thick fine tailings can be performed in-line via a pipe junction. The immobilization chemical and the thick fine tailings can be supplied through a static mixer to form the pre-treated material; and the pre-treated material can be supplied through a conditioning pipeline in order to impart all of the pipeline shear conditioning to the pre-treated material prior to addition of the flocculant. Optionally, the immobilization chemical includes alum, gypsum, or ferric sulphate.
In another implementation, there is provided a process for treating thick fine tailings. The process includes adding an acidic solution comprising an immobilization chemical to the thick fine tailings having an initial tailing pH to form a pre-treated material having a reduced pH; and subjecting the pre-treated material to pipeline shear conditioning to form a conditioned pre-treated material. The pipeline shear conditioning is provided such that the conditioned pre-treated material has at least a target pH that is greater than the reduced pH. The process further includes adding a flocculant to the conditioned pre-treated material to produce a flocculated material; and dewatering the flocculated material.
In some implementations of the process, adding the acidic solution to the thick fine tailings is performed in-line via a pipe junction; the immobilization chemical and the thick fine tailings are supplied through a static mixer to form the pre-treated material; the pre-treated material is supplied through a conditioning pipeline in order to impart all of the pipeline shear conditioning to the pre-treated material prior to addition of the flocculant.
In certain implementations related to shearing, the pipeline shear conditioning can be performed such that the target pH is at least 7.5 or at least 8. Optionally, the pipeline shear conditioning is performed such that the target pH is at least 15%, at least 25%, at least 50%, at least 75%, or higher, above a lowest pH obtained for the pre-treated material after addition of the acidic solution. The pipeline shear conditioning can also be performed such that the target pH within 10% of the initial tailings pH. The pipeline shear conditioning can further be performed to achieve the target pH that is based on optimal activity of the flocculant.
In certain implementations related to immobilization, the acidic solution includes sulphuric acid. The immobilization chemical can include alum, gypsum, or ferric sulphate. The immobilization chemical can be completely dissolved in the acidic solution prior to addition to the thick fine tailings.
In another implementation, there is provided a process for treating thick fine tailings. The process includes adding an immobilization chemical to the thick fine tailings and supplying the same to a mixer to form a pre-treated material. The immobilization chemical dosage is determined based on the mixer and density characteristics of the thick fine tailings. The process further includes subjecting the pre-treated material to pipeline shear conditioning to form a conditioned pre-treated material. The process also includes adding a flocculant to the conditioned pre-treated material to produce a flocculated material; and dewatering the flocculated material.
In certain implementations of the above process, the immobilization chemical is added to the thick fine tailings via a pipe junction, optionally a T junction, and the mixer is a static mixer located downstream and proximate to the pipe junction. The density characteristics of the thick fine tailings can be measured on-line prior to adding the immobilization chemical, and on-line density measurements are used to control the immobilization chemical dosage.
In another implementation, there is provided a process for treating thick fine tailings. The process includes adding an immobilization chemical to the thick fine tailings to form a pre-treated material; and subjecting the pre-treated material to shear conditioning to form a conditioned pre-treated material. The process further includes adding a flocculant to the conditioned pre-treated material to produce a flocculating material; and subjecting the flocculating material to shear conditioning to increase floc size up to an upper level and to then break down the flocs and decrease floc size to within a target floc size range, thereby forming a conditioned flocculated material. The process also includes discharging the conditioned flocculated material into a pit to enable settling and consolidation of the flocs and separation of water to form an upper water cap, thereby forming a permanent aquatic storage structure (PASS).
In some implementations of the above process, the target floc size range is pre-determined based on a minimum settling rate and a maximum settled volume within the PASS. Optionally, the target floc size range is between about 50 microns and about 200 microns. Further optionally, the target floc size range is sufficient to provide a minimum settling rate to achieve a clay-to-water ratio (CWR) greater than 0.65 within one year within the PASS; or the target floc size range is tailored to a starting CWR of the thick fine tailings to achieve the CWR greater than 0.65 within one year within the PASS.
In certain implementations related to shearing, subjecting the flocculating material to the shear conditioning can consist of pipeline shear conditioning, optionally pipe shear conditioning the flocculating material in a conditioning pipeline to form the conditioned flocculated material. Discharging of the conditioned flocculated material into the pit can be performed immediately after exiting the conditioning pipeline.
In certain implementations related to conveyance, the process further includes conveying the conditioned flocculated material from the conditioning pipeline to a discharge location. The conveying can be performed via a conveyance pipeline fluidly coupled to a downstream end of the conditioning pipeline. The conveyance pipeline can be located on a sloped side of the pit, and/or can be configured and operated such that the conditioned flocculated material flows therethrough under a non-turbulent flow regime. Alternatively, the conveyance pipeline can be configured and operated such that the conditioned flocculated material flows therethrough under a laminar flow regime. In addition, the conveying can be performed at shear conditions that are sufficiently low to substantially maintain flocs size within the target floc size range.
In another implementation, there is provided a process for treating thick fine tailings. The process includes adding an immobilization chemical to the thick fine tailings to form a pre-treated material; and subjecting the pre-treated material to shear conditioning to form a conditioned pre-treated material. The process also includes adding a flocculant to the conditioned pre-treated material to produce a flocculating material; and subjecting the flocculating material to shear conditioning to form a conditioned flocculated material. The process further includes conveying the conditioned flocculated material to a discharge location under a non-turbulent flow conditions and under shear rate and energy conditions that are lower than those of the shear conditioning used to form the conditioned flocculated material. The process then includes discharging the conditioned flocculated material at the discharge location into a pit to enable settling and consolidation of the flocs and separation of water to form an upper water cap, thereby forming a permanent aquatic storage structure (PASS).
In certain implementations related to shearing, subjecting the flocculating material to shear conditioning is performed in a conditioning pipeline to increase the yield stress of the flocculating material to an upper crest and then decrease the yield stress and enter a water release zone where water releases from flocs.
In certain implementations related to conveyance, the conveying is performed via a conveyance pipeline fluidly coupled to a downstream end of the conditioning pipeline. The conveyance pipeline can be located on a sloped side of the pit; and/or can be configured and operated such that the conditioned flocculated material flows therethrough under a laminar flow regime. The conveying can be performed at shear conditions that are sufficiently low to substantially maintain flocs size unchanged. The conveyance pipeline can have a pipe diameter greater than that of the conditioning pipeline, and can be operated such that a flow rate therethrough is lower than that of the conditioning pipeline. Optionally, the conveyance pipeline comprises multiple conveyance pipe sections arranged in parallel and in fluid communication with the conditioning pipeline. The multiple conveyance pipe sections can supply respective discharge units that are positioned for discharging the conditioning flocculated material at different locations in the pit. Optionally, the process can further include relocating the conveyance pipeline as fluid rises within the pit.
In certain implementations related to immobilization and flocculation, the steps of adding the immobilization chemical to the thick fine tailings, subjecting the pre-treated material to shear conditioning, adding the flocculant to the conditioned pre-treated material, and subjecting the flocculating material to shear conditioning are all performed at locations spaced away from the pit. Alternatively, these same steps can be all performed by equipment that is not relocated.
In another implementation, there is provided a process for treating thick fine tailings. The process includes adding an immobilization chemical to the thick fine tailings to form a pre-treated material, the immobilization chemical comprising a ferric cation; and subjecting the pre-treated material to shear conditioning to form a conditioned pre-treated material. The process also includes adding a flocculant to the conditioned pre-treated material to produce a flocculated material; and discharging the conditioned flocculated material into a pit to enable settling and consolidation of the flocs and separation of water to form an upper water cap, thereby forming a permanent aquatic storage structure (PASS). Optionally, the immobilization chemical includes ferric sulphate.
In another implementation, there is provided a process for treating thick fine tailings that includes constituents of concern (CoCs) and suspended solids. The process includes subjecting the thick fine tailings to chemical immobilization and polymeric flocculation to chemically immobilize the CoCs and polymerically flocculate the suspended solids, to produce treated thick fine tailings. The chemical immobilization includes the addition of ferric sulphate. The process further includes dewatering the treated thick fine tailings to produce an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
In another implementation, there is provided a process for treating mature fine tailings (MFT) derived from oil sands extraction and including constituents of concern (CoCs) comprising bitumen, naphthenic acid, arsenic and selenium. The process includes retrieving MFT from a tailings pond; providing an in-line flow of the MFT; adding in-line an aqueous immobilization solution into the in-line flow of MFT and in-line mixing therewith, thereby producing a pre-treated tailings flow. The aqueous immobilization solution includes an immobilization chemical comprising ferric sulphate. The pre-treated tailings flow includes immobilized bitumen-clay complexes comprising ferric cations forming cation bridges between negatively charged bitumen droplets and negatively charged clay particles; insolubilized naphthenic acid; insolubilized arsenic; and insolubilized selenium. The process further includes adding in-line an aqueous flocculant solution into the pre-treated tailings flow to form a flocculating material; and in-line conditioning of the flocculating material to produce a flocculated material in a water release zone. The process also includes discharging the flocculated material into a pit and allowing release water to separate from a solids-enriched material. The process additionally includes forming a permanent aquatic storage structure (PASS) in the pit for retaining the solids-enriched material and a water cap. The solids-enriched material forms a consolidating solids-rich lower stratum below the water cap; and retains the immobilized bitumen-clay complexes, the insolubilized naphthenic acid, the insolubilized arsenic and the insolubilized selenium to inhibit migration of the CoCs into the water cap.
The techniques described herein relate to the treatment of thick fine tailings that include constituents of concern (CoCs) and suspended solids. The thick fine tailings can be subjected to treatments including chemical immobilization of the CoCs, polymer flocculation of the suspended solids, and dewatering.
The long-term result of treating the tailings can be a permanent aquatic storage structure (PASS) that includes a water cap suitable for supporting aquatic life and recreational activities. Techniques are described to facilitate the deposition of treated thick fine tailings at a deposition site that over time becomes the PASS. In some implementations, the solids separated from water during the dewatering of the thick fine tailings do not need to be relocated, e.g., from a drying area, as can be the case for other known techniques for dewatering thick fine tailings. Rather, the solids remain in place and form the basis of a sedimentary layer of solids at the bottom of the PASS. Previous techniques for treating tailings are known to use polymer flocculation for dewatering a stream of thick fine tailings. However, the PASS technique additionally provides for treating the thick fine tailings to provide chemical immobilization of CoCs that would otherwise remain in or transfer into the water, such that the water layer that inherently forms over the solid, sedimentary layer has CoCs removed allowing for the water cap to be of such a quality it can support aquatic life. Although the size of a PASS can vary, in some implementations the PASS can contain a volume of 100,000,000 to 300,000,000 cubic metres and can be approximately 100 metres deep at its greatest depth. With a PASS of this scale, flocculated material from the treated thick fine tailings can be directly deposited onto a sub-aerial deposition area that is proximate and/or forms part of the PASS footprint. Within a relatively short period of time following closure of a mine that is feeding treated thick fine tailings into the PASS, e.g., 10 years, reclamation of the tailings is complete. That is, the solids are contained in the base of the PASS and CoCs are immobilized within the solid layer. The water cap is of a quality to support aquatic life and recreational activities.
For example, in the context of oil sands mature fine tailings (MFT) that include CoCs such as dissolved metals, metalloids and/or non-metals, naphthenic acids and bitumen, the chemical immobilization can include the addition of compounds enabling the insolubilization of the metals, metalloids and/or non-metals, as well as naphthenic acids, in addition to chemical bridging of bitumen droplets with suspended clays. The MFT can also be subjected to polymer flocculation, which can include the addition of a polymer flocculant solution followed by pipeline conditioning. The MFT that has been subjected to immobilization and flocculation can then be dewatered. The dewatering can be performed by supplying the flocculated tailings material to a dewatering device and/or a sub-aerial deposition site. While MFT derived from oil sands extraction operations will be discussed and referred to in herein, it should be noted that various other contaminant-containing tailings and slurry streams can be treated using techniques described herein.
It should be noted that the term “constituents” in the expression “constituents-of-concern” (CoC) can be considered to include or correspond to substances that are considered as “contaminants” by certain institutions, regulatory bodies, or other organizations, which can vary by jurisdiction and by evaluation criteria.
In some implementations, subjecting the thick fine tailings to chemical immobilization and polymer flocculation facilitates production of a reclamation-ready material, which can enable disposing of the material as part of a permanent aquatic storage structure (PASS).
Tailings are left over material derived from a mining extraction process. Many different types of tailings can be treated using one or more of the techniques described herein. In some implementations, the techniques described herein can be used for “thick fine tailings”, where thick fine tailings mainly include water and fines. The fines are small solid particulates having various sizes up to about 44 microns. The thick fine tailings have a solids content with a fines portion sufficiently high such that the fines tend to remain in suspension in the water and the material has slow consolidation rates. More particularly, the thick fine tailings can have a ratio of coarse particles to the fines that is less than or equal to one. The thick fine tailings have a fines content sufficiently high such that polymer flocculation of the fines and conditioning of the flocculated material can achieve a two-phase material where release water can flow through and away from the flocs. For example, thick fine tailings can have a solids content between 10 wt % and 45 wt %, and a fines content of at least 50 wt % on a total solids basis, giving the material a relatively low sand or coarse solids content. The thick fine tailings can be retrieved from a tailings pond, for example, and can include what is commonly referred to as “mature fine tailings” (MFT).
MFT refers to a tailings fluid that typically forms as a layer in a tailings pond and contains water and an elevated content of fine solids that display relatively slow settling rates. For example, when whole tailings (which include coarse solid material, fine solids, and water) or thin fine tailings (which include a relatively low content of fine solids and a high water content) are supplied to a tailings pond, the tailings separate by gravity into different layers over time. The bottom layer is predominantly coarse material, such as sand, and the top layer is predominantly water. The middle layer is relatively sand depleted, but still has a fair amount of fine solids suspended in the aqueous phase. This middle layer is often referred to as MFT. MFT can be formed from various different types of mine tailings that are derived from the processing of different types of mined ore. While the formation of MFT typically takes a fair amount of time (e.g., between 1 and 3 years under gravity settling conditions in the pond) when derived from certain whole tailings supplied from an extraction operation, it should be noted that MFT and MFT-like materials can be formed more rapidly depending on the composition and post-extraction processing of the tailings, which can include thickening or other separation steps that can remove a certain amount of coarse solids and/or water prior to supplying the processed tailings to the tailings pond.
In one implementation, the thick fine tailings are first subjected to chemical immobilization, followed by polymer flocculation, and then dewatering to produce a solids-enriched tailings material in which CoCs are immobilized. CoCs can sometimes be referred to as contaminants in the sense that the presence of certain constituents can be undesirable for various reasons at certain concentrations, within certain matrices, and/or in certain chemical forms. Various tailings treatments including chemical immobilization, polymer flocculation and dewatering, are described in further detail below.
Chemical ImmobilizationThick fine tailings can include a number of CoCs depending on the nature of the mined ore and processing techniques used to extract valuable compounds from the ore. Thick fine tailings can include dissolved CoCs, dispersed CoCs that are immiscible in water, as well as fine suspended solids.
For example, thick fine tailings derived from oil sands mining can include metals (e.g., heavy metals), polyatomic non-metals (e.g., selenium), metalloids (e.g., arsenic), surfactants (e.g., naphthenic acids), residual bitumen, as well as other CoCs. The CoCs can exist in various forms and as part of various compounds in the tailings material. In order to reclaim the thick fine tailings, the CoCs can be treated so that the eventual landform that includes the treated tailings meets regulatory requirements.
In some implementations, a process for treating thick fine tailings includes immobilization of bitumen; removal of toxicity due to surfactants, metals, non-metals and/or metalloids; and polymer flocculation of the slurry material to reduce hydraulic conductivity of the resultant treated fine tailings landform.
In some implementations, the thick fine tailings can be treated with an immobilization chemical, which can include multivalent cations (e.g., trivalent or divalent). The multivalent cation can be added as part of an inorganic salt. The multivalent salts can be added to the thick fine tailings pre-dissolved in an aqueous solution, which can be acidic or neutral for example. Various multivalent inorganic salts can be used as immobilization chemicals. For example, aluminum sulphate (e.g., in acid solution which can be sulfuric acid), aluminum potassium sulphate, iron sulphate, or chloride or hydrated calcium sulphate (gypsum) can be used for chemical immobilization of certain CoCs. For example, the trivalent cation Fe3+ can be added as part of iron (III) sulphate Fe2(SO4)3. Addition of ferric sulphate to the thick fine tailings can provide certain advantages, such as lower potential H2S emissions.
The multivalent cation added to thick fine tailings can perform various functions. One function is that the multivalent cation can form a cation bridge between negatively charged bitumen droplets and negatively charged clay particles in the fine tailings. This bitumen droplet bridging can help immobilize the bitumen within the solids-enriched material that is formed after dewatering of the treated tailings. Chemical bridging of bitumen droplets with clays can decrease the potential for gas bubbles to adsorb onto bitumen and migrate out of the solids-enriched material; or chemical bridging of bitumen droplets with clays can increase the density and viscosity of the bitumen droplet and prevent upward migration in the deposit through buoyancy effects as the deposit densifies. Thus, the bitumen can remain immobilized within the solid material and thus inhibiting its migration into adjacent water regions.
Another function of the multivalent inorganic salt is to insolubilize certain CoCs present in the thick fine tailings. For instance, surfactants, metals, non-metals, metalloids and other compounds can be present in soluble form in the water of the fine tailings material. In thick fine tailings derived from oil sands, surfactants such as naphthenic acids are considered CoCs in terms of water toxicity. In addition, compounds such as selenium and arsenic can also be present and subject to certain regulatory requirements. The addition of the multivalent inorganic salt enables such dissolved CoCs to be precipitated and to remain insolubilized so that the CoCs cannot re-solubilize. Insolubilization decreases the risk of the CoCs migrating out of the solid material or entering the water column.
In some implementations, chemical immobilization is performed with addition of a coagulant that destabilizes particles in the thick fine tailings through double-layer compression and modifies the pore water chemistry. In this sense, the immobilization chemical can include or be a coagulant for coagulating CoCs from the thick fine tailings to form coagulated CoCs. The coagulant can include a multivalent inorganic salt as described above and can include other various conventional coagulant species. Chemical immobilization by addition of the coagulant to the thick fine tailings can be performed before, during or after flocculation as will be further described in relation to
Certain chemicals referred to herein can be known as coagulants in the field of water treatment and can therefore can be referred to as “coagulants” in the present application. However, it should be noted that such chemicals are used herein for the purpose of immobilization in PASS techniques rather than mere coagulation as would be understood in the water treatment industry, for example. In this sense, the terms “coagulant” and “immobilization chemical” can be used interchangeably as long as the coagulant performs the function of immobilization as described in the present application. It should still be noted that certain immobilization chemicals described herein can or can not perform the function of coagulation. In some implementations, the so-called coagulant is added to the fine tailings in quantities superior to what is known in the water treatment industry for coagulation, e.g., superior to 350 ppm, which is used for purpose of mere coagulation rather than immobilization. It is noted that in many cases the immobilization chemical that is added will in effect cause some or substantial coagulation. It is also noted that immobilization chemicals that generally do not cause coagulation can be used in conjunction with a separate coagulant chemical that provides coagulation effects.
Immobilization Chemical Addition and Mixing into Thick Fine Tailings
When the immobilization chemical is added upstream prior to flocculation, certain features of the immobilization chemical injection and the subsequent mixing can be provided for enhancing the pre-treatment (e.g., pre-coagulation) prior to flocculation. For example, the immobilization chemical injector, subsequent mixers, as well as pipeline length and diameter leading up to the flocculant injector can be designed and provided to ensure a desired immobilization chemical mixing and coagulation time to facilitate benefits of pre-coagulation. In some scenarios, the immobilization chemical injector can be an in-line addition unit, such as a T or Y pipe junction, and at least one static mixer can be provided downstream of the immobilization chemical injector. It should nevertheless be noted that the immobilization chemical injector can take other forms and have alternative constructions for adding the immobilization chemical. For example, the immobilization chemical injector can be configured for injecting an immobilization chemical solution that includes immobilization chemical species in solution (e.g., in an aqueous acid-containing solution), and can thus be adapted for liquid-phase injection of the immobilization chemical solution into an in-line flow of the thick fine tailings. Alternatively, certain immobilization chemicals can be added in dry form (e.g., powders) and the immobilization chemical addition unit can in such cases be designed for dry addition. The immobilization chemical addition unit can include an in-line dynamic mixer (e.g., paddle mixer type) or other types of mixer units.
In some implementations, immobilization chemical dosage can be determined based on various factors, including properties of the thick fine tailings and the configuration of the immobilization chemical addition unit and subsequent mixer devices that can be present. For example, in some implementations, the immobilization chemical can be added as an immobilization chemical solution by in-line addition into the in-line flow of the thick fine tailings followed immediately by a mixer, such as a static mixer. Immobilization chemical dosage can be determined and provided based on the solids content and/or density of the thick fine tailings as well as the given mixer design (e.g., number and type of static mixers). For example, the mixer effects can be pre-determined in terms of the shear imparted to the immobilization chemical-tailings mixture, which can depend on thick fine tailings properties and other operating parameters, such as flow rate and temperature of the fluid.
Immobilization chemical dosage determination can take various forms. For example, given a particular thick fine tailings density and a given mixer design, a range of effective immobilization chemical dosages can be determined along with an optimal immobilization chemical dose. Such determinations can be based in laboratory experiments (e.g., using batch mixers units, such as stirred vessels) and/or small scale pilot experiments (e.g., small continuous in-line addition and mixing units). In addition, immobilization chemical dispersion targets for dispersing the immobilization chemical upon addition into the thick fine tailings can be determined and used to provide an appropriate pipe length and diameter leading up to the immobilization chemical injector to ensure turbulent flow of the tailings at the immobilization chemical injector. For example, target dispersion shear rates can be tested on laboratory and/or small-scale units, and the pipeline leading to the immobilization chemical injector as well as the operating conditions (e.g., flow rate) for larger scale operations can be determined accordingly. For example, should a certain Reynolds Number (Re) of the thick fine tailings flow be targeted for immobilization chemical addition, the pipeline diameter and flow rate can be provided to ensure a minimum turbulence level based on density and viscosity of the thick fine tailings to be treated. Once the system is operational and the pipeline diameter is fixed, the minimum turbulence level can be achieved by controlling certain operating variables, such as flow rate (e.g., regulated by an upstream pump) and potentially the density and/or viscosity of the thick fine tailings (e.g., regulated by dilution or heating).
In some scenarios, immobilization chemical dosage and dispersion requirements can be determined in part or primarily based on thick fine tailings density and a given mixer design. It should also be noted that other methods can be used to design the system for immobilization chemical addition, dispersion and subsequent transportation to the flocculation step. In some implementations, the flow regime of the thick fine tailings is turbulent at the immobilization chemical addition point and a static mixer is provided just downstream of the immobilization chemical addition point to produce a thoroughly mixed coagulating material (which can also be referred to as a pre-treated material in general as coagulation can or cannot be present), which is then transported via pipeline toward the flocculation step.
Pipeline design, flow rate control and determining properties of the thick fine tailings can be used to achieve a first turbulent flow regime at the immobilization chemical addition point, while mixer design downstream of the immobilization chemical addition point can be used to achieve a second turbulent flow regime at that point in the process. The first and second turbulent flow regimes can have different minimum target thresholds or target ranges.
It should also be noted that a single immobilization chemical addition point or multiple immobilization chemical addition points can be used. Each immobilization chemical addition point can have a subsequent mixer arrangement, and the dosage at each addition point can be determined based on the properties of the incoming tailing stream as well as the downstream mixer design.
Pipelining Pre-Treated Thick Fine Tailings to FlocculationAfter addition of the immobilization chemical, a series of kinetics-limiting reactions occurs between the immobilization chemical and components of the thick fine tailings. In some implementations, these reactions result in pH and rheology changes in the coagulating thick fine tailings (which can also be referred to as the pre-treated TFT) during pipeline transportation. It should be noted that the changes in pH and rheology can further affect the subsequent process steps, in particular the flocculation stage. Impacts of the mixing intensity on pH and rheology are further discussed below and also described in the experimentation section.
In terms of pH, when the immobilization chemical is a basic compound that is added as part of an acid-containing solution (e.g., alum in a sulfuric acid solution), the pH of the resulting immobilization chemical-tailings mixture can show an initial decrease followed by an increase as the mixture buffers back to a higher pH.
In some implementations, the pipeline that transports the coagulating material to flocculation can be configured and operated to impart at least a target pipe-mixing level to the coagulating material prior to flocculation. For example, the pipeline can be provided with sufficient length and diameter to impart pipe-shear mixing so that the pH of the material has bounced back to a minimum target value or within a target range. The target pH bounce-back value can be, for example, the initial pH of the thick fine tailings or a desired pH based on optimal activity of the flocculant. In some scenarios, the target pH bounce-back value can be between 7.5 and 8.5. The target pH bounce-back value can also be based on the lowest pH that is obtained, e.g., a pH increase of 5%, 10%, 15%, 20%, 25%, 35%, 45%, 55%, 65%, 75%, 85%, 95% or higher based on the lowest pH value that is obtained from the initial decrease after immobilization chemical addition.
In addition, the pipeline transporting the coagulating material can be configured in terms of mixing intensity and/or total mixing energy imparted to the material. For example, higher mixing intensities can result in a more rapid pH decrease followed by a more rapid pH increase (see
Furthermore, properties of the thick fine tailings (e.g., CWR) can also be measured and used to configure the pipeline transporting the coagulating material. As can be seen in
In some implementations, when the coagulating material is subjected to pipeline transportation and pipe-shear based mixing certain rheological changes can occur. For example, pipeline mixing can be performed for a sufficient time and under shear conditions that cause the coagulating material to reach a post gel-stage state, which can reduce polymer flocculant dosage in the subsequent step. More particularly, the pipeline mixing can be conducted to cause the coagulating material to increase in yield strength and reach a generally gel-like state having gel-like properties, and then the pipeline mixing can be continued so that this gel-like material returns to an ungelled state having slurry-like fluid properties. In this manner, the pipeline mixing can be conducted to ensure adequate progression of the coagulation/immobilization reactions between the immobilization chemical and components of the thick fine tailings while avoiding the difficulties that would occur if the flocculant were mixed with a gelled, high yield strength material. In this regard, it should be noted that gel-like materials have higher yield strength and would be more difficult to mix with the flocculant. Therefore, adding the flocculant to the coagulated slurry after the gel-like material has been “broken” and the yield strength has decreased significantly, can facilitate rapid and thorough mixing of the flocculant and reduced flocculant dosage requirements. Imparting sufficient pipeline shear energy to the coagulating material can be done to achieve such a post gel-stage material prior to flocculation. Shear intensity and duration as well as total mixing energy can be assessed in order to provide a pipeline configuration and operating conditions (e.g., pipeline diameter and length, flow rates, etc.) which can also be based on properties of the material (e.g., density, CWR, viscosity, yield strength, etc.).
In some implementations, the pipeline mixing of the coagulating material can also be provided to ensure a turbulent flow regime or a target turbulence level of the coagulated slurry at the flocculant addition point. The coagulating material can thus have different flow regime properties along the pipeline due to its changing properties. The pipeline diameter and length as well as the flow rate can be provided such that the thick fine tailings have turbulent flow regimes at the immobilization chemical addition point and at the flocculant addition point while the flow regime of the coagulating material at certain points in between these two addition points can be non-turbulent or laminar. In order to provide such flow regime properties, a number of factors can be manipulated including flow rates, pipe sizes (length and diameters), immobilization chemical mixer type and operation, immobilization chemical dosage, and incoming thick fine tailings properties (e.g., viscosity or density, which can be manipulated by pre-dilution, for example).
It should be noted that different flow regimes can be used upon injection of the immobilization chemical and/or flocculant depending on the mixing requirements of the corresponding injected chemical at the initial mixing state. Laminar flow regime can be therefore used for initial mixing upon injection of certain chemicals.
In an in-line system, it should be noted that timing of the flocculant injection is related to the distance between the immobilization chemical and flocculant injection points. The distance between those injection points can also be characterized by the mixing of the pre-treated fine tailings between the immobilization chemical and flocculant injection points, in terms of intensity and time. Thus, mixing time and mixing distance can both be used to assess the impact of mixing on the coagulating material and the flocculant addition point. As mentioned above, the immobilization chemical pipeline mixing and the flocculant injection point can be provided such that the flocculant is added once the coagulated material has left a gel-stage and/or experienced pH bounce back. In another example, injecting the polymer flocculant downstream of the immobilization chemical injection point such that pipeline mixing is within a critical mixing range can facilitate enhanced flocculation. Critical mixing ranges can be determined for open-pipe configurations by using various empirical and/or computational methods. In addition, in dynamic paddle mixers it has been found that the optimum polymer flocculant dosage decreases as the critical mixing constant (Kc) increases (e.g., (Kc) of 20 to 12,000). Kc values determined for batch or in-line stirred tank impeller vessels may be used to help predict critical mixing ranges for in-line open-pipe operations, and Camp Number-based scaling methods can be used.
In some implementations, pre-shearing is performed to enhance uniform shearing within the coagulated tailings before injection of the flocculant. In addition, one or more in-line high-shear static mixer(s) (or other in-line shear devices) can be used to enhance or ensure mixing of the core of the coagulated tailings within the pipe to further reduce the yield stress within the pipe.
In some implementations, the coagulating material is subjected to sufficient mixing (e.g., pipeline shear mixing) to reach a generally stable yield stress plateau after descending from a crest in terms of its yield stress properties.
It should be noted that certain polymer flocculants can be sensitive to pH and rheology variation. Consequently, both polymer flocculant consumption and deposit performance can be impacted by the polymer flocculant injection location downstream of the immobilization chemical injection location. In some implementations, timing of the flocculant injection can be enhanced based on properties including yield strength and/or pH of the pre-treated thick fine tailings that is subjected to flocculation. Certain enhancement techniques and details related thereto will also be discussed in the experimentation section. It should also be noted that the pipeline transporting the coagulating material can have various arrangements, including a single pipeline composed of a series of pipe sections or a pipeline network that includes a splitter leading into multiple parallel pipelines that can rejoined into a single pipeline prior to flocculation. Such pipeline networks can be configured to increase pipeline shear imparted to the material, and can also be controlled and operated to impart different levels of shear to the material when desired. It is also noted that the pipeline can include one or more shear devices (e.g., static mixer) arranged along its length to impart part of the desired shear to the material, and such shear devices and pipeline can be arranged so that the material can either pass through or bypass the shear devices.
Thus, various pipeline configurations can be provided in order to produce a pre-treated coagulated material that is ready for flocculation. For example, mixing intensity, mixing time, pipeline length and diameter, immobilization chemical dosage, yield stress of the material, and flow rate are relevant interconnected factors that can be managed to produce the pre-treated coagulated material having target pH, yield stress and flow regime characteristics at the flocculation point. For in-line systems that include a simple pipeline from the immobilization chemical mixer to the flocculant injector, pipeline length and diameter can be designed in view of flow rate and tailings properties (notably density) in order to impart pipe shear energy in an intensity and over a time period that enable the target pH, yield stress and flow regime characteristics.
This pipeline can have a single diameter along most or all of its length, or it can have different diameters at particular locations along its length to achieve desired effects at certain locations. For example, the pipeline can include a pipe section proximate the immobilization chemical addition point with a first, relatively small diameter to impart higher shear rates (i.e., higher shear intensity) to cause a sharp pH reduction and/or a sharp yield stress increase at that upstream location. The pipeline can also include a subsequent intermediate pipe section that has a second, larger diameter and a pipe length that provide a desired shear energy and residence time for the coagulating material. This intermediate pipe section can be configured to impart a desired mixing energy and intensity to achieve the desired pH and yield stress characteristics, but is not necessarily concerned in a direct manner with turbulence or flow regime. Next, the pipeline can include a downstream pipe section that feeds into the flocculant injector, and this downstream pipe section can have a third, smaller diameter to ensure turbulence as the material contacts the flocculant. This downstream pipe section could be relatively short in length as it simply has to ramp up the turbulence of the material to a desired level prior to flocculant addition and is not necessarily designed for imparting a given amount of energy for the pH or yield stress evolution. Various other pipeline configurations are also possible for achieving desired pH, yield stress and flow regime characteristics. For example, alternatively, pipe section can be increased to ensure laminar flow.
FlocculationA polymer flocculant can be added to the fine tailings in order to flocculate suspended solids and facilitate separation of the water from the flocculated solids. The polymer flocculant can be selected for the given type of fine tailings to be treated and also based on other criteria. In the case of oil sands MFT, the polymer flocculant can be a medium charge (e.g., 30%) high molecular weight anionic polymer. The polymer flocculant can be a polyacrylamide-based polymer, such as a polyacrylamide-polyacrylate co-polymer. The polymer flocculant can have various structural and functional features, such as a branched structure, shear-resilience, water-release responsiveness to fast-slow mixing, and so on.
It should be noted that polymer flocculant is not limited to a medium charge, as altering the pH can influence the charge requirements. In some implementations, the polymer flocculant charge is selected in accordance with pH.
In some implementations, the overall flocculation and dewatering operations can include various techniques described in Canadian patent application No. 2,701,317; Canadian patent application No. 2,820,259; Canadian patent application No. 2,820,324; Canadian patent application No. 2,820,660; Canadian patent application No. 2,820,252; Canadian patent application No. 2,820,267; Canadian patent application No. 2,772,053; and/or Canadian patent application No. 2,705,055. Such techniques—including those related to flocculant selection; rapid dispersion; pipeline flocculation and water-release condoning; Camp Number-based design and operation; injector design and operation; sub-aerial deposition and handling; pre-shearing; pre-thinning; and pre-screening—can be used or adapted for use with techniques described herein related to chemical immobilization, polymer flocculation and dewatering. The above documents are incorporated herein by reference. It should also be noted that various techniques described in such documents can be adapted when included with techniques described in the present application, such as chemical immobilization and coagulation as well as post-flocculation handling, discharging and management.
In some implementations, the polymer flocculant is added as part of an aqueous solution. Alternatively, the polymer flocculant can be added as a powder, a dispersion, an emulsion, or an inverse emulsion. Introducing the polymer flocculant as part of a liquid stream can facilitate rapid dispersion and mixing of the flocculant into the thick fine tailings.
In some implementations, the polymer flocculant can be injected into the pre-treated thick fine tailings using a polymer flocculant injector. For example, static injectors and/or dynamic injectors can be used to perform flocculant addition. The injection can be performed in-line, that is, into the pipeline for example. A length of the pipeline downstream of the flocculant injection point can be dedicated to dispersion of the polymer flocculent into the pre-treated thick fine tailings, thereby producing treated thick fine tailings that is ready for conditioning and eventual dewatering.
As mentioned further above, the incoming pre-treated thick fine tailings that has been subjected to coagulation can arrive at the flocculant injector with certain pH, yield stress, and flow regime characteristics that facilitate flocculant dispersion, mixing and reaction with suspended solids.
Immediately after flocculant injection (e.g., via a co-annular injector where flocculant inlets are spaced away from the pipe side wall and are distributed around an annular ring through which the pre-treated tailings flow), there can be a dispersion pipe section that receives the flocculating material and imparts pipe shear energy to the material. The dispersion pipe length as well as polymer flocculant dosage can be provided based on various factors, which can include the density and/or clay content of the thick fine tailings as well as the flocculant injector design. In some scenarios, for a given injector design and density of the thick fine tailings, optimum ranges of polymer flocculant dosage and dispersion pipe length can be determined, particularly when the target pH, yield stress, and flow regime characteristics have been provided. More regarding process modelling will be discussed in further detail in the experimentation section below.
Pipeline Conditioning and Transport After FlocculationIn some implementations, the process includes pipeline conditioning of the treated thick fine tailings after flocculant addition and dispersion. The pipeline conditioning can notably be adapted to the type of dewatering, deposition and disposal that will be conducted (e.g., ex situ dewatering devices, sub-aerial deposition in thin lifts, or discharging into a pit to form a permanent aquatic storage structure (PASS), as will be discussed in greater detail below). For dewatering by sub-aerial deposition in thin lifts, the pipeline conditioning can be conducted to increase the yield stress of the flocculated material to a crest or maximum where the material presents gel-like characteristics, and then reduce the yield stress and effect floc breakdown to form a flocculated material in a water release zone yet still having relatively large flocs. For dewatering within a PASS, the pipeline conditioning can be modified such that the floc breakdown reduces the flocs to smaller sizes that provide settling time and settled volume characteristics for formation of the PASS. The floc size for thin lift dewatering can be provided to promote rapid initial water release a separation from the flocculated solids, while the floc size for the PASS implementation can be provided to promote both fast settling time and small settled volumes. For example, the target floc size for dewatering by sub-aerial deposition in thin lifts can be greater than about 100 μm, about 150 μm, about 200 μm, or about 250 μm; while the target floc size for dewatering via the PASS implementation can be between about 50 μm and about 200 μm, between about 50 μm and about 150 μm, or between about 75 μm and about 125 μm. The target floc size can be treated as an average floc size for process control and measurement. The floc size for the PASS implementation can be provided in order to balance competing effects of settling speed and settled volumes, which will depend on the starting CWR of the thick fine tailings, in order to achieve a CWR of at least 0.65 within one year after discharge into the PASS containment structure. The target floc size depends on polymer dosage of the thick fine tailings, regardless of the starting CWR. For example, with a starting CWR of about 0.1, the target floc size can be provided to achieve above 80% volume reduction within one year of discharge, whereas with a starting CWR of about 0.4, the target floc size can be provided to achieve above 32% volume reduction within one year of discharge.
Floc size reduction can be achieved by subjecting the treated thick fine tailings to pipeline shear sufficient to break down larger flocs to form smaller flocs while avoiding over-shearing the material where the flocs would be substantially broken down and the material would generally return to its initial slow settling characteristics. The pipeline shear can include high shear rates and/or sufficiently small pipe diameters in the conditioning section. The conditioning pipeline can be configured and implemented based on pre-determined target values for shear rates and total shear energy to impart to the material, based for example on empirical and/or modelling information. It should also be noted that the system can include monitoring equipment for measuring the approximate floc size (e.g., in-line, at-line or off-line) so that the conditioning pipeline can be adapted and/or regulated based on the measured floc size to provide the shear necessary to be within a target floc size range.
In some implementations, the conditioning pipeline terminates at a discharge point where the treated thick fine tailings are supplied to the dewatering device or site. In alternative implementations, the conditioning pipeline feeds into a conveyance pipeline that transports the treated thick fine tailings to the discharge location under reduced shear conditions. The conditioning and conveyance pipelines can be configured together to provide a target total shear energy to the material prior to deposition as well as high initial shear (i.e., in the conditioning pipeline) followed by lower shear (i.e., in the conveyance pipeline).
In some implementations, the total shear energy imparted to the treated thick fine tailings prior to discharge is sufficiently high to reach the target floc breakdown and yet within a range to facilitate water clarity and settling characteristics within the PASS. For example, it was found that, at optimum polymer dosage an average shear rate within 150 s−1 for 30 minutes could be imparted after flocculant addition to coagulated thick fine tailings. Based on this value, a conditioning and conveyance pipelines can be designed and implemented to operate within this envelope. More regarding conveyance will be discussed below.
Water separation from the flocs within the PASS can include several physical mechanisms. Settlement can be understood as volume reduction of the flocculated material, such that settlement is obtained by settling, consolidation and other volume reduction mechanisms. For example, during water separation, settling mechanisms where solid flocs and grains fall downward through the liquid phase can evolve into consolidation mechanisms. Modeling settlement within the PASS can combine various input data including settling data, consolidation data and other water-separation data.
Conveyance and Discharge of Treated Thick Fine TailingsAs mentioned above, the system can include a conveyance pipeline that is sized and configured for imparting a reduced or minimum shear to the material from the conditioning pipeline until discharge. This can be particularly advantageous when the distance from the flocculant injector to the discharge point is substantial or sufficiently great such that simple continuation of the conditioning pipeline would impart excess shear and risk over-shearing the material prior to discharge. The conveyance pipeline can be provided to have a larger diameter compared to the conditioning pipeline in order to reduce shear during this transportation step. Alternatively, the conveyance step can include other methods or systems that do not necessarily involve increasing pipe diameter, such as splitting the flow of treated thick fine tailings coming from a single conditioning pipeline into multiple conveyance lines and operating the conveyance lines at reduced flow rates, thereby reducing shear imparted to the material prior to discharge.
Flow rate and pipe diameter can be controlled in tandem in order to reduce the shear sufficiently to substantially maintain the floc size during conveyance (i.e., from conditioning to discharge). In some scenarios, the floc size change during conveyance is kept within 150 μm while keeping the floc size within 50 μm to 200 μm. Thus, if the initial floc size prior to conveyance is at the maximum target size of 200 μm, then the maximum floc size change should be 150 μm such that the floc size upon discharge is at least 50 μm. If the initial floc size is smaller than 200 μm, then the maximum floc size change should be kept at a lower level to ensure a minimum floc size of 50 μm upon discharge. Alternatively, when the initial floc size prior to conveyance is above 200 μm, then the floc size change can be greater than 150 μm. In general, the floc size prior to conveyance and after conveyance can be targeted and the process conditions (e.g., shear conditions) can be managed such that the floc size upon discharge is within the desired range.
Referring to
In a first implementation shown in
In a second implementation, as illustrated in
In terms of the conveyance method, in an in situ or ex situ dewatering case, conveyance of the flocculated and conditioned thick fine tailings can be controlled to maintain the floc size at an optimal value or within an optimal range for dewatering until deposition into the containment structure of the PASS. For example, lengths and diameters of the pipes can be chosen in accordance with various parameters including the distance to the discharge section and the attrition resistance of the flocs from the treated fine tailings. In addition, the conveyance pipes can be configured, positioned and operated such that no additional pumping is required to transport the material to the discharge locations. For example, the conveyance pipes can be positioned on a clopped section of the PASS containment structure having an inclination sufficient for the material to flow under gravity and remaining head provided by upstream pumps to the discharge locations.
In terms of discharge methods, in an in situ dewatering case, the treated thick fine tailings can be discharged continuously into the subaerial pit over a relatively long period of time (e.g., rise rate of about 20 meters per year) with the release water coming to the surface and the solids settling to the bottom. The discharge points can sometimes be submerged in the water or within the underlying tailings deposit, but the primary discharge method would include discharging the material onto the top of the fluid and/or onto a solid earth surface proximate to the fluid surface. The discharge should be designed and managed to avoid over-shearing or destroying the flocs in order to facilitate initial high water release and good settling rates. Thus, the discharge points should not be located at a significant height above a solid surface which could lead to a high-energy impact causing over-shearing.
In some implementations, floating pipe sections with discharge ends can be used to gain access to underutilized areas of discharge. The floating can be equipped with floating devices or can be supported by other means.
In an ex situ dewatering case, where the bulk of the water has been removed prior to deposition, the discharge method can be modified, such as distributing the discharge to prevent water pooling and modifying the pipe sections and discharge ends to accommodate higher-solids material.
It should also be understood that similar principles can apply to both the conveyance section and the discharge section to maintain the floc size in an optimal range for the desired water release and settling characteristics. For example, the conveyance section can be designed to include a plurality of pipes for splitting the flow of treated fine tailings coming from the conditioning section. Similarly, the discharge section can be designed to include a plurality of pipes for splitting the flow of treated fine tailings coming from the conditioning section or the conveyance section.
DewateringAs mentioned above, various dewatering techniques described in several Canadian patent applications can be used in the context of the techniques described herein. It should be noted that the overall process can include several dewatering steps, which will be discussed in greater detail in relation to
Various types of SLS's can be used. For example, belt filters and/or thickeners can be used to separate a solids-depleted water stream from a solids-enriched tailings material, both of which can be subjected to further processing after dewatering.
In the case of dewatering by sub-aerial deposition, various dewatering mechanisms can be at work depending on the deposition and post-deposition handling methods that are used. For instance, thin lift deposition can promote release water flowing away from the deposited material followed by dewatering by freeze-thaw, evaporation, and permeation mechanisms. For deposition that is performed to promote the formation of a much thicker lower stratum of treated fine tailings with an upper water cap, the lower stratum can dewater with consolidation as a significant dewatering mechanism. More regarding this will be discussed in relation to forming and managing the permanent aquatic storage structure (PASS) for the fine tailings and CoCs.
Characteristics of PASS LandformIn some implementations, as mentioned above, a permanent aquatic storage structure (PASS) can be built via in situ and/or ex situ dewatering of thick fine tailings that has been subjected to chemical immobilization and flocculation. A summary of some characteristics of the PASS landform is provided below.
The containment structure of the PASS can be a former mine pit, which can include various in-pit structural features such as benches and in-pit dykes. After closure of a mine pit, preparation of in-pit structures and landforms (e.g., dykes, dumps, temporary dams, pit walls) can be undertaken. Placement of the treated fine tailings can then begin. The treated fine tailings can be discharged in various ways at different stages of forming the PASS. The treated fine tailings can be discharged within the pit in accordance with tailings management and reclamation considerations. During or after placement of the treated fine tailings, additional landforms, surface water inlets and outlets, and operational infrastructure can be constructed as part of the overall PASS system.
The PASS can be seen as a type of end pit lake—but how it is formed and its target characteristics are different than a conventional end pit lake. For example, the discharged fine tailings are pre-treated before depositing into the landform that will become the end pit lake, to enhance dewatering and stability of the landform. Conventional end pit lakes are formed by placing tailings into the mine pit (i.e., the landform), capping with water, and treating the water within the landform. In an oil sands application, a conventional end pit lake directly deposits untreated MFT into the landform. In contrast, the PASS is formed from pre-treated material such that the MFT is dewatered at deposition and the water released from the MFT is pre-treated to chemically immobilize CoCs in the solids layer formed at the base of the PASS. Thus the PASS has several advantages over conventional end pit lakes, such as more consistent immobilization characteristics throughout the sediment layer, accelerated dewatering, and mitigation of long-term risks related to CoCs in the tailings.
In a PASS, the CoCs are immobilized prior to deposition in the landform. Fresh water dilution can be used in the aquatic reclamation process, in addition to the chemical immobilization of CoCs in the sedimentary layer. Note that fresh water dilution, meaning dilution of the already present pre-treated water cap, is different than relying on a fresh water cap to overlay fluid fine tails that were deposited untreated into the landform (i.e., as in a conventional end pit lake). The PASS in a reclaimed state will have no persistent turbidity, no (or negligible) bitumen in the water cap and toxicity and metals below guidelines required to support aquatic life. By contrast, a conventional end pit lake uses a fresh water cap and microbial activity as the aquatic reclamation process, and steps are not taken specifically to remove bitumen from water released from the fine tailings. A conventional end pit lake will have low persistent turbidity.
Process ImplementationsReferring to
The processes illustrated in
In some implementations, as illustrated in
Still referring to
A recycle water stream 48 can be withdrawn from the PASS for recycling purposes. In addition, recycle water 48 is withdrawn from the water cap 42 and can be supplied to various processing units, e.g., as polymer solution make-up water 50 and water 52 for use in extraction operations 54.
Referring now to
Turning now to
Referring to
Referring to
Referring to
Referring to
Referring now to
It should be noted that various other scenarios beyond those illustrated in
It should be noted that the techniques described herein can be used to treat MFT derived from oil sands extraction operations as well as various other thick fine tailings or slurries that include CoCs such as surfactants, metal compounds and/or hydrocarbons or other compounds immiscible in the water phase of the slurries. Whether applied to oil sands MFT or other types of MFT or thick fine tailings, various implementations described herein enable effective and efficient conversion of the thick fine tailings into a viable aquatic landform and facilitates permanent storage of thick fine tailings in a reclaimed landscape. In addition, in some implementations, a number of operational and environmental compliance constraints can be dealt with such as facilitating large scale storage of legacy and newly generated fine tailings in a permanent aquatic landform that is ready for reclamation within a relatively short timeframe (e.g., 10 years) from the end of mine life, while enabling efficient overall tailings management.
EXPERIMENTATION, RESULTS & CALCULATIONSVarious experiments and calculations were conducted to assess chemical immobilization compounds, flocculation, and other process parameters related to treating and dewatering MFT.
Chemical ImmobilizationSeveral multivalent salts were evaluated to assess reduction of CoCs in the release water to levels dictated by performance metrics. Chemicals tested include alum (Al2(SO4)3.14H2O), gypsum (CaSO4.2H2O), iron (II) sulphate (FeSO4 and also referred to as ferrous sulphate), iron (III) sulphate (Fe2(SO4)3 and also referred to as ferric sulphate) and lime (Ca(OH)2).
Two sets of experiments were conducted to assess impacts of alum and gypsum on the release water. First, different chemical dosages were added to undiluted MFT with a solids content of about 38 wt %, homogenized and the entire suspension centrifuged for chemical analysis of the concentrate. The second set of tests was conducted by adding equivalent dosages (on a water basis) to the same MFT diluted with process effluent water (PEW) down to about 3 wt %. These diluted MFT samples were placed in settling columns and allowed to settle for 24 hrs prior to decanting the water for chemical analysis.
The MFT pore water and PEW were tested to determine concentrations of certain components. For the particular set of tests, it was observed that naphthenic acid concentrations appeared uniform between the MFT pore water and the PEW that were used, and that there was a difference between other CoCs (arsenic and selenium) between MFT pore water and the PEW. Thus, when PEW is used for dilution of the MFT and/or preparation of flocculant solution, it should be noted that potential differences and variations in water compositions can influence the immobilization and flocculation and, consequently, the dosages of the additives can be adapted accordingly. In addition, implementation of the process can include a step of determining by measurement or calculation a contaminant concentration in the tailings pore water and/or the PEW or other water source used to add the immobilization chemical and flocculant, in order to control the immobilization and flocculation steps (e.g., chemical dosages).
AlumA summary of the effectiveness of alum at removing CoCs from the MFT pore water is presented in
The lower arsenic reduction with higher alum concentration for the undiluted MFT can have been due to inadequate mixing at the higher alum dosages (duplicate errors were >50%). Typically, alum is hydrolyzed into Al(OH)+(1,2,4) within approximately one second where the hydrolysis species neutralize the charge on clay particles. At high alum doses and slower dispersion or mixing times, aluminum hydroxide precipitate can be formed and, in turn, can promote sweep flocculation. Given that the charge neutralization is the primary intent of alum addition, rapid high-shear mixing should be implemented to facilitate consistent performance.
The removal of bitumen from the water column was visually observed to coincide with TSS removal (about 4.5 meq/L or 1.5 mM Al3+). While it can be desirable to add enough alum to lower the naphthenic acid below 1 ppm, increasing alum can also increase the release water conductivity and calcium content in the release water. FIG. 5 illustrates an increase in release water conductivity and calcium content with alum addition. Note that the solubility limit of alum in water at room temperature is about 36 wt %. Calcium content in the release water can be relevant for various reasons, particularly when the water is recycled into extraction operations. For example, when the water is reused in extraction operations and is heated using heat exchangers in a hot process water circuit, the heat exchangers can have certain calcium content limits (e.g., can only tolerate a maximum of about 30 ppm calcium to prevent scaling at design conditions or capacity) which can depend on the use of anti-scaling compounds for example. The maximum alum concentration can be provided based on the calcium concentrations of the waters (MFT pore water, MFT dilution water and/or polymer solution water), and fresh water can be used for one or more of the water streams added to the process. For example, considering fresh water for dilution, the optimum alum concentration can be selected.
GypsumAnother set of experiments was conducted to assess the quality of release water after MFT settling for 30 days, after the addition of the following screened immobilization chemicals: alum (Al3+), ferric sulphate (Fe3+) and sulphuric acid (H+). These latter immobilization chemicals were screened for chemical immobilization because gypsum dosages above around 10 meq/L Ca2+ (860 ppm gypsum in water) remove TSS below the 25 ppm threshold whereas alum, ferric sulphate and sulfuric acid removes TSS below the threshold at concentrations around 5 meq/L of their cation. Under test conditions, only alum and ferric sulphate removed arsenic to below the regulatory levels and gypsum had minimal arsenic reduction capability at saturation. Alum, ferric sulphate and sulphuric acid also seem to reduce naphthenic acids significantly, which would reduce the amount of fresh water dilution that can be required at closure of the PASS to safe levels that will ensure a self-establishment of aquatic biota or organisms.
A standard batch extraction unit (BEU) was used to simulate effects of oil sands derived MFT settling after addition of the screened immobilization chemicals. Results are presented in
Impact of mixing intensity and time on pH and rheology of the coagulated thick fine tailings was assessed as follows.
Impact of Mixing Intensity and Time on pHA series of experiments were conducted on two MFT types (CWR of 0.2 and 0.35). The tests were conducted with an alum dosage of 950 mg/L of MFT water and different mixer rpms. A pH reduction is expected when alum is added to MFT because alum is supplied in a sulfuric acid solution. However, the experiments were performed particularly to assess how rapidly the pH would buffer back to the equilibrium pH of the MFT. It should be noted that the time needed for pH bounce back (within seconds or minutes) can impact pipeline hydraulics as well as polymer flocculant dosage or shear sensitivity of the treated MFT (coagulated and flocculated).
- N—impeller rotational speed (rps)
- D—Impeller diameter (m)
- V—Liquid volume (m3)
- t—Mixing time (s)
It should be noted that experimentation was conducted in an open vessel and therefore, the impact of CO2 equilibration with air was unaccounted for. Iron and calcium carbonates in MFT are expected to dissolve with alum addition with the production of CO2, which remain dissolved in a closed system but dissipated in the open system during mixing experimentation.
Impact of Mixing Intensity and Time on RheologyA series of experiments was conducted on two MFT types (CWR of 0.2 and 0.3) for a mixer speed of 425 rpm and different alum dosages. Results are provided in
It should be noted that the rheology response is dependent on the alum dosage. The peak yield stress increases by up to 10 times with alum addition and coagulated MFT exhibits significantly higher thixotropic behaviour under constant shear rate as the alum dosage increases.
Another series of experiments was conducted on one type of MFT (CWR of 0.35) with alum dosage of 950 ppm and different mixer rpms. Results are provided in
A series of experiments was conducted with coagulated MFT of CWR from 0.1 to 0.35 in a 6″-diameter vessel, with a 5″ by 1″ paddle mixer, to assess the impact of immobilization chemical to flocculant injection distance on performance targets including water clarity and 28-day CWR. The tests used a total volume of about 750 ml, which included the combined volume of MFT, polymer solution and immobilization chemical solution.
Dewatering Performance of Low Shear Coagulated MFT-
- the water clarity degrades with polymer overdose. For both feed CWRs, water clarity begins to degrade above approximately 2000 g/T of clay, for an alum dosage of 950 mg/L of water;
- the polymer dosage at which water clarity degradation starts is dependent on the alum dosage (on a clay basis). Higher alum dosage (g/T of clay) will tolerate more polymer flocculant before water clarity is impacted. While the alum dose on a water basis was 950 mg/L of water in MFT, the alum dosage on clays vary. Alum dosage on a clay basis was 9500 g/T for 0.1 CWR, 4750 g/T for 0.2 CWR, and 2714 g/T for 0.35 CWR;
- optimum polymer dosage for the low-shear coagulated MFT, defined as the highest 28-day CWR given high water clarity (3 on a 1-3 scale), varied between 2200 and 2800 g/T clay for CWR of 0.1 to 0.35; and
- at the optimum polymer dosage, deleterious impact of the coagulated and flocculated MFT mixing intensity on water clarity and 28-d CWR is minimal between 462 and 9508 kJ/m3.
-
- the polymer overdose state is reached quicker for the high shear MFT than the low-shear MFT. Similar to the low-shear MFT, the water clarity degrades rapidly with polymer overdose. For both feed CWRs, water clarity begins to degrade above approximately 1500 g/T of clay, for an alum dosage of 950 mg/L of water;
- the optimum polymer dosage for the high-shear coagulated MFT , defined as the highest 28-d CWR given high water clarity (3 on a 1-3 scale), varied between 1000 and 1500 g/T clay for CWR of 0.1 to 0.35; and
- at the optimum polymer dosage (1000-1500 g/T clay), the impact of coagulated and flocculated MFT mixing intensity on water clarity and 28-d CWR is also minimal between 462 and 9508 kJ/m3.
The following conclusions can be derived from the above experiments:
The polymer injection can be performed after addition of the immobilization chemical such that mixing is within a critical mixing range. For impeller mixers, such critical mixing can correspond to (Kc) of 20 to 12,000. At the design alum dosages between 950 and 1200 ppm, the optimum polymer dosage decreases as the immobilization chemical to flocculant injection distance or Kc increases. For example, the optimum dosage for coagulated MFT with 0.35 CWR mixed at a Kc of 20 is approximately 2800 g/T of clay, while mixing at Kc of 12,000 requires a polymer flocculant dosage of approximately 1400 g/T of clay.
For a given flocculant injector design and MFT, dosed between 950 and 1200 ppm alum, the polymer flocculant dosage can vary by as much as 20% between MFT with a CWR of 0.1 and 0.35. Once the mixing distance between coagulation and flocculation is fixed, the polymer flocculant dosage per m3 of coagulated MFT is dependent on the coagulated MFT solids volume fraction (or CWR) and the alum dosage.
At the optimum polymer dosage, and treated MFT conditioning and conveyance energies tested (up to 9500 kJ/m3), the deposited material meets the water clarity criteria (<25 ppm TSS) and CWR>0.65 within a year. The 9500 kJ/m3 tested is equivalent to an average shear rate of 150 s−1 for 30 minutes after flocculant addition to coagulated MFT. This approximates to a maximum of 6 km in a 20″ pipeline at an average line velocity of 3.5 m/s that can be used in large scale operations.
Flocculation and Dewatering (In Situ Dewatering)On a bench scale, flocculation and in-line dewatering processes were evaluated concurrently as it has been found that maximum dewatering can be coupled to optimum flocculation. The flocculation polymer selection is based on direct experience from thin lift drying technology in which polymeric flocculants react with minerals in the tailings through a number of mechanisms to remove minerals from the tailings suspension (e.g., MFT) by forming aggregates (flocs). However, in addition to the polymer flocculant properties, the extent of interaction between the flocculant and the mineral particles is also dependent on the thick fine tailings properties (e.g., particle size and shapes, pore water chemistry, rheology, and the slurry hydrodynamic condition during polymer injection). In the in situ dewatering option where the immobilization chemical is added before the flocculant, alum and gypsum can act as coagulants that destabilize the particles in the thick fine tailings through double-layer compression and modify the pore water chemistry. These effects can change the nature of the flocculant-particle interaction relative to a process utilizing only polymer flocculant.
Polymer Flocculant ScreeningScreening tests were conducted to narrow down potential flocculants for MFT either untreated or previously coagulated with gypsum and alum. Three sodium-based anionic polyacrylamides (aPAMs) were tested: polymer A; polymer B; and polymer C. In addition, a deep deposit specialty chemical (DDSC) was tested, as well as a calcium-based anionic polyacrylamide (polymer D). A combination of alum and sodium aluminate was also tested.
Dewatering efficiency (24 hour CWR) was used as a screening parameter. At each immobilization chemical dosage (typically between 0 and −10 meq/L for alum and gypsum) the optimum polymer dosage was determined, followed by determination of the 24 hour CWR, the suspended solids and water chemistry of release water. Selection was based on the lowest immobilization chemical dosage for maximum 24 hour CWR meeting operational criteria of 0.65. The quality of the water recovered from the 24-hour CWR (sieved through a 325-mesh screen) was used to represent the expected water quality at closure. The total suspended solids in the pore water can be at most 25 ppm, and the suspended bitumen on water cap of approximately 0 ppm.
Given the differences in the chemistry of the polymers, it was found that each polymer flocculant benefited from mixing control to maximize dewatering efficiency. The four aPAMs (polymers A to D) performed well in the screening tests and the three sodium-based aPAMs (polymers A to C) were further evaluated with respect to flocculation.
Tests were conducted with immobilization chemical addition either before or after flocculant addition. It was found that adding the immobilization chemical (which can also be referred to as coagulant here) prior to the flocculant facilitated achieving advantageous CWR level and TSS reduction. When the MFT was flocculated prior to adding the immobilization chemical in the in situ dewatering process, the resultant CWR was found to be notably reduced at the dosages required for low TSS in the water phase.
Tests generally showed that MFT with CWR of at most 0.2 can require a higher immobilization chemical dosage demand (but lower polymer dosage demand), while MFT with CWR of at least 0.35 will require lower immobilization chemical dosage demand but higher polymer dosage demand.
Flocculent Dosages for Alum- or Gypsum-Treated MFTUsing the same mixing parameters, the optimum dosages for flocculation (measured by the 24 hour CWR) were evaluated for the aPAM polymers A, B and C. As shown in
Extensive investigation was conducted on the dewatering potential of alum-treated MFT at the respective optimum polymer dosages. Again, the mixing parameters were fixed at the optimum for the no-immobilization chemical case and could be enhanced.
To achieve the desired CWR performance in the treatment of these MFT samples, it was found that the alum dosage should not exceed approximately 1000 ppm. At 950 ppm of alum, the TSS, bitumen and metals should meet the performance criteria, and naphthenic acid would be approximately 60% remediated to target levels. To confirm the geochemical performance, the release waters collected after flocculation and 24-hour dewatering were analyzed in a similar fashion to the procedure to obtain the data in
Referring to
The following Table A provides some release water chemistry results of MFT after flocculation and treatment with 360 ppm and 950 ppm alum:
While a higher alum dosage (>10 meq/L Al3+) can improve the release water clarity, it can result in levels of dissolved salts (including calcium and sulphate) higher than operational and closure threshold. Increasing alum dosage was found to increase the dynamic yield stress and viscosity of the MFT, and therefore the mixing intensity required for inline flocculation. Optionally, polymers that can achieve the operational and closure threshold at lower alum dosages can be chosen. Optionally, ferric sulphate and sulfuric acid can be used as alternative immobilization chemicals to alum.
Impact of Gypsum on MFT Dewatering Performance
The 24 hour CWR at saturated gypsum addition (2500 ppm) was consistently higher than the base case. Also, at these dosage levels, the TSS and bitumen are removed from suspension. Similar to the results shown in
Based on field experience in flocculation and dewatering operations of MFT as well as investigations into fundamentals of chemical mixing, the polymer dosage can be minimized and 24 hour CWR maximized through optimal mixing at mesoscale, i.e., the scale of the bulk of clay mineral particles in a dispersed slurry (between 0.1 μm and 1 μm equivalent spherical diameter). Addition of alum or gypsum changes the clay-aggregate scales and would benefit from optimization. To determine the required range of mixing on a bench scale, an optimized fractional factorial experiment (108) was conducted at two immobilization chemical dosages (0 ppm and 950 ppm alum), three mixer rotations per minute (RPM) (300 RPM (base case), 600 RPM and 900 RPM), three polymer injection rates, and two MFT clay-to-water ratios (0.25 CWR and 0.35 CWR). Polymers B and C, which had given the best results according to previous testing, were selected for this stage of testing.
The polymer dosage was optimized at each test condition.
It is noted that the mixing could be provided based on the particular immobilization chemical and polymer flocculant used in the process in order to enable greater dewatering and lower polymer dosages particularly for the larger scale operations. Mixing design and control could include, for example, special injector designs and/or dilution control.
Characteristics of PASS Performance Via In Situ Dewatering Operational PerformanceCertain aspects of the operational performance of the PASS are provided below.
Volume ReductionThe deposited or discharged treated MFT is expected to be at a steady state CWR≥0.65 during operations and continue to densify and consolidate after the end of mine life (EOML). The consolidation rate can be determined via additional bench scale studies and/or monitoring of a field prototype. Based on bench scale studies, the use of 950 ppm alum or saturated gypsum in the MFT slurry did not reduce the CWR achievable in the field relative to a base case in which no immobilization chemical is used.
Recycle Water Quality
At 950 ppm alum, the unmitigated residual calcium in the recycle water would be within the desired operating envelope for certain heat exchangers in which anti-scaling agents are used. For gypsum-treated MFT, the residual calcium is about 100 ppm and would benefit from additional mitigation within the operating envelope for certain heat exchangers. The calcium concentration in the release water and/or cap water can be monitored and calcium reduction can be implemented depending on the equipment (e.g., heat exchanger) or process requirements to which the water is recycled. Calcium levels can be reduced by dilution with other water streams, exchanging for sodium on clay surfaces, and/or precipitating as calcium carbonate prior to incorporation into certain equipment or unit operation of the extraction process.
In addition, an unmitigated increase in the total dissolved salts and reduction in bicarbonate of the recycled water could have a negative impact on bitumen recovery. Using water chemistry data, the bitumen recovery loss due to increased salt levels was estimated to be about 0.5 wt % for 950 ppm alum and about 2 wt % for MFT treated with saturated gypsum. The bitumen recovery losses can also become progressively greater with increasing clay content in the oil sands ore.
Closure PerformanceCertain aspects of the closure performance of the PASS are provided below.
Suspended SolidsWithout alum or gypsum addition, the water cap of the PASS is expected to contain significant amounts of suspended solids, which are currently difficult to mitigate at large scales. Suspended solids in the water column would also be exacerbated during the spring and fall pond turnover events. At 950 ppm alum and 2500 ppm gypsum, the TSS is expected to be close to zero. Pond turnover would generate suspended solids during the event, but would settle fairly rapidly depending on the aggregate sizes of the aggregated solids.
After closure, fresh water dilution provided would change the chemistry of the water cap of the PASS. Negative impacts of the chemistry change on suspended solids could be mitigated by controlling the dilution water (e.g., fresh or surface run off rather than process water with high bicarbonate content). In addition, capping the sediment layer with a coarse material (e.g., coke or sand) could mitigate against re-suspension of fine solids or bitumen during pond turnovers. The coarse material could be distributed over the water cap (e.g., via an aqueous slurried stream containing the coarse material pumped to the PASS) and the coarse material would then settle by gravity onto the lower layer of sediment. This intermediate layer could be used to cap the mud layer, which is the interface between water and the sediment, at the end of operation and start of reclamation. For example, coke could be slurried through the water cap and would be light enough to stay on top of the mud layer. The coke layer or another type of intermediate layer could facilitate minimizing the flux of CoCs between the lower deposit and the water cap. Coke could potentially adsorb some of the CoCs. Other particular material could also be used, particular those that are porous and have absorptive properties.
Bitumen in SuspensionBench scale studies suggest that bitumen immobilization within the sediment tracks suspended solids removal. This can be at least partly due to negatively charged bitumen surface being able to coagulate with cations similar to the negatively charged clay surfaces. Calcium, magnesium or an aluminum hydroxyl complex could bridge destabilized clay particles to bitumen droplets, thereby chemically immobilizing bitumen within the sediment. This mechanism has been observed in primary bitumen extraction where overly high calcium content in the process or ore connate water can depress flotation of bitumen into the froth layer.
Microbial activity due to increased concentrations of sulphate and possible availability of easily degradable organic carbon (e.g., from aPAMs or bitumen light fractions) could generate gas. Gas bubbles can potentially refloat bitumen droplets into the water column if the bitumen is insufficiently immobilized. However, microbial activity further degrades bitumen and promotes mineral adsorption on bitumen surfaces, which, in turn, can inhibit bitumen flotation. Both alum and gypsum at the appropriate dosages should immobilize bitumen through to reclamation and inhibit substantial remobilization or flotation. The immobilization chemicals and polymer flocculant can be selected and dosed such that gas-induced floatation of bitumen is inhibited within the PASS.
Regulated MetalsArsenic and selenium are the primary metals in exceedance of fresh water guidelines for aquatic life for certain example MFT samples under study. Referring to
In some scenarios, certain CoCs or categories of CoCs can be used as a proxy for toxicity. For instance, for certain MFT materials naphthenic acid can be used as proxy for the toxicity. Unlike metals, naphthenic acids degrade at a notable rate (e.g., at about 16% per year in column tests and even more rapidly within years at larger commercial scale operations). Referring to
Fresh water dilution is advisable to bring the dissolved salts down to levels that can support freshwater organisms. The electrical conductivity of 340 μS/cm was used for fresh river water in this analysis. At 2000 μS/cm, the release water can support freshwater plants, and below 1000 μS/cm phytoplankton can be supported. With no immobilization chemical, 50% and 80% dilutions are required to achieve the freshwater plants and phytoplankton criteria respectively. For alum additions at 950 ppm, a 60% dilution can be required for freshwater plants and up to 80% for phytoplankton, while about 70% dilution can be required to meet the freshwater plants criterion for gypsum, according to the example dosages obtained pursuant to the testing described herein. If, at maximum dilution rates, saturated gypsum treatment is not able to meet the phytoplankton criteria and/or the salt loading in the process water and the pore water of the MFT increase during the life of mine, water treatment can be implemented accordingly.
In summary, according to the studies based on example water and tailings properties, a 50% to 60% fresh water dilution of 950 ppm alum treated landform would meet geochemical criteria to support freshwater plants, and 80% fresh water dilution would ensure support for all freshwater aquatic organisms within a ten-year timeframe. For gypsum, fresh water dilution at the maximum 80% would meet all criteria except for freshwater aquatic organisms. In the corresponding base case, although an 80% dilution would meet the criteria for freshwater aquatic organisms, the suspended solids and bitumen migration in the water column would not be mitigated by fresh water dilution and would have to be dealt with via other means.
Impacts of Water Chemistry on Dewatering OperationsStudies were conducted to evaluate potential impacts of increasing process water ionic strength on MFT drying operations. The ionic strength increases that were investigated were from NaCl (ore connate water) and flue gas desulfurization (FGD) gypsum. Other additives, including reverse osmosis reject brine solutions or evaporator feed with high organic acids, were also tested.
In these studies, the NaCl or Flue Gas Desulfurization (FGD) gypsum salts were introduced into the polymer make-up water which was about 10% of the total water in MFT. Manipulating the salt content of the polymer make-up water was operationally less intrusive and offers greater process performance predictability than adding salt directly into the MFT flow. Other additives were also tested. A 0.45% polymer solution was created for each additive. Polymer A was used. A dose sweep was conducted to determine the optimum dose for the MFT sample. Optimally flocculated MFT was stacked in 2 cm lifts and allowed to drain for 24 hrs to determine the initial water release (or net water release) and the release water chemistry. Evaporation of the lifts was monitored over a week until completely dried.
In terms of the findings, the use of saturated gypsum, reverse osmosis reject brine solutions or evaporator feed with high organic acids did not significantly impact flocculation of MFT or the release water chemistry. Increases in PEW TDS to a maximum of about 5500 ppm in future operations would not significantly impact flocculation efficiency or release water chemistry, although polymer dosage can increase by about 10%. For a saturated gypsum make-up water, the optimum polymer demand increased by 15%. In addition, for polymer make up water saturated with gypsum, adsorption of Ca2+ on clays limited the Ca2+ in the 24-hour release water to below 30 ppm. The Ca2+ concentration from recycle water resulting from the use of a saturated gypsum solution for polymer make-up, should not have a significant impact on pipe scaling or bitumen extraction. Furthermore, the Ca2+ appeared to improve the initial evaporation rate of 2 cm lifts. In addition, run off from dried MFT with reverse osmosis brine and evaporator feed had TDS higher than PEW and varied with the TDS in the polymer water; high gypsum concentrations did not significantly increase TDS in the runoff; and runoff water quality can be better in the field compared to lab work as only exposed surfaces are impacted in field operations.
It was found that salts additives can reduce the maximum drying rate (including sub-aerial deposition cell utilization) determined for existing MFT drying operations. For FGD gypsum, this would indicate that large amounts of gypsum should not be stored in the dried MFT matrix; and for high NaCl make-up water, a mitigation strategy can be implemented to reduce NaCl content in the waters (MFT pore water and/or polymer make-up water) present in the MFT drying process, particularly as higher NaCl concentrations occur as PEW salts cycle up. Increased TDS in runoff water can also merit mitigation strategy to reduce the impact on recycled water that influences PEW chemistry. A reduction in the geotechnical stability of the deposit due to salt additions would also warrant assessment to reduce potential negative impacts on final reclamation on closure.
PASS Process Modelling and ExperimentationAdditional experimentation and modelling were conducted regarding target steady-state CWR of the treated material in the PASS. An exemplary target was a CWR of at least 0.65 within one year of discharge into the PASS structure.
Process modelling strategy included evaluation of the parameters influencing the dewatering rate and the steady-state CWR. Dewatering rate is considered to vary according to the floc size distribution and the floc density of the coagulated and flocculated MFT, and therefore according to the CWR of the MFT, the immobilization chemical and flocculant dosage and the shear history. The steady-state CWR is considered to vary according to deposit depth (also referred to as total stress) and floc size distribution and density of the coagulated and flocculated MFT.
The following equation was used to empirically model the CWR as a function of time with a variable slope.
-
- CWRt=0 and T (days) are independent variable
- CWRt=∞ is the final (steady state) CWR
- T50 is the time to reach 50% of the total strain (CWRt=∞−CWRt=0)
- Rate is a dimensionless quantity to characterize the relative “deformation or strain rate”. It is the slope of the logistic function—a logarithm slope. So, Rate <1 is very rapid initial settling and >1 is slower initial settling.
The above empirical model resulted from experimentation including columns tests filled with coagulated and flocculated MFT. The experimental matrix include varying the initial CWR, cMFT preshear, immobilization chemical and polymer dosages and several levels of cfMFT shear. Each output cfMFT is allowed to settle over a period of several months in columns between 10 cm to 200 cm tall, and the settling profile continuous monitored. Once the columns have reached steady state (from a few days to several months depending on the input variables), the sediment layer is sectioned and analyzed for density, clay content and pore water chemistry. Full geochemical and toxicology analyses are also conducted on the release water.
Steady-State CWR (CWRt=∞)Major variables influencing steady-state CWR include feed CWR and deposit height (also referred to as total stress). More precisely, CWRt=∞ increases as feed CWR increases (Floc density increases with feed CWR). In addition, CWRt=∞ increases with deposit height (self weight). Experimentation parameters and results for two columns with respective feed CWR of 0.35 and 0.2 are reproduced below in Table C and the modelled CWR reported in
Minor variables influencing steady-state CWR include polymer dosage and shear rate. More precisely, experimentations showed that high polymer dosage and high shear rate reduce CWRt=∞. Longer shear duration appears to favor enhanced floc packing efficiency. Experimentation parameters and results are reproduced below in Table D and the corresponding modelled CWR illustrated in
Referring to
Major variables influencing the time to reach 50% of the total strain (T50) include polymer dosage, feed CWR and total stress. More precisely, referring to
The average floc size is expected to drive the “initial settlement or deformation rate”. Referring to
Experimentation parameters and results are reproduced below in Table F, and the corresponding average CWR showed on
Claims
1. A process for treating mature fine tailings (MFT) derived from oil sands extraction and including contaminants of concern (CoCs) comprising bitumen, naphthenic acid, arsenic and selenium, the process comprising:
- retrieving MFT from a tailings pond;
- providing an in-line flow of the MFT;
- adding in-line an aqueous immobilization solution into the in-line flow of MFT and in-line mixing therewith, the aqueous immobilization solution comprising an immobilization chemical selected from multivalent inorganic salts, thereby producing a pre-treated tailings flow comprising: immobilized bitumen-clay complexes comprising multivalent cations forming cation bridges between negatively charged bitumen droplets and negatively charged clay particles; insolubilized naphthenic acid; insolubilized arsenic; and insolubilized selenium;
- adding in-line an aqueous flocculant solution into the pre-treated tailings flow to form a flocculating material;
- in-line conditioning of the flocculating material to produce a flocculated material in a water release zone;
- depositing the flocculated material onto a sub-aerial deposition area, allowing release water to separate from a solids-enriched material;
- forming a permanent aquatic storage structure (PASS) for retaining the solids-enriched material and a water cap, wherein the solids-enriched material: forms a consolidating solids-rich lower stratum below the water cap; and retains the immobilized bitumen-clay complexes, the insolubilized naphthenic acid, the insolubilized arsenic and the insolubilized selenium to inhibit migration of the CoCs into the water cap.
2. The process of claim 1, wherein the aqueous immobilization solution is neutral or acidic.
3. The process of claim 1, wherein the immobilization chemical is fully dissolved in the immobilization solution prior to the in-line addition into the in-line flow of MFT.
4. The process of claim 1, wherein the immobilization chemical comprises a divalent cation or a trivalent cation.
5. The process of claim 1, wherein the in-line addition and the in-line mixing of the immobilization chemical into the MFT are performed at concentration and mixing intensity sufficient to substantially inhibit aggregation of multivalent cation hydroxides and promote charge neutralization between the negatively charged bitumen droplets and the negatively charged clay particles.
6. The process of claim 1, wherein the aqueous flocculant solution comprises an anionic polymer flocculant.
7. The process of claim 6, wherein the anionic polymer flocculant comprises a sodium-based or a calcium-based polyacrylamide-polyacrylate co-polymer with high molecular weight.
8. The process of claim 6, wherein the anionic polymer flocculant is fully dissolved in the aqueous flocculant solution prior to addition to the pre-treated tailings flow.
9. The process of claim 1, wherein in-line conditioning of the flocculating material consists of pipeline shearing that is managed to increase a yield strength of the flocculating material to a maximum, and then decrease the yield strength to achieve the water release zone while avoiding overshearing.
10. The process of claim 1, wherein the immobilization chemical comprises or consists of gypsum, alum, ferric sulphate or a combination thereof.
11. The process of claim 1, wherein the immobilization chemical comprises an aluminum cation or a calcium cation.
12. The process of claim 1, wherein the immobilization chemical comprises a sulphate anion.
13. The process of claim 1, wherein the immobilization chemical is added in a concentration below water saturation thereof.
14. The process of claim 1, wherein the immobilization chemical is selected, formulated and/or added in a concentration so as to immobilize substantially all of the bitumen, naphthenic acid, arsenic and selenium present in the MFT.
15. The process of claim 1, wherein the immobilization chemical is selected, formulated and/or added in a concentration so as to immobilize substantially all of the CoCs present in the MFT.
16. The process of claim 1, wherein the immobilization chemical is selected, formulated and/or added in a concentration so as to avoid increasing flocculant dosage more than 20% or more than 10% to achieve a same clay-to-water ratio (CWR) as an equivalent process excluding addition of an immobilization chemical.
17. The process of claim 1, further comprising providing an intermediate layer of coke in between the water cap and the solids-rich lower stratum.
18. The process of claim 1, further comprising managing the PASS to render the water cap suitable to supporting aquatic life.
19. The process of claim 18, wherein the managing includes supplying fresh water into the water cap.
20. The process of claim 18, wherein the managing comprises construction and maintenance of reclamation landforms.
21. The process of claim 20, wherein the reclamation landforms comprise shorelines, littoral zones, water inlets and water outlets.
22. The process of claim 18, wherein the managing comprises monitoring composition of the water cap.
23. The process of claim 18, wherein the managing comprises controlling water levels of the water cap.
24. The process of claim 1, wherein the deposited solids-enriched material remains in-place after deposition and forms the consolidating solids-rich lower stratum of the PASS.
25. The process of claim 1, wherein the deposited solids-enriched material is not relocated after deposition.
26. A process for treating thick fine tailings that includes contaminants of concern (CoCs) and suspended solids, the process comprising:
- subjecting the thick fine tailings to chemical immobilization and polymeric flocculation to chemically immobilize the CoCs and polymerically flocculate the suspended solids, to produce treated thick fine tailings; and
- dewatering the treated thick fine tailings to produce: an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
27. The process of claim 26, wherein subjecting the thick fine tailings to chemical immobilization and polymeric flocculation comprises:
- subjecting the thick fine tailings to the chemical immobilization to immobilize the CoCs and produce a pre-treated tailings material; and
- subjecting the pre-treated tailings material to the polymeric flocculation to flocculate the suspended solids and produce a flocculated tailings material.
28. The process of claim 26, wherein subjecting the thick fine tailings to chemical immobilization and polymeric flocculation comprises:
- adding an immobilization chemical to the thick fine tailings to produce a pre-treated tailings; and
- adding a flocculant into the pre-treated tailings to form a flocculating material.
29. The process of claim 28, wherein the immobilization chemical and the flocculant are added in-line.
30. The process of claim 28, wherein the immobilization chemical is added as part of an aqueous immobilization solution, and the flocculant is added as part of an aqueous flocculant solution.
31. The process of claim 26, wherein the chemical immobilization includes insolubilization of dissolved or soluble CoCs, forming cation bridges between negatively charged CoCs and negatively charged mineral particles, or a combination thereof.
32. The process of claim 26, wherein the dewatering comprises depositing the treated thick fine tailings onto a sloped sub-aerial beach.
33. The process of claim 26, wherein the dewatering comprises depositing the treated thick fine tailings into a pit.
34. The process of claim 33, wherein the pit is a mine pit.
35. The process of claim 33, further comprising forming a permanent aquatic storage structure (PASS) for retaining the solids-enriched component, the PASS comprising:
- a water cap; and
- a consolidating solids-rich lower stratum below the water cap and inhibiting migration of the CoCs into the water cap.
36. The process of claim 26, wherein the thick fine tailings comprise mature fine tailings derived from oil sands extraction.
37. A process for treating thick fine tailings that includes contaminants of concern (CoCs), the process comprising:
- adding an immobilization chemical into the thick fine tailings in order to immobilize the CoCs and produce a pre-treated tailings comprising immobilized CoCs;
- adding a flocculant into the pre-treated tailings to flocculate suspended solids and form a flocculating material;
- conditioning the flocculating material to produce a flocculated material; and
- dewatering the flocculated material to produce: an aqueous component depleted in the CoCs and suspended solids; and a solids-enriched component comprising the immobilized CoCs and the flocculated solids.
38. The process of claim 37, wherein the CoCs comprise surfactants and soluble metal, metalloid and/or non-metal compounds, the pre-treated tailings comprises insolubilized surfactants; and insolubilized metal, metalloid and/or non-metal compounds; and the immobilized CoCs comprise insolubilized surfactants, the insolubilized metal, metalloid and/or non-metal compounds.
39. The process of claim 37, wherein the CoCs comprise hydrocarbons, surfactants and soluble metal, metalloid and/or non-metal compounds, the pre-treated tailings comprise immobilized hydrocarbon-mineral complexes, insolubilized surfactants; and insolubilized metal, metalloid and/or non-metal compounds; and the immobilized CoCs comprise immobilized hydrocarbon-mineral complexes, insolubilized surfactants, the insolubilized metal, metalloid and/or non-metal compounds.
40. The process of claim 37, wherein the flocculant is an anionic polyacrylamide based flocculant and the immobilization chemical is an aluminum sulphate based compound, the process comprising adding the aluminum sulphate based compound into the thick fine tailings at sufficient dosage and mixing so that aluminum cations:
- form cation bridges between negatively charged immiscible CoCs and negatively charged clay particles, to produce immobilized complexes; and
- insolubilize dissolved CoCs to form insolubilized CoCs.
41. The process of claim 37, wherein the flocculant is an anionic polyacrylamide based flocculant and the immobilization chemical is a calcium sulphate based compound, the process comprising adding the calcium sulphate based compound into the thick fine tailings at sufficient dosage and mixing so that calcium cations:
- form cation bridges between negatively charged immiscible CoCs and negatively charged clay particles, to produce immobilized complexes; and insolubilize dissolved CoCs to form insolubilized CoCs.
42. A system for treating thick fine tailings comprising contaminants of concern (CoCs) and suspended solids, the system comprising:
- a tailings supply pipeline for transporting the thick fine tailings;
- an immobilization addition line in fluid communication with the tailings pipeline for adding an immobilization chemical;
- a polymer flocculant injector in fluid communication with the tailings pipeline for injecting a polymer flocculant to produce a flocculation tailings material;
- a tailings conditioning pipeline in fluid communication with the polymer flocculant injector for transporting and conditioning the flocculation tailings material;
- a deposition outlet for receiving flocculation tailings material and depositing the same onto a sub-aerial deposition area; and
- a containment structure including the sub-aerial deposition area and configured to contain the flocculation tailings material and allow formation of a water cap and a solids-rich lower stratum below the water cap, the solids-rich lower stratum comprising polymercially flocculated solids and chemically immobilized CoCs.
43. The system of claim 42, further comprising a fresh water line for introducing fresh water into the water cap from the containment structure.
44. A process for treating fine tailings that include contaminants of concern (CoCs) that are water mobile and suspended solids, the process comprising:
- adding an immobilization chemical to react with the CoCs and enable immobilization of the same;
- adding a flocculant to flocculate the suspended solids;
- producing a treated tailings material;
- dewatering the treated tailings material to produce:
- a water component; and
- a solids-enriched component comprising: the CoCs rendered water immobile; and flocculated solids.
45. The process of claim 44, wherein the immobilization chemical comprises a divalent cation and/or a trivalent cation.
46. The process of claim 44, wherein the flocculant comprises an anionic polymer flocculant.
47. The process of claim 46, wherein the anionic polymer flocculant comprises a sodium-based or calcium-based polyacrylamide-polyacrylate co-polymer with high molecular weight.
48. The process of claim 44, wherein the immobilization chemical comprises gypsum, alum, ferric sulphate or a combination thereof.
49. The process of claim 44, wherein the immobilization chemical and the polymer flocculant are each added in-line.
50. The process of claim 44, wherein the immobilization chemical and the polymer flocculant are each added dissolved in a corresponding aqueous solution.
51. The process of claim 44, wherein the immobilization chemical is selected to immobilize at least one of:
- bitumen by cation bridging with suspended clays;
- naphthenic acids;
- arsenic; and
- selenium.
52. The process of claim 44, wherein the dewatering comprises:
- continuously discharging the treated tailings material into a pit to allow an initial water release from the solids-enriched component; and
- compressing the solids-enriched component below subsequently deposited treated tailings and/or a water cap.
53. The process of claim 44, further comprising forming a permanent aquatic storage structure (PASS) for retaining the solids-enriched component, the PASS comprising:
- a water cap; and
- a consolidating solids-rich lower stratum below the water cap and inhibiting migration of the CoCs into the water cap.
54. The process of claim 53, further comprising managing the PASS to render the water cap suitable to supporting aquatic life.
55. The process of claim 54, wherein the managing includes supplying fresh water into the water cap; construction and maintenance of reclamation landforms; monitoring composition of the water cap; and/or controlling water levels of the water cap.
56. The process of claim 53, wherein the deposited solids-enriched component remains in-place after deposition and forms the consolidating solids-rich lower stratum of the PASS.
57. The process of claim 53, wherein the PASS is contained in a mine pit.
58. The process of claims 52, wherein the initial water release results in an initial clay-to-water ratio (CWR) in the solids-enriched component of at least 0.55 or at least 0.65.
59. The process of claim 52, wherein the treated tailings material is discharged so that the initial water release results in an initial clay-to-water ratio (CWR) in the solids-enriched component of at least 1.
60. The process of claim 53, wherein the treated tailings material is discharged sub-aerially.
61. The process of claim 53, wherein the treated tailings material is discharged to avoid overshearing flocs in the treated tailings material.
62. The process of claim 44, wherein the fine tailings comprise thick fine tailings, and the thick fine tailings comprise mature fine tailings derived from oil sands extraction.
63. The process of claim 44, wherein the addition of the immobilization chemical forms a pre-treated material, and the process comprises:
- subjecting the pre-treated material to pipeline shear conditioning to form a conditioned pre-treated material, the pipeline shear conditioning being provided such that the conditioned pre-treated material has target rheological characteristics; and the flocculant being added to the conditioned pre-treated material to produce the treated tailings material.
64. The process of claim 63, wherein the pipeline shear conditioning is performed to modify a yield stress of the pre-treated material from an initial yield stress up to an upper crest yield stress, and then down to a lower yield stress that is in between the initial yield stress and the upper crest yield stress, such that the conditioned pre-treated material has the lower yield stress.
65. The process of claim 64, wherein the pipeline shear conditioning is performed so that the lower yield stress represents a reduction in the yield stress of about 30% to 80% from the upper crest yield stress.
66. The process of claim 64, wherein the pipeline shear conditioning is performed so that at least one of the following is met:
- the lower yield stress is at least about 25 Pa lower than the upper crest yield stress;
- the lower yield stress is between about 10 Pa and about 15 Pa; and
- the lower yield stress is on a generally flat plateau of yield stress versus time.
67. The process of claim 63, wherein the pipeline shear conditioning is performed to:
- produce a gel-state pre-treated material having increased yield stress; and then
- produce the conditioned pre-treated material having an ungelled state and a decreased yield stress compared to the gel-state pre-treated material.
68. The process of claim 63, wherein the pipeline shear conditioning is performed such that the conditioned pre-treated material has a turbulent flow regime upon addition of the flocculant thereto.
69. The process of claim 63, wherein adding the immobilization chemical to the thick fine tailings is performed in-line via a pipe junction; the immobilization chemical and the thick fine tailings are supplied through a static mixer to form the pre-treated material; and the pre-treated material is supplied through a conditioning pipeline in order to impart all of the pipeline shear conditioning to the pre-treated material prior to addition of the flocculant.
70. The process of claim 63, wherein the immobilization chemical comprises alum, gypsum, or ferric sulphate.
71. The process of claim 63, wherein the pipeline shear conditioning is controlled according to shear intensity, shear duration and/or total shear energy imparted to the pre-treated material.
72. The process of claim 63, wherein the immobilization chemical is added via an acidic solution having an initial tailing pH to form the pre-treated material having a reduced pH;
- and wherein the pipeline shear conditioning is provided such that the conditioned pre-treated material has at least a target pH that is greater than the reduced pH.
73. The process of claim 72, wherein the pipeline shear conditioning is performed such that the target pH is at least 7.5 or at least 8.
74. The process of claim 72, wherein the pipeline shear conditioning is performed such that the target pH is at least 15% above a lowest pH obtained for the pre-treated material after addition of the acidic solution; or such that the target pH is at least 25% above the lowest pH obtained for the pre-treated material after addition of the acidic solution.
75. The process of claim 72, wherein the pipeline shear conditioning is performed such that the target pH within 10% of the initial tailings pH.
76. The process of claim 72, wherein the pipeline shear conditioning is performed to achieve the target pH that is based on optimal activity of the flocculant.
77. The process of claim 72, wherein the acidic solution comprises sulphuric acid.
78. The process of claim 72, wherein the immobilization chemical is completely dissolved in the acidic solution prior to addition to the thick fine tailings.
79. The process of claim 72, wherein adding the acidic solution to the thick fine tailings is performed in-line via a pipe junction; the immobilization chemical and the thick fine tailings are supplied through a static mixer to form the pre-treated material; the pre-treated material is supplied through a conditioning pipeline in order to impart all of the pipeline shear conditioning to the pre-treated material prior to addition of the flocculant.
80. The process of claim 63, comprising supplying the immobilization chemical and the thick fine tailings to a mixer to form the pre-treated material, wherein immobilization chemical dosage is determined based on the mixer and density characteristics of the thick fine tailings.
81. The process of claim 80, wherein the immobilization chemical is added to the thick fine tailings via a pipe junction and the mixer is a static mixer located downstream and proximate to the pipe junction.
82. The process of claim 81, wherein the pipe junction is a T junction.
83. The process of claim 80, wherein the density characteristics of the thick fine tailings are measured on-line prior to adding the immobilization chemical, and on-line density measurements are used to control the immobilization chemical dosage.
84. A process for treating thick fine tailings, comprising:
- adding an immobilization chemical to the thick fine tailings to form a pre-treated material;
- subjecting the pre-treated material to shear conditioning to form a conditioned pre-treated material;
- adding a flocculant to the conditioned pre-treated material to produce a flocculating material;
- subjecting the flocculating material to shear conditioning to form a conditioned flocculated material;
- discharging the conditioned flocculated material into a pit to enable settling and consolidation of the flocs and separation of water to form an upper water cap, thereby forming a permanent aquatic storage structure (PASS).
85. The process of claim 84, wherein subjecting the flocculating material to shear conditioning is performed to increase floc size up to an upper level and to then break down the flocs and decrease floc size to within a target floc size range.
86. The process of claim 85, wherein the target floc size range is pre-determined based on a minimum settling rate and a maximum settled volume within the PASS.
87. The process of claim 85, wherein the target floc size range is between about 50 microns and about 44 microns.
88. The process of claim 85, wherein the target floc size range is sufficient to provide a minimum settling rate to achieve a clay-to-water ratio (CWR) greater than 0.65 within one year within the PASS.
89. The process of claim 88, wherein the target floc size range is tailored to a starting CWR of the thick fine tailings to achieve the CWR greater than 0.65 within one year within the PASS.
90. The process of claim 85, wherein subjecting the flocculating material to the shear conditioning consists of pipeline shear conditioning.
91. The process of claim 85, wherein subjecting the flocculating material to the shear conditioning comprises pipe shear conditioning the flocculating material in a conditioning pipeline to form the conditioned flocculated material.
92. The process of claim 91, wherein discharging of the conditioned flocculated material into the pit is performed immediately after exiting the conditioning pipeline.
93. The process of claim 91, further comprising conveying the conditioned flocculated material from the conditioning pipeline to a discharge location.
94. The process of claim 93, wherein the conveying is performed via a conveyance pipeline fluidly coupled to a downstream end of the conditioning pipeline.
95. The process of claim 94, wherein the conveyance pipeline is located on a sloped side of the pit.
96. The process of claim 94, wherein the conveyance pipeline is configured and operated such that the conditioned flocculated material flows therethrough under a non-turbulent flow regime.
97. The process of claim 95, wherein the conveyance pipeline is configured and operated such that the conditioned flocculated material flows therethrough under a laminar flow regime.
98. The process of claim 93, wherein the conveying is performed at shear conditions that are sufficiently low to substantially maintain flocs size within the target floc size range.
99. The process of claim 84, comprising conveying the conditioned flocculated material to a discharge location under a non-turbulent flow conditions and under shear rate and energy conditions that are lower than those of the shear conditioning used to form the conditioned flocculated material; and the discharging of the conditioned flocculated material being performed at the discharge location into the pit.
100. The process of claim 99, wherein subjecting the flocculating material to shear conditioning is performed in a conditioning pipeline to increase the yield stress of the flocculating material to an upper crest and then decrease the yield stress and enter a water release zone where water releases from flocs.
101. The process of claim 100, wherein the conveying is performed via a conveyance pipeline fluidly coupled to a downstream end of the conditioning pipeline.
102. The process of claim 101, wherein the conveyance pipeline is located on a sloped side of the pit.
103. The process of claim 101, wherein the conveyance pipeline is configured and operated such that the conditioned flocculated material flows therethrough under a laminar flow regime.
104. The process of claim 99, wherein the conveying is performed at shear conditions that are sufficiently low to substantially maintain flocs size unchanged.
105. The process of claim 101, wherein the conveyance pipeline has a pipe diameter greater than that of the conditioning pipeline.
106. The process of claim 101, wherein the conveyance pipeline is operated such that a flow rate therethrough is lower than that of the conditioning pipeline.
107. The process of claim 101, wherein the conveyance pipeline comprises multiple conveyance pipe sections arranged in parallel and in fluid communication with the conditioning pipeline.
108. The process of claim 107, wherein the multiple conveyance pipe sections supply respective discharge units that are positioned for discharging the conditioning flocculated material at different locations in the pit.
109. The process of claim 84, wherein the steps of adding the immobilization chemical to the thick fine tailings, subjecting the pre-treated material to shear conditioning, adding the flocculant to the conditioned pre-treated material, and subjecting the flocculating material to shear conditioning are all performed at locations spaced away from the pit.
110. The process of claim 109, wherein the steps of adding the immobilization chemical to the thick fine tailings, subjecting the pre-treated material to shear conditioning, adding the flocculant to the conditioned pre-treated material, and subjecting the flocculating material to shear conditioning are all performed by equipment that is not relocated.
111. The process of claim 101, further comprising relocating the conveyance pipeline as fluid rises within the pit.
112. The process of claim 84, wherein the immobilization chemical comprises a ferric cation.
113. The process of claim 112, wherein the immobilization chemical comprises ferric sulphate.
114. A process for treating mature fine tailings (MFT) derived from oil sands extraction and including constituents of concern (CoCs) comprising bitumen, naphthenic acid, arsenic and selenium, the process comprising:
- retrieving MFT from a tailings pond;
- providing an in-line flow of the MFT;
- adding in-line an aqueous immobilization solution into the in-line flow of MFT, the aqueous immobilization solution comprising an immobilization chemical comprising ferric sulphate, and in-line mixing thereof with the MFT, thereby producing a pre-treated tailings flow comprising: immobilized bitumen-clay complexes comprising ferric cations forming cation bridges between negatively charged bitumen droplets and negatively charged clay particles; insolubilized naphthenic acid; insolubilized arsenic; and insolubilized selenium;
- adding in-line an aqueous flocculant solution into the pre-treated tailings flow to form a flocculating material;
- in-line conditioning of the flocculating material to produce a flocculated material in a water release zone;
- discharging the flocculated material into a pit and allowing release water to separate from a solids-enriched material;
- forming a permanent aquatic storage structure (PASS) in the pit for retaining the solids-enriched material and a water cap, the solids-enriched material: forming a consolidating solids-rich lower stratum below the water cap; and retaining the immobilized bitumen-clay complexes, the insolubilized naphthenic acid, the insolubilized arsenic and the insolubilized selenium to inhibit migration of the CoCs into the water cap.
115. A process for treating thick fine tailings that includes contaminants of concern (CoCs) and suspended solids, the process comprising:
- subjecting the thick fine tailings to polymeric flocculation to flocculate the suspended solids and produce a flocculated tailings material;
- dewatering the flocculated tailings material to produce: an aqueous component depleted in the suspended solids and including CoCs; and a solids-enriched component comprising the flocculated solids; and
- subjecting the aqueous component to chemical immobilization to immobilize the CoCs and produce a contaminant-depleted water stream and a contaminant enriched stream including the immobilized CoCs.
116. A process for treating thick fine tailings that includes contaminants of concern (CoCs) and suspended solids, the process comprising:
- subjecting the thick fine tailings to polymeric flocculation to flocculate the suspended solids and produce a flocculated tailings material;
- subjecting the flocculated tailings material to chemical immobilization to immobilize the CoCs; and
- dewatering the flocculated tailings material to produce: an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
117. A process for treating thick fine tailings that includes contaminants of concern (CoCs) and suspended solids, the process comprising:
- simultaneously adding an immobilization chemical and a polymer flocculent into the thick fine tailings, in order to chemically immobilize the CoCs and polymerically flocculate the suspended solids; and
- dewatering the thick fine tailings to produce: an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
118. A process for treating thick fine tailings that includes contaminants of concern (CoCs) and suspended solids, the process comprising:
- adding a polymeric compound to the thick fine tailings, the polymeric compound comprising multivalent cation groups and organic polymeric groups, the multivalent cation groups effecting chemical immobilization of the CoCs and the organic polymeric groups effecting the polymeric flocculation of the suspended solids; and
- dewatering the thick fine tailings to produce: an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
119. A process for treating thick fine tailings that includes constituents of concern (CoCs) and suspended solids, the process comprising:
- subjecting the thick fine tailings to chemical immobilization and polymeric flocculation to chemically immobilize the CoCs and polymerically flocculate the suspended solids, to produce treated thick fine tailings, the chemical immobilization including the addition of ferric sulphate; and
- dewatering the treated thick fine tailings to produce: an aqueous component depleted in the CoCs and the suspended solids; and a solids-enriched component comprising the chemically immobilized CoCs and the flocculated solids.
120. A permanent aquatic storage structure (PASS) for storing thick fine tailings, the PASS comprising:
- a containment structure defining side walls and a bottom;
- a water cap within the containment structure;
- a solids-rich lower stratum below the water cap, the solids-rich lower stratum comprising polymercially flocculated solids and immobilized contaminants of concern (CoCs).
121. The PASS of claim 120, wherein the solids-rich lower stratum is formed from discharging thick fine tailings pre-treated by chemical immobilization and polymer flocculation into the containment structure.
122. The PASS of claim 120, wherein the immobilized CoCs comprise immobilized bitumen-clay complexes, insolubilized CoCs or a combination thereof.
123. The PASS of claim 122, wherein the insolubilized CoCs comprise insolubilized surfactants, insolubilized naphthenic acids, insolubilized arsenic, insolubilized selenium, insolubilized heavy metals, or any combinations thereof.
124. The PASS of claim 120, wherein the immobilized CoCs comprise an immobilization chemical selected from divalent and trivalent salts.
125. The PASS of claim 124, wherein the immobilization chemical comprises alum, gypsum, ferric sulphate or a combination thereof.
126. The PASS of claim 120, further comprising a fresh water line for introducing fresh water into the water cap.
127. The PASS of claim 120, further comprising a recycle water line for removing recycle water from the water cap.
128. The PASS of claim 120, wherein the water cap has a composition suitable to support aquatic life.
129. The PASS of claim 120, further comprising reclamation landforms selected from shorelines and littoral zones.
130. The PASS of claim 120, further comprising monitoring systems configured form monitoring a composition of the water cap.
131. The PASS of claim 120, further comprising an intermediate layer in between the water cap and the solids-rich lower stratum.
132. The PASS of claim 131, wherein the intermediate layer is composed of coarse particulate material or coke.
133. The PASS of claim 132, wherein the coke is derived from a bitumen processing operation.
134. The PASS of claim 120, wherein the solids-rich lower stratum is from a deposited pre-treated material and remains in-place after deposition.
135. A process for immobilizing bitumen contained in fine tailings derived from oil sands extraction, the process comprising:
- providing an in-line flow of fine tailings, and
- adding in-line an aqueous immobilization solution into the in-line flow of fine tailings and effecting in-line mixing, the aqueous immobilization solution comprising an immobilization chemical selected from multivalent inorganic salts, thereby producing a pre-treated tailings flow comprising immobilized bitumen-clay complexes comprising multivalent cations forming cation bridges between negatively charged bitumen droplets and negatively charged clay particles; and
- wherein the in-line addition and the in-line mixing of the immobilization chemical into the fine tailings are performed at a concentration and a mixing intensity sufficient to substantially inhibit aggregation of multivalent cation hydroxides and promote charge neutralization between the negatively charged bitumen droplets and the negatively charged clay particles.
136. The process of claim 135, wherein the aqueous immobilization solution is neutral or acidic.
137. The process of claim 136, wherein the immobilization chemical is fully dissolved in the immobilization solution prior to the in-line addition into the in-line flow of fine tailings.
138. The process of claim 135, wherein the immobilization chemical comprises a divalent cation.
139. The process of claim 135, wherein the immobilization chemical comprises a trivalent cation.
140. The process of claim 135, wherein immobilization chemical dosage is determined based on the density characteristics of the fine tailings.
141. The process of claim 140, wherein the density characteristics of the fine tailings are measured on-line prior to adding the immobilization chemical.
142. A process for treating tailings derived from oil sands extraction, the process comprising:
- adding an aqueous immobilization solution into an in-line flow of the tailings, the aqueous immobilization solution comprising ferric sulphate; and
- subjecting the in-line flow to shearing to form a pre-treated in-line tailings flow.
143. A process for treating tailings, comprising:
- adding a flocculant to an in-line flow of material comprising tailings to produce a flocculating material;
- subjecting the flocculating material to shear conditioning to form a conditioned flocculated material;
- conveying the conditioned flocculated material to a pit under non-turbulent flow conditions and under shear rate and energy conditions that are lower than those of the shear conditioning used to form the conditioned flocculated material; and
- discharging the conditioned flocculated material into the pit to enable water separation.
Type: Application
Filed: Feb 23, 2017
Publication Date: Nov 21, 2019
Inventors: Oladipo OMOTOSO (Calgary), Adrian REVINGTON (Calgary), Marc GORANSON (Calgary), Patrick Sean WELLS (Calgary), Macoura KONE (Calgary), Daryl HOCKLEY (Vancouver), Baha Elsayed ABULNAGA (Abbotsford), John DIEP (Burnaby), Benito MOYLS (Burnaby), Alan MELANSON (Calgary), Rodney GUEST (Calgary), Naveen PRATHAP (Calgary), Babak DERAKHSHANDEH (Burnaby)
Application Number: 16/079,455