ZWITTERIONIC NANOPARTICLES
The present invention relates to a zwitterionic nanoparticle, the zwitterionic nanoparticle comprising at least one nanoparticle and a zwitterionic case enclosing the nanoparticle. Furthermore, the present invention relates to a composition, a method of binding a zwitterionic nanoparticle and the use of a zwitterionic nanoparticle.
The present invention relates to zwitterionic nanoparticles. In particular, zwitterionic compounds covering the surface of nanoparticles are described. Furthermore, the present invention describes the use of such a preparation and ways and means for producing it.
TECHNICAL BACKGROUNDNanoparticles are of great interest because they promise broad technical applications, such as in image display devices, as information storage devices, as biological markers, in diagnostic imaging, as drug transporters, as theranostics, in photovoltaics, as sensors and as catalysts. Due to their small dimensions, nanoparticles can have physicochemical properties that lie between those of molecules and macroscopic materials. For example, nanoparticles made of semiconductor materials may exhibit quantum effects, both of the electron and thus also of the electron gap in all three dimensions, leading to an increase in the band gap of the material with decreasing size of the crystallite. The magnetic properties of the matter also change dramatically depending on the particle size. Similarly, the plasmon absorption of nanoparticles, e.g. gold nanoparticles, depends predominantly on the size and shape of said particles.
The biological effects of nanoparticles, such as the penetration capacity of biological barriers, such as membranes or the skin, or the toxicity of nanoparticles, however, depend not only on the particle properties themselves, but also on changes caused by the introduction of said particles into biological systems. In particular, spontaneous appositions of biological molecules comprising peptide-, protein-, nucleic acid-, or carbohydrate-like structural elements can take place, whereby a “biomolecular corona” may form around the original nanoparticle, which imparts novel, unpredictable and therefore mostly undesirable properties to it and significantly determines the further biological behavior of said particles. This process is known to the person skilled in the art as opsonization, and the resulting undesirable properties are known, inter alia, as “fouling”. Said undesired effects represent a major obstacle to the utilization of nanoparticles for bio-medical applications, since a high selectivity or specificity of said nanoparticles for the biological target structures, such as cells, tissue, organs, tumors, etc., is indispensable for the targeted manipulation of biological processes.
This is why numerous attempts have been made to suppress these undesired processes by providing said nanoparticles with an appropriate surface finish, thus eliminating the associated disadvantages. In particular, poly(ethylene glycol) (PEG) and oligo(ethylene glycol) (OEG) have been proposed to cover nanoparticle surfaces. Zwitterionic structures were also described for this purpose, with the latter reflecting the state of the art. Thus, WO2013090601 (A2) claims nanoparticles with zwitterionic ligands, in particular to achieve a low degree of non-specific protein absorption. Furthermore, WO2013090601 (A2) claims the functionalization of said nanoparticles with one or more functional groups to give said nanoparticles the desired properties, such as binding to a target molecule or to a receptor.
Thus, the coating of nanoparticles with zwitterionic structures aims at passivating or desensitizing the surface of said nanoparticles against biological influences. This effect is called “stealth” in the Anglo-Saxon literature. The desired effect is that nanoparticles desensitized in this way initially exhibit an indifferent behavior toward biological influences, are thus “invisible” to the respective biological system, and are made suitable for the respective purpose only by linking specific recognition motifs.
US 2014/0235803 A1 relates to nanoparticle-based biotechnological applications with materials that are insensitive to opsonization (“non-fouling materials”), such as poly(ethylene glycol) (PEG) and oligo(ethylene glycol) (OEG).
It is therefore the object of the present invention to further develop zwitterionic nanoparticles of the type mentioned above in an advantageous way, in particular to the effect that an improved and alternative application possibility of nanoparticles is made possible.
SUMMARY OF THE PRESENT INVENTIONThis object is achieved according to the invention by a zwitterionic nanoparticle with the characteristics of claim 1, according to which a zwitterionic nanoparticle comprises at least one nanoparticle and a zwitterionic case enclosing the nanoparticle.
Further configurations of the present invention are the subject-matter of the dependent claims.
Furthermore, the present invention relates to a composition which comprises at least one zwitterionic nanoparticle in an aqueous solution.
In addition, the present invention in a possible configuration relates to a method of binding a zwitterionic nanoparticle or a composition to a biological molecule or a plurality of biological molecules.
Furthermore, the present invention relates to the use of a zwitterionic nanoparticle and to a composition for a biological event or a biological application.
It was surprisingly found that the procedure described by the state of the art did not result in the expected effects in the present invention, but rather that the nanoparticles in question, which were coated with zwitterionic structures, showed a surprisingly pronounced, structure-dependent selectivity with regard to uptake into cells even without modification with specific recognition motifs. Thus, the present invention is excellently suited to specifically control the uptake of said nanoparticles into cells by structural variations of the zwitterionic motifs on the surface of nanoparticles. Such an application has not yet been described so far and is therefore new.
In the Figures:
The present invention describes nanoparticles with an organic zwitterionic case, said nanoparticles being suitable for the transport of molecules, in particular drug molecules, and optionally having superparamagnetic, plasmonic or fluorescent properties, including combinations of said properties. Nanoparticles in the sense of the invention are spatial objects which have an extension of 1 to 1000 nm in at least one spatial direction. The nanoparticles in question may be available in the form of both solid particles and hollow bodies in various shapes which include spherical, elongated, e.g. rod-shaped, elliptical, egg-shaped, dumbbell-shaped, ring-shaped, cube-shaped or cube-like, prismatic or cylindrical, regularly or irregularly multiply facetted geometric bodies, polygonal plates with e.g. a triangular, square or hexagonal shape, flakes, multi-arm or star-shaped bodies such as tetrapods, or a wire-like shape, etc. Said nanoparticles may optionally be coated with at least one shell made of a material other than that of the core. The term “nanoparticles” includes the terms “nanocrystal” or “ultra-small particle”.
The detailed description of the invention should be preceded by the statement that this invention is not limited to the methods, devices or preparations, as these can of course be modified. Furthermore, the terms used to describe the invention are merely intended to explain certain embodiments and in no way to restrict the scope of the invention. Thus, the specific or indefinite singular article “a” and “the” also includes the plural, unless the context clearly requires the opposite. Consequently, for example, the term “a cell” includes a large number of cells, “a nanoparticle” a large number of nanoparticles, “a biomolecule” such as DNA, protein, peptide, carbohydrate, etc. includes a large number of biomolecules, and so on.
All technical and scientific terms have the meaning as understood by the person skilled in the field of the present invention, unless otherwise defined or the context suggests a different meaning. Although any other method or other substances, similar to or equivalent to those described here, are also suitable for practicing or testing the invention, the preferred methods and substances are described below.
All publications mentioned here are hereby included by reference for the purpose of disclosure and description of the individual materials and processes for which the relevant reference has been cited. These publications, as described here, are provided only for disclosure thereof prior to the filing date of the present invention. However, it cannot be inferred from this what can be interpreted as an admission to the effect that the invention is not entitled to pre-date such disclosure as prior art. In describing the present invention, the following terms are used and shall be understood as defined below.
The term “inorganic nanocrystal” means a particle, generally a semiconductor particle, or a nanocrystalline particle which is not based on semiconductor materials, in particular a rare earth-doped metal oxide particle, or a rare earth-doped salt-like particle, or an oxidic or metallic particle with a diameter in the range of 1 nm to 1000 nm, preferably in the range of approx. 2 nm to 100 nm. The terms “semiconductor nanocrystal” and “quantum dot”, “quantum rod”, “quantum dot rod” or the abbreviations QD, QDs, QR, QRs, QDR, QDRs, SCNC or SCNCs are used interchangeably to denote semiconductor nanoparticles consisting of an inorganic substance which is optionally luminescent (i.e. capable of emitting electromagnetic radiation upon excitation) and comprises an inner core of one or more first semiconductor materials optionally enclosed by a sheath or “shell” of a second semiconductor material. For example, the encasing shell material may have a bandgap energy higher than that of the core material and selected such that the inter-atomic distances are similar to those of the core material. A semiconductor nanocrystal encased in a semiconductor shell is referred to as a “core/shell semiconductor nano crystal”.
Semiconductors are described in particular by their electrical conductivity, which lies between that of a conductor and that of a non-conductor. Suitable semiconductor materials may be the following materials, without being limited to them, and consist of a first element selected from groups 2 and 12 of the Periodic Table of the Elements and a second element selected from group 16 of the Periodic Table (e.g. ZnS, ZnSe, ZnTe, CdS, CdSe, CdTe, HgS, HgSe, HgTe, MgS, MgSe, MgTe, CaS, CaSe, CaTe, SrS, SrSe, SrTe, BaS, BaSe, BaTe, and the like); further, materials consisting of a first element selected from Group 15 of the Periodic Table of the Elements and a second element from Group 15 (e.g. GaN, GaP, GaAs, GaSb, InN, InP, InAs, InSb, etc.); furthermore, materials consisting of Group 14 of the Periodic Table of the Elements (Ge, Si, etc.); materials such as PbS, PbSe, PbTe, etc., materials such as CuInS, CuInGaS, etc., and alloys and mixtures thereof. As used here, all information on the Periodic Table of the Elements and its groups refers to the new IUPAC element group numbering system as described in Handbook of Chemistry and Physics, 61 st 20 Edition (CRC Press, 2000).
An SCNC (semi conductor nano crystal) is optionally surrounded by a layer made of an organic material. This organic layer may consist of a variety of substances and is distinguished by its affinity to the surface of the SCNC. In general, the coating material may consist of small organic individual molecules, polymers (or monomers that can be used in a polymerization reaction), inorganic complexes, or an extended crystalline structure. This coating can serve to impart the solubility of such a coated SCNC in a chosen solvent, certain functionalities or binding properties. In addition, the coating can also be used to adjust the optical properties of the SCNC. Accordingly, the terms “semiconductor nano crystal”, “SCNC”, “quantum dot”, as described here, also include organically encapsulated SCNC cores as well as organically encapsulated core/shell SCNCs.
“Monodisperse particles” include a stock of particles in which at least 60%, but preferably between 75% and 90%, of the particles in the stock correspond to a given size range. A stock of monodisperse particles has a particle diameter deviation of less than 10%, but preferably a deviation of less than 5% from the root mean square (RMS) of the stock. The term “one or more sizes of SCNC” is used to mean “one or more particle size distributions”. The expert will understand that certain sizes of nanoparticles are actually obtained as particle size distributions.
“Luminescence” is to be understood as a process in which an object emits electromagnetic radiation (light). Luminescence occurs when a system changes from an excited state to a lower-energy state, with the energy delivered being released in the form of photons. These energy states may have various forms, such as oscillation energy, rotational energy, may be of electronic nature, or exist in any combination of these energies. The transition that causes luminescence can be triggered by chemical energy stored in the system or by an external source. The external energy source can be supplied in various forms, including chemical, thermal, electrical, magnetic, electromagnetic, physical, or any other form capable of causing excitation to a higher energy state than the ground state. For example, a system can be excited by the absorption of at least one photon, by introduction into an electric field, or by a chemical redox reaction. The energy of the photon emitted during luminescence can be in the range from low-energy microwave radiation to high-energy X-ray radiation. Typically, luminescence refers to photons in the range from UV to IR radiation.
“Biological molecule” or “biomolecule” refers to any type of molecule found in biological applications, see following non-limiting enumeration: Optionally glycosylated proteins, e.g. antibodies, nano bodies, parts of antibodies such as single chain antibodies, Fab fragments, viral proteins, lectins, peptides including polyamino acids, nucleic acids including deoxyribonucleic acids (DNA), ribonucleic acids (RNA, siRNA, miRNA), “locked nucleic acid” (LNA), aptamers, lipids. Steroids, messengers, prions, carbohydrates, small molecules, etc.
The term “micelle” generally refers to a colloidal arrangement of surfactants distributed in a liquid, and the term “surfactant” refers to a surface active agent that reduces the surface tension of a liquid, usually organic compounds that are amphiphilic. The term “transfection” means the intentional or unintentional introduction of material, such as micelle-encapsulated nanoparticles into cells. The term “marking” generally refers to the intentional or unintentional attachment of material, such as micelle-encapsulated nanoparticles, to a cell, a biological molecule or a biological sample. Such material may, for example, be attached to or within the cell. Transfection and marking of a cell or the marking of a biological molecule or a biological sample are examples of biological applications. The term “biological event” includes an interaction of biological structures, a biological process, structural changes in a biological compound or a change in a biological process. The term “biological sample” means a tissue sample or a fluid derived from an individual, including but not limited to e.g. plasma, serum, spinal fluid, sperm, lymphatic fluid, external sections of the skin, respiratory system, digestive system, urogenital tract, tear fluid, saliva, milk, blood cells, tumors, organs, and samples from in vitro cell culture components (including but not limited to processed cell culture medium derived from cell growth in cell cultures, optionally from virally infected cells, recombinant cells and cell components). Terms such as “bio-functionalized”, “bonded”, “attached”, “linked” or “conjugated” are used interchangeably here and include both direct and indirect linking, attachment or conjugation, unless the context requires otherwise.
In this context, the term “zwitterionic nanoparticle” means a spatial object having an extension of 1 to 1000 nm in at least one spatial direction, said extension being enclosed by a zwitterionic case. In various embodiments, this case may consist of individual molecules that are not covalently connected to each other. The outer shape of the case can be produced in different embodiments of the invention by ionic, non-ionic, electrostatic or covalent interactions, based on thermodynamic, such as negentropic effects, such as micelle formation, or by combinations of these binding forces. Alternatively, the formation of this case may be produced by association of the case components on at least one formative inorganic nanocrystal, such as a nanocrystal consisting of semiconductors, silicates, salts, metals, or metal oxides, or on a nanoparticle consisting of organic components, such as polymers or solid lipids, or by intermolecular interactions without the involvement of a formative nanoparticle. Thus, the present invention also provides a preparation containing at least one micelle in a non-aqueous solution. Said micelle may encapsulate one or more nanoparticles, which may be monodisperse nanoparticles. Said micelle may optionally contain at least one active ingredient instead of one or more nanoparticles. Said micelle may optionally be empty.
The term “zwitterionic compound” includes the terms “zwitterionic ligand” or “zwitterionic group”. The terms “zwitterion” and “betaine” are also interchangeable.
Said zwitterionic compounds have the general formula (I):
A-X-[L1-Z1-L2-Z2]n Formula (I)
In this formula, A is optionally a group having affinity for the surface of the inorganic nanoparticle, or is an at least divalent atom, preferably from the group C, N, O, S, P or Si, capable of forming a covalent bond to the nanoparticle. X is an optional branching element such that X has, in addition to the bond to A, at least one further bond to L1. X optionally represents a bond or an at least divalent atom, preferably from the group C, N, O, S, P or Si. L1 and L2 are mutually independent linker groups; Z1 includes a first charged or ionizable group; Z2 includes a second charged or ionizable group, provided that they are opposite in case Z1 or Z2 carry charges. n comprises the integers between 1 and the maximum valence of X-1.
A includes or optionally comprises at least one amino, mercapto, dithiocarbamate, carboxylate, phosphate, phosphonate group.
L1 and L2 are mutually independent, linear or branched, optionally saturated or unsaturated hydrocarbon chains having one to forty carbon atoms, which may optionally contain heteroatoms selected from the group consisting of N, O, P, Si and S.
The following examples are intended to illustrate the invention without limiting its scope.
EXAMPLE 1 Preparation of tert-butyl(3-(dimethylamino)propyl)(methyl)carbamateN,N,N′-trimethylpropane-1,3-diamine (586 μL, 3.98 mmol) and triethylamine (TEA) (1.6 mL, 11.54 mmol) were dissolved in dry dichloromethane (DCM) (12 mL) and cooled in an ice bath. Subsequently, Di-tert-butyl dicarbonate (1 mL, 4.35 mmol) was dissolved in dry DCM (2 mL) and slowly added drop-wise at a temperature below 2° C. The reaction mixture was stirred for a further 45 minutes at 0° C. and overnight (15 hours) at room temperature. For reprocessing, the organic phase was extracted with saturated NaCl, saturated NaHCO3 solution and H2O (5 mL each), dried over Na2SO4 and the solvent was removed in vacuum. The product had the form of a light yellow oil.
Yield: 87%
1H-NMR (600 MHz, CDCl3): δ [ppm]=7.26 (CDCl3); 3.28-3.20 (m, 2H, H-3); 2.84 (s, 3H, H-1); 2.31-2.25 (m, 2H, H-5); 2.23 (s, 6H, H-7 and H-8); 1.73-1.66 (m, 2H, H-4) and 1.45 (s, 9H, H-13, H-14 and H-15).
EXAMPLE 2 Preparation of 3-((3-((tert-butoxycarbonyl)(methyl)amino)propyl)-dimethylammonio)-propane-1-sulfonateTert-butyl(3-(dimethylamino)propyl)(methyl)carbamate (1.11 g, 5.13 mmol) and 1,3-propane sultone (677 μL, 7.70 mmol) were dissolved in dry DCM (25 mL). The reaction mixture was stirred for five days at room temperature to form a pearly solid. The solvent was largely removed at a rotary evaporator and the excess of 1,3-propane sultone separated by repeated washing with dry THF. The residue was dried in vacuum and the product was present as a colorless solid.
Yield: 81%
1H-NMR (400 MHz, D2O): δ [ppm]=4.79 (D2O); 3.55-3.51 (m, 2H, H-7); 3.42-3.35 (m, 4H, H-3 and H-5); 3.16 (s, 6H, H-11 and H-12); 3.02 (t, 2H, J=7.2 Hz, H-9), 2.91 (s, 3H, H-1); 2.29-2.21 (m, 2H, H-8), 2.12-2.04 (m, 2H, H-4) and 1.50 (s, 9H, H-17, H-18 and H-19).
13C-NMR (100 MHz, D2O): δ [ppm]=157.6 (C-13); 81.8 (C-16); 62.3 (C-5); 62.0 (C-7); 50.6 (C-11 and C-12); 47.2 (C-9); 45.0 (C-3); 33.8 (C-1); 27.7 (C-17, C-18 and C-19); 20.8 (C-4) and 18.2 (C-8).
ESI-MS: (m/z) calc. for C14H31N2O2S (M+H)+ 339.1948, ascertained 339.1955.
IR (neat): υ [cm−1]=2973; 2925; 1679 (C═O); 1199 (S═O); 1161 (C—O); 1034 (S═O), 605 and 524.
EXAMPLE 3 Preparation of 3-(dimethyl(3-(methylamino)propyl)ammonio)propane-1-sulfonate3-((3-((tert-butoxycarbonyl)(methyl)amino)propyl)dimethylammonio)-propane-1-sulfonate (435 mg, 1.29 mmol) was dissolved in ultrapure water (13 mL) and the reaction vessel was rinsed with nitrogen. The solution was then heated to 135° C. in the microwave for 90 minutes. After removing the water, the crude product was dissolved in MeOH (8 mL), mixed with Amberlyst A26 and stirred for four hours at room temperature. The Amberlyst was then filtered off and the solvent removed in the rotary evaporator. For complete drying, the residue was absorbed in a small amount of ultrapure water and lyophilized. The product was present as a colorless, strongly hygroscopic solid.
Yield: 88%
1H-NMR (400 MHz, D2O): δ [ppm]=4.79 (D2O); 3.52-3.48 (m, 2H, H-7); 3.41-3.37 (m, 2H, H-5); 3.13 (s, 6H, H-11 and H-12); 3.00 (t, 2H, J=7.1 Hz, H-9); 2.76-2.72 (m, 2H, H-3); 2.42 (s, 3H, H-1); 2.27-2.19 (m, 2H, H-8) and 2.06-1.99 (m, 2H, H-4).
13C-NMR (100 MHz, D2O): δ [ppm]=62.2 (C-7); 61.9 (C-5); 50.7 (C-11 and C-12); 47.1 (C-9); 46.6 (C-3); 34.1 (C-1); 21.2 (C-4) and 18.1 (C-8).
ESI-MS: (m/z) calc. for C9H23N2O3S (M+H)+ 239.1424, ascertained 239.1430.
IR (neat): υ[cm−1]=432; 3034; 2968; 1164 (S═O); 1032 (S═O), 601 and 521.
EXAMPLE 4 Preparation of tert-butyl-bis(3-(dimethylamino)propyl)carbamate3,3′-Iminobis-N,N-dimethylpropylamine (891 μL, 4.00 mmol) and TEA (1.6 mL, 11.54 mmol) were dissolved in dry DCM (12 mL) and cooled in an ice bath. Di-tert-butyldicarbonate (1 mL, 4.35 mmol) was then dissolved in dry DCM (2 mL) and slowly added in drops at a temperature below 3° C. The reaction mixture was stirred for further 90 minutes at 1° C. and overnight (15 hours) at room temperature. For reprocessing, the organic phase was extracted with saturated NaCl, saturated NaHCO3 solution and H2O (5 mL each), dried over Na2SO4 and the solvent was removed in vacuum. The product had the form of a light yellow oil.
Yield: 68%
1H-NMR (400 MHz, CDCl3): δ [ppm]=7.26 ppm (CDCl3); 3.24-3.17 (m, 4H, H-2 and H-8); 2.25 (t, 4H, J=7.4 Hz, H-4 and H-10); 2.21 (s, 12H, H-6, H-7, H-12 and H-13); 1.72-1.65 (m, 4H, H-3 and H-9) and 1.45 (s, 9H, H-18, H-19 and H-20).
EXAMPLE 5 Preparation of 3,3′-(((((tert-butoxycarbonyl)azadiyl)bis(propane-3,1-diyl))bis(dimethylammoniodiyl))bis(propane-1-sulfonate)Tert-butyl-bis(3-(dimethylamino)propyl)carbamate (500 mg, 1.74 mmol) and 1,3-propane sultone (459 μL, 5.22 mmol) were dissolved in dry DCM (20 mL). After 24 hours, a colorless solid had formed and the resulting suspension had such a high viscosity that dry DCM (20 mL) was added again. The reaction mixture was stirred at room temperature for a further three days. The solvent was removed as far as possible at the rotary evaporator and the excess of 1,3-propane sultone was separated by repeated washing with dry THF. The residue was dried in vacuum and the product was present as a colorless solid.
Yield: 91%
1H-NMR (400 MHz, D2O): δ [ppm]=4.79 (D2O); 3.55-3.51 (m, 4H, H-6 and H-14); 3.40-3.36 (m, 8H, H-2, H-4, H-10 and H-12); 3.16 (s, 12H, H-18, H-19, H-20 and H-21); 3.02 (t, 4H, J=7.1 Hz, H-8 and H-16); 2.27-2.21 (m, 4H, H-7 and H-15); 2.13-2.05 (m, 4H, H-3 and H-11) and 1.52 (s, 9H, H-26, H-27 and H-28).
13C-NMR (100 MHz, D2O): δ [ppm]=157.1 (C-22); 82.3 (C-25); 62.2 (C-4, C-6, C-12 and C-14); 50.8 (C-18, C-19, C-20 and C-21); 47.2 (C-8 and C-16); 40.3 (C-2 and C-10); 27.7 (C-26, C-27 and C-28); 22.7 (C-3 and C-11) and 18.2 (C-7 and C-15).
ESI-MS: (m/z) calc. for C21H46N3O8S2 (M+H)+ 532.2721, ascertained 532.2741.
IR (neat): υ [cm−1]=3452; 3038; 2974; 1676 (C═O), 1157 (C—O); 1033 (S═O), 602 and 521.
EXAMPLE 6 Preparation of the 3,3′-((Azadiylbis(propane-3,1-diyl))bis(dimethylammoniodiyl))bis-(propane-1-sulfonate)3,340 -(((((tert-butoxycarbonyl)azanediyl)bis(propane-3,1-diyl))bis(dimethylammoniodiyl))bis-(propane-1-sulfonate) (783 mg, 1.47 mmol) was dissolved in ultrapure water (14.7 mL). The reaction vessel was rinsed with nitrogen and the solution was heated to 13° C. for 90 minutes in the microwave. After lyophilization, the product was dissolved in MeOH (10 mL) and stirred overnight in the presence of Amberlyst A 26. After filtering off the Amberlyst, the solvent was removed at the rotary evaporator and the residue lyophilized again after adding a small amount of ultrapure water. The product had the form of a light yellow, foam-like solid.
Yield: 71%
1H-NMR (400 MHz, D2O): δ [ppm]=4.79 (D2O); 3.55-3.51 (m, 4H, H-4 and H-12); 3.44-3.39 (4H, m, H-6 and H-14); 3.16 (s, 12 H, H-18, H-19, H-20 and H-21); 3.03 (t, 4H, J=7.1 Hz, H-8 and H-16); 2.77-2.74 (m, 4H, H-2 and H-10); 2.30-2.22 (m, 4H, H-7 and H-15) and 2.07-1.99 (m, 4H, H-3 and H-11).
13C-NMR (100 MHz, D2O): δ [ppm]=62.2 (C-4 and C-12); 62.00 (C-6 and C-14); 50.7 (C-18, C-19, C-20 and C-21); 47.2 (C-8 and C-16); 44.9 (C-2 and C-10); 21.7 (C-7 and C-15) and 18.1 (C-3 and C-11).
ESI-MS: (m/z) calc. for C16H38N3O6O2 (M+H)+ 432.2197, ascertained 432.2216.
IR (neat): υ [cm−1]=3434; 3038; 2968; 2824; 1167 (S═O); 1033 (S═O), 602 and 521.
EXAMPLE 7 Preparation of 1-((3-((tert-butoxycarbonyl)(methyl)amino)dimethyl-ammonio)hex-5-en-3-sulfonateTert-butyl(3-(dimethylamino)propyl)(methyl)carbamate (434 mg, 2.01 mmol) and 3-allyl-1,2-oxathiolane-2,2-dioxide (442 mg, 2.72 mmol) were dissolved in dry DCM (20 mL). The reaction mixture was stirred for five days at room temperature and a pearly solid was formed. The solvent was largely removed at the rotary evaporator and the excess of 3-Allyl-1,2-oxathiolane-2,2-dioxide was separated by repeated washing with dry THF. The residue was dried in vacuum and the product was present as a colorless solid.
Yield: 83%
1H-NMR (400 MHz, D2O): δ [ppm]=5.98-5.87 (m, 1H, H-14); 5.31-5.22 (m, 2H, H-15); 4.79 (D2O); 3.67-3.60 (m, 1H, H-7a); 3.55-3.31 (m, 5H, H-3, H-5 and H-7b); 3.14 (s, 6H, H-11 and H-12); 3.04-2.98 (m, 1H, H-9), 2.91 (s, 3H, H-1); 2.79-2.72 (m, 1H, H-13a); 2.42-2.36 (m, 1H, H-13b); 2.26-2.14 (m, 2H, H-8), 2.08-2.03 (m, 2H, H-4) and 1.50 (s, 9H, H-20, H-21 and H-22).
13C-NMR (100 MHz, D2O): δ [ppm]=157.1 (C-16); 134.2 (C-14); 118.4 (C-15); 81.8 (C-19); 61.6 (C-5 and C-7); 56.5 (C-9); 50.8 (C-11 and C-12); 45.3 (C-3); 34.0 (C-13); 33.7 (C-1); 27.7 (C-20, C-21 and C-22); 22.2 (C-8) and 20.8 (C-4).
ESI-MS: (m/z) calc. for C17H35N2O5S (M+H)+ 379.2261, ascertained 379.2284.
IR (neat): υ [cm−1]=2976; 1679 (C═O); 1199 (S═O); 1172 (C—O); 1028 (S═O), 602 and 537.
EXAMPLE 8 Preparation of 1-(dimethyl(3-methylamino)propyl)ammonio)hex-5-ene-3-sulfonate1-((3-((tert-butoxycarbonyl)(methyl)amino)dimethylammonio)hex-5-en-3-sulfonate (568 mg, 1.50 mmol) was dissolved in ultrapure water (15 mL). The reaction vessel was rinsed with nitrogen and the solution was heated to 135° C. in the microwave for 90 minutes. After lyophilization, the product was dissolved in MeOH (10 mL) and stirred overnight in the presence of Amberlyst A 26. After filtering off the Amberlyst, the solvent was removed at the rotary evaporator and the residue lyophilized again after adding a small amount of ultrapure water. The product had the form of a light yellow, foam-like solid.
Yield: 90%
1H-NMR (400 MHz, D2O): δ [ppm]=5.97-5.87 (m, 1H, H-14); 5.31-5.23 (m, 2H, H-15); 4.79 (D2O); 3.68-3.60 (m, 1H, H-7a); 3.54-3.47 (m, 1H, H-7b); 3.41-3.37 (m, 2H, H-5); 3.13 (s, 6H, H-11 and H-12); 3.04-2.98 (m, 1H, H-9); 2.79-2.72 (m, 3H, H-3 and H-13a); 2.43 (s, 3H, H-1); 2.42-2.36 (m, 1H, H-13b); 2.27-2.11 (m, 2H, H-8) and 2.06-1.98 (m, 2H, H-4).
13C-NMR (100 MHz, D2O): δ [ppm]=134.2 (C-14); 118.4 (C-15); 61.7 (C-5); 61.5 (C-7); 56.5 (C-9); 50.7 (C-11 and C-12); 46.7 (C-3); 34.2 (C-1); 34.0 (C-13); 22.2 (C-8) and 21.3 (C-4).
ESI-MS: (m/z) calc. for C12H27N2O3S (M+H)+ 279.1737, ascertained 279.1751.
IR (neat): υ [cm−1]=3453; 3028; 2942; 2847; 2793; 1173 (S═O); 1028 (S═O), 601 and 532.
EXAMPLE 9 Preparation of 11-bromo-N-methylundecanamide11-bromoundecanoic acid (5.00 g, 18.85 mmol) was dissolved in dry DCM (100 mL) and a solution of oxalyl chloride (1.7 mL, 19.82 mmol) was added in drops to dry DCM (10 mL) within five minutes. An evolution of gas was observed at the beginning and the reaction mixture was stirred for one hour at room temperature. Subsequently, the solvent and excess oxalyl chloride were removed in vacuum and the raw product dissolved in dry Et2O (12 mL). The activated acid was added in drops to an aqueous methylamine solution (40%, 4.3 mL, 49.80 mmol) cooled in an ice bath, and a colorless precipitate was immediately formed. The precipitate was filtered off and washed with H2O (50 mL). After drying in vacuum, the product was present as a colorless solid.
Yield: 89%
1H-NMR (400 MHz, CDCl3): δ [ppm]=7.26 (CDCl3); 5.82 (brs, 1H, NH); 3.40 (t, 2H, J=6.9 Hz, H-2); 2.82 (s, 3H, H-14); 2.21 (t, 2H, J=7.6 Hz, H-11); 1.88-1.81 (m, 2H, H-3); 1.65-1.60 (m, 2H, H-10); 1.43-1.38 (m, 2H, H-4) and 1.34-1.25 (m, 10H, H-5 to H-9).
EXAMPLE 10 Preparation of 11-(dimethylamino)-N-methylundecanamide11-bromo-N-methylundecanamide (1.39 g, 5.00 mmol) and a solution of dimethylamine in EtOH (33% by weight, 9 mL, 50.40 mmol) were heated to 60° C. in the microwave for two hours. The solvent and the excess dimethylamine were removed in vacuum and the hydrobromide of the product was obtained in the form of a light yellow solid. The solid was suspended in MTBE (10 mL) and extracted with 1 M NaOH (5 mL). The organic phase was dried over Na2SO4 and the solvent was removed in vacuum. The product had the form of a light yellow solid.
Yield: 91%
1H-NMR (400 MHz, CDCl3): δ [ppm]=7.26 (CDCl3); 5.50 (brs, 1H, NH); 2.80 (s, 3H, H-15); 2.33 (t, 2H, J=7.7 Hz, H-3); 2.29 (s, 6H, H-1 and H-16); 2.15 (t, 2H, J=7.6 Hz, H-12); 1.65-1.57 (m, 2H, H-11); 1.53-1.46 (m, 2H, H-4) and 1.34-1.22 (m, 12H, H-5 to H-10).
EXAMPLE 12Preparation of N,N,N′-Trimethylundecane-1,11-diamine
LiAlH4 (2 M in dry THF, 2.7 mL, 5.40 mmol) in dry THF (5 mL) was cooled to −2° C. in an ice bath. At this temperature, a solution of 11-(dimethylamino)-N-methylundecanamide (660 mg, 2.72 mmol) in dry THF (15 mL) was slowly added in drops. The solution became turbid during addition. After addition, the reaction mixture was slowly heated to room temperature and then heated under reflux for three hours. The reaction mixture was then cooled to 0° C. and carefully quenched with H2O (205 μL), 15% NaOH (205 μL) and again H2O (615 μL), whereby the inorganic salts precipitated. The suspension was stirred at room temperature for a further 30 minutes. To separate the solid, the suspension was centrifuged and the solid washed several times with dry THF. The combined organic phases were dried over Na2SO4 and the solvent was removed in vacuum. The raw product had the form of a yellow oil and was used without further reprocessing.
Yield: 96% (raw yield)
1H-NMR (600 MHz, CDCl3): δ [ppm]=7.26 (CDCl3); 2.55 (t, 2H, J=7.2 Hz, H-13); 2.43 (s, 3H, H-15); 2.23 (t, 2H, J=7.4 Hz, H-3); 2.21 (s, 6H, H-1 and H-16); 1.51-1.43 (m, 4H, H-4 and H-12) and 1.34-1.23 (m, 14H, H-5 to H-11).
EXAMPLE 12 Preparation of the tert-butyl(11-(dimethylamino)undecyl(methyl)carbamateDi-tert-butyl dicarbonate (512 μL, 2.23 mmol) and Amberlyst 15 (76 mg, 15 wt. %) were put in a round flask. Subsequently, N,N,N′-trimethylundecane-1,11-diamine (505 mg, 2.21 mmol) was added in drops and a strong evolution of gas was observed. The reaction mixture was stirred for 15 minutes, then diluted with DCM (22 mL), and the Amberlyst was filtered off. The solvent was removed at the rotary evaporator and the raw product was purified by column chromatography (DCM/methanol/TEA). The product had the form of a light yellow oil.
Yield: 57%
1H-NMR (400 MHz, CDCl3): δ [ppm]=7.26 (CDCl3); 3.17 (t, 2H, J=6.9 Hz, H-3); 2.82 (s, 3H, H-1); 2.27 (t, 2H, J=7.6 Hz, H-13); 2.24 (s, 6H, H-15 and H-16); 1.52 -1.46 (m, 4H, H-4 and H-12); 1.45 (s, 9H, H-21, H-22 and H-23) and 1.28-1.26 (m, 14H, H-5 to H-11).
13C-NMR (100 MHz, CDCl3): δ [ppm]=156.0 (C-17); 79.2 (C-20); 77.2 (CDCl3); 60.0 (C-13); 48.7 (C-3); 45.5 (C-15 and C-16); 34.2 (C-1); 29.7-29.5 (C-5 to C-11); 28.6 (C-21, C-22 and C-23); 27.8-27.6 (C-4 and C-12) and 26.9 (C-5 to C-11).
ESI-MS: (m/z) calc. for C19H41N2O2 (M+H)+ 329.3163, ascertained 329.3169.
IR (neat): υ [cm−1]=2973; 2925; 2854; 1696 (C═O) and 1153 (C—O).
EXAMPLE 13 Preparation of 3-((11-((tert-butoxycarbonyl)(methyl)amino)undecyl)-dimethylammonio)-propane-1-sulfonateTert-butyl-(11-(dimethylamino)undecyl(methyl)carbamate (250 mg, 0.76 mmol) and 1,3-propane sultone (105 μL, 1.17 mmol) were dissolved in dry DCM (10 mL). The reaction mixture was stirred at room temperature for 11 days. The solvent was largely removed at the rotary evaporator and the excess 1,3-propane sultone was separated by repeated washing with dry THF. The residue was dried in vacuum and the product was present as a colorless solid.
Yield: 77%
1H-NMR (600 MHz, D2O): δ [ppm]=4.79 (D2O); 3.50-3.47 (m, 2H, H-15); 3.35-3.32 (m, 2H, H-13); 3.24-3.25 (m, 2H, H-3); 3.12 (s, 6H, H-26 and H-27); 2.99 (t, 2H, J=7.1 Hz, H-17); 2.84 (s, 3H, H-1); 2.26-2.20 (m, 2H, H-16); 1.79-1.77 (m, 2H, H-12); 1.57-1.53 (m, 2H, H-4); 1.46 (s, 9H, H-23, H-24 and H-25); 1.38 (m, 4H, H-10 and H-11); 1.33 (m, 8H, H-6 to H-9) and 1.30-1.28 (m, 2H, H-5).
13C-NMR (150 MHz, D2O): δ [ppm]=156.8 (C-19); 81.1 (C-22); 65.1 (C-13); 62.9 (C-15); 51.5 (C-26 and C-27); 49.4 (C-3); 48.2 (C-17); 34.5 (C-1); 29.9-29.3 (C-5 to C-10); 28.8 (C-23, C-24 and C-25); 26.9 (C-4); 26.5 (C-12); 22. 8 (C-11) and 19.0 (C-16).
ESI-MS: (m/z) calc. for C22H46N2O5S (M+H)+ 451.3200, ascertained 451.3214.
IR (neat): υ [cm−1]=3456; 2973; 2925; 2855; 1680 (C═O); 1165 (C—O); 1035 (S═O), 606 and 521.
EXAMPLE 14 Preparation of 3-(dimethyl(11-(methylamino)undecyl)ammonio)propane-1-sulfonate3-((11-((tert-butoxycarbonyl)(methyl)amino)undecyl)dimethylammonio)-propane-1-sulfonate (600 mg, 1.33 mmol) was dissolved in ultrapure water (13 mL). The reaction vessel was rinsed with nitrogen and the solution was heated to 135° C. in the microwave for 90 minutes. The water was removed by lyophilization and the product was present as a colorless, strongly hygroscopic solid.
Yield: 93%
1H-NMR (400 MHz, D2O): δ [ppm]=4.79 (D2O); 3.51-3.46 (m, 2H, H-15); 3.36-3.32 (m, 2H, H-13); 3.12 (s, 6H, H-19 and H-20); 3.01 (t, 2H, J=7.2 Hz, H-17); 2.95-2.91 (m, 2H, H-3); 2.63 (s, 3H, H-1); 2.28-2.20 (m, 2H, H-16); 1.81-1.77 (m, 2H, H-12); 1.69-1.61 (m, 2H, H-4); 1.39 (m, 4H, H-5 and H-11) and 1.33 (m, 10H, H-6 to H-10).
13C-NMR (100 MHz, D2O): δ [ppm]=64.2 (C-13); 61.9 (C-15); 50.6 (C-19 and C-20); 49.5 (C-3); 47.3 (C-17); 33.0 (C-1); 28.4-28.1 (C-6 to C-10); 26.0 (C-4); 25.7-25.4 (C-5 and C-11); 21.7 (C-12) and 18.1 (C-16).
ESI-MS: (m/z) calc. for C17H39N2O3S (M+H)+ 351.2676, ascertained 351.2689.
IR (neat): υ [cm−1]=2919; 2849; 1196 (S═O); 1036 (S═O), 603 and 526.
EXAMPLE 15 Formation of DithiocarbamateThe formation of dithiocarbamate was monitored by absorption spectroscopy in the range of 230-400 nm. For this purpose, 1 mL of a 25 mM solution of the amine according to example 3 or example 14 and 500 μL of a 0.66 M solution CS2 were prepared in MeOH. For the reference measurements of the starting substances, 10 μL each of the stock solutions were diluted with 1.5 mL MeOH in a UV semi-micro cuvette and the absorption was measured. To monitor the dithiocarbamate formation, 38 μL of the CS2 solution were added to the remaining amine solution and the absorption was monitored over a period of 40 and 110 minutes, respectively. For this purpose, 10 μL of the reaction mixture were diluted with 1.5 mL MeOH after different time intervals and measured at the absorption spectrometer. As soon as the typical absorption maxima at 255 and 291 nm did not increase any more, the dithiocarbamate formation was completed and the ligand solution was used in the next step.
EXAMPLE 16 Ligand ExchangePrior to the ligand exchange, the QDQRs (1 nmol) were precipitated three times with MeOH and centrifuged at 6,700×g. The colorless supernatant was discarded and the nanoparticles were absorbed in 2.5 mL n-hexane. Furthermore, dilutions of the zwitterionic amines according to example 3, example 14, example 6 and example 8 (each 0.2 M) as well as of CS2 (0.66 M) were prepared in MeOH. The ligand surpluses varied between 10,000 and 100,000 related to the concentration of nanoparticles, and the ratio of amine to CS2 was 1:1. To form the dithiocarbamate ligands, the corresponding amounts of amine and CS2 were filled up to a total volume of 1 mL with MeOH and stirred at room temperature for 15 minutes (for the amines according to example 3, 14 and 8) or 90 minutes (for the amine of example 6). The ligand solution was then added to the nanoparticles in n-hexane and the two-phase system was vigorously stirred for 30 minutes until the QDQRs precipitated from the reaction solution. In some cases, an extended reaction time of up to six hours was necessary to achieve precipitation of the nanoparticles. After short centrifugation (1 minute at 1,000×g), the now colorless organic phases were removed, the nanoparticles were carefully dried in a nitrogen stream and then incorporated in ultrapure water (0.5-1 mL).
EXAMPLE 17 Stability MeasurementsThe following pH buffers were prepared for the stability measurements:
Citrate Buffer pH 5.1Citric acid (960 mg, 5 mmol) was weighed in a 50 mL graduated flask, dissolved in ultrapure water (approx. 40 mL) and adjusted to a pH value of 5.1 using 1 M NaOH. Then it was filled up to the mark with ultrapure water (concentration: 0.1 M).
Phosphate Buffer pH 7.4PBS buffer with a pH value of 7.4 was purchased commercially.
Borate Buffer pH 9.0H3BO3 (62 mg, 1 mmol) was weighed in a 50 mL graduated flask, dissolved in ultrapure water (approx. 40 mL) and adjusted to a pH value of 9.0 using 1 M NaOH. Then it was filled up to the mark with ultrapure water (concentration: 20 mM).
Phosphate Buffer pH 11.5K2HPO4 (8.71 g, 50 mmol) was weighed in a 50 mL graduated flask and dissolved in a small amount of ultrapure water. Subsequently, it was filled up to the mark with ultrapure water (concentration: 1 M). From this solution, 500 μL were diluted with 49.5 mL ultrapure water (concentration 0.01 M) and a pH value of 11.5 was adjusted using 1 M NaOH.
Furthermore, the following media were used for the stability measurements: 10 mM HEPES, DMEM (without phenol red), 10% FCS in DMEM, PBS and 1% BSA in PBS.
For the stability measurements, 990 μL of the pH buffer or medium were put in a quartz cuvette and 10 μL of the nanoparticle solution were added (final concentration: 20 nM). After an incubation period of two minutes, the fluorescence intensity of the samples was measured every 20 minutes within the first two hours, hourly in the further course of the day and thereafter every 24 hours. On the whole, the fluorescence intensity was monitored over a period of one week. The measurements were performed at an excitation wavelength of 350 nm.
EXAMPLE 18 Cell Culture ExperimentsThe culture medium consisted of 10% FCS in DMEM with 1% PenStrep and sodium pyruvate in each case. The incubation of the cells always took place at 37° C. and a CO2 content of 5%.
The zwitterionic Quantum Dots/Quantum Rods (QDQRs) nanoparticles were examined in various in vitro experiments with regard to their toxicity and non-specific cell uptake. Yellow-emitting QDQRs comprising the short- and long-chain zwitterionic ligand (QDQRs-17a and QDQRs-17b) were used for the studies to investigate a possible influence of the chain length of the ligand on the interactions of the QDQRs with cells. A549 cells were used for both toxicity and cell uptake studies. A549 cells are human basal epithelial cells derived from an adenocarcinoma of the lung which have been cultured as a cell line.
For the use of nanoparticles in biochemistry or medicine, it is essential that they do not produce intolerable toxicity. In the case of cadmium-containing nanoparticles, there is the general possibility that the cells may be damaged by escaping cadmium ions. The probability that cadmium ions are released into the environment is relatively high, especially with the QDQRs used here. On the one hand, the proportion of cadmium in the elongated nanoparticles is higher by a factor of 12 compared to spherical particles of the same diameter. On the other hand, the QDQRs lack a passivating shell of zinc sulfide, which is often used to coat cadmium-containing nanoparticles to prevent cadmium ions from leaching out.
The toxicity of the zwitterionic QDQRs-17a and QDQRs-17b was tested using the Cellomics Array Scan. For the toxicity tests, A549 cells were plated on a 96-well plate and incubated with QDQR solutions in a concentration range of 25 to 500 nM. Cadmium chloride, which was used in a concentration range from 25 to 1,000 μM, was used as the positive control. The increase in the cadmium chloride concentration by a factor of 1,000 is due to the fact that a single QDQR of the tested samples contains about 8,200 cadmium atoms. Assuming that the totality of the nanoparticles dissolve and release the cadmium contained in them, the lowest concentration of 25 nM QDQRs used would correspond to a concentration of 205 μM cadmium chloride. After an incubation period of 16 hours, the cells were blended with a staining solution consisting of the cell nucleus dye Hoechst 33342 and the mitochondrial dye MitoTracker® Deep Red FM and then fixed with formaldehyde solution. The 96-well plates were then read out with the Cellomics Array Scan. A software was used to automatically determine the parameters number of cells, cell nucleus intensity and cell nucleus size using the intensity of the dye by Hoechst, and the transmembrane potential of the mitochondria on the basis of the mitochondrial dye. In addition, microscopic images of the cells were taken to control the number of cells and cell morphology.
EXAMPLE 19 Toxicity TestsFor the toxicity tests, A549 cells were plated in culture medium on a 96-well plate (10,000 cells per well) and incubated overnight. When the medium had been sucked off, the samples to be tested (diluted with culture medium, 100 μL per well) were applied in different concentrations and incubated for 16 hours. The samples were then removed and the cells were mixed with 100 μL staining solution (final concentration: 75 nM MitoTracker® Deep Red and 2.5 μg/ml Hoechst 33342 in DMEM with 10% FCS) and incubated for a further 30 minutes. To fix the cells, the staining solution was removed and 100 μL of a warm fixing solution (3.7% formaldehyde in Dulbecco's PBS, DPBS) were added. After 20 minutes, the fixing solution was sucked off and washed twice with DPBS before the samples were measured on the Cellomics Array Scan.
Similarly, no morphological changes of the cells or cell nuclei after 16 hours of incubation with zwitterionic QDQRs are discernible in the microscopic images. As an example, the microscopic images of the A549 cells after incubation with QDQRs-17a are shown in
In contrast, cadmium chloride at a concentration of 100 μM or more, which corresponds approximately to a QDQR concentration of 12 nM or more, has a toxic effect on the cells. The number of cells per well, the cell nucleus intensity and the cell nucleus size decreases significantly due to cell death (
This becomes particularly clear when looking at the microscopic images of the cells after 16 hours of incubation with cadmium chloride, which are shown in
In summary, it can be said that despite the high cadmium content in the QDQRs used and the absence of an additional passivating zinc sulfide case, there is no measurable toxicity originating from the QDQRs up to a concentration of 500 nM. Thus, the zwitterionic QDQRs produced fulfil an important prerequisite for later biomedical applications.
Thus, it could be shown that zwitterionic QDQRs have no toxic effect on A549 cells even in high concentrations of up to 500 nM.
Next, the uptake behavior of the QDQRs-17a and QDQRs-17b with A549 cells was analyzed and it was examined whether the nanoparticles were accommodated in different ways depending on the chain length of the ligand.
EXAMPLE 20 Cell Uptake Experiments with A549 Cells (In Vitro)For the cell uptake experiments, A549 cells were plated in culture medium on an 8 well Labtek (20,000 cells per well) and incubated for 24 and 48 hours, respectively. The medium was sucked off and the samples to be investigated (diluted with DMEM and correspondingly with or without 10% FCS, concentration: 100 nM) were added. The cells were then incubated for four and 16 hours, respectively. After expiry of the incubation period, the medium was removed, the cells were blended with a staining solution (final concentration: 2.5 μg/ml Hoechst 33342 in DMEM, 200 μL per well) and incubated again for 30 minutes. Here again, the cells were fixed with a 3.7% formaldehyde solution in DPBS for 20 minutes. After washing the cells twice with DPBS, the samples were measured with a confocal microscope.
On the one hand, two different incubation times (four and 16 hours) were tested. On the other hand, incubation was performed either in the presence or absence of 10% FCS. The absence of FCS in the medium was used to investigate whether nanoparticle uptake into the possibly famishing cells could be forced. In all experiments the cells were incubated with a 100 nM QDQR solution. After incubation, the cells were washed, the cell nuclei stained with Hoechst 33342, fixed and analyzed with a confocal microscope.
For QDQRs-17a, an unspecific uptake of the nanoparticles was visible under all experimental conditions, see
The incubation of A549 cells with QDQRs-17b surprisingly showed a completely different picture (see
After an incubation period of four hours, the nanoparticles were absorbed by the cells neither under serum-containing conditions (B) nor under serum-free conditions (A). Also the increased incubation time of 16 hours in the presence of 10% FCS did not result in an unspecific uptake of QDQRs (D). Only in serum-free medium, a slight unspecific uptake of QDQRs was detectable (C), which, however, was significantly lower compared to QDQRs-17a.
In general, the cell uptake of nanoparticles depends on many different factors, such as the size and shape of the particles, their surface charge, or the presence of a protein corona. As could be demonstrated by the DLS measurements and TEM images, both the size and shape of QDQRs-17a and QDQRs-17b are almost identical, so that these factors cannot explain the different cell uptake behavior.
In summary, it can be said that QDQRs are different from A549 cells in their uptake behavior in a surprisingly high extent. Thus, the zwitterionic ligands on the nanoparticle surface are suitable for influencing cell uptake by structural changes.
Claims
1. A zwitterionic nanoparticle, wherein the zwitterionic nanoparticle comprises at least one nanoparticle and a zwitterionic case which encloses the nanoparticle.
2. The zwitterionic nanoparticle according to claim 1, wherein the nanoparticle is one or more of a luminescent, magnetic, or plasmonic nanoparticle.
3. The zwitterionic nanoparticle according to claim 1, wherein the nanoparticle contains at least one active substance molecule.
4. The zwitterionic nanoparticle according to claim 1, wherein the nanoparticle is a semiconductor nanoparticle.
5. The zwitterionic nanoparticle according to claim 4, wherein the nanoparticle is doped with heavy metal ions such as Ag, Cu, Co or Mn.
6. The zwitterionic nanoparticle according to claim 1, wherein the nanoparticle is selected from lanthanide-doped nanoparticles having salt-like host lattices.
7. The zwitterionic nanoparticle according to claim 1, wherein the nanoparticle is a metallic nanoparticle or consists of a metal oxide.
8. The zwitterionic nanoparticle according to claim 1, wherein a structure of the nanoparticle is described by formula MwNxAyBz, wherein M and N are independently selected from elements of groups 8, 9, 10, 11, 12, 13 or 14 of a Periodic Table of the Elements, including Fe, Co, Ni, Pt, Cu, Zn, Cd, Al, Ga, In, Ge, Sn or Pb, and A and B are independently selected from the elements 10, 11, 13, 15 or 16 of the Periodic Table of the Elements, including Pd, Pt, N, P, As, Sb, Ga, O, S, Se or Te, and wherein w, x, y and z can independently attain integer multiples of a value between 0 and 1, provided that a total positive charge of cationic elements is opposite and equal to a negative charge of anionic elements.
9. The zwitterionic nanoparticle according to claim 8, wherein the nanoparticle is surrounded by at least one shell.
10. The zwitterionic nanoparticle according to claim 9, wherein a composition of the shell is described by formula OsCtDu O1CzD1-z, wherein O is independently selected from the elements of the groups 8, 9, 10, 11, 12, 13 or 14 of the Periodic Table of the Elements, including Co, Ni, Pt, Cu, Zn, Cd, Al, Ga, In, Ge, Sn or Pb, and C and D are independently selected from the elements 10, 11, 15 or 16 of the Periodic Table of the Elements, including Pd, Pt, N, P, As, Sb, O, S, Se or Te, and wherein s, t, and u can independently attain integer multiples of a value between 0 and 1, provided that the total positive charge of the cationic elements is opposite and equal to the negative charge of the anionic elements and that the compositions of MwNxAyBz and OsCtDu are different.
11. The zwitterionic nanoparticle according to claim 1, wherein the zwitterionic compound is described by the formula A-X-[L1-Z1-L2-Z2]n wherein
- A is optionally a group having affinity for a surface of the nanoparticle or is an at least divalent atom capable of forming a covalent bond to the nanoparticle; and
- L1 and L2 are mutually independent linker groups.
12. The zwitterionic nanoparticle according to claim 11, wherein A is selected from the group consisting of C, N, O, S, P or Si, wherein at least one amino, mercapto, dithiocarbamate, carboxy, phosphate, phosphonate group is provided.
13. The zwitterionic nanoparticle according to claim 12, wherein L1 and L2 are mutually independent linear or branched, optionally saturated or unsaturated hydrocarbon chains having one to forty carbon atoms, optionally containing heteroatoms from the group consisting of N, O, P, Si and S.
14. A composition containing at least one zwitterionic nanoparticle in an aqueous solution, the at least one zwitterionic nanoparticle comprising at least one nanoparticle and a zwitterionic case which encloses the nanoparticle.
15. A method, comprising: binding a zwitterionic nanoparticle comprising at least one nanoparticle and a zwitterionic case which encloses the nanoparticle or a composition of the zwitterionic nanoparticle in an aqueous solution to a biologic molecule or a plurality of biological molecules.
16. The method of claim 15, further comprising, using the zwitterionic nanoparticle or the composition of claim 15 for a biological event or a biological application.
17. (canceled)
Type: Application
Filed: Jan 19, 2018
Publication Date: Dec 5, 2019
Inventors: Theo SCHOTTEN (Hamburg), Michaela STEUTER (Hamburg), Jan-Philip MERKL (Hamburg), Horst WELLER (Hamburg)
Application Number: 16/479,581